Next Article in Journal
Uncertainty Impact on Water Management Analysis of Open Water Reservoir
Next Article in Special Issue
Negative Reagent Ions for Real Time Detection Using SIFT-MS
Previous Article in Journal
Response of Red-Backed Salamanders (Plethodon Cinereus) to Changes in Hemlock Forest Soil Driven by Invasive Hemlock Woolly Adelgid (Adelges Tsugae)
Previous Article in Special Issue
Investigation of Air Quality beside a Municipal Landfill: The Fate of Malodour Compounds as a Model VOC
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Photocatalytic Degradation of Toluene, Butyl Acetate and Limonene under UV and Visible Light with Titanium Dioxide-Graphene Oxide as Photocatalyst

Bundesanstalt für Materialforschung und-prüfung (BAM), Berlin 12205, Germany
*
Author to whom correspondence should be addressed.
Environments 2017, 4(1), 9; https://doi.org/10.3390/environments4010009
Submission received: 21 November 2016 / Revised: 21 December 2016 / Accepted: 13 January 2017 / Published: 25 January 2017
(This article belongs to the Special Issue Volatile Organic Compounds in Environment)

Abstract

:
Photocatalysis is a promising technique to reduce volatile organic compounds indoors. Titanium dioxide (TiO2) is a frequently-used UV active photocatalyst. Because of the lack of UV light indoors, TiO2 has to be modified to get its working range shifted into the visible light spectrum. In this study, the photocatalytic degradation of toluene, butyl acetate and limonene was investigated under UV LED light and blue LED light in emission test chambers with catalysts either made of pure TiO2 or TiO2 modified with graphene oxide (GO). TiO2 coated with different GO amounts (0.75%–14%) were investigated to find an optimum ratio for the photocatalytic degradation of VOC in real indoor air concentrations. Most experiments were performed at a relative humidity of 0% in 20 L emission test chambers. Experiments at 40% relative humidity were done in a 1 m³ emission test chamber to determine potential byproducts. Degradation under UV LED light could be achieved for all three compounds with almost all tested catalyst samples up to more than 95%. Limonene had the highest degradation of the three selected volatile organic compounds under blue LED light with all investigated catalyst samples.

1. Introduction

People from the Western world spend most of their time indoors, either in houses or in transportation, hence, the indoor air quality is of particular importance [1]. Though, volatile organic compounds (VOC) are ubiquitous in the indoor air, emitting, e.g., from building materials, wall and floor coverings and interior equipment. Those emissions can have a negative impact on the indoor air quality, health and wellbeing of occupants. This effect is described as sick-building-syndrome [2]. An approach to improve the indoor air quality, which has come more and more into focus during the last years, is the photocatalytic degradation of pollutants by photoredox catalysis. Photocatalytic active coatings, mostly made of the semiconductor titanium dioxide (TiO2) [3], have been developed and tested for indoor air use. TiO2 in its anatase modification has a band gap of 3.2 eV and can hence be activated under UV-light (λ = 387 nm). By light irradiation with a corresponding wavelength, electrons from the valence band are transferred to the conduction band and as a result electron-hole pairs are formed (Figure 1).
TiO2 + hν → h+ + e
The excited electrons can proceed in a single electron reduction and, in the presence of O2, form a superoxide radical anion O2•−. Simultaneously, the electron holes (h+) can react with H2O to yield hydroxyl radicals OH• (single electron oxidation). These resulting radicals are highly reactive and can mineralize organic substrates to CO2 and H2O as generalized in equations 2 and 3 [3,4].
OH• + VOC + O2 ➔ nCO2 + mH2O
O2•− + pollutant ➔➔➔ CO2 + H2O
Since TiO2 can only be activated under UV light it has to be doped or modified to shift its working range in the visible light spectrum. Banerjee et al. published an article summarizing and describing possibilities, e.g., metal and non-metal doping, dye sensitization, combination of TiO2 with reduced graphene oxide, to improve the visible light activity of TiO2 [5]. Graphene is a relatively new but promising material [6] and its oxide in combination with TiO2 is already known to successfully catalyze degradation of VOC, methyl orange and methylene blue under visible light [7,8,9]. With its high surface area of 2600 m2·g−1 [10] graphene sheets are highly reactive thus enhancing the photocatalytic activity of TiO2 due to the fact that more π–π interactions are possible [8]. The band gap has to be below 3.0 eV to get absorption under visible light [11], the light absorption is extended by increasing the amount of GO [9]. However, if the amount of graphene in the catalyst system is too high the photocatalytic activity is reduced [12,13].
One additional substantial aspect for the reactivity is the relative humidity in the emission test chamber which can both increase or decrease the photocatalytic degradation of VOC. According to Zhao and Yang [14] and Mo et al. [15] too little water vapor results in a retard of the degradation; whereas too much water vapor is also not appropriate for the degradation process. In the second case, the water molecules and the VOC compete for adsorption positions on the TiO2 surface. Furthermore, the effect is also depended on the inlet concentration of the VOC [16]. However, the optimum relative humidity level seems to be different depending on the investigated compound and used catalyst [17].
This work focuses on the photocatalytic degradation and investigation of potential byproducts of toluene, butyl acetate and limonene on pure TiO2 and TiO2 modified with different amounts of graphene oxide (GO; 0.75%, 1%, 2.5%, 5%, 10%, 14%) under UV and visible (blue) LED light. These compounds were selected because of their frequent occurrence in the indoor environment [2]. Experiments were performed in emission test chambers of various volumes under controlled climatic conditions. A reference VOC atmosphere in the range of real indoor air concentrations was created by using a gas mixing system (GMS) [18].

2. Materials and Methods

2.1. Chemicals

Toluene (108-88-3, for organic residue analysis) and methanol (67-56-1, ultra resi-analyzed) were purchased from J. T. Baker, butyl acetate (123-86-4, 99+%) and (R)-(+)-limonene (5989-27-5, 97%) from Aldrich and naphthalene d8 in methanol (2000 µg·mL−1) from Restek. A graphene oxide water dispersion was purchased from Graphenea (4 mg·mL−1, monolayer content >95%). The TiO2 was commercially available N-doped anatase.

2.2. Analytical Parameters and Instrumentation

Quantification was done using calibration curves (8 points) in combination with an internal standard (naphthalene d8 in methanol). Each tube was loaded with 1 µL of internal standard and methanol was flushed off with a nitrogen stream for 10 min (100 mL·min−1) before air samples were taken.
Air sampling was done periodically with Tenax® TA sorption tubes (Gerstel; 1 L with 50 or 100 mL·min−1). For the determination of lower volatile byproducts air sampling was done with Carbograph® 1TD (Markes International, Llantrisant, UK), a multi-bed tube containing Tenax® TA, Carbograph® 1TD and Carboxen® 1000, DNPH-cartridges (Supelco, Bellefonte, PA, USA; 2,4-dinitrophenylhydrazine) and silica cartridges (self-made with silica purchased from Supelco; 30 L and 60 L with 1 L·min−1).
Tenax TA® tubes were measured with a TD-GC-FID system (thermal desorption-gas chromatograph-flame ionization detector) for a quantitative determination. To determine the formation of byproducts measurements were done with a TD-GC-MS (mass spectrometer) system, HPLC (high performance liquid chromatography) and IC (ion chromatography) for a quantitative determination. The limit of quantification for VOC is 1 µg·m−3, for formaldehyde 5 µg·m−3, for acetaldehyde 7 µg·m−3, for formic acid 4 µg·m−3 and for acetic acid 5 µg·m−3.
Tenax TA® measurements were carried out on a GC-FID system from Agilent Technologies (Santa Clara, CA, USA) (GC: 6890 N) equipped with a thermal desorption system (TDS) from Gerstel temperature program: 40 °C for 1 min, 40 °C·min−1 to 280 °C for 5 min) and a cooled injection system (CIS 4; temperature program: −100 °C for 0.01 min, 12 °C·s−1 to 280 °C for 3 min). Chromatographic separation of the VOC was done on a Rtx-Volatiles column (Restek; 30 m × 320 µm × 1.5 μm) with the following temperature program: splitless, 60 °C for 1 min, 10 °C·min−1 to 180 °C for 3 min, 20 °C·min−1 to 260 °C for 5 min (run time 25 min).
Carbograph® 1TD and multi-bed tubes were thermally desorbed in a thermal desorption system (TD-100™, Markes International) and trapped afterwards in a cold trap made of glass. This was connected to a gas chromatograph 6890 N (Agilent Technologies) coupled with a 5975B mass spectrometer (Agilent Technologies) for quantification and identification. The gas chromatographic separation was done on an Rxi-5MS column (Restek, 60 m × 0.25 mm × 0.25 µm) with a constant helium flow (Alphagaz Air Liquide) of 1.5 mL·min−1. Thermal desorption was done at 300 °C for 10 min followed by 320 °C for 5 min with a flow of 50 mL·min−1. The cold trap started at −5 °C and was heated up to 320 °C for 15 min. The transfer line was set at 180 °C. A split (4.3:1) injection on the GC column was done and the GC oven program started at 50 °C (initial time 0.5 min) and heated up with 6 °C·min−1 to 300 °C (holding time 5 min). The MS (transfer line at 300 °C, EI-source at 230 °C and quadrupole at 150 °C) operated in SCAN-mode (m/z 35–450) without solvent delay.
HPLC measurements were done on 1100 Series (Agilent Technologies) equipped with an ULTRASEP ES ALD column (125 mm × 2 mm) with a pre-column (10 mm × 2 mm). The column temperature is set to 25 °C. Acetonitrile (solvent A) and a mixture of water and tetrahydrofuran (1:16.7; solvent B) were the used solvents. The pump program was the following: 30% solvent A, 70% solvent B with a flow of 0.5 mL·min−1; 30% solvent A, 70% solvent B with a flow of 0.5 mL·min−1 for 5 min; 32% solvent A, 68% solvent B with a flow of 0.5 mL·min−1 for 10 min; 32% solvent A, 68% solvent B with a flow of 0.6 mL·min−1 for 30 min; 83% solvent A, 17% solvent B with a flow of 0.6 mL·min−1 for 55 min; 30% solvent A, 70% solvent B with a flow of 0.6 mL·min−1 for 60 min; 30% solvent A, 70% solvent B with a flow of 0.5 mL·min−1 for 70 min. The detector wavelength was set at 365 nm and 380 nm.
IC measurements were carried out on a Thermo Scientific ICS 2100 instrument equipped with a Dionex IONPAC® AS18 (2 × 250 mm) column. The oven was set to 30 °C. A KOH-solution was used as eluent generator with water as solvent. The chromatographic separation was done as follows: 0 min: eluent concentration: 1 mmol; 23 min: eluent concentration: from 1 mmol to 50 mmol; 33 min: eluent concentration: from 50 mmol to 1 mmol; 43 min: end run.

2.3. Chamber Parameters

VOC degradation was investigated in 20 L and 1 m³ emission test chambers. The 20 L emission test chambers operated under the following conditions. A translucent plate of borosilicate glass was used as chamber cover and the light sources were placed on top of it. The chambers were equipped with a stirrer to guarantee a homogenous air distribution. A GMS was used to generate stable toluene, butyl acetate and limonene concentrations. The GMS consists of a mixing chamber (V = 24 L), into which the gaseous VOC are transferred by a nitrogen stream. This mixing chamber is supplied with an air flow (114 L·h−1) of purified and dry air to get a concentration reduction of the generated VOC. Two 20 L emission test chambers were connected to the mixing chamber (Figure 2). An air flow of 200 mL·min−1 was transferred into these chambers where the degradation experiments were carried out. The photocatalytic degradation was investigated at T = 23 °C, relative humidity (r.h.) = 0%, air change rate n = 0.6 h−1 and a loading factor of 0.5 m2·m−3, which describes the ratio of catalyst surface (m2) to emission test chamber volume (m3). These parameters were not changed during all experiments.
The 1 m³ emission test chamber was directly connected to the GMS without interposing of a mixing chamber. Hence, the VOC concentration was adjusted by the chambers air change rate, which was set at 1 h−1. Degradation experiments were performed at a relative humidity of 40% with a loading factor of 0.03 m2·m−3.

2.4. Light Sources

As light sources a UV LED lamp (λ = 365 nm; irradiance of 1.9 mW·cm−2 in a distance of 25 cm) and a blue LED lamp (λ = 455 nm; irradiance of 1.9 mW·cm−2 in a distance of 25 cm) were used for the experiments in the 20 L emission test chambers. Degradation experiments in a 1 m³ emission test chamber used an UV lamp (λmin = 297 nm; irradiance of 5.6 W·m−2 in a distance of 25 cm) and blue LED lights (λ = 444 nm; irradiance of 5.9 W·m−2 in a distance of 25 cm).

2.5. Degradation Experiments under UV and Visible Light

2.5.1. General Information

Customary ceramic tiles (10 cm × 10 cm) were coated with the catalyst (GO-modified and pure TiO2). Seven different GO-TiO2 amounts (A–G, Table 1) were tested, each with two diverse catalyst loadings (39 and 78 mg, samples A–F). The catalysts were applied by spraying and either cured for 60 min at 100 °C (samples A–F) or for 360 min at 470 °C (sample G). For sample G, only one loading amount was tested, which differs from the others. For sample D a third loading applied by doctor blade technique was tested as well. All irradiation experiments lasted up to 7 days and air sampling was done periodically. Before each experiment the chambers were tested for blank values. Furthermore, it was tested beforehand if the VOC are degraded by photolysis under UV LED and blue LED light, which they did not. Hence, degradation was achieved photocatalytically.

2.5.2. Degradation Experiments in 20 L Emission Test Chambers

The chambers were loaded with the respective catalyst samples under exposure of the reference VOC atmosphere. Unexpectedly, after the installation of samples A to E the limonene and butyl acetate concentrations dropped significantly (down to 0 µg·m−3). The reason for that was a strong adsorption of these compounds onto the catalyst surface. Over time, the concentration increased again due to saturation; however, it took between 1 and 5 weeks until equilibrium and thereby a constant VOC atmosphere was reached. In contrast to that the adsorption of toluene was negligible. Since it could take up to 5 weeks until an adsorption-desorption equilibrium was achieved, sample B-1 and B-2 were pre-stored in a toluene, butyl acetate and limonene atmosphere in a desiccator for up to 24 days. After this time saturation of the catalyst samples was achieved and the degradation experiments could be started within one day after loading the catalyst samples in the emission test chambers. After the concentrations had stabilized, the degradation experiments were started by irradiation of the catalyst samples with either UV LED or blue LED light. For an overview of the starting concentrations see Table 1.

2.5.3. Degradation Experiments in a 1 m³ Emission Test Chamber

The main focus of the experiments in a 1 m³ emission test chamber was the determination of potential byproducts. For that reason, concentrations higher than usual indoor air concentrations were generated (Table 2). The experiments were done with two samples, A-1 (pure TiO2) and D-1 (2.5% GO), under UV LED light at 40% relative humidity. Three catalyst samples were loaded into the emission test chamber simultaneously. For the determination of potential byproducts air sampling was done additionally with Carbograph® 1TD tubes, multi-bed tubes, DNPH-cartridges and silica cartridges.

3. Results

3.1. Results of the Experiments in 20 L Emission Test Chambers

A degradation of toluene, butyl acetate and limonene was achieved with pure TiO2 and TiO2-GO catalyst samples under UV LED light (Table 3). Within 24 h the degradation maxima were achieved and stayed constant until the light was switched off. By using GO amounts of 10% and 14% the VOC degradation was inhibited under UV and blue LED light. This phenomenon is already described in the literature by Aleksandrzak et al. [13] for the photocatalytic degradation of phenol. The photocatalytic degradation was highest when using single layered graphene, while by increasing the amount of layers, the photocatalytic degradation decreased. It is assumed that this effect is a result of surface and electronic properties of graphene oxide with TiO2, e.g., the transport of electron-hole pairs between TiO2 and GO is reduced. Under blue LED light limonene was degraded in most cases but butyl acetate could only be degraded by six samples, whereas toluene could not be degraded at all (see Table 3). Limonene has the highest degradation rate of the three VOC, which becomes most obvious by comparing the results obtained under blue LED light (Table 3). When using pure TiO2 only limonene could be degraded under blue LED light, but when GO was introduced into the catalytic system butyl acetate was also degraded at least in some cases. This might be a result of the fact that graphene oxide enhances the reactivity of the catalytic system due to the formation of more π–π interactions between catalyst and VOC.

3.2. Results of the Experiments in a 1 m³ Emission Test Chamber

Degradation experiments were performed with samples A-1 and D-1. Both catalyst samples showed a slight degradation of all VOC after 24 h (Table 4). The degradation obtained in the 1 m³ emission test chamber was lower than in the 20 L emission test chambers (Table 3), which might be caused by the lower loading factor (20 L emission test chamber: L = 0.5 m2·m−3; 1 m³ emission test chamber: L = 0.03 m2·m−3) and the higher air change rate (20 L emission test chamber: n = 0.6 h−1; 1 m³ emission test chamber: n = 1 h−1) resulting in a shorter reaction time of the VOC molecules with the catalyst.
Byproducts detected for sample A-1 were formaldehyde, acetic acid, formic acid and traces of crotonaldehyde, octenal, nonenal and undecenal. Degradation of sample D-1 resulted in similar byproducts namely formaldehyde, acetaldehyde, acetic acid, formic acid and traces of octenal (Table 4). Formaldehyde, acetaldehyde, formic acid and acetic acid are already literature known byproducts of photocatalytic toluene degradation [19]. The same applies to the formed byproducts of limonene [20].

3.3. Influence of Relative Humidity

According to the literature [14,15] a certain amount of relative humidity is necessary to obtain photocatalytic degradation by using TiO2 as catalytic material (see Section 1). The experiments presented in this article were either performed at 0% relative humidity (20 L emission test chamber) or 40% relative humidity (1 m³ emission test chamber). A better VOC degradation was obtained at 0% relative humidity for catalyst samples made of pure TiO2 and combinations of TiO2 and GO as can be seen by comparing the results in Table 3 and Table 4. This outcome disproves the theory that a certain level of relative humidity is inevitable to obtain photocatalytic degradation. Consequently, in the presented experiments the superoxide radical anion might lead to photocatalytic VOC degradation. This radical is formed of the atmospheric oxygen in the air and is also strong enough to degrade VOC. This is supported by an article from Sun et al. [21] where the superoxide anion radical is described as the active species which degrades toluene photocatalytically.

4. Conclusions

Various TiO2-GO composite photocatalysts have been tested for the degradation of reference VOC toluene, butyl acetate and limonene at typical indoor air concentration levels at 0% relative humidity. During irradiation experiments it has been revealed, that a modification of TiO2 with trace amounts of GO (0.75%–5%) is beneficial for its photocatalytic performance under blue light. Increasing the amount of GO (10% or higher) however significantly reduces its activity both under UV as well as blue light irradiation.
Adsorption on the catalyst surface strongly affected the time for the degradation experiment. Toluene showed no adsorption onto the catalyst but butyl acetate and limonene adsorbed on its surface. It took up to 5 weeks until an adsorption-desorption equilibrium was achieved. For the investigation of photocatalytic degradation, it is very important to distinguish between adsorption and degradation. When measuring the decrease of VOC concentrations, it is necessary to ensure that the decrease is induced only by degradation.
In an experiment with VOC air concentrations of approximately 300 µg·m−3 at 40% relative humidity it was investigated if byproducts are formed during the degradation process. Byproducts already known from literature, e.g., formaldehyde, acetaldehyde, formic acid and acetic acid, could be detected. Unfortunately, those byproducts might be more harmful than the original VOC. For that reason, it would be helpful to develop catalysts which do not form byproducts but only water and carbon dioxide. The described test method is a useful tool for such development.

Acknowledgments

The research project was supported by the Federal Ministry of Economics and Technology under grant number KF2201064ZG3.

Author Contributions

Birte Mull and Olaf Wilke conceived and designed the experiments. Lennart Möhlmann performed the experiments and analyzed the data. Birte Mull wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Klepeis, N.E.; Nelson, W.C.; Ott, W.R.; Robinson, J.P.; Tsang, A.M.; Switzer, P.; Behar, J.V.; Hern, S.C.; Engelmann, W.H. The national human activity pattern survey (NHAPS): A resource for assessing exposure to environmental pollutants. J. Expo. Anal. Environ. Epidemiol. 2001, 11, 231–252. [Google Scholar] [CrossRef] [PubMed]
  2. Wolkoff, P.; Clausen, P.A.; Jensen, B.; Nielsen, G.D.; Wilkins, C.K. Are we measuring the relevant indoor pollutants? Indoor Air 1997, 7, 92–106. [Google Scholar] [CrossRef]
  3. Mo, J.; Zhang, Y.; Xu, Q.; Lamson, J.J.; Zhao, R. Photocatalytic purification of volatile organic compounds in indoor air: A literature review. Atmos. Environ. 2009, 43, 2229–2246. [Google Scholar] [CrossRef]
  4. Pelaez, M.; Nolan, N.T.; Pillai, S.C.; Seery, M.K.; Falaras, P.; Kontos, A.G.; Dunlop, P.S.M.; Hamilton, J.W.J.; Byrne, J.A.; O’Shea, K.; et al. A review on the visible light active titanium dioxide photocatalysts for environmental applications. Appl. Catal. B Environ. 2012, 125, 331–349. [Google Scholar] [CrossRef]
  5. Banerjee, S.; Pillai, S.C.; Falaras, P.; O’Shea, K.E.; Byrne, J.A.; Dionysiou, D.D. New insights into the mechanism of visible light photocatalysis. J. Phys. Chem. Lett. 2014, 5, 2543–2554. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  6. Geim, A.K.; Novoselov, K.S. The rise of graphene. Nat. Mater. 2007, 6, 183–191. [Google Scholar] [CrossRef] [PubMed]
  7. Jo, W.-K.; Kang, H.-J. Titanium dioxide-graphene oxide composites with different ratios supported by pyrex tube for photocatalysis of toxic aromatic vapors. Powder Technol. 2013, 250, 115–121. [Google Scholar] [CrossRef]
  8. Khalid, N.R.; Ahmed, E.; Hong, Z.L.; Sana, L.; Ahmed, M. Enhanced photocatalytic activity of graphene-TiO2 composite under visible light irradiation. Curr. Appl. Phys. 2013, 13, 659–663. [Google Scholar] [CrossRef]
  9. Nguyen-Phan, T.-D.; Pham, V.H.; Shin, E.W.; Pham, H.-D.; Kim, S.; Chung, J.S.; Kim, E.J.; Hur, S.H. The role of graphene oxide content on the adsorption-enhanced photocatalysis of titanium dioxide/graphene oxide composites. Chem. Eng. J. 2011, 170, 226–232. [Google Scholar] [CrossRef]
  10. Stankovich, S.; Dikin, D.A.; Dommett, G.H.; Kohlhaas, K.M.; Zimney, E.J.; Stach, E.A.; Piner, R.D.; Nguyen, S.T.; Ruoff, R.S. Graphene-based composite materials. Nature 2006, 442, 282–286. [Google Scholar] [CrossRef] [PubMed]
  11. Leary, R.; Westwood, A. Carbonaceous nanomaterials for the enhancement of TiO2 photocatalysis. Carbon 2011, 49, 741–772. [Google Scholar] [CrossRef]
  12. Zhang, Y.; Tang, Z.-R.; Fu, X.; Xu, Y.-J. TiO2-graphene nanocomposites for gas-phase photocatalytic degradation of volatile aromatic pollutant: Is TiO2-graphene truly different from other TiO2-carbon composite materials? ACS Nano 2010, 4, 7303–7314. [Google Scholar] [CrossRef] [PubMed]
  13. Aleksandrzak, M.; Adamski, P.; Kukulka, W.; Zielinska, B.; Mijowska, E. Effect of graphene thickness on photocatalytic activity of TiO2-graphene nanocomposites. Appl. Surface Sci. 2015, 331, 193–199. [Google Scholar] [CrossRef]
  14. Zhao, J.; Yang, X. Photocatalytic oxidation for indoor air purification: A literature review. Build. Environ. 2003, 38, 645–654. [Google Scholar] [CrossRef]
  15. Mo, J.H.; Zhang, Y.P.; Xu, Q.J. Effect of water vapor on the by-products and decomposition rate of ppb-level toluene by photocatalytic oxidation. Appl. Catal. B Environ. 2013, 132, 212–218. [Google Scholar] [CrossRef]
  16. Demeestere, K.; Dewulf, J.; van Langenhove, H. Heterogeneous photocatalysis as an advanced oxidation process for the abatement of chlorinated, monocyclic aromatic and sulfurous volatile organic compounds in air: State of the art. Crit. Rev. Environ. Sci. Technol. 2007, 37, 489–538. [Google Scholar] [CrossRef]
  17. Korologos, C.A.; Philippopoulos, C.J.; Poulopoulos, S.G. The effect of water presence on the photocatalytic oxidation of benzene, toluene, ethylbenzene and m-xylene in the gas-phase. Atmos. Environ. 2011, 45, 7089–7095. [Google Scholar] [CrossRef]
  18. Richter, M.; Jann, O.; Horn, W.; Pyza, L.; Wilke, O. System to generate stable long-term voc gas mixtures of concentrations in the ppb range for test and calibration purposes. Gefahrst. Reinhalt. Luft 2013, 73, 103–106. [Google Scholar]
  19. Mo, J.; Zhang, Y.; Xu, Q.; Zhu, Y.; Lamson, J.J.; Zhao, R. Determination and risk assessment of by-products resulting from photocatalytic oxidation of toluene. Appl. Catal. B Environ. 2009, 89, 570–576. [Google Scholar] [CrossRef]
  20. Ourrad, H.; Thevenet, F.; Gaudion, V.; Riffault, V. Limonene photocatalytic oxidation at ppb levels: Assessment of gas phase reaction intermediates and secondary organic aerosol heterogeneous formation. Appl. Catal. B Environ. 2015, 168–169, 183–194. [Google Scholar] [CrossRef]
  21. Sun, J.J.; Li, X.Y.; Zhao, Q.D.; Ke, J.; Zhang, D.K. Novel V2O5/BiVO4/TiO2 nanocomposites with high visible-light-induced photocatalytic activity for the degradation of toluene. J. Phys. Chem C 2014, 118, 10113–10121. [Google Scholar] [CrossRef]
Figure 1. Photocatalytic degradation mechanism.
Figure 1. Photocatalytic degradation mechanism.
Environments 04 00009 g001
Figure 2. Experimental setup of the gas mixing chamber with two connected 20 L emission test chambers. Both chambers are equipped with ceramic tiles and one is irradiated with UV light.
Figure 2. Experimental setup of the gas mixing chamber with two connected 20 L emission test chambers. Both chambers are equipped with ceramic tiles and one is irradiated with UV light.
Environments 04 00009 g002
Table 1. Maximum initial concentrations.
Table 1. Maximum initial concentrations.
SampleGO (%)Catalyst Loading (mg)Toluene (µg·m−3)Butyl Acetate (µg·m−3)Limonene (µg·m−3)
A-1039230130110
B-10.7539100140170
B-20.7578100220390
C-113919012060
C-217823014040
D-12.539140130100
D-22.57815011090
D-3 *2.559014080
E-153980120100
E-25789014040
F-11039220190420
F-2 #1078230170330
G-1141080120140
* Applied by doctor blade technique; # investigated only under UV light.
Table 2. Initial concentrations.
Table 2. Initial concentrations.
SampleGO (%)Catalyst Loading (mg)Toluene (µg·m−3)Butyl Acetate (µg·m−3)Limonene (µg·m−3)
A-1039290380360
D-12.539290390330
Table 3. Degradation (%) of toluene, butyl acetate and limonene under UV and blue LED light.
Table 3. Degradation (%) of toluene, butyl acetate and limonene under UV and blue LED light.
SampleGO (%)Catalyst Loading (mg)UV LED LightBlue LED Light
Toluene (%)Butyl Acetate (%)Limonene (%)Toluene (%)Butyl Acetate (%)Limonene (%)
A-1039>95>95>950092
B-10.7539>95>95>95012>95
B-20.7578>95>95>95010>95
C-1139>95>95>9500>95
C-2178>95>95>95039>95
D-12.539>95>95>95014>95
D-22.578>95>95>95034>95
D-3 *2.55>95>95>950092
E-153993>95>95011>95
E-257894>95>9500>95
F-110392392940014
F-21078188184n.m.n.m.n.m.
G-11410026>950010
* Applied by doctor blade technique; n.m.: not measured.
Table 4. Degradation of volatile organic compounds (VOC) in a 1 m³ emission test chamber at 40% relative humidity under UV light.
Table 4. Degradation of volatile organic compounds (VOC) in a 1 m³ emission test chamber at 40% relative humidity under UV light.
SampleToluene (%)Butyl Acetate (%)Limonene (%)Formaldehyde (µg·m−3)Acetaldehyde (µg·m−3)Formic Acid (µg·m−3)Acetic Acid (µg·m−3)
A-1510129n.d.1432
D-19211518105543
n.d.: Not detected.

Share and Cite

MDPI and ACS Style

Mull, B.; Möhlmann, L.; Wilke, O. Photocatalytic Degradation of Toluene, Butyl Acetate and Limonene under UV and Visible Light with Titanium Dioxide-Graphene Oxide as Photocatalyst. Environments 2017, 4, 9. https://doi.org/10.3390/environments4010009

AMA Style

Mull B, Möhlmann L, Wilke O. Photocatalytic Degradation of Toluene, Butyl Acetate and Limonene under UV and Visible Light with Titanium Dioxide-Graphene Oxide as Photocatalyst. Environments. 2017; 4(1):9. https://doi.org/10.3390/environments4010009

Chicago/Turabian Style

Mull, Birte, Lennart Möhlmann, and Olaf Wilke. 2017. "Photocatalytic Degradation of Toluene, Butyl Acetate and Limonene under UV and Visible Light with Titanium Dioxide-Graphene Oxide as Photocatalyst" Environments 4, no. 1: 9. https://doi.org/10.3390/environments4010009

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop