Next Article in Journal
Effects of the Crack Tip Constraint on the Fracture Assessment of an Al 5083-O Weldment for Low Temperature Applications
Next Article in Special Issue
Synthesis and Characterization of Gelatin-Based Crosslinkers for the Fabrication of Superabsorbent Hydrogels
Previous Article in Journal
Low-Temperature Preparation of Tungsten Oxide Anode Buffer Layer via Ultrasonic Spray Pyrolysis Method for Large-Area Organic Solar Cells
Previous Article in Special Issue
Effect of Silver Dopants on the ZnO Thin Films Prepared by a Radio Frequency Magnetron Co-Sputtering System
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Thin-Film Coated Plastic Wrap for Food Packaging

1
Graduate Institute of Optoelectronic Engineering and Department of Electrical Engineering, National Chung Hsing University, Taichung 40227, Taiwan
2
Department of Electrical Engineering, Da-Yeh University, Chunghua 51591, Taiwan
3
Department of Materials Science and Engineering, Da-Yeh University, Chunghua 51591, Taiwan
4
Bachelor Program for Design and Materials for Medical Equipment and Devices, Da-Yeh University, Changhua 51591, Taiwan
5
Institute of Biomedical Engineering, National Taiwan University, Taipei 106, Taiwan
*
Author to whom correspondence should be addressed.
Materials 2017, 10(7), 821; https://doi.org/10.3390/ma10070821
Submission received: 27 June 2017 / Revised: 12 July 2017 / Accepted: 13 July 2017 / Published: 18 July 2017
(This article belongs to the Special Issue Selected Papers from IEEE ICASI 2017)

Abstract

:
In this study, the antimicrobial property and food package capability of polymethylpentene (PMP) substrate with silicon oxdie (SiOx) and organic silicon (SiCxHy) stacked layers deposited by an inductively coupled plasma chemical vapor deposition system were investigated. The experimental results show that the stacked pair number of SiOx/SiCxHy on PMP is limited to three pairs, beyond which the films will crack and cause package failure. The three-pair SiOx/SiCxHy on PMP shows a low water vapor transmission rate of 0.57 g/m2/day and a high water contact angle of 102°. Three-pair thin-film coated PMP demonstrates no microbe adhesion and exhibits antibacterial properties within 24 h. Food shelf life testing performed at 28 °C and 80% humidity reports that the three-pair thin-film coated PMP can enhance the food shelf-life to 120 h. The results indicate that the silicon-based thin film may be a promising material for antibacterial food packaging applications to extend the shelf-life of food products.

1. Introduction

There has been growing interest in recent years to develop materials with antibacterial properties which improve food safety and shelf-life. Antibacterial packaging is one of the most promising active packaging systems [1,2,3,4,5]. In addition to the basic properties of packaging materials, antimicrobial food package should prevent the gain of moisture, hinder microbial contamination, and act as a barrier against the permeation of water vapor, oxygen, carbon dioxide, and other volatile compounds.
Basic packaging materials, such as paper and paperboard, plastic, glass, and metal, are used to fulfill the capabilities and requirements of packaged foods, depending on their type. However, there has been an ever-increasing endeavor to develop different kinds of food packaging materials in order to extend the shelf-life with improved water vapor resistivity and antibacterial property. Silicon oxide (SiOx) barrier films with high density and mechanical resistance, as well as a low water permeation rate can be deposited using plasma-enhanced chemical vapor deposition at low temperatures [6,7]. It has been proven that SiOx is useful in improving the gas barrier properties of some food packaging materials such as polyethylene terephthalate [8,9] and polyvinyl chloride [10]. Polymethylpentene (PMP) is a thermoplastic polyolefin with excellent mechanical and thermal stabilities [11]. However, PMP plastic food wraps have a high moisture permeation rate and there are few research studies related to the improvement of the water vapor resistivity and antibacterial property of PMP.
In this paper, inorganic SiOx and organic silicon (SiCxHy) stacked layers were prepared on a PMP substrate by using inductively coupled plasma chemical vapor deposition (ICPCVD). Silicon oxide-based thin film is widely known as a great barrier against water vapor [12], but SiOx may likely have cracks induced by the accumulation of internal residual compressive stress when the film thickness increases. SiCxHy films with good tensile stress were thus stacked with SiOx to reduce the total internal stress. The stacked layers were continually deposited in the same chamber without breaking the vacuum conditions. The pair of the SiOx/SiCxHy stacked layers was varied in order to reduce the water vapor transmission rate (WVTR). Finally, the food package capability of PMP with SiOx/SiCxHy stacked layers was evaluated, and the PMP with the stacked layers demonstrated greatly improved antibacterial properties and extended the food shelf-life.

2. Materials and Methods

2.1. Materials

Silicon-based thin films, such as SiOx and SiCxHy layers, were prepared on PMP substrates by a 13.56-MHz radio frequency ICPCVD system. A gas mixture of oxygen (O2) and tetramethylsilane (TMS) was used to deposit SiOx, while argon (Ar) and TMS were used to deposit SiCxHy. For SiOx layers, the gas flow ratio of O2 to TMS was 4. For SiCxHy layers, the gas flow ratio of Ar to TMS was 0.03. The radio frequency power for SiOx and SiCxHy were 600 and 400 W, respectively. The deposition pressure was 5 mTorr and the temperature was kept at 90 °C. In our previous study, a minimal internal stress was obtained when the thicknesses of SiOx and SiCxHy were 300 and 30 nm, respectively. The pair number of the silicon-based stacked layers was varied from one to three.

2.2. Antibacterial Efficacy Test

The bacterial strains used in this study were Escherichia coli (E. coli) (ATCC, strain 25922) from Creative Life Science Co., Ltd. (Taipei, Taiwan). The antimicrobial effect was tested by the Kirby-Bauer diffusimetrical method. The bacteria was incubated for 17 h with vigorous shaking (250 rad/min) at 37 °C, and were obtained from a bacterial inoculum, which was standardized according to the McFarland scale, yielding to 107 CFU/mL. Luria-Bertani (LB) medium was inoculated with that inoculum and afterwards, different pairs of the SiOx/SiCxHy films with a diameter of 1 cm were applied on the surface of the medium. The antimicrobial property against the strains of E. coli was assessed by measuring the ratio of microbes to sample area after 0, 2, 4, 8, 12, 24, 48, and 72 h of incubation at 37 °C.

2.3. Bread Packaging Test

Four fresh toast slices (size: 10 cm × 5 cm) without preservatives were packed in the PMP without and with different pairs of SiOx/SiCxHy films. The toast slices were stored at a relatively humidity of 80% and a temperature of 28 °C. Photographs of the toast slices were taken after 120 h, and ImageJ computing software (National Institute of Mental Health, Maryland, MD, USA) [13,14] was used to evaluate the area of fungal contamination.

2.4. Characterization

The topographical morphologies of the SiOx/SiCxHy films were observed by optical microscopy (OM, MICROTECH MX810-RF, M&T Optics, Co., Ltd., Taipei, Taiwan). The WVTR of the films was measured by a WVTR permeation instrument (PERMATRAN-WR Model 3/61, Mocon Inc., Minneapolis, MN, USA) under the conditions of 40 °C and 100% relative humidity (RH) [15,16]. Water contact angle measurements were performed with a pocket goniometer (Model PGX, Testing Machines Inc., Veenendaal, The Netherlands) using 2 μL droplets, with at least five repetitions for each sample. The morphologies of E. coli grown on PMP without and with different pairs of SiOx/SiCxHy films were observed using high resolution thermal field emission scanning electron microscopy (HRFEG-SEM, JSM-7610F, JEOL, Tokyo, Japan) at 10 kV.

3. Results and Discussion

3.1. Properties of Silicon-Based Thin Films

The OM images of PMP with different pairs of SiOx/SiCxHy films are shown in Figure 1. The PMP without, with one-, two-, and three-pair SiOx/SiCxHy stacked layers show smooth surface and good structural integrity without significant pores or cracks. The four-pair SiOx/SiCxHy stacked layer exhibits crack patterns on the film surface. One possible reason for the cracks might be attributed to the heat accumulation on the substrate during the deposition process. PMP substrate is very likely to curl under long plasma deposition as the ion bombardment will heat the PMP substrate. Another reason might be due to the increased internal residual stress as the pair number increases. Overall, the maximal pair number of SiOx/SiCxHy on PMP was limited to three in order to avoid film cracking and packaging failure.
Figure 2 shows the WVTR at 40 °C/100% RH of the SiOx/SiCxHy stacked layers with one, two, and three pairs. It can be seen that the WVTR of the PMP substrate is as high as 775 g/m2/day. The one-pair SiOx/SiCxHy significantly reduced WVTR values to 8.82 g/m2/day, which further decreases to 1.04 g/m2/day for the two-pair SiOx/SiCxHy. The three-pair SiOx/SiCxHy demonstrates a WVTR value of 0.57 g/m2/day. The reduction in WVTR can be related to the increase of the total thickness of the gas barrier, which causes the water vapor to spend more time traveling through the barrier layer to the other side. A WVTR value ranging from 0.01 to 1 g/m2/day is suggested for food packaging [17]. The PMP substrate can satisfy this requirement if the three-pair SiOx/SiCxHy film is coated.
The hydrophobicity of a packaging material is a major concern, as it limits water vapor attachments. However, the SiOx/SiCxHy stacked films may exhibit a hydrophilic surface with the water contact angle <90°, due to the hydrophilicity of the silicon oxide nature. In this study, a 30 nm SiCxHy layer was intentionally added to the top of the stacked structure to produce a hydrophobic surface. The water contact angle measurement results for the PMP without, and with SiCxHy/three-pair SiOx/SiCxHy stack are shown in Figure 3. The water contact angles for the PMP without and with the stacked layer are approximately 65° and 102°, respectively. Hydrophobic properties are known to be observed at contact angles above 90° [18]. The PMP with the stacked layer is confirmed to attain a desirable level of hydrophobicity.

3.2. Evaluation of the Antibacterial Effect

The adhesion of the microbes covered by PMP without and with stacked layers is observed by SEM, and the ratio of microbes to sample area as a function of time is shown in Figure 4. For the PMP substrate without the stacked layers, the microbe ratio is negligible for the first 8 h. Afterwards, the ratio rapidly increases to 80% at 72 h. With the stacked layers, the microbe ratio significantly decreases as compared to that of the PMP without stacked layers. The one- and two-pair stacked layers can lead to a microbe ratio of 0% within 12 h, while the PMP with the three-pair stacked layer demonstrates no microbe adhesion within 24 h. This result indicates the great antibacterial function of the PMP with the SiOx/SiCxHy stacks. The SEM images at a certain position on each sample at 72 h are shown in Figure 5. The microbe ratios are 79.3%, 25.9%, 18.5%, and 3.9% for the PMP without, and with one-, two-, and three-pair stacked layers, respectively.
The PMP substrates without and with different pairs of SiOx/SiCxHy stacked films are applied to food packaging, and the appearances of the packed toasts stored at 80% RH and 28 °C after 120 h are shown in Figure 6. In this study, we choose the toast without any added preservatives. It can be observed that fungi grow on the toasts packed by the PMP without, as well as with one-pair and two-pair SiOx/SiCxHy stacked films. While the toast packed with the three-pair stacked film shows the absence of fungi growth. The extent of the fungi growth is evaluated as listed in Table 1. The area ratio of the fungi to sample surface is greater than 2% for the PMP substrate without the stacked films. The ratio is significantly reduced to less than 1% for the PMP with one pair of stacked film. The two-pair stacked film further decreases the ratio to 0.7%. Finally, no observable fungi are presented for the three-pair stacked film. The trend of this result can be directly linked to the WVTR values. Lower WVTR value means decreased water and vapor pass through the packaging layer, and this reduces fungi growth.
The package technique in this work can be used in large area (25 cm × 25 cm) or roll-to-roll deposition, as shown in Figure 7. The PMP with the three-pair stacked film can easily be stretched and rolled without obvious film cracking, and the film retains its flexibility. The SiOx/SiCxHy stacked film demonstrates great potential to be used in food package applications.

4. Conclusions

Silicon-based SiOx and SiCxHy layers are prepared on PMP using the ICPCVD system. The PMP with the three-pair SiOx/SiCxHy stack shows a low WVTR value of 0.57 g/m2/day and a high contact angle value of 102°. The three-pair stack exhibits a remarkable antibacterial ability against E. coli within 24 h. The food package testing shows that the PMP with the stacked films can extend the food shelf-life to 120 h at 28 °C and 80% RH. These results suggest that the SiOx/SiCxHy stack has great moisture barrier property as well as antimicrobial characteristics, making it useful in food packaging applications.

Acknowledgments

This work is sponsored by the Ministry of Science and Technology of the Republic of China under contract Nos. 105-2632-E-212-001- and 104-2221-E-212-002-MY3.

Author Contributions

Hsin-Yu Wu and Shui-Yang Lien designed the experiments; Hsin-Yu Wu, Ting-Xuan Liu, Zhi-Jia Xu and Bo-Han Zeng performed the experiments and measurements; Hsin-Yu Wu, Ting-Xuan Liu, Chia-Hsun Hsu, Yun-Shao Cho, Zhi-Jia Xu, Shu-Chuan Liao, Bo-Han Zeng, Yeu-Long Jiang and Shui-Yang Lien analyzed the results; Hsin-Yu Wu, Chia-Hsun Hsu and Shu-Chuan Liao wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Tripathi, S.; Mehrotra, G.K.; Dutta, P.K. Physicochemical and bioactivity of cross-linked chitosan–PVA film for food packaging applications. Int. J. Biol. Macromol. 2009, 45, 372–376. [Google Scholar] [CrossRef] [PubMed]
  2. Silvestre, C.; Duraccio, D.; Marra, A.; Strongone, V.; Cimmino, S. Development of antibacterial composite films based on isotactic polypropylene and coated ZnO particles for active food packaging. Coatings 2016, 6, 4. [Google Scholar] [CrossRef]
  3. Krepker, M.; Shemesh, R.; Poleg, Y.D.; Kashi, Y.; Vaxman, A.; Segal, E. Active food packaging films with synergistic antimicrobial activity. Food Control 2017, 76, 117–126. [Google Scholar] [CrossRef]
  4. Vasile, C.; Sivertsvik, M.; Mitelut, A.C.; Brebu, M.A.; Stoleru, E.; Rosnes, J.T.; Tanase, E.E.; Khan, W.; Pamfil, D.; Cornea, C.P.; et al. Comparative Analysis of the Composition and active property evaluation of certain essential oils to assess their potential applications in active food packaging. Materials 2017, 10, 45. [Google Scholar] [CrossRef]
  5. Soumya, B.N.; Jyothi, A.N.; Sajeev, M.S. Chitosan-konjac glucomannan-cassava starch-nanosilver composite films with moisture resistant and antimicrobial properties for food-packaging applications. Starch-Starke 2017, 69, 1600210. [Google Scholar]
  6. Martin, S. Atmospheric pressure PE-CVD of silicon based coatings using a glow dielectric barrier discharge. Surf. Coat. Technol. 2004, 177, 693–698. [Google Scholar] [CrossRef]
  7. Scopece, P.; Viaro, A.; Sulcis, R.; Kulyk, I.; Patelli, A.; Guglielmi, M. SiOx-based gas barrier coatings for polymer substrates by atmospheric pressure plasma jet deposition. Plasma Process. Polym. 2009, 6, S705–S710. [Google Scholar] [CrossRef]
  8. Plog, S.; Schneider, J.; Walker, M.; Schulz, A.; Stroth, U. Investigations of plasma polymerized SiOx barrier films for polymer food packaging. Surf. Coat. Technol. 2011, 205, S165–S170. [Google Scholar] [CrossRef]
  9. Deilmann, M.; Grabowski, M.; Theiß, S.; Bibinov, N.; Awakowicz, P. Permeation mechanisms of pulsed microwave plasma deposited silicon oxide films for food packaging applications. J. Phys. D Appl. Phys. 2008, 41, 135207. [Google Scholar] [CrossRef]
  10. Fei, F.; Wang, Z.; Chen, Q.; Liu, Z.; Sang, L. Study of functional barrier layer on PVC by PECVD for migrations resistant. Surf. Coat. Technol. 2013, 228, S61–S66. [Google Scholar] [CrossRef]
  11. Michaljanicova, I.; Slepicka, P.; Kasalkova, N.S.; Sajdl, P.; Svorcik, V. Plasma and laser treatment of PMP for biocompatibility improvement. Vacuum 2014, 107, 184–190. [Google Scholar] [CrossRef]
  12. Kima, H.; Sohn, S. Permeabilities of inorganic thin composite (SiO2)1-x(ZnO)x Films prepared by RF-magnetron sputtering method. ECS Trans. 2009, 19, 795–802. [Google Scholar]
  13. Schneider, C.A.; Rasband, W.S.; Eliceiri, K.W. NIH image to imageJ: 25 years of image analysis. Natl. Methods 2012, 9, 671–675. [Google Scholar] [CrossRef]
  14. ImageJ, version 1.50i; Software for Image Processing and Analysis; National Institutes of Mental Health: Bethesda, MD, USA, 2016.
  15. Koo, W.H.; Jeong, S.M.; Choi, S.H.; Baik, H.K.; Lee, S.M.; Lee, S.J. Water Vapor Barrier Properties of Transparent SnO2-SiOx Composite Films on Polymer Substrate. J. Phys. Chem. B 2004, 108, 18884–18889. [Google Scholar] [CrossRef]
  16. Dimitrov, V.; Komatsu, T. Classification of Simple Oxides: A Polarizability Approach. J. Sol. State Chem. 2002, 163, 100–112. [Google Scholar] [CrossRef]
  17. Spee, D.A.; Rath, J.K.; Schropp, R.E.I. Using hot wire and initiated chemical vapor deposition for gas barrierthin film encapsulation. Thin Solid Films 2015, 575, 67–71. [Google Scholar] [CrossRef]
  18. Block, S.; Hupfield, P.; Itami, Y.; Kitaura, E.; Kleyer, D.; Masutani, T.; Nakai, Y. New Anti-Fingerprint Coatings. PCI Mag. 2008, 24, 88–93. [Google Scholar]
Figure 1. Optical microscope images of the polymethylpentene (PMP) without, with one-, two-, three- and four-pair SiOx/SiCxHy films.
Figure 1. Optical microscope images of the polymethylpentene (PMP) without, with one-, two-, three- and four-pair SiOx/SiCxHy films.
Materials 10 00821 g001
Figure 2. Water vapor transmission rate for the PMP without and with one-, two-, and three-pair SiOx/SiCxHy layers at 40 °C/100% relative humidity (RH).
Figure 2. Water vapor transmission rate for the PMP without and with one-, two-, and three-pair SiOx/SiCxHy layers at 40 °C/100% relative humidity (RH).
Materials 10 00821 g002
Figure 3. Water contact angle images for the PMP (a) without and (b) with SiCxHy/three-pair SiOx/SiCxHy stack.
Figure 3. Water contact angle images for the PMP (a) without and (b) with SiCxHy/three-pair SiOx/SiCxHy stack.
Materials 10 00821 g003
Figure 4. Ratio of microbe adhesion area to sample area for PMP without and with different pairs of SiOx/SiCxHy stacked films as a function of time.
Figure 4. Ratio of microbe adhesion area to sample area for PMP without and with different pairs of SiOx/SiCxHy stacked films as a function of time.
Materials 10 00821 g004
Figure 5. SEM images for Escherichia coli adhesion on PMP without and with different pairs of SiOx/SiCxHy stacked films at 72 h. The percentage represents the ratio of microbes to total area.
Figure 5. SEM images for Escherichia coli adhesion on PMP without and with different pairs of SiOx/SiCxHy stacked films at 72 h. The percentage represents the ratio of microbes to total area.
Materials 10 00821 g005
Figure 6. Images of food packed by PMP without and with different pairs of SiOx/SiCxHy stacked film.
Figure 6. Images of food packed by PMP without and with different pairs of SiOx/SiCxHy stacked film.
Materials 10 00821 g006
Figure 7. Photograph of stretched and rolled PMP with three-pair SiOx/SiCxHy stack.
Figure 7. Photograph of stretched and rolled PMP with three-pair SiOx/SiCxHy stack.
Materials 10 00821 g007
Table 1. Extent of fungi growth area ratio for food packed by PMP without and with different pairs of SiOx/SiCxHy stacked film.
Table 1. Extent of fungi growth area ratio for food packed by PMP without and with different pairs of SiOx/SiCxHy stacked film.
Type of PackagingPMP1-Pair2-Pair3-Pair
Fungi growth 1++++++
1 absence of fungal growth, + fungal growth on <0.7% of the surface, ++ fungal growth on <1% of the surface, +++ fungal growth on >2% of the surface.

Share and Cite

MDPI and ACS Style

Wu, H.-Y.; Liu, T.-X.; Hsu, C.-H.; Cho, Y.-S.; Xu, Z.-J.; Liao, S.-C.; Zeng, B.-H.; Jiang, Y.-L.; Lien, S.-Y. Thin-Film Coated Plastic Wrap for Food Packaging. Materials 2017, 10, 821. https://doi.org/10.3390/ma10070821

AMA Style

Wu H-Y, Liu T-X, Hsu C-H, Cho Y-S, Xu Z-J, Liao S-C, Zeng B-H, Jiang Y-L, Lien S-Y. Thin-Film Coated Plastic Wrap for Food Packaging. Materials. 2017; 10(7):821. https://doi.org/10.3390/ma10070821

Chicago/Turabian Style

Wu, Hsin-Yu, Ting-Xuan Liu, Chia-Hsun Hsu, Yun-Shao Cho, Zhi-Jia Xu, Shu-Chuan Liao, Bo-Han Zeng, Yeu-Long Jiang, and Shui-Yang Lien. 2017. "Thin-Film Coated Plastic Wrap for Food Packaging" Materials 10, no. 7: 821. https://doi.org/10.3390/ma10070821

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop