Next Article in Journal
Extended Near-Infrared Photoactivity of Bi6Fe1.9Co0.1Ti3O18 by Upconversion Nanoparticles
Previous Article in Journal
Effect of Tb-doped Concentration Variation on the Electrical and Dielectric Properties of CaF2 Nanoparticles
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 8
Issue 7
10.3390/nano8070533
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

A Novel Radiation Method for Preparing MnO2/BC Monolith Hybrids with Outstanding Supercapacitance Performance

by
Fan Yang
1,†,
Xichuan Liu
1,2,†,
Rui Mi
1,
Lei Yuan
1,
Xi Yang
1,
Minglong Zhong
1,
Zhibing Fu
1,
Chaoyang Wang
1 and
Yongjian Tang
1,*
1
Science and Technology on Plasma Physics Laboratory, Research Centre of Laser Fusion, China Academy of Engineering Physics, Mianyang 621900, China
2
Shanghai EBIT Lab, Key Laboratory of Nuclear Physics and Ion-beam Application, Institute of Modern Physics, Department of Nuclear Science and Technology, Fudan University, Shanghai 200433, China
*
Author to whom correspondence should be addressed.
†
These authors contributed equally to this work.
Nanomaterials 2018, 8(7), 533; https://doi.org/10.3390/nano8070533
Submission received: 7 June 2018 / Revised: 6 July 2018 / Accepted: 7 July 2018 / Published: 14 July 2018
Browse Figures
Versions Notes

Abstract

:
A novel facile process for fabrication of amorphous MnO2/bamboo charcoal monolith hybrids (MnO2/BC) for potential supercapacitor applications using γ-irradiation methods is described. The structural, morphological and electrochemical properties of the MnO2/BC hybrids have been investigated using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), cyclic voltammetry (CV), galvanostatic charge/discharge (GCD) and electrochemical impedance spectroscopy (EIS) techniques. The combination of BC (electrical double layer charge) and MnO2 (pseudocapacitance) created a complementary effect, which enhanced the specific capacitance and good cyclic stability of the MnO2/BC hybrid electrodes. The MnO2/BC hybrids showed a higher specific capacitance (449 F g−1 at the constant current density of 0.5 A g−1 over the potential range from –0.2 V to 0.8 V), compared with BC (101 F g−1) in 1 M of Na2SO4 aqueous electrolyte. Furthermore, the MnO2/BC hybrid electrodes showed superior cycling stability with 78% capacitance retention, even after 10,000 cycles. The experimental results demonstrated that the high performance of MnO2/BC hybrids could be a potential electrode material for supercapacitors.

1. Introduction

With the rapid increase of global energy demand and the depletion risk of fossil fuels, developing alternative sustainable, affordable, efficient and clean energy has become very urgent in recent decades [1,2]. Among energy storage devices, supercapacitors (or ultracapacitors) have attracted intense interest because of their high energy density, safe operation, super-high service life and great power density [3,4,5]. Due to these features they have broad application areas, such as hybrid vehicles, pulse power systems and digital products [6,7,8]. Depending on the charge storage mechanism, supercapacitors are generally classified into electrical double layer charge (EDLC) and pseudoprocess charge storage. The former stores charge electrostatically in double layers, whereas the latter stores charge on the surface of the electrode active materials as faradaic redox reactions. In general, carbon-based materials are EDLC type [9], while transition metal oxides and conducting polymers are pseudocapacitor type materials [10].
The charge storage of pseudocapacitors is much higher in comparison with that of EDLCs. More recently, transition metal oxides, such as RuO2, MnO2, NiO, SnO2 and WO3, have been widely studied as supercapacitor electrode materials because they generate capacitances from fast superficial redox reactions [11,12,13]. Among many of the reported transition metal oxides, RuO2 has been extensively studied as a suitable material with excellent capacitive performance. However, RuO2 is expensive and rare, constraining its wide practical applications in electrode materials [14]. Except for its poor electric conductivity (10‒5–10‒6 S cm−1), MnO2 is promising as an electrode material due to its natural abundance, various morphology, high theoretical specific capacitance (~1100 F g−1), high density, environmental friendliness and low-cost [15,16]. However, the low electrical conductivity also leads to the decrease of its specific capacitance from theoretical values and limits its wide application. Therefore, many researchers have focused on incorporating MnO2 with highly conductive carbon materials to establish a hybrid type material which combines the advantages of each component [16,17,18]. Yuan et al. fabricated porous MnO2/rice husk derived carbon composites for supercapacitors by in situ chemical precipitation, with outstanding cycling stability (80.2% retention after 5000 cycles), and with specific capacitance of about 210.3 F g−1 at 0.5 A g−1 [6]. Li et al. also used a chemical precipitation method when designing MnO2 nanoflakes/hierarchical porous carbon nanocomposites with a great improvement in specific capacitance (326.9 F g−1 at 1 A g−1) [19]. Li et al. reported hovenia-acerba-like hierarchical MnO2/C hybrids which showed a performance of 132 F g−1 at 0.5 A g−1 [20].
Among conductive materials, activated carbon-based materials are the most promising candidates for supercapacitor applications due to their unique characteristics of large surface area, high electrochemical stability and conductivity [21,22,23,24]. In carbon materials, bamboo charcoal draws research attention for its extraordinarily porous microstructure, cost-efficiency and high absorptive capacity [22,23,25,26,27,28,29,30]. Li et al. studied water bamboo-derived porous carbon with a maximum specific capacitance of 268 F g−1 at a current density of 1 A g−1 in 6 M of KOH electrolyte and showed good capacity retention of 97.28%, even over 5000 cycles at a current density of 10 A g−1 [25]. Yang et al. also synthesized BC by KOH activation, and the specific capacitance retention was more than 91% after 3000 cycles [22]. Impressively, BC has long-lasting life, while MnO2 has high energy density. In this respect, combining each component advantage from BC and MnO2 to improve the performance might bring novel and excellent properties for supercapacitors. However, so far, to the best of our knowledge, nearly no works have been done on this aspect.
For decades, researchers have reported many ways to fabricate MnO2/carbon-based materials, such as a traditional hydrothermal method, chemical precipitation methods, electro-deposition methods, laser/microwave method and sol-gel method [30,31]. Comparing with these methods, as we previously reported [32], the radiation method is facile and fast without using a chemical reagent or even a heat process, and this γ-radiation method has been widely used in biology [33,34,35]. Moreover, we have successfully applied the radiation method for H2 storage [32]. However, so far nearly no studies have been conducted on the preparation of metal oxides and carbon hybrid materials for supercapacitor applications by an irradiation method. The formation mechanism for fabrication materials of irradiation methods also needs further study. In order to broaden the application of this method and further improve the capacitive performance, there is an urgent need to develop this method.
In this work, novel amorphous MnO2/BC hybrids were designed and fabricated by a facile γ-irradiation strategy. Morphologies and microstructures of the samples were investigated by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM), while cyclic voltammetry (CV), galvanostatic charge/discharge (GCD) and electrochemical impedance spectroscopy (EIS) were carried out to study capacitive properties. The electrochemical results demonstrated that MnO2 hybrids delivered a high specific capacity (499 F g−1 at a current density of 0.5 A g−1) and excellent cycle stability (78% capacitance retention even after 10,000 cycles at 1 A g−1). The combination of bamboo (EDLC) and MnO2 (pseudocapacitance) provided short ion diffusion paths and rapid electronic transport, indicating good performance for supercapacitor applications.

2. Materials and Methods

2.1. Preparation of MnO2/BC Hybrids

All the chemical reagents and solvents in this work were analytical grade and used without additional purification. In a typical process, MnO2/BC hybrids were prepared as follows. Mn(NO3)2 (3 mg) was added to deionized water (20 mL) under stirring until complete dissolution for 20 min in a glass vial at room temperature. Then, the BC monoliths (0.2 g) were slowly impregnated with 10 mL of Mn(NO3)2 solution. After 30 min of continuous stirring, 2-Propanol was added with the proper amount to scavenge H* and OH* radicals which were generated during irradiation. The mixture was irradiated at room temperature with a 60Co γ-ray source at a dose rate of 200 Gy min−1, and the total dose was 500 kGy. The product was collected by centrifugation and rinsed several times with deionized (DI) water and ethanol, and then dried at 60 °C for 12 h. Figure 1 shows the schematic diagram for the synthesis of MnO2/BC hybrids and its supercapacitor performance.
For comparison, Bamboo charcoal monoliths were prepared by carbonization of natural bamboo with the KOH-modified method, as described elsewhere [21,26]. The bamboo was washed to remove dust, cut in to small pieces and then dried at 80 °C. After preheating under N2 gas at 500 °C for 3 h in a furnace, the as-prepared materials were ground to powder and mixed with KOH (KOH/C = 1:1) to further carbonize at 850 °C for 4h under a N2 atmosphere. The obtained materials were washed several times with 1 M HCl solution and DI water and then dried at 60 °C.

2.2. Materials Characterization

The crystal structure of the MnO2/BC hybrids was characterized by powder X-ray diffraction (XRD, X’pert PRO, PANalytical B. V, Holand) employing monochromatized Cu Kα incident radiation. The morphology and microstructure of the materials were investigated by field emission scanning electron microscopy (FESEM, Nova 600i, FEI, Hillsboro, OR, USA) equipped with energy dispersive X-ray spectroscopy (EDS) analysis operated at 15 kV and transmission electron microscopy (TEM, FEI-2100 Plus, JEOL, Japan). The surface chemical composition and oxidation state of the MnO2/BC hybrids were determined using X-ray photoelectron spectroscopy (XPS, Kratos Analytical Ltd., Manchester, UK). The nitrogen adsorption/desorption isotherms were carried out at 77 K using a Quantachrome Autosorb-1 instrument (Quantachrome Corporation, Florida, USA). The specific surface area and pore size distribution were calculated by the Brunauer-Emmett-Teller (BET) and density functional theory (DFT) methods, respectively.

2.3. Electrochemical Measurements

The electrochemical tests were carried out at room temperature in a conventional three- and two-electrode configuration, with 1 M of Na2SO4 as an electrolyte using an electrochemical workstation (CHI 660E, Chenhua, Shanghai, China), MnO2/BC as a working electrode, platinum foil as a counter electrode and a saturated calomel electrode (SCE) as a reference electrode. For electrochemical tests, the MnO2/BC (80%) was mixed with acetylene black (10%) and a binder (polyvinylidene fluoride, PVDF, 10%) in Nmethyl-2-pyrrolidone (NMP) to form slurry. Then, the slurry was coated on glassy carbon to fabricate a working electrode with the mass loading of the active material at about 1 mg. The potential range for CV tests was from 0.2 V to 0.8 V, and the measurement range for EIS tests was between 0.01 Hz and 100 kHz, with an alternating current amplitude of 5 mV.

3. Results and Discussion

3.1. Characterization of MnO2/BC Hybrids

Crystal structures of the as-prepared BC and MnO2/BC hybrids were first studied by XRD, and their XRD patterns were shown in Figure 2a. In the XRD pattern of the BC, just like any other pyrolytic carbons, two broad peaks near 23° and 43°correspond to the graphite reflections from (002) and (100) crystal planes respectively, which can be identified as the amorphous forms of BC [6,36]. For the MnO2/BC hybrids, two broad peaks of BC also appeared and almost no obvious difference between BC and MnO2/BC hybrids could be found. Owing to the low content or the amorphous forms of MnO2, no clear diffraction peaks for MnO2 can be detected [37,38]. Ultimately, no other impurity phase peak is found from these patterns, indicating the high purity of the products. A Raman spectrometer was used to further investigate the structural features of the BC and MnO2/BC hybrids, as shown in Figure 2b. We can see two remarkable peaks for both BC and MnO2/BC hybrids at 1353 and 1591 cm−1, which are respectively assigned to the typical D band from the presence of an sp3 defect, and the G band from the in-plane vibration of sp2 carbon atoms of BC [39,40]. Furthermore, the ID/IG ratio is widely applied in evaluating graphitization degree and structural defects. Compared with BC, it can be observed that the ID/IG value for MnO2/BC hybrids ascends from 0.844 to 0.868, manifesting a slight increase in the defect ratio of the deposition of MnO2 and a negligible effect on the structure of the BC. The peak of MnO2/BC hybrids were located at the low wave number region of 640 cm−1, which matches well with the major feature of Mn–O symmetric stretching vibration, around 635–650 cm−1 for MnO2 [40,41,42,43]. This result is in good agreement with the previous reports, providing evidence for the formation of amorphous MnO2 in BC. Thus, XRD and Raman results can clearly demonstrate the successful preparation of the MnO2/BC hybrids. The presence of MnO2/BC hybrids can be confirmed in depth by the results of SEM, TEM and XPS.
The surface morphologies of BC and MnO2/BC hybrids were characterized by SEM and TEM. As shown in Figure S1, we can see clearly that the BC has a smooth surface and irregular forms. Figure 3a shows the morphology of MnO2/BC hybrids, and the skeleton of BC can be seen clearly with a random distribution of MnO2. In particular, the amorphous MnO2 possesses a flower-like structure (Figure 3b). EDS mapping was further used to demonstrate the formation of the MnO2/BC hybrids, and is shown in Figure S2. Obviously, the C, Mn and O elements exist in the MnO2/BC hybrids. To investigate more detailed information about the microstructural features, TEM and high-resolution TEM micrographs of MnO2/BC hybrids are shown in Figure 3c,d. In the TEM image of MnO2/BC hybrids, it is clearly revealed that the amorphous MnO2 is successfully connected with BC. Figure 3d shows an HRTEM image of MnO2/BC and the inset refers to the corresponding selected area electron diffraction (SAED) pattern, further confirming the amorphous structure of MnO2. Therefore, as confirmed by the above SEM, TEM and EDS elemental mapping results, the amorphous MnO2/BC hybrids have been successfully synthesized via a simple γ-irradiation method. This great interfacial contact between MnO2 and BC is favorable for the electronic transport process, thus resulting in enhanced electrochemical performance [44].
The detailed surface chemical composition and valence state of the MnO2/BC hybrids were probed by XPS measurements. Figure 4a shows the XPS spectrum of the MnO2/BC hybrids, and the full survey scan spectrum shows that only three elements (Mn, O and C) are contained in the sample, confirming the high purity of the MnO2/BC hybrids. In the high-resolution scan, Figure 4b shows the XPS spectrum of the Mn 2p doublet peak. The peaks were located at binding energies of 642.4 and 654 eV, which correspond to the Mn 2p3/2 and Mn 2p1/2, respectively. The observed energy position of the doublet is in good agreement with the literature for the Mn4+ oxidation state [45,46]. The energy separation between Mn 2p3/2 and Mn 2p1/2 is 11.6 eV, indicating a normal state of Mn4+ in MnO2 [3,47]. Therefore, MnO2 successfully grows on BC to form the MnO2/BC hybrids, which is a good analogue of the Raman and EDS studies. The XPS spectrum of C 1s from the MnO2/BC hybrids (seen in Figure 4c) is also decomposed into four peaks at 284.6, 285.7, 287.1 and 289.1 eV, which are attributed to (C–C/C=C sp2), (C–O), (C=O) and (–COOH) [48,49], respectively, suggesting bonding between carbon atoms of BC with oxygen atoms of MnO2 facilitates the charge transportation and conductivity of the hybrids [14,50]. As shown in Figure 4d, the O 1s spectrum can be resolved into the three binding energy components of 531, 531.9 and 533.2 eV, which are attributed to the Mn–O–Mn bond of the tetravalent oxide, Mn–O–H bond of hydroxide and H–O–H bond of water, respectively [49,51].
As we know, the specific surface area of the electrode materials is an important factor for supercapacitor performance. The nitrogen adsorption/desorption isotherms and corresponding DFT pore size distribution curves of BC and MnO2/BC hybrids are shown in Figure 5. The detailed porous properties of BC and MnO2/BC hybrids are summarized in Table 1. Both BC and MnO2/BC hybrids (Figure 5a) show type I and IV isotherm curves with type H4 hysteresis loops (IUPAC) [42], indicating micropores and mesopores exist in the samples. The high relative pressure also refers to the macroporous nature of the BC and MnO2/BC hybrids. Detailed DFT pore size distribution structure is shown in Figure 5b. Notably, the BET surface area of BC and MnO2/BC hybrids are 414 and 323 m2 g−1, respectively (Table 1). The BET surface area of the MnO2/BC hybrids is smaller than that of the BC, indicating the amorphous MnO2 partially blocked the pores of the BC, and this phenomenon is consistent with previous reports [52,53]. In addition, the proper pore size distribution and high specific surface area of MnO2/BC hybrids are of huge benefit for faster charge transfers and suitable paths for the electrolyte ions, resulting in excellent electrochemical performance [54,55,56,57].

3.2. Electrochemical Performance of MnO2/BC Hybrids

Cyclic voltammetry (CV) is a powerful technique for the determination of potentials involved. Figure 6a shows the CV curves of the BC and MnO2/BC electrodes at the same scan rate of 5 mV s−1 with a potential window between −0.2 V to 0.8 V in 1 M of Na2SO4 electrolyte. Compared with BC, having almost no obvious redox peaks in CV curves of MnO2/BC is a very common feature among various MnO2 analogues [58,59]. Moreover, it is well known that the charge which is stored within the capacitor may be determined by integrating the CV. The observed integrated area and the current density of the CV curve for the MnO2/BC electrode are much higher than those for the BC electrode, indicating that the contribution of MnO2 to the specific capacitance of MnO2/BC and the complementary effects of MnO2 and BC are significant [59]. The results obtained here are also consistent with the SEM, TEM, XPS and N2 adsorption desorption tests, suggesting the MnO2/BC hybrid morphology provides good contact enabling a fast charge intercalation/deintercalation process. Figure 6b shows the CV curves of the MnO2/BC in 1 M Na2SO4 at different scan rates (2, 5, 10, 20 and 50 mV s−1) over a potential window of −0.2 V to 0.8 V. The corresponding CV curves of BC are provided in Figure S3a. The increase in area under the curve with scan rate is clearly observed, indicating an excellent capacitance behavior and high-rate capability of the electrode.
Charge–discharge measurements were conducted under galvanostatic conditions at different applied current densities. The GCD plots of the BC and MnO2/BC electrodes at a current density of 1 A g−1 are presented in Figure 6c. According to the galvanostatic discharge curves, the specific capacitance Cs (F g−1) of the electrode is calculated based on the following equation:
C s ( F g − 1 ) = I Δ t m Δ V
where I (mA) is the current used for charge-discharge, Δt (s) is the time of the galvanostatic discharging, ΔV (V) is the potential drop during discharge, and m (mg) is the weight of the active material in the electrode. Additionally, the discharge time of MnO2/BC is much longer than BC, showing higher capacitance. This result is in consistent with the CV tests. GCD curves of MnO2/BC and BC (Figure S3b) electrodes recorded at 0.5, 1, 2, 5 and 10 A g−1 are shown in Figure 6d. With the increasing charge and discharge currents, the highly linear and nearly symmetric relationship between potential versus time was also observed, suggesting the desired fast charge and discharge property of the materials. No obvious internal resistance (IR) drop of the BC (Figure S3b) and MnO2/BC electrode was observed for any of the curves, which indicates high conductivity of the materials. The higher C of MnO2/BC is due to the achievement of optimal complementary effects between MnO2 and BC [18]. As shown in Figure 6e, the plot of calculated Cs of MnO2/BC is 449, 319, 310, 299 and 275 F g−1 at current densities of 0.5, 1, 2, 5 and 10 A g−1, respectively, demonstrating that the specific capacitance decreases with increasing current density [60]. Furthermore, about 61% of the capacitance was retained when the current density increased from 0.5 to 10 A g−1. These results are comparable to those MnO2-carbon based electrodes in earlier reports (Table S1). In summary, the enhancement in the electrochemical performance of the MnO2/BC hybrids is mainly explained as follows: (i) The great interfacial contact between MnO2/BC and BC provides short ion diffusion paths and rapid electronic transports; (ii) the complementary effects of the hybrids are favorable for charge storage by EDLC and pseudocapacitance.
The EIS study was conducted to elucidate electrical conductivity and ion transfer features of BC and MnO2/BC electrodes. Electrochemical impedance characteristics of the electrodes were investigated in a frequency range from 100 kHz to 0.01 Hz with an alternating current amplitude of 5 mV in 1 M of Na2SO4 electrolyte. Figure 6f displays the typical Nyquist plots of these BC and MnO2/BC samples and the inset figure shows the magnified plots. All the EIS curves show a semicircle in the high-frequency and a straight line in the low frequency regions. According to previous reports [53,61,62], a straight line should relate to the diffusion of electrolyte ions into the active electrode, whereas the semicircle can be assigned to the charge transfer resistance (Rct) due to the faradic reactions and double-layer capacitance of the electrode/electrolyte interface. The intercept of the semicircle with real axis gives Rs, which is the sum of the ionic resistance of electrolyte, the intrinsic resistance of the active materials and the contact resistance at the interface between electrode and electrolyte, with the Rs values of BC and MnO2/BC hybrids of 0.57 and 1.51 Ω, respectively. In addition, comparing with the BC electrode, the MnO2/BC electrode exhibits much larger Rct, Rs and electrolyte ion diffusion, which is mainly due to the poor electric conductivity of MnO2, partially blocked pores of the BC and the decrease of BET specific surface area. These results coincide with other reports [20,39].
Long term cycling stability is the key factor for evaluating the practical applications of electrodes. In order to explore this, the cycling stability of MnO2/BC hybrids was further investigated by repeating the constant current charge/discharge test between −0.2 V to 0.8 V at a current density of 1 A g−1 for 10,000 cycles in 1 M of Na2SO4 electrolyte as shown in Figure 7. Impressively, after 10,000 continuous charge/discharge cycles, it is observed that the initial capacitance (328 F g−1) of MnO2/BC electrode slightly decreased to 255 F g−1 and about 78% of the initial capacitance was retained, possibly owing to the desquamation of MnO2 from BC monoliths [6]. The inset shows the 1st, 5000th and 10,000th GCD curves, respectively, indicating that the charging/discharging profiles retain excellent linearity and symmetry even after 10,000 cycles. The coulombic efficiency of MnO2/BC hybrids is approximately 100%. Comparing with other studies, to the best of our knowledge, the MnO2/BC hybrid electrode shows comparable cycling stability (Table S1). Moreover, the BC used in our work is much cheaper, and the radiation method is facile and fast. Ragone plots tested by two symmetric electrode configurations of the MnO2/BC hybrids compared with the values of similar MnO2 based supercapacitors are shown in Figure S4. The highest energy density is 23 Wh kg−1 at 50 kW kg−1. Therefore, the complementary effect of MnO2 and BC plays an important role in the sufficient diffusion of electrolyte ions. This result confirms that the prepared MnO2/BC hybrids were highly stable as a novel supercapacitor electrode.

4. Conclusions

In summary, we successfully synthesized MnO2/BC hybrids via a facile γ-irradiation method. The electrochemical capacitive behaviors of the MnO2/BC hybrids and BC have been demonstrated in 1 M Na2SO4 electrolyte between −0.2 V to 0.8 V. In comparison with the BC electrode, MnO2/BC hybrid electrodes showed a higher specific capacitance (449 F g−1 at 0.5 A g−1) and superior cycling performance (about 78% retention even after 10,000 cycles). The excellent performance achieved by the MnO2/BC hybrid electrodes could be ascribed to the complementary effect of conductive BC and the pseudocapacitive behavior of MnO2. We hope that this γ-irradiation method would also pave a new way for the design of other conducting semiconductors as promising electrode materials with enhanced performance for energy storage device applications, as well as expanding practical application fields, such as selective adsorption and catalyst support.

Supplementary Materials

The following are available online at https://www.mdpi.com/2079-4991/8/7/533/s1, Figure S1: (a) Typical SEM images of BC. (b) HRTEM images of the BC (the inset shows SAED pattern), Figure S2: The corresponding elemental mapping of C, Mn, and O for the MnO2/BC hybrids), Figure S3: (a) The CV curves of the BC electrode at different scan rates, and (b) GCD curves of the BC electrode at different current densities, Figure S4: Ragone plots of the MnO2/BC hybrids compared with the values of similar MnO2 based supercapacitors, Table S1: Comparison of various MnO2-carbon based electrodes in recent years as supercapacitors, Table S2: Impedance parameters derived by equivalent circuit model for BC and MnO2/BC electrodes.

Author Contributions

Conceptualization, Y.T. and C.W.; methodology, Z.F. and M.Z.; data Curation, R.M., X.Y. and L.Y.; writing-Original Draft Preparation, F.Y.; writing-Review & Editing, F.Y. and X.L.; supervision, Y.T.

Funding

This research was funded by Research Program of Sichuan province grant number (2016GZ0235) and the Development Foundation of China Academy of Engineering Physics grant number (2015B0302003).

Acknowledgments

We acknowledge Q. Yang, Y. Zeng, J. Li (Science and Technology on plasma physics Laboratory, Research Centre of Laser Fusion, China Academy of Engineering physics, Mianyang, China) for the TEM, SEM and XRD measurements, respectively.

Conflicts of Interest

The authors declare no conflict of interest. The funding bodies had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript; and in the decision to publish the results.

References

  1. Ren, H.; Shi, X.; Zhu, J.; Zhang, Y.; Bi, Y.; Zhang, L. Facile synthesis of n-doped graphene aerogel and its application for organic solvent adsorption. J. Mater. Sci. 2016, 51, 6419–6427. [Google Scholar] [CrossRef]
  2. Zhao, H.-B.; Fu, Z.-B.; Liu, X.-Y.; Zhou, X.-C.; Chen, H.-B.; Zhong, M.-L.; Wang, C.-Y. Magnetic and conductive Ni/carbon aerogels toward high-performance microwave absorption. Ind. Eng. Chem. Res. 2017, 57, 202–211. [Google Scholar] [CrossRef]
  3. Chen, Y.; Qin, W.-Q.; Wang, J.-W.; Chen, B.-Z. Fabrication and electrochemical performance of nanoflake MnO2@carbon fiber coaxial nanocables for supercapacitors. J. Appl. Electrochem. 2015, 46, 241–249. [Google Scholar] [CrossRef]
  4. Xia, X.; Chao, D.; Fan, Z.; Guan, C.; Cao, X.; Zhang, H.; Fan, H.J. A new type of porous graphite foams and their integrated composites with oxide/polymer core/shell nanowires for supercapacitors: Structural design, fabrication, and full supercapacitor demonstrations. Nano Lett. 2012, 14, 1651–1658. [Google Scholar] [CrossRef] [PubMed]
  5. Peng, L.; Peng, X.; Liu, B.; Wu, C.; Xie, Y.; Yu, G. Ultrathin two-dimensional MnO2/graphene hybrid nanostructures for high-performance, flexible planar supercapacitors. Nano Lett. 2013, 13, 2151–2157. [Google Scholar] [CrossRef] [PubMed]
  6. Yuan, C.; Lin, H.; Lu, H.; Xing, E.; Zhang, Y.; Xie, B. Synthesis of hierarchically porous MnO2/rice husks derived carbon composite as high-performance electrode material for supercapacitors. Appl. Energy 2016, 178, 260–268. [Google Scholar] [CrossRef]
  7. Zhao, H.B.; Yuan, L.; Fu, Z.B.; Wang, C.Y.; Yang, X.; Zhu, J.Y.; Qu, J.; Chen, H.B.; Schiraldi, D.A. Biomass-based mechanically strong and electrically conductive polymer aerogels and their application for supercapacitors. ACS Appl. Mater. Interfaces 2016, 8, 9917–9924. [Google Scholar] [CrossRef] [PubMed]
  8. Zhu, J.; He, J. Facile synthesis of graphene-wrapped honeycomb MnO2 nanospheres and their application in supercapacitors. ACS Appl. Mater. Interfaces 2012, 4, 1770–1776. [Google Scholar] [CrossRef] [PubMed]
  9. Ko, J.M.; Kim, K.M. Electrochemical properties of MnO2/activated carbon nanotube composite as an electrode material for supercapacitor. Mater. Chem. Phys. 2009, 114, 837–841. [Google Scholar] [CrossRef]
  10. Lv, G.; Wu, D.; Fu, R. Preparation and electrochemical characterizations of MnO2-dispersed carbon aerogel as supercapacitor electrode material. J. Non-Cryst. Solids 2009, 355, 2461–2465. [Google Scholar] [CrossRef]
  11. Huang, Y.; Li, Y.; Hu, Z.; Wei, G.; Guo, J.; Liu, J. A carbon modified MnO2 nanosheet array as a stable high-capacitance supercapacitor electrode. J. Mater. Chem. A 2013, 1, 9809–9813. [Google Scholar] [CrossRef]
  12. Patil, U.M.; Kulkarni, S.B.; Jamadade, V.S.; Lokhande, C.D. Chemically synthesized hydrous RuO2 thin films for supercapacitor application. J. Alloys Compd. 2011, 509, 1677–1682. [Google Scholar] [CrossRef]
  13. Yao, S.; Zheng, X.; Zhang, X.; Xiao, H.; Qu, F.; Wu, X. Facile synthesis of flexible WO3 nanofibers as supercapacitor electrodes. Mater. Lett. 2017, 186, 94–97. [Google Scholar] [CrossRef]
  14. Cai, Y.; Wang, Y.; Deng, S.; Chen, G.; Li, Q.; Han, B.; Han, R.; Wang, Y. Graphene nanosheets-tungsten oxides composite for supercapacitor electrode. Ceram. Int. 2014, 40, 4109–4116. [Google Scholar] [CrossRef]
  15. Sharma, R.K.; Oh, H.-S.; Shul, Y.-G.; Kim, H. Growth and characterization of carbon-supported MnO2 nanorods for supercapacitor electrode. Phys. B Condens. Matter 2008, 403, 1763–1769. [Google Scholar] [CrossRef]
  16. Hassan, S.; Suzuki, M.; Mori, S.; Abd El-Moneim, A. MnO2/carbon nanowalls composite electrode for supercapacitor application. J. Power Sources 2014, 249, 21–27. [Google Scholar] [CrossRef]
  17. Kiani, M.A.; Khani, H.; Mohammadi, N. MnO2/ordered mesoporous carbon nanocomposite for electrochemical supercapacitor. J. Solid State Electrochem. 2014, 18, 1117–1125. [Google Scholar] [CrossRef]
  18. Li, L.; Hu, Z.A.; An, N.; Yang, Y.Y.; Li, Z.M.; Wu, H.Y. Facile synthesis of MnO2/cnts composite for supercapacitor electrodes with long cycle stability. J. Phys. Chem. C 2014, 118, 22865–22872. [Google Scholar] [CrossRef]
  19. Li, H.; Jiang, L.; Cheng, Q.; He, Y.; Pavlinek, V.; Saha, P.; Li, C. MnO2 nanoflakes/hierarchical porous carbon nanocomposites for high-performance supercapacitor electrodes. Electrochim. Acta 2015, 164, 252–259. [Google Scholar] [CrossRef]
  20. Li, Q.; He, J.; Liu, D.; Yue, H.; Bai, S.; Liu, B.; Gu, L.; He, D. Facile preparation of hovenia-acerba-like hierarchical MnO2/C composites and their excellent energy storage performance for supercapacitors. J. Alloys Compd. 2017, 693, 970–978. [Google Scholar] [CrossRef]
  21. Li, J.; Wu, Q. Water bamboo-derived porous carbons as electrode materials for supercapacitors. New J. Chem. 2015, 39, 3859–3864. [Google Scholar] [CrossRef]
  22. Wang, C.-H.; Wen, W.-C.; Hsu, H.-C.; Yao, B.-Y. High-capacitance KOH-activated nitrogen-containing porous carbon material from waste coffee grounds in supercapacitor. Adv. Powder Technol. 2016, 27, 1387–1395. [Google Scholar] [CrossRef]
  23. Yang, C.-S.; Jang, Y.S.; Jeong, H.K. Bamboo-based activated carbon for supercapacitor applications. Curr. Appl. Phys. 2014, 14, 1616–1620. [Google Scholar] [CrossRef]
  24. Boyjoo, Y.; Cheng, Y.; Zhong, H.; Tian, H.; Pan, J.; Pareek, V.K.; Jiang, S.P.; Lamonier, J.-F.; Jaroniec, M.; Liu, J. From waste Coca Cola® to activated carbons with impressive capabilities for CO2 adsorption and supercapacitors. Carbon 2017, 116, 490–499. [Google Scholar] [CrossRef]
  25. Khamlich, S.; Abdullaeva, Z.; Kennedy, J.V.; Maaza, M. High performance symmetric supercapacitor based on zinc hydroxychloride nanosheets and 3D graphene-nickel foam composite. Appl. Surf. Sci. 2017, 405, 329–336. [Google Scholar] [CrossRef]
  26. Wang, W.; Wang, X.; Wang, X.; Yang, L.; Wu, Z.; Xia, S.; Zhao, J. Cr(VI) removal from aqueous solution with bamboo charcoal chemically modified by iron and cobalt with the assistance of microwave. J. Environ. Sci. 2013, 25, 1726–1735. [Google Scholar] [CrossRef]
  27. Wang, R.; Wang, P.; Yan, X.; Lang, J.; Chao, P.; Xue, Q. Promising porous carbon derived from celtuce leaves with outstanding supercapacitance and CO2 capture performance. ACS Appl. Mater. Interfaces 2012, 4, 5800–5808. [Google Scholar] [CrossRef] [PubMed]
  28. Yu, S.; Liu, D.; Zhao, S.; Bao, B.; Jin, C.; Huang, W.; Chen, H.; Shen, Z. Synthesis of wood derived nitrogen-doped porous carbon–polyaniline composites for supercapacitor electrode materials. RSC Adv. 2015, 5, 30943–30949. [Google Scholar] [CrossRef]
  29. Zhang, Z.; Wang, X.; Wang, Y.; Xia, S.; Chen, L.; Zhang, Y.; Zhao, J. Pb(II) removal from water using Fe-coated bamboo charcoal with the assistance of microwaves. J. Environ. Sci. 2013, 25, 1044–1051. [Google Scholar] [CrossRef]
  30. Strauss, V.; Marsh, K.; Kowal, M.D.; El-Kady, M.; Kaner, R.B. A simple route to porous graphene from carbon nanodots for supercapacitor applications. Adv. Mater. 2018, 30, 1704449. [Google Scholar] [CrossRef] [PubMed]
  31. Pan, Q.; Shim, E.; Pourdeyhimi, B.; Gao, W. Nylon-graphene composite nonwovens as monolithic conductive or capacitive fabrics. ACS Appl. Mater. Interfaces 2017, 9, 8308–8316. [Google Scholar] [CrossRef] [PubMed]
  32. Zhong, M.; Fu, Z.; Huang, W.; Yang, X.; Liu, M.; Huang, X.; Wang, C.; Tang, Y. Fabrication of porous Pd/C microspheres in carbon aerogels by radiation method. Mater. Lett. 2015, 139, 314–317. [Google Scholar] [CrossRef]
  33. Youn-Il, P.; Huang, W.; Chen, H.; Shen, Z. Effects of low dose γ-radiation on photosynthesis of red pepper (Capsicum annuum L.) and the reduction of photoinhibition. Korean Soc. Environ. Agric. 2002, 21, 83–89. [Google Scholar]
  34. Yu, D.; Yang, S. Effects of low dose γ radiation on the dormancy, growth and physiological activity of seed potato (Solanum tuberosum L.). Hortic. Environ. Biotechnol. 2002, 43, 596–602. [Google Scholar]
  35. Dewir, Y.H.; Yanping, F.; Yoeup, P.K.; Rangcai, Y.; Ali, M.B. Effect of temperature and γ-radiation on antioxidant defense system in suspension cell culture of carnation (Dianthus caryophyllus). Hortic. Environ. Biotechnol. 2005, 46, 329–334. [Google Scholar]
  36. Sudhan, N.; Subramani, K.; Karnan, M.; Ilayaraja, N.; Sathish, M. Biomass-derived activated porous carbon from rice straw for a high-energy symmetric supercapacitor in aqueous and non-aqueous electrolytes. Energy Fuels 2017, 31, 977–985. [Google Scholar] [CrossRef]
  37. Tong, D.G.; Chu, W.; Wu, P.; Gu, G.F.; Zhang, L. Mesoporous multiwalled carbon nanotubes as supports for monodispersed iron–boron catalysts: Improved hydrogen generation from hydrous hydrazine decomposition. J. Mater. Chem. A 2013, 1, 358–366. [Google Scholar] [CrossRef]
  38. Li, C.; Miao, X.; Chu, W.; Wu, P.; Tong, D.G. Hollow amorphous NaFePO4 nanospheres as a high-capacity and high-rate cathode for sodium-ion batteries. J. Mater. Chem. A 2015, 3, 8265–8271. [Google Scholar] [CrossRef]
  39. Zhang, L.; Li, T.; Ji, X.; Zhang, Z.; Yang, W.; Gao, J.; Li, H.; Xiong, C.; Dang, A. Freestanding three-dimensional reduced graphene oxide/MnO2 on porous carbon/nickel foam as a designed hierarchical multihole supercapacitor electrode. Electrochim. Acta 2017, 252, 306–314. [Google Scholar] [CrossRef]
  40. Xu, L.; Jia, M.; Li, Y.; Jin, X.; Zhang, F. High-performance MnO2-deposited graphene/activated carbon film electrodes for flexible solid-state supercapacitor. Sci. Rep. 2017, 7, 8440–8448. [Google Scholar] [CrossRef] [PubMed]
  41. Luo, X.; Yang, J.; Yan, D.; Wang, W.; Wu, X.; Zhu, Z. MnO2-decorated 3D porous carbon skeleton derived from mollusc shell for high-performance supercapacitor. J. Alloys Compd. 2017, 723, 505–511. [Google Scholar] [CrossRef]
  42. Wen, Y.; Qin, T.; Wang, Z.; Jiang, X.; Peng, S.; Zhang, J.; Hou, J.; Huang, F.; He, D.; Cao, G. Self-supported binder-free carbon fibers/MnO2 electrodes derived from disposable bamboo chopsticks for high-performance supercapacitors. J. Alloys Compd. 2017, 699, 126–135. [Google Scholar] [CrossRef]
  43. He, Y.; Du, S.; Li, H.; Cheng, Q.; Pavlinek, V.; Saha, P. MnO2/polyaniline hybrid nanostructures on carbon cloth for supercapacitor electrodes. J. Solid State Electrochem. 2016, 20, 1459–1467. [Google Scholar] [CrossRef]
  44. Liu, X.; Sheng, G.; Zhong, M.; Zhou, X. Hybrid nanowires and nanoparticles of WO3 in a carbon aerogel for supercapacitor applications. Nanoscale 2018, 10, 4209–4217. [Google Scholar] [CrossRef] [PubMed]
  45. Zhu, G.; He, Z.; Chen, J.; Zhao, J.; Feng, X.; Ma, Y.; Fan, Q.; Wang, L.; Huang, W. Highly conductive three-dimensional MnO2-carbon nanotube-graphene-Ni hybrid foam as a binder-free supercapacitor electrode. Nanoscale 2014, 6, 1079–1085. [Google Scholar] [CrossRef] [PubMed]
  46. Hu, M.; Liu, Y.; Zhang, M.; Wei, H.; Gao, Y. MnO2/porous carbon film/Ni electrodes with high-quality interface for high rate and performance flexible supercapacitors. Electrochim. Acta 2018, 218, 58–65. [Google Scholar] [CrossRef]
  47. Liu, Y.; Liu, J. Hierarchically porous carbon/MnO2 nanocomposites as high-performance electrode for asymmetric supercapacitors. Adv. Mater. 2014, 1070–1072, 530–533. [Google Scholar]
  48. Sari, F.N.I.; Lin, H.-M.; Ting, J.-M. Surface modified catalytically grown carbon nanofibers/MnO2 composites for use in supercapacitor. Thin Solid Films 2016, 620, 54–63. [Google Scholar] [CrossRef]
  49. Liu, W.; Wang, S.; Wu, Q.; Huan, L.; Zhang, X.; Yao, C.; Chen, M. Fabrication of ternary hierarchical nanofibers MnO2/PANI/CNT and theirs application in electrochemical supercapacitors. Chem. Eng. Sci. 2016, 156, 178–185. [Google Scholar] [CrossRef]
  50. Nayak, A.K.; Das, A.K.; Pradhan, D. High performance solid-state asymmetric supercapacitor using green synthesized graphene-WO3 nanowires nanocomposite. ACS Sustain. Chem. Eng. 2017, 5, 10128–10138. [Google Scholar] [CrossRef]
  51. Lv, H.; Gao, X.; Xu, Q.; Liu, H.; Wang, Y.-G.; Xia, Y. Carbon quantum dot-induced MnO2 nanowire formation and construction of a binder-free flexible membrane with excellent superhydrophilicity and enhanced supercapacitor performance. ACS Appl. Mater. Interfaces 2017, 9, 40394–40403. [Google Scholar] [CrossRef] [PubMed]
  52. Wang, J.-W.; Chen, Y.; Chen, B.-Z. Synthesis and control of high-performance MnO2/carbon nanotubes nanocomposites for supercapacitors. J. Alloys Compd. 2016, 688, 184–197. [Google Scholar] [CrossRef]
  53. Ju, J.; Zhao, H.; Kang, W.; Tian, N.; Deng, N.; Cheng, B. Designing MnO2 & carbon composite porous nanofiber structure for supercapacitor applications. Electrochim. Acta 2017, 258, 116–123. [Google Scholar]
  54. Jiang, H.; Li, C.; Sun, T.; Ma, J. A green and high energy density asymmetric supercapacitor based on ultrathin MnO2 nanostructures and functional mesoporous carbon nanotube electrodes. Nanoscale 2012, 4, 807–812. [Google Scholar] [CrossRef] [PubMed]
  55. Luan, Y.; Huang, Y.; Wang, L.; Li, M.; Wang, R.; Jiang, B. Porous carbon@ MnO2 and nitrogen-doped porous carbon from carbonized loofah sponge for asymmetric supercapacitor with high energy and power density. J. Electroanal. Chem. 2016, 763, 90–96. [Google Scholar] [CrossRef]
  56. Wang, X.; Chen, S.; Li, D.; Sun, S.; Peng, Z.; Komarneni, S.; Yang, D. Direct interfacial growth of MnO2 nanostructure on hierarchically porous carbon for high-performance asymmetric supercapacitors. ACS Sustain. Chem. Eng. 2017, 6, 380–387. [Google Scholar] [CrossRef]
  57. Zhi, J.; Reiser, O.; Huang, F. Hierarchical MnO2 spheres decorated by carbon coated cobalt nanobeads: Low cost and high performance electrode materials for supercapacitors. ACS Appl. Mater. Interfaces 2016, 8, 8452–8460. [Google Scholar] [CrossRef] [PubMed]
  58. Guo, C.; Li, H.; Zhang, X.; Huo, H.; Xu, C. 3D porous CNT/MnO2 composite electrode for high-performance enzymeless glucose detection and supercapacitor application. Sens. Actuators B Chem. 2015, 206, 407–414. [Google Scholar] [CrossRef]
  59. Ramezani, M.; Fathi, M.; Mahboubi, F. Facile synthesis of ternary MnO2/graphene nanosheets/carbon nanotubes composites with high rate capability for supercapacitor applications. Electrochim. Acta 2015, 174, 345–355. [Google Scholar] [CrossRef]
  60. Chen, W.; Tao, X.; Wei, D.; Wang, H.; Yu, Q.; Li, Y. High-performance supercapacitor based on actived carbon–MnO2–polyaniline composite. J. Mater. Sci. Mater. Electron. 2015, 27, 1357–1362. [Google Scholar] [CrossRef]
  61. Liu, M.; Gan, L.; Xiong, W.; Xu, Z.; Zhu, D.; Chen, L. Development of MnO2/porous carbon microspheres with a partially graphitic structure for high performance supercapacitor electrodes. J. Mater. Chem. A 2014, 2, 2555–2562. [Google Scholar] [CrossRef]
  62. Vinny, R.T.; Chaitra, K.; Venkatesh, K.; Nagaraju, N.; Kathyayini, N. An excellent cycle performance of asymmetric supercapacitor based on bristles like alpha-MnO2 nanoparticles grown on multiwalled carbon nanotubes. J. Power Sources 2016, 309, 212–220. [Google Scholar] [CrossRef]
Nanomaterials 08 00533 g001 550
Figure 1. Schematic diagram for the synthesis of MnO2/BC hybrids and its supercapacitor performance.
Figure 1. Schematic diagram for the synthesis of MnO2/BC hybrids and its supercapacitor performance.
Nanomaterials 08 00533 g001
Nanomaterials 08 00533 g002 550
Figure 2. (a) XRD pattern and (b) Raman spectrum of the BC and MnO2/BC hybrids.
Figure 2. (a) XRD pattern and (b) Raman spectrum of the BC and MnO2/BC hybrids.
Nanomaterials 08 00533 g002
Nanomaterials 08 00533 g003 550
Figure 3. (a,b) Typical SEM images of the MnO2/BC hybrids. (c,d) TEM and HRTEM images of the MnO2/BC hybrids.
Figure 3. (a,b) Typical SEM images of the MnO2/BC hybrids. (c,d) TEM and HRTEM images of the MnO2/BC hybrids.
Nanomaterials 08 00533 g003
Nanomaterials 08 00533 g004 550
Figure 4. The XPS spectra of MnO2/BC hybrids: (a) Survey scan spectrum; (b) W 2p core level spectrum; (c) C 1s core level spectrum; (d) O 1s core level spectrum.
Figure 4. The XPS spectra of MnO2/BC hybrids: (a) Survey scan spectrum; (b) W 2p core level spectrum; (c) C 1s core level spectrum; (d) O 1s core level spectrum.
Nanomaterials 08 00533 g004
Nanomaterials 08 00533 g005 550
Figure 5. (a) N2 adsorption desorption isotherms and (b) pore size distribution of MnO2/BC hybrids.
Figure 5. (a) N2 adsorption desorption isotherms and (b) pore size distribution of MnO2/BC hybrids.
Nanomaterials 08 00533 g005
Nanomaterials 08 00533 g006 550
Figure 6. (a) The CV curves of BC and MnO2/BC electrodes at a scan rate of 5 mV s−1 in 1 M of Na2SO4, (b) the CV curves of the MnO2/BC electrode at different scan rates, (c) GCD curves of BC and MnO2/BC electrodes at a current density of 1 A g−1, (d) GCD curves of the MnO2/BC electrode at different current densities, (e) specific capacitance of MnO2/BC electrode at different current density, (f) EIS of the BC and MnO2/BC electrode (The inset shows the expanded high-frequency region of Nyquist plots).
Figure 6. (a) The CV curves of BC and MnO2/BC electrodes at a scan rate of 5 mV s−1 in 1 M of Na2SO4, (b) the CV curves of the MnO2/BC electrode at different scan rates, (c) GCD curves of BC and MnO2/BC electrodes at a current density of 1 A g−1, (d) GCD curves of the MnO2/BC electrode at different current densities, (e) specific capacitance of MnO2/BC electrode at different current density, (f) EIS of the BC and MnO2/BC electrode (The inset shows the expanded high-frequency region of Nyquist plots).
Nanomaterials 08 00533 g006
Nanomaterials 08 00533 g007 550
Figure 7. Cycling stability of the MnO2/BC electrode at a current density of 1 A g−1 in 1 M of Na2SO4 electrolyte (the inset shows GCD curves at different cycles).
Figure 7. Cycling stability of the MnO2/BC electrode at a current density of 1 A g−1 in 1 M of Na2SO4 electrolyte (the inset shows GCD curves at different cycles).
Nanomaterials 08 00533 g007
Table
Table 1. Relevant parameters for the pore properties determined by nitrogen adsorption and desorption isotherms of the BC and MnO2/BC hybrids.
Table 1. Relevant parameters for the pore properties determined by nitrogen adsorption and desorption isotherms of the BC and MnO2/BC hybrids.
SampleBET Specific Surface Area/
(m2 g−1)		Average Pore Size/
(nm)		Total Pore Volume/
(cm3 g−1)
BC4143.910.404
MnO2/BC hybrids3233.820.309

Share and Cite

MDPI and ACS Style

Yang, F.; Liu, X.; Mi, R.; Yuan, L.; Yang, X.; Zhong, M.; Fu, Z.; Wang, C.; Tang, Y. A Novel Radiation Method for Preparing MnO2/BC Monolith Hybrids with Outstanding Supercapacitance Performance. Nanomaterials 2018, 8, 533. https://doi.org/10.3390/nano8070533

AMA Style

Yang F, Liu X, Mi R, Yuan L, Yang X, Zhong M, Fu Z, Wang C, Tang Y. A Novel Radiation Method for Preparing MnO2/BC Monolith Hybrids with Outstanding Supercapacitance Performance. Nanomaterials. 2018; 8(7):533. https://doi.org/10.3390/nano8070533

Chicago/Turabian Style

Yang, Fan, Xichuan Liu, Rui Mi, Lei Yuan, Xi Yang, Minglong Zhong, Zhibing Fu, Chaoyang Wang, and Yongjian Tang. 2018. "A Novel Radiation Method for Preparing MnO2/BC Monolith Hybrids with Outstanding Supercapacitance Performance" Nanomaterials 8, no. 7: 533. https://doi.org/10.3390/nano8070533

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop