Article

Fabrication of Polypyrrole Nanowire and Nanotube Arrays

Dongguan University of Technology, Dongguan 523106, P. R. China
*
Author to whom correspondence should be addressed.
Sensors 2005, 5(4), 245-249; https://doi.org/10.3390/s5040245
Submission received: 25 June 2004 / Accepted: 5 November 2005 / Published: 15 April 2005
(This article belongs to the Special Issue Papers presented at I3S2004, Nanjing)

Abstract

:
Large area highly uniform and ordered polypyrrole nanowire and nanotube arrays were fabricated by chemical oxidation polymerization with the help of a porous anodic aluminium oxide (AAO) template. Under 0.2 moL/L pyrrole (H2O) and 0.2 moL/L FeCl3 (H2O) pattern, polypyrrole nanowire arrays were obtained after 2.0 hours polymerization reaction in a two-compartment reaction cell. When the reaction was stopped after 15 minutes, polypyrrole nanotube arrays have been formed. The diameter, length and density of compositive nanowires and nanotubes could be controlled by parameters of AAO template.

1. Introduction

It is an unquestionable fact that nanomaterials possessed several unique properties superior to their bulky counterparts [1]. Many fabrication methods have been developed, but difficulty and challenge are still exist presently in preparing large area highly ordered nanoarray materials, which would be directly utilized in many devices. Among available approaches, template-based synthesis was well suited for producing arrays with uniform diameters and high aspect ratio wires [2]. Porous anodic aluminium oxide (AAO) templates especially attracted extensive interest because of its desirable characteristics, including highly ordered porous distribution, uniform and tunable pore diameters over a wide rang (∼ 7 – 300 nm) and lengths (to > 100 μm), good mechanical and thermal stability and well-developed preparation methods [3]. Polypyrrole and other conductive polymers stimulated great interest on the basis of their importance in basic scientific research and potential technology applications. Meanwhile, conductive polymer nanomaterials were also extensively studied [4]. However, to our knowledge, polypyrrole nanowires or nanotube arrays were less reported than films [5]. Due to the excellent biologic compatibility, catalysis, stability and conductivity, polypyrrole was considered fabricating nanowire and nanotube arrays for using biosensors. Herein, we report a simple chemical oxidation polymerization approach to prepare polypyrrole nanowire and nanotube arrays under room temperature.

2. Experimental

All the common chemicals were of analytical grade and were commercially available. The water used in all experiments is twice distilled with a quartz heating tube. A model HITACHI S-5200 scanning electron microscope (SEM) was used for morphology analysis. All experiments were carried out under room temperature (about 20 ºC).
The experimental equipment and AAO templates were both prepared in our laboratory. The concise drawing of the experimental equipment was shown in Fig. 1. The template was clamped in a two-compartment U-shaped cell. The pyrrole and oxide reagent solutions were carefully added to two cells with the same speed, respectively. The polymerization reaction was carried out under room temperature. The two side solutions diffused to each other through the nanochannels of the AAO template. The balanceable diffusion could be controlled by adjusting the solution height in two U-shaped tubes.

3. Results and Discussion

The AAO templates were fabricated by a two-step anodizing approach in 1.0 moL/L sulfuric acid electrolyte with 20 V steady potential at 0 ∼ 5 ºC. The preparing of templates was described in detailed elsewhere [6]. The AAO template possessed closely monodisperse packed hexagonal cylindrical nanochannels with an average porous diameter of 35 nm, a channel length at about 30 ∼ 50 μm and a porous density of about at 4.8×1010 pores·cm-2. The representative scanning electron microscope photograph of our template was shown in Figure 2.
In the chemical oxidation polymerization reaction, ammonium persulfate ((NH4)2S2O8) and ferric chloride (FeCl3) were used as oxidants. 0.2 moL/L oxidant aqueous solution was placed in the right side compartment. Considering of controlling diffusion speed of the two reactants by changing the solvent compatible extent between the two sides of template, pyrrole was dissolved in carbon tetrachloride (CCl4), diethyl ether (C2H5OC2H5), n-butanol (C4H9OH), methanol (CH3OH) and water (H2O), respectively. 0.2 moL/L different pyrrole solution was added to the left side compartment, respectively. Numerous experimental results indicated that under CCl4/H2O and C2H5OC2H5/H2O patterns, polymerization reactions were very slow; furthermore, no nanowires were obtained and usually produced some films on the templates surface. Under C4H9OH/H2O and CH3OH/H2O patterns, although polymerization reaction rate were relatively appropriate, the synthetic nanowire arrays were not good. Lots of them were broken and some segments were dispersed during removing the templates. The possible reasons are that many diminutive air bubbles would be produced during the interdiffusion process with releasing of dissolving heat, which made polymerization reaction uneven. Consequently, the polypyrrole nanowires were loose and easily broken. The last polymerization reactions were carried out rapidly and effectively under H2O/H2O homogeneous pattern. Compared with (NH4)2S2O8, FeCl3 used as oxidant made polymerization reaction more effective and the obtained polypyrrole nanowires were better. It is obvious that the Fe3+ ion is smaller than the S2O82- ion. In addition, the anodic alumina template used in our experiments only possessed 30 nm porous diameters. So the Fe3+ ion could move more freely in the template nanochannels than the S2O82- ion.
The influence of reactants concentrations on the polymerization reaction was investigated. The concentration ratio of pyrrole and FeCl3 was kept at 1:1. Polypyrrole nanowire arrays were fabricated under the reactants concentration at 1.0, 0.8, 0.6, 0.4, 0.2, 0.05 and 0.01 moL/L, respectively. The results show that at high concentrations, the polymerization reactions were fast and there were thick polypyrrole layers on the two surfaces of the templates. The nanowires were not uniform, loose and broken. The possible reason is that the polymerization reaction is too fast and the formed polypyrrole has no time to assemble. Moreover, two polypyrrole layers on the surfaces of template blocked the diffusion of reactants in the nanochannels. On the other side, when the reactants concentrations were lower than 0.01 moL/L, it was difficult to form polypyrrole nanowire arrays. Thinking of efficiency and quality, 0.2 moL/L was selected as the optimal concentration. Under 0.2 moL/L pyrrole (H2O)/0.2 moL/L FeCl3 (H2O) pattern, the reaction time was further optimized. Many experimental results revealed that the polypyrrole nanowire arrays were basically formed after 2.0 hours.
Under optimal experimental conditions, after the end of the reaction, the template was taken out and polypyrrole on the template surfaces was carefully scraped off. The template was removed with 5% H3PO4 aqueous solution. An exemplary SEM photograph was shown in Figure 3. From that, although some portions were collapsed, it is clear that the nanowire array was highly ordered and uniform on a large area. The inset has indicated the amplificatory polypyrrole nanowires with 38 nm uniform diameters. Considering a little swell of the nanowires after removing the template, it agreed well with the porous diameters of the used template.
In order to investigate the polymerization process, the polymerization reaction was ceased after 15 minutes. In this experiment, another kind of AAO template with about 60 nm porous diameter was utilized. The result was shown in Figure 4. For clarity of SEM, the template was not removed completely.
One can see that a large-scale uniform polypyrrole nanotube array has been formed. The inset indicated that the polypyrrole nanotubes were hexagonal prism and possessed about 60 nm outer diameters and 10 nm wall thickness. This result helped us to confirm that polypyrrole nanowires are formed from outer diameter to inner diameter, which agrees to the previous research report [7]. This experiment also made us believe that we could obtain many different parameters for polypyrrole nanotube arrays by controlling the polymerization reaction times and conditions. Further systematic works are in progress.
In conclusion, large-scale highly uniform polypyrrole nanowire and nanotube arrays have been fabricated under room temperature with an AAO template aid. The polymerization reaction conditions were optimized. The experimental results revealed that polypyrrole was formed from wall to the center of nanochannels. If the different parameters for AAO templates were used, corresponding polypyrrole nanowire and nanotube arrays could be obtained.

Acknowledgments

This work was supported by the National Natural Science Foundation of China (20375008), the Natural Science Foundation of Guangdong Province (32167), Technologies R&D Programs of Guangdong Province (C31902) and the Natural Science Research Programs of High School (Z03091).

References

  1. Jin, R.; Cao, Y.; Mirkin, C. A.; Kelly, K. L.; Schatz, G. C.; Zheng, J. G. Photo Induced Conversion of Silver Nanospheres to Nanoprisms. Science 2001, 294, 1901–1903. [Google Scholar]
  2. Martin, C. R. Nanomaterials: a membrane-based synthetic approach. Science 1994, 266, 1961–1966. [Google Scholar] Martin, C. R. Membrane-Based Synthesis of Nanomaterials. Chem. Mater. 1996, 8, 1739. [Google Scholar]
  3. Masuda, H.; Hasegwa, F.; Ono, S. Self-ordering of cell arrangement of anodic porous alumina formed in sulfuric acid solution. J. Electrochem. Soc. 1997, 144, L127–L130. [Google Scholar] Jessensky, O.; Müller, F.; Gösele, U. Self-organized formation of hexagonal pore arrays in anodic alumina. J. Appl. Phys. 1998, 72, 1173–1175. [Google Scholar]
  4. Choi, S. J.; Park, S. M. Electrochemical Growth of Nanosized Conducting Polymer Wires on Gold Using Molecular Templates. Adv. Mater. 2000, 12, 1547. [Google Scholar] Fu, M. X.; Zhu, Y. F.; Tan, R. Q.; Shi, G. Q. Aligned Polythiophene Micro- and Nanotubules. Adv. Mater. 2001, 13, 1874–1877. [Google Scholar]
  5. Demoustier-Champagne, S.; Ferain, E.; Jérôme, C.; Jérôme, R.; Legras, R. Electrochemically synthesized polypyrrole nanotubules: effects of different experimental conditions. Eur. Polym. J. 1998, 34, 1767–1774. [Google Scholar]
  6. Cheng, F. L.; Jing, B. K.; Wang, H.; Wu, J.; Zhang, M. L. Study on Preparation of highly ordered nanochannel array aluminum oxide template. Asian J. Chem. 2004, 16. in press. [Google Scholar]
  7. Duchet, J.; Legras, R.; Demoustier-Champagne, S. Chemical synthesis of polypyrrole: Structure–properties relationship. Synth. Met. 1998, 98, 113–122. [Google Scholar]
Figure 1. The drawing of reaction equipment.
Figure 1. The drawing of reaction equipment.
Sensors 05 00245f1
Figure 2. The SEM photograph of AAO template.
Figure 2. The SEM photograph of AAO template.
Sensors 05 00245f2
Figure 3. Polypyrrole nanowire array (SEM photograph).
Figure 3. Polypyrrole nanowire array (SEM photograph).
Sensors 05 00245f3
Figure 4. SEM photograph of polypyrrole nanotube array.
Figure 4. SEM photograph of polypyrrole nanotube array.
Sensors 05 00245f4

Share and Cite

MDPI and ACS Style

Cheng, F.-L.; Zhang, M.-L.; Wang, H. Fabrication of Polypyrrole Nanowire and Nanotube Arrays. Sensors 2005, 5, 245-249. https://doi.org/10.3390/s5040245

AMA Style

Cheng F-L, Zhang M-L, Wang H. Fabrication of Polypyrrole Nanowire and Nanotube Arrays. Sensors. 2005; 5(4):245-249. https://doi.org/10.3390/s5040245

Chicago/Turabian Style

Cheng, Fa-Liang, Ming-Liang Zhang, and Hong Wang. 2005. "Fabrication of Polypyrrole Nanowire and Nanotube Arrays" Sensors 5, no. 4: 245-249. https://doi.org/10.3390/s5040245

Article Metrics

Back to TopTop