The irradiation of pulp is of interest from different perspectives. Mainly it is required when a modification of cellulose is needed. Irradiation could bring many advantages, such as chemical savings and, therefore, cost savings and a reduction in environmental pollutants. In this account, pulp and dissociated celluloses were analyzed before and after irradiation by electron beaming. The focus of the analysis was the oxidation of hydroxyl groups to carbonyl and carboxyl groups in pulp and the degradation of cellulose causing a decrease in molar mass. For that purpose, the samples were labeled with a selective fluorescence marker and analyzed by gel permeation chromatography (GPC) coupled with multi-angle laser light scattering (MALLS), refractive index (RI), and fluorescence detectors. Degradation of the analyzed substrates was the predominant result of the irradiation; however, in the microcrystalline samples, oxidized cellulose functionalities were introduced along the cellulose chain, making this substrate suitable for further chemical modification. Full article

The biomedical properties of a porous bio-collagenic polymer extracted from leather industrial waste residues have been investigated in wound healing and tissue regeneration in induced wounds in rats. Application of the pure undiluted bio-collagen to induced wounds in rats dramatically improved its healing after 7 days in terms of collagen production and wound filling as well as in the migration and differentiation of keratinocytes. The formulation tested was found to be three times more effective than the commercial reference product Catrix^® (Heal Progress (HP): 8 ± 1.55 vs. 2.33 ± 0.52, p < 0.001; Formation of Collagen (FC): 7.5 ± 1.05 vs. 2.17 ± 0.75, p < 0.001; Regeneration of Epidermis (RE): 13.33 ± 5.11 vs. 5 ± 5.48, p < 0.05). Full article

Microencapsulated paraffin wax/polyaniline was prepared using a simple in situ polymerization technique, and its performance characteristics were investigated. Weight losses of samples were determined by Thermal Gravimetry Analysis (TGA). The microencapsulated samples with 23% and 49% paraffin showed less decomposition after 330 °C than with higher percentage of paraffin. These samples were then subjected to a thermal cycling test. Thermal properties of microencapsulated paraffin wax were evaluated by Differential Scanning Calorimeter (DSC). Structure stability and compatibility of core and coating materials were also tested by Fourier transform infrared spectrophotometer (FTIR), and the surface morphology of the samples are shown by Field Emission Scanning Electron Microscopy (FESEM). It has been found that the microencapsulated paraffin waxes show little change in the latent heat of fusion and melting temperature after one thousand thermal recycles. Besides, the chemical characteristics and structural profile remained constant after one thousand thermal cycling tests. Therefore, microencapsulated paraffin wax/polyaniline is a stable material that can be used for thermal energy storage systems. Full article

Two structural forms of a ternary alloy PtRuIr/C catalyst, one amorphous and one highly crystalline, were synthesized and compared to determine the effect of their respective structures on their activity and stability as anodic catalysts in methanol oxidation. Characterization techniques included TEM, XRD, and EDX. Electrochemical analysis using a glassy carbon disk electrode for cyclic voltammogram and chronoamperometry were tested in a solution of 0.5 mol L⁻¹ CH₃OH and 0.5 mol L⁻¹ H₂SO₄. Amorphous PtRuIr/C catalyst was found to have a larger electrochemical surface area, while the crystalline PtRuIr/C catalyst had both a higher activity in methanol oxidation and increased CO poisoning rate. Crystallinity of the active alloy nanoparticles has a big impact on both methanol oxidation activity and in the CO poisoning rate. Full article

Cell colonization of synthetic polymers can be regulated by physical and chemical modifications of the polymer surface. High-density and low-density polyethylene (HDPE and LDPE) were therefore activated with Ar⁺ plasma and grafted with fibronectin (Fn) or bovine serum albumin (BSA). The water drop contact angle usually decreased on the plasma-treated samples, due to the formation of oxidized groups, and this decrease was inversely related to the plasma exposure time (50–300 s). The presence of nitrogen and sulfur on the polymer surface, revealed by X-ray photoelectron spectroscopy (XPS), and also by immunofluorescence staining, showed that Fn and BSA were bound to this surface, particularly to HDPE. Plasma modification and grafting with Fn and BSA increased the nanoscale surface roughness of the polymer. This was mainly manifested on HDPE. Plasma treatment and grafting with Fn or BSA improved the adhesion and growth of vascular smooth muscle cells in a serum-supplemented medium. The final cell population densities on day 6 after seeding were on an average higher on LDPE than on HDPE. In a serum-free medium, BSA grafted to the polymer surface hampered cell adhesion. Thus, the cell behavior on polyethylene can be modulated by its type, intensity of plasma modification, grafting with biomolecules, and composition of the culture medium. Full article

LiFePO₄ is considered to be one of the most promising cathode materials for lithium ion batteries for electric vehicle (EV) application. However, there are still a number of unsolved issues regarding the influence of Li and Fe-site substitution on the physicochemical properties of LiFePO₄. This is a review-type article, presenting results of our group, related to the possibility of the chemical modification of phosphoolivine by introduction of cation dopants in Li and Fe sublattices. Along with a synthetic review of previous papers, a large number of new results are included. The possibility of substitution of Li⁺ by Al³⁺, Zr⁴⁺, W⁶⁺ and its influence on the physicochemical properties of LiFePO₄ was investigated by means of XRD, SEM/EDS, electrical conductivity and Seebeck coefficient measurements. The range of solid solution formation in Li_1−3xAl_xFePO₄, Li_1−4xZr_xFePO₄ and Li_1−6xW_xFePO₄ materials was found to be very narrow. Transport properties of the synthesized materials were found to be rather weakly dependent on the chemical composition. The battery performance of selected olivines was tested by cyclic voltammetry (CV). In the case of LiFe_1−yM_yPO₄ (M = Mn, Co and Ni), solid solution formation was observed over a large range of y (0 < y ≤ 1). An increase of electrical conductivity for the substitution level y = 0.25 was observed. Electrons of 3d metals other than iron do not contribute to the electrical properties of LiFe_1−yM_yPO₄, and substitution level y > 0.25 leads to considerably lower values of σ. The activated character of electrical conductivity with a rather weak temperature dependence of the Seebeck coefficient suggests a small polaron-type conduction mechanism. The electrochemical properties of LiFe_1−yM_yPO₄ strongly depend on the Fe substitution level. Full article

Production of a high value zeolite from fly ash has been shown to be an avenue for the utilization of South African fly ash which presently constitutes a huge disposal problem. The synthesis of zeolites Na-P1 and analcime on a micro-scale has been successful and preliminary investigation shows that scale-up synthesis is promising. However, the post-synthesis supernatant waste generated contains high levels of NaOH that may constitute a secondary disposal problem. A waste minimization protocol was developed to reduce the volume of waste generated with a view to enhancing the feasibility of the scale synthesis. Series of experiments were conducted in 100 mL jacketed batch reactors. Fly ash was reacted with 5 Mol NaOH on a 1:1 mass basis during the aging step, followed by hydrothermal treatment in which ultrapure water was added to the slurry. This study shows that by re-introducing the supernatant waste into the experiments in such a way that it supplies the required reagent (NaOH) for the zeolite synthesis, zeolite Na-P1 and analcime can be synthesized. It also shows that the synthesis process can be altered to allow up to 100% re-use of the supernatant waste to yield high value zeolitic products. This study effectively constructed two protocols for the minimization of waste generated during the synthesis of zeolites from South African coal fly ash. This result could be used to establish a basis for legal and environmental aspects involved in the commission of a full-scale plant synthesizing zeolites NaP1 and analcime. Full article

In this study, we report the light-emitting assistance effect of perylene on a polymer electrochemiluminescence (ECL) device using poly(3-octylthiophene-2,5-diyl) (P3OT). An ECL device is a liquid type self-luminous device with a simple structure, and can be fabricated by a relatively easy procedure. Significant improvement in luminescence properties was confirmed when 1.0 wt % perylene was added to the ECL device using 3.0 wt % P3OT. Improvements of about 12 times of the maximum luminescence intensity and about 23 times of the light-emitting time ratio compared with that of a P3OT ECL device were obtained. We conclude that the light-emitting assistance of perylene is achieved by perylene radical ions shuttling electrons to P3OT while they are moving around in the emitting solution. The light-emitting assistance effect of perylene was also confirmed when poly(3-dodecylthiophene-2,5-diyl), which has almost identical electrochemical and photophysical characteristics to those of P3OT, was used instead of P3OT. Full article

MCM-41 was used as a support and, by using atomic layer deposition (ALD) in the liquid phase, a catalyst was prepared by consecutively loading titanium oxide and vanadium oxide to the support. This research analyzes the effect of the loading amount of vanadium oxide on the acidic characteristics and catalytic performance in the dehydration of butanol. The physical and chemical characteristics of the TiO₂-V₂O₅/MCM-41 catalysts were analyzed using XRF, BET, NH₃-TPD, XRD, Py-IR, and XPS. The dehydration reaction of butanol was performed in a fixed bed reactor. For the samples with vanadium oxide loaded to TiO₂/MCM-41 sample using the liquid phase ALD method, it was possible to increase the loading amount until the amount of vanadium oxide reached 12.1 wt %. It was confirmed that the structural properties of the mesoporous silica were retained well after titanium oxide and vanadium loading. The NH₃-TPD and Py-IR results indicated that weak acid sites were produced over the TiO₂/MCM-41 samples, which is attributed to the generation of Lewis acid sites. The highest activity of the V₂O₅(12.1)-TiO₂/MCM-41 catalyst in 2-butanol dehydration is ascribed to it having the highest number of Lewis acid sites, as well as the highest vanadium dispersion. Full article

The ablation and oxidation of ZrB₂-based ultra high temperature ceramic (UHTC) composites containing 10%, 15% and 30% v/v SiC were tested under different heat fluxes in a high frequency plasma wind tunnel. Performance was significantly affected by the surface temperature, which was strongly dependent on the composition. Composites containing 10% SiC showed the highest surface temperature (>2300 °C) and underwent a marked degradation under both conditions. In contrast, composites with 30% SiC exhibited the lowest surface temperature (<2000 °C) and demonstrated excellent ablation resistance. The surface temperature of UHTCs in aerothermal testing was closely associated with the dynamic evolution of the surface and bulk oxide properties, especially for the change in chemical composition on the exposed surface, which was strongly dependent on the material composition and testing parameters (i.e., heat flux, enthalpy, pressure and test time), and in turn affected its oxidation performance. Full article

Zeolite-geopolymer hybrid materials have been formed when kaolin was used as a starting material. Their characteristics are of interest because they can have a wide pore size distribution with micro- and meso-pores due to the zeolite and geopolymer, respectively. In this study, Zeolite-geopolymer hybrid bulk materials were fabricated using four kinds of kaolinitic clays (a halloysite and three kinds of kaolinite). The kaolinitic clays were first calcined at 700 °C for 3 h to transform into the amorphous aluminosilicate phases. Alkali-activation treatment of the metakaolin yielded bulk materials with different amounts and types of zeolite and different compressive strength. This study investigated the effects of the initial kaolinitic clays on the amount and types of zeolite in the resultant geopolymers as well as the strength of the bulk materials. The kaolinitic clays and their metakaolin were characterized by XRD analysis, chemical composition, crystallite size, ²⁹Si and ²⁷Al MAS NMR analysis, and specific surface area measurements. The correlation between the amount of zeolite formed and the compressive strength of the resultant hybrid bulk materials, previously reported by other researchers was not positively observed. In the studied systems, the effects of Si/Al and crystalline size were observed. When the atomic ratio of Si/Al in the starting kaolinitic clays increased, the compressive strength of the hybrid bulk materials increased. The crystallite size of the zeolite in the hybrid bulk materials increased with decreasing compressive strength of the hybrid bulk materials. Full article

Novel structures of an near-infrared (NIR) tetraarylazadipyrromethene (aza-BODIPY) series have been prepared. We designed the core structure containing two amido groups at the para-position of the aromatic rings. The amido group was incorporated to secure insensitivity to pH and to ensure a bathochromic shift to the NIR region. Forty members of aza-BODIPY compounds were synthesized by substitution of the acetyl group with commercial amines on the alpha bromide. The physicochemical properties and photostability were investigated and the fluorescence emission maxima (745~755 nm) were found to be in the near infrared (NIR) range of fluorescence. Full article

The dimensionless Niyama criterion was used to predict the formation of microporosity in nickel-based superalloy casting, which extended the model application from a simple plate casting to complex thin-wall superalloy casting. The physical characteristics of the superalloy were calculated by JMatPro software. The relation between the volume percentage of microporosity and the dimensionless Niyama values were constructed. Quantitative metallographic measurements of the microporosity of the practical thin-wall casting were carried out. The prediction agreed well with the experiment in general, except for some thick-wall sites in the casting. Full article

In the present study, room temperature mechanical properties of pure magnesium, Mg/ZrO₂ and Mg/(ZrO₂ + Cu) composites with various compositions are investigated. Results revealed that the use of hybrid (ZrO₂ + Cu) reinforcements in Mg led to enhanced mechanical properties when compared to that of single reinforcement (ZrO₂). Marginal reduction in mechanical properties of Mg/ZrO₂ composites were observed mainly due to clustering of ZrO₂ particles in Mg matrix and lack of matrix grain refinement. Addition of hybrid reinforcements led to grain size reduction and uniform distribution of hybrid reinforcements, globally and locally, in the hybrid composites. Macro- and micro- hardness, tensile strengths and compressive strengths were all significantly increased in the hybrid composites. With respect to unreinforced magnesium, failure strain was almost unchanged under tensile loading while it was reduced under compressive loading for both Mg/ZrO₂ and Mg/(ZrO₂ + Cu) composites. Full article

The surface of a glassy carbon (GC) electrode was modified with reduced graphene oxide (rGO) to evaluate the electrochemical response of the modified GC electrodes to hydrogen peroxide (H₂O₂) and hydrazine. The electrode potential of the GC electrode was repeatedly scanned from −1.5 to 0.6 V in an aqueous dispersion of graphene oxide (GO) to deposit rGO on the surface of the GC electrode. The surface morphology of the modified GC electrode was characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM). SEM and AFM observations revealed that aggregated rGO was deposited on the GC electrode, forming a rather rough surface. The rGO-modified electrodes exhibited significantly higher responses in redox reactions of H₂O₂ as compared with the response of an unmodified GC electrode. In addition, the electrocatalytic activity of the rGO-modified electrode to hydrazine oxidation was also higher than that of the unmodified GC electrode. The response of the rGO-modified electrode was rationalized based on the higher catalytic activity of rGO to the redox reactions of H₂O₂ and hydrazine. The results suggest that rGO-modified electrodes are useful for constructing electrochemical sensors. Full article

Leaching of calcium ions increases the porosity of cement-based materials, consequently resulting in a negative effect on durability since it provides an entry for aggressive harmful ions, causing reinforcing steel corrosion. This study investigates the effects of leaching behavior of calcium ions on the compression and durability of cement-based materials. Since the parameters influencing the leaching behavior of cement-based materials are unclear and diverse, this paper focuses on the influence of added mineral admixtures (fly ash, slag and silica fume) on the leaching behavior of calcium ions regarding compression and durability of cemented-based materials. Ammonium nitrate solution was used to accelerate the leaching process in this study. Scanning electron microscopy, X-ray diffraction analysis, and thermogravimetric analysis were employed to analyze and compare the cement-based material compositions prior to and after calcium ion leaching. The experimental results show that the mineral admixtures reduce calcium hydroxide quantity and refine pore structure through pozzolanic reaction, thus enhancing the compressive strength and durability of cement-based materials. Full article

Plastic worm wheel is widely used in the vehicle manufacturing field because it is favorable for weight lightening, vibration and noise reduction, as well as corrosion resistance. However, it is very difficult for general plastics to secure the mechanical properties that are required for vehicle gears. If the plastic resin is reinforced by glass fiber in the fabrication process of plastic worm wheel, it is possible to achieve the mechanical properties of metallic material levels. In this study, the mechanical characteristic analysis of the glass-reinforced plastic worm wheel, according to the contents of glass fiber, is performed by analytic and experimental methods. In the case of the glass fiber-reinforced resin, the orientation and contents of glass fibers can influence the mechanical properties. For the characteristic prediction of plastic worm wheel, computer-aided engineering (CAE) analysis processes such as structural and injection molding analysis were executed with the polyamide resin reinforcement glass fiber (25 wt %, 50 wt %). The injection mold for fabricating the prototype plastic worm wheel was designed and made to reflect the CAE analysis results. Finally, the durability of prototype plastic worm wheel fabricated by the injection molding process was evaluated by the experimental method and the characteristics according to the glass fiber contents. Full article

Metal-containing mesoporous starches have been synthesized using a simple and efficient microwave-assisted methodology followed by metal impregnation in the porous gel network. Final materials exhibited surface areas >60 m² g⁻¹, being essentially mesoporous with pore sizes in the 10–15 nm range with some developed inter-particular mesoporosity. These materials characterized by several techniques including XRD, SEM, TG/DTA and DRIFTs may find promising catalytic applications due to the presence of (hydr)oxides in their composition. Full article

TiB₂-based ceramic matrix composites (CMCs) were fabricated using elemental powders of Ti, B and C. The self-propagating high temperature synthesis (SHS) was carried out for the highly exothermic “in situ” reaction of TiB₂ formation and the “tailing” synthesis of boron carbide characterized by weak exothermicity. Two series of samples were fabricated, one of them being prepared with additional milling of raw materials. The effects of TiB₂ vol fraction as well as grain size of reactant were investigated. The results revealed that combustion was not successful for a TiB₂:B₄C molar ratio of 0.96, which corresponds to 40 vol% of TiB₂ in the composite, however the SHS reaction was initiated and self-propagated for the intended TiB₂:B₄C molar ratio of 2.16 or above. Finally B₁₃C₂ was formed as the matrix phase in each composite. Significant importance of the grain size of the C precursor with regard to the reaction completeness, which affected the microstructure homogeneity and hardness of investigated composites, was proved in this study. The grain size of Ti powder did not influence the microstructure of TiB₂ grains. The best properties (HV = 25.5 GPa, average grain size of 9 μm and homogenous microstructure), were obtained for material containing 80 vol% of TiB₂, fabricated using a graphite precursor of 2 μm. Full article

In this study the development of a metakaolin based geopolymeric mortar to be used as bonding matrix for external strengthening of reinforced concrete beams is reported. Four geopolymer formulations have been obtained by varying the composition of the activating solution in terms of SiO₂/Na₂O ratio. The obtained samples have been characterized from a structural, microstructural and mechanical point of view. The differences in structure and microstructure have been correlated to the mechanical properties. A major issue of drying shrinkage has been encountered in the high Si/Al ratio samples. In the light of the characterization results, the optimal geopolymer composition was then applied to fasten steel fibers to reinforced concrete beams. The mechanical behavior of the strengthened reinforced beams was evaluated by four-points bending tests, which were performed also on reinforced concrete beams as they are for comparison. The preliminary results of the bending tests point out an excellent behavior of the geopolymeric mixture tested, with the failure load of the reinforced beams roughly twice that of the control beam. Full article

In this study, magnesium composites with nano-size boron nitride (BN) particulates of varying contents were synthesized using the powder metallurgy (PM) technique incorporating microwave-assisted two-directional sintering followed by hot extrusion. The effect of nano-BN addition on the microstructural and the mechanical behavior of the developed Mg/BN composites were studied in comparison with pure Mg using the structure-property correlation. Microstructural characterization revealed uniform distribution of nano-BN particulates and marginal grain refinement. The coefficient of thermal expansion (CTE) value of the magnesium matrix was improved with the addition of nano-sized BN particulates. The results of XRD studies indicate basal texture weakening with an increase in nano-BN addition. The composites showed improved mechanical properties measured under micro-indentation, tension and compression loading. While the tensile yield strength improvement was marginal, a significant increase in compressive yield strength was observed. This resulted in the reduction of tension-compression yield asymmetry and can be attributed to the weakening of the strong basal texture. Full article

Bacterial cellulose (BC) is characterized for its high water holding capacity, high crystallinity, an ultrafine fiber network and high tensile strength. This work demonstrates the production of a new interpenetrated polymer network nanocomposite obtained through the incorporation of poly(vinyl alcohol) (PVA) on the BC matrix and evaluates the effect of oven drying on the morphological, mechanical and mass transfer properties of the composite membranes. Both the addition of PVA and oven drying induce the appearance of larger pores (circa 1–3 µm in average diameter) in dried BC/PVA membranes. Both types of treatments also affect the permeability of the composite, as assessed by the diffusion coefficients of polyethylene glycol (PEG) molecules (900, 8,000, 35,000 and 100,000 Da) across the membranes. Finally, the Young’s modulus of dry pristine BC decreases following PVA incorporation, resulting in a change from 3.5 GPa to 1 GPa and a five-fold loss in tensile strength. Full article

The unique properties of ceramic foams enable their use in a variety of applications. This work investigated the effects of different parameters on the production of zirconia ceramic foam using the sol-gel process associated with liquid foam templates. Evaluation was made of the influence of the thermal treatment temperature on the porous and crystalline characteristics of foams manufactured using different amounts of sodium dodecylsulfate (SDS) surfactant. A maximum pore volume, with high porosity (94%) and a bimodal pore size distribution, was observed for the ceramic foam produced with 10% SDS. Macropores, with an average size of around 30 μm, were obtained irrespective of the SDS amount, while the average size of the supermesopores increased systematically as the SDS amount was increased up to 10%, after which it decreased. X-ray diffraction analyses showed that the sample treated at 500 °C was amorphous, while crystallization into a tetragonal metastable phase occurred at 600 °C due to the presence of sulfate groups in the zirconia structure. At 800 and 1000 °C the monoclinic phase was observed, which is thermodynamically stable at these temperatures. Full article

This work aims at studying the effect of the milling conditions on the microstructure and mechanical properties of a ZrB₂-5 vol% Si₃N₄ matrix reinforced with chopped Hi-Nicalon SiC fibers. Several composites were obtained using different milling conditions in terms of time, speed and type of milling media. The composites were prepared from commercial powders, ball milled, dried and shaped, and hot pressed at 1720 °C. Their relative bulk densities achieved values as high as 99%. For each material the fiber length distribution, the extent of reacted fiber area and matrix mean grain size were evaluated in order to ascertain the effects of milling time, milling speed and type of milling media. While the fracture toughness and hardness were statistically the same independently of the milling conditions, the flexural strength changed. From the results obtained, the best milling conditions for optimized mechanical properties were determined. Full article

In this study, we first investigated changes seen in electrical and optical properties of a polymer light-emitting diode due to using different kinds of solvents and their mixture. Two-layer light emitting diodes with organic small molecules doped in a PVK polymer host were fabricated using (i) non-aromatic solvent chloroform with a high evaporation rate; (ii) aromatic solvent chlorobenzene with a low evaporation rate, and (iii) their mixture with different relative ratios. The effect of nano-scale layer thickness, surface roughness and internal nano-morphology on threshold voltage and the amount of electric current, the luminance and efficiency of a device were assessed. Results indicated the importance of majority charge carriers’ type in the selection of solvent and tuning its properties. Then, the effect of thermal annealing on electrical and optical properties of polymer light emitting diodes was investigated. During the device fabrication, pre-annealing in 80 and/or 120 °C and post-annealing in 120 °C were performed. The nano-scale effect of annealing on polymer-metal interface and electric current injection was described thoroughly. A comparison between threshold voltage, luminance and electric current efficiency of luminescence for different annealing processes was undertaken, so that the best electric current efficiency of luminescence achieved at 120 °C pre-annealing accompanied with 120 °C post-annealing. Full article

Time-of-flight secondary ion mass spectrometry (TOF-SIMS) and X-ray photoelectron spectroscopy (XPS) are well established surface techniques that provide both elemental and organic information from several monolayers of a sample surface, while also allowing depth profiling or image mapping to be carried out. The static TOF-SIMS with improved performances has expanded the application of TOF-SIMS to the study of a variety of organic, polymeric and biological materials. In this work, TOF-SIMS, XPS and Fourier Transform Infrared (FTIR) measurements were used to characterize commercial natural dyes and traditional silk fabric dyed with plant extracts dyes avoiding the time-consuming and destructive extraction procedures necessary for the spectrophotometric and chromatographic methods previously used. Silk textiles dyed with plant extracts were then analyzed for chemical and functional group identification of their dye components and mordants. TOF-SIMS spectra for the dyed silk fabric showed element ions from metallic mordants, specific fragment ions and molecular ions from plant-extracted dyes. The results of TOF-SIMS, XPS and FTIR are very useful as a reference database for comparison with data about traditional Korean silk fabric and to provide an understanding of traditional dyeing materials. Therefore, this study shows that surface techniques are useful for micro-destructive analysis of plant-extracted dyes and Korean dyed silk fabric. Full article

Doxorubicin hydrochloride (DOX) is an effective anticancer agent for leukemia chemotherapy, although its clinical use has been limited because of its side effects such as cardiotoxicity, alopecia, vomiting, and leucopenia. Attention has been focussed on developing new drug carriers with high adsorption capacity and rapid adsorption rate in order to minimize the side effects of DOX. Graphene oxide (GO), a new type of nanomaterial in the carbon family, was prepared by Hummers method and used as adsorbent for DOX from aqueous solution. The physico-chemical properties of GO were characterized by transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FTIR), zeta potential, and element analysis. The adsorption properties of DOX on GO were studied as a function of contact time, adsorbent dosage, temperature and pH value. The results showed that GO had a maximum adsorption capacity of 1428.57 mg/g and the adsorption isotherm data fitted the Langmuir model. The kinetics of adsorption fits a pseudo-second-order model. The thermodynamic studies indicate that the adsorption of DOX on GO is spontaneous and endothermic in nature. Full article

High-grade cellulose (97% α-cellulose content) of 48% crystallinity index was extracted from the renewable marine biomass waste Posidonia oceanica using H₂O₂ and organic peracids following an environmentally friendly and chlorine-free process. This cellulose appeared as a new high-grade cellulose of waste origin quite similar to the high-grade cellulose extracted from more noble starting materials like wood and cotton linters. The benefits of α-cellulose recovery from P. oceanica were enhanced by its transformation into cellulose acetate CA and cellulose derivative GMA-C. Fully acetylated CA was prepared by conventional acetylation method and easily transformed into a transparent film. GMA-C with a molar substitution (MS) of 0.72 was produced by quenching Fenton’s reagent (H₂O₂/FeSO₄) generated cellulose radicals with GMA. GMA grafting endowed high-grade cellulose from Posidonia with adsorption capability. GMA-C removes β-naphthol from water with an efficiency of 47%, as measured by UV-Vis spectroscopy. After hydrolysis of the glycidyl group to glycerol group, the modified GMA-C was able to remove p-nitrophenol from water with an efficiency of 92%, as measured by UV-Vis spectroscopy. α-cellulose and GMA-Cs from Posidonia waste can be considered as new materials of potential industrial and environmental interest. Full article

e effects of biological pretreatment on the rubberwood (Hevea brasiliensis), was evaluated after cultivation of white rot fungi Ceriporiopsis subvermispora, Trametes versicolor, and a mixed culture of C. subvermispora and T. versicolor. The analysis of chemical compositions indicated that C. subvermispora had greater selectivity for lignin degradation with the highest lignin and hemicellulose loss at 45.06% and 42.08%, respectively, and lowest cellulose loss (9.50%) after 90 days among the tested samples. X-ray analysis showed that pretreated samples had a higher crystallinity than untreated samples. The sample pretreated by C. subvermispora presented the highest crystallinity of all the samples which might be caused by the selective degradation of amorphous components. Fourier transform infrared (FT-IR) spectroscopy demonstrated that the content of lignin and hemicellulose decreased during the biological pretreatment process. A study on hydrolysis of rubberwood treated with C. subvermispora, T. versicolor, and mixed culture for 90 days resulted in an increased sugar yield of about 27.67%, 16.23%, and 14.20%, respectively, as compared with untreated rubberwood (2.88%). The results obtained demonstrate that rubberwood is a potential raw material for industrial applications and white rot fungus C. subevermispora provides an effective method for improving the enzymatic hydrolysis of rubberwood. Full article

South African fly ash has been shown to be a useful feedstock for the synthesis of some zeolites. The present study focuses on the effect of impeller design and agitation rates on the synthesis of zeolite Na-P1 which are critical to the commercialization of this product. The effects of three impeller designs (4-flat blade, Anchor and Archimedes screw impellers) and three agitation speeds (150, 200 and 300 rpm) were investigated using a modified previously reported synthesis conditions; 48 hours of ageing at 47 °C and static hydrothermal treatment at 140 °C for 48 hours. The experimental results demonstrated that the phase purity of zeolite Na-P1 was strongly affected by the agitation rate and the type of impeller used during the ageing step of the synthesis process. Although zeolite Na-P1 was synthesized with a space time yield (STY) of 15 ± 0.4 kg d⁻¹m⁻³and a product yield of 0.98±0.05 g zeolites/g fly ash for each impeller at different agitation speeds, zeolite formation was assessed to be fairly unsuccessful in some cases due the occurrence of undissolved mullite and/or the formation of impurities such as hydroxysodalite with the zeolitic product. This study also showed that a high crystalline zeolite Na-P1 can be synthesized from South African coal fly ash using a 4-flat blade impeller at an agitation rate of 200 rpm during the ageing step at 47 °C for 48 hours followed by static hydrothermal treatment at 140 °C for 48 hours. Full article

Alumina-zirconia (AZ) composites are attractive structural materials, which combine the high hardness and Young’s modulus of the alumina matrix with additional toughening effects, due to the zirconia dispersion. In this study, AZ composites containing different amounts of zirconia (in the range 5–20 vol %) were prepared by a wet chemical method, consisting on the surface coating of alumina powders by mixing them with zirconium salt aqueous solutions. After spray-drying, powders were calcined at 600 °C for 1 h. Green bodies were then prepared by two methods: uniaxial pressing of spray-dried granules and slip casting of slurries, obtained by re-dispersing the spray dried granulates. After pressureless sintering at 1500 °C for 1 h, the slip cast samples gave rise to fully dense materials, characterized by a quite homogeneous distribution of ZrO₂ grains in the alumina matrix. The microstructure, phase composition, tetragonal to monoclinic transformation behavior and mechanical properties were investigated and are here discussed as a function of the ZrO₂ content. The material containing 10 vol % ZrO₂ presented a relevant hardness and exhibited the maximum value of K_I0, mainly imputable to the t → m transformation at the crack tip. Full article

Ce-modified mesoporous silica materials MCM-41 and SBA-15, namely 32 wt % Ce–Si–MCM-41, 16 wt % Ce–H–MCM-41 and 20 wt % Ce–Si–SBA-15, were prepared, characterized and studied in the selective preparation of trans-carveol by α-pinene oxide isomerization. The characterizations of these catalysts were performed using scanning electron microscopy, X-ray photoelectron spectroscopy, nitrogen adsorption and FTIR pyridine adsorption. Selective preparation of trans-carveol was carried out in the liquid phase in a batch reactor. The activity and the selectivity of catalyst were observed to be influenced by their acidity, basicity and morphology of the mesoporous materials. The formation of trans-carveol is moreover strongly influenced by the basicity of the used solvent and in order to achieve high yields of this desired alcohol it is necessary to use polar basic solvent. Full article

A wider utilization of ultra high temperature ceramics (UHTC) materials strongly depends on the availability of efficient techniques for their fabrication as dense bodies. Based on recent results reported in the literature, it is possible to state that Spark Plasma Sintering (SPS) technology offers a useful contribution in this direction. Along these lines, the use of two different SPS-based processing routes for the preparation of massive UHTCs is examined in this work. One method, the so-called reactive SPS (R-SPS), consists of the synthesis and densification of the material in a single step. Alternatively, the ceramic powders are first synthesized by Self-propagating High-temperature Synthesis (SHS) and then sintered by SPS. The obtained results evidenced that R-SPS method is preferable for the preparation of dense monolithic products, while the sintering of SHS powders requires relatively milder conditions when considering binary composites. The different kinetic mechanisms involved during R-SPS of the monolithic and composite systems, i.e., combustion-like or gradual solid-diffusion, respectively, provides a possible explanation. An important role is also played by the SHS process, particularly for the preparation of composite powders, since stronger interfaces are established between the ceramic constituents formed in situ, thus favoring diffusion processes during the subsequent SPS step. Full article

Interest in nanofibrillated cellulose (NFC) has increased notably over recent decades. This bio-based nanomaterial has been used essentially in bionanocomposites or in paper thanks to its high mechanical reinforcement ability or barrier property respectively. Its nano-scale dimensions and its capacity to form a strong entangled nanoporous network have encouraged the emergence of new high-value applications. It is worth noting that chemical surface modification of this material can be a key factor to achieve a better compatibility with matrices. In order to increase the compatibility in different matrices or to add new functions, surface chemical modification of NFC appears to be the prior choice to conserve its intrinsic nanofibre properties. In this review, the authors have proposed for the first time an overview of all chemical grafting strategies used to date on nanofibrillated cellulose with focus on surface modification such as physical adsorption, molecular grafting or polymer grafting. Full article

Fabricating industrial-scale photoreactive composite materials containing living cells, requires a deposition strategy that unifies colloid science and cell biology. Convective assembly can rapidly deposit suspended particles, including whole cells and waterborne latex polymer particles into thin (<10 µm thick), organized films with engineered adhesion, composition, thickness, and particle packing. These highly ordered composites can stabilize the diverse functions of photosynthetic cells for use as biophotoabsorbers, as artificial leaves for hydrogen or oxygen evolution, carbon dioxide assimilation, and add self-cleaning capabilities for releasing or digesting surface contaminants. This paper reviews the non-biological convective assembly literature, with an emphasis on how the method can be modified to deposit living cells starting from a batch process to its current state as a continuous process capable of fabricating larger multi-layer biocomposite coatings from diverse particle suspensions. Further development of this method will help solve the challenges of engineering multi-layered cellular photocomposite materials with high reactivity, stability, and robustness by clarifying how process, substrate, and particle parameters affect coating microstructure. We also describe how these methods can be used to selectively immobilize photosynthetic cells to create biomimetic leaves and compare these biocomposite coatings to other cellular encapsulation systems. Full article