Next Article in Journal
Characterizing the Conductivity and Enhancing the Piezoresistivity of Carbon Nanotube-Polymeric Thin Films
Next Article in Special Issue
Preparation of Luminescent Metal-Organic Framework Films by Soft-Imprinting for 2,4-Dinitrotoluene Sensing
Previous Article in Journal
Controlling Morphology and Aggregation in Semiconducting Polymers: The Role of Solvents on Lasing Emission in Poly[2-methoxy-5-(2′-ethyl-hexyloxy)-1,4-phenylene-vinylene]
Previous Article in Special Issue
Warm White Light-Emitting Diodes Based on a Novel Orange Cationic Iridium(III) Complex
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Insight the Luminescence Properties of AlON: Eu, Mg Phosphor under VUV Excitation

1
School of Energy Science and Engineering, University of Electronic Science and Technology of China, 2006 Xiyuan Road, Chengdu 611731, China
2
Department of Physics, Tamkang University, Tamsui, New Taipei 25137, Taiwan
3
School of Physics, University of Sydney, Sydney, NSW 2006, Australia
4
Laboratory of Materials for Energy Conversion, Department of Materials Science and Engineering, University of Science and Technology of China, Hefei 230026, China
*
Author to whom correspondence should be addressed.
Materials 2017, 10(7), 723; https://doi.org/10.3390/ma10070723
Submission received: 27 April 2017 / Revised: 23 June 2017 / Accepted: 26 June 2017 / Published: 29 June 2017
(This article belongs to the Special Issue Luminescent Materials 2017)

Abstract

:
Owing to high quantum efficiency, adjustable composition and antioxidation properties of oxynitride phosphors, extensive investigations have focused on their photoluminescence properties under low-energy light excitation (UV or blue light). However, the vacuum ultraviolet (VUV) luminescence properties of oxynitride phosphors are rarely researched. Present work studies the structure and VUV luminescence properties of an oxynitride phosphor: AlON: Eu, Mg, which is synthesized by solid-state reaction. Under 147 nm excitation, it was found that AlON: Eu, Mg phosphor shows a blue emission band centered at about 470 nm. The first principle calculation is used to analyze the origin of the VUV absorption. Compared with BaMgAl10O17: Eu2+ phosphor, AlON: Eu, Mg phosphor shows better thermal stability.

1. Introduction

Recently, extensive investigations have focused on rare-earth-doped oxynitride phosphors due to their high quantum efficiency, adjustable composition, and antioxidation properties [1,2,3,4]. These characteristics make them successful applications in White-Light Emitting Diode (W-LED). As one kind of oxynitride, γ-aluminum oxynitride with spinel structure (hereafter AlON) is well known as a transparent ceramic in the visible light range and it has superior mechanical properties both at room and high temperature [5], which makes AlON a promising host-lattice for doping transition or rare-earth luminescent ions [6,7,8,9]. In particular, when doped with Eu2+ ions, AlON can be developed into an interesting blue-green luminescent material which exhibits a strong emission band centered at 470–500 nm under 310–330 nm light irradiation [10,11,12].
In addition to the general luminescence properties under ultraviolet (UV) or blue light excitation, it has been proved that some of oxynitride phosphors show intriguing luminescence under VUV excitation [13,14]. To the best of our knowledge, there is still no report on the VUV luminescence properties of AlON based phosphors. Therefore, it is spectroscopically interesting to study their VUV luminescence properties.
In this study, Eu doped AlON phosphor with a single spinel structure was prepared by solid-state reaction. Its VUV luminescent properties, as well as the thermal stability, were experimentally determined. First-principle calculations were adopted to propose the possible origin of the absorption in VUV band.

2. Results and Discussion

As reported, the addition of Mg can effectively suppress the impurity of corundum and promote the AlON formation [7]. X-ray diffraction (XRD) patterns of Figure 1 show that the samples have the single AlON phase with spinel crystal structure (JCPDS card No. 00-048-0686, Al5O6N). The strong XRD peaks of the powders match well with the standard date, indicating the high purity and good crystallinity of the products. Based on XRD peaks, the cell parameter increases from a = 7.95 Å in AlON to a = 8.00 Å in AlON: Eu, Mg due to Mg doping. The measured metallic elemental composition is 0.28 mol% (Eu), 8.91 mol% (Mg) and 90.81 mol% (Al). Therefore, the overall composition of synthesized AlON: Eu, Mg phosphor can be expressed as Eu0.06Mg2.05Al20.89O29.11N2.89, which is close to the designed composition of Eu0.046Mg2.3Al20.654O29.346N2.654.
In order to study element distribution in AlON, energy-dispersive X-ray spectrometry (EDS) mapping analyses are performed in Figure 2. All element mappings are in accordance with the TEM images of the particle shapes. EDS mapping result shows the uniform distribution of Al, O, N and Mg elements in AlON particle, validating the dissolution of Mg into AlON lattice. Although the signal corresponding to Eu is quite weak due to its low concentration, it is still clear to see that the Eu distribution almost matches the particle shape. This indicates that the Eu is dissolved into AlON lattice.
The previous report has indicated that AlON: Eu, Mg phosphor can be effectively excited by 330 nm UV light and give a strong blue emission [10,12]. Their VUV luminescence property is researched here. Figure 3a exhibits the emission spectrum of the AlON: Eu, Mg phosphor under 147 nm excitation. The emission spectrum is dominated by a blue emission band centered at about 470 nm, which is assigned to the typical 4f65d1-4f7 transition of the Eu2+ ion. Note that the emission spectrum is very broad, meaning that filtering is needed to improve its color purity in actual display applications. No sharp f-f transition lines characteristic for Eu3+ are detected, indicating that Eu is mainly present as the divalent valence in AlON: Eu, Mg.
Figure 3b presents the VUV excitation spectrum of the AlON: Eu, Mg phosphor. The spectrum consists of three main broad bands in the VUV to UV range: 120 to 150 nm, 230–270 nm and 300–350 excitation band. According to the previous reports, excitation band from 230 to 270 nm is due to absorption of the AlON host material because the bandgap of AlON is estimated to approximately 5 eV [15,16]. The 300–350 nm excitation band is caused by the absorption of Eu2+. Noticeably, there is an obvious absorption from 120 to 150 nm, centered at 136 nm, which is located in the VUV spectrum. It means that AlON: Eu, Mg phosphor can be excited by VUV light and give a blue emission.
Up to now, the exact sites of Eu2+ ions in AlON lattice are still unknown since it is a challenging work to make it clear. On account of large difference of ionic radius between Eu2+ and Al3+, Eu2+ ions are expected to locate at some layered structure like EuMgAl10O17, which has been verified in Eu, Si co-doped AlN [17]. As a comparison, the VUV excitation spectrum of BaMgAl10O17: Eu2+ is included in Figure 3b. There is a significant difference for the 120–270 nm excitation band due to the different host materials. Both phosphors show absorption in the range of 300–350 nm band, which possibly indicates their similar coordination environment around Eu2+. To clarify the origin of the first VUV absorption peak, first-principles calculation is performed here. Before that, a clear structure model of AlON: Eu, Mg, Mg is needed. Considering that the VUV absorption is more ascribed to the intrinsic property of AlON host lattice, Eu2+ was not included in calculation process because the intrinsic optical property of AlON will not be altered by quite low doping concentration of Eu.
It is generally believed that, for the transparent ceramic γ-AlON, the crystal would have a cubic spinel-type structure, with space group of Fd 3 ¯ m. Crystallographically, the ideal spinel space group demands totally 24 cations and 32 anions per unit cell (M24X32 type). In the structure, octahedrons are connected to each other by edge sharing and to the neighbored tetrahedrons by point sharing. To balance charge neutrality in the structure of AlON, the following formula for a constant anion model can be written as [18]:
Al(64+z)/3V(8−z)/3O32−zNz,
where V is cation vacancy. It is investigated that γ-AlON is compositionally stable when z = 5, forming Al23O27N5 due to the low concentration of Al vacancy. By comparing the system energy of two structures with different Al vacancy site (Table 1), the model with an Al vacancy in the octahedral sites have the lowest total energy and is therefore more acceptable, which agrees with the previous calculation results based on density functional theory (DFT) [19,20].
As expressed in the experimental part, Mg addition is used to suppress the formation of corundum and promise the high purity of obtained AlON powders [7]. Considering approximately two Mg2+/Al3+ substitutions with unequal charge, O2−/N3− substitution is introduced to neutralize the charge, i.e., forming Al21Mg2O29N3. To determine the Mg sites in AlON structure, total energy of Al21Mg2O29N3 with different Mg occupation sites are calculated, respectively. Totally, three are three possible configurations for Al21Mg2O29N3 as shown in Figure 4: (a) both Mg atoms substitute octahedral sites; (b) both Mg atoms substitute tetrahedral sites; (c) one Mg atom substitutes octahedral site and one substitutes tetrahedral site, respectively. Table 2 summarizes the total energy calculated for the different configurations. It is seen that the energy increases in the order:
E b   <   E a   <   E c
It stabilizes the AlON crystal that both Mg atoms occupy tetrahedral Al sites in Al21Mg2O29N3. In the view of ionic radius (Mg2+, 4CN, 0.57 Å), tetrahedral volume matches better with Mg2+, which reduces the lattice stress of crystal structure. Therefore, Mg occupation at tetrahedral sites in is more favorable.
Figure 5 shows the total and the atom-resolved partial DOS (PDOS) for all the different atoms in optimized Al21Mg2O29N3 configuration. For clarity, the Fermi level is set to zero. Clearly, a sharp peak I mainly comes from N 2s states. The peak II around −4.05 eV is mostly contributed by O 2p state with slight mixings of Al 3s, 3p states. The peak III around 5.3 eV is mainly attributed to Al 3s, 3p, O 2p states. As talked about the VUV excitation spectrum of AlON: Eu, Mg phosphor, the experimental absorption peak around 136 nm corresponds to 9.12 eV. Although the band gap underestimation shown in Figure 5 is typical by DFT (the band gap is smaller than 5 eV), such underestimation does not mean that the higher energy states which results in higher energy (120 nm~160 nm) photon absorption is equally largely underestimated [21,22]. Actually, the energy value of electron transitions just matches the peak of absorption around 136 nm. Thus, it indicates VUV excitation ranging from 120 to 160 nm originates from the O 2p states to Al 3s, 3p states transitions (9.35 eV). This kind of host-lattice excitation associated with Al-O groups in the spinel blocks is also observed in the commercial BaMgAl10O17: Eu2+ and BaAl12O19: Mn2+ phosphor [23,24].
As known, one of luminescence routes is to excite the host lattice firstly, followed by the efficient energy transfer from the excited state of the host lattice to the luminescent ion, resulting in the typical emission of Eu2+. The observed luminescence under 147 nm excitation is through this way that an efficient energy transfers from the host lattice to Eu2+ ions.
Thermal stability is a very important factor for phosphors when working at high temperature. As a popular blue phosphor, BaMgAl10O17: Eu2+ (BAM) with typical layered structure allows intercalation of oxygen ions into its interlayers easily and causes the oxidation of Eu2+ into Eu3+, leading to severe luminescence degradation [25,26]. On the contrary, AlON consists of a three-dimensional rigid Al (O, N)4 network, which will decrease the oxidation degree of Eu2+ to Eu3+ [27]. As shown in Figure 6, the emission intensity of AlON: Eu, Mg phosphor decreases only 21% after annealing at 600 °C for 1 h in air, while that of the commercial BAM has more than 28% degradation under 147 nm excitation [28]. The improved thermal stability can also be proved by the Eu L3-edge X-ray absorption near edge structure (XANES) spectra in the corresponding samples. Two peaks can be clearly seen at about 6977 and 6984 eV, which are due to the divalent and trivalent oxidation states of europium ions, respectively. For AlON: Eu, Mg and BAM, Eu2+ is oxidized into Eu3+ after heat-treatment at 600 °C in air. However, the oxidation degree differs each other. The relative intensities of the peaks ascribed to Eu2+ and Eu3+ for the samples suggest that the oxidation degree of Eu2+ in AlON: Eu, Mg sample is partly suppressed in the thermal treatment process. The above results indicate AlON: Eu, Mg phosphor shows higher thermal stability than BAM.

3. Experimental Section

Materials synthesis. Compared to total cation number, 0.2 mol% Eu and 10 mol% Mg concentration doped AlON (Eu0.046Mg2.3Al20.654O29.346N2.654) phosphor was synthesized by conventional solid-state reaction. Mg element was introduced to promote the high purity of AlON. The powder mixtures of Al2O3 (Sinopharm Chemical Reagent Co. Ltd., Shanghai, China), AlN (Sinopharm Chemical Reagent Co. Ltd., Shanghai, China), MgO (Sinopharm Chemical Reagent Co. Ltd., Shanghai, China), and Eu2O3 (Sinopharm Chemical Reagent Co. Ltd., Shanghai, China) were well mixed in a Si3N4 mortar by grinding. The resulting mixtures were fired in BN crucibles under N2 atmosphere for 2 h at 1800 °C. The samples were heated at a constant rate of 360 °C/h and cooled to room temperature naturally.

3.1. Material Characterization

The phase formation was analyzed by an X-ray diffractometer (Model PW 1700, Philips Research Laboratories, Eindhoven, The Netherlands) using Cu Kα radiation at a scanning rate of 0.5 degree/min. The composition analysis was performed by transmission electron microscopy-energy dispersion X-ray spectroscopy (Model 2100F, JEOL, Tokyo, Japan). Metallic elements content was analyzed by inductively coupled plasma atomic emission spectrometer (ICP-AES) (Optima 7300DV, Perkin Elmer Corporation, Waltham, MA, USA). The VUV excitation and emission spectra were measured at the VUV spectroscopic experimental station on beam line U10B of the National Synchrotron Radiation Laboratory of China. The synchrotron radiation was monochromatized through a Seya-Namioka monochromator and the signal was received by a Hamamatsu R456 photomultiplier. The X-ray absorption spectra at the Eu L3-edge of AlON: Eu, Mg were measured at the beamline of BL14W1 at Shanghai Synchrotron Radiation Facility.

3.2. Computational Methodology

The theoretical calculations were performed using the Cambridge Sequential Total Energy Package (CASTEP) code [29,30]. A plane wave basis set with kinetic energy cutoff at 500 eV was employed, with the electron-ion interaction accounted for through the use of ultrasoft pseudopotentials [31]. Such E_cut allows the convergence of total energy to be within 0.1 eV/atom. The Perdew-Burke-Enzerhof form [32,33] of the generalized gradient approximation (GGA) was used to describe the exchange-correlation interactions. Actual spacing of k-point sampling is 0.067 Ang−1. Monkhorst-Pack sets of k points = 1 × 1 × 1 was sufficient, and we set SCF tolerance threshold to be 1.0 × 10−5 eV/atom. In Mg doped AlON cell structure, two Al atoms are substituted by same quantity of Mg atoms. Then the cell-varying geometry optimization is processed for relaxing crystal lattice, giving the supercell parameters of a = 8.08 Å, b = 8.05 Å and c = 8.11 Å. The yielded lattice parameters errors (when compared with experimental values: 8.00 Å) Err (a, b, c) = (1.00%, 0.63%, 1.38%), respectively.

4. Conclusions

AlON: Eu, Mg phosphor is synthesized by solid-state reaction. Its structure and VUV luminescence properties are investigated. The experimental results indicate that Al, O, N, Mg and Eu elements are successfully dissolved into AlON lattice. Under 147 nm excitation, the phosphor shows a blue emission band centered at about 470 nm. First principle calculation results indicate that the VUV excitation ranging from 120 to 160 nm originates from host-lattice excitation of Al-O groups in the spinel blocks. Compared with BaMgAl10O17: Eu2+ phosphor, AlON: Eu, Mg phosphor shows higher thermal stability due to the three-dimensional rigid Al (O, N)4 network.

Acknowledgments

This research was supported by the National Natural Science Foundation of China (Grant No. 51302029 and 51402040) and the Fundamental Research Funds for the Central Universities (Grant No. ZYGX2015J110)). The authors thank National Synchrotron Radiation Laboratory of China for providing the VUV measurements. Ming-Hsien Lee thanks supports of hardware from KeyWin Inc., ICSD access from NCHC and financial support from MOST-Taiwan. Especially, the authors thank Yi-Fei Wang for providing the VUV excitation spectrum and XANES results of BaMgAl10O17: Eu2+, performed in the National Synchrotron Radiation Laboratory of China, and thank Shanghai Synchrotron Radiation Facility for providing the XANES measurements of AlON: Eu, Mg phosphor.

Author Contributions

X. Jian and H. Wang performed the experiments, M.-H. Lee and G.-Z. Chen were responsible for the first-principle calculations, W. Tian performed and analyzed the EDS mapping, W.-Q. Chen analyzed the XANES spectra, W.-W. Ji measured the XANES spectra, Xin Xu gave many comments on this manuscript and L.-J. Yin was responsible for the idea and organized the manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Xie, R.J.; Hirosaki, N. Silicon-based oxynitride and nitride phosphors for white leds—A review. Sci. Technol. Adv. Mater. 2007, 8, 588–600. [Google Scholar] [CrossRef]
  2. Xia, Z.; Liu, Q. Progress in discovery and structural design of color conversion phosphors for leds. Prog. Mater. Sci. 2016, 84, 59–117. [Google Scholar] [CrossRef]
  3. Yin, L.-J.; Ji, W.-W.; Liu, S.-Y.; He, W.-D.; Zhao, L.; Xu, X.; Fabre, A.; Dierre, B.; Lee, M.-H.; van Ommen, J.R.; et al. Intriguing luminescence properties of (Ba, Sr)3Si6O9N4: Eu2+ phosphors via modifying synthesis method and cation substitution. J. Alloys Compd. 2016, 682, 481–488. [Google Scholar] [CrossRef]
  4. Chen, G.; Yin, L.-J.; Dong, J.-T.; Feng, Y.-Y.; Gao, Y.; He, W.; Jia, Y.; Xu, X.; Hintzen, H.T. Synthesis, crystal structure, and luminescence properties of Y4Si2O7N2: Eu2+ oxynitride phosphors. J. Am. Ceram. Soc. 2016, 99, 183–190. [Google Scholar] [CrossRef]
  5. McCauley, J.W.; Corbin, N.D. Phase relations and reaction sintering of transparent cubic aluminum oxynitride spinel (ALON). J. Am. Ceram. Soc. 1979, 62, 476–479. [Google Scholar] [CrossRef]
  6. Zhang, F.; Wang, S.W.; Liu, X.J.; An, L.Q.; Yuan, X.Y. Upconversion luminescence in er-doped Gamma-ALON ceramic phosphors. J. Appl. Phys. 2009, 105, 4. [Google Scholar] [CrossRef]
  7. Xie, R.J.; Hirosaki, N.; Liu, X.J.; Takeda, T.; Li, H.L. Crystal structure and photoluminescence of Mn2+–Mg2+ codoped gamma aluminum oxynitride (Gamma-ALON): A promising green phosphor for white light-emitting diodes. Appl. Phys. Lett. 2008, 92, 3. [Google Scholar] [CrossRef]
  8. Liu, L.H.; Wang, L.; Zhang, C.N.; Cho, Y.J.; Dierre, B.; Hirosaki, N.; Sekiguchi, T.; Xie, R.J. Strong energy-transfer-induced enhancement of luminescence efficiency of Eu2+- and Mn2+-codoped gamma-aion for near-UV-led-pumped solid state lighting. Inorg. Chem. 2015, 54, 5556–5565. [Google Scholar] [CrossRef] [PubMed]
  9. Akhmadullina, N.S.; Lysenkov, A.S.; Ashmarin, A.A.; Kargin, Y.F.; Ishchenko, A.V.; Yagodin, V.V.; Shul’gin, B.V. Effect of dopant concentration on the phase composition and luminescence properties of Eu2+- and Ce3+-doped alons. Inorg. Mater. 2015, 51, 473–481. [Google Scholar] [CrossRef]
  10. Yin, L.-J.; Hu, W.-W.; Xu, X.; Hao, L.-Y. Synthesis of pure ALON: Eu2+, Mg2+ phosphors by a mechanochemical activation route. Ceram. Int. 2013, 39, 2601–2604. [Google Scholar] [CrossRef]
  11. Yin, L.; Xu, X.; Hao, L.; Xie, W.; Wang, Y.; Yang, L.; Yang, X. Synthesis and photoluminescence of Eu2+–Mg2+ Co-doped [Gamma]-ALON phosphors. Mater. Lett. 2009, 63, 1511–1513. [Google Scholar] [CrossRef]
  12. Yin, L.-J.; Yu, W.; Xu, X.; Hao, L.-Y. Synthesis and photoluminescence of Eu, Mg-ALON phosphors by carbothermal reduction. J. Lumin. 2012, 132, 671–675. [Google Scholar] [CrossRef]
  13. Tang, J.-Y.; Xie, W.-J.; Huang, K.; Hao, L.-Y.; Xu, X.; Xie, R.-J. A high stable blue BaSi3Al3O4N5:Eu2+ phosphor for white leds and display applications. Electrochem. Solid-State. Lett. 2011, 14, J45–J47. [Google Scholar] [CrossRef]
  14. Yang, L.; Xu, X.; Hao, L.; Yang, X.; Agathopoulos, S. Synthesis and characterization of fast-decaying bluish green phosphors of Tb3+-doped CaSi2O2N2 for 2D/3D plasma display panels. J. Lumin. 2012, 132, 1540–1543. [Google Scholar] [CrossRef]
  15. Soignard, E.; Machon, D.; McMillan, P.F.; Dong, J.J.; Xu, B.; Leinenweber, K. Spinel-structured gallium oxynitride (Ga3O3N) synthesis and characterization: An experimental and theoretical study. Chem. Mater. 2005, 17, 5465–5472. [Google Scholar] [CrossRef]
  16. Zhong, H.-M.; Liu, Q.; Zhou, Y.; Zhuang, J.-D.; Zhou, H. Synthesis and photoluminescence of ALON: Ce3+ phosphors. Acta Phys. Sin. 2013, 62. [Google Scholar] [CrossRef]
  17. Takeda, T.; Hirosaki, N.; Xie, R.-J.; Kimoto, K.; Saito, M. Anomalous eu layer doping in Eu, Si Co-doped aluminium nitride based phosphor and its direct observation. J. Mater. Chem. 2010, 20, 9948–9953. [Google Scholar] [CrossRef]
  18. McCauley, J.W. A simple model for aluminum oxynitride spinels. J. Am. Ceram. Soc. 1978, 61, 372–373. [Google Scholar] [CrossRef]
  19. Tu, B.; Wang, H.; Liu, X.; Wang, W.; Fu, Z. First-principles insight into the composition-dependent structure and properties of γ-ALON. J. Am. Ceram. Soc. 2014, 97, 2996–3003. [Google Scholar] [CrossRef]
  20. Batyrev, I.G.; Taylor, D.E.; Gazonas, G.A.; McCauley, J.W. Density functional theory and evolution algorithm calculations of elastic properties of alon. J. Appl. Phys. 2014, 115, 6. [Google Scholar] [CrossRef]
  21. Yazdanmehr, M.; Asadabadi, S.J.; Nourmohammadi, A.; Ghasemzadeh, M.; Rezvanian, M. Electronic structure and bandgap of γ-Al2O3 compound using mbj exchange potential. Nanoscale Res. Lett. 2012, 7, 488. [Google Scholar] [CrossRef] [PubMed]
  22. Amat, A.; Mosconi, E.; Ronca, E.; Quarti, C.; Umari, P.; Nazeeruddin, M.K.; Grätzel, M.; De Angelis, F. Cation-induced band-gap tuning in organohalide perovskites: Interplay of spin–orbit coupling and octahedra tilting. Nano. Lett. 2014, 14, 3608–3616. [Google Scholar] [CrossRef] [PubMed]
  23. Wang, Y.F.; Liu, L.H.; Xie, R.J.; Huang, Q. Microwave assisted sintering of thermally stable BaMgAl10O17:Eu2+ phosphors. ECS J. Solid State Sci. Technol. 2013, 2, R196–R200. [Google Scholar] [CrossRef]
  24. Wang, Y.; Xu, X.; Yin, L.; Hao, L. High photoluminescence of Si-N-Co-doped BaAl12O19:Mn2+ green phosphors. Electrochem. Solid. State. Lett. 2010, 13, J119–J121. [Google Scholar] [CrossRef]
  25. Dawson, B.; Ferguson, M.; Marking, G.; Diaz, A.L. Mechanisms of vuv damage in BaMgAl10O17: Eu2+. Chem. Mater. 2004, 16, 5311–5317. [Google Scholar] [CrossRef]
  26. Pike, V.; Patraw, S.; Diaz, A.L.; DeBoer, B.G. Defect chemistry and VUV optical properties of the BaMgAl10O17: Eu2+-Ba0.75Al11O17.25: Eu2+ solid solution. J. Solid State Chem. 2003, 173, 359–366. [Google Scholar] [CrossRef]
  27. Xie, R.-J.; Hintzen, H.T. Optical properties of (Oxy)nitride materials: A review. J. Am. Ceram. Soc. 2013, 96, 665–687. [Google Scholar] [CrossRef]
  28. Wang, Y.-F.; Wang, Y.-F.; Zhu, Q.-Q.; Hao, L.-Y.; Xu, X.; Xie, R.-J.; Agathopoulos, S. Luminescence and structural properties of high stable Si-N-doped BaMgAl10O17:Eu2+ phosphors synthesized by a mechanochemical activation route. J. Am. Ceram. Soc. 2013, 96, 2562–2569. [Google Scholar] [CrossRef]
  29. Cheng, Y.C.; Wu, X.L.; Zhu, J.; Xu, L.L.; Li, S.H.; Chu, P.K. Optical properties of rocksalt and zinc blende aln phases: First-principles calculations. J. Appl. Phys. 2008, 103, 073707. [Google Scholar] [CrossRef]
  30. Duan, C.-J.; Wang, X.-J.; Zhao, J.-T. Luminescent properties and electronic structures of rare earth and alkaline earth borates of ReBa3B9O18 (RE = Lu,Y). J. Appl. Phys. 2007, 101. [Google Scholar] [CrossRef]
  31. Vanderbilt, D. Soft self-consistent pseudopotentials in a generalized eigenvalue formalism. Phys. Rev. B 1990, 41, 7892–7895. [Google Scholar] [CrossRef]
  32. Perdew, J.P.; Burke, K.; Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 1996, 77, 3865–3868. [Google Scholar] [CrossRef] [PubMed]
  33. Perdew, J.P.; Zunger, A. Self-interaction correction to density-functional approximations for many-electron systems. Phys. Rev. B 1981, 23, 5048. [Google Scholar] [CrossRef]
Figure 1. X-ray diffraction (XRD) patterns of AlON: Eu, Mg phosphor.
Figure 1. X-ray diffraction (XRD) patterns of AlON: Eu, Mg phosphor.
Materials 10 00723 g001
Figure 2. Energy-dispersive X-ray spectrometry (EDS) mapping showing the distribution of Al, O, N, Mg and Eu in AlON: Eu, Mg phosphor.
Figure 2. Energy-dispersive X-ray spectrometry (EDS) mapping showing the distribution of Al, O, N, Mg and Eu in AlON: Eu, Mg phosphor.
Materials 10 00723 g002
Figure 3. Emission (a) and excitation spectra (b) of the AlON: Eu, Mg phosphor. The sharp signal in the excitation spectrum at about 240 nm is due to no use of the correct filter, as a consequence of which second order radiation is transmitted.
Figure 3. Emission (a) and excitation spectra (b) of the AlON: Eu, Mg phosphor. The sharp signal in the excitation spectrum at about 240 nm is due to no use of the correct filter, as a consequence of which second order radiation is transmitted.
Materials 10 00723 g003
Figure 4. Three Al21Mg2O29N3 configurations with different Mg occupation sites.
Figure 4. Three Al21Mg2O29N3 configurations with different Mg occupation sites.
Materials 10 00723 g004
Figure 5. The total and the atom-resolved partial density of states (PDOS) for all the different atoms in Al21Mg2O29N3.
Figure 5. The total and the atom-resolved partial density of states (PDOS) for all the different atoms in Al21Mg2O29N3.
Materials 10 00723 g005
Figure 6. Emission intensity (a) and Eu L3-edge X-ray absorption near edge structure (XANES) spectra (b) of AlON: Eu, Mg and BaMgAl10O17: Eu2+ phosphors before and after annealing at 600 °C for 1 h in air.
Figure 6. Emission intensity (a) and Eu L3-edge X-ray absorption near edge structure (XANES) spectra (b) of AlON: Eu, Mg and BaMgAl10O17: Eu2+ phosphors before and after annealing at 600 °C for 1 h in air.
Materials 10 00723 g006
Table 1. Total energy E (eV) and relative energies ΔE (eV) of Al23O27N5 with Al vacancy at different sites obtained from the generalized gradient approximation (GGA) calculations.
Table 1. Total energy E (eV) and relative energies ΔE (eV) of Al23O27N5 with Al vacancy at different sites obtained from the generalized gradient approximation (GGA) calculations.
NumberAl VacancyE (eV)ΔE (eV)
1octahedral site−14,534.340
2tetrahedral site−14,521.6912.65
Table 2. Total energy E (eV) and relative energies ΔE (eV) of Al21Mg2O29N3 with Mg at different sites obtained from the GGA calculations.
Table 2. Total energy E (eV) and relative energies ΔE (eV) of Al21Mg2O29N3 with Mg at different sites obtained from the GGA calculations.
NumberMg SitesE (eV)ΔE (eV)
aoctahedral sites−16,689.9613.04
btetrahedral sites−16,703.000
coctahedral and tetrahedral sites−16,687.0715.93

Share and Cite

MDPI and ACS Style

Jian, X.; Wang, H.; Lee, M.-H.; Tian, W.; Chen, G.-Z.; Chen, W.-Q.; Ji, W.-W.; Xu, X.; Yin, L.-J. Insight the Luminescence Properties of AlON: Eu, Mg Phosphor under VUV Excitation. Materials 2017, 10, 723. https://doi.org/10.3390/ma10070723

AMA Style

Jian X, Wang H, Lee M-H, Tian W, Chen G-Z, Chen W-Q, Ji W-W, Xu X, Yin L-J. Insight the Luminescence Properties of AlON: Eu, Mg Phosphor under VUV Excitation. Materials. 2017; 10(7):723. https://doi.org/10.3390/ma10070723

Chicago/Turabian Style

Jian, Xian, Hui Wang, Ming-Hsien Lee, Wei Tian, Guo-Zhang Chen, Wen-Qiao Chen, Wei-Wei Ji, Xin Xu, and Liang-Jun Yin. 2017. "Insight the Luminescence Properties of AlON: Eu, Mg Phosphor under VUV Excitation" Materials 10, no. 7: 723. https://doi.org/10.3390/ma10070723

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.