Previous Article in Journal
Fabricating Water Dispersible Superparamagnetic Iron Oxide Nanoparticles for Biomedical Applications through Ligand Exchange and Direct Conjugation
Previous Article in Special Issue
Effects of Atomization Injection on Nanoparticle Processing in Suspension Plasma Spray
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

TiAl3-TiN Composite Nanoparticles Produced by Hydrogen Plasma-Metal Reaction: Synthesis, Passivation, and Characterization

1
School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan 430023, China
2
Department of Materials Engineering, School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2016, 6(6), 101; https://doi.org/10.3390/nano6060101
Submission received: 5 April 2016 / Revised: 18 May 2016 / Accepted: 23 May 2016 / Published: 1 June 2016
(This article belongs to the Special Issue Plasma Nanoengineering and Nanofabrication)

Abstract

:
TiAl3 and TiN composite nanoparticles were continuously synthesized from Ti–48Al master alloy by hydrogen plasma-metal reaction in a N2, H2 and Ar atmosphere. The phase, morphology, and size of the nanoparticles were studied by X-ray diffraction (XRD) and transmission electronic microscopy (TEM). X-ray photoelectron spectroscopy (XPS) and evolved gas analysis (EGA) were used to analyze the surface phase constitution and oxygen content of the nanoparticles. The as-synthesized nanopowders were mainly composed of nearly spherical TiAl3 and tetragonal TiN phases, with a mean diameter of ~42 nm and mass fractions of 49.1% and 24.3%, respectively. Passivation in the atmosphere of Ar and O2 for 24 h at room temperature led to the formation of amorphous Al2O3 shells on the TiAl3 particle surface, with a mean thickness of ~5.0 nm and a mass fraction of ~23.5%, as well as TiO2 with a mass fraction of ~3.2%.

Graphical Abstract

1. Introduction

Hydrogen plasma-metal reaction (HPMR) is an effective method to synthesis nanoparticles of pure metals or alloys that was first developed by Uda and coauthors [1,2,3]. After that, improvements have been made on this method so that metal nanoparticles can be continuously produced [4]. The merits of HPMR include: (1) high generation rate; (2) wide applicability; (3) high purity of the produced particles; and (4) nanoscale particle size. By now, nanoparticles of pure metals and different binary or ternary alloys have been successfully produced by HPMR [5,6,7,8,9]. Synthesis of nanoparticles in a large quantity is important for the manufacturing of components by the traditional powder metallurgy method and the 3D rapid prototyping that has quickly developed in recent years [10]. The Ti-Al system is important for applications in automobile and aerospace industries. In previous studies [11,12], nanoparticles of titanium aluminides were investigated in the Ti-Al binary alloy by HPMR. However, the synthesis of nanopowders containing Ti-Al intermetallic and ceramic nanoparticles has not been reported. Due to the large surface area, the as-synthesized metallic nanoparticles usually need to be passivated before full exposure to the air. Passivation of metallic nanoparticles (e.g., Al nanoparticles) was usually conducted in Ar and O2 atmosphere, and sometimes in different liquid or solid substances [13,14]. As passivation can lead to changes in the composition, phase, and property of the surface of nanoparticles, the investigation and characterization of the surface of passivated nanoparticles are necessary [15,16,17] but quantitative characterization is usually difficult. In our previous study [18], Al2O3/Ti2AlN composites with a novel combination of high temperature properties were fabricated successfully from TiAl3-TiN composite nanoparticles by HPMR, for which quantitative characterization of the composition, surface structure, and phase fraction of the composite nanoparticles after passivation is of great importance.
In this study, we reported the synthesis and quantitative characterization of TiAl3-TiN composite nanoparticles from a Ti-Al binary system by hydrogen plasma-metal reaction in a N2, H2, and Ar atmosphere. The phase, morphology, and size of the composite nanoparticles, as well as their passivation behaviors, were studied by X-ray diffraction (XRD), transmission electronic microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and evolved gas analysis (EGA). The surface composition, structure, and phase fraction of the composite nanoparticles after passivation were determined.

2. Experiment Procedure

2.1. Synthesis of Nanoparticles

The master alloys used in this work were prepared from 99.5% sponge Ti and 99.8% Al buttons by melting three times using a consumable electrode vacuum furnace. The master alloy was designed as Ti–48Al (at. %, the same for below) and machined into 20 mm in diameter and 200 mm in height. The HPMR equipment used in this study was developed on the base of [1,2,3]. The chamber was then evacuated to about 100 Pa using a rotary pump, washed three times with argon gas, and backfilled with high purity argon, hydrogen, and nitrogen to a predetermined pressure. The chamber atmosphere is the mixture gas of N2, H2, and Ar (0.2:1:1) with a total pressure of 0.1 MPa. The master alloy underwent evaporation, reaction, and condensation to form nanoparticles. The nanoparticles were then transferred by a circulating pump and deposited onto the inner surfaces of the collection chamber. Passivation of nanoparticles was performed in the atmosphere of Ar and O2 at room temperature for 24 h.

2.2. Characterization

XPS analysis was performed on the ESCALAD-250 spectrometer (Thermo Electron, Waltham, MA, USA) using monochromated Al Kα X-rays (1486.6 eV) and a hemispherical analyzer. The samples were mounted onto carbon adhesive tape. The operating parameters were as follows: the system base pressure was 1 × 10−6–7 × 10−6 Pa; the diameter of the X-ray beam was 100 μm, and the angle of emission of the detected photoelectrons (relative to the surface normal) was 45°. The evolved gas analysis (EGA) was performed on a TC-436 Oxygen/Nitrogen determinator (LECO, Saint Joseph, MI, USA) operating in the inert gas fusion principle. The samples (0.1–0.3 g in mass) were mixed with a pre-degassed graphite powder as a reducing agent, placed into pre-degassed graphite crucibles, and ramp heated under a helium flow. The evolution of the CO and CO2 gases was monitored on-line with non-dispersive infrared detectors (NDIR) (LECO, Saint Joseph, MI, USA). XRD was performed with an Ultima IV diffractometer (Rigaku, Tokyo, Japan) using Cu Kα radiation. The microscopic images of the nanoparticles were obtained using a JEOL-2000FX (JEOL, Tokyo, Japan) TEM. High resolution transmission electron microscopy (HRTEM) was conducted on a JEOL-TEM2100 transmission electron microscope (JEOL, Tokyo, Japan). The sample was sonicated in acetone and dropped onto a carbon coated copper grid.

3. Results and Discussion

Figure 1 shows typical bright-field TEM images of nanoparticles produced from Ti–48Al master alloy in the N2, H2, and Ar atmosphere. Two kinds of morphologies of the as-synthesized nanoparticles can be seen from Figure 1: nearly spherical and tetragonal shapes, all dispersing well on the carbon film. The inset of Figure 1b is the corresponding micro-diffraction pattern of the tetragonal particle, which can be indexed as TiN phase. At high temperatures produced by the electric arc, nitrogen atoms can react with the metal vapor containing two elements: Ti and Al. Here TiN phase is formed instead of AlN by the selective reaction of N and Ti atoms. Thermodynamic analysis can explain this selectivity: at the same temperature, the enthalpy of formation of TiN is lower than that of AlN (e.g., the values of enthalpy of formation of TiN and AlN at 298 K are −339.4 kJ/mol and −319.2 kJ/mol, respectively, and those at 2300 K are −264.9 kJ/mol and −258.6 kJ/mol, respectively) [19]. Figure 1c is the particle size distribution of as-synthesized nanoparticles. As shown in Figure 1c, the distribution of nanoparticle size is between 10 nm and 200 nm, with an average of about 42 nm. Interestingly, although the as-synthesized nanoparticles contain two main phases with different morphologies, the average sizes of them are similar. The XRD pattern (Figure 2) further indicates that the as-synthesized nanoparticles comprise two main phases of TiAl3 and TiN. This is different from the Ti-Al nanoparticles synthesized in Ar and H2 atmosphere: the Ti-Al nanoparticles synthesized in Ar and H2 atmosphere from the same master alloy are composed of TiAl3, Ti2Al5, TiAl, and Al phases [11]. In this study, TiAl and Ti2Al5 phases did not appear as indicated by XRD. This is because in the nitrogen-containing atmosphere, Ti first reacts with N to form TiN, which consumes a large fraction of Ti. As Ti content in the vapor decreases, the formation of TiAl and Ti2Al5 phases is suppressed.
Due to the large surface area and high surface activity, the composite nanoparticles were passivated to avoid violent reaction with oxygen by direct exposure to air. Figure 3 is the XPS result of the composite nanoparticles after passivation. As shown in Figure 3, the surface elements of nanopowders are mainly composed of Al, O, and Ti. As can be seen from Figure 3b,c, the O1S photoelectron spectrum shows the binding energy of 531.5 eV, and the Ti2p photoelectron spectrum shows the binding energy of 458.8 eV. As shown in Figure 3d, the fitting analysis of the Al2p photoelectron spectrum agrees well with the experiment data, indicating the binding energies of 73.2 eV and 75.6 eV, respectively. Compared with the standard database, the state of Al element is 3+ of Al2O3, and the state of Ti element is 4+ of TiO2 [20]. A semi quantitative analysis of the surface elemental composition of the composite nanoparticles is listed in Table 1. Table 1 generally indicates that the main surface phase of nanopowders is Al2O3, with only a small amount of TiO2.
Figure 4 shows the total oxygen release curve of the passivated nanoparticles. As shown in Figure 4a, the main oxygen release peak occurs at the time between 110 s and 152 s, and the temperature between 1900 °C and 2100 °C, which corresponds to the oxygen release peak of Al2O3 phase in the nanopowders. The corresponding oxygen fraction for this peak is 12.22 wt. %. As shown in Figure 4b, the oxygen release peak at the time between 66 s and 110 s and the temperature between 1400 °C and 1800 °C has the oxygen content of 1.30 wt. %. It can be concluded that this is the oxygen release peak for TiO2 in the nanopowders. In Figure 4b, the oxygen release peak at the time between 0 s and 41 s and the temperature between 2200 °C and 1100 °C has the oxygen content of 0.18 wt. %, which corresponds to the release peak of adsorbed oxygen. The above results indicate that oxygen in the nanopowders mainly exists in the form of Al2O3 compounds, with a small amount in TiO2 compounds and surface adsorbed oxygen.
The mass fraction of TiN (WTiN) in the powder can be calculated by:
WTiN = WN + WTi/TiN
where WN is the mass fraction of N in the powder, and WTi/TiN is the mass fraction of Ti in TiN, which can be calculated by:
WTi/TiN = WN(MTi + MN)/MN
where MTi and MN are the atomic mass of Ti and N, respectively. The mass fraction of TiO2 (WTiO2) in the powder can be calculated by:
WTiO2 = WO/TiO2 + WTi/O2
where WO/TiO2 and WTi/TiO2 are the mass fraction of O and Ti in TiO2, respectively. WTi/TiO2 can be calculated by:
WTi/TiO2 = WO/TiO2MTi/2MO
where MO is the atomic mass of oxygen.
Similarly, the mass fraction of Al2O3 (WAl2O3) in the powder can be calculated by:
WAl2O3 = WO/Al2O3(1 + 2MAl/3MO)
where MAl is the atomic mass of Al. Also, the mass fraction of TiAl3 (WTiAl3) can be calculated by:
WTiAl3 = (WTi − WTi/TiN − WTi/TiO2) × (1 + 3MAl/MTi)
where WTi is the mass fraction of Ti in the powder.
Table 2 lists the elemental composition of the nanopowders after passivation, measured by gas analysis and chemical analysis, as well as the fractions of oxygen in Al2O3, TiO2, and adsorbed oxygen. Using the data in Table 2, the mass fraction of difference phases in the nanopowders can be calculated by Equations (1)–(6), and the results are given in Table 3.
As shown in Table 3, Al2O3 has a mass fraction of about 23.5% in the nanopowders. However, the XRD pattern of the nanopowders (Figure 2) does not show the Al2O3 peak. This is because the surface oxide is an amorphous structure, as shown in Figure 5. As shown in Figure 5, Al2O3 forms a thin shell structure on the surface of the TiAl3 particle, as similar to the surface oxide shells of Al and Fe nanoparticles [16,17]. Here, the average shell thickness (t) can be estimated by:
t = ( 1 + W Al 2 O 3 ρ TiAl 3 W TiAl 3 ρ Al 2 O 3 3 1 ) R
where R is the radius of the TiAl3 particle, and ρAl2O3 and ρTiAl3 are the density of TiAl3 and Al2O3, respectively. From Equation (7), an average shell thickness of about 5.0 nm is obtained, which agrees well with the HRTEM observations (Figure 5). The surface oxide Al2O3 is dense and protective, which can hinder the further oxidation of nanopowders in air. No further increase of the oxygen content was found in the sample of nanopowders after exposed in air for more than 600 h.

4. Conclusions

In this study, nanopowders were produced continuously by the HPMR method in a N2, H2 and Ar atmosphere from the master alloy of Ti–48Al, followed by passivation in the Ar and O2 atmosphere for 24 h at room temperature. The phase constitution, morphology, and size of the nanopowders were investigated, and the surface composition and phase were quantitatively characterized. The main results are summarized as follows:
(1)
The nanopowders are mainly composed of TiAl3 and TiN phases with an average diameter of ~42 nm. TiAl3 nanoparticles are nearly spherical with a mass fraction of ~49.1%, and TiN nanoparticles are tetragonal with a mass fraction of ~24.3%.
(2)
Passivation of the nanopowders led to the formation of protective amorphous Al2O3 shells on the particle surface, with a mean thickness of ~5.0 nm and a mass fraction of ~23.5%, as well as TiO2 with a mass fraction of ~3.2%.

Acknowledgments

Financial supports from the National Natural Science Foundation of China (Grant 51371128) and the Research Foundation of Wuhan Polytechnic University (Grant 2014833) are acknowledged. Q.S.M. is also supported by the Research Foundation of Wuhan University.

Author Contributions

Q.S.M. and J.Y.L. conceived and designed the experiments; J.Y.L. performed the experiments; Q.S.M. and J.Y.L. analyzed the data and wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Uda, M. Synthesis of new ultrafine metal particles. Bull. Jpn. Inst. Met. 1983, 22, 412–420. [Google Scholar] [CrossRef]
  2. Ohno, S.; Uda, M. Generation rate of ultrafine metal particles in hydrogen plasma-metal reaction. J. Jpn. Inst. Met. 1984, 48, 640–646. [Google Scholar]
  3. Ohno, S.; Uda, M. Preparation for ultrafine particles of Fe–Ni, Fe–Cu and Fe–Si alloys by hydrogen plasma-metal reaction. J. Jpn. Inst. Met. 1999, 53, 946–952. [Google Scholar]
  4. Cui, Z.L.; Zhang, Z.K.; Hao, C.C.; Dong, L.F.; Meng, Z.G.; Yu, L.Y. Structures and properties of nano-particles prepared by hydrogen arc plasma method. Thin Solid Films 1998, 318, 76–82. [Google Scholar] [CrossRef]
  5. Li, X.G.; Liu, T.; Sato, M.; Takahashi, S. Synthesis and characterization of Fe–Ti nanoparticles by nitrogen plasma metal reaction. Powder Technol. 2006, 163, 183–187. [Google Scholar] [CrossRef]
  6. Ohsaki, K.; Uda, M.; Okazaki, K. Preparation of ultra-fine titanium powder by arc-plasma process. Mater. Trans. JIM 1995, 36, 1386–1391. [Google Scholar] [CrossRef]
  7. Liu, T.; Zhang, Y.H.; Li, X.G. Preparations and characteristics of Ti hydride and Mg ultrafine particles by hydrogen plasma–metal reaction. Scr. Mater. 2003, 48, 397–402. [Google Scholar] [CrossRef]
  8. Li, X.G.; Takahashi, S. Synthesis and magnetic properties of Fe–Co–Ni nanoparticles by hydrogen plasma-metal reaction. J. Magn. Magn. Mater. 2000, 214, 195–203. [Google Scholar] [CrossRef]
  9. Sakka, Y.; Okuyama, H.; Uchikoshi, T.; Ohno, S. Synthesis and characterization of Fe and composite Fe–TiN nanoparticles by dc arc-plasma. J. Alloys Compd. 2002, 346, 285–291. [Google Scholar] [CrossRef]
  10. Murr, L.E.; Gaytan, S.M.; Ceylan, A.; Martinez, E.; Martinez, J.L.; Hernandez, D.H.; Machado, B.I.; Ramirez, D.A.; Medina, F.; Collins, S.; et al. Characterization of titanium aluminide alloy components fabricated by additive manufacturing using electron beam melting. Acta Mater. 2010, 58, 1887–1894. [Google Scholar] [CrossRef]
  11. Li, J.Y.; Mei, Q.S. Synthesis of nanoparticles of titanium aluminides by hydrogen plasma-metal reaction: Effects of master alloy composition and chamber pressure on particle size, composition and phase. Powder Metall. 2015, 58, 209–213. [Google Scholar] [CrossRef]
  12. Luo, J.S.; Li, K.; Li, X.B.; Shu, Y.J.; Tang, Y.J. Phase evolution and alloying mechanism of titanium aluminide nanoparticles. J. Alloys Compd. 2014, 615, 333–337. [Google Scholar] [CrossRef]
  13. Kwon, Y.S.; Gromov, A.A.; Strokova, J.I. Passivation of the surface of aluminum nanopowders by protective coatings of the different chemical origin. Appl. Surf. Sci. 2007, 253, 5558–5564. [Google Scholar] [CrossRef]
  14. Nazarenko, O.B.; Amelkovich, Y.A.; Sechin, A.I. Characterization of aluminum nanopowders after long-term storage. Appl. Surf. Sci. 2014, 321, 475–480. [Google Scholar] [CrossRef]
  15. Krasovskii, P.V.; Samokhin, A.V.; Malinovskaya, O.S. Characterization of surface oxide films and oxygen distribution in α-W nanopowders produced in a DC plasma reactor from an oxide feedstock. Powder Technol. 2015, 286, 144–150. [Google Scholar] [CrossRef]
  16. Fung, K.K.; Qin, B.X.; Zhan, X.X. Passivation of α-Fe nanoparticle by γ-Fe2O3 epitaxial shell. Mater. Sci. Eng. A 2000, 286, 135–138. [Google Scholar] [CrossRef]
  17. Sánchez-López, J.C.; Caballero, A.; Fernkndez, A. Characterisation of Passivated Aluminium Nanopowders: An XPS and TEM/EELS Study. J. Eur. Ceram. Soc. 1998, 18, 1195–1200. [Google Scholar] [CrossRef]
  18. Li, J.Y.; Mei, Q.S.; Cui, Y.Y.; Yang, R. Production of Al2O3/Ti2AlN composite with novel combination of high temperature properties. Mater. Sci. Eng. A 2014, 607, 6–9. [Google Scholar] [CrossRef]
  19. Haynes, W.M. Handbook of Chemistry and Physics, 96th ed.; Bruno, T.J., Lide, D.R., Eds.; CRC Press: Boca Raton, FL, USA, 2016. [Google Scholar]
  20. Moulder, J.F. Handbook of X-ray Photoelectron Spectroscopy; Wagner, C.D., Riggs, W.M., Davies, L.E., Muilenberg, G.E., Eds.; Perkin-Elmer: Waltham, MA, USA, 1979. [Google Scholar]
Figure 1. (a) and (b) Typical bright-field transmission electron microscope (TEM) micrographs of the nanoparticles synthesized from the master alloy of Ti–48Al by hydrogen plasma-metal reaction (HPMR) in N2, H2, and Ar atmosphere; (c) particle size distribution.
Figure 1. (a) and (b) Typical bright-field transmission electron microscope (TEM) micrographs of the nanoparticles synthesized from the master alloy of Ti–48Al by hydrogen plasma-metal reaction (HPMR) in N2, H2, and Ar atmosphere; (c) particle size distribution.
Nanomaterials 06 00101 g001
Figure 2. X-ray diffraction analysis (XRD) pattern of the nanoparticles synthesized from the master alloy of Ti–48Al by HPMR in N2, H2, and Ar atmosphere.
Figure 2. X-ray diffraction analysis (XRD) pattern of the nanoparticles synthesized from the master alloy of Ti–48Al by HPMR in N2, H2, and Ar atmosphere.
Nanomaterials 06 00101 g002
Figure 3. (a) X-ray photoelectron spectroscopy (XPS) patterns of the nanoparticles synthesized from the master alloy of Ti–48Al by HPMR in N2, H2, and Ar atmosphere; (bd) are the enlargements corresponding to different ranges of binding energy.
Figure 3. (a) X-ray photoelectron spectroscopy (XPS) patterns of the nanoparticles synthesized from the master alloy of Ti–48Al by HPMR in N2, H2, and Ar atmosphere; (bd) are the enlargements corresponding to different ranges of binding energy.
Nanomaterials 06 00101 g003
Figure 4. (a) Release curve of oxygen in the passivated nanopowders synthesized from the master alloy of Ti–48Al by HPMR in N2, H2, and Ar atmosphere; (b) the amplification in the time range of 0–110 s.
Figure 4. (a) Release curve of oxygen in the passivated nanopowders synthesized from the master alloy of Ti–48Al by HPMR in N2, H2, and Ar atmosphere; (b) the amplification in the time range of 0–110 s.
Nanomaterials 06 00101 g004
Figure 5. High resolution transmission electron microscopy (HRTEM) micrograph of the passivated TiAl3 nanoparticle showing the surface oxide.
Figure 5. High resolution transmission electron microscopy (HRTEM) micrograph of the passivated TiAl3 nanoparticle showing the surface oxide.
Nanomaterials 06 00101 g005
Table 1. Surface composition of the nanopowders.
Table 1. Surface composition of the nanopowders.
ElementOAlTi
Content (at. %)60.9%38.4%1.7%
Table 2. Mass fractions of the elements in the nanopowders and those of oxygen in different phases. See the text for details.
Table 2. Mass fractions of the elements in the nanopowders and those of oxygen in different phases. See the text for details.
WNWTiWAlWO
WOAWO/Al2O3WO/TiO2
5.5%39.0%41.8%0.18%12.22%1.3%
Table 3. Calculated mass fractions of different phases in the nanopowders. See the text for details.
Table 3. Calculated mass fractions of different phases in the nanopowders. See the text for details.
WTiNWTiAl3WAl2O3WTiO2
24.3%49.1%23.5%3.2%

Share and Cite

MDPI and ACS Style

Li, J.Y.; Mei, Q.S. TiAl3-TiN Composite Nanoparticles Produced by Hydrogen Plasma-Metal Reaction: Synthesis, Passivation, and Characterization. Nanomaterials 2016, 6, 101. https://doi.org/10.3390/nano6060101

AMA Style

Li JY, Mei QS. TiAl3-TiN Composite Nanoparticles Produced by Hydrogen Plasma-Metal Reaction: Synthesis, Passivation, and Characterization. Nanomaterials. 2016; 6(6):101. https://doi.org/10.3390/nano6060101

Chicago/Turabian Style

Li, Ju Ying, and Qing Song Mei. 2016. "TiAl3-TiN Composite Nanoparticles Produced by Hydrogen Plasma-Metal Reaction: Synthesis, Passivation, and Characterization" Nanomaterials 6, no. 6: 101. https://doi.org/10.3390/nano6060101

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.