Effect of Alkali Metal Atoms Doping on Structural and Nonlinear Optical Properties of the Gold-Germanium Bimetallic Clusters
Previous Article in Journal
Comparison of Erosion Behavior and Particle Contamination in Mass-Production CF4/O2 Plasma Chambers Using Y2O3 and YF3 Protective Coatings
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Nano-Silica Sol-Gel and Carbon Nanotube Coupling Effect on the Performance of Cement-Based Materials

1
Guangdong Key Provincial Durability Center for Marine Structure, Shenzhen Durability Center for Civil Engineering, Department of Civil Engineering, Shenzhen University, Shenzhen 518060, China
2
Department of Architecture and Civil Engineering, City University of Hong Kong, Kowloon 999077, Hong Kong, China
3
Dipartimento di Chimica, Materiali e Ingegneria Chimica “G. Natta” via Mancinelli, Politecnico di Milano, 7-20131 Milano, Italy
4
College of Water Conservancy and Civil Engineering, South China Agricultural University, Guangzhou 510642, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2017, 7(7), 185; https://doi.org/10.3390/nano7070185
Submission received: 13 April 2017 / Revised: 29 June 2017 / Accepted: 11 July 2017 / Published: 14 July 2017

Abstract

:
Carbon nanotubes (CNTs) have shown promise for improving the mechanical performance of cement composites through crack-bridging and frictional pull-out. The interactive behaviors between CNTs and cement matrix act are crucial in optimizing the reinforcement of CNTs in cement composites. This study investigates the effects of nano-silica (NS) sol-gel on the interactive behaviors of CNTs and the cement matrix through a series of experiments and analyses. UV-visible spectrometer results show that CNTs are well-dispersed in suspension and the addition of NS has a negligible effect on the stability of CNT dispersion. Calorimetry tests and dynamic mechanical analysis demonstrate the nucleation and frictional performance of CNTs in cement matrix, respectively. The paper shows that the physical adsorption of NS on the CNT surface could result in the acceleration of cement hydration. Morphology observation confirms that a denser interface between CNTs and cement hydrates is formed. Finally, the improved interaction between CNTs and cement hydrates leads to a substantial increase in friction between CNTs and the cement matrix under periodic loading. NS may act as an ideal admixture for improving both the interactive behaviors between CNTs and cement matrix and the damping properties of cement composite.

1. Introduction

Concrete is used as a structural material due to its low cost, wide availability and ideal mechanical properties. However, its most important ingredient, hydrated cement paste, is a quasi-brittle material and has disadvantages such as low tensile strength, low ductility and susceptibility to cracking due to early-age shrinkage, which would reduce the mechanical performance of concrete and the service life of concrete structures.
Adding fibers to cement-based materials to develop crack-free concretes with improved ductility is a strategy that has gained considerable attention worldwide in recent years. Among different fiber materials, carbon nanotubes (CNTs) are a promising candidate due to their excellent mechanical, thermal and electrical properties. Theoretically, for an individual CNT, the Young’s modulus and tensile strength could reach 1 TPa and 100 GPa, respectively, with an ultimate strain of up to 15% and specific surface area of up to 1000 m2/g [1,2,3]. To date, many investigations have shown the excellent mechanical and electrical properties of CNTs when they are added to cement-based composites [4,5,6,7,8,9,10].
However, the tendency that CNTs have to agglomerate is still a key issue when they are dispersed in a cement matrix due to their high specific surface area and van der Waals’ force. This poor dispersion confines CNTs as reinforcements in the hydrated cement paste. Various physical and chemical techniques have been introduced to assist with the dispersion of CNTs, such as ultra-sonication, ball-milling, surface functionalization, ionic surfactant and non-ionic surfactant methods [11,12,13,14,15,16,17]. The mechanisms for these dispersion methods could be explained as follows: ultra-sonication releases high levels of energy, which generate microscopic bubbles in suspension, and the bubbles separate individual CNTs from bundles [18]; ball-milling process would charge the surface of CNTs and enable the individual CNTs insert into the composite [19]; using functional groups introduced by surface functionalization and ionic surfactants could form micelles around the CNTs and inhibit its aggregation [20]; the non-ionic surfactants could be absorbed into the surface of CNTs, which contributes to exfoliating individual CNTs from bundles through a steric stabilization effect [14]. Aside from these mentioned methods, another optional method is dispersing CNTs in water with non-covalent functionalization surfactant, which has the characteristic of not changing the inherent electrical and mechanical properties of CNTs [15].
The performance of CNTs/cement composite is not only influenced by the dispersion of CNTs in cement paste, but also related to their interaction. Computational simulation analyses demonstrated that CNTs will provide good reinforcement when the matrix is under loading, when a good connection between the CNTs and matrix is formed [21]. Furthermore, Al–Rub et al. [22] used the finite element simulation method to investigate the key parameters that control the pull-out behavior of a single CNTs from cement matrix and found that the interfacial adhesion governs the pull-out strength. However, due to its smooth surface at an atomic scale [23], the CNTs shows little potential for forming a strong interface with a cement matrix. Few researchers have concentrated on the bonding strength between CNTs and the cement matrix in order to obtain ideal reinforcement of CNTs. The interfacial adhesion between CNTs and cement matrix may be improved either by functional treatment on the CNT surface or by adding additional materials in the composite. Previous efforts have been made to introduce hydroxyl, carboxyl and silica functional groups to the CNT surface for the purposes of higher interfacial strength between CNTs and cement matrix and greater mechanical enhancement of cement composites [24,25,26,27]. Also, due to small particle size and pozzolanic potential, silica fume is used to densify the interface between CNTs and cement matrix and enhance the capacity of load transfer and the overall strength of the cement composite [28]. However, it is reported that silica functional groups actually retard the nucleation effects of CNTs during cement hydration [27]. Although existing studies have shown the potential role of the silica-functional group in the interfacial bond between CNTs and the cement matrix, the probable role of NS in enhancement of interfacial bonds between CNTs and the cement matrix has not been widely studied in the current literature. As stated by Makar and Chan [29], the nucleation of hydration products, calcium silicate hydrate (C–S–H), during the acceleration period by the CNT bundles is responsible for the reinforcements to the matrix. Makar et al. [30] also prove that development of the strength of the matrix is due to the increase in the nucleation effect to the point where C–S–H is held together by the CNTs, producing a dense C–S–H structure against the surfaces of CNTs and leading to crack bridging. The influence of NS on the interaction between CNTs and the cement matrix are not well known, and efficient means for improving damping properties of CNTs/cement composite are urgently needed. Our study will close the knowledge gap concerning the improvement of interfacial interaction between CNTs and cement matrix and provide useful information to alleviate the dynamic vibration response and damage or fatigue in order to meet people’s safety and comfort needs.
In this work, the effects of NS on CNT performance, including nucleation and energy dissipation in the cement matrix, are studied systematically. Dispersion of CNTs in suspension is characterized with a UV-visible spectrophotometer. The influence of nano-silica (NS) on the microstructure and hydration promotion of CNT-reinforced cement pastes are investigated by means of scanning electron microscopy (SEM) and calorimetry tests, respectively. Dynamic mechanical analysis (DMA) is utilized to study the effects of NS on the energy dissipation behavior of CNTs in the cement matrix. The experimental program, analyses and discussions on the results are introduced in detail in this paper as well.

2. Results

2.1. Characterization of Multi-Walled CNT (MWCNT) Dispersion in Aqueous Suspension

In this study, the definitions of samples are explained in Table 1. Figure 1 presents the Ultraviolet-Visible (UV-Visible) Spectroscopy results for MWCNT aqueous suspensions. The characteristic absorbance peak is an indicator for concentration of individual MWCNTs obtained in the suspension. As seen in Figure 1, the characteristic peak (at a wave length of 250 nm) of MW3 (prepared using NS gel) had close intensity as MW1 which was pure MWCNTs suspension. For both of the samples adding NS, an increase in the concentration of MWCNTs from 0.02% (the MW2 samples) to 0.08% (the MW3 samples) led to a slight decrease in absorbance. Table 2 shows the intensity of the characteristic peak at the wave length of 250 nm and its change during the initial 48 h standing. It can be observed that the intensity of the characteristic peak, which compares the concentration of individually dispersed MWCNTs, kept consistent along with the standing duration when the dosage of MWCNTs is 0.02% by weight of cement. However, MWCNTs with a dosage of 0.08% by weight of cement decreased in the intensity as time went by.
The results indicate that addition of NS can negligibly affect the dispersion and stability of MWCNTs in aqueous suspension. For the MWCNT dispersion in NS gel, the optimal dosage of MWCNTs in this study is 0.02% by weight of cement. At a higher MWCNT content, its stability is poor and the NS seems to have slight negative effect on the dispersion in the long term. With a higher MWCNT content, the distance between dispersed individual MWCNTs might diminish, which may lead to a stronger Van del Waals’ force and hence to easier re-agglomeration of MWCNTs.

2.2. Heat of Hydration Test

In this study, the definitions of samples are explained in Table 3. Figure 2 presents the kinetics of the cement hydration of various samples during the initial 72 h, and the total amounts of heat released are listed in Table 4. As seen from Table 4 and Figure 2a, the total amount of heat released during the initial 72 h of hydration follows a descending order of MW0.24-NG (0.02% MWCNT + NS) ≈ MW0.24-W (0.02% MWCNT) > MW0.96-NG (0.08% MWCNT + NS) > MW0-W > MW0-NG (NS). The similar results of MW0.24-NG and MW0.24-W further confirm the dispersion characterization above. For the three samples containing MWCNTs, the less-dispersed MW0.96-NG (using MW3 suspension) seems to slightly decelerate the hydration of cement at the early stage (Figure 4a). The agglomerated CNTs will exhibit smaller specific surface areas and provides fewer precipitation sites for hydration products.
The acceleration period during the first day of calorimetry curves can be assumed to be mainly the hydration of C3S [29]. As seen in Figure 2c, it was found that the extent of C3S hydration followed a descending order of MW0.24-NG > MW0.96-NG > MW0.24-W > MW0-NG > MW0-W. The hydration reaction can be accelerated both by chemical means such as chemical reaction or through the addition of nucleating agents, which promotes the formation of hydration products by offering more sites for the reaction. It is clear from the data in Figure 2c that incorporation of MWCNTs promoted hydration of cement in the composite, which is consistent with other reported findings [11,29]. MWCNTs are physically inert and do not participate in the hydration process; they were assumed to act as nucleation spots for formation of C–S–H, and the C–S–H appears to have formed preferentially around the MWCNTs, which accelerates the formation rate of the C–S–H. Furthermore, a distinct increase in C–S–H formation is detected in samples of MWCNTs dispersed by NS. It should be noted that addition of NS only marginally enhances C–S–H formation.

2.3. Morphology Observation

Figure 3 presents the SEM micrographs of the MWCNT/cement composites with and without the assistance of NS for dispersion. From the micrographs presented, it can be observed that individual MWCNTs were firmly embedded in hydration products, which proved that MWCNTs were well-dispersed in the samples by means of the sonication method. In Figure 3a, individual MWCNTs in the hydrated cement paste with smooth surface can be observed. In comparison, as shown in Figure 3b, the individual MWCNTs dispersed by NS in the cement paste presented in a rough surface morphology. Figure 3c,d indicate that MWCNTs dispersed by NS in cement matrix had bridging and cross-linking effects, respectively.
It is noteworthy that the interface between MWCNTs and cement matrix was densified in Figure 3c,d when compared with the interface from our previous research [13]. As cracks go through the reinforced zone, the pullout performance of MWCNTs dissipates the energy working on crack development under loading. The direct nucleation on the MWCNTs bundles would produce a dense C–S–H structure against the surfaces that would be capable of improving the load-transfer capacity between MWCNTs and the cement matrix.
The nano-fibers in the two samples present different morphologies. An energy dispersive spectrometer (EDS) was used to analyze the difference in the fibers, as shown in Figure 4. For pure MWCNTs with a smooth surface (Figure 4a), carbon was the most common element. In comparison, for the NS-conditioned sample that had the rough MWCNT surface (Figure 4b), elements included in hydration products can be detected, e.g., an obviously high content of Ca. The rough morphology observed in Figure 4b might be a nano-carbon fiber covered with hydration products of NS. NS is believed to adsorb on the surface of MWCNTs and improve density and C-S-H hydration through a pozzolanic reaction [27]. The NS acts as a media to improve the interaction between MWCNTs and C–S–H products, finally leading to a denser interface.

2.4. Damping Property

Figure 5 shows the results of the loss factor Tan δ (Figure 5a), the storage modulus G (Figure 5b) and the loss modulus G″ (Figure 5c) of the cement composites, which were obtained from the DMA test. The results show that the vibration frequency applied to the samples during the DMA test had a limited influence on the results.
As seen from Figure 5a, the sample MW0.24-W had a higher loss factor than MW0-W. Based on Duan and Luo’s theory [31], this could be attributed to dislocations, multi-phase boundaries and multiform interfaces of the MWCNTs. The apparent internal friction forces among the MWCNT bundles and the external friction between MWCNTs and cement matrix might be another main reason. In Figure 5a, the sample MW0.24-NG exhibited a much higher loss factor than MW0.24-W, which indicates an improvement in the vibration-reduction property of MWCNT/cement composite due to the NS coating on MWCNTs. The sample MW0.96-NG has a relatively lower loss factor in comparison with the samples MW0.24-W and MW0.24-NG due to the agglomeration of MWCNTs, which was evidenced by the UV-Visible spectroscopy results in Section 2.1. The agglomerated MWCNTs will degrade the interaction with cement matrix and therefore reduce the friction force under an applied tension.
Figure 5b shows the variation of storage modulus at different frequencies. Comparing the MW0-W and MW0.24-W samples, the latter had a higher storage modulus, especially at low frequencies. This could mean that a relatively strong internal force was formed in MW0.24-W, which was due to be the interactive friction between MWCNTs and hydration products [32]. Meanwhile, it was found that MW0.24-NG presented a marginal higher value than MW0.24-W, indicating that incorporation of NS may increase the friction strength between MWCNTs and hydration products. In comparison, a relatively low storage modulus was observed in MW0.96-NG. The results indicated that the re-agglomeration of MWCNTs in high dosages will lead to poor connection between the MWCNTs and cement matrix, which did not exhibit any noticeable increase in material elasticity.
From the results presented in Figure 5c, it can be observed that MWCNT/cement composites see a significant improvement in the loss modulus after adding NS. The enhancements in sample MW0.24-NG were 48% and 66% with respect to MW0.24-W and MW0-W, respectively. Therefore, addition of NS could improve the energy dissipation ability of MWCNT/cement composite.

3. Discussions

This study investigates the effects of NS on interfacial adhesion between MWCNTs and cement matrix using various methods. Prior to the tests, UV-Visible spectroscopy showed that addition of NS does not affect the dispersion of MWCNTs in suspension. A calorimetry test indicated that NS promotes the nucleation of C–S–H around MWCNTs in cement hydration. Hence, it is proposed in this study that NS may adsorb on and activate the surface of MWCNTs, which offered more active nuclei for formation of C–S–H on MWCNTs and condensed the interface between MWCNTs and cement matrix. Further investigations are carried out to prove this hypothesis. The morphology observation also proves that NS absorbs on the surface of MWCNTs and accelerates the formation of hydration products, leading to a rough MWCNT surface and compact interface between MWCNTs and cement matrix. Based on the previous findings [33], the damping mechanism in cement composite could be attributed to different sources of energy dissipation, including multiform interfaces of cement matrix, frictional damping due to slip-in the unbound regions and damping due to damaged cement matrix. For CNT-reinforced cement composite, addition of CNTs to the cement matrix would introduce diversified dislocation of cement matrix and additional friction damping in the interface. In this study, CNTs are dispersed in the same state and the samples are subjected to non-destructive periodic load, so both multiform interfaces and damping from damage would not contribute greatly to the difference of damping properties. During the small deformation, MWCNTs is able to form friction force with the cement matrix through marginal slippage and hence dissipate the vibration energy. Therefore, in this work, the frictional damping mechanism is highly expected to be the dominant factor affecting the damping properties of cement composite. Compared with the smooth surface of pure CNTs, the NS is able to densify the interface between CNTs and cement matrix through a pozzolanic reaction and enhance the capacity for load transfer [28]. The higher densification between MWCNTs and cement matrix produces better reinforcement of MWCNTs through higher interface frictional strength, which is responsible for the significant energy dissipation of cement composite [31], leading to higher loss modulus and better energy dissipation in DMA tests. Figure 6 shows the schematic representation of the damping properties tested in DMA test. The interface between the NG hydration product and MWCNTs was physically connected, which is supposed to be a new form of friction regime introduced into the composite and should contribute to greater energy dissipation during the DMA analysis. In conclusion, addition of NS can improve the interfacial adhesion between MWCNTs and cement matrix. Compared with the negative nucleation effects of silica-functional CNTs during the cement hydration [28], it is found that NS produces greater improvement in CNT nucleation, which may accelerate the early growth of cement composite strength. Due to the excellent damping ability, it is expected that NS-CNT-reinforced cement composite will be used for important civil infrastructure to alleviate the dynamic vibration response and damage or fatigue, in order to meet the safety and comfort needs of the people.

4. Materials and Methods

4.1. Materials

The cement used in this study is Type I 42.5R Portland cement manufactured by Guangzhou Xinhe Co., Ltd. (Guangzhou, China). The carbon nanotubes are carboxylated multi-walled CNTs (MWCNTs) from Chengdu Organic Chemistry Research Institute (Chengdu, China). Their physical properties are provided by the manufacturer and are shown in Table 5. The nano-silica sol-gel (NS) is bought from Qingdao Yumin Ltd. (Qingdao, China) and its physical properties are provided by the manufacturer and presented in Table 6.

4.2. Methods

In this study, MWCNT/cement composites were prepared in two steps: (a) dispersion of MWCNTs in water for aqueous suspension; (b) manufacture of specimens by mixing cement with the obtained MWCNTs aqueous suspension.

4.2.1. Preparation of Aqueous Dispersion

During the preparation, designated amount of MWCNTs was added into NS gel and water and the composite was mixed with a magnetic stirrer at a constant speed of 200 rpm/min for 10 min. The aqueous suspension of MWCNTs was successively sonicated with a probe sonicator of ultrasonic cell disrupter (JY92-IIN Ultrasonic cell disrupter, Ningbo Scientz Biotechnology Co., Ltd., Ningbo, China). For the sonication process, the total energy output was controlled at 125,000 J/mL and it was set in a cyclic stirring and standing regime, where the duration for each stage was 3 s.

4.2.2. Manufacture of CNTs/Cement Composite

A water-to-cement ratio (w/c) of 0.4 was used for the specimens. One percent (1%) nano-silica by weight of cement was added, and the water content of NS suspension is considered in total water to cement ratio during casting. Plain cement pastes with NS were also prepared as controls. Manufacture and curing of samples followed the following procedures:
The obtained MWCNTs suspension was mixed with cement in a cement paste mixer (NJ-160A, Hebei Dahong Experimental Instrument Co., Ltd., Cangzhou, China) at a low speed of 140 ± 5 r/min for 1 min;
(a)
Extra amount of water was added into the suspension and the composite was mixed at a high speed of 285 ± 10 r/min for 3 min;
(b)
The fresh pastes were cast into molds with dimension of 100 × 12 × 5 mm for DMA test;
(c)
The samples were demolded after 24 h and cured in a 20 °C and relative humidity of 95% environment until test.

4.3. Characterization of the Degree of MWCNT Dispersion

The degree of MWCNT dispersion in water or NS was evaluated based on the absorbance of characteristic peaks in the ultraviolet spectral region (at a length of 250 nm) [34,35] of a UV-Visible spectroscopy (LAMBADA 950, Perkin Elmer, Waltham, MA, USA). The tested substance of 1 mL was taken directly after sonication, and the substance was then diluted in 40 mL distilled water.
Based on the authors’ knowledge, the MWCNTs aqueous suspension may be unstable when standing still in room environment and its properties will change along with standing duration. This change in degree of dispersion within the first 48 h was discussed in this study with a loss rate, ΔA, calculated based on following equation:
Δ A = A 0 A n A 0 × 100 %
where A0 and An are the intensity for the absorbance of the characteristic peaks at a length of 250 nm of the samples tested immediately after the preparation and after standing in the room environment for n hours, respectively.

4.4. Calorimetry Test

2 g of water or aqueous suspension with different MWCNTs concentrations obtained after sonication was poured into a glass ampoule with 5 g of cement inside the calorimeter. The glass ampoule was, then, placed into the isothermal calorimeter (Toni 7338, Zwick Roell, Ulm, Germany). The instrument is set to a temperature of 25 ± 0.1 °C. After equilibrating whole system, the heat evolution of the cement pastes was tracked continuously for three days. Finally, the total rate of heat evolution during early-age cement hydration was recorded.

4.5. Morphology Observation

The scanning electron microscope (SEM) (SU-70, Hitachi, Tokyo, Japan) was used for study the influences of NS on morphology of MWCNTs in cement matrix. Also, energy dispersive spectrometer (EDS) was used to analyze the elemental composition of the fiber structure.

4.6. Dynamic Mechanical Analysis

A dynamic mechanical analysis (DMA) instrument (DMA+1000, Metravib, Limonest, France), as shown in Figure 7, was used to determine the damping properties of materials on 100 × 12 × 5 mm samples. Damping refers to the loss of mechanical energy as the amplitude of motion gradually decreases. Samples were fixed in a three-point bending clamp and tested with a cyclic bending method, in which the temperature was set at 25 °C. The maximum deformation was 7 μm and the frequencies was at 0.5 Hz, 1.0 Hz, 1.5 Hz, 2.0 Hz and 2.5 Hz, respectively. During the analysis, the loss factor (Tan δ) and storage modulus (G) of MWCNT/cement composites were recorded directly by the machine. Then, a loss modulus, namely G″, a measure of the energy dissipated as heat in a viscoelastic material, can be calculated based on Equation (2).
G = T a n δ × G
where Tan δ is a measure of material damping, such as vibration or sound damping; G is a measure on elasticity, revealing ability of a sample in energy reservation; G″ represents the capacity of a material to dissipate energy (mechanical or acoustic) as heat, owing to molecular motion within the sample that dissipate energy as heat. In this study, the G″ is considered to be a comprehensive parameter to explore the effects of NS on MWCNT energy dissipation behavior in cement matrix.

5. Conclusions

In this study, damping properties were first investigated to study the influence of NS on the interactive behaviors between MWCNTs and cement matrix. Addition of NS to MWCNT-reinforced cement composite is proposed as an effective way to improve the interactive behaviors in the interface. The effect of NS on MWCNT dispersion in aqueous suspension was characterized using UV-Visible spectroscopy. Hydration heat and morphology were also investigated to demonstrate the nucleation effect and interface of MWCNTs. Damping properties were evaluated with a DMA test to demonstrate the energy dissipation capacity of MWCNT/cement composite. The following conclusions were drawn:
(a)
For MWCNT dispersion in NS gel, the optimal dosage of MWCNTs in this study is 0.02% by weight of cement;
(b)
Addition of NS does not affect the dispersion of MWCNTs in aqueous suspension;
(c)
NS absorbs on the surface of MWCNTs and promotes the formation of hydration products on the surface of MWCNTs;
(d)
NS improves the interfacial adhesion between MWCNTs and cement matrix, leading to higher loss modulus and improved energy dissipation ability. The property enhancements in the MW0.24-NG sample were 48% and 66% higher than in the MW0.24-W and MW0-W samples, respectively.

Acknowledgments

The authors would like to gratefully acknowledge the Shenzhen Strategic Emerging Industry Development Special Fund (No. JCYJ20150625102603853, No. JCYJ20150324141711682), the National Natural Science Foundation of China (Project numbers: 51408366, 51378303) and Guangdong province science and technology plan projects (Project No. 2015A010105029) for financial support for this study.

Author Contributions

Weiwen Li sketched out the initial idea of this study, contributed to the experimental design and handled the progress of the entire project. Weiming Ji was the main operator for this study, carried out data analyses and drafted this paper. Yaocheng Wang contributed to the revision of this paper, including further data analyses, logic of discussion during writing and basic grammar revision. Forood Torabian Isfahani and Yi Liu and carried out the initial trial experiments and parts of the results. Gengying Li and Feng Xing offered suggestions and detailed methods used for this study and commented on data analyses.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Salvetat, J.P.; Bonard, J.M.; Thomson, N.H.; Kulik, A.J.; Forro, L.; Benoit, W.; Zuppiroli, L. Mechanical properties of carbon nanotubes. Appl. Phys. A 1999, 69, 255–260. [Google Scholar] [CrossRef]
  2. Belytschko, T.; Xiao, S.P.; Schatz, G.C.; Ruoff, R.S. Atomistic simulations of nanotube fracture. Phys. Rev. B 2002, 65, 235430. [Google Scholar] [CrossRef]
  3. Kaushik, B.K.; Goel, S.; Rauthan, G. Future VLSI interconnects: Optical fiber or carbon nanotube—A review. Microelectron. Int. 2007, 24, 53–63. [Google Scholar] [CrossRef]
  4. Konsta-Gdoutos, M.S.; Metaxa, Z.S.; Shah, S.P. Multi-scale mechanical and fracture characteristics and early-age strain capacity of high performance carbon nanotube/cement nanocomposites. Cem. Concr. Compos. 2010, 32, 110–115. [Google Scholar] [CrossRef]
  5. Li, G.Y.; Wang, P.M.; Zhao, X. Pressure-sensitive properties and microstructure of carbon nanotube reinforced cement composites. Cem. Concr. Compos. 2007, 29, 377–382. [Google Scholar] [CrossRef]
  6. Del Carmen Camacho, M.; Galao, O.; Baeza, F.J.; Zornoza, E.; Garcés, P. Mechanical properties and durability of CNTs cement composites. Materials 2014, 7, 1640–1651. [Google Scholar] [CrossRef]
  7. Mendoza, O.; Sierra, G.; Tobón, J.I. Influence of super plasticizer and Ca(OH)2 on the stability of functionalized multi-walled carbon nanotubes dispersions for cement composites applications. Constr. Build. Mater. 2013, 47, 771–778. [Google Scholar] [CrossRef]
  8. Han, B.; Yang, Z.; Shi, X.; Yu, X. Transport properties of carbon-nanotube/cement composites. J. Mater. Eng. Perform. 2013, 22, 184–189. [Google Scholar] [CrossRef]
  9. Li, W.W.; Ji, W.M.; Liu, Y.; Xing, F.; Liu, Y.K. Damping property of a cement-based material containing carbon nanotube. J. Nanomater. 2015, 16, 418. [Google Scholar] [CrossRef]
  10. Xu, S.; Liu, J.; Li, Q. Mechanical properties and microstructure of multi-walled carbon nanotube-reinforced cement paste. Constr. Build. Mater. 2015, 76, 16–23. [Google Scholar] [CrossRef]
  11. Isfahani, F.T.; Li, W.; Redaelli, E. Dispersion of multi-walled carbon nanotubes and its effects on the properties of cement composites. Cem. Concr. Compos. 2016, 74, 154–163. [Google Scholar] [CrossRef]
  12. Siddique, R.; Mehta, A. Effect of carbon nanotubes on properties of cement mortars. Constr. Build. Mater. 2014, 50, 116–129. [Google Scholar] [CrossRef]
  13. Li, W.W.; Ji, W.M.; Wang, Y.C.; Liu, Y.; Shen, R.X.; Xing, F. Investigation on the mechanical properties of a cement-based material containing carbon nanotube under drying and freeze-thaw conditions. Materials 2015, 8, 8780–8792. [Google Scholar] [CrossRef]
  14. Cwirzen, A.; Habermehl-Cwirzen, K.; Penttala, V. Surface decoration of carbon nanotubes and mechanical properties of cement/carbon nanotube composites. Adv. Cem. Res. 2008, 20, 65–74. [Google Scholar] [CrossRef]
  15. Parveen, S.; Rana, S.; Fangueiro, R.; Paiva, M.C. Microstructure and mechanical properties of carbon nanotube reinforced cementitious composites developed using a novel dispersion technique. Cem. Concr. Res. 2015, 73, 215–227. [Google Scholar] [CrossRef]
  16. Wernik, J.M.; Meguid, S.A. On the mechanical characterization of carbon nanotube reinforced epoxy adhesives. Mater. Des. 2014, 59, 19–32. [Google Scholar] [CrossRef]
  17. Ntim, S.A.; Sae-Khow, O.; Witzmann, F.A.; Mitra, S. Effects of polymer wrapping and covalent functionalization on the stability of MWCNTs in aqueous dispersions. J. Colloid Interface Sci. 2011, 355, 383–388. [Google Scholar] [CrossRef] [PubMed]
  18. Konsta-Gdoutos, M.S.; Metaxa, Z.S.; Shah, S.P. Highly dispersed carbon nanotube reinforced cement based materials. Cem. Concr. Res. 2010, 40, 1052–1059. [Google Scholar] [CrossRef]
  19. Liu, Z.Y.; Xu, S.J.; Xiao, B.L.; Xue, P.; Wang, W.G.; Ma, Z.Y. Effect of ball-milling time on mechanical properties of carbon nanotubes reinforced aluminum matrix composites. Compos. A Appl. Sci. Manuf. 2012, 43, 2161–2168. [Google Scholar] [CrossRef]
  20. Sun, Z.; Nicolosi, V.; Rickard, D.; Bergin, S.D.; Aherne, D.; Coleman, J.N. Quantitative evaluation of surfactant-stabilized single-walled carbon nanotubes: Dispersion quality and its correlation with zeta potential. J. Phys. Chem. C 2008, 112, 10692–10699. [Google Scholar] [CrossRef]
  21. Frankland, S.J.V.; Caglar, A.; Brenner, D.W.; Griebel, M. Molecular simulation of the influence of chemical cross-links on the shear strength of carbon nanotube-polymer interfaces. J. Phys. Chem. B 2002, 106, 3046–3048. [Google Scholar] [CrossRef]
  22. Al-Rub, R.K.A.; Kim, S.M.; Bani-Hani, K.A.; Al-Nuaimi, N.; Senouci, A. Finite element simulation of single carbon nanotube pull-outs from a cementitious nanocomposite material using an elastic-plastic-damage and cohesive surface models. Int. J. Theor. Appl. Multiscale Mech. 2014, 3, 31–57. [Google Scholar] [CrossRef]
  23. Schadler, L.S.; Giannaris, S.C.; Ajayan, P.M. Load transfer in carbon nanotube eposy composites. Appl. Phys. Lett. 1998, 73, 3842–3844. [Google Scholar] [CrossRef]
  24. Li, G.Y.; Wang, P.M.; Zhao, X. Mechanical behavior and microstructure of cement composites incorporating surface-treated multi-walled carbon nanotubes. Carbon 2005, 43, 1239–1245. [Google Scholar] [CrossRef]
  25. Hu, Y.; Luo, D.; Li, P.; Li, Q.; Sun, G. Fracture toughness enhancement of cement paste with multi-walled carbon nanotubes. Constr. Build. Mater. 2014, 70, 332–338. [Google Scholar] [CrossRef]
  26. Al-Rub, R.K.A.; Tyson, B.M.; Yazdanbakhsh, A.; Grasley, Z. Mechanical properties of nanocomposite cement incorporating surface-treated and untreated carbon nanotubes and carbon nanofibers. J. Nanomech. Micromech. 2011, 2, 1–6. [Google Scholar] [CrossRef]
  27. Stynoski, P.; Mondal, P.; Marsh, C. Effects of silica additives on fracture properties of carbon nanotube and carbon fiber reinforced Portland cement mortar. Cem. Concr. Compos. 2015, 55, 232–240. [Google Scholar] [CrossRef]
  28. Sanchez, F.; Ince, C. Microstructure and macroscopic properties of hybrid carbon nanofiber/silica fume cement composites. Compos. Sci. Technol. 2009, 69, 1310–1318. [Google Scholar] [CrossRef]
  29. Makar, J.M.; Chan, G.W. Growth of Cement Hydration Products on Single-Walled Carbon Nanotubes. J. Am. Ceram. Soc. 2009, 92, 1303–1310. [Google Scholar] [CrossRef]
  30. Makar, J.; Margeson, J.; Luh, J. Carbon nanotube/cement composites-early results and potential applications. In Proceedings of the 3rd Conference on Construction Materials: Performance, Innovations and Structural Implications, Vancouver, BC, Canada, 22–24 August 2005. [Google Scholar]
  31. Duan, Z.; Luo, J. Effect of multi-walled carbon nanotubes on the vibration-reduction behavior of cement. In Proceedings of the International Conference on Smart Materials and Nanotechnology in Engineering, Harbin, China, 1–4 July 2007; pp. 64230R-1–64230R-6. [Google Scholar]
  32. Guchhait, P.K.; Bhandari, S.; Singh, S.; Rahaman, M. Study on the effect of nanosilica particles on morphology, thermo-mechanical and electrical properties of liquid polysulfide modified epoxy hybrid nanocomposites. Int. J. Plast. Technol. 2011, 15, 150–162. [Google Scholar] [CrossRef]
  33. Chandra, R.; Singh, S.P.; Gupta, K. Damping studies in fiber-reinforced composites—A review. Compos. Struct. 1999, 46, 41–51. [Google Scholar] [CrossRef]
  34. Rastogi, R.; Kaushal, R.; Tripathi, S.K.; Sharma, A.L.; Kaur, I.; Bharadwaj, L.M. Comparative study of carbon nanotube dispersion using surfactants. J. Colloid Interface Sci. 2008, 328, 421–428. [Google Scholar] [CrossRef] [PubMed]
  35. Rausch, J.; Zhuang, R.C.; Mäder, E. Surfactant assisted dispersion of functionalized multi-walled carbon nanotubes in aqueous media. Compos. A Appl. Sci. Manuf. 2010, 41, 1038–1046. [Google Scholar] [CrossRef]
Figure 1. Ultraviolet–Visible (UV-Visible) absorbance of multi-walled carbon nanotubes (MWCNTs) suspension (MW1 refers to 0.02% MWCNTs without nano-silica (NS); MW2 refers to 0.02% MWCNTs with NS; MW3 refers to 0.08% MWCNTs with NS).
Figure 1. Ultraviolet–Visible (UV-Visible) absorbance of multi-walled carbon nanotubes (MWCNTs) suspension (MW1 refers to 0.02% MWCNTs without nano-silica (NS); MW2 refers to 0.02% MWCNTs with NS; MW3 refers to 0.08% MWCNTs with NS).
Nanomaterials 07 00185 g001
Figure 2. Generation of heat during initial hydration. (a) Cumulative heat curves for 72 h hydration; (b) Rate of hydration; (c) Heat flow during 1–24 h.
Figure 2. Generation of heat during initial hydration. (a) Cumulative heat curves for 72 h hydration; (b) Rate of hydration; (c) Heat flow during 1–24 h.
Nanomaterials 07 00185 g002
Figure 3. Scanning electron microscope (SEM) images of MWCNT/cement composites. (a) MWCNTs × 20 K; (b) MWCNTs + NS × 25 K; (c) MWCNTs + NS × 90 K; (d) MWCNTs + NS × 40 K.
Figure 3. Scanning electron microscope (SEM) images of MWCNT/cement composites. (a) MWCNTs × 20 K; (b) MWCNTs + NS × 25 K; (c) MWCNTs + NS × 90 K; (d) MWCNTs + NS × 40 K.
Nanomaterials 07 00185 g003aNanomaterials 07 00185 g003bNanomaterials 07 00185 g003c
Figure 4. Energy dispersive spectrometer (EDS) results of MWCNT/cement composites without and with NS. (a) EDS spectrum (MW-W × 40 K); (b) EDS spectrum (MW-NG × 40 K).
Figure 4. Energy dispersive spectrometer (EDS) results of MWCNT/cement composites without and with NS. (a) EDS spectrum (MW-W × 40 K); (b) EDS spectrum (MW-NG × 40 K).
Nanomaterials 07 00185 g004
Figure 5. Damping property of MWCNT/cement composite. (a) Loss factor; (b) Storage modulus; (c) Loss modulus.
Figure 5. Damping property of MWCNT/cement composite. (a) Loss factor; (b) Storage modulus; (c) Loss modulus.
Nanomaterials 07 00185 g005aNanomaterials 07 00185 g005b
Figure 6. Schematic representation of damping property.
Figure 6. Schematic representation of damping property.
Nanomaterials 07 00185 g006
Figure 7. DMA instrument.
Figure 7. DMA instrument.
Nanomaterials 07 00185 g007
Table 1. Proportions for aqueous dispersion of multi-walled carbon nanotubes (MWCNTs) (MW1 refers to 0.02% MWCNTs without nano-silica (NS); MW2 refers to 0.02% MWCNTs with NS; MW3 refers to 0.08% MWCNTs with NS).
Table 1. Proportions for aqueous dispersion of multi-walled carbon nanotubes (MWCNTs) (MW1 refers to 0.02% MWCNTs without nano-silica (NS); MW2 refers to 0.02% MWCNTs with NS; MW3 refers to 0.08% MWCNTs with NS).
NotationMWCNTs (g)Water (mL)NG (mL)
MW10.241000
MW20.240100
MW30.960100
Table 2. UV-Visible absorbance of multi-walled carbon nanotube (MWCNT) suspension during the initial 48 h standing.
Table 2. UV-Visible absorbance of multi-walled carbon nanotube (MWCNT) suspension during the initial 48 h standing.
Notation0 h3 h12 h24 h48 h
AΔAAΔAAΔAAΔAAΔA
MW1-W1.2001.191%1.182%1.182%1.173%
MW2-NG1.3301.34−1% *1.37−4% *1.36−3% *1.320
MW3-NG1.2000.3273%0.3075%0.2976%0.2976%
* Negative ΔA values indicate increase in intensity of the UV-Visible absorbance.
Table 3. Mix proportions for CNTs/cement composite.
Table 3. Mix proportions for CNTs/cement composite.
NotationCement (g)MWCNTs (g)Water (mL)NG (mL)
MW0-W120004800
MW0-NG11880372120
MW0.24-W12000.24 (0.02%)4800
MW0.24-NG11880.24 (0.02%)372120
MW0.96-NG11880.96 (0.08%)372120
The weight ratio of MWCNTs to cement is calculated in the parenthesis.
Table 4. Summary of cumulative heat of hydration of MWCNT/cement composites.
Table 4. Summary of cumulative heat of hydration of MWCNT/cement composites.
NotationMW0-WMW0-NGMW0.24-WMW0.24-NGMW0.96-NG
Heat (J/g)296.97292.4 (−1.54%)313.13 (+5.44%)314.36 (+5.86%)304.28 (+2.46%)
Table 5. Properties of the MWCNTs.
Table 5. Properties of the MWCNTs.
NotationDiameterLengthPuritySpecific Surface Area–COOHMaking Method
MWCNTs10–20 nm10–30 μm>95%>120 m2/g2 wt %CVD
Table 6. Properties of the NG.
Table 6. Properties of the NG.
NotationSiO2/gelNa2OpHDensityAverage Diameter
NG10%0.18%8.31.04 g/cm314 nm

Share and Cite

MDPI and ACS Style

Li, W.; Ji, W.; Torabian Isfahani, F.; Wang, Y.; Li, G.; Liu, Y.; Xing, F. Nano-Silica Sol-Gel and Carbon Nanotube Coupling Effect on the Performance of Cement-Based Materials. Nanomaterials 2017, 7, 185. https://doi.org/10.3390/nano7070185

AMA Style

Li W, Ji W, Torabian Isfahani F, Wang Y, Li G, Liu Y, Xing F. Nano-Silica Sol-Gel and Carbon Nanotube Coupling Effect on the Performance of Cement-Based Materials. Nanomaterials. 2017; 7(7):185. https://doi.org/10.3390/nano7070185

Chicago/Turabian Style

Li, Weiwen, Weiming Ji, Forood Torabian Isfahani, Yaocheng Wang, Gengying Li, Yi Liu, and Feng Xing. 2017. "Nano-Silica Sol-Gel and Carbon Nanotube Coupling Effect on the Performance of Cement-Based Materials" Nanomaterials 7, no. 7: 185. https://doi.org/10.3390/nano7070185

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop