Characterization of the Materials Synthesized by High Pressure-High Temperature Treatment of a Polymer Derived t-BC2N Ceramic
Previous Article in Journal
Dense CO2 as a Solute, Co-Solute or Co-Solvent in Particle Formation Processes: A Review
Previous Article in Special Issue
The Origin of Tc Enhancement in Heterostructure Cuprate Superconductors
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Nanorod Self-Assembly in High Jc YBa2Cu3O7−x Films with Ru-Based Double Perovskites

1
Superconductivity Technology Center, 30 Bikini Atoll Rd, Los Alamos, NM 87545, USA
2
Condensed Matter and Magnet Science, Materials Physics and Applications Division, Los Alamos National Laboratory, Los Alamos, NM 87545, USA
*
Author to whom correspondence should be addressed.
Materials 2011, 4(11), 2042-2056; https://doi.org/10.3390/ma4112042
Submission received: 7 September 2011 / Revised: 24 October 2011 / Accepted: 9 November 2011 / Published: 17 November 2011
(This article belongs to the Special Issue New High Tc Superconductor)

Abstract

:
Many second phase additions to YBa2Cu3O7−x (YBCO) films, in particular those that self-assemble into aligned nanorod and nanoparticle structures, enhance performance in self and applied fields. Of particular interest for additions are Ba-containing perovskites that are compatible with YBCO. In this report, we discuss the addition of Ba2YRuO6 to bulk and thick-film YBCO. Sub-micron, randomly oriented particles of this phase were found to form around grain boundaries and within YBCO grains in bulk sintered pellets. Within the limits of EDS, no Ru substitution into the YBCO was observed. Thick YBCO films were grown by pulsed laser deposition from a target consisting of YBa2Cu3Oy with 5 and 2.5 mole percent additions of Ba2YRuO6 and Y2O3, respectively. Films with enhanced in-field performance contained aligned, self-assembled Ba2YRuO6 nanorods and strained Y2O3 nanoparticle layers. A 0.9 µm thick film was found to have a self-field critical current density (Jc) of 5.1 MA/cm2 with minimum Jc(Θ, H=1T) of 0.75 MA/cm2. Conversely, Jc characteristics were similar to YBCO films without additions when these secondary phases formed as large, disordered phases within the film. A 2.3 µm thick film with such a distribution of secondary phases was found to have reduced self-field Jc values of 3.4 MA/cm2 at 75.5 K and Jc(min, Θ, 1T) of 0.4 MA/cm2.

1. Introduction

Optimizing the film deposition for high-performance thick films of the high-temperature superconductor (HTS) YBa2Cu3Oy (YBCO) and rare-earth substituted polymorphs (REBCO) is a critical area of HTS wire development. HTS coated conductor wires are engineered composites consisting of epitaxially deposited buffer and HTS layers on bi-axially textured templates [1,2,3,4,5]. Applications of HTS wires in transmission lines, motors, and generators require operation of the conductor in moderate to high magnetic fields [6,7]. Efforts to minimize dissipation arising from vortex motion in applied fields have resulted in HTS films that are highly-engineered materials consisting of YBCO or REBCO films with well-defined distributions of nano-sized defects and/or second-phases. These defects and secondary phases need to have dimensions on the order of 5–10 nm in order to effectively pin vortices and improve the overall performance in self and applied magnetic fields at liquid nitrogen temperatures and below [8].
Maximizing the temperature (T) and magnetic field (H) dependent critical current density (Jc) requires optimization of the size, density and distribution of nanoscale structures which act as vortex pins [9,10]. The anisotropic nature of YBCO and its effects on Jc(H, Θ, T) further complicate this process by requiring optimization of pinning defects for different orientations of applied field [11]. Significant effort has been spent to introduce nanoscale pinning structures in materials such as YBCO and REBCO though the incorporation of second phase materials such as BaZrO3 [12,13,14], BaSnO3 [15], Y2O3 [16] Y2BaCuO5 (Y-211) [17] or rare-earth tantalates [18] to the YBCO source material to induce second phase growth. Efforts are made to maximize self-field Jc, while maintaining the highest possible minimum Jc for any applied field orientation (Θ) [14]. Recent results combining both Y2O3 and BaZrO3 additions in a single-layer, 1.95 μm thick film returned a Jc(75.6K, self-field) of 5.2 MA/cm2 (1010 A/cm-w) and a minimum Jc(75.6K, 1T) of 1.2 MA/cm2 (240 A/cm-w) in the maximum Lorentz force measurement configuration [19]. Self-assembled Y2O3 nanoparticle layers and Zr-based nanorods were produced in these films as pinning defect structures for H||ab and H||c, respectively.
Perovskite-based additions have garnered the most interest as a class of materials for incorporation into REBCO films. It was suggested early on that perovskites could be easily incorporated into YBCO or used as substrates due to their similar crystal structures to YBCO [20,21,22,23,24]. Many Ba-containing perovskites, including those with Zr [25], are double-perovskites of the general form A2BB′O6. One early work in the field reported the formation of Ba2YNbO6 within YBCO films, but without improvements in performance [24]. However, renewed interest in the double perovskites was recently generated from works with pulsed laser deposition (PLD) films in which BaNbO3 additions to an ErBa2Cu3Oy source material resulted in self-assembled nanorods of the double perovskite Ba2ErNbO6 within the Er-123 film matrix [26,27]. The nanorods were shown to easily span the entire thickness of the ErBa2Cu3Oy film. Other groups quickly followed with positive results using Ba2YNbOy additions to Y-123 films [28,29,30]. Recently, extremely high pinning forces (Fp) were obtained in a 0.5 μm thick film with Jc(75.6 K, 1T, H||c) > 2 MA/cm2 and Fp (H||c) values in excess of 30 and 120 GN/m3 at 75.5 K and 65 K, respectively [28,29,30]. Such results have spurred further efforts in exploring other possible perovskite-based additions. In this work, we report our results on the incorporation of a Ru-based double-perovskite phase into bulk YBCO and the deposition of YBCO films with Ba2YRuOy nanorod structures and enhanced Jc performance in self and applied magnetic fields.

2. Results and Discussion

It is well known that a large number of perovskites can be formed with Ba [31,32,33] However, their incorporation into YBCO bulk and film forms must occur with minimal detrimental effects to the superconducting phase. Ruthenium was investigated as a potential material for addition to YBCO based on its known formation into the ordered, tilted perovskite A2BB’O6 of composition Ba2YRuO6 [32]. Its compatibility with YBCO was tested with mixtures of bulk YBCO and RuO2 additions and its potential for performance improvements though its incorporation as nanorod secondary phases in YBCO films. It should be noted that Ru is an expensive material. Based on 5 mol % additions of Ba2YRuO6 to YBCO in the fabrication of the targets used for PLD, costs for the HTS materials would increase by 13 to 22%, depending on the starting purity of the RuO2.

2.1. Ba2YRuO6 Double-Perovskite

Ba2YRuO6 was synthesized as a single phase material using conventional milling and sintering processes. Shown in Figure 1 is the XRD scan of the single-phase material and its ordered crystal structure. Table 1 contains the XRD data pertaining to observed and calculated peak positions and intensities. A single-phase diffraction pattern characteristic of a perovskite was obtained. The refined lattice parameter based on the integrated Bragg reflections obtained from diffraction experiments using Si (NIST SRM 640a) mixed in with the sample was a0 = 8.3381(4). Observed intensities and peak positions are consistent with previous reported work on this phase which includes ordering of the Y and Ru atoms on the B sites of the perovskite structure [32].
Figure 1. (a) XRD powder diffraction scan of Ba2YRuO6. The refined lattice parameter from this material was found to be a0 = 8.3381(4); (b) Crystral structure of Ba2YRuO6 based on space group Fm-3m and atom positions from reference [32].
Figure 1. (a) XRD powder diffraction scan of Ba2YRuO6. The refined lattice parameter from this material was found to be a0 = 8.3381(4); (b) Crystral structure of Ba2YRuO6 based on space group Fm-3m and atom positions from reference [32].
Materials 04 02042 g001
Table 1. Table of observed and calculated XRD characteristics for Ba2YRuO6. Calculated values are based on the earlier work of Battle et al. with a0 = 8.3390(5) and space group Fm-3m.
Table 1. Table of observed and calculated XRD characteristics for Ba2YRuO6. Calculated values are based on the earlier work of Battle et al. with a0 = 8.3390(5) and space group Fm-3m.
hkl2Q(obs)Int(obs)d(obs)2Q(calc)d*(calc)Int*(calc)
11118.41514.81418.45494.803440.8
00221.2821.34.171521.3414.15990.6
02230.2831002.94930.36052.94149100
113 35.76362.508510.1
22237.3235.12.407337.41152.401725.8
00443.362292.08543.47092.0799530.9
133 47.60041.908690
02448.7530.51.866348.91671.860360.5
22453.80531.81.702453.94331.6982739.3
115 57.50951.601150.2
04463.00513.81.474263.16341.4707518.7
135 66.42051.40630.1
006 67.48781.386630.3
02671.504121.318471.68081.3154817.4
335 74.75881.268760
226 75.77441.254261.5
44479.6043.51.203379.79491.200866.2
117 82.77621.165010.1
046 83.76521.153750.2
24687.48511.31.114187.70561.1117821.4

2.2. Bulk YBCO with RuO2 Additions

Shown in Figure 2 are SEM and STEM images of material taken from a pressed pellet containing 9 wt % RuO2 additions to stoichiometric YBCO powder. The resulting material was multiphase containing primarily YBCO and a sub-micron sized secondary phase containing Ru along with small amounts of BaCu2Oy and CuO, STEM/EDS analysis suggested an approximate ratio of 2:1:1 of Ba:Y:Ru with a small amount of Cu present in the material. However, the copper content in this phase was not consistent with the reported formation of the 2411 phase in other works [34]. Within the limits of EDS, no Ru was detected within the YBCO phase. Figure 3 contains the XRD analysis of the pellet which showed a multiphase material with the major peaks identified as either YBCO or the double-perovskite Ba2YRuO6. The intensities of the peaks associated with Ba2YRuO6 are consistent with the observed amounts of the double-perovskite phase present in the sample.
Figure 2. (a) SEM backscattered electron image and (b) STEM Z-contrast image showing the large amount of submicron Ru-containing secondary phases formed in the bulk YBCO sample containing 9 wt % additions of RuO2. The inclusion of round, sub-micron grains and clusters of grains within the YBCO phase is readily apparent in (b). Ba-Cu-O is also present in the form of large irregularly shaped phases as indicated.
Figure 2. (a) SEM backscattered electron image and (b) STEM Z-contrast image showing the large amount of submicron Ru-containing secondary phases formed in the bulk YBCO sample containing 9 wt % additions of RuO2. The inclusion of round, sub-micron grains and clusters of grains within the YBCO phase is readily apparent in (b). Ba-Cu-O is also present in the form of large irregularly shaped phases as indicated.
Materials 04 02042 g002
Figure 3. XRD scan of the bulk sample consisting of YBCO powder with 9 wt % RuO2 additions. Most peaks in the XRD scan can be indexed to YBCO or Ba2YRuO6 (*).
Figure 3. XRD scan of the bulk sample consisting of YBCO powder with 9 wt % RuO2 additions. Most peaks in the XRD scan can be indexed to YBCO or Ba2YRuO6 (*).
Materials 04 02042 g003

2.3. YBCO with Self-Assembled Nanorods of Ba2YRuOy

Films containing the Ba2YRuOy (BRYO) secondary phase were grown from PLD targets consisting of YBa2Cu3Oy with 2.5 mol % additions of Y2O3 and 5 mol % additions of Ba2YRuO6. The addition of the extra Y2O3 was included for the purposes of producing the two-phase pinning mesostructure of strained Y2O3 nanoparticle layers and perovskite-based nanorods [19]. High self-field Jc values of 5.0, 5.1, 4.5, and 3.4 MA/cm2 were obtained in measurements at 75.5 K and self-field for films of thickness 0.85, 0.9, 0.95 and 2.3 μm, respectively.
Detailed Jc characteristics of the 0.95 and 2.3 µm thick films are shown in Figure 4, which contains the angular dependence of Jc for applied magnetic fields of 1, 3, and 5 T. The 0.95 µm film had a self-field Jc value of 4.5 MA/cm2 along with Jc(H=1T, H||c) = 0.75 MA/cm2 and Jcmin(Θ, H=1T) = 0.7 MA/cm2. The 2.3 µm thick film had a self-field Jc value of 3.4 MA/cm2 along with Jc(H=1T, H||c) = 0.45 MA/cm2 and Jcmin(Θ, H=1T) = 0.4 MA/cm2. For reference, a plain YBCO without nanorod structures would have a Jcmin(Θ, H=1T) = 0.4 MA/cm2 [35]. While there was clearly an Jc(H) improvement for the 0.95 micron thick film, there was essentially none above what would be expected for plain YBCO for the 2.3 micron thick film. Hence, a close comparison of the microstructural properties with Jc performance is necessary for understanding these differences.
Figure 4. (a) Measurement of the Jc characteristics at 75.5 K as a function of magnetic field strength and applied field orientation for a 0.95 μm thick film; and (b) a 2.3 μm thick film.
Figure 4. (a) Measurement of the Jc characteristics at 75.5 K as a function of magnetic field strength and applied field orientation for a 0.95 μm thick film; and (b) a 2.3 μm thick film.
Materials 04 02042 g004
Figure 5 shows the general microstructure of a 0.9 µm thick film which had a self-field Jc of 5.1 MA/cm2. This film also showed enhanced performance with Jc(H=1T, H||c) = 0.8 MA/cm2 and Jcmin(Θ, H=1T) = 0.75 MA/cm2. The second phase assemblage or mesostructure within the film consisted of BRYO nanorods aligned with the film normal and tilted Y2O3 nanoparticle layers. The STEM and EDS spectral images of Figure 6 show the Ru to be associated with the BYRO nanorod structures that are continuous though the full thickness of the film. EDS analysis of the BYRO nanorods showed a small copper content. However, the amount detected was not consistent with the reported 2411 phase [36]. The continuous nature of these nanorod structures is confirmed with the Moire fringe analysis shown in Figure 7. Growth of the nanorods starts at the CeO2 buffer layer. Indexing of the diffraction pattern the double perovskite in Figure 5(a) revealed the nanorod phases to have an alignment defined by [1,2,3,4,5,6,7,8,9,10] BRYO || [1,2,3,4,5,6,7,8,9,10] YBCO with (220) BRYO || (110) YBCO, identical to the one found for Ba2YNbO6 nanorods [28]. The lobe-shaped contrast around the Y2O3 particles in the TEM image (arrows Figure 5(b)) indicates that the alignment of the Y2O3 particles with the YBCO is highly strained. Hence, these additions were nearly successful in the reproduction of the idealized, two phase, strained nanoparticle layer and nanorod pinning mesostructure as first reported by the Los Alamos group [14,19]. The only difference between the ideal structure and the mesostructure observed here being the continuous nature of the BYRO nanorods versus the short, segmented structure of the Zr-based nanorods.
Figure 5. (a) TEM diffraction data for the 0.9 µm thick film showing the alignment of the Ba2YRuO6 phase with YBCO; (b) High magnification bright field TEM image showing the BRYO nanords (white dots) and strained and tilted Y2O3 (arrows) nanoparticle layers. Low magnification TEM bright field (c) and weak-beam (d) images showing a mostly uniform distribution of secondary phases in this particular TEM specimen.
Figure 5. (a) TEM diffraction data for the 0.9 µm thick film showing the alignment of the Ba2YRuO6 phase with YBCO; (b) High magnification bright field TEM image showing the BRYO nanords (white dots) and strained and tilted Y2O3 (arrows) nanoparticle layers. Low magnification TEM bright field (c) and weak-beam (d) images showing a mostly uniform distribution of secondary phases in this particular TEM specimen.
Materials 04 02042 g005
Figure 6. STEM bright-field image and associated energy dispersive spectral imaging showing Ru in secondary phases.
Figure 6. STEM bright-field image and associated energy dispersive spectral imaging showing Ru in secondary phases.
Materials 04 02042 g006
Figure 7. (a) TEM two-beam, bright field image of the nanorods imaged using conditions g = (110) and (b) g = (00–6). The continuous Moiré fringe structure in (a) shows that each nanorod is a single phase rather than a stack of individual particles.
Figure 7. (a) TEM two-beam, bright field image of the nanorods imaged using conditions g = (110) and (b) g = (00–6). The continuous Moiré fringe structure in (a) shows that each nanorod is a single phase rather than a stack of individual particles.
Materials 04 02042 g007
The improvements in observed performance, relative to plain YBCO are then understood quite well. In this particular TEM FIB specimen, the distribution of the secondary phases was very uniform as indicated by the low magnification images of Figure 5(c,d). Figure 5(d), the dark-field, weak-beam TEM image shows this distribution quite well. Weak-beam diffraction contrast is well-suited for imaging the nano-sized phases and structures at relatively low magnifications as the strain associated with the phases allows the phases to be highlighted in the images. The arrows in Figure 5(c) indicate localized reactions between the substrate and CeO2 buffer layer to form BaCeO3 [37]. This latter phase is not aligned and appears dark against the contrast from the YBCO film in the weak-beam image of Figure 5(d). The low-magnification TEM images also show the surface porosity “P” that is commonly found in these PLD films when the surface morphology is examined in the SEM. While the porosity depth is small for these nominally 1 micron thick samples, it becomes more pronounced for the thicker films as shown below.
While an enhancement in the in-field performance of the films of thickness 0.85 to 0.95 µm in thickness was observed, the absolute level of performance was still not to the level of the best, optimized YBCO films with BaZrO3 and Y2O3 additions. Hence, further microstructural investigations were undertaken using plan view (S)TEM. Figure 8(a) shows a STEM plan view image where the observed material is located near the top surface of the 0.9 µm thick film described above. As indicated by the circles, areas could be identified that were devoid of any secondary phases. Further investigations of this film with additional cross-sectional specimens showed that indeed, these regions existed within the films. These clear areas were found to occur above regions where interruptions occurred in the development of the nanorod/strained nanoparticle mesostructure. As shown in the example of Figure 8(b), growth of the nanorod/nanoparticle mesostructure did not occur across the full thickness of the film. Instead, there was a change to a structure that ended with large Y2O3/ Ba2YRuO6 composite particles capping the growth of the nanorods. Above this structure, a region free of secondary phases could be found. This degradation of the mesostructure was present in moderate amounts in the submicron films and would explain why the in-field performance of these first films were not to the levels found in related films that have been optimized for additions of BaZrO3, for example [19]. The mechanism for this mesostructure degradation will be the focus of future work.
Figure 8. (a) Areas devoid of secondary phases are highlighted in the plan-view, bright-field STEM image of the 0.95 mm thick film taken from an area near the top surface of the film. (b) White dots in the cross-sectional TEM bright-field mark large Y2O3 particles that cap or disrupt the growth of the BRYO nanorods, resulting in nearby areas of the YBCO film to be devoid of secondary phases.
Figure 8. (a) Areas devoid of secondary phases are highlighted in the plan-view, bright-field STEM image of the 0.95 mm thick film taken from an area near the top surface of the film. (b) White dots in the cross-sectional TEM bright-field mark large Y2O3 particles that cap or disrupt the growth of the BRYO nanorods, resulting in nearby areas of the YBCO film to be devoid of secondary phases.
Materials 04 02042 g008
The identification of the mesostructure degradation in regions of the nominally 1 µm thick films was important as it leads to the basis of understanding performance degradation in the 2.3 µm thick film. While the self-field Jc value of 3.4 MA/cm2 obtained in the latter film was very respectable, its Jc performance in field was no different from that measured in plain YBCO films without c-axis aligned defects. Now it has been commonly observed in many works that Jc decreases as a function of film thickness (See reference [9] and works cited therein). It is tempting to assume that this is an intrinsic property of these thick films. However, in recent works where detailed microstructural analysis was coupled to film performance in high quality PLD or ex situ metal orgranic deposition (MOD) films, it was shown that Jc becomes independent of thickness when the microstural features are uniform though thickness [10,19,38]. The 2 micron, 5 MA/cm2 (75K, SF) film reported by Feldmann et al. is a clear illustration of the effects of uniformity though thickness and its pronounced influence on film properties. It also strongly supports the notion that the Jc dependence for film thickness is an extrinsic property.
The STEM images of Figure 9 show significant degradation of the film structure, especially for those sections of the film more than 0.5 microns from the CeO2 buffer. The z-contrast image, Figure 9a, shows a distribution of large secondary phases that appear to be composites of multiple phases based on their z-contrast. The spectral imaging data of Figure 10 revealed these composite phases to be composed of Y2O3 and Ba2YRuO6. Hence, we attribute the degradation of the in-field properties to the consolidation of the nanorod/strained nanoparticle mesostructure into large composite secondary phases. The remaining BYRO nanorods that are still present in this sample are much larger and irregularly shaped compared to those found in the nominally 1 µm thick films. Understanding the underlying causes to the changes in this mesostructure is important for incorporating these structures into continuous processing of YBCO films for long-length wires [39,40]. Related work by one of the authors suggests that these same degradation mechanisms can also occur in films with BaZrO3 or Ba2YNbO6 additions [41]. The difference in the mesostructure would also explain the early results with Ba2YNbO6 additions in which the phases were present, but no appreciable increase in performance was observed [24].
Figure 9. (a) STEM Z-contrast image showing a distribution of large Y2O3 particles, many of which appear to have a composite structure containing a second, higher Z material (arrows); (b) Bright field STEM image showing the splayed, ill-formed, and non-continuous network of BRYO nanorods (white dots) within this thick film. Surface pores, which extend into the sample for appreciable distances in this thick film, are marked with a “P”.
Figure 9. (a) STEM Z-contrast image showing a distribution of large Y2O3 particles, many of which appear to have a composite structure containing a second, higher Z material (arrows); (b) Bright field STEM image showing the splayed, ill-formed, and non-continuous network of BRYO nanorods (white dots) within this thick film. Surface pores, which extend into the sample for appreciable distances in this thick film, are marked with a “P”.
Materials 04 02042 g009
Figure 10. STEM Z-contrast image and associated EDS spectral images showing that large, striped secondary phases are actually composites of Y2O3 and the BRYO double-perovskite.
Figure 10. STEM Z-contrast image and associated EDS spectral images showing that large, striped secondary phases are actually composites of Y2O3 and the BRYO double-perovskite.
Materials 04 02042 g010

3. Experimental Section

Ba2YRuO6 was prepared by mixing individual elemental oxide precursors and milling for 8 h in a Retsch mortar grinder with distilled H2O, Isopropanol, and KD-1 dispersant. After milling, the slurry was dried on a Schlink line. The dried powder was hand-ground with a mortar and pestle and pressed at 5 K psi into 1.25 cm diameter pellets. The pellets were heat treated in flowing O2 in a high-temperature box furnace. The pellets were ramped to 1000 °C at 10 °C/h and held for 15 h. They were then ramped at 1 °C/h to 1550 °C and held for 15 h. The pellets were then cooled to 1000 °C at 2 °C/h for a final dwell of 2 h, and then ramped to room temperature at 15 °C/h. Bulk YBa2Cu3O7 (YBCO) pellets with additions of 9 wt % RuO2 were prepared by milling stoichiometric mixtures of prepared YBCO with RuO2. The powders were pressed into 1.25 cm diameter pellets which were then sintered at 1000 °C for 50 h, followed by an annealing step at 400 °C for 50 h in flowing oxygen. Powder X-ray diffraction (XRD) patterns were obtained on a Scintag X-1 Advanced Diffraction System using filtered Cu Ka radiation (λ = 1.5406 Å). XRD patterns were taken with and without a Si reference material (NIST SRM 640a); scans with Si were used for quantitative structure refinements. Scans were collected at room temperature in Θ-Θ mode (2Θ = 90°) with a step size of 0.02 and collection time of 10 sec/step. The XRD data collected was analyzed though the Jade 6.5 software package which as used for phase identification and determination of refined unit cell parameters [42]. Crystal structures and calculated diffraction patterns were obtained using CrystalMaker® [43]. Targets for pulsed laser deposition (PLD) were made by mixing precursor powders in the desired ratios, followed by milling in isopropanol in a Retsch motar grinder for 8 h. Powders were dried on a shlenk line and then calcined as a loose powder for 15 h at 900 °C. This powder was then lightly ground in a glove box, pressed into a 5.5 cm diameter target 0.5 cm thick, and then sintered at 925 °C and 950 °C for 15 h each with a furnace cool to 400 °C for 5 h in between steps. The sintering process ended with a low temperature anneal at 400 °C for 50 h.
Films of thickness 0.8 to 2.3 µm were grown by PLD using a KrF laser (248 nm). The target material was YBa2Cu3O7 (YBCO) with 5 mol % additions of Ba2YRuO6 and 2.5 mol % additions of Y2O3. Substrates were single crystals of either SrTiO3 or Y-stabilized Zr2O3 with a 40 nm thick CeO2 buffer layer. The deposition temperature during growth was either 775 °C or 795 °C. Films were patterned for transport measurement using standard photolithography and wet etching techniques. Before photolithography, Ag pads were deposited by thermal evaporation and the films subsequently annealed at 500 °C for 30 minutes in flowing O2. Values of critical temperature (Tc) were determined by an inductive method and values of Jc were determined using the standard 1 µV/cm electric field criterion and a four-point transport measurement. All bridges were 1.5 mm long and approximately 200 µm wide. Measurements of Jc as a function of field orientation were performed in the maximum Lorentz force configuration, with Θ being the angle between the film normal and field vector. Jc measurements in applied magnetic fields were performed in a 1 T split coil electromagnet or in a 7 T split coil superconducting magnet. (Scanning) transmission electron microscopy ((S)TEM) characterizations were performed on foils thinned by either conventional dimple-polishing and ion-milling or foils prepared with a focused ion beam (FIB) technique.

4. Conclusions

We have shown that the double-perovskite Ba2YRuO6 can be an effective and compatible addition for both bulk and thick film YBCO materials. In the former case, this secondary phase distributed itself within the YBCO material as small, sub-micron randomly-oriented secondary phases. Additions of 5 mol % Ba2YRuO6 and 2.5 mol % Y2O3 to YBCO thick films resulted in mesostructures within the film of aligned, continuous BYRO nanorod and strained Y2O3 nanoparticle structures. The departure from the idealized mesostructure being the presence of the continuous, as opposed to the optimal short segmented, nanorods. Self-field Jc values up to 5.2 MA/cm2 were obtained in 0.95 µm thick films with improved in-field performance as indicated by the measured minimum Jc(Θ, H=1T) of 0.75 MA/cm2 We also showed how the degradation to the mesostructure can lead to performance that is not very different from YBCO films without additions. High self-field Jc values are still possible as indicated by the measurement of 3.4 MA/cm2 (self-field, 75.5 K) in a 2.3 µm thick film with the BYRO and Y2O3 additions. However, the degradation of the mesostructure within this thick film results in a measured minimum Jc(Θ, H=1T) of only 0.4 MA/cm2. The observed mesostructure degradation is important in understanding the variable range of performance one can obtain when investigating pinning additions to YBCO films. It is believed that continued optimization of the deposition process and chemistry for Ba2YRuO6 and Y2O3 additions would lead to performance levels comparable to the best achieved with BaZrO3 and Y2O3 additions.

Acknowledgments

The authors would like to acknowledge our discussions of the double-perovskite structure with Kurt Sickafus of LANL. This work was supported by the U.S. Department of Energy, Office of Electricity Delivery and Energy Reliability, as part of a DOE program to develop high temperature superconductors for electric power technologies. Los Alamos National Laboratory is operated for the DOE by Los Alamos National Security, LLC, under contract W-7405-ENG-36.

References

  1. Iijima, Y.; Tanabe, N.; Kohno, O.; Ikeno, Y. In-plane aligned YBa2Cu3O7−x thin films deposited on polycrystalline metallic substrates. Appl. Phys. Lett. 1992, 60, 769–771. [Google Scholar] [CrossRef]
  2. Wu, X.D.; Foltyn, S.R.; Arendt, P.; Townsend, J.; Adams, C.; Campbell, I.H.; Tiwari, P.; Coulter, Y.; Peterson, D.E. High current YBa2Cu3O7−∂ thick films on flexible nickel substrates with textured buffer layers. Appl. Phys. Lett. 1994, 65, 1961–1963. [Google Scholar] [CrossRef]
  3. Arendt, P.N.; Foltyn, S.R.; Groves, J.R.; Depaula, R.F.; Dowden, P.C.; Roper, J.M.; Coulter, J.Y. YBCO/YSZ coated conductors on flexible Ni alloy substrates. Appl. Supercond. 1996, 4, 429–434. [Google Scholar] [CrossRef]
  4. Goyal, A.; Norton, D.P.; Budai, J.D.; Paranthaman, M.; Specht, E.D.; Kroeger, D.M.; Chisten, D.K.; He, Q.; Saffian, B.; List, F.A.; et al. High critical current density superconducting tapes by epitaxial deposition of YBa2Cu3Ox thick films on biaxially textured metals. Appl. Phys. Lett. 1996, 69, 1795–1797. [Google Scholar] [CrossRef]
  5. Arendt, P.N.; Foltyn, S.R. Biaxially textured IBAD-MgO templates for YBCO-coated conductors. MRS Bull. 2004, 29, 543–550. [Google Scholar] [CrossRef]
  6. Larbalestier, D.; Gurevich, A.; Feldmann, D.M.; Polyanskii, A. High-TC superconducting materials for electric power applications. Nature 2001, 414, 368–377. [Google Scholar] [CrossRef] [PubMed]
  7. Scanlan, R.M.; Malozemoff, A.P.; Larbalestier, D.C. Superconducting materials for large scale applications. Proc. IEEE 2004, 92, 1639–1654. [Google Scholar] [CrossRef]
  8. Civale, L.; Marwick, A.D.; Worthington, T.K.; Kirk, M.A.; Thompson, J.R.; Krusin-Elbaum, L.; Sun, Y.; Clem, J.R.; Holtzberg, F. Vortex confinement by columnar defects in YBa2Cu3O7 crystals: Enhanced pinning at high fields and temperatures. Phys. Rev. Lett. 1991, 67, 648–651. [Google Scholar] [CrossRef] [PubMed]
  9. Foltyn, S.R.; Civale, L.; Macmanus-Driscoll, J.L.; Jia, Q.X.; Maiorov, B.; Wang, H.; Maley, M. Materials science challenges for high-temperature superconducting wire. Nat. Mater. 2007, 6, 631–642. [Google Scholar] [CrossRef] [PubMed]
  10. Holesinger, T.G.; Civale, L.; Maiorov, B.; Feldmann, D.M.; Coulter, J.Y.; Miller, D.J.; Maroni, V.A.; Chen, Z.; Larbalestier, D.C.; Feenstra, R.; et al. Progress in nanoengineered microstructures for tunable high-current, high-temperature superconducting wires. Adv. Mater. 2008, 20, 391–407. [Google Scholar] [CrossRef]
  11. Civale, L.; Maiorov, B.; Serquis, A.; Willis, J.O.; Coulter, J.Y.; Wang, H.; Jia, Q.X.; Arendt, P.N.; MacManus-Driscoll, J.L.; Maley, M.P.; et al. Angular-dependent vortex pinning mechanisms in YBa2Cu3O7 coated conductors and thin films. Appl. Phys. Lett. 2004, 84, 2121–2123. [Google Scholar] [CrossRef]
  12. MacManus-Driscoll, J.L.; Foltyn, S.R.; Jia, Q.; Wang, H.; Serquis, A.; Civale, L.; Maiorov, B.; Hawley, M.E.; Maley, M.P.; Peterson, D.E. Strongly enhanced current densities in superconducting coated conductors of YBa2Cu3O7−x + BaZrO3. Nat. Mater. 2004, 3, 439–443. [Google Scholar] [CrossRef] [PubMed]
  13. Goyal, A.; Kang, S.; Leonard, K.J.; Martin, P.M.; Gapud, A.A.; Varela, M.; Paranthaman, M.; Ijaduola, A.O.; Specht, E.D.; Thompson, J.R.; et al. Irradiation-free, columnar defects comprised of self-assembled nanodots and nanorods resulting in strongly enhanced flux-pinning in YBa2Cu3O7−d films. Supercond. Sci. Technol. 2005, 18, 1533–1538. [Google Scholar] [CrossRef]
  14. Maiorov, B.; Baily, S.A.; Zhou, H.; Ugurlu, O.; Kennison, J.A.; Dowden, P.C.; Holesinger, T.G.; Foltyn, S.R.; Civale, L. Synergetic combination of different types of defect to optimize pinning landscape using BaZrO3-doped YBa2Cu3O7. Nat. Mater. 2009, 8, 398–404. [Google Scholar] [CrossRef] [PubMed]
  15. Mele, P.; Matsumoto, K.; Ichinose, A.; Mukaida, M.; Yoshida, Y.; Horii, S.; Kita, R. Systematic study of BaSnO3 doped YBa2Cu3O7−x films. Phys. C Supercond. 2009, 469, 1380–1383. [Google Scholar] [CrossRef]
  16. Lu, P.; Li, Y.Q.; Zhao, J.; Chern, C.S.; Gallois, B.; Norris, P.; Kear, B.; Cosandey, F. High density, ultrafine precipitates in YBa2Cu3O7−x thin films prepared by plasma-enhanced metalorganic chemical vapor deposition. Appl. Phys. Lett. 1992, 60, 1265–1267. [Google Scholar] [CrossRef]
  17. Haugan, T.; Barnes, P.N.; Wheeler, R.; Meisenkothen, F.; Sumption, M. Addition of nanoparticle dispersions to enhance flux pinning of the YBa2Cu3O7−x superconductor. Nature 2004, 430, 867–870. [Google Scholar] [CrossRef] [PubMed]
  18. Harrington, S.A.; Durrell, J.H.; Maiorov, B.; Wang, H.; Wimbush, S.C.; Kursumovic, A.; Lee, J.H.; MacManus-Driscoll, J.L. Self-assembled, rare earth tantalate pyrochlore nanoparticles for superior flux pinning in YBa2Cu3O7 films. Supercond. Sci. Technol. 2009, 22, 02201–02205. [Google Scholar]
  19. Feldmann, D.M.; Holesinger, T.G.; Maiorov, B.; Zhou, H.; Foltyn, S.R.; Coulter, J.Y.; Apodoca, I. 1000 A cm—1 in a 2 µm thick YBa2Cu3O7−x film with BaZrO3 and Y2O3 additions. Supercond. Sci. Technol. 2010, 23, 115016–115023. [Google Scholar] [CrossRef]
  20. Goretta, K.C.; Lacy, O.D.; Balachandran, U.; Shi, D.; Routbort, J.L. YBa2Cu3Ox toughened by ZrO2 additions. J. Mater. Sci. Lett. 1990, 9, 380–381. [Google Scholar] [CrossRef]
  21. Osamura, K.; Kizu, T.; Oku, T. Critical current density in YBa2Cu3O6+x added with perovskite type impurity. Phys. C Supercond. 1994, 226, 113–120. [Google Scholar] [CrossRef]
  22. Paulose, K.V.; Sebastian, M.T.; Nair, K.R.; Koshy, J.; Damodaran, A.D. Synthesis of Ba2YZrO6: A new phase in YBa2Cu3O7-ZrO2 system and its suitability as a substrate material for YBCO films. Solid State Commun. 1992, 83, 985–988. [Google Scholar] [CrossRef]
  23. Paulose, K.V.; Koshy, J.; Damodaran, A.D. YBa2NbO6: Synthesis, properties and compatibility with YBa2Cu3O7−d. Phys. C Supercond. 1992, 193, 273–276. [Google Scholar] [CrossRef]
  24. Jia, j.; Qi, z. Effect of the second phase on critical current density in Nb-added YBCO films. Mod. Phys. Lett. B 1995, 9, 439–443. [Google Scholar] [CrossRef]
  25. Holesinger, T.G.; Feldman, D.M.; Maiorov, B.; Civale, L. Strategic materials development for coated conductor performance. In Poceedings of Advanced Cables and Conductors Program Peer Review, Alexandria, VA, USA, 29 June–1 July 2010; Available online: http://www.htspeerreview.com/agenda.html (accessed on 11 August 2011).
  26. Horii, S.; Yamada, K.; Kai, H.; Ichinose, A.; Mukaida, M.; Teranishi, R.; Kita, R.; Matsumoto, K.; Yoshida, Y.; Shimoyama, J.; et al. Introduction of c-axis-correlated 1D pinning centers and vortex Bose glass in Ba-Nb-O-doped ErBa2Cu3Oy films. Supercond. Sci. Technol. 2007, 20, 1115–1119. [Google Scholar] [CrossRef]
  27. Kai, H.; Mukaida, M.; Horii, S.; Ichinose, A.; Kita, R.; Kato, S.; Matsumoto, K.; Yoshida, Y.; Teranishi, R.; Yamada, K.; et al. Superconducting properties and microstructure of PLD-ErBa2Cu3O7−d film with BaNb2O6. Phys. C Supercond. 2007, 463–465, 895–899. [Google Scholar] [CrossRef]
  28. Feldmann, D.M.; Holesinger, T.G.; Maiorov, B.; Foltyn, S.R.; Coulter, J.Y.; Apodaca, I. Improved flux pinning in YBa2Cu3O7 with nanorods of the double perovskite Ba2YNbO6. Supercond. Sci. Technol. 2010, 23, 095004–095009. [Google Scholar] [CrossRef]
  29. Reich, E.; Thersleff, T.; Hühne, R.; Iida, K.; Schultz, L.; Holzapfel, B. Structural and pinning properties of Y2Ba4CuMOy (M = Nb,Zr)/YBa2Cu3O7−δ quasi-multilayers fabricated by off-axis pulsed laser deposition. Supercond. Sci. Technol. 2009, 22, 105004–105010. [Google Scholar] [CrossRef]
  30. Ercolano, G.; Harrington, S.A.; Wang, H.; Tsai, C.F.; MacManus-Driscoll, J.L. Enhanced flux pinning in YBa2Cu3O7−δ thin films using Nb-based double perovskite additions. Supercond. Sci. Technol. 2010, 23, 022003–022008. [Google Scholar] [CrossRef]
  31. Brixner, L. Preparation and crystallographic study of some new rare earth compounds. J. Inorg. Nucl. Chem. 1960, 15, 352–355. [Google Scholar] [CrossRef]
  32. Battle, P.D.; Jones, C.W. The crystal and magnetic structures of Sr2LuRuO6, Ba2YRuO6, and Ba2LuRuO6. J. Solid State Chem. 1989, 78, 108–116. [Google Scholar] [CrossRef]
  33. Fu, W.T.; Ijdo, D.J.W. On the symmetry and structure of the double perovskites Ba2LnRuO6 (Ln = La, Pr and Nd). Solid State Commun. 2005, 136, 456–461. [Google Scholar] [CrossRef]
  34. Babu, N.H.; Iida, K.; Shi, Y.; Withnell, T.D.; Cardwell, D.A. YBa2Cu3O7−d /Y2Ba4CuMOy single grain nanocomposite superconductors with high critical current densities. Supercond. Sci. Technol. 2006, 19, S461–S465. [Google Scholar] [CrossRef]
  35. Feldmann, D.M.; Ugurlu, O.; Maiorov, B.; Stan, L.; Holesinger, T.G.; Civale, L.; Foltyn, S.R.; Jia, Q.X. Influence of growth temperature on critical current and magnetic flux pinning structures in YBa2Cu3O7−x. Appl. Phys. Lett. 2007, 91, 162501–162503. [Google Scholar] [CrossRef]
  36. Siraj, K.; Pedarnig, J.D.; Moser, A.; Bäuerle, D.; Hari Babu, N.; Cardwell, D.A. Enhanced self-field critical current density of nano-composite YBa2Cu3O7 thin films grown by pulsed-laser deposition. EPL Europhys. Lett. 2008, 82, 57006–57010. [Google Scholar] [CrossRef]
  37. Holesinger, T.G.; Foltyn, S.R.; Arendt, P.N.; Kung, H.; Jia, Q.X.; Dickerson, R.M.; Dowden, P.C.; DePaula, R.F.; Coulter, J.Y. The microstructure of continously processed YBa2Cu3Oy coated conductors with underlying CeO2 and IBAD YSZ Buffer Layers. J. Mater. Res. 2000, 15, 222–240. [Google Scholar] [CrossRef]
  38. Kim, S.I.; Gurevich, A.; Song, X.; Li, X.; Zhang, W.; Kodendandath, T.; Rupich, M.W.; Holesinger, T.G.; Larbalestier, D.C. Mechanisms of weak thickness dependence of the critical current density in strong-pinning ex situ metal-organic-deposition-route YBa2Cu3O7−x coated conductors. Supercond. Sci. Technol. 2006, 19, 1–12. [Google Scholar] [CrossRef]
  39. Holesinger, T.G.; Maiorov, B.; Ugurlu, O.; Civale, L.; Chen, Y.; Xiong, X.; Xie, Y.; Selvamanickam, V. Microstructural and superconducting properties of high current metal-organic chemical vapor deposition YBa2Cu3O7−d; coated conductor wires. Supercond. Sci. Technol. 2009, 22, 045025–045038. [Google Scholar] [CrossRef]
  40. Selvamanickam, V.; Guevara, A.; Zhang, Y.; Kesgin, I.; Xie, Y.; Carota, G.; Chen, Y.; Dackow, J.; Zhang, Y.; Zuev, Y.; et al. Enhanced and uniform in-field performance in long (Gd, Y)-Ba-Cu-O tapes with zirconium doping fabricated by metal-organic chemical vapor deposition. Supercond. Sci. Technol. 2010, 23, 014014–014019. [Google Scholar] [CrossRef]
  41. Holesinger, T.G. Though-Thickness Structural Degradation in Nano-Structured YBCO Thick Films; Superconductivity Technology Center: Los Alamos, NM, USA, 2011; Unpublished work. [Google Scholar]
  42. JADE, Version 6.5; Materials Data, Inc.: Livermore, CA, USA, 2003.
  43. CrystalMaker, Images Generated Using CrystalMaker®, a Crystal and Molecular Structures Program for Mac and Window; CrystalMaker Software LTD: Oxford, UK, 1994–2011; Available online: www.crystalmaker.com (accessed on 14 January 2011).

Share and Cite

MDPI and ACS Style

Holesinger, T.G.; Feldmann, M.D.; Maiorov, B.; Civale, L.; Kennison, J.A.; Coulter, Y.J.; Dowden, P.D.; Baca, J.F.; Tobash, P.H.; Bauer, E.D.; et al. Nanorod Self-Assembly in High Jc YBa2Cu3O7−x Films with Ru-Based Double Perovskites. Materials 2011, 4, 2042-2056. https://doi.org/10.3390/ma4112042

AMA Style

Holesinger TG, Feldmann MD, Maiorov B, Civale L, Kennison JA, Coulter YJ, Dowden PD, Baca JF, Tobash PH, Bauer ED, et al. Nanorod Self-Assembly in High Jc YBa2Cu3O7−x Films with Ru-Based Double Perovskites. Materials. 2011; 4(11):2042-2056. https://doi.org/10.3390/ma4112042

Chicago/Turabian Style

Holesinger, Terry G., Matthew D. Feldmann, Boris Maiorov, Leonardo Civale, John A. Kennison, Yates J. Coulter, Paul D. Dowden, Javier F. Baca, Paul H. Tobash, Eric D. Bauer, and et al. 2011. "Nanorod Self-Assembly in High Jc YBa2Cu3O7−x Films with Ru-Based Double Perovskites" Materials 4, no. 11: 2042-2056. https://doi.org/10.3390/ma4112042