Next Article in Journal
Development of Triamcinolone Acetonide-Loaded Nanostructured Lipid Carriers (NLCs) for Buccal Drug Delivery Using the Box-Behnken Design
Next Article in Special Issue
Performance Comparisons of Polymer Semiconductors Synthesized by Direct (Hetero)Arylation Polymerization (DHAP) and Conventional Methods for Organic Thin Film Transistors and Organic Photovoltaics
Previous Article in Journal
Biomedical Applications of Polylactide (PLA) and Its Copolymers
Previous Article in Special Issue
Direct (Hetero)Arylation Polymerization of a Spirobifluorene and a Dithienyl-Diketopyrrolopyrrole Derivative: New Donor Polymers for Organic Solar Cells
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 23
Issue 4
10.3390/molecules23040981
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synthesis of a 1,2-Dithienylethene-Containing Donor-Acceptor Polymer via Palladium-Catalyzed Direct Arylation Polymerization (DArP)

by
Masayuki Wakioka
1,*,
Natsumi Yamashita
1,
Hiroki Mori
2,
Yasushi Nishihara
2 and
Fumiyuki Ozawa
1,*
1
International Research Center for Elements Science (IRCELS), Institute for Chemical Research, Kyoto University, Uji, Kyoto 611-0011, Japan
2
Research Institute for Interdisciplinary Science, Okayama University, 3-1-1 Tsushimanaka, Kita-ku, Okayama 700-8530, Japan
*
Authors to whom correspondence should be addressed.
Molecules 2018, 23(4), 981; https://doi.org/10.3390/molecules23040981
Submission received: 10 April 2018 / Revised: 19 April 2018 / Accepted: 20 April 2018 / Published: 23 April 2018
(This article belongs to the Special Issue Direct (Hetero)Arylation: A New Tool for Organic Electronics)
Browse Figures
Versions Notes

Abstract

:
This paper reports the synthesis of D-A polymers containing 1,2-dithienylethene (DTE) units via palladium-catalyzed direct arylation polymerization (DArP). The reaction of dibromoisoindigo (1-Br) and DTE (2-H), in the presence of Pd2(dba)3·CHCl3 (0.5 mol%), P(2-MeOC6H4)3 (L1) (2 mol%), pivalic acid (1 equiv) as catalyst precursors, and Cs2CO3 (3 equiv) as a base affords poly(1-alt-2) with a high molecular weight (Mn up to 44,900). Although, it has been known that monomers, with plural C–H bonds, tend to form insoluble materials via direct arylation at undesirable C–H positions; the reaction of 1-Br and 2-H cleanly proceeds without insolubilization. The resulting polymer has a well-controlled structure and exhibits good charge transfer characteristics in an organic field-effect transistor (OFET), compared to the polymer produced by Migita–Kosugi–Stille cross-coupling polymerization. The DArP product displays an ideal linear relationship in the current–voltage curve, whereas the Migita–Kosugi–Stille product shows a VG-dependent change in the charge mobility.

Graphical Abstract

1. Introduction

π-Conjugated polymers with donor–acceptor combinations of repeated units (D-A polymers) often exhibit a high device performance in organic field-effect transistors (OFETs) and thin-film solar cells [1,2,3,4]. Thus far, such polymers have been prepared by Migita–Kosugi–Stille cross-coupling polymerization. However, this method needs toxic tin reagents for the monomer preparation, and the polymerization forms a highly toxic side product such as Me3SnBr [5]. It has also been implicated that the residual impurities that arise from tin reagents may deteriorate the device performance [6,7,8,9]. In this context, the palladium-catalyzed direct arylation polymerization (DArP), that proceeds via C–H bond activation, has recently emerged as a simple yet fundamental solution for these problems [10,11,12]. We have developed a highly efficient DArP catalyst using P(2-MeOC6H4)3 (L1) as a ligand to produce D-A polymers with a high molecular weight [13,14,15,16,17,18,19,20]. The resulting polymers have well-controlled structures without tin impurities, thereby leading to good material properties [16].
In this study, we examined the synthesis of a D-A polymer with 1,2-dithienylethene (DTE) as donor units; poly(1-alt-2) in Scheme 1. DTE-based D-A polymers, such as poly(1-alt-2), have been prepared by Migita–Kosugi–Stille cross-coupling polymerization and have proven to be competent compounds in OFETs [21,22,23]; however, their synthesis via DArP has been poorly successful [24]. This is probably due to the existence of plural C–H bonds in DTE. Direct arylation at undesirable C–H positions forms branching and cross-linking polymers, which eventually change to insoluble materials [25,26,27,28]. On the other hand, we found that the L1-based catalyst successfully produces the desired poly(1-alt-2) without formation of insoluble materials. The resulting polymer has a well-controlled structure and shows better charge transfer properties in OFET than Migita–Kosugi–Stille cross-coupling products.

2. Results and Discussion

2.1. Synthesis of Poly(1-alt-2)

First, we examined the DArP of dibromoisoindigo (1-Br) and DTE (2-H) in several types of solvents (Scheme 1). Table 1 summarizes the results. The reaction was conducted with Pd2(dba)3·CHCl3 (0.5 mol%), L1 (2 mol%), pivalic acid (1 equiv) as catalyst precursors, and Cs2CO3 (3 equiv) as a base. When the reaction was carried out in toluene at 100 °C, the reaction mixture turned into a dark red mass in 5 h; however, Soxhlet extraction with o-Cl2C6H4 afforded poly(1-alt-2) (Mn = 17,000) in almost quantitative yield and no colored substance remained in the extraction thimble (run 1). THF was less effective as a solvent, giving a low-molecular weight polymer (Mn = 7400) (run 2). On the other hand, the molecular weight increased in 2-MeTHF (Mn = 22,700) (run 3), and when a low-molecular weight portion was removed by Soxhlet extraction with CHCl3, poly(1-alt-2) with Mn = 44,900 was obtained in a recovery rate of 63% (run 3a). Unlike the reaction in toluene, the reaction system retained liquidity in 2-MeTHF.
Next, we examined the synthesis of poly(1-alt-2) in the presence of N,N,N′,N′-tetramethylethylenediamine (TMEDA). We have documented that, while the reaction becomes slow, the combined use of L1 and TMEDA effectively prevents the formation of structural defects, including homocoupling, branching, and cross-linking defects leading to insolubilization [18,19]. The reaction in toluene proceeded without the formation of a solid mass, and poly(1-alt-2) with Mn = 15,700 was produced in a high yield, in 24 h (run 4). On the other hand, the DArP in the presence of TMEDA was significantly slow in 2-MeTHF, and the molecular weight remained moderate, even after 96 h (run 5).
For comparison, poly(1-alt-2) was prepared by Migita–Kosugi–Stille cross-coupling polymerization (Scheme 2). Referring to the literature [22,23], the reactions of 1-Br and 2-SnMe3 were examined in toluene under two catalytic conditions. The reaction in the presence of Pd2(dba)3·CHCl3 (2 mol%) and P(o-tolyl)3 (8 mol%) at 90 °C for 24 h yielded poly(1-alt-2) with moderate molecular weight (Mn = 17,700, PDI = 1.7) in quantitative yield [22]. Although the GPC molecular weight of the polymer prepared under those reactions conditions has been reported to be Mn = 98,800 (PDI = 3.1), this value has been estimated at 40 °C, using CHCl3 as the column eluate [22]. In contrast, we performed GPC calibration at 140 °C, using o-Cl2C6H4. Thus, we re-examined the polymer under the same GPC conditions using CHCl3 and confirmed that our product (Mn = 93,400, PDI = 4.6) has comparable molecular weight to that of the literature.
The synthesis of poly(1-alt-2) via Migita–Kosugi–Stille cross-coupling was also carried out under dilute conditions (monomers: 8 mM) using a large amount of P(o-tolyl)3 (16 mol%) at 115 °C for 48 h [23]. In this case, the resulting polymer was sparingly soluble and unable to be examined by GPC using o-Cl2C6H4 at 140 °C, whereas the molecular weight could be estimated at 150 °C using 1,2,4-Cl3C6H3 as the column eluate (Mn = 53,800, PDI = 2.8). The NMR analysis described below was performed for a soluble part of the product, prepared by Soxhlet extraction with CHCl3 (18% recovery, Mn = 24,400, PDI = 2.5).

2.2. 1H-NMR Analysis of Poly(1-alt-2)

Figure 1 compares 1H-NMR spectra of the four types of poly(1-alt-2)s prepared by DArP (a and b) and Migita–Kosugi–Stille cross-coupling polymerization (c and d). The signal assignments are based on the spectra of model compounds of substructures and structural defects (see the Supplementary Materials). In Figure 1a—for the polymer of run 4, Table 1 (Mn = 15,700)—the spectrum consists of the main signals due to cross-coupling units (A1–A6) and small signals arise from three kinds of terminal groups (a1–a3, b1–b4, and c1–c7). Although the signal due to 1-1 homocoupling defects (B) is observed, its ratio is less than 0.1%. On the other hand, signals assignable to 2-2 homocoupling, branching, and cross-linking defects are not observed. Figure 1b, which corresponds to the polymer of run 3 in Table 1 (Mn = 22,700), displays the same signals as Figure 1a, although the relative intensity of each unit is changed, and the signals are broadened reflecting the increase in molecular weight. The number of 1-1 homocoupling defects (B) is estimated to be less than 0.1%, whereas other structural defects are not observed. Hence, the highly controlled structures of the DArP polymers have been confirmed.
On the other hand, Figure 1c,d for the Migita–Kosugi–Stille cross-coupling products (Mn = 17,700 and 24,400) contain many unidentified peaks in addition to the signals assigned to the core and terminal groups of poly(1-alt-2). Moreover, the signals are somewhat broadened as compared to the DArP products of comparable molecular weight.

2.3. Electronic Properties of Poly(1-alt-2)

Table 2 summarizes the optical and electrochemical properties of poly(1-alt-2)s, in thin film, which were evaluated by UV–vis spectroscopy and cyclic voltammetry. The absorption spectra of poly(1-alt-2)s, listed in Table 2, are shown in Figure 2. All spectra consist of two absorption bands around 600–700 (band I) and 650–750 nm (band II). The band I arises from the intramolecular charge transfer (ICT) transitions in the donor–acceptor units, whereas the band II is induced for the aggregation of polymer chains through strong intermolecular interactions [29]. In Figure 2, the changes in the relative intensity, from band II to band I, are small. The maximum absorption wavelengths of polymers are approximately the same (λmax = 638(3) and 700(2) nm). Moreover, the absorption onsets (λonset) are within the range of 746–753 nm, showing that the optical band gaps are little affected by the polymerization methods, as well as the molecular weight (Egopt = 1.66(1) eV). Indeed, the electronic properties evaluated by cyclic voltammetry are consistent for all polymers: EHOMO = −5.34(2) eV, ELUMO = −3.60(3) eV, EgCV = 1.74(2) eV.

2.4. OFET Characteristics of Poly(1-alt-2)

OFET characteristics of the DArP polymers were compared with those of the Migita–Kosugi–Stille cross-coupling products. OFET devices were fabricated on an n+-Si/SiO2 substrate treated with n-octyltriethoxysilane (OTS) as a self-assembled monolayer (SAM). The active layer of poly(1-alt-2) was formed by spin-coating from a CHCl3 or o-Cl2C6H4 solution, and sequential thermal annealing was carried out at 240 °C for 30 min under an inert atmosphere. The solvents for spin-coating were changed according to the solubility of polymers. We confirmed that the solvents little affected the carrier mobility (Table S1).
Poly(1-alt-2) exhibited typical p-type characteristics under ambient conditions in the dark. Table 3 lists the hole mobility observed for the polymers shown in Table 2. The highest hole mobility was observed for the DArP polymer in entry 1 (Mn = 15,700, μh = 0.31 cm2 V−1 s−1), and this value was comparable to that for the Migita–Kosugi–Stille cross-coupling product with similar molecular weight in entry 5 (Mn = 17,700, μh = 0.28 cm2 V−1 s−1). On the other hand, the hole mobility for the other polymers was low (entries 2–4 and 6). It emerges that the hole mobility depends on the weight average molecular weight (Mw), not on the number average molecular weight (Mn). Indeed, the hole mobility decreases significantly with increasing the Mw values.
To understand the reasons behind the large variation in device performance depending on molecular weight, polymer thin films formed on an OTS-treated substrate were investigated by grazing incidence wide-angle X-ray scattering (GIWAXS) and atomic force microscopy (AFM). These investigations indicated that the hole mobility changes with the surface morphology rather than with the crystallinity (Figures S4–S6). The GIWAXS analysis revealed the predominant edge-on orientation on the substrate for all films. Moreover, in Table 3, the lamellar d-spacings (dl) and π–π stacking distances (dπ) were very similar to each other, regardless of the Mw values and the polymerization methods dl = 21.4(7) Å and dπ = 3.75(4) Å. On the other hand, in the AFM images, the surface morphology clearly changed with Mw, and the polymer with a lower Mw value tended to form a smoother surface. The polymers with a high Mw value in entries 4 and 6 showed several clear grain boundaries, suppressing the carrier transport efficiency.
While the hole mobility was little affected by the polymerization methods, the charge transfer characteristics were clearly different for the DArP and Migita–Kosugi–Stille cross-coupling products. In Figure 3a, the DArP polymer (entry 1, Table 3) has the ideal transfer characteristics, showing a linear correlation in the current–voltage curve. Thus, this polymer exhibited a VG-independent change in the hole mobility. A similar trend was observed for all DArP products (see Figure S2). On the other hand, in Figure 3b, the Migita–Kosugi–Stille cross-coupling product (entry 5, Table 3) exhibited non-ideal double slope characteristics [30], which are often related to the contact resistance and/or the presence of carrier traps due to defects or impurities in the polymer transistors. The same phenomenon has already been documented for the poly(1-alt-2) prepared by Migita–Kosugi–Stille cross-coupling polymerization [22].

3. Conclusions

We have described the synthesis of D-A polymers containing 1,2-dithienylethene (DTE) units via palladium-catalyzed direct arylation polymerization (DArP). The reaction of dibromoisoindigo (1-Br) and DTE (2-H) using the catalytic system with P(2-MeOC6H4)3 (L1) as a ligand afforded the desired poly(1-alt-2) with a high molecular weight (Mn up to 44,900) and yield. The 1H-NMR analysis revealed a highly controlled structure for the resulting polymer. On the other hand, the 1H-NHR spectrum of the Migita–Kosugi–Stille cross-coupling polymerization product indicated the contamination of unknown structural defects. These polymers showed almost the same optical properties, independently of the polymerization methods. Moreover, they exhibited comparable charge mobility when the weight average molecular weight (Mw) was similar. However, the charge transfer characteristics of the DArP product in OFET were superior to those of the Migita–Kosugi–Stille cross-coupling product. The DArP product displayed an ideal linear relationship in the current–voltage curve, whereas the Migita–Kosugi–Stille product showed a non-ideal double-slope curve. The so-called double-slope characteristics have been recognized to be a crucial problem in the practical applications of polymer-based OFETs [30]. Since the physical properties observed by spectroscopic and electrochemical methods were almost the same, the difference in charge transfer characteristics of these products is possibly due to the difference in structural defects. Moreover, there is a possibility that impurities arising from tin reagents cause the deterioration in device performance. Thus, the present study indicates that the highly selective synthesis of D-A polymers via DArP using P(2-MeOC6H4)3 (L1) as a ligand provides a simple but powerful approach for developing OFETs with good properties.

4. Materials and Methods

4.1. General Considerations

All manipulations were performed under a nitrogen atmosphere using Schlenk techniques or a glove box. Toluene, THF, and 2-MeTHF were dried over Na/Ph2CO, distilled, and stored over activated MS4A. Cs2CO3 was dried overnight at 120 °C under vacuum and handled in a glove box. PivOH was distilled and handled in a glove box. TMEDA was dried over CaH2 and distilled. 1-Br [31], 2-H [32], 2-SnMe3 [33], and Pd2(dba)3·CHCl3 [34] were prepared according to the literature. The other chemicals were obtained from commercial sources and used without purification.

4.2. Direct Arylation Polymerization of 1-Br and 1-H

A typical procedure is reported for run 3 in Table 1. The compounds Cs2CO3 (195 mg, 0.60 mmol) and pivalic acid (20.4 mg, 0.20 mmol) were placed in a 10 mL Schlenk tube equipped with a Teflon screw cock in a glove box. Then, 1-Br (219 mg, 0.20 mmol), 2-H (38.5 mg, 0.20 mmol), Pd2(dba)3·CHCl3 (1.0 mg, 1.0 μmol), L1 (1.4 mg, 4.0 μmol), and 2-MeTHF (0.4 mL) were added. The mixture was stirred at room temperature for 0.5 h, and next at 100 °C for 24 h. The mixture was cooled up to room temperature, diluted with CHCl3 (100 mL), and washed with water (3 × 10 mL). The organic phase was poured into a vigorously stirred MeOH (400 mL). A dark red precipitate was collected by filtration, washed with MeOH, and dried under vacuum overnight. The product was subjected to Soxhlet extraction with acetone and hexane, and next with o-Cl2C6H4 (100 mL) containing diethylammonium diethyldithiocarbamate (10 mg). No colored substance remained in the extraction thimble. The o-Cl2C6H4 extract was poured into a vigorously stirred MeOH (400 mL), to produce a dark red solid of poly(1-alt-2), in >99% yield (231 mg, Mn = 22,700, Mw/Mn = 3.9).
1H-NMR (C2D2Cl4, 130 °C, 600 MHz): δ 9.26 (d, J = 8.1 Hz, 2H), 7.35 (d, J = 3.3 Hz, 2H), 7.32 (d, J = 8.5 Hz, 2H), 7.14–7.08 (m, 4H), 7.04 (s, 2H), 3.77 (br, 4H), 2.11–2.01 (br, 2H), 1.54–1.22 (m, 80H), 0.94–0.86 (m, 12H).

Supplementary Materials

Supplementary materials including detailed experimental procedures, characterizations of all new compounds and polymers, as well as additional figures and tables are available online.

Acknowledgments

This work was supported by KAKENHI (JP17H03055, JP15K17855, JP17K05883) from Japan Society for the Promotion of Science and the ACT-C program of Japan Science and Technology Agency. The GIWAXS experiments were performed on beamline BL46XU of SPring-8 with the approval of the Japan Synchrotron Radiation Research Institute (JASRI) (Proposal 2017B1831). We are grateful to Atsushi Wakamiya (ICR, Kyoto University) for analytical GPC assistance, Takeshi Hasegawa and Takafumi Shimoaka (ICR, Kyoto University) for AFM assistance, and Itaru Osaka (Hiroshima University) and Tomoyuki Koganezawa (JASRI) for the measurement of GIWAXS images. The NMR measurements (600 MHz spectrometer) were supported by the Joint Usage/Research Center (JURC) at ICR, Kyoto University.

Author Contributions

M.W. and F.O. conceived and designed the experiments; M.W., N.Y., and H.M. performed the experiments; M.W., N.Y., and F.O. prepared the manuscript; all authors discussed and commented on the manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Boudreault, P.L.T.; Najari, A.; Leclerc, M. Processable Low-Bandgap Polymers for Photovoltaic Applications. Chem. Mater. 2011, 23, 456–469. [Google Scholar] [CrossRef]
  2. Beaujuge, P.M.; Frechet, J.M.J. Molecular Design and Ordering Effects in π-Functional Materials for Transistor and Solar Cell Applications. J. Am. Chem. Soc. 2011, 133, 20009–20029. [Google Scholar] [CrossRef] [PubMed]
  3. Zhou, H.; Yang, L.; You, W. Rational Design of High Performance Conjugated Polymers for Organic Solar Cells. Macromolecules 2012, 45, 607–632. [Google Scholar] [CrossRef]
  4. Sirringhaus, H. 25th Anniversary Article: Organic Field-Effect Transistors: The Path Beyond Amorphous Silicon. Adv. Mater. 2014, 26, 1319–1335. [Google Scholar] [CrossRef] [PubMed]
  5. Carsten, B.; He, F.; Son, H.J.; Xu, T.; Yu, L. Stille Polycondensation for Synthesis of Functional Materials. Chem. Rev. 2011, 111, 1493–1528. [Google Scholar] [CrossRef] [PubMed]
  6. Van Mierloo, S.; Hadipour, A.; Spijkman, M.-J.; Van den Brande, N.; Ruttens, B.; Kesters, J.; D’Haen, J.; Van Assche, G.; de Leeuw, D.M.; Aernouts, T.; et al. Improved Photovoltaic Performance of a Semicrystalline Narrow Bandgap Copolymer Based on 4H-Cyclopenta[2,1-b:3,4-b′]dithiophene Donor and Thiazolo[5,4-d]thiazole Acceptor Units. Chem. Mater. 2012, 24, 587–593. [Google Scholar] [CrossRef]
  7. Nikiforov, M.P.; Lai, B.; Chen, W.; Chen, S.; Schaller, R.D.; Strzalka, J.; Maser, J.; Darling, S.B. Detection and role of trace impurities in high-performance organic solar cells. Energy Environ. Sci. 2013, 6, 1513–1520. [Google Scholar] [CrossRef]
  8. Usluer, O.; Abbas, M.; Wantz, G.; Vignau, L.; Hirsch, L.; Grana, E.; Brochon, C.; Cloutet, E.; Hadziioannou, G. Metal Residues in Semiconducting Polymers: Impact on the Performance of Organic Electronic Devices. ACS Macro Lett. 2014, 3, 1134–1138. [Google Scholar] [CrossRef]
  9. Bannock, J.H.; Treat, N.D.; Chabinyc, M.; Stingelin, N.; Heeney, M.; de Mello, J.C. The influence of polymer purification on the efficiency of poly(3-hexylthiophene): Fullerene organic solar cells. Sci. Rep. 2016, 6, 23651. [Google Scholar] [CrossRef] [PubMed]
  10. Rudenko, A.E.; Thompson, B.C. Optimization of direct arylation polymerization (DArP) through the identification and control of defects in polymer structure. J. Polym. Sci. Part A Polym. Chem. 2015, 53, 135–147. [Google Scholar] [CrossRef]
  11. Bura, T.; Blaskovits, J.T.; Leclerc, M. Direct (Hetero)arylation Polymerization: Trends and Perspectives. J. Am. Chem. Soc. 2016, 138, 10056–10071. [Google Scholar] [CrossRef] [PubMed]
  12. Pouliot, J.-R.; Grenier, F.; Blaskovits, J.T.; Beaupré, S.; Leclerc, M. Direct (Hetero)arylation Polymerization: Simplicity for Conjugated Polymer Synthesis. Chem. Rev. 2016, 116, 14225–14274. [Google Scholar] [CrossRef] [PubMed]
  13. Wang, Q.; Takita, R.; Kikuzaki, Y.; Ozawa, F. Palladium-Catalyzed Dehydrohalogenative Polycondensation of 2-Bromo-3-hexylthiophene: An Efficient Approach to Head-to-Tail Poly(3-hexylthiophene). J. Am. Chem. Soc. 2010, 132, 11420–11421. [Google Scholar] [CrossRef] [PubMed]
  14. Wakioka, M.; Kitano, Y.; Ozawa, F. A Highly Efficient Catalytic System for Polycondensation of 2,7-Dibromo-9,9-dioctylfluorene and 1,2,4,5-Tetrafluorobenzene via Direct Arylation. Macromolecules 2013, 46, 370–374. [Google Scholar] [CrossRef]
  15. Wakioka, M.; Ichihara, N.; Kitano, Y.; Ozawa, F. A Highly Efficient Catalyst for the Synthesis of Alternating Copolymers with Thieno[3,4-c]pyrrole-4,6-dione Units via Direct Arylation Polymerization. Macromolecules 2014, 47, 626–631. [Google Scholar] [CrossRef]
  16. Wakioka, M.; Ishiki, S.; Ozawa, F. Synthesis of Donor–Acceptor Polymers Containing Thiazolo[5,4-d]thiazole Units via Palladium-Catalyzed Direct Arylation Polymerization. Macromolecules 2015, 48, 8382–8388. [Google Scholar] [CrossRef]
  17. Iizuka, E.; Wakioka, M.; Ozawa, F. Mixed-Ligand Approach to Palladium-Catalyzed Direct Arylation Polymerization: Synthesis of Donor–Acceptor Polymers with Dithienosilole (DTS) and Thienopyrroledione (TPD) Units. Macromolecules 2015, 48, 2989–2993. [Google Scholar] [CrossRef]
  18. Iizuka, E.; Wakioka, M.; Ozawa, F. Mixed-Ligand Approach to Palladium-Catalyzed Direct Arylation Polymerization: Effective Prevention of Structural Defects Using Diamines. Macromolecules 2016, 49, 3310–3317. [Google Scholar] [CrossRef]
  19. Wakioka, M.; Takahashi, R.; Ichihara, N.; Ozawa, F. Mixed-Ligand Approach to Palladium-Catalyzed Direct Arylation Polymerization: Highly Selective Synthesis of π-Conjugated Polymers with Diketopyrrolopyrrole Units. Macromolecules 2017, 50, 927–934. [Google Scholar] [CrossRef]
  20. Wakioka, M.; Nakamura, Y.; Montgomery, M.; Ozawa, F. Remarkable Ligand Effect of P(2-MeOC6H4)3 on Palladium-Catalyzed Direct Arylation. Organometallics 2015, 34, 198–205. [Google Scholar] [CrossRef]
  21. Zhang, W.; Yu, G. Rational Design of Diarylethylene-Based Polymeric Semiconductors for High-Performance Organic Field-Effect Transistors. J. Polym. Sci. Part A Polym. Chem. 2017, 55, 585–603. [Google Scholar] [CrossRef]
  22. Shin, J.; Um, H.A.; Lee, D.H.; Lee, T.W.; Cho, M.J.; Choi, D.H. High mobility isoindigo-based π-extended conjugated polymers bearing di(thienyl)ethylene in thin-film transistors. Polym. Chem. 2013, 4, 5688–5695. [Google Scholar] [CrossRef]
  23. Gao, Y.; Deng, Y.; Tian, H.; Zhang, J.; Yan, D.; Geng, Y.; Wang, F. Multifluorination toward High-Mobility Ambipolar and Unipolar n-Type Donor–Acceptor Conjugated Polymers Based on Isoindigo. Adv. Mater. 2017, 29, 1606217. [Google Scholar] [CrossRef] [PubMed]
  24. Gao, Y.; Zhang, X.; Tian, H.; Zhang, J.; Yan, D.; Geng, Y.; Wang, F. High Mobility Ambipolar Diketopyrrolopyrrole-Based Conjugated Polymer Synthesized Via Direct Arylation Polycondensation. Adv. Mater. 2015, 27, 6753–6759. [Google Scholar] [CrossRef] [PubMed]
  25. Lu, W.; Kuwabara, J.; Kanbara, T. Polycondensation of Dibromofluorene Analogues with Tetrafluorobenzene via Direct Arylation. Macromolecules 2011, 44, 1252–1255. [Google Scholar] [CrossRef]
  26. Fujinami, Y.; Kuwabara, J.; Lu, W.; Hayashi, H.; Kanbara, T. Synthesis of Thiophene- and Bithiophene-Based Alternating Copolymers via Pd-Catalyzed Direct C–H Arylation. ACS Macro Lett. 2012, 1, 67–70. [Google Scholar] [CrossRef]
  27. Chang, S.-W.; Waters, H.; Kettle, J.; Kuo, Z.-R.; Li, C.-H.; Yu, C.-Y.; Horie, M. Pd-Catalysed Direct Arylation Polymerisation for Synthesis of Low-Bandgap Conjugated Polymers and Photovoltaic Performance. Macromol. Rapid Commun. 2012, 33, 1927–1932. [Google Scholar] [CrossRef] [PubMed]
  28. Kuwabara, J.; Nohara, Y.; Choi, S.J.; Fujinami, Y.; Lu, W.; Yoshimura, K.; Oguma, J.; Suenobu, K.; Kanbara, T. Direct arylation polycondensation for the synthesis of bithiophene-based alternating copolymers. Polym. Chem. 2013, 4, 947–953. [Google Scholar] [CrossRef] [Green Version]
  29. Jackson, N.E.; Savoie, B.M.; Kohlstedt, K.L.; de la Cruz, M.O.; Schatz, G.C.; Chen, L.X.; Ratner, M.A. Controlling Conformations of Conjugated Polymers and Small Molecules: The Role of Nonbonding Interactions. J. Am. Chem. Soc. 2013, 135, 10475–10483. [Google Scholar] [CrossRef] [PubMed]
  30. Phan, H.; Ford, M.J.; Lill, A.T.; Wang, M.; Bazan, G.C.; Nguyen, T.-Q. Double-Slope Nonideality in Organic Field-Effect Transistors. Adv. Funct. Mater. 2018, in press. [Google Scholar] [CrossRef]
  31. Grenier, F.; Berrouard, P.; Pouliot, J.-R.; Tseng, H.-R.; Heeger, A.J.; Leclerc, M. Synthesis of new n-type isoindigo copolymers. Polym. Chem. 2013, 4, 1836–1841. [Google Scholar] [CrossRef]
  32. Lee, W.-H.; Kong, H.; Oh, S.-Y.; Shim, H.-K.; Kang, I.-N. Field-effect transistors based on PPV derivatives as a semiconducting layer. J. Polym. Sci. Part A Polym. Chem. 2009, 47, 111–120. [Google Scholar] [CrossRef]
  33. Kim, R.; Amegadze, P.S.K.; Kang, I.; Yung, H.-J.; Noh, Y.-Y.; Kwon, S.-K.; Kim, Y.-H. High-Mobility Air-Stable Naphthalene Diimide-Based Copolymer Containing Extended π-Conjugation for n-Channel Organic Field Effect Transistors. Adv. Funct. Mater. 2013, 23, 5719–5727. [Google Scholar] [CrossRef]
  34. Ukai, T.; Kawazura, H.; Ishii, Y. Chemistry of dibenzylideneacetone-palladium(0) complexes: I. Novel tris(dibenzylideneacetone)dipalladium(solvent) complexes and their reactions with quinones. J. Organomet. Chem. 1974, 65, 253–266. [Google Scholar] [CrossRef]
Molecules 23 00981 sch001 550
Scheme 1. Synthesis of poly(1-alt-2) via DArP.
Scheme 1. Synthesis of poly(1-alt-2) via DArP.
Molecules 23 00981 sch001
Molecules 23 00981 sch002 550
Scheme 2. Synthesis of poly(1-alt-2) via Migita–Kosugi–Stille cross-coupling polymerization.
Scheme 2. Synthesis of poly(1-alt-2) via Migita–Kosugi–Stille cross-coupling polymerization.
Molecules 23 00981 sch002
Molecules 23 00981 g001 550
Figure 1. 1H-NMR spectra of poly(1-alt-2) prepared via DArP (Mn = 15,700 (a) and Mn = 22,700 (b)) and Migita–Kosugi–Stille cross-coupling polymerization (Mn = 17,700 (c) and Mn = 24,400 (d)) in C2D2Cl4 at 130 °C (600 MHz). *: unidentified signals.
Figure 1. 1H-NMR spectra of poly(1-alt-2) prepared via DArP (Mn = 15,700 (a) and Mn = 22,700 (b)) and Migita–Kosugi–Stille cross-coupling polymerization (Mn = 17,700 (c) and Mn = 24,400 (d)) in C2D2Cl4 at 130 °C (600 MHz). *: unidentified signals.
Molecules 23 00981 g001
Molecules 23 00981 g002 550
Figure 2. UV-vis spectra of poly(1-alt-2) in thin film. The entry number follows Table 2.
Figure 2. UV-vis spectra of poly(1-alt-2) in thin film. The entry number follows Table 2.
Molecules 23 00981 g002
Molecules 23 00981 g003 550
Figure 3. Charge transfer characteristics of the OFETs using poly(1-alt-2) of entries 1 (a) and 5 (b) in Table 3 (VD = −60 V).
Figure 3. Charge transfer characteristics of the OFETs using poly(1-alt-2) of entries 1 (a) and 5 (b) in Table 3 (VD = −60 V).
Molecules 23 00981 g003
Table
Table 1. DArP of 1-Br and 2-H.
Table 1. DArP of 1-Br and 2-H.
Run 1SolventTime (h)Yield (%) 2Mn3Mw/Mn3
1toluene59917,0002.6
2THF48807,4002.0
32-MeTHF24>9922,7003.9
3a--(63) 4(44,900) 4(2.2) 4
4 5toluene249315,7002.3
5 52-MeTHF96>9914,1002.5
1 Reactions were run at 100 °C using 1-Br (0.20 mmol) and 2-H (0.20 mmol), Pd2(dba)3·CHCl3 (0.5 mol%), L1 (2 mol%), Cs2CO3 (0.60 mmol), and pivalic acid (0.20 mmol) in toluene (0.40 mL) unless otherwise stated. 2 Isolated yield after Soxhlet extraction with hexane, acetone, and o-Cl2C6H4. 3 Determined by GPC calibration based on polystyrene standards (140 °C, o-Cl2C6H4). 4 After removal of a low molecular weight portion from the product in run 3 by Soxhlet extraction with CHCl3. 5 The reaction was carried out in the presence of TMEDA (10 mol%).
Table
Table 2. Electronic properties of poly(1-alt-2).
Table 2. Electronic properties of poly(1-alt-2).
EntryMethodMn (PDI) 1λmax 2λonset 2Eg(opt/CV) 3Eox4EHOMO5Ered4ELUMO5
1DArP15,700 (2.3)637, 6997471.66/1.730.53−5.33−1.20−3.60
2DArP17,000 (2.6)638, 7007461.66/1.740.54−5.34−1.20−3.60
3DArP22,700 (3.9)638, 7007471.66/1.750.54−5.34−1.21−3.59
4DArP44,900 (2.2)639, 7017531.65/1.740.54−5.34−1.20−3.60
5Stille17,700 (1.7)636, 6997481.66/1.760.54−5.34−1.22−3.58
6Stille53,800 (2.8)641, 7027471.66/1.730.56−5.36−1.17−3.63
1 Determined by GPC calibration based on polystyrene standards (entries 1–5: 140 °C, o-Cl2C6H4; entry 6: 150 °C, 1,2,4-Cl3C6H3). 2 Values in nm; observed by UV-vis spectroscopy in thin films spin-coated on quartz plates. 3 Values in eV, estimated from the absorption onset (Egopt = 1240/λonset) and cyclic voltammetry (EgCV). 4 Onset potentials in V (vs. Fc/Fc+) for oxidation (Eox) and reduction (Ered). 5 Values in eV, according to the following equation: EHOMO = −4.80 − Eox; ELUMO = −4.80 − Ered.
Table
Table 3. OFET characteristics and ordering parameters for poly(1-alt-2).
Table 3. OFET characteristics and ordering parameters for poly(1-alt-2).
Transistor PropertiesDistance (Å) 5
EntryMethodMn 1Mw 1μh (cm2 V−1 s−1) 2Vth (V) 3Ion/Ioff 4dl 6dπ 7
1DArP15,70035,8000.31
(0.21–0.37)		−16 to −5102–10821.13.76
2DArP17,00044,0000.020
(0.013–0.030)		−15 to −5102–10822.03.76
3DArP22,70088,2000.016
(0.012–0.022)		−21 to −2103–10620.73.74
4DArP44,90097,0000.0030
(0.0024–0.0033)		−29 to −4104–10722.03.74
5Stille17,70030,3000.28
(0.15–0.51)		−29 to −3102–10722.03.79
6Stille53,800 8151,000 80.004
(–) 9		−6>10522.03.72
1 Determined by GPC calibration based on polystyrene standards (140 °C, o-Cl2C6H4), unless otherwise stated. 2 Average mobilities for over 5 devices tested unless otherwise stated. 3 The threshold voltage. 4 The on/off current ratio. 5 Determined by GIWAXS analysis. 6 d-Spacing to the lamellar structure of the edge-on crystallite, (100) along the qz axis. 7 d-Spacing to the π–π stacking of the edge-on crystallites, (010) along the qxy axis. 8 Determined by GPC calibration and based on polystyrene standards (150 °C, 1,2,4-Cl3C6H3). 9 Only one device showed FET characteristics among the 12 devices fabricated.

Share and Cite

MDPI and ACS Style

Wakioka, M.; Yamashita, N.; Mori, H.; Nishihara, Y.; Ozawa, F. Synthesis of a 1,2-Dithienylethene-Containing Donor-Acceptor Polymer via Palladium-Catalyzed Direct Arylation Polymerization (DArP). Molecules 2018, 23, 981. https://doi.org/10.3390/molecules23040981

AMA Style

Wakioka M, Yamashita N, Mori H, Nishihara Y, Ozawa F. Synthesis of a 1,2-Dithienylethene-Containing Donor-Acceptor Polymer via Palladium-Catalyzed Direct Arylation Polymerization (DArP). Molecules. 2018; 23(4):981. https://doi.org/10.3390/molecules23040981

Chicago/Turabian Style

Wakioka, Masayuki, Natsumi Yamashita, Hiroki Mori, Yasushi Nishihara, and Fumiyuki Ozawa. 2018. "Synthesis of a 1,2-Dithienylethene-Containing Donor-Acceptor Polymer via Palladium-Catalyzed Direct Arylation Polymerization (DArP)" Molecules 23, no. 4: 981. https://doi.org/10.3390/molecules23040981