Next Article in Journal
The Stability Analysis Method of the Cohesive Granular Slope on the Basis of Graph Theory
Previous Article in Journal
In Vitro Evaluation of Dentin Tubule Occlusion for Novel Calcium Lactate Phosphate (CLP) Paste
Previous Article in Special Issue
Role of Hydrogen Bonding in the Formation of Adenine Chains on Cu(110) Surfaces
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Fabrication of p-Type ZnO:N Films by Oxidizing Zn3N2 Films in Oxygen Plasma at Low Temperature

Institute of Modern Physics, Fudan University, Shanghai 200433, China
*
Author to whom correspondence should be addressed.
Materials 2017, 10(3), 236; https://doi.org/10.3390/ma10030236
Submission received: 1 December 2016 / Revised: 31 January 2017 / Accepted: 8 February 2017 / Published: 27 February 2017

Abstract

:
The oxygen vacancy (VO) is known as the main compensation center in p-type ZnO, which leads to the difficulty of fabricating high-quality p-type ZnO. To reduce the oxygen vacancies, we oxidized Zn3N2 films in oxygen plasma and successfully prepared p-type ZnO:N films at temperatures ranging from room temperature to 300 °C. The films were characterized by X-ray diffraction (XRD), non-Rutherford backscattering (non-RBS) spectroscopy, X-ray photoelectron spectroscopy, photoluminescence spectrum, and Hall Effect. The results show that the nitrogen atoms successfully substitute the oxygen sites in the ZnO:N films. The film prepared at room temperature exhibits the highest hole concentration of 6.22 × 1018 cm−3, and the lowest resistivity of 39.47 Ω∙cm. In all ZnO:N films, the VO defects are reduced significantly. At 200 °C, the film holds the lowest value of VO defects and the strongest UV emission. These results imply that oxygen plasma is very efficient in reducing VO defects in p-type ZnO:N films, and could greatly reduce the reaction temperature. This method is significant for the development of ZnO-based optoelectronic devices.

Graphical Abstract

1. Introduction

The broad band gap (3.37 eV at room temperature), the large exciton binding energy (60 meV at room temperature), the amenability to wet chemical etching, the realization of high quality single crystal, the possibility of low-temperature growth, and the transparent nature make ZnO a great potential material in optoelectronic devices—especially in the area of invisible and flexible electronics [1,2,3]. During the past few decades, flexible and transparent electronics have been an area of active research by several companies and by the scientific community [4,5]. With this technology, the fabrication of a wide range of innovative products will be possible, from flexible displays to wearable electronics. The most commonly used substrate materials are polyethylene terephthalate (PET) and polycarbonate (PC) because of their superior optical properties. As these plastic substrates are very temperature sensitive, the suitability for low-temperature deposition is very important. So far, ZnO could be fabricated at low temperature, and n-type ZnO growth is very mature. However, the difficulty of preparing reproducible and low-resistivity p-type ZnO has prevented ZnO from further development. The difficulty can arise from a variety of causes. Undoped ZnO shows intrinsic n-type conductivity, due to the probable impurity H [6,7]. While the intrinsic defects VO (oxygen vacancies) and Zni (interstitial zinc atoms) may not cause n-type conductivity, they will compensate the acceptor dopants during the doping process [8]. Furthermore, the acceptor dopants generally have a low solubility in ZnO [9]. It has been believed that the most promising dopant for p-type ZnO is N, because of its similar radius to O. As N is not very soluble in ZnO, several groups have attempted p-type doping of ZnO by thermally oxidizing Zn3N2 [10,11,12]. The results show that a high concentration of N can be doped into ZnO through this method, and that the highest hole concentration can reach a level of 1018 cm−3. Nevertheless, the obtained p-type ZnO films contain a high concentration of VO, resulting in poor electrical property. In addition, the reported p-type ZnO:N films prepared by thermally oxidizing Zn3N2 films require very high temperature, which makes it impossible in flexible electronics. Therefore, the reduction of VO concentration is obviously significant in p-type ZnO preparation. At the same time, searching for a low-temperature preparation method is quite meaningful.
In the photoluminescence (PL) spectra of ZnO, the broad-band emission locating in the visible region is commonly attributed to the VO-related defects [13,14]. To reduce the intensity of this peak, thermal annealing is usually adopted [15,16,17]. The mainly used annealing environment includes vacuum, oxygen, and nitrogen. Although the concentration of VO can be reduced to a certain extent, the required annealing temperatures are very high.
In this letter, we report a simple method to fabricate p-type ZnO:N films. By oxidizing Zn3N2 films in oxygen plasma, the p-type ZnO:N films were obtained at low temperature. As the energy of oxygen plasma is very high, the transformation from Zn3N2 phase to ZnO phase will happen at low temperature. Moreover, the high energy oxygen ions could access the VO sites in ZnO during the oxidizing process. As a result, the VO defects can be significantly reduced. We have investigated the optical property of ZnO:N films prepared at different temperatures. Through the room-temperature photoluminescence spectra, we discovered that the oxygen plasma is quite efficient in reducing VO defects in the ZnO:N films. Significantly, the hole concentration of film oxidized at room temperature reaches 6.22 × 1018 cm3, almost greater than the reported results that were achieved with a high temperature process.

2. Materials and Methods

2.1. Zn3N2 Films Preparation

Zn3N2 samples were grown on quartz substrates by RF (radio frequency) reactive magnetron sputtering. A Zinc disk (99.999%), Ar gas (99.999%), and N2 gas (99.999%) were used. When the background pressure was less than 6 ×10−4 Pa, the Ar and N2 were introduced into the chamber, both with the flow rate of 30 standard-state cubic centimeters per minute (SCCM). The sputtering power, pressure, sputtering time, and substrate temperature were 40 W, 5 Pa, 30 min, and 200 °C, respectively. Before sputtering, a 15 min pre-sputtering was performed to clean the surface of the zinc disk. Here we have prepared two kinds of Zn3N2 films; the difference between them is the substrate temperature—one at 200 °C and the other at room temperature. Then, the two kinds of Zn3N2 films were cut into small pieces for the next oxidizing process.

2.2. Oxidizing Process

The Zn3N2 films were oxidized in a PECVD (plasma enhanced chemical vapor deposition) system. The background vacuum was better than 2 × 10−5 mbar. The O2 gas (99.999%) was inlet with the flow rate 9.5 SCCM. The working pressure and RF power were 400 mtorr and 100 W, respectively. The temperatures during oxidation were varied from room temperature (RT) to 400 °C. The oxidation time was set to 2 h. After oxidation, the samples were naturally cooled down to RT in the vacuum.

2.3. Measurements

X-ray diffraction (XRD) was performed to characterize the structural properties of the films on an X’Pert PRO diffractometer system with Cu Kα radiation (λ = 1.54060 Å). The composition and thickness of the films were measured by non-Rutherford backscattering (non-RBS) at the NEC 9SDH-2 3 MV pelletron tandem accelerator at Fudan University (details can be found in our former report [18]). The content and local chemical states of N were investigated by high-resolution X-ray photoelectron spectroscopy (XPS) at room temperature. The binding energy scale was calibrated using the C 1s line at 284.8 eV. Hall-effect measurement was carried out on an ACCENT HL5500PC Hall system using a Van der Pauw four-point configuration. Indium (In) electrodes were deposited on the four corners of the sample by RF magnetron sputtering at room temperature. The linear I–V behavior of all the samples indicated a good Ohmic contact between the In electrodes and the film layer. The photoluminescence (PL) property was measured with a He-Cd laser source with a wavelength of 325 nm at room temperature.

3. Results and Discussion

Firstly, the as-grown Zn3N2 film grown at 200 °C and its oxidized films were investigated. The as-grown sample is labelled as 2-Zn3N2, and the oxidized films are labelled as 2-RT, 2-100, 2-200, 2-300, and 2-400, respectively. Figure 1 shows the XRD patterns of the Zn3N2 film labelled as 2-Zn3N2 and ZnO:N films. The Zn3N2 film shows two broad peaks at 36.76° and 52.98°, respectively, corresponding to (400) and (440) planes of Zn3N2 (JCPDS file 35-0762). After being oxidized in oxygen plasma, the film labelled as 2-Zn3N2 completely transformed into ZnO phase, even at RT. For the oxidized films, seven peaks emerge in the XRD patterns at 2θ = 31.80°, 34.44°, 36.30°, 47.60°, 56.63°, 62.86°, and 68.06°, which are attributed to (100), (002), (101), (102), (110), (103), and (112) planes of hexagonal wurtzite ZnO (JCPDS file 36-1451), respectively. The intensity of the ZnO (101) peak was the strongest at RT and 100 °C; it then weakened as the temperature increased. On the contrary, the intensity of ZnO (002) peak increased with the temperature and got stronger than that of the ZnO (101) peak at 200 °C. In other words, the prepared ZnO films tended to a (101) preferred orientation at RT and 100 °C, while to a (002) preferred orientation at temperatures higher than 100 °C. The growth of c-axis-oriented ZnO films was explained in terms of the low surface free energy for the (001) plane [19]. This is commonly found at high temperature. Nguyen et al. has reported that if the deposition is performed at non-equilibrium conditions (such as low temperature), another orientation can also be achieved [20]. Hence, low temperature may be responsible for the (101) preferred orientation of the 2-RT and 2-100 samples.
Figure 2 shows the non-RBS spectra of the films. By simulating the data with SIMNRA 6.0 code, we obtain the thickness and the components of the films. For all the films, the thicknesses are about 120 nm. The Zn3N2 film labelled as 2-Zn3N2 shows Zn/N ratio of 3:2, while the oxidized films all exhibit no N peak, with Zn/O ratio of 1:1. This means that the Zn3N2 and ZnO films were prepared successfully, and that the oxidation by oxygen plasma could totally change the Zn3N2 film into ZnO film, even at RT. This is the same with XRD results. In addition, we can see that the carbon contamination is inevitable in the samples because of the ex-situ oxidation process, which was demonstrated in our former report [18].
The XPS measurement was conducted to investigate the local chemical states of N atoms in the as-grown Zn3N2 film labelled as 2-Zn3N2 and ZnO:N, as shown in Figure 3. Three peaks were found in the as-grown Zn3N2 film at 395.6 eV, 397.8 eV, and 400 eV, which were assigned to Zn-N [21], N-H, and N-N bonds [22], respectively. This agrees with our previous results [18]. After being oxidized in the oxygen plasma, the Zn-N and N-H peaks disappeared, meaning that the film completely transformed into ZnO, and a new peak at 398.6 eV emerged at temperatures ranging from RT to 300 °C. This new peak is suggested to be NO (substitutional nitrogen in oxygen site in the ZnO crystalline) [12,23,24], an acceptor in N-doped ZnO film. Another new peak at 400.8 eV was associated with the characteristic N 1s→π* transition in molecular nitrogen [22]. This indicates that the molecular nitrogen is produced during the oxidizing process. The contents of N and NO of the ZnO:N films are listed in Table 1, which are obtained by simulating XPS data with Gaussian curves. At RT, the film contained 0.4 at % of N elements, among which 0.22 at % of N elements were existing as NO. As the temperature increased—except for the film oxidized at 100 °C—the total N contents in the ZnO:N films changed slightly, while the NO contents reduced and vanished at 400 °C. At 100 °C, the film had 0.23 at % of total N content—the lowest among the ZnO:N films.
The Hall-effect measurements were conducted to obtain the electricity property of the films, as shown in Table 1. Claflin et al. mentioned that the low hole mobility makes ZnO:N susceptible to mixed-conduction effects. Even weak light exposure can potentially make a significant impact on the results [25]. Here, the Hall-effect measurements were conducted in the dark at room temperature. The magnetic field was 0.35 T. The as-grown Zn3N2 film labelled as 2-Zn3N2 exhibited n-type conduction, with carrier concentration of 1.08 × 1019 cm−3. After oxidizing in the oxygen plasma, the conduction type turned into p-type at temperatures ranging from RT to 300 °C, then into n-type again at 400 °C. The processing window of the p-type ZnO:N films was much lower than that by annealing at elevated temperatures (usually higher than 400 °C) in oxygen ambient. This could be attributed to the high energy of oxygen plasma. At RT, the energy of oxygen plasma was high enough to oxidize Zn3N2 into ZnO. When the temperature rose to 400 °C, the oxygen plasma was able to push NO out of O site in the ZnO crystalline. At 100 °C, the film exhibited the lowest hole concentration. To ensure that the results are correct, we repeated the experiment. The results show that the hole concentration of the sample labelled as 2-100 was 2.23 × 1016 cm−3, almost the same as the results listed in Table 1. At RT, the film exhibited the highest hole concentration of 6.22 × 1018 cm−3, due to the highest NO concentration. As the oxidizing temperature increased, the change of the hole concentration was the same as the change of NO concentration. This means that the NO is the dominant factor in the mechanism of N-doped p-type ZnO film using this method. This is because the concentration of the oxygen vacancies (VO)—acting as the compensate center in the p-type doping ZnO—in all the ZnO:N films were reduced efficiently. This will be discussed in detail in the part of the PL results. The carrier concentration for the ZnO:N films as a function of oxidizing temperature (T) is shown in Figure 4. As we discussed in the XRD results, the ZnO:N films preferred (101) plane orientation at RT and 100 °C, and (002) plane orientation at 200 °C, 300 °C, and 400 °C. Different crystal preferential orientation might affect the results of Hall-effect. Thus, the samples were clarified into two regions by their crystal preferential orientation. In the (101) preferred orientation region, the carrier concentration reduced from 6.22 × 1018 cm−3 to 1.67 × 1016 cm−3 as the temperature increased from RT to 100 °C. In the (002) preferred orientation region, the carrier concentration reached the highest value of 3.73 × 1018 cm−3 at 200 °C; it initially decreased as the temperature increased, then was followed by the transformation of conduction type from p-type to n-type at 400 °C.
Figure 5 shows the photoluminescence spectra of the ZnO:N films. In Figure 5a, the spectra are normalized. The UV emissions of ZnO at 380 nm are quite strong to be found in all ZnO:N films. The weak broad peaks in the visible region from 450 to 700 nm are usually attributed to oxygen vacancy (VO) defects [13], acting as the donors in N-doped ZnO and compensating the effective N-acceptors. Compared with our previous work, where the Zn3N2 films were oxidized in the oxygen atmosphere, the VO defects in all films were reduced obviously, meaning that the oxygen plasma has a high enough energy to access the VO sites in the ZnO crystal. The enlarged figure of visible region (Figure 5a) shows the change of optical property with oxidizing temperature. The intensity of the VO peak decreased initially and then increased when the oxidizing temperature was higher than 200 °C. On the contrary, the intensity of the UV emissions of ZnO at 380 nm (shown in Figure 5b) firstly increased and then decreased above 200 °C of the oxidizing temperature. That is, at 200 °C, the ZnO:N film maintained the strongest UV emission and the weakest deep level emission. In addition, high oxidizing temperature might increase the VO defects, which generally happens at temperatures higher than 200 °C. In our experiments, above 200 °C, the VO defects increased with the increasing oxidizing temperature.
As we mentioned above, the Zn3N2 film could be oxidized into p-type ZnO film even at RT, but the Zn3N2 films used above were prepared at 200 °C. In order to study the possibility of preparing p-type ZnO:N films at RT from beginning to end, the following experiment was performed. Using the same method, we prepared the Zn3N2 film at RT (labeled as RT-Zn3N2), then oxidized it in oxygen plasma atmosphere at RT (the oxidized sample is labeled as RT-RT). All the other experiment parameters were the same as before. The XRD patterns (Figure 6) show that the crystallinity of the Zn3N2 film deposited at RT (labelled as RT-Zn3N2) was not better than that of the Zn3N2 film deposited at 200 °C (labelled as 2-Zn3N2). However, after oxidizing in the oxygen plasma at RT, the Zn3N2 film deposited at RT also totally transformed into hexagonal wurtzite ZnO phase, with a (101) plane preferred orientation. From the photoluminescence spectra (Figure 7), we can also see the strong UV emission and the weak VO defects peak. The electricity property of the RT-RT sample was also measured by Hall Effect, with resistivity of 7.67 × 104 Ω∙cm and hole concentration of 1.81 × 1016 cm−3, which are not better than that of the 2-RT sample. E. Kaminska et al. suggested that a number of factors need to be considered in optimizing the technological procedure to obtain a high quality p-type ZnO [26]. This includes the microstructure of Zn3N2 and its potential contamination with hydrogen, the crystalline structure of the substrate, and the temperature and time of thermal processing. It was also mentioned that the microstructure of Zn3N2 was sensitive to the partial pressure of the nitrogen gas during deposition. In our experiments, the only difference between the two samples RT-RT and 2-RT was the deposited temperature of Zn3N2—one was at room temperature, another was at 200 °C. Obviously, the deposited temperature affects the microstructure of Zn3N2. To get good microstructure of Zn3N2 at room temperature, according to above suggestion, changing the partial pressure of the nitrogen gas during deposition might be an effective choice in further experiments. Therefore, oxidizing Zn3N2 with oxygen plasma is an efficient method to reduce the VO in N-doped ZnO films. In addition, the preparation of p-type ZnO:N film could be realized at low temperature, even at RT.

4. Conclusions

In this letter, we report a simple method to prepare p-type ZnO:N films. By oxidizing Zn3N2 films in oxygen plasma atmosphere, the p-type N doped ZnO films were obtained at low temperature. The results show that:
(1)
p-type N-doped ZnO films can be prepared by oxidizing Zn3N2 films in oxygen plasma atmosphere. Even at room temperature, the Zn3N2 film completely transformed into hexagonal wurtzite ZnO, with a hole concentration of 6.22 × 1018 cm−3 and a resistivity of 39.47 Ω∙cm.
(2)
The Zn3N2 film prepared at room temperature could also be oxidized into p-type ZnO film in oxygen plasma atmosphere, but with a poor electrical property.
(3)
The contents of NO in the ZnO:N films decreased with the increasing oxidizing temperature, but exhibited the lowest value at 100 °C.
(4)
The oxidizing process in oxygen plasma could significantly reduce the VO defects in the ZnO:N films. The film obtained at 200 °C had the lowest value of VO defects and the strongest UV emission.
(5)
The oxidizing temperature did not always act as a positive factor in reducing the VO defects in the preparation of ZnO:N films. When the temperature was higher than 200 °C, the concentration of VO defects increased with the increasing temperature.

Acknowledgments

This work is supported by the National Natural Science Foundation of China (Grant Nos. 10775033 and 11075038).

Author Contributions

Yuping Jin and Bin Zhang conceived and designed the experiments; Yuping Jin and Nuannuan Zhang performed the experiments; Yuping Jin and Bin Zhang analyzed the data; Yuping Jin and Nuannuan Zhang wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Fortunato, E.M.; Pimentel, A.; Gonçalves, A.; Marques, A.; Pereira, L.; Martins, R. Fully transparent ZnO thin-film transistor produced at room temperature. Adv. Mater. 2005, 17, 590–594. [Google Scholar] [CrossRef]
  2. Tsukazaki, A.; Ohtomo, A.; Onuma, T.; Ohtani, M.; Makino, T.; Sumiya, M.; Ohtani, K.; Chichibu, S.F.; Fuke, S.; Segawa, Y.; et al. Repeated temperature modulation epitaxy for p-type doping and light-emitting diode based on ZnO. Nat. Mater. 2005, 4, 42–46. [Google Scholar] [CrossRef]
  3. Janotti, A.; van de Walle, C.G. Fundamentals of zinc oxide as a semiconductor. Rep. Prog. Phys. 2009, 72, 126501. [Google Scholar] [CrossRef]
  4. Fortunato, E.; Barquinha, P.; Martins, R. Oxide semiconductor thin-film transistors: A review of recent advances. Adv. Mater. 2012, 24, 2945–2986. [Google Scholar] [CrossRef] [PubMed]
  5. Sirringhaus, H. 25th Anniversary article: Organic field-effect transistors: The path beyond amorphous silicon. Adv. Mater. 2014, 26, 1319–1335. [Google Scholar] [CrossRef] [PubMed]
  6. Hofmann, D.M.; Hofstaetter, A.; Leiter, F.; Zhou, H.; Henecker, F.; Meyer, B.K.; Orlinskii, S.B.; Schmidt, J.; Baranov, P.G. Hydrogen: A relevant shallow donor in zinc oxide. Phys. Rev. Lett. 2002, 88, 045504. [Google Scholar] [CrossRef] [PubMed]
  7. Van de Walle, C.G. Hydrogen as a cause of doping in zinc oxide. Phys. Rev. Lett. 2000, 85, 1012. [Google Scholar] [CrossRef] [PubMed]
  8. Janotti, A.; Van de Walle, C.G. Native point defects in ZnO. Phys. Rev. B 2007, 76, 165202. [Google Scholar] [CrossRef]
  9. Kobayashi, A.; Sankey, O.F.; Dow, J.D. Deep energy levels of defects in the wurtzite semiconductors AIN, CdS, CdSe, ZnS, and ZnO. Phys. Rev. B 1983, 28, 946. [Google Scholar] [CrossRef]
  10. Li, B.; Liu, Y.; Zhi, Z.; Shen, D.; Lu, Y.; Zhang, J.; Fan, X.; Mu, R.; Henderson, D.O. Optical properties and electrical characterization of p-type ZnO thin films prepared by thermally oxiding Zn3N2 thin films. J. Mater. Res. 2003, 18, 8–13. [Google Scholar] [CrossRef]
  11. Nakano, Y.; Morikawa, T.; Ohwaki, T.; Taga, Y. Electrical characterization of p-type N-doped ZnO films prepared by thermal oxidation of sputtered Zn3N2 films. Appl. Phys. Lett. 2006, 88, 2103. [Google Scholar] [CrossRef]
  12. Bin, Z.; Min, L.; Jian-Zhong, W.; Li-Qun, S. P-type ZnO: N films prepared by thermal oxidation of Zn3N2. Chin. Phys. Lett. 2013, 30, 027303. [Google Scholar]
  13. Wu, X.; Siu, G.; Fu, C.; Ong, H. Photoluminescence and cathodoluminescence studies of stoichiometric and oxygen-deficient ZnO films. Appl. Phys. Lett. 2001, 78, 2285–2287. [Google Scholar] [CrossRef]
  14. Panigrahy, B.; Aslam, M.; Misra, D.S.; Ghosh, M.; Bahadur, D. Defect-related emissions and magnetization properties of ZnO nanorods. Adv. Funct. Mater. 2010, 20, 1161–1165. [Google Scholar] [CrossRef]
  15. Yang, Y.; Yan, H.; Fu, Z.; Yang, B.; Xia, L.; Xu, Y.; Zuo, J.; Li, F. Photoluminescence and Raman studies of electrochemically as-grown and annealed ZnO films. Solid State Commun. 2006, 138, 521–525. [Google Scholar] [CrossRef]
  16. Lee, J.; Chung, J.; Lim, S. Improvement of optical properties of post-annealed ZnO nanorods. Phys. E Low-Dimens. Syst. Nanostruct. 2010, 42, 2143–2146. [Google Scholar] [CrossRef]
  17. Cui, L.; Zhang, H.-Y.; Wang, G.-G.; Yang, F.-X.; Kuang, X.-P.; Sun, R.; Han, J.-C. Effect of annealing temperature and annealing atmosphere on the structure and optical properties of ZnO thin films on sapphire (0001) substrates by magnetron sputtering. Appl. Surf. Sci. 2012, 258, 2479–2485. [Google Scholar] [CrossRef]
  18. Jin, Y.-P.; Zhang, B.; Wang, J.-Z.; Shi, L.-Q. P-type nitrogen-doped ZnO films prepared by in-situ thermal oxidation of Zn3N2 films. Chin. Phys. Lett. 2016, 33, 058101. [Google Scholar] [CrossRef]
  19. Fujimura, N.; Nishihara, T.; Goto, S.; Xu, J.; Ito, T. Control of preferred orientation for ZnOx films: Control of self-texture. J. Cryst. Growth 1993, 130, 269–279. [Google Scholar] [CrossRef]
  20. Nguyen, H.T.; Andreas, J.H.; Lamb, R.N. Structural order of nanocrystalline ZnO film. J. Phys. Chem. B 1999, 103, 4264–4268. [Google Scholar]
  21. Futsuhara, M.; Yoshioka, K.; Takai, O. Structural, electrical and optical properties of zinc nitride thin films prepared by reactive rf magnetron sputtering. Thin Solid Films 1998, 322, 274–281. [Google Scholar] [CrossRef]
  22. Petravic, M.; Deenapanray, P.; Coleman, V.A.; Jagadish, C.; Kim, K.-J.; Kim, B.; Koike, K.; Sasa, S.; Inoue, M.; Yano, M. Chemical states of nitrogen in ZnO studied by near-edge X-ray absorption fine structure and core-level photoemission spectroscopies. Surf. Sci. 2006, 600, L81–L85. [Google Scholar] [CrossRef]
  23. Jiao, S.; Zhang, Z.; Lu, Y.; Shen, D.; Yao, B.; Zhang, J.; Li, B.; Zhao, D.; Fan, X.; Tang, Z. ZnO pn junction light-emitting diodes fabricated on sapphire substrates. Appl. Phys. Lett. 2006, 88, 031911. [Google Scholar] [CrossRef]
  24. Nie, X.; Zhang, B.; Wang, J.; Shi, L.; Di, Z.; Guo, Q. Room-temperature ferromagnetism in p-type nitrogen-doped ZnO films. Mater. Lett. 2015, 161, 355–359. [Google Scholar] [CrossRef]
  25. Claflin, B.; Look, D.C.; Park, S.J.; Cantwell, G. Persistent n-type photoconductivity in p-type ZnO. J. Cryst. Growth 2006, 287, 16–22. [Google Scholar] [CrossRef]
  26. Kaminska, E.; Piotrowska, A.; Kossut, J.; Barcz, A.; Butkute, R.; Dobrowolski, W.; Dynowska, E.; Jakiela, R.; Przezdziecka, E.; Lukasiewicz, R.; et al. Transparent p-type ZnO films obtained by oxidation of sputter-deposited Zn3N2. Solid State Commun. 2005, 135, 11–15. [Google Scholar] [CrossRef]
Figure 1. XRD patterns of as-grown 2-Zn3N2 film and ZnO:N films (labels 2-Zn3N2 and 2-RT/2-100/2-200/2-300/2-400 means that the Zn3N2 film was grown at 200 °C and that the oxidizing temperatures are room temperature (RT), 100 °C, 200 °C, 300 °C, and 400 °C, respectively).
Figure 1. XRD patterns of as-grown 2-Zn3N2 film and ZnO:N films (labels 2-Zn3N2 and 2-RT/2-100/2-200/2-300/2-400 means that the Zn3N2 film was grown at 200 °C and that the oxidizing temperatures are room temperature (RT), 100 °C, 200 °C, 300 °C, and 400 °C, respectively).
Materials 10 00236 g001
Figure 2. Non-Rutherford backscattering (non-RBS) spectra of as-grown 2-Zn3N2 film and ZnO:N films.
Figure 2. Non-Rutherford backscattering (non-RBS) spectra of as-grown 2-Zn3N2 film and ZnO:N films.
Materials 10 00236 g002
Figure 3. N 1s core-level X-ray photoelectron spectroscopy (XPS) spectra of as-grown 2-Zn3N2 film and ZnO:N films.
Figure 3. N 1s core-level X-ray photoelectron spectroscopy (XPS) spectra of as-grown 2-Zn3N2 film and ZnO:N films.
Materials 10 00236 g003
Figure 4. Carrier concentration for the ZnO:N films as a function of oxidizing temperature (T). Samples are classified by their crystal preferential orientation.
Figure 4. Carrier concentration for the ZnO:N films as a function of oxidizing temperature (T). Samples are classified by their crystal preferential orientation.
Materials 10 00236 g004
Figure 5. (a) Normalized photoluminescence spectra of ZnO:N films. The inset shows the enlarged photoluminescence spectra of ZnO:N films in the visual region; (b) Intensity of near-band emission peaks.
Figure 5. (a) Normalized photoluminescence spectra of ZnO:N films. The inset shows the enlarged photoluminescence spectra of ZnO:N films in the visual region; (b) Intensity of near-band emission peaks.
Materials 10 00236 g005
Figure 6. XRD patterns of Zn3N2 film grown at room temperature (labelled as RT-Zn3N2), and the ZnO:N film prepared by oxidizing RT-Zn3N2 at room temperature in the oxygen plasma atmosphere (labelled as RT-RT).
Figure 6. XRD patterns of Zn3N2 film grown at room temperature (labelled as RT-Zn3N2), and the ZnO:N film prepared by oxidizing RT-Zn3N2 at room temperature in the oxygen plasma atmosphere (labelled as RT-RT).
Materials 10 00236 g006
Figure 7. Normalized photoluminescence (PL) spectra of ZnO:N film prepared by oxidizing Zn3N2 film grown at RT. The insert shows the enlargement of the visible region.
Figure 7. Normalized photoluminescence (PL) spectra of ZnO:N film prepared by oxidizing Zn3N2 film grown at RT. The insert shows the enlargement of the visible region.
Materials 10 00236 g007
Table 1. The electricity property of the as-grown 2-Zn3N2 and oxidized ZnO:N films.
Table 1. The electricity property of the as-grown 2-Zn3N2 and oxidized ZnO:N films.
SamplesN (at %)NO (at %)Resistivity (Ω∙cm)Hall Mobility (cm2·V−1·s−1)Carrier Concentration (cm−3)Type
2-Zn3N2----1.56 × 10−237.00−1.08 × 1019n
2-RT0.400.2239.470.036.22 × 1018p
2-1000.230.041.59 × 1030.241.67 × 1016p
2-2000.390.1496.920.023.73 × 1018p
2-3000.430.072.57 × 1020.151.60 × 1017p
2-4000.43--26.890.42−5.55 × 1017n

Share and Cite

MDPI and ACS Style

Jin, Y.; Zhang, N.; Zhang, B. Fabrication of p-Type ZnO:N Films by Oxidizing Zn3N2 Films in Oxygen Plasma at Low Temperature. Materials 2017, 10, 236. https://doi.org/10.3390/ma10030236

AMA Style

Jin Y, Zhang N, Zhang B. Fabrication of p-Type ZnO:N Films by Oxidizing Zn3N2 Films in Oxygen Plasma at Low Temperature. Materials. 2017; 10(3):236. https://doi.org/10.3390/ma10030236

Chicago/Turabian Style

Jin, Yuping, Nuannuan Zhang, and Bin Zhang. 2017. "Fabrication of p-Type ZnO:N Films by Oxidizing Zn3N2 Films in Oxygen Plasma at Low Temperature" Materials 10, no. 3: 236. https://doi.org/10.3390/ma10030236

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.