In Situ TEM Study of Microstructure Evolution of Zr-Nb-Fe Alloy Irradiated by 800 keV Kr2+ Ions

College of Energy, Xiamen University, Xiamen 361102, Fujian, China
*
Author to whom correspondence should be addressed.
Materials 2017, 10(4), 437; https://doi.org/10.3390/ma10040437
Submission received: 19 March 2017 / Revised: 15 April 2017 / Accepted: 20 April 2017 / Published: 22 April 2017

Abstract

:
The microstructure evolution of Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni zirconium alloy, irradiated by 800 keV Kr2+ ions at 585 K using the IVEM-Tandem Facility at Argonne National Laboratory, was observed by in situ transmission electron microscopy. A number of β-Nb precipitates with a body-centered cubic (BCC) structure were distributed in the as-received zirconium alloy with micrometer-size grains. Kr2+ ion irradiation induced the growth of β-Nb precipitates, which could be attributed to the segregation of the dissolved niobium atoms in the zirconium lattice and the migration to the existing precipitates. The size of precipitates was increased with increasing Kr2+ ion fluence. During Kr2+ iron irradiation, the zirconium crystals without Nb precipitates tended to transform to the nanocrystals, which was not observed in the zirconium crystals with Nb nanoparticles. The existing Nb nanoparticles were the key factor that constrained the nanocrystallization of zirconium crystals. The thickness of the formed Zr-nanocrystal layer was about 300 nm, which was consistent with the depth of Kr2+ iron irradiation. The mechanism of the precipitate growth and the formation of zirconium nanocrystal was analyzed and discussed.

Graphical Abstract

1. Introduction

Zirconium alloys are used as fuel cladding tubes and structural materials in water-cooled nuclear reactors due to their low thermal neutron absorption cross section, excellent resistance to corrosion, remarkable resistance to irradiation-induced swelling and creep, and adequate mechanical properties [1]. Along with increased fuel burnup and extended reload cycle of fuel assembly, zero tolerance on nuclear accidents requires further improvement of the properties and performance of zirconium alloy fuel cladding. In recent years, various new zirconium alloys have been designed and developed in China, USA and Europe [2]. In the recent accident tolerant fuel (ATF) project, new types of zirconium alloys with better comprehensive properties and performance are called as safer fuel cladding materials [3]. One of the most important approaches used in improving properties and performance of zirconium alloys is the changing concentrations of alloying elements, such as Nb, Sn, Cu, Fe, etc. [4]. N36 zirconium alloy with Zr-1Sn-1Nb-0.3Fe was developed in China. The material shows a higher performance than Zr-4 alloy [5]. In order to further improve comprehensive performance of zirconium alloys, a new type of zirconium alloy with the composition of Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni is developed in the present work.
In service, zirconium alloys will be subjected to not only X-rays and neutrons, but also significant ion fluxes that vary in type, nature, energy, and intensity. Therefore, it is important to investigate the irradiation behavior of zirconium alloys, especially for a new zirconium alloy before using it in commercial nuclear reactors. The irradiation with high energetic particles will induce the degradation of properties and performance including irradiation hardening, embrittlement, and swelling. These irradiation-induced damages originate from the microstructure changes such as amorphization, nanocrystallization, particle dissolution or precipitation, formation of dislocation, and voids. Knowledge of the microstructure evolution under irradiation is important for predicting in-service behaviors of zirconium alloy components.
In the past several decades, the irradiation behaviors of zirconium alloys have been widely investigated [5,6,7,8,9,10,11,12,13]. The main investigations conducted so far including the following: (i) phase changes, nanocrystallization, and amorphization [5,6]; (ii) particle dissolution or precipitation [7]; (iii) the effect of chemical composition and preparation technology on the irradiation behaviors [8,9]; (iv) helium behaviors in zirconium alloys [10]; (v) dislocation formation and characteristic [11]; (vi) post-irradiation corrosion behaviors [12]; (vii) computer simulation such as molecular dynamics for irradiation behaviors [13]. In addition, the microhardness obtained by nanoindenter is an important method for characterizing the mechanical properties before and after ion irradiation because of the limited irradiation depth. The nanoindentation is widely used in thin film metallic glass [14,15] and ion irradiated samples [16]. However, there are still some questions that need to be addressed and answered, such as the irradiation-induced growth behavior of precipitates, the amorphization mechanism of zirconium crystals.
The new type of zirconium alloy with the composition of Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni is developed on the basis of N36 zirconium alloy by means of adding the chemical content of elemental Ni, Fe, and Cu, and eliminating elemental Sn. Elemental Cu and Fe can increase mechanical strength and corrosion resistance [17]. Elemental Nb can enhance corrosion and irradiation-induced swelling resistance [17,18,19]. Although elemental Sn can improve creep resistance, it decreases corrosion resistance [18]. Liu [20,21] reported a zirconium alloy with uniform distribution of fine β-Nb particles containing iron element had high corrosion resistance. Nb atoms were easily dissolved into zirconium lattice, but the formation of precipitates containing Nb would reduce the amount of Nb presenting as a solid solution in the α-Zr crystal structure [22]. Irradiation is likely to accelerate precipitate dissolution or coarsening, prompt phase transformation, and induce new phase formation [7]. The redistribution of microalloying elements was observed under irradiation. Perovic [23] reported that ion irradiation induced the redistribution of alloy elements, the desolvation of elemental Nb from β-Nb precipitates, and the increase in solid solution ability of alloying elements in zirconium matrix. Shishov [24,25] presented a similar result of Zr-Nb-Sn-Fe alloys. Meanwhile, during neutron irradiation, the elemental Fe depleted from β-Nb precipitates and some precipitates enriched with Nb atoms were formed. However, Sylvie Doriot [26] reported the diameter of β-Nb particles increased with irradiation dose, while their number density did not exhibit a significant decrease. For the highest dose (13.1 × 1025 n/m2), the measured particle density in M5 appeared to decrease. Kai [27] reported the dissolution of ZrFe2 precipitates, the transformation of Zr(Fe,Cr)2 precipitates from hcp to fcc structure, and the nucleation and growth of Zr4Sn precipitates in a Zr-4 alloy irradiated by proton with ion dose up to 1 dpa at 623 K. The different research results in Ref. [23,24,25,26,27] could be due to the irradiation experiment conditions (such as irradiated by 3.58 × 1024 n/m2 at 583 K for 52 days in-reactor [23], under BOR-60 irradiation with E > 0.1 MeV at different temperature [24] and 1 MeV H+ irradiation at 350 °C up to a total dose of 1 dpa [27]) and the chemical compositions (such as Zr-2.5%Nb [23], upgraded Zr-1%Nb and Zr-1%Nb-0.35%Fe-1.2%Sn [25], and Zr-1.53%Sn-0.22%Fe-0.11%Cr [27]). However, some scientific questions related to the irradiation behaviors of precipitates in zirconium alloys needed to be further investigated.
Moreover, most of the irradiation experiments and subsequent microstructure analysis in the previous studies were carried out in separate steps and did not reflect irradiation behaviors of zirconium alloys in real time and space. In situ transmission electron microscopy (TEM) observation under ion irradiation is a very useful technique to study mechanisms of damage accumulation and reveal the progressive microstructure changes, which is not only important for understanding the fundamentals of irradiation damage but also important for obtaining irradiation damage data in real time and space to establish basic irradiation rules that can be used to estimate in-service irradiation life of a new zirconium alloy with Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni. Although the physical mechanism of ion irradiation is different with that of neutron irradiation, the same microstructural characteristics such as the distribution and size of dislocation loops and voids in the matrix, and the chemical composition segregation at the grain boundary, will be obtained during ion irradiation [28,29]. Meanwhile, there is a test standard ASTM E521-1996 (Reapproved 2009) “Standard practice for neutron radiation damage simulation by charged-particle irradiation” [30]. Therefore, it is effective to use ion irradiation to simulate neutron irradiation effect.
To understand the microstructure evolution and precipitate behaviors of Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni zirconium alloy during krypton ion irradiation, an in situ irradiation experiment was carried out in the IVEM-Tandem facility. In this study, an 800 keV Kr2+ ion beam was used to (1) simulate heavy particle irradiation effect; and (2) simulate gas bubble behaviors. The mechanisms of precipitate evolution and the nanocrystallization of zirconium crystal were analyzed and discussed.

2. Experimental Methods

The zirconium alloy with Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni (wt %) chemical composition, which came from a fuel cladding tube, was used in the present work. The sheet sample of 10 × 3 × 0.5 mm3 in dimensions was first cut from as-received cladding tube by a precision diamond knife-cutting machine and then ground to less than 100 μm in thickness by SiC sandpaper. After that, the samples with 3 mm in diameter were obtained by a hole-punching machine. Both sides of each sample were ground using SiC sandpaper from 240 to 5000 grit and then polished using 1 μm diamond paste. After thinning the thickness to about 30 μm, the samples were twin-jet electropolished using a mixed solution with 60 mL of HClO4, 350 mL of 2-butoxyethanaol, and 590 mL of methanol to perforation for TEM observations. After twin-jet electropolishing, the thickness of TEM sample with 3 mm in diameter was about 100 nm near the perforation position and was about 30 μm near the edge of TEM sample. The sample thickness continuously changed from 30 μm near the edge to 100 nm near the perforation position. Therefore, during ion irradiation, the region monitored by in situ TEM was located near the perforation position (about 100 nm in thickness). After ion irradiation, the region for preparing the cross-sectional specimen in the ion-irradiated TEM sample was located near the edge (about 30 μm thickness). Ex situ TEM and HRTEM were carried out in a JEM 3011 electron microscope (JEOL, Tokyo, Japan) with 300 keV of electron voltage.
Ion irradiations were conducted at 585 K with 800 keV Kr2+ using the IVEM-Tandem Facility (National Electrostatics Corp., Middleton, WI, USA) at Argonne National Laboratory, USA. The sample temperature was provided and controlled by a Gatan TEM sample holder. The facility consists of a modified H-9000 electron microscope that is interfaced to a 650 KV NEC ion accelerator. The microstructure evolution was monitored in situ during ion irradiation using a 300 keV electron beam.
The Kr-ion flux was kept at 6.25 × 1015 Kr2+ ions/m2·s to prevent excessive beam heating. The depth distribution of implanted Kr2+ ions and displacement damage was simulated using the Stopping and Range of Ions in Matter (SRIM) code in quick Kinchin-Pease mode (SRIM.EXE, (C) 1984–2013, James F. Ziegler, Annapolis, MD, USA). The atom displacement threshold energy (Ed) of zirconium was designed to be 40 eV. The SRIM simulation of 800 keV Kr2+ into zirconium alloy indicated a peak value of 0.0078 atom % Kr ion concentration at a 280 nm depth after irradiation with 1.0 × 1018 Kr2+ ions/m2 fluence (equivalent to 1.0 Kr2+/nm2), as indicated by the dash line in Figure 1. The peak displacement damage at a 160 nm depth was 0.313 dpa after irradiation with 1.0 × 1018 Kr2+ ions/m2 fluence, as indicated by the full line in Figure 1. Multiplying these value by the implanted ion fluence gave the peak atomic density of implanted Kr and the peak displacement damage. In the present work, the total Kr2+ ion fluence was set as 1.7 × 1020 Kr2+ ions/m2, so the calculated peak value of displacement damage and Kr2+ ion concentration in Zr alloy were 53 dpa and 1.33 atom %, respectively. The displacement damage of zirconium alloy fuel cladding is approximately 10 dpa at water-cooled nuclear reactors. Along with increased fuel burnup and extended reload cycle of fuel assembly, and zero tolerance on nuclear accidents, zirconium alloy fuel cladding needs to be kept a stable ability at high displacement damage, even under a severe nuclear accident. Therefore, in the present work, the high displacement damage (53 dpa) was designed and carried out for this new type of zirconium alloy.

3. Results and Discussion

3.1. Microstructure Analysis of As-Received Alloy

The bright field TEM images of zirconium alloy before ion irradiation are shown in Figure 2. The size of zirconium crystal is above one micron. The insert image located at the top left in Figure 2a is a selected area electron diffraction (SAED) pattern of the zirconium matrix along the [1,2,3,4,5,6,7,8,9,10] crystal orientation. According to equilibrium phase diagram of Zr-Nb alloy, the thermally stable status of a binary zirconium alloy with a few percent of Nb is the solid solution of Nb in the α-Zr matrix when the temperature is below the monotectoid reaction temperature [31]. Niobium will precipitate as a β phase in the α-Zr grain matrix. According to TEM observation, the precipitates do not uniformly distribute in the zirconium matrix as illustrated by Figure 2a,b. The total volume fraction of the precipitates measured according to the bright field TEM images is about 4.0%, which is close to the value obtained by Nikulina [32], who measured the total volume fraction of precipitates at about 3~3.5% in Zr-1%Sn-1%Nb-0.4%Fe alloy.
Most of the precipitates have a roughly spherical shape with diameters mostly in the range of 30 to 60 nm although the diameters of a few precipitates are up to 100 nm. Quantitative analysis was conducted in a Climax Image Analysis system to obtain the roundness and sphericity of precipitates used to describe the precipitate shape. Roundness is a measurement of the length/width relationship, with values in the range 0–1.0. A perfect circle has a roundness of 1.0, while a needle shaped object has a roundness close to 0. Intuitively, the roundness is a comparison between the “strength” of the major axis and the “strength” of the minor axis. Roundness = 4 A/(πLL), where A is the area of the precipitate, and L is precipitate length. Sphericity is equal to 4 πA/P2, where P is perimeter of precipitate. According to bright field TEM images, the statistic results show that the roundness and sphericity of the precipitates are about 0.90 and 0.91, respectively. The measurement error for a precipitate is less than 3%. The count number for quantitative analysis is over 30. Therefore, the effect of slightly bending and tilting the sample on both the shape and the size of the precipitates is small.
The typical EDS results of the precipitate is shown in Figure 2c. Only zirconium peaks coming from the alloy matrix and niobium peaks coming from the nanoparticle can be observed in the EDS. Similar EDS results are obtained at several other nanoparticles. It can be concluded that most nanoparticles in the zirconium alloy matrix are β-Nb precipitates with a globular shape.

3.2. Precipitate Growth

Irradiation of multi-component alloy by high energetic ions will lead to the change of phase microstructure such as the nucleation and growth of precipitates because of the enhancement of atomic mobility [26]. The morphology evolution of niobium nanoparticles with increasing of irradiation damage is shown in Figure 3. In the monitored area, the size of niobium particle is increased with increasing Kr2+ ion fluence. The size of Particle A is increased from 78 nm to 85 nm, 96 nm and 123 nm after irradiation with Kr2+ ion fluence from 1.35 × 1019 Kr2+/m2 to 2.7 × 1019 Kr2+/m2, 5.4 × 1019 Kr2+/m2, and 1.7 × 1020 Kr2+/m2, respectively. Obviously, the size of Precipitate A is increased with increasing Kr2+ ion fluence. Certainly, if the foil is hardly bent, the diffraction contrast may influence the observation of precipitates and further influence the size measurement of the precipitates. However, in the present work, the effect of diffraction contrast on size measurement was small when the foil was slightly bent during ion bombardment because the edge of Precipitate A is always sharp, as shown in Figure 3. Moreover, the roundness and sphericity of the precipitates are about 0.90 and 0.91, respectively, before ion irradiation according to the statistical results. The ion-irradiation-induced bend of foil also hardly changes the shape and size of the precipitates. In fact, from Figure 3a to Figure 3d, the distances between the center of Precipitate A and the center of Precipitate B are the same, do1 = do2 = do3 = do4 = 490 nm and the distances between the center of Precipitate A and the center of Precipitate C are also the same, dk1 = dk3 = dk4 = 310 nm, which indicates that the monitored area of the foil in the present work is not substantially more bent. Therefore, the size increment of the precipitate comes from the growth of precipitate induced by ion irradiation.
Like Precipitate A, the size of Precipitate B is increased from 62 nm to 69 nm, 74 nm, and 89 nm after irradiation with Kr2+ ion fluence from 1.35 × 1019 Kr2+/m2 to 2.7 × 1019 Kr2+/m2, 5.4 × 1019 Kr2+/m2, and 1.7 × 1020 Kr2+/m2, respectively. Our results are different from that reported in the reference. The size, distribution, and total concentration of the precipitates were almost kept constant before and after neutron irradiation [32]. The difference may be due to the different chemical composition and the incredibly different irradiation conditions. The chemical composition was Zr-1%Sn-1%Nb-0.4Fe, and their main experiment conditions were neutron irradiation up to 4.1 × 1026 nm−2 (E > 0.1 MeV) at 300 to 350 °C [32]. Wan [33] reported that the growth of precipitates was closely related to the atomic diffusion process. The irradiation-induced defects could accelerate the diffusion of solute atoms and promoted the growth of precipitates.
Ion irradiation causes alloying element redistribution. The irradiation-induced defects accelerate the movement of alloying atoms to the precipitates and makes them grow [34]. Nucleation will induce the change of free energy (∆G), including volume free energy (∆GV) and surface free energy (∆GS). When the crystal nucleus of fresh precipitate is formed at the previous precipitates in the zirconium alloy, the total change of free energy can be expressed as Δ G = ( 4 3 π r 3 Δ G V + 4 π r 2 σ α L ) ( 2 3 c o s θ + c o s 3 θ 4 ) , where r is the radius of spherical crystal nucleus, and θ is the contact angle, ranging from 0 to 180°. If θ = 0°, the nucleation energy is equal to zero, which indicates that the precipitated Nb atoms freely occupy the lattice position of previous precipitates. Therefore, the nucleation energy of the precipitated Nb atoms attaching at previous precipitates is obviously lower than that of fresh precipitate formed independently in the zirconium matrix, which is the reason for precipitate growth.
The solid solution of elemental Nb is decreased in the zirconium alloy matrix with increasing Kr2+ ion fluence. The growth rate of Nb precipitates depends on the concentration of elemental Nb in the zirconium lattice and the irradiation conditions. The growth rate will increase first and then decrease because of the limited Nb content in the zirconium lattice. When the chemical potential gradient ( μ / x ) of elemental Nb in the precipitates and zirconium lattice is equal, the precipitates can stop growing. The chemical potential (μi) is related with the Gibbs free energy of i atom, μ i = ( G n i ) . ni is the atom numbers of the i component. Ion irradiation will change the Gibbs free energy of elemental Nb in the zirconium alloy matrix and can induce the uphill diffusion of niobium. The diffusion coefficient of elemental Nb can be written as D = k T B i ( 1 + l n r i l n x i ) , where Bi is the migration rate of elemental Nb; T is the temperature; k is the coefficient; ri is the activity coefficient; x i = ρ i / ρ . ρi is the concentration of elemental Nb in the alloy matrix, which would be decreased by the ion irradiation. Although the irradiation experiment was carried out at 585 K, the growth of Nb precipitates may be mainly induced by Kr2+ ion irradiation and less by the thermal effect because no fresh precipitates can be detected after aging for 1500 h at 770 K [35].
Quantitative measurement was conducted according to pixel resolution in a Photoshop software to obtain precipitate diameter at different ion irradiation conditions. The error value is less than 3%. The relationship between the size of the precipitate and Kr2+ ion fluence is shown in Figure 4. It can be seen that the size of the precipitate is increased with increasing Kr2+ ion fluence. The growth rate is large in the initial stage and will decrease to zero when the chemical potential gradient of elemental Nb in the precipitates and alloy matrix is equal.

3.3. Nanocrystallization

The irradiation-induced dislocation walls will induce the formation of low-angle grain boundary in the microsize grain [36]. With increasing Kr2+ ion fluence, the zirconium grains with a micrometer size will be transformed into nanograins. Figure 5 shows the microstructure of zirconium alloy irradiated by 800 keV Kr2+ ion irradiation with a fluence of 1.7 × 1020 Kr2+/m2 at 585 K. Figure 5a indicates the sketch of the ion-irradiated TEM sample prepared by twin-jet electropolishing, the monitored region during Kr2+ ion irradiation, and the location of the FIB-prepared cross-section specimen in the ion-irradiated TEM sample after Kr2+ ion irradiation.
In order to observe the distribution characteristic of the microstructure along with the irradiation depth, the cross-sectional “TEM specimen” was prepared using the focused ion beam (FIB) “lift-out” technique covering a region that extended to areas far away from the irradiated surface as indicated by the white arrow in Figure 5a. The bright field TEM image of the cross-sectional microstructure of the irradiated sample is shown in Figure 5b. The direction of ion incidence, irradiated sample surface, and Pt coating are marked in a TEM image. The most severe problem is the damage layer produced as a result of the bombardment by highly accelerated gallium ion beams during FIB preparation [37]. The thickness of the damage layer with voids, dislocation, point defects, and amorphization is from several to tens of nanometers, which is decided by the preparation parameters such as the ion voltage and current, the ion incident angle, and the operation level of the experimenter. The damage layer induced by FIB will affect the quality of TEM images and interfere with the analysis. In order to decrease the thickness of the damage layer as far as possible, in the present work, a glancing angle of about 0.5° to 1°, a final beam current of 10 pA, and a beam voltage of 5 keV were used to clean the specimen surface, which significantly reduced the damage depth. The principal drawback of a 5 keV ion beam is that the etching rate and the resolution are lowered. The use of the 5 keV beam was be restricted to final milling. Meanwhile, in the present work, the beam voltage and current of Kr2+ ion irradiation in the IVEM-Tandem Facility are much higher than those of Ga+ ion during FIB preparation. Therefore, the effect of FIB damage on microstructural analysis can be neglected, and the analysis of the microstructure shown in Figure 5b is effective. The distribution band of nanocrystals under the irradiated surface can be seen. The width of the nanocrystal band (300 nm) is the same as the value calculated by SRIM software. The insert image located at the top right corner in Figure 5b is the SAED pattern of the zirconium matrix, which is typical nanocrystal diffraction pattern. Figure 5c is a dark field TEM image showing the plan-view microstructure of the irradiated sample, which has some characteristic microstructures with nanoscale. The insert image located at the left bottom in Figure 5c also shows nanocrystal diffraction rings. The high resolution TEM image of the plan-view microstructure is shown in Figure 5d.
Several theories were developed to describe phase-stability loss under irradiation [31,38,39,40]. The mechanism involves irradiation mixing, irradiation-enhanced diffusion, and irradiation-induced segregation. The irradiation-enhanced diffusion is controlled by the migration of non-equilibrium point defects (PD), vacancies and interstitial atoms due to ion irradiation. The irradiation-induced segregation is caused by the coupling of PD fluxes with the fluxes of alloying elements [31]. From in situ TEM observation, the zirconium grain with large amount of niobium particles was difficultly changed to Nano grain as shown in Figure 3. However, the zirconium grain without niobium nanoparticle was easily transferred to nanograin as show in Figure 5. This indicated that the Nb nanoparticles were the key factor that controlled the nanocrystallization of zirconium crystals. Nb particles are the sinks for point defects induced by Kr2+ ion irradiation. The interstitials and vacancies will move to Nb particles. The grain boundaries of the nanocrystals could also be the sinks to absorb defects, and the formation of more nanocrystals may slow down subsequent irradiation damage and improve radiation resistance of the materials [41]. Displacement damage drives complex microstructural and microchemical evolutions, including the accumulation of extended vacancy and SIA defect clusters, changes in the dislocation structures, nonequilibrium solute segregation, radiation-enhanced and-induced precipitation, and growing voids [42]. Xian-Ming Bai [41] reported that grain boundaries had a surprising “loading–unloading” effect. Upon irradiation, interstitials are loaded into the boundary, which then acts as a source, emitting interstitials to annihilate vacancies in the bulk. This unexpected recombination mechanism has a much lower energy barrier than conventional vacancy diffusion and is efficient for annihilating immobile vacancies in the nearby bulk, resulting in self-healing of the radiation-induced damage.

4. Conclusions

The microstructure evolution of the Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni zirconium alloy irradiated by 800 keV Kr2+ ions at 585 K was investigated by in situ transmission electron microscopy on the IVEM-Tandem Facility. The experiment results can be made as follows:
(1)
Many β-Nb precipitates with a BCC structure are distributed in the as-received zirconium alloy with micrometer-size grains. Most of the precipitates have a globular shape. The roundness and sphericity of precipitates are about 0.90 and 0.91, respectively.
(2)
Kr2+ ion irradiation induces the growth of β-Nb precipitates, which is due to the segregation of the dissolved niobium atoms in zirconium crystal structure and the migration to the existing precipitates. The size of precipitates is increased with increasing Kr2+ ion fluence.
(3)
During Kr2+ iron irradiation, the zirconium crystals without Nb precipitates tend to transform to the nanocrystals, which is not observed in the zirconium crystals with Nb nanoparticles. The existing Nb nanoparticles are the key factor that constrains the nanocrystallization of zirconium crystals. The thickness of the formed Zr-nanocrystal layer is about 300 nm, which is consistent with the depth of Kr2+ iron irradiation.

Acknowledgments

The work was supported by the National Natural Science Foundation of China, through Grant No. 11305136 and by NPL, CAEP, through Project 2015AB001.

Author Contributions

Guang Ran conceived, designed, and performed the experiments; Penghui Lei, Chenwei Liu, and Jiangkun Xu analyzed the data; Penghui Lei wrote the manuscript under the supervision of Guang Ran. All authors contributed to the scientific discussion of the results and reviewed the manuscript.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Gabory, B.D.; Motta, A.T.; Wang, K. Transmission electron microscopy characterization of Zircaloy-4 and ZIRLO™ oxide layers. J. Nucl. Mater. 2015, 456, 272–280. [Google Scholar] [CrossRef]
  2. Ran, G.; Xu, J.; Shen, Q.; Zhang, J.; Wang, L.M. In situ TEM observation of growth behavior of Kr bubbles in zirconium alloy during post-implantation annealing. Nucl. Instrum. Methods Phys. Res. B 2013, 307, 516–521. [Google Scholar] [CrossRef]
  3. Younker, I.; Fratoni, M. Neutronic evaluation of coating and cladding materials for accident tolerant fuels. Prog. Nucl. Energ. 2016, 88, 10–18. [Google Scholar] [CrossRef]
  4. Christensen, M.; Angeliu, T.M.; Ballard, J.D.; Vollmer, J.; Najafabadi, R.; Wimmer, E. Effect of impurity and alloying elements on Zr grain boundary strength from first-principles computations. J. Nucl. Mater. 2010, 404, 121–127. [Google Scholar] [CrossRef]
  5. Robson, J.D. Modeling precipitate evolution in zirconium alloys during irradiation. J. Nucl. Mater. 2016, 476, 123–131. [Google Scholar] [CrossRef]
  6. Shen, H.H.; Zhang, J.M.; Peng, S.M.; Xiang, X.; Sun, K.; Zu, X.T. In situ TEM investigation of amorphization and recrystallization of Zr (Fe, Cr, Nb)2 precipitates under Ne ion irradiation. Vacuum 2014, 110, 24–29. [Google Scholar] [CrossRef]
  7. Yan, C.; Wang, R.; Wang, Y.; Wang, X.; Bai, G. Effects of ion irradiation on microstructure and properties of zirconium alloys-A review. Nucl. Eng. Technol. 2015, 47, 323–331. [Google Scholar] [CrossRef]
  8. Charit, I.; Murty, K.L. Creep behavior of niobium-modified zirconium alloys. J. Nucl. Mater. 2008, 374, 354–363. [Google Scholar] [CrossRef]
  9. Shishov, V.N.; Peregud, M.M.; Nikulina, A.V.; Shebaldov, P.V.; Tselischev, A.V.; Novoselov, A.E.; Kobylyansky, G.P.; Ostrovsky, Z.E.; Shamardin, V.K. Influence of zirconium alloy chemical composition on microstructure formation and irradiation induced growth. In Zirconium in the Nuclear Industry: Thirteenth International Symposium; ASTM International: Conshohocken, PA, USA, 2002. [Google Scholar]
  10. Shen, H.H.; Peng, S.M.; Chen, B.; Naab, F.N.; Sun, G.A.; Zhou, W.; Xiang, X.; Sun, K.; Zu, X.T. Helium bubble evolution in a Zr–Sn–Nb–Fe–Cr alloy during post-annealing: An in-situ investigation. Mater. Charact. 2015, 107, 309–316. [Google Scholar] [CrossRef]
  11. Choi, S.I.; Kim, J.H. Radiation-induced dislocation and growth behavior of zirconium and zirconium alloys—A review. Nucl. Eng. Technol. 2013, 45, 385–392. [Google Scholar] [CrossRef]
  12. Lei, P.H.; Ran, G.; Liu, C.W.; Shen, Q.; Zhang, R.Q.; Ye, C.; Li, N.; Yang, P.H.; Yang, Y.C. Microstructure analysis of Kr+ irradiation and post-irradiation corrosion of modified N36 zirconium alloy. Nucl. Instrum. Methods Phys. Res. B. [CrossRef]
  13. Arjhangmehr, A.; Feghhi, S.A.H. Irradiation deformation near different atomic grain boundaries in α-Zr: An investigation of thermodynamics and kinetics of point defects. Sci. Rep. 2016, 6, 23333. [Google Scholar] [CrossRef] [PubMed]
  14. Ghidelli, M.; Gravier, S.; Blandin, J.-J.; Djemia, P.; Mompiou, F.; Abadias, G.; Pardoen, J.-R. Extrinsic mechanical size effects in thin ZrNi metallic glass films. Acta Mater. 2015, 90, 232–241. [Google Scholar] [CrossRef]
  15. Ghidelli, M.; Volland, A.; Blandin, J.-J.; Pardoen, T.; Raskin, J.P.; Mompiou, F.; Djemia, P.; Gravier, S. Exploring the mechanical size effects in Zr65Ni35 thin film metallic glasses. J. Alloys Compd. 2014, 615, S90–S92. [Google Scholar] [CrossRef]
  16. Huang, S.L.; Ran, G.; Lei, P.H.; Chen, N.J.; Wu, S.H.; Li, N.; Shen, Q. Effect of crystal orientation on hardness of He+ ion irradiated tungsten. Nucl. Instrum. Methods Phys. Res. B 2017. [Google Scholar] [CrossRef]
  17. Kim, H.G.; Kim, Y.H.; Choi, B.K.; Jeong, Y.H. Effect of alloying elements (Cu, Fe, and Nb) on the creep properties of Zr alloys. J. Nucl. Mater. 2006, 359, 268–273. [Google Scholar] [CrossRef]
  18. Ko, S.; Hong, S.I.; Kim, K.T. Creep properties of annealed Zr–Nb–O and stress-relieved Zr–Nb–Sn–Fe cladding tubes and their performance comparison. J. Nucl. Mater. 2010, 404, 154–159. [Google Scholar] [CrossRef]
  19. Byun, T.S.; Farrel, K. Irradiation hardening behavior of polycrystalline metals after low temperature irradiation. J. Nucl. Mater. 2004, 326, 86–96. [Google Scholar] [CrossRef]
  20. Li, Q.; Liu, W.Q.; Zhou, B.X. Effect of the deformation and heat treatment on the decomposition of β-Zr in Zr-Sn-Nb alloys. Rare Met. Mater. Eng. 2002, 31, 389–392. [Google Scholar]
  21. Liu, W.Q.; Li, Q.; Zhou, B.X.; Yao, M.Y. Effect of the microstructure on the corrosion resistance of ZIRLO alloy. Nucl. Power Eng. 2003, 24, 33–36. [Google Scholar]
  22. Liu, W.; Li, Q.; Zhou, B.; Yan, Q.; Yao, M. Effect of heat treatment on the microstructure and corrosion resistance of a Zr–Sn–Nb–Fe–Cr alloy. J. Nucl. Mater. 2005, 341, 97–102. [Google Scholar] [CrossRef]
  23. Perovic, V.; Perovic, A.; Weatherly, G.C.; Purdy, G.R. The distribution of Nb and Fe in a Zr-2.5 wt % Nb alloy before and after irradiation. J. Nucl. Mater. 1995, 224, 93–102. [Google Scholar] [CrossRef]
  24. Shishov, V.N.; Barberis, P.; Dean, S.W. The evolution of microstructure and deformation stability in Zr–Nb–(Sn,Fe) alloys under neutron irradiation. J. ASTM Int. 2010, 7, 479–500. [Google Scholar] [CrossRef]
  25. Shishov, V.N.; Peregud, M.M.; Nikulina, A.V.; Pimenov, Y.V.; Kobylyansky, G.P.; Novoselov, A.E.; Ostrovsky, Z.E.; Obukhov, A.V. Influence of structure—Phase state of Nb containing Zr alloys on irradiation-induced growth. J. ASTM Int. 2005, 2, 201–218. [Google Scholar] [CrossRef]
  26. Doriot, S.; Gilbon, D.; Béchade, J.-L.; Mathon, M.-H.; Legras, L.; Mardon, J.-P. Microstructural Stability of M5TM Alloy Irradiated up to High Neutron Fluences. J. ASTM Int. 2005, 2, 1–24. [Google Scholar]
  27. Kai, J.J.; Huang, W.I.; Chou, H.Y. The microstructural evolution of zircaloy-4 subjected to proton irradiation. J. Nucl. Mater. 1990, 170, 193–209. [Google Scholar] [CrossRef]
  28. Hernandez-Mayoral, M.; Heintze, C.; Onorbe, E. Transmission electron microscopy investigation of the microstructure of Fe-Cr alloys induced by neutron and ion irradiation at 300 degrees C. J. Nucl. Mater. 2016, 474, 88–98. [Google Scholar] [CrossRef]
  29. Was, G.S.; Busby, J.T.; Allen, T.; Kenik, E.A.; Jenssen, A.; Bruemmer, S.M.; Gan, J.; Edwards, A.D.; Scott, P.M.; Andresen, P.L. Emulation of neutron irradiation effects with protons: Validation of principle. J. Nucl. Mater. 2012, 300, 198–216. [Google Scholar] [CrossRef]
  30. Standard Practice for Neutron Radiation Damage Simulation by Charged-Particle Irradiation; ASTM International: West Conshohocken, PA, USA, 2009; ASTM-E-521–96.
  31. Turkin, A.A.; Buts, A.V.; Bakai, A.S. Construction of radiation-modified phase diagrams under cascade-producing irradiation: Application to Zr–Nb alloy. J. Nucl. Mater. 2002, 305, 134–152. [Google Scholar] [CrossRef]
  32. Nikulina, A.V.; Markelov, V.A.; Peregud, M.M.; Voevodin, V.N.; Panchenko, V.L.; Kobylyansky, G.P. Irradiation-induced microstructural changes in Zr-1% Sn-1% Nb-0.4% Fe. J. Nucl. Mater. 1996, 238, 205–210. [Google Scholar] [CrossRef]
  33. Wan, F.R. Irradiation Damage of Metallic Materials; Beijing Science Press: Beijing, China, 1993; pp. 23–127. [Google Scholar]
  34. Doriot, S.; Gilbon, D.; Bechade, J.L.; Mathon, M.H.; Legras, L.; Mardon, J.P. Microstructural stability of M5 (TM) alloy irradiated up to high neutron fluences. J. ASTM Int. 2005, 2, 175–198. [Google Scholar] [CrossRef]
  35. Perovic, V.; Perovic, A.; Weatherly, G.C.; Brown, L.M.; Purdy, G.R.; Fleck, R.G.; Holtl, R.A. Microstructural and microchemical studies of Zr-2.5 Nb pressure tube alloy. J. Nucl. Mater. 1993, 205, 251–257. [Google Scholar] [CrossRef]
  36. Ran, G.; Huang, S.L.; Huang, Z.J.; Yan, Q.Z.; Xu, J.K.; Li, N.; Wang, L.M. In situ Observation of Microstructure Evolution in Tungsten under 400keV Kr+ Irradiation. J. Nucl. Mater. 2014, 455, 320–324. [Google Scholar] [CrossRef]
  37. Kato, N.I. Reducing focused ion beam damage to transmission electron microscopy samples. J. Electron. Microsc. 2004, 53, 451–458. [Google Scholar] [CrossRef]
  38. Wollenberger, H. Phase transformations under irradiation. J. Nucl. Mater. 1994, 216, 63–77. [Google Scholar] [CrossRef]
  39. Russell, K.C. Phase instability under cascade damage irradiation. J. Nucl. Mater. 1993, 206, 129–138. [Google Scholar] [CrossRef]
  40. Szenes, G. Physics of Irradiation Effects in Metals. Mater. Sci. Forum 1992, 23, 97–99. [Google Scholar]
  41. Bai, X.M.; Voter, A.F.; Hoagland, R.G.; Nastasi, M.; Uberuaga, B.P. Efficient annealing of radiation damage near grainboundaries via interstitial emission. Science 2012, 327, 1631–1634. [Google Scholar] [CrossRef] [PubMed]
  42. Odette, G.R.; Alinger, M.J.; Wirth, B.D. Recent Developments in Irradiation-Resistant Steels. Annu. Rev. Mater. Res. 2008, 38, 471–503. [Google Scholar] [CrossRef]
Figure 1. Depth profile of displacement damage and implanted ion concentration in zirconium alloy irradiated by 800 keV Kr2+ to 1.0 × 1018 ions/m2 calculated by SRIM 2008 (Quick mode).
Figure 1. Depth profile of displacement damage and implanted ion concentration in zirconium alloy irradiated by 800 keV Kr2+ to 1.0 × 1018 ions/m2 calculated by SRIM 2008 (Quick mode).
Materials 10 00437 g001
Figure 2. Bright field TEM images showing the as-received zirconium alloy, (a) zirconium crystal without precipitates. (b) Nanoparticles in zirconium matrix. (c) Typical energy dispersive spectrometer (EDS) results of precipitate.
Figure 2. Bright field TEM images showing the as-received zirconium alloy, (a) zirconium crystal without precipitates. (b) Nanoparticles in zirconium matrix. (c) Typical energy dispersive spectrometer (EDS) results of precipitate.
Materials 10 00437 g002
Figure 3. In situ TEM observation of nanoparticle evolution during 800 keV Kr2+ irradiation at 585 K with the ion fluence of (a) 1.35 × 1019 Kr2+/m2; (b) 2.7 × 1019 Kr2+/m2; (c) 5.4 × 1019 Kr2+/m2; (d) 1.7 × 1020 Kr2+/m2.
Figure 3. In situ TEM observation of nanoparticle evolution during 800 keV Kr2+ irradiation at 585 K with the ion fluence of (a) 1.35 × 1019 Kr2+/m2; (b) 2.7 × 1019 Kr2+/m2; (c) 5.4 × 1019 Kr2+/m2; (d) 1.7 × 1020 Kr2+/m2.
Materials 10 00437 g003
Figure 4. The relationship between the size of precipitate and Kr2+ ion fluence, (a) Precipitate A; (b) Precipitate B, as shown in Figure 3.
Figure 4. The relationship between the size of precipitate and Kr2+ ion fluence, (a) Precipitate A; (b) Precipitate B, as shown in Figure 3.
Materials 10 00437 g004
Figure 5. The microstructure of zirconium alloy irradiated by 800 keV Kr2+ ions with a fluence of 1.7 ×10 20 Kr2+/m2. (a) The sketch of sample for in situ ion irradiation and the direction for microstructure observation; (b) the microstructure of the cross-section sample prepared by FIB; (c) the dark field TEM image showing the plan-view microstructure of the irradiated sample; (d) high resolution TEM image of (c).
Figure 5. The microstructure of zirconium alloy irradiated by 800 keV Kr2+ ions with a fluence of 1.7 ×10 20 Kr2+/m2. (a) The sketch of sample for in situ ion irradiation and the direction for microstructure observation; (b) the microstructure of the cross-section sample prepared by FIB; (c) the dark field TEM image showing the plan-view microstructure of the irradiated sample; (d) high resolution TEM image of (c).
Materials 10 00437 g005

Share and Cite

MDPI and ACS Style

Lei, P.; Ran, G.; Liu, C.; Ye, C.; Lv, D.; Lin, J.; Wu, Y.; Xu, J. In Situ TEM Study of Microstructure Evolution of Zr-Nb-Fe Alloy Irradiated by 800 keV Kr2+ Ions. Materials 2017, 10, 437. https://doi.org/10.3390/ma10040437

AMA Style

Lei P, Ran G, Liu C, Ye C, Lv D, Lin J, Wu Y, Xu J. In Situ TEM Study of Microstructure Evolution of Zr-Nb-Fe Alloy Irradiated by 800 keV Kr2+ Ions. Materials. 2017; 10(4):437. https://doi.org/10.3390/ma10040437

Chicago/Turabian Style

Lei, Penghui, Guang Ran, Chenwei Liu, Chao Ye, Dong Lv, Jianxin Lin, Yizhen Wu, and Jiangkun Xu. 2017. "In Situ TEM Study of Microstructure Evolution of Zr-Nb-Fe Alloy Irradiated by 800 keV Kr2+ Ions" Materials 10, no. 4: 437. https://doi.org/10.3390/ma10040437

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.