Construction of Thermo-Responsive Elastin-Like Polypeptides (ELPs)-Aggregation-Induced-Emission (AIE) Conjugates for Temperature Sensing

1
Faculty of Health Sciences, University of Macau, Taipa 999078, Macau, China
2
Department of Materials Science and Engineering, Southern University of Science and Technology, Shenzhen 518055, China
3
Department of Biotechnology and Bioengineering, Huaqiao University, Xiamen 361021, China
*
Authors to whom correspondence should be addressed.
Molecules 2018, 23(7), 1725; https://doi.org/10.3390/molecules23071725
Submission received: 10 June 2018 / Revised: 11 July 2018 / Accepted: 12 July 2018 / Published: 14 July 2018

Abstract

:
In this work, an aggregation-induced emission (AIE) molecule (tetraphenylethene derivative, TPE-COOH) was conjugated to elastin-like polypeptides (ELPs40) via an amide bond to form ELPs40-TPE. The successful synthesis of ELPs40-TPE was confirmed by Circular Dichroism spectroscopy, gel electrophoresis, UV-vis absorption, and fluorescence emission spectroscopy. ELPs40-TPE possessed both amphiphilicity and the features of an AIE, and the fluorescence intensity was dependent on the local temperature. The Hela cells imaging indicated that ELPs40-TPE has great potential for bio-imaging applications because of its advantages of high fluorescence intensity, good water-solubility, and remarkable biocompatibility.

Graphical Abstract

1. Introduction

Stimuli-responsive materials are becoming increasingly attractive in biomedical applications [1]. Such materials are characterized by a change in properties/behavior upon external stimuli [2], including light [3], temperature [4,5], electric field [6], and pH [7]. Among them, thermo-responsive materials have huge potential in biomedical applications due to their capability of phase transition above or below a certain temperature [8,9,10].
Elastin-like polypeptides (ELPs) are candidates with thermo-responsive characteristics for in vivo applications [11]. ELPs consist of Val-Pro-Gly-Xaa-Gly (VPGXG) pentapeptide repeats, where X represents the guest residue (any amino acid other than proline). ELPs undergo a reversible phase transition at their inverse transition temperature (Tt) [12]. Below the Tt, ELPs disperse well and exist as disordered structures in water; while above the Tt, ELPs form aggregates. The Tt of ELPs is highly tunable by altering molecular parameters, such as amino acid composition and molecular weight, and the Tt can be accurately adjusted between 0 °C and 100 °C, which can be applied to a wider area of temperature-sensitive applications [13]. Moreover, the biological composition of ELPs ensures its low cytotoxicity, good biocompatibility, and biodegradation [14]. Therefore, ELPs are extensively applied in vivo for their unique stability and drug activities [15,16], thus investigation of the thermal responsive property of ELPs is significant.
However, there are few studies that report the temperature response of ELPs through fluorescence methodology. The thermal transition of ELPs can be monitored by conjugating fluorescent molecules, where the fluorophores must have the characteristics of high sensitivity and fast response [17]. Conventionally used fluorogens usually suffer from the aggregation-caused quenching (ACQ) effect that is caused by π–π stacking interactions, which restricts their applications when they are used at a high concentration [18]. In 2001, Tang’s group [19] discovered an extraordinary photophysical phenomenon opposite to ACQ where luminogens become non-emissive in good solvents and intensively emit as solid aggregates in poor solvents. They termed the phenomenon aggregation-induced emission (AIE), and the fluorophores with the AIE property were termed as AIEgens. Thus the advantages of strong sensitivity, high selectivity, fast response, and low background noise make AIEgens mostly used as turn-on fluorescent probes for bio-sensors [20,21,22] and bio-imaging [23,24,25]. Inspired by the great fluorescence performance of AIEgens, we designed a new thermo-sensitive material by incorporating an AIE molecule into ELPs to explore its temperature-responsive behavior and cell imaging potential.
In this work, we used ELPs [KV8F-40] (abbreviated as ELPs40) which contained a sequence of 40 (VPGXG) pentapeptide repeats, the fourth amino acid residue of the repeats consisted of Lys, Val, and Phe in a 1:8:1 ratio. A typical AIE molecule 4-((4-(1,2,2-Triphenylvinyl) benzyl) oxy) benzoic acid (abbreviated as TPE-COOH) was used as the fluorescent marker. It was hypothesized that after the hydrophobic TPE-COOH was conjugated to hydrophilic ELPs40 via amidation, the resulting ELPs40-TPE conjugates could exhibit both water solubility and temperature sensitivity. It was the first example of an ELPs-based amphiphilic material with AIE properties. The transformation of the conformation of ELPs40-TPE occurred as the temperature changed, which led to a difference in its fluorescence. We anticipated that the novel material would show the capacities of temperature-responsive fluorescent variation and excellent biocompatibility and be used as a fluorescent probe for cell imaging.

2. Results and Discussion

2.1. Synthesis of ELP40-TPE

ELPs40-TPE was synthesized via an amidation reaction between the carboxyl-functionalized TPE derivative (TPE-COOH) and the amine-containing ELPs40 peptide as shown in Scheme 1, in which EDC and sulfo-NHS were used to activate the carboxyl group for efficient coupling. The synthetic processes of the representative AIE molecule TPE-COOH (2) was based on the reported literature [26] (all the compounds were characterized by 1H NMR, 13C NMR spectroscopies (Figures S1–S4). The activation reaction of the carboxyl group of (2) was carried out in DMSO, while the conjugation reaction of ELPs40 and (2) took place in a DMSO–water mixture. The resultant ELPs40-TPE was purified through dialysis and ultrafiltration. From the composition of the amino acid sequence of ELPs40 (Table 1), there was one amine at the N-terminus and four amines at the lysine residues, thus up to five TPE molecules could be connected to each ELPs40 chain. The TPE:ELPs40 average molar conjugation ratio was about 2.5, which was determined by the UV-vis absorbance spectra of ELPs40-TPE (according to the Equation (1), see the Materials and Methods for calculational details). Considering the steric hindrance, the resulting label ratio was reasonable.

2.2. Characterizations of ELPs40-TPE

The ELPs40-TPE was characterized by Circular Dichroism (CD) spectra (Figure S5), gel electrophoresis (Figure 1), UV-Vis absorption spectra (Figure 2a), and fluorescence emission spectra (Figure 2b). CD spectroscopy was usually used for the characterization of ELPs40 peptide by its unique secondary structure, where a positive peak in the region of 206 nm to 212 nm was characteristic of a type II β-turn [27,28]. As shown in Figure S5, in the CD spectra of ELPs40 and ELPs40-TPE, negative peaks at about 195 nm and 224 nm and positive peak at about 210 nm correspond to the random coil, helix, and type II β-turn secondary structure of ELPs40, respectively. The accurate composition of the secondary structure of ELPs40 and ELPs40-TPE were calculated through the Pro-Data Viewer program (Table 2). The type II β-turn ratio in the secondary structure of ELPs40-TPE was shown to decrease from 22.2% to 20.4% by conjugating the AIEgen to the ELPs40 peptide. These results indicated that the TPE-COOH molecule underwent interactions with ELPs40 and the synthesis of ELPs40-TPE was successful.
Successful conjugation of TPE-COOH to ELPs40 was further proved by 12.0% sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) as shown in Figure 1. The gel was directly visualized under UV lamp to observe the fluorescence of TPE-containing band in the lane of ELPs40-TPE (Figure 1a), which was ascribed to the aggregation of the AIE groups in ELPs40-TPE. After further staining of the same gel with CuCl2 for 2h (Figure 1b), the ELPs40-TPE lane displayed the same band due to ELPs40. Besides, the ELPs40 lane showed a clear band at the same location (between 15 kDa and 25 kDa, where the molecular weight of ELPs40 was about 17 kDa). Under the UV light, the smearing of the ELPs40-TPE band in the gel indicated that ELPs40 was decorated with TPE but with a diverse label degree, which resulted in different electrophoretic migration rate and the appearance of smearing.
Then, the optical properties of ELPs40-TPE and ELPs40 were studied by measuring their absorption and emission spectra at the same concentration. From Figure 2a, both ELPs40 and ELPs40-TPE showed the absorption maxima at about 270 nm, attributed to the peptide structure, while ELPs40-TPE exhibited another absorption peak at about 320 nm due to the TPE moiety. As we expected, the ELPs40 peptide endowed ELPs40-TPE with good water solubility. However, ELPs40-TPE emitted a strong fluorescence in water (Figure 2b). This interesting phenomenon different from the conventional AIE effect, where AIEgens usually exhibited non-emissive in good solvents. The conjugation of AIEgens with ELPs40 enhanced the hydrophobicity of ELPs40, thus the amphiphilicity of ELPs40-TPE conjugates made the TPE moiety aggregate and emit intense fluorescence, which was similar to the hydrophobic small molecule conjugated ELPs-dox system [29,30].

2.3. AIE Property of ELPs40-TPE

In order to elucidate the phenomenon of strong fluorescence of ELPs40-TPE in water, the AIE effect of ELPs40-TPE was investigated by fluorescent spectra in DMF/water system with different water fractions. From Figure 3, ELPs40-TPE showed a weak fluorescence, because it was completely dispersed in pure DMF and low water fractions (fW < 50%). However, when the fraction of water increased to 90%, ELPs40-TPE suddenly emitted remarkable fluorescence. It is well known that the mechanism of AIE is based on mainly Restriction of Intramolecular Motions (RIM), which includes Restriction of Intramolecular Rotations (RIR) and Restriction of Intramolecular Vibrations (RIV) [20]. In the aggregated state, the restriction of such motions resulted in the blocking of the non-radiative pathway, which made the AIEgens emit strong fluorescence [32]. Thus, the aggregation was regarded as a necessary requirement [33], while Kazuki and coworkers recently pointed out that aggregation was a sufficient condition for AIE rather than a necessary requirement [34]. ELPs40-TPE existed as a random coil conformation in aqueous solution and the hydrogen bonds formed between acid amides groups and water molecules increased the rigidity of the environment. Besides, the hydrophobic effect effectively promoted the aggregation of the hydrophobic AIE-featured TPE group of the ELPs40-TPE chain. Therefore, both the rigidity-enhanced environment and hydrophobic effect restricted the intermolecular motions and inhibited non-radiative pathway, leading to strong emission. In contrast, ELPs40-TPE was non-emissive in pure DMF, owing to the free intramolecular motions of phenyl rings in TPE segments and the flexibility of ELPs40 peptide chain.

2.4. Temperature Responsivity of ELPs40-TPE

We then explored the temperature responsiveness of ELPs40-TPE in water. As temperature increased from 25 °C to 50 °C in steps of 5 °C, the fluorescent intensity of ELPs40-TPE decreased gradually (Figure 4). In the range of 25 °C to 50 °C, the plot of fluorescence intensity at 460 nm of ELPs40-TPE as a function of temperature was in a good linear regression with a correlation coefficient of 0.9953. The Tt of ELPs was related to its sequence, chain length, polypeptide concentration, and the type and concentration of solution [12]. According to the reported literature [35], the Tt of ELPs40 was more than 53 °C in water, which was consistent with the phenomena during the process of heating (the solution of the ELPs40-TPE was always transparent). The mechanism of temperature-responsive behavior of ELPs40-TPE in aqueous solution was shown in Scheme 2. The hydrophobic effect made the TPE groups of ELPs40-TPE aggregate and emit a strong fluorescence at 25 °C. Raising the temperature resulted in two different effects on ELPs40-TPE. As the temperature rose, the ELPs40 peptide of ELPs40-TPE gradually accumulated, which synchronously accelerated the intramolecular rotation of TPE moieties and the motion of whole conjugates. The former effect enhanced the emission of the TPE groups, and the latter effect weakened the emission. ELPs40-TPE had already aggregated in aqueous solution at 25 °C, thus the latter effect played the dominant role during the heating, and the fluorescence intensity gradually decreased.
The reversibility of the temperature responsiveness of ELPs40-TPE was then investigated by heating the aqueous solution of ELPs40-TPE to 50 °C and then cooling it to 25 °C. As shown in Figure 5, the fluorescence intensity of ELPs40-TPE gradually increased as the temperature returned to 25 °C. During the reduction of temperature, there were also two effects to the ELPs40-TPE. The ELPs40 peptide chain gradually disaggregated, which made the TPE fluorogen emit weaker fluorescence, while the intramolecular rotations of TPE moiety was hindered with the reduction in temperature, which caused stronger fluorescence. Ultimately, the latter effect acted as the major role during the cooling process. The results of the heating–cooling cycle (25 °C–50 °C) of ELPs40-TPE indicated its reversibility.

2.5. DLS Study

DLS was used to monitor the temperature response of ELPs40-TPE in aqueous solution. As shown in Figure 6, the results displayed that the ELPs40-TPE conjugates indeed aggregated at 25 °C, and the size of ELPs40-TPE increased from 65 nm to 135 nm in the temperature range of 25 °C to 50 °C. The DLS outcomes of ELPs40-TPE further demonstrated the mechanism of temperature-responsive behavior we proposed in 2.4. Temperature Responsivity of ELPs40-TPE.

2.6. Cell Imaging Applications

Based on the amino acid components of the ELPs40 peptide chain, it was deduced that ELPs40-TPE might display good biocompatibility. MTT cell viability assays were conducted to evaluate the cytotoxicity of ELPs40-TPE. Hela cells were incubated with different concentrations of ELPs40-TPE at 37 °C for 24 h, while TPE-COOH was used as the control (Figure 7). As shown in Figure 7, ELPs40-TPE exhibited lower cytotoxicity and better biocompatibility than TPE-COOH in the range of 5–15 µM. However, they showed comparable biocompatibility across all concentrations.
The AIE property and the results of cell viability suggested that ELPs40-TPE might be utilized as a fluorescent bioprobe for cell imaging (Figure 8). The uptake of small particles (less than 200 nm) by cells was generally through the endocytosis pathway [36]. As shown in Figure 8, the cytoplasm of Hela cells emitted a strong blue fluorescence, demonstrating that the ELPs40-TPE probe entered into the cytoplasm in the aggregated form. In contrast, Hela cells stained by TPE-COOH only exhibited a weak fluorescence, probably due to the low uptake efficiency of TPE-COOH. The hydrophobic TPE-COOH was prone to aggregation in cell culture medium and could be subsequently cleared by phosphate buffer. Thus, the amphiphilic ELPs40-TPE fluorescent probe with AIE characteristics showed promising biocompatibility for bio-imaging.

3. Materials and Methods

3.1. Materials

1-[(4-bromomethyl)-phenyl]-1,2,2-triphenylethene and 4-methyl hydroxybenzoate were purchased from Rhea Biotech Company (Xian, China). Potassium carbonate, anhydrous MgSO4, sodium hydroxide, tetrabutylammonium bromide (TBAB), 1-ethyl-3-(-3-dimethylaminopropyl) carbodiimide hydrochloride (EDC), and N-hydroxysulfosuccinimide sodium salt (sulfo-NHS) were purchased from Sigma-Aldrich. Dialysis bag (3 KDa) was purchased from Sangon Biotech Company (Shanghai, China), Ultra-4 Centrifugal Filter Devices (3 KDa) was purchased from Merck Millipore (Darmstadt, Germany). All the solvents of analytical grade were employed without more purification. ELPs40 was kindly provided by Guangya Zhang’s Group (Huaqiao university).

3.2. Synthesis of Methyl 4-((4-(1,2,2-triphenylvinyl) benzyl) oxy) Benzoate (1)

1-[(4-bromomethyl)-phenyl]-1,2,2-triphenylethene (0.427 g, 1 mmol), 4-methyl hydroxybenzoate (0.42 g, 2 mmol), and potassium carbonate (0.553 g, 4 mmol) were mixed in of DMF (20 mL), the mixture was heated to 80 °C overnight. After the reaction was completed, the mixture was poured into ice water and filtered, and the solid product was then dissolved in CH2Cl2 and washed with 1 M NaOH (50 mL × 3) and dried over anhydrous MgSO4. After the evaporation of solvent, the crude product was purified by a silica gel column using CH2Cl2/hexane (v/v 1:1) as eluent to give compound (1) as a white solid (0.195 g, 40% yield). 1H NMR (400MHz, CDCl3), δ (TMS, ppm): 8.01 (d, 2H, ArH), 7.19 (s,1H, ArH), 7.18 (s, 1H, ArH), 7.11–7.14 (m, 9H, ArH), 7.09 (s, 1H, ArH), 7.03–7.07 (m, 7H, ArH), 6.98 (d, 2H, ArH), 5.04 (s, 2H, -ArCH2-), 3.92 (s, 3H, -COOCH3). 13C NMR (100 MHz, CDCl3) δ: 166.9, 162.5, 143.6, 141.4, 140.4, 134.2, 131.6, 131.3, 127.7, 127.7, 126.8, 126.5, 122.8, 114.5, 70.0, 51.9.

3.3. Synthesis of 4-((4-(1,2,2-triphenylvinyl) benzyl) oxy) Benzoic acid (2)

The THF solution of compound (1) (100 mg/10 mL) was added to 10 mL 30% NaOH solution, then 30 mg tetrabutylammonium bromide (TBAB) was mixed to the mixture and stirred at 70 °C overnight and cooled to room temperature. The reaction mixture was then neutralized with 1 M HCl until the white precipitate appeared (pH was about 7) followed by the addition of ethyl acetate for extraction. The white solids were obtained after the evaporation of solvent (70 mg, 70% yield). 1H NMR (400 MHz, DMSO-d6), δ (TMS, ppm): 7.88 (d, 2H, ArH), 7.21 (d, 2H, ArH), 7.12–7.17 (d, 9H, ArH), 7.06 (d, 2H, ArH), 6.95–7.02 (m, 8H, ArH), 5.07 (s, 2H, -ArCH2-). 13C NMR (100 MHz, DMSO-d6) δ: 167.6, 162.3, 143.6, 143.4, 141.3, 140.7, 135.1, 131.8, 131.2, 131.1, 128.3, 127.9, 127.1, 115.0, 69.8.

3.4. Synthesis and Purification of ELPs40-TPE (3)

0.4 mg 1-ethyl-3-(-3-dimethylaminopropyl) carbodiimide hydrochloride (EDC) and 0.6 mg N-hydroxysulfosuccinimide sodium salt (sulfo-NHS) were added to a solution of (2) in DMSO (1 mL, 2 mg/mL). The solution was shaken slightly for 1 h on a 37 °C constant thermo-shaker. Then 1 mL ELPs40 solution (1 µmol) was added to the reaction mixture and continued shaking for 2 h.
The ELPs40-TPE reaction solution was transferred to a 3 K dialysis bag for dialysis for 48 h. After dialysis, the crude products in the dialysis bag were ultrafiltered via 3 K ultra-4 centrifugal filter devices, and 400 µL ELPs40-TPE concentrate was collected. The TPE concentration was quantified by the calibration curve drawn from the UV absorption of TPE-COOH at 320 nm. The ELPs40 concentration was calculated using the derived Equation (1) [31]:
[ ELPs 40 ]   =   ( Abs 280   nm     ( 1.063   ×   Abs 320   nm ) ) ε   ×   1   cm  
where ε was the molar extinction coefficient of the protein (ε = 7190 L/mol cm). The ELPs40-TPE concentrates was stored in −20 °C refrigerator for subsequent analysis.

3.5. Characterizations

3.5.1. Circular Dichroism (CD) Spectroscopy Measurements

Circular Dichroism (CD) spectra were studied on a Chirascan-plus Circular Dichroism Spectrometer (Applied Photophysics Ltd., Leatherhead, Surrey, UK). Measurements were conducted in a quartz cell with a 2 mm path length over the range of 190–300 nm in the nitrogen atmosphere. The concentrations of ELPs40-TPE and ELPs40 were 10 µM in aqueous solution.

3.5.2. Gel Electrophoresis Analysis

Gel electrophoresis was performed using 12.0% SDS-PAGE at 120 V for 1 h. The gel images were captured on gel image system (Bio-Rad, Hercules, CA, USA).

3.5.3. UV-Vis Absorbance Spectroscopy and Fluorescence Emission Spectroscopy Measurements

UV-vis absorbance spectra were measured via a UV-1800 spectrophotometer (SHIMADZU, Japan) and a quartz cell with 1 cm optical pathway. Fluorescence emission spectra were measured with a Fluoromax-4 spectrofluorometer (HORIBA, Edison, NJ, USA) and a quartz fluorescence cuvette (2 mm × 10 mm), and with the following settings: λex = 320 nm, λem = 460 nm.

3.5.4. DLS Measurements

Dynamic light scattering (DLS) measurements were performed on Brookhaven NanoBrook Omni instrument (Brookhaven Instruments Corporation, New York, NY, USA). The concentration of ELPs40-TPE was 5 µM in aqueous solution.

3.5.5. Cell Culture

HeLa cells were provided by the Faculty of Health Sciences, University of Macau, which were cultured in RPMI-1640 medium containing 10% Fetal Bovine Serum (FBS) and 1% penicillin–streptomycin in a humidity incubator (5% CO2, 37 °C).

3.5.6. Cell Imaging

The cytotoxicity assay was performed before cell imaging by using a methyl thiazolyl tetrazolium (MTT) Cell Proliferation and Cytotoxicity Assay Kit (Beyotime, Shanghai, China) against HeLa cells. The absorbance of MTT at 570 nm was recorded by the Tecan plate reader (Tecan, Männedorf, Switzerland). Cell viability was estimated by the ratio of the absorbance of the cells incubated with ELPs40-TPE to that of the cells incubated with RPMI-1640 medium only. HeLa cells were precultured on 35 mm glass bottom cell culture dishes in incubator. After 80% confluence, the cells were washed three times with 1 × PBS buffer. Then the cells were incubated with ELPs40-TPE and TPE-COOH for 30 min at 37 °C, respectively (the concentration of TPE was identical, 10 µM). After the incubation, the cells were washed three times with 1 × PBS buffer. Fixative solution (Histochoice® Mb Tissue Fixative, Amresco, Solon, OH, USA) was added at room temperature for 15 min, then the cells were washed with 1 × PBS buffer and used for cell imaging.

4. Conclusions

We have synthesized a novel amphiphilic ELPs40-TPE material by using hydrophilic ELPs40 peptide and hydrophobic TPE-COOH molecule via amidation. The obtained ELPs40-TPE conjugates with AIE attributes were different from the conventional AIE fluorogens, which exhibited strong fluorescence in aqueous solution and good water solubility. Moreover, the ELPs40-TPE conjugates were temperature-responsive and their fluorescence could be tuned by changing temperature. HeLa cells imaging demonstrated that not only does ELPs40-TPE have great luminescent properties, but also low cytotoxicity and excellent biocompatibility. Thus, we believe that the new material described here could attract much attention because of the above advantages, especially in bio-imaging applications.

Supplementary Materials

The following are available online. Figure S1: 1H NMR spectrum of (1) in CDCl3, Figure S2: 13C NMR spectrum of (1) in CDCl3, Figure S3: 1H NMR spectrum of (2) in DMSO-d6, Figure S4: 13C NMR spectrum of (2) in DMSO-d6, Figure S5: CD spectra of ELPs40 and ELPs40-TPE.

Author Contributions

Z.C., Z.D., and X.Z. conceived and designed the experiments; Z.C. performed the experiments and analyzed the data; G.Z. contributed samples and materials; Z.C. wrote the paper. Z.D., L.T. and X.Z. revised the manuscript and supervised the project.

Funding

This work was supported by the Research Grant of University of Macau (Nos. MYRG2017-00066-FHS, MYRG2016-00058-FHS); the Macao Science and Technology Development Fund (Nos. 082/2016/A2, 052/2015/A2).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Roy, D.; Cambre, J.N.; Sumerlin, B.S. Future perspectives and recent advances in stimuli-responsive materials. Prog. Polym. Sci. 2010, 35, 278–301. [Google Scholar] [CrossRef]
  2. Wei, M.; Gao, Y.; Li, X.; Serpe, M.J. Stimuli-responsive polymers and their applications. Polym. Chem. 2017, 8, 127–143. [Google Scholar] [CrossRef] [Green Version]
  3. Duval, A.; Lange, H.; Lawoko, M.; Crestini, C. Modification of Kraft lignin to expose diazobenzene groups: Toward pH- and light-responsive biobased polymers. Biomacromolecules 2015, 16, 2979–2989. [Google Scholar] [CrossRef] [PubMed]
  4. Kohsaka, Y.; Tanimoto, Y. Synthesis of thermo-responsive polymer via radical (co)polymerization of N,N-dimethyl-α-(hydroxymethyl)acrylamide with N,N-diethylacrylamide. Polymers 2016, 8, 374. [Google Scholar] [CrossRef]
  5. Ding, Z.Y.; Wang, C.F.; Feng, G.; Zhang, X.J. Thermo-responsive fluorescent polymers with diverse LCSTs for ratiometric temperature sensing through FRET. Polymers 2018, 10, 283. [Google Scholar] [CrossRef]
  6. Ge, J.; Neofytou, E.; Cahill, T.J.; Beygui, R.E.; Zare, R.N. Drug release from electric-field-responsive nanoparticles. ACS Nano 2012, 6, 227–233. [Google Scholar] [CrossRef] [PubMed]
  7. Kocak, G.; Tuncer, C.; Bütün, V. pH-responsive polymers. Polym. Chem. 2017, 8, 144–176. [Google Scholar] [CrossRef]
  8. Teotia, A.K.; Sami, H.; Kumar, A. Thermo-responsive polymers. In Switchable and Responsive Surfaces and Materials for Biomedical Applications; Elsevier: New York, NY, USA, 2015; pp. 3–43. [Google Scholar]
  9. Ding, Z.Y.; Cao, X.J. Affinity precipitation of human serum albumin using a thermo-response polymer with an L-thyroxin ligand. BMC Biotechnol. 2013, 13, 109. [Google Scholar] [CrossRef] [PubMed]
  10. Ding, Z.Y.; Zheng, X.X.; Li, S.P.; Cao, X.J. Immobilization of cellulase onto a recyclable thermo-responsive polymer as bioconjugate. J. Mol. Catal. B-Enzym. 2016, 128, 39–45. [Google Scholar] [CrossRef]
  11. Fujita, Y.; Mie, M.; Kobatake, E. Construction of nanoscale protein particle using temperature-sensitive elastin-like peptide and polyaspartic acid chain. Biomaterials 2009, 30, 3450–3457. [Google Scholar] [CrossRef] [PubMed]
  12. Shang, Y.Z.; Yan, Y.F.; Hou, X. Stimuli responsive elastin-like polypeptides and applications in medicine and biotechnology. J. Biomater. Sci.-Polym. Ed. 2014, 25, 101–120. [Google Scholar] [CrossRef] [PubMed]
  13. Meyer, D.E.; Chilkoti, A. Genetically encoded synthesis of protein-based polymers with precisely specified molecular weight and sequence by recursive directional ligation: Examples from the elastin-like polypeptide system. Biomacromolecules 2002, 3, 357–367. [Google Scholar] [CrossRef] [PubMed]
  14. MacEwan, S.R.; Chilkoti, A. Applications of elastin-like polypeptides in drug delivery. J. Control. Release 2014, 190, 314–330. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  15. Betre, H.; Liu, W.; Zalutsky, M.R.; Chilkoti, A.; Kraus, V.B.; Setton, L.A. A thermally responsive biopolymer for intra-articular drug delivery. J. Control. Release 2006, 115, 175–182. [Google Scholar] [CrossRef] [PubMed]
  16. Herrero-Vanrell, R.; Rincon, A.C.; Alonso, M.; Reboto, V.; Molina-Martinez, I.T.; Rodriguez-Cabello, J.C. Self-assembled particles of an elastin-like polymer as vehicles for controlled drug release. J. Control. Release 2005, 102, 113–122. [Google Scholar] [CrossRef] [PubMed]
  17. Swift, T.; Swanson, L.; Rimmer, S. Poly(acrylic acid) interpolymer complexation: Use of a fluorescence time resolved anisotropy as a poly(acrylamide) probe. RSC Adv. 2014, 4, 57991–57995. [Google Scholar] [CrossRef]
  18. Ding, D.; Li, K.; Liu, B.; Tang, B.Z. Bioprobes based on AIE fluorogens. Acc. Chem. Res. 2013, 46, 2441–2453. [Google Scholar] [CrossRef] [PubMed]
  19. Luo, J.D.; Xie, Z.L.; Lam, J.W.Y.; Cheng, L.; Chen, H.Y.; Qiu, C.F.; Kwok, H.S.; Zhan, X.W.; Liu, Y.Q.; Zhu, D.B.; et al. Aggregation-induced emission of 1-methyl-1,2,3,4,5-pentaphenylsilole. Chem. Commun. 2001, 18, 1740–1741. [Google Scholar] [CrossRef]
  20. Mei, J.; Leung, N.L.C.; Kwok, R.T.K.; Lam, J.W.Y.; Tang, B.Z. Aggregation-induced emission: Together we shine, united we soar! Chem. Rev. 2015, 115, 11718–11940. [Google Scholar] [CrossRef] [PubMed]
  21. Zhang, R.Y.; Kwok, R.T.K.; Tang, B.Z.; Liu, B. Hybridization induced fluorescence turn-on of aiegen-oligonucleotide conjugates for specific DNA detection. RSC Adv. 2015, 5, 28332–28337. [Google Scholar] [CrossRef]
  22. Zhuang, Y.; Huang, F.J.; Xu, Q.; Zhang, M.S.; Lou, X.D.; Xia, F. Facile, fast-responsive, and photostable imaging of telomerase activity in living cells with a fluorescence turn-on manner. Anal. Chem. 2016, 88, 10335. [Google Scholar] [CrossRef] [PubMed]
  23. Li, Y.H.; Wu, Y.Q.; Chang, J.; Chen, M.; Liu, R.; Li, F.Y. A bioprobe based on aggregation induced emission (AIE) for cell membrane tracking. Chem. Commun. 2013, 49, 11335–11337. [Google Scholar] [CrossRef] [PubMed]
  24. Leung, C.W.T.; Hong, Y.N.; Chen, S.J.; Zhao, E.G.; Lam, J.W.Y.; Tang, B.Z. A photostable AIE luminogen for specific mitochondrial imaging and tracking. J. Am. Chem. Soc. 2013, 135, 62–65. [Google Scholar] [CrossRef] [PubMed]
  25. Ding, D.; Mao, D.; Li, K.; Wang, X.M.; Qin, W.; Liu, R.R.; Chiam, D.S.; Tomczak, N.; Yang, Z.M.; Tang, B.Z.; et al. Precise and long-term tracking of adipose-derived stem cells and their regenerative capacity via superb bright and stable organic nanodots. ACS Nano 2014, 8, 12620–12631. [Google Scholar] [CrossRef] [PubMed]
  26. Gao, Y.; Han, B.; Chen, Y.T.; Wang, X.; Bai, M. Phenylcarboxyl-decorated tetraphenylethene with diverse molecular rim-induced emission from host-guest inclusion and aggregation formation. RSC Adv. 2016, 6, 16581–16585. [Google Scholar] [CrossRef]
  27. Reiersen, H.; Clarke, A.R.; Rees, A.R. Short elastin-like peptides exhibit the same temperature-induced structural transitions as elastin polymers: Implications for protein engineering. J. Mol. Biol. 1998, 283, 255–264. [Google Scholar] [CrossRef] [PubMed]
  28. Gross, P.C.; Possart, W.; Zeppezauer, M. An alternative structure model for the polypentapeptide in elastin. Z. Naturforsch. C 2003, 58, 873–878. [Google Scholar] [CrossRef] [PubMed]
  29. Dreher, M.R.; Raucher, D.; Balu, N.; Michael Colvin, O.; Ludeman, S.M.; Chilkoti, A. Evaluation of an elastin-like polypeptide-doxorubicin conjugate for cancer therapy. J. Control. Release 2003, 91, 31–43. [Google Scholar] [CrossRef]
  30. McDaniel, J.R.; Bhattacharyya, J.; Vargo, K.B.; Hassouneh, W.; Hammer, D.A.; Chilkoti, A. Self-assembly of thermally responsive nanoparticles of a genetically encoded peptide polymer by drug conjugation. Angew. Chem. Int. Ed. Engl. 2013, 52, 1683–1687. [Google Scholar] [CrossRef] [PubMed]
  31. Moktan, S.; Perkins, E.; Kratz, F.; Raucher, D. Thermal targeting of an acid-sensitive doxorubicin conjugate of elastin-like polypeptide enhances the therapeutic efficacy compared with the parent compound in vivo. Mol. Cancer Ther. 2012, 11, 1547–1556. [Google Scholar] [CrossRef] [PubMed]
  32. Mei, J.; Hong, Y.N.; Lam, J.W.Y.; Qin, A.J.; Tang, Y.H.; Tang, B.Z. Aggregation-induced emission: The whole is more brilliant than the parts. Adv. Mater. 2014, 26, 5429–5479. [Google Scholar] [CrossRef] [PubMed]
  33. Shi, J.; Chang, N.; Li, C.; Mei, J.; Deng, C.; Luo, X.; Liu, Z.; Bo, Z.; Dong, Y.Q.; Tang, B.Z. Locking the phenyl rings of tetraphenylethene step by step: Understanding the mechanism of aggregation-induced emission. Chem. Commun. (Camb.) 2012, 48, 10675–10677. [Google Scholar] [CrossRef] [PubMed]
  34. Machida, T.; Taniguchi, R.; Oura, T.; Sada, K.; Kokado, K. Liquefaction-induced emission enhancement of tetraphenylethene derivatives. Chem. Commun. (Camb.) 2017, 53, 2378–2381. [Google Scholar] [CrossRef] [PubMed]
  35. Van Eldijk, M.B.; Smits, F.C.M.; Vermue, N.; Debets, M.F.; Schoffelen, S.; van Hest, J.C.M. Synthesis and self-assembly of well-defined elastin-like polypeptide-poly(ethylene glycol) conjugates. Biomacromolecules 2014, 15, 2751–2759. [Google Scholar] [CrossRef] [PubMed]
  36. Vivero-Escoto, J.L.; Slowing, I.I.; Trewyn, B.G.; Lin, V.S.Y. Mesoporous silica nanoparticles for intracellular controlled drug delivery. Small 2010, 6, 1952–1967. [Google Scholar] [CrossRef] [PubMed]
Sample Availability: Samples of the ELPs40-TPE conjugates are available from the authors.
Scheme 1. Synthetic route of ELPs40-TPE.
Scheme 1. Synthetic route of ELPs40-TPE.
Molecules 23 01725 sch001
Figure 1. 12.0% SDS-PAGE analysis of ELPs40 and ELPs40-TPE. The gel was visualized under UV lamp first (a), and then stained with 0.5 M CuCl2 (b).
Figure 1. 12.0% SDS-PAGE analysis of ELPs40 and ELPs40-TPE. The gel was visualized under UV lamp first (a), and then stained with 0.5 M CuCl2 (b).
Molecules 23 01725 g001
Figure 2. (a) UV-Vis absorption spectra of ELPs40 (blue) and ELPs40-TPE (red) in aqueous solution. (b) Fluorescence emission spectra of ELPs40 (blue) and ELPs40-TPE (red) in aqueous solution. The concentrations of ELPs40 and ELPs40-TPE were 5 µM (ELPs40 concentration was determined using the protein absorbance at 280 nm and the protein’s molar extinction coefficient (7190 L/mol cm) [31]), λex = 320 nm.
Figure 2. (a) UV-Vis absorption spectra of ELPs40 (blue) and ELPs40-TPE (red) in aqueous solution. (b) Fluorescence emission spectra of ELPs40 (blue) and ELPs40-TPE (red) in aqueous solution. The concentrations of ELPs40 and ELPs40-TPE were 5 µM (ELPs40 concentration was determined using the protein absorbance at 280 nm and the protein’s molar extinction coefficient (7190 L/mol cm) [31]), λex = 320 nm.
Molecules 23 01725 g002
Figure 3. (a) Fluorescent spectra of ELPs40-TPE in the DMF–water system with different water fractions. (The concentrations ELPs40-TPE was 5 µM, λex = 320 nm); (b) The maximum fluorescence intensity of ELPs40-TPE in the DMF–water system at 460 nm. (F0 is the fluorescence intensity of blank background, the concentrations of ELPs40 and ELPs40-TPE were 1 µM, λex = 320 nm); (c) Photographs of ELPs40-TPE under UV light (365 nm) in different water fractions.
Figure 3. (a) Fluorescent spectra of ELPs40-TPE in the DMF–water system with different water fractions. (The concentrations ELPs40-TPE was 5 µM, λex = 320 nm); (b) The maximum fluorescence intensity of ELPs40-TPE in the DMF–water system at 460 nm. (F0 is the fluorescence intensity of blank background, the concentrations of ELPs40 and ELPs40-TPE were 1 µM, λex = 320 nm); (c) Photographs of ELPs40-TPE under UV light (365 nm) in different water fractions.
Molecules 23 01725 g003
Figure 4. (a) The fluorescent spectra of ELPs40-TPE in water at different temperatures. (b) Linear relationships between the fluorescence intensity of ELPs40-TPE at 460 nm and temperature from 25 °C to 50 °C. The concentration of ELPs40-TPE was 10 µM, λex = 320 nm.
Figure 4. (a) The fluorescent spectra of ELPs40-TPE in water at different temperatures. (b) Linear relationships between the fluorescence intensity of ELPs40-TPE at 460 nm and temperature from 25 °C to 50 °C. The concentration of ELPs40-TPE was 10 µM, λex = 320 nm.
Molecules 23 01725 g004
Scheme 2. Mechanism for temperature-responsive behavior of ELPs40-TPE in aqueous solution.
Scheme 2. Mechanism for temperature-responsive behavior of ELPs40-TPE in aqueous solution.
Molecules 23 01725 sch002
Figure 5. The reversibility of ELPs40-TPE. The concentration of ELPs40-TPE was 5 µM, λex = 320 nm.
Figure 5. The reversibility of ELPs40-TPE. The concentration of ELPs40-TPE was 5 µM, λex = 320 nm.
Molecules 23 01725 g005
Figure 6. Particle size distributions of ELPs40-TPE in aqueous solution under different temperatures.
Figure 6. Particle size distributions of ELPs40-TPE in aqueous solution under different temperatures.
Molecules 23 01725 g006
Figure 7. Cell viability (%) of Hela cells treated with different concentrations of ELPs40-TPE and TPE-COOH for 24 h by MTT assay. Data as mean values ± SD (n = 3). The Student’s t-test was used to compare the results of the experiments. A * p-value < 0.05 was considered significant.
Figure 7. Cell viability (%) of Hela cells treated with different concentrations of ELPs40-TPE and TPE-COOH for 24 h by MTT assay. Data as mean values ± SD (n = 3). The Student’s t-test was used to compare the results of the experiments. A * p-value < 0.05 was considered significant.
Molecules 23 01725 g007
Figure 8. Fluorescent images of HeLa cells stained with (a) TPE-COOH for 30 min and (b) ELPs40-TPE conjugates for 30 min. λex = 365 nm. (The concentration of TPE was identical, 10 µM).
Figure 8. Fluorescent images of HeLa cells stained with (a) TPE-COOH for 30 min and (b) ELPs40-TPE conjugates for 30 min. λex = 365 nm. (The concentration of TPE was identical, 10 µM).
Molecules 23 01725 g008
Table 1. Protein sequence of ELPs40.
Table 1. Protein sequence of ELPs40.
Amino Acid Sequence *
ELPs40VPGKGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGFGVPGVG
VPGKGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGFGVPGVG
VPGKGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGFGVPGVG
VPGKGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGVGVPGFGVPGWP
* The underlined amino acids indicate the position of the amines at the N-terminus and the lysine residues. There was a tryptophan codon added to the end of ELPs40 gene to synthesize ELPs40, thus each ELPs40 contained one tryptophan (W).
Table 2. The composition of the secondary structure of ELPs40 and ELPs40-TPE.
Table 2. The composition of the secondary structure of ELPs40 and ELPs40-TPE.
The Type of StructureELPs40ELPs40-TPE
Helix18.7%21.2%
Antiparallel42.7%29.6%
Parallel8.4%9.0%
Beta-turn22.2%20.4%
Random coil17.7%23.2%

Share and Cite

MDPI and ACS Style

Chen, Z.; Ding, Z.; Zhang, G.; Tian, L.; Zhang, X. Construction of Thermo-Responsive Elastin-Like Polypeptides (ELPs)-Aggregation-Induced-Emission (AIE) Conjugates for Temperature Sensing. Molecules 2018, 23, 1725. https://doi.org/10.3390/molecules23071725

AMA Style

Chen Z, Ding Z, Zhang G, Tian L, Zhang X. Construction of Thermo-Responsive Elastin-Like Polypeptides (ELPs)-Aggregation-Induced-Emission (AIE) Conjugates for Temperature Sensing. Molecules. 2018; 23(7):1725. https://doi.org/10.3390/molecules23071725

Chicago/Turabian Style

Chen, Zhe, Zhaoyang Ding, Guangya Zhang, Leilei Tian, and Xuanjun Zhang. 2018. "Construction of Thermo-Responsive Elastin-Like Polypeptides (ELPs)-Aggregation-Induced-Emission (AIE) Conjugates for Temperature Sensing" Molecules 23, no. 7: 1725. https://doi.org/10.3390/molecules23071725

Article Metrics

Back to TopTop