Effects of Textural Properties on the Response of a SnO2-Based Gas Sensor for the Detection of Chemical Warfare Agents

1
Department of Chemical Engineering, Kyungpook National University, Daegu 702-701, Korea
2
School of Electrical Engineering and Computer Science, Kyungpook National University, Daegu 702-701, Korea
3
Department of Applied Chemistry, Kyungpook National University, Daegu 702-701, Korea
*
Author to whom correspondence should be addressed.
These authors contributed equally to this work.
Sensors 2011, 11(7), 6893-6904; https://doi.org/10.3390/s110706893
Submission received: 2 June 2011 / Revised: 29 June 2011 / Accepted: 30 June 2011 / Published: 1 July 2011
(This article belongs to the Section Chemical Sensors)

Abstract

: The sensing behavior of SnO2-based thick film gas sensors in a flow system in the presence of a very low concentration (ppb level) of chemical agent simulants such as acetonitrile, dipropylene glycol methyl ether (DPGME), dimethyl methylphosphonate (DMMP), and dichloromethane (DCM) was investigated. Commercial SnO2 [SnO2(C)] and nano-SnO2 prepared by the precipitation method [SnO2(P)] were used to prepare the SnO2 sensor in this study. In the case of DCM and acetonitrile, the SnO2(P) sensor showed higher sensor response as compared with the SnO2(C) sensors. In the case of DMMP and DPGME, however, the SnO2(C) sensor showed higher responses than those of the SnO2(P) sensors. In particular, the response of the SnO2(P) sensor increased as the calcination temperature increased from 400 °C to 800 °C. These results can be explained by the fact that the response of the SnO2-based gas sensor depends on the textural properties of tin oxide and the molecular size of the chemical agent simulant in the detection of the simulant gases (0.1–0.5 ppm).

1. Introduction

Chemical warfare agents (CWAs) are chemical substances intended for use in military operations to kill, injure or incapacitate an enemy. These agents are classified according to their mechanism of toxicity in humans into blister agents, nerve agents, blood agents, and pulmonary agents [1]. These agents still remain a threat, especially from other countries and terrorists, as they are easy to manufacture, cheap and have devastating effects [1].

In recent years, there has been an increasing demand for sensing devices which monitor low concentration levels of toxic gases [210]. SnO2-based gas sensors have been used to detect toxic gases and CWAs, even at low concentration levels (ppm level) [816]. The advantages of sensors fabricated with SnO2 are as follows: high level of sensor response, simple design, low weight, and cheap price. Additionally, SnO2 gas sensors have greater sensitivity in detecting organic compounds due to the control of particle size and the addition of promoters [9,10]. Choi et al. fabricated semiconductor-thick film gas sensors based on tin oxide, and examined their gas response characteristics for four chemical warfare agent (CWA) simulant gases [16]. Lee et al. determined the sensing and regeneration properties of SnO2-based thick film gas sensors for low concentration levels of chemical agent simulants such as acetonitrile, dipropylene glycol methyl ether (DPGME), dimethyl methylphosphonate (DMMP) and dichloromethane (DCM) [17,18]. However, the SnO2-based gas sensors were not completely regenerated after the detection of DMMP and dichloromethane (DCM), which are commonly used as chemical agent simulants in nerve agents and pulmonary agents. Recently, the new recoverable SnO2-based thick film gas sensors promoted by Mo and Ni promoters were developed to detect low concentrations of DMMP and DCM by Lee et al. [1820]. The SnO2-based gas sensors showed not only an excellent sensor response in the detection of DMMP and DCM, but also a complete recovery by means of the thermal decomposition under air. In addition, a relationship between the textural properties of SnO2 and the response of a SnO2 gas sensor for chemical agent simulants was shown in our previous papers [19,21]. However, the effect of the physical property of tin oxide and chemical agent simulants such as acetonitrile, DPGME, DMMP and DCM on the response level of the SnO2 gas sensor has not been explained in detail.

The objective of this study was to identify the effects of the textural properties of tin oxide, including the surface area and pore size distribution, and the molecular size of the chemical agent simulants on the sensing properties. The physical properties of various tin oxides were investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), BET and porosimetry.

2. Experimental Section

2.1. Preparation of Materials

Commercial SnO2 [SnO2(C), Aldrich, 325 mesh, 99.9%] and SnO2 prepared by the precipitation method [SnO2(P)] were used as the raw materials for preparing the SnO2 sensors used in this study. SnO2(P) was prepared by the precipitation method using SnCl4 and an ammonia solution as reported in our previous papers [18,19]. Products were calcined in a muffle furnace at various temperatures such as 400, 600, and 800 °C for 4 h. The ramping rate of the temperature was maintained at 3 °C/min. Henceforth we denote the sensors as SnO2(C)600 and SnO2(P)400, where SnO2(C) and SnO2(P) represent commercial SnO2 and SnO2 prepared by the precipitation method, respectively and 600 and 400 represent the calcination temperatures.

2.2. Preparation of Sensors

A thick film sensor device was fabricated by a screen-printing method. Each powder sample above was mixed with an organic binder (α-terpineol, Aldrich, 90%) and the resulting paste was printed on an alumina substrate through a 200 mesh screen by using a semi-automatic screen printer [1821]. The alumina substrate was equipped with a pair of screened Pt electrodes on the front side and a heater on the back side. The printed thick–film sensor devices were dried and calcined at 600 °C for 1 h. A SnO2(P)400 sensor device was calcined at 400 °C for 1 h.

2.3. Sensor Testing System

The measured gases were acetonitrile (CH3CN, 99%, Aldrich), dimethylmethylphosphonate (DMMP; CH3P(O)(OCH3)2, 97%, Aldrich), di(propyleneglycol) methyl ether (DPGME; CH3OC3H6OC3H6OH, 99+%, Aldrich), and dichloromethane (DCM; CH2Cl2, 99.9%, Aldrich) which are chemical agent simulants of blood agents, nerve agents, blister agents, and pulmonary agents, respectively. The concentration of chemical agent simulant was controlled by its relative vapor pressure in the saturator [18,19,21]. The gas was diluted with dry air, and then a part of the diluted gas was extracted by a metering valve. The extracted gas was diluted again with dry air to prepare a low concentration of 0.8 ppm or less. Then the gas flow was introduced into the two-liter chamber. The total flow rate of the gas diluted with air was 1,000 mL/min. The chemical agent simulant was injected for 10 min. Most of the sensors used in our work reached 95% of the maximum response before reaching 10 min in the presence of the dichloromethane gas. In the present study, sensor response is defined by Equation (1):

Sevsor response ( % ) = [ ( R a R g ) / R a ] × 100
where Ra and Rg are the electric resistance in air and in the chemical agent simulants, respectively. Rg is the resistance value measured at the end of the 10 min gas injection. Recovery is defined as the ability to reach again 90% of the original resistance of the sensor.

2.4. Characterization of Materials

The film thicknesses of the SnO2-based sensors were measured with the aid of a scanning electron microscopy (SEM; JEOL, JSM-6701F). In addition, the morphology of the SnO2 powder was investigated using transmission electron microscopy (TEM; Hitachi, H-7100). X-ray diffraction (XRD; Philips, X’PERT) was performed to identify the crystalline phases in regard to the materials. The pore size distribution and surface area of the materials were measured by using an Hg porosimetry (Micromeritics, AutoPore IV 9500), which operated at a pressure range between 0.005 and 413.7 MPa, and a BET (Quantachrome, AUTOSORB-14200), respectively.

3. Results and Discussion

3.1. Comparison of the Responses of SnO2(C) and SnO2(P) Sensors

Figure 1 shows the responses at 350 °C of the SnO2(C)600 and the SnO2(P)600 sensors to various chemical agent simulants such as DCM, acetonitrile, DMMP, and DPGME at a concentration range between 0.02 ppm and 0.8 ppm. In the cases of DCM and acetonitrile, the responses of the SnO2(P)600 sensor using tin oxide prepared by the precipitation method was higher than that of the SnO2(C)600 sensor using commercial tin oxide at all the concentrations, as shown in Figure 1(a,b). On the other hand, in the cases of DMMP and DPGME, the responses of the SnO2(C)600 sensor were higher than those of the SnO2(P)600 sensors at almost all concentrations, as shown in Figure 1(c,d). The important point to note is that the responses of the SnO2 gas sensors were affected by the kinds of tin oxide and chemical agent simulant, regardless of the concentration of the chemical agent simulant.

Figure 2 shows the response curves of the SnO2(P)600 and SnO2(C)600 sensors at a concentration range between 0.1 and 0.8 ppm of chemical agent simulants such as DCM, acetonitrile, DMMP, and DPGME. The response curves of the SnO2(P)600 and SnO2(C)600 sensors showed excellent recovery ability, as well as excellent sensor response, for acetonitrile and DPGME, respectively. On the other hand, in the case of DCM and DMMP, these sensors did not recover after the detection of these gases as shown in Figure 2(a,c). In our previous papers [19,20], however, it was reported that the SnO2-based sensor promoted simultaneously with NiO and MoO3 not only showed excellent sensor response in the detection of DCM and DMMP, but also complete recovery under air.

To identify the reason for these results as mentioned previously, we investigated the sensing behaviors and the physical properties of various pure tin oxide materials. SnO2(P)400, SnO2(P)600, and SnO2(P)800 were prepared by calcining tin oxides, which were produced using the precipitation method, at various temperatures (400, 600, and 800 °C, respectively). Figure 3 shows the responses of the SnO2(C)600, SnO2(P)400, SnO2(P)600, and SnO2(P)800 sensors to chemical agent simulants such as DCM, acetonitrile, DMMP, and DPGME of 0.5 ppm at 350 °C. In the cases of DCM and acetonitrile, the SnO2(P) sensors gave higher sensor responses as compared with the SnO2(C) sensors. Also, the response of the SnO2(P) sensor decreased slightly as the calcination temperature increased from 400 °C to 800 °C. In the cases of DMMP and DPGME, however, the responses of the SnO2(C) sensor were higher than those of all SnO2(P) sensors. In addition, the response of the SnO2(P) sensor increased as the calcination temperature increased, unlike the cases of DCM and acetonitrile. It must be noted that the sensor responses to DCM and acetonitrile tended to be different than those of DMMP and DPGME. From these results, it is known that the response of the SnO2 sensor is directly related to the types of tin oxide and chemical agent simulants. These results are thought to be due to the structure effect and/or the textural property of the tin oxides.

3.2. Effect of Textural Property on the Sensor Response

Figure 4 shows the XRD patterns of pure SnO2(C)600, SnO2(P)400, SnO2(P)600, and SnO2(P)800 materials. The XRD patterns of SnO2(C)600 showed only a SnO2 phase (JCPDS No. 88-0287) as having a tetragonal structure. The XRD patterns of SnO2(P)400, 600, and 800 were completely consistent with that of the SnO2(C)600. These results indicate that the difference in the sensor response of the SnO2(C)600 and the SnO2(P)600 sensors to the chemical agent simulants was not affected by the structure of the tin oxide.

Figure 5 shows SEM images of surfaces and thick layers of the SnO2(P)400 (a), SnO2(P)600 (b), SnO2(P)800 (c), and SnO2(C)600 (d) sensors. As shown in Figure 5(a–c), it was observed that the tin oxides prepared by precipitation (SnO2(P)) were composed of nano-sized particles and narrow size distribution and that the particle size of tin oxide increased with increasing calcination temperature. On the other hand, the commercial tin oxide (SnO2(C)) has the particle size ranges between about 30 nm and 200 nm. The film thicknesses of these sensors were observed at about 20 μm.

Figure 6 shows TEM morphologies of pure SnO2(C)600, SnO2(P)400, SnO2(P)600, and SnO2(P)800 materials. The particle sizes of the SnO2(P)400, SnO2(P)600, SnO2(P)800, and SnO2(C)600 observed from TEM images were 4–5, 10–15, 30–40, and 40–50 nm, respectively. Their crystallite sizes were calculated from the XRD results of Figure 4 with the Scherrer equation and were found to be 4.9, 14.8, 29.6, and 39.9 nm. These results are in agreement with their particle sizes from the TEM results. These results show that the crystallite size grows gradually as the calcination temperature increases.

Figure 7 shows the pore size distribution of SnO2(P)400, SnO2(P)600, SnO2(P)800, and SnO2(C)600. The pore diameter of the SnO2(P) prepared by precipitation was increased with an increase in the calcination temperature. The pore diameter increased as the following order: SnO2(P)400 < SnO2(P)600 < SnO2(P)800 < SnO2(C)600. In a separate BET experiment, it was known that the surface areas of SnO2(P)400, SnO2(P)600, SnO2(P)800, and SnO2(C)600 were 74.0, 17.2, 10.9, and 9.2 m2/g, respectively and that they decreased in the following order: SnO2(P)400 > SnO2(P)600 > SnO2(P)800 > SnO2(C)600. However, the surface area of the SnO2(P)400 sensor was approximately four times greater than that of the SnO2(P)600 sensor, but the response of these sensors slightly increased for both the DCM and acetonitrile as shown in Figure 3(a,b). It was thought that these results was due to the high surface area offered by micropore distribution of the SnO2(P)400 material, into which it was difficult for the DCM and acetonitrile to diffuse.

Figure 8 shows the ratio of SSnO2(C)600/SSnO2(P)400 for chemical agent simulants. SSnO2(C)600 and SSnO2(P)400 represent the responses of the SnO2(C)600 sensor and the SnO2(P)400 sensor, respectively. The SSnO2(C)600/SSnO2(P)400 ratio for DCM and acetonitrile showed value less than 1, indicating the sensor response for DCM and acetonitrile tended to be negatively correlated with pore diameter. On the other hand, the SSnO2(C)600/SSnO2(P)400 ratio for DMMP and DPGME was higher than 1, indicating the sensor responses for DMMP and DPGME tended to increase as the pore diameter increased. These results mean that the sensor responses for DMMP and DPGME depend on the pore diameter, and that the sensor responses for DCM and acetonitrile depend on the surface area rather than pore diameter. However, as shown in Figure 8, the trend in the SSnO2(C)600/SSnO2(P)400 ratio for the acetonitrile and DPGME appears less clearly as compared with that for the DCM and DMMP. To clarify the reason for these results, further studies are necessary to verify the role of other parameters like the gas/surface interactions.

To identify the reason for the results of Figure 8, the molecular diameter and volume of the chemical agent simulants were calculated by numerical Monte Carlo simulations on the basis of the simple molecular model of various isomers for chemical agent simulants. These results are shown in Table 1.

The molecular diameter of acetonitrile was found to be approximately 6.52 Å and was almost similar to that of DCM. In addition, both the molecular diameters and volumes of DMMP and DPGME were relatively much larger than those of DCM and acetonitrile, as shown in Table 1. From these results, it is clear that the pore size of the tin oxide being used as the sensing material is a very important factor in the response of the SnO2-based sensor for DMMP and DPGME due to their large molecular sizes and volumes. Also, it is clear that in the cases of DCM and acetonitrile, the surface area of the tin oxide plays an important role in the sensor response due to their small molecular sizes and volumes. It is concluded that the sensing property of the SnO2-based sensor for the chemical agent simulants is directly related to the molecular diameter and volume of the chemical agent simulants, as well as the textural properties of the tin oxide.

4. Conclusions

Sensing behaviors of SnO2-based gas sensors prepared from various tin oxides were investigated to identify the effects of the textural properties of tin oxide and the molecular size of chemical agent simulants on the sensing properties. Tin oxide having a large pore size shows higher sensor response for DPGME and DMMP, as compared with that of tin oxide having a small pore size. This can be explained by the fact that the sensor response of the SnO2-based sensor for DPGME and DMMP is affected by the pore size of tin oxide due to their large molecular diameters and volumes. On the other hand, the sensor response for DCM and acetonitrile depends on the surface area rather than pore diameter due to their small molecular diameters and volumes. From these results, it is concluded that both the textural properties of the tin oxide and the molecular diameter of chemical agent simulants must to be considered when designing a SnO2-based sensor if one desires an excellent sensor response for chemical agent simulants.

Acknowledgments

This work was supported by the Energy Efficiency & Resources of the Korea Insitute of Energy Technology Evaluation and Planning (KETEP) grant funded by the Korea government Ministry of Knowledge Economy (2010201020007A). This work was supported by Priority Research Centers Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (2009-0093819).

References

  1. Chauhana, S; Chauhanb, S; D’Cruzf, R; Faruqic, S; Singhd, KK; Varmae, S; Singha, M; Karthik, V. Chemical warfare agents. Environ. Toxicol. Pharmacol 2008, 26, 113–122. [Google Scholar]
  2. Abu-Qare, AW; Abou-Donia, MB. Sarin: Health effects, metabolism, and methods of analysis. Food Chem. Toxicol 2002, 40, 1327–1333. [Google Scholar]
  3. Liu, J; Huang, X; Ye, G; Liu, W; Jiao, Z; Chao, W; Zhou, Z; Yu, Z. H2S detection sensing characteristic of CuO/SnO2 Sensor. Sensors 2003, 3, 110–118. [Google Scholar]
  4. Patel, SV; Mlsna, TE; Fruhberger, B; Klaassen, E; Cemalovic, S; Baselt, DR. Chemicapacitive microsensors for volatile organic compound detection. Sens. Actuat. B 2003, 96, 541–553. [Google Scholar]
  5. Nieuwenhuizen, MS; Harteveld, JLN. An automated SAW gas sensor testing system. Sens. Actuat. A 1994, 44, 219–229. [Google Scholar]
  6. Du, X; Ying, Z; Jiang, Y; Liu, Z; Yang, T; Xie, G. Synthesis and evaluation of a new polysiloxane as SAW sensor coatings for DMMP detection. Sens. Actuat. B 2008, 134, 409–413. [Google Scholar]
  7. Wang, Y; Yang, Z; Hou, Z; Xu, D; Wei, L; Kong, ESW; Zhang, Y. Flexible gas sensors with assembled carbon nanotube thin films for DMMP vapor detection. Sens. Actuat. B 2010, 150, 708–714. [Google Scholar]
  8. Choi, YH; Yang, M; Hong, SH. H2 sensing characteristics of highly textured Pd-doped SnO2 thin films. Sens. Actuat. B 2008, 134, 117–121. [Google Scholar]
  9. Kim, JC; Jun, HK; Huh, JS; Lee, DD. Tin oxide-based methane gas sensor promoted by alumina-supported Pd catalyst. Sens. Actuat. B 1997, 45, 271–277. [Google Scholar]
  10. Xu, C; Tamaki, J; Miura, N; Yamazoe, N. Grain size effects on gas sensitivity of porous SnO2-based elements. Sens. Actuat. B 1991, 3, 147–155. [Google Scholar]
  11. Oh, SW; Kim, YH; Yoo, DJ; Oh, SM; Park, SJ. Sensing behaviour of semiconducting metal oxides for the detection of organophorus compounds. Sens. Actuat. B 1993, 13–14, 400–403. [Google Scholar]
  12. Berger, F; Brunol, E; Planade, R; Chambaudet, A. Detection of DEMP vapors using SnO2-based gas sensors: Understanding of the chemical reactional mechanism. Thin Solid Films 2003, 436, 1–8. [Google Scholar]
  13. Brunol, E; Berger, F; Fromm, M; Planade, R. Detection of dimethyl methylphosphonate (DMMP) by tin dioxide-based gas sensor: Response curve and understanding of the reactional mechanism. Sens. Actuat. B 2006, 120, 35–41. [Google Scholar]
  14. Tomchenko, AA; Harmer, GP; Marquis, BT. Detection of chemical warfare agents using nanostructured metal oxide sensors. Sens. Actuat. B 2005, 108, 41–55. [Google Scholar]
  15. Park, HD; Lee, DD; Lee, WI; Kim, JM; Kim, JM. Sensitivity of SnO2-based thick-film devices to CH3CN. Sens. Mater 1994, 5, 209–220. [Google Scholar]
  16. Choi, NJ; Kwak, JH; Lim, YT; Bahn, TH; Yun, KY; Kim, JC; Huh, JS; Lee, DD. Classification of chemical warfare agents using thick film gas sensor array. Sens. Actuat. B 2005, 108, 298–304. [Google Scholar]
  17. Lee, WS; Choi, HY; Lee, SC; Lee, SJ; Lee, DD; Huh, JS; Kim, JC. Recoverable SnO2-based sensors promoted with MoO3 and Sb2O3 for the detection of DMMP. Rare Met. Mater. Eng 2006, 35, 155–156. [Google Scholar]
  18. Lee, SC; Choi, HY; Lee, SJ; Lee, WS; Huh, JS; Lee, DD; Kim, JC. The development of SnO2-based recoverable gas sensors for the detection of DMMP. Sens. Actuat. B 2009, 137, 239–245. [Google Scholar]
  19. Lee, SC; Choi, HY; Lee, SJ; Lee, WS; Huh, JS; Lee, DD; Kim, JC. Novel SnO2-based gas sensors promoted with metal oxides for the detection of dichloromethane. Sens. Actuat. B 2009, 138, 446–452. [Google Scholar]
  20. Lee, SC; Choi, HY; Lee, WS; Lee, SJ; Ragupathy, D; Lee, DD; Kim, JC. Improvement of recovery of SnO2-based thick film gas sensors for dimethyl methylphosphonate (DMMP) detection. Sens. Lett 2011, 9, 101–105. [Google Scholar]
  21. Lee, WS; Lee, SC; Lee, SJ; Lee, DD; Huh, JS; Jun, HK; Kim, JC. The sensing behavior of SnO2-based thick-film gas sensors at a low concentration of chemical agent simulants. Sens. Actuat. B 2005, 108, 148–153. [Google Scholar]
Figure 1. Responses of SnO2(C)600 (•) and SnO2(P)600 (▾) sensors as a function of chemical agent simulant concentration; (a) DCM; (b) acetonitrile; (c) DMMP; (d) DPGME.
Figure 1. Responses of SnO2(C)600 (•) and SnO2(P)600 (▾) sensors as a function of chemical agent simulant concentration; (a) DCM; (b) acetonitrile; (c) DMMP; (d) DPGME.
Sensors 11 06893f1 1024
Figure 2. The response curves of the SnO2(P)600 (a,b) and SnO2(C)600 (c,d) sensors at a concentration range between 0.1 and 0.8 ppm of chemical agent simulants; (a) DCM; (b) acetonitrile; (c) DMMP; (d) DPGME.
Figure 2. The response curves of the SnO2(P)600 (a,b) and SnO2(C)600 (c,d) sensors at a concentration range between 0.1 and 0.8 ppm of chemical agent simulants; (a) DCM; (b) acetonitrile; (c) DMMP; (d) DPGME.
Sensors 11 06893f2 1024
Figure 3. The responses of the SnO2(P)400 (i), SnO2(P)600 (ii), SnO2(P)800 (iii), and SnO2(C)600 (iv) sensors at chemical agent simulants of 0.5 ppm. (a) DCM; (b) acetonitrile; (c) DMMP; (d) DPGME.
Figure 3. The responses of the SnO2(P)400 (i), SnO2(P)600 (ii), SnO2(P)800 (iii), and SnO2(C)600 (iv) sensors at chemical agent simulants of 0.5 ppm. (a) DCM; (b) acetonitrile; (c) DMMP; (d) DPGME.
Sensors 11 06893f3 1024
Figure 4. XRD patterns of pure SnO2(C)600 (a); SnO2(P)400 (b); SnO2(P)600 (c); and SnO2(P)800 (d) materials; (•) SnO2 (tetragonal).
Figure 4. XRD patterns of pure SnO2(C)600 (a); SnO2(P)400 (b); SnO2(P)600 (c); and SnO2(P)800 (d) materials; (•) SnO2 (tetragonal).
Sensors 11 06893f4 1024
Figure 5. SEM images of surfaces (I) and thick layers (II) of the SnO2(P)400 (a); SnO2(P)600 (b); SnO2(P)800 (c); and SnO2(C)600 (d) sensors.
Figure 5. SEM images of surfaces (I) and thick layers (II) of the SnO2(P)400 (a); SnO2(P)600 (b); SnO2(P)800 (c); and SnO2(C)600 (d) sensors.
Sensors 11 06893f5a 1024Sensors 11 06893f5b 1024
Figure 6. TEM morphologies of pure SnO2(C)600 (a); SnO2(P)400 (b); SnO2(P)600 (c); and SnO2(P)800 (d) materials.
Figure 6. TEM morphologies of pure SnO2(C)600 (a); SnO2(P)400 (b); SnO2(P)600 (c); and SnO2(P)800 (d) materials.
Sensors 11 06893f6 1024
Figure 7. Pore size distribution of SnO2(P)400, SnO2(P)600, SnO2(P)800,and SnO2(C)600 materials.
Figure 7. Pore size distribution of SnO2(P)400, SnO2(P)600, SnO2(P)800,and SnO2(C)600 materials.
Sensors 11 06893f7 1024
Figure 8. The ratio of SSnO2(C)600/SSnO2(P)400 for chemical agent simulants; (a) DCM; (b) Acetonitrile; (c) DMMP; (d) DPGME.
Figure 8. The ratio of SSnO2(C)600/SSnO2(P)400 for chemical agent simulants; (a) DCM; (b) Acetonitrile; (c) DMMP; (d) DPGME.
Sensors 11 06893f8 1024
Table 1. The molecular diameter and molecular volume of chemical agent simulants.
Table 1. The molecular diameter and molecular volume of chemical agent simulants.
SimulantsMolecular diameter (Å)Molecular volume (cm3/mol)
DCM6.2834.84
Acetonitrile6.5239.67
DMMP8.4296.40
DPGME9.28134.34

Share and Cite

MDPI and ACS Style

Lee, S.C.; Kim, S.Y.; Lee, W.S.; Jung, S.Y.; Hwang, B.W.; Ragupathy, D.; Lee, D.D.; Lee, S.Y.; Kim, J.C. Effects of Textural Properties on the Response of a SnO2-Based Gas Sensor for the Detection of Chemical Warfare Agents. Sensors 2011, 11, 6893-6904. https://doi.org/10.3390/s110706893

AMA Style

Lee SC, Kim SY, Lee WS, Jung SY, Hwang BW, Ragupathy D, Lee DD, Lee SY, Kim JC. Effects of Textural Properties on the Response of a SnO2-Based Gas Sensor for the Detection of Chemical Warfare Agents. Sensors. 2011; 11(7):6893-6904. https://doi.org/10.3390/s110706893

Chicago/Turabian Style

Lee, Soo Chool, Seong Yeol Kim, Woo Suk Lee, Suk Yong Jung, Byung Wook Hwang, Dhanusuraman Ragupathy, Duk Dong Lee, Sang Yeon Lee, and Jae Chang Kim. 2011. "Effects of Textural Properties on the Response of a SnO2-Based Gas Sensor for the Detection of Chemical Warfare Agents" Sensors 11, no. 7: 6893-6904. https://doi.org/10.3390/s110706893