Next Article in Journal
Manganese Fluorene Phosphonates: Formation of Isolated Chains
Previous Article in Journal
Assembly of ZnO Nanoparticles on SiO2@α-Fe2O3 Nanocomposites for an Efficient Photo-Fenton Reaction
Previous Article in Special Issue
Interface Enthalpy-Entropy Competition in Nanoscale Metal Hydrides
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Editorial

Functional Materials Based on Metal Hydrides

1
Kyushu University Platform of Inter/Transdisciplinary Energy Research, International Research Center for Hydrogen Energy and WPI International Institute for Carbon-Neutral Energy Research, Kyushu University, Fukuoka 819-0395, Japan
2
School of Materials Science and Engineering, Key Laboratory of Advanced Energy Storage Materials of Guangdong Province, South China University of Technology, Guangzhou 510641, China
3
Department of Physics and Astronomy, Faculty of Science & Engineering, Curtin University of Technology, GPO Box U 1987, Perth 6845, WA, Australia
4
Center for Materials Crystallography, Interdisciplinary Nanoscience Center and Department of Chemistry, Aarhus University, DK-8000 Aarhus C, Denmark
*
Author to whom correspondence should be addressed.
Inorganics 2018, 6(3), 91; https://doi.org/10.3390/inorganics6030091
Submission received: 28 August 2018 / Revised: 29 August 2018 / Accepted: 30 August 2018 / Published: 4 September 2018
(This article belongs to the Special Issue Functional Materials Based on Metal Hydrides)

Abstract

:
Storage of renewable energy remains a key obstacle for the implementation of a carbon free energy system. There is an urgent need to develop a variety of energy storage systems with varying performance, covering both long-term/large-scale and high gravimetric and volumetric densities for stationary and mobile applications. Novel materials with extraordinary properties have the potential to form the basis for technological paradigm shifts. Here, we present metal hydrides as a diverse class of materials with fascinating structures, compositions and properties. These materials can potentially form the basis for novel energy storage technologies as batteries and for hydrogen storage.

Our extreme and growing energy consumption, based on fossil fuels, has significantly increased the levels of carbon dioxide, which may lead to irreversible global climate change. The planet has plentiful renewable energy, e.g., sun and wind, but the fluctuations over time and geography call for a range of new ideas, and possibly novel technologies. The most difficult challenge appears to be the development of efficient and reliable storage of renewable energy [1]. Hydrogen has long been considered a potential means of energy storage; however, storage of hydrogen is also challenging [2]. Therefore, a wide range of hydrogen-containing materials with energy-related functions has been discovered over the past few decades [3,4]. The chemistry of hydrogen is diverse, and so also are the new hydrides that have been discovered, not only in terms of structure and composition, but also in terms of their properties [5,6]. This has led to a wide range of possible applications for metal hydrides that permeate beyond solid-state hydrogen storage [7,8,9,10,11]. A variety of new hydrides, proposed as battery materials, have been discovered [3]. Their properties can be exploited as fast ion conductors or as conversion-type electrodes with much higher potential energy capacities compared to materials currently used in commercial batteries [3,7,12]. Solar heat storage is also an area of great potential for metal hydrides, in principle offering orders of magnitude higher energy densities than existing materials [3,13,14,15].
This Special Issue of Inorganics, entitled “Functional Materials Based on Metal Hydrides”, is dedicated to the wide range of emerging energy-related inorganic hydrogen-containing materials. We have collected thirteen publications, which clearly document that metal hydrides are a diverse class of materials with a range of properties, here denoted as “multi-functional materials”. We hope you will enjoy the breadth of science presented in this open-access Special Issue that highlights the many different potential applications of metal hydrides.
An excellent overview of hydride composition and properties is provided by C. Pistidda and co-workers, which also includes important historical landmarks for this class of materials from the past century [16]. In this review, a detailed account of selected aspects of the most relevant complex hydrides is reported. Owing to their high gravimetric hydrogen capacity, tetrahydroborates are extremely appealing for hydrogen storage. However, these materials have some limitations for their use for practical applications, as highlighted in [16], and as also discussed in several research papers in this special issue. The energy density of the reported materials in this special issue are compared in Table 1, which exhibit great potential of hydrides for high capacity energy storage.
An interesting research paper by Chong, Autrey and Jensen investigate one of the most promising hydrogen storage materials, magnesium borohydride, Mg(BH4)2, with a high gravimetric hydrogen density of 14.7 wt % H2 [28]. Their recent research reveals that tetrahydofuran complexes of magnesium borohydride are significantly more prone to release and uptake of hydrogen under more moderate conditions. Hydrogen is released at T < 200 °C via the intermediate Mg(B10H10). These studies reveal new methods to optimize the hydrogen release and uptake reaction through modification of ligand coordination to magnesium [28].
The properties of complex hydrides, such as lithium borohydride, LiBH4, can also be improved creating a reactive hydride composite (RHC) [16] using aluminium, i.e., LiBH4−Al [29]. Here, Carrillo-Bucio, Tena-García and Suárez-Alcántara investigate the dehydrogenation reactions of the mechanochemically treated 2LiBH4−Al composite; also with additives, TiF3 or CeO2 [17]. A reduction in the dehydrogenation temperature and an increase in the reaction kinetics compared to LiBH4 is observed. The dehydrogenation reactions were observed to take place in two main steps, with onsets at 100 °C and 200–300 °C, with a maximum release of 9.3 wt % H2 for 2LiBH4−Al/TiF3 [17]. However, aluminium-based complex hydrides were the first complex hydrides to be successfully catalysed. Nakagawa, Isobe, Ohki and Hashimoto recently investigated new types of additive effects of ball milled lithium alanate with hexagonal boron nitride, LiAlH4h-BN [18]. The role of h-BN on the desorption process of LiAlH4 was discussed in comparison with the desorption properties of LiAlH4X (X = graphite, LiCl or LiI) [18].
The paper by Ouyang, Zhong, Li and Zhu, discuss the use of another additive, namely water, to promote hydrogen production from NaBH4 by hydrolysis [19]. The reaction of NaBH4 and water readily produces hydrogen, but also a stable oxide, NaBO2, as a by-product. The paper discusses the possible regeneration mechanisms of NaBO2 using magnesium [19].
Michael Heere and co-workers present an interesting paper concerning hydrogen release and uptake of a new type of reactive hydride composite based on a rare earth metal borohydride, erbium borohydride, Er(BH4)3, combined with LiBH4 and/or LiH, 3LiBH4−Er(BH4)3−3LiH with a capacity of 9 wt % H2 [20]. Sieverts-type measurements reveal a three-step desorption-absorption cycle with release of 4.2, 3.7 and 3.5 wt % H2 for the first, second and third cycle. This work adds a new example to the growing interest in utilisation of rare earth metals and their unique properties [30,31].
Chaudhary, Dornheim, Orimo and co-workers investigated a transition metal containing a reactive hydride composite (1 − x)LiBH4xMg2FeH6, and measured excellent pressure–composition–isothermal (PCT) data [21]. The results indicate that the same stoichiometric reaction (x = 0.5) occurred in all investigated samples with optimal hydrogen storage and reversibility properties. This is much lower than those required for the partial rehydrogenation of LiBH4. Moreover, the x = 0.5 composite could be reversibly hydrogenated for more than four cycles without degradation of the H2 capacity. The authors conclude that magnesium hydride plays a vital role as an intermediate in the hydrogen release and uptake reactions [21].
Magnesium hydride remains highly relevant as a hydrogen storage material, and has been investigated in great detail previously [32,33]. Priscilla Huen, Mark Paskevicius, Dorthe B. Ravnsbæk and co-workers investigated the direct synthesis of nano-particulate MgH2 in a nanoporous carbon scaffold [22]. A solvent-based approach using dibutyl magnesium, MgBu2, infiltrated into four different carbon aerogels with different porosities is investigated. Three independent infiltrations of MgBu2, each with three individual hydrogenations, are conducted for each scaffold. Systematic experimental work shows that butane is release over many cycles, inferring that the dibutyl magnesium precursor is not completely reduced. The large difference in molar volume of MgH2 and MgBu2 is highlighted as a drawback for this approach [22].
Nano-particles are known to have different properties as compared to the bulk state, and this can also be used to improve metal hydride properties, including hydrogen storage [34]. Lei Wang and Kondo-Francois Aguey-Zinsou report on a novel approach to produce nanoscale LiAlH4 via a bottom-up synthesis [24]. Upon further coating of these nanoparticles with Ti, the composite nanomaterial was found to decompose at 120 °C in one single and extremely sharp exothermic event with instant hydrogen release. This finding implies a significant thermodynamic alteration of the hydrogen properties of LiAlH4 induced by the synergetic effects of the Ti catalytic coating and nanosizing effects [24].
Nicola Patelli, Marco Calizzi, and Luca Pasquini analysed the effect of the interfacial free energy on the thermodynamics of hydrogen sorption in nano-scaled materials [23]. When the enthalpy and entropy terms are the same for all interfaces, as in an isotropic bi-phasic system, a compensation temperature is obtained, which does not depend on the system size nor on the relative phase abundance. They also consider the possible effect of elastic strains on the stability of the hydride phase and on hysteresis. They compare a simple model with experimental data obtained on two different systems: (1) bi-phasic nanocomposites where ultrafine TiH2 crystallite are dispersed within a Mg nanoparticle and (2) Mg nanodots encapsulated by different phases [23].
Most frequently, nano-materials for hydrogen storage are produced by mechano-chemistry [35]. However, Sleiman and Huot [25] investigated the effect of arc melting Ti1V0.9Cr1.1 with zirconium additives on the microstructure and hydrogen storage properties of main BCC alloy and secondary Laves phase alloys C15 and C14. Small amounts of Zr produced fast kinetics and high hydrogen storage capacity [25].
Metal hydrides have been receiving increasing interest as battery materials, both as electrodes and ion conductors [3,5,12]. This is clearly demonstrated by Yang, Wang, Ouyang, Liu and Zhu [26] who prepared MgH2-based composites with expanded graphite (EG) and TiO2 by a plasma-assisted milling process as composite electrodes. A stable discharge capacity of 305.5 mAh/g could be achieved after 100 cycles for the 20 h-milled MgH2–TiO2–EG-20 h composite electrode and the reversibility of the conversion reaction of MgH2 could be greatly enhanced. This improvement in cyclic performance is attributed mainly to the composite microstructure by the specific plasma-assisted milling process, and the additives TiO2 and graphite that could effectively ease the volume change during the de-/lithiation process, as well as inhibit the particle agglomeration [26].
Weeks, Tinkey, Ward, Lascola, Zidan, and Teprovich [27] analyse and compare the physical and electrochemical properties of an all solid-state cell utilizing LiBH4 as the electrolyte and aluminium as the active anode material. An initial capacity of 895 mAh/g was observed and is close to the theoretical capacity of aluminium due to the formation of a LiAl (1:1) alloy. This work is the first example of reversible lithiation of aluminium in a solid-state cell and further emphasizes the robust nature of the LiBH4 electrolyte. This demonstrates the possibility of utilising other high-capacity anode materials with a LiBH4-based solid electrolyte in all-solid-state batteries [27].
We hope you will enjoy the breadth of science offered in this open-access Special Issue of Inorganics, now organised as a book. Many current frontier research challenges are discussed in the included articles. We hope this unique collection of science can create inspiration for the design and synthesis of other novel “energy-materials”. This research field emphatically contributes towards a cleaner and carbon-free future.

References

  1. Møller, K.T.; Jensen, T.R.; Akiba, E.; Li, H.-W. Hydrogen—A sustainable energy carrier. Prog. Nat. Sci. Mater. 2017, 27, 34–40. [Google Scholar] [CrossRef]
  2. Ley, M.; Jepsen, L.; Lee, Y.-S.; Cho, Y.; Colbe, J.; Dornheim, M.; Rokni, M.; Jensen, J.; Sloth, M.; Filinchuk, Y.; et al. Complex hydrides for hydrogen storage—New perspectives. Mater. Today 2014, 17, 122–128. [Google Scholar] [CrossRef] [Green Version]
  3. Møller, K.T.; Sheppard, D.; Ravnsbæk, D.; Buckley, C.; Akiba, E.; Li, H.-W.; Jensen, T.R. Complex metal hydrides for hydrogen, thermal and electrochemical energy storage. Energies 2017, 10, 1645. [Google Scholar] [CrossRef]
  4. Yu, X.; Tang, Z.; Sun, D.; Ouyang, L.; Zhu, M. Recent advances and remaining challenges of nanostructured materials for hydrogen storage applications. Prog. Mater. Sci. 2017, 88, 1–48. [Google Scholar] [CrossRef]
  5. Paskevicius, M.; Jepsen, L.; Schouwink, P.; Ĉerný, R.; Ravnsbæk, D.; Filinchuk, Y.; Dornheim, M.; Besenbacher, F.; Jensen, T.R. Metal Borohydrides and derivatives—Synthesis, structure and properties. Chem. Soc. Rev. 2017, 46, 1565–1634. [Google Scholar] [CrossRef] [PubMed]
  6. Jepsen, L.; Ley, M.; Lee, Y.; Cho, Y.; Dornheim, M.; Jensen, J.; Filinchuk, Y.; Jørgensen, J.; Besenbacher, F.; Jensen, T.R. Boron-nitrogen based hydrides and reactive composites for hydrogen storage. Mater. Today 2014, 17, 129–135. [Google Scholar] [CrossRef] [Green Version]
  7. Paskevicius, M.; Hansen, B.; Jørgensen, M.; Richter, B.; Jensen, T.R. Multifunctionality of silver closo-boranes. Nat. Commun. 2017, 8, 15136. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  8. Payandeh GharibDoust, S.; Dorthe, B.; Černý, R.; Jensen, T.R. Synthesis, structure and properties of bimetallic sodium rare earth (RE) borohydrides, NaRE(BH4)4, RE = Ce, Pr, Er or Gd. Dalton Trans. 2017, 46, 13421–13431. [Google Scholar] [CrossRef] [PubMed]
  9. Schouwink, P.; Ley, M.; Tissot, A.; Hagemann, H.; Jensen, T.R.; Smrčok, L.; Černý, R. Structure and properties of complex hydride perovskite material. Nat. Commun. 2014, 5, 5706. [Google Scholar] [CrossRef] [PubMed]
  10. Paskevicius, M.; Ley, M.; Sheppard, D.; Jensen, T.R.; Buckley, C. Eutectic melting in metal borohydrides. Phys. Chem. Chem. Phys. 2013, 15, 19774–19789. [Google Scholar] [CrossRef] [PubMed]
  11. He, L.; Li, H.-W.; Nakajima, H.; Tumanov, N.; Filinchuk, Y.; Hwang, S.-J.; Sharma, M.; Hagemann, H.; Akiba, E. Synthesis of a bimetallic dodecaborate LiNaB12H12 with outstanding superionic conductivity. Chem. Mater. 2015, 27, 5483–5486. [Google Scholar] [CrossRef]
  12. Hansen, B.; Paskevicius, M.; Li, H.-W.; Akiba, E.; Jensen, T.R. Metal boranes: Progress and applications. Coord. Chem. Rev. 2016, 323, 60–70. [Google Scholar] [CrossRef]
  13. Harries, D.; Paskevicius, M.; Sheppard, D.A.; Price, T.; Buckley, C.E. Concentrating solar thermal heat storage using metal hydrides. Proc. IEEE 2012, 100, 539–549. [Google Scholar] [CrossRef]
  14. Sheppard, D.A.; Paskevicius, M.; Humphries, T.D.; Felderhoff, M.; Capurso, G.; Bellosta von Colbe, J.; Dornheim, M.; Klassen, T.; Ward, P.A.; Teprovich, J.A., Jr.; et al. Metal hydrides for concentrating solar-thermal power energy storage. Appl. Phys. A 2016, 122, 1–15. [Google Scholar] [CrossRef]
  15. Javadian, P.; Sheppard, D.; Jensen, T.R.; Buckley, C. Destabilization of lithium hydride and the thermodynamic assessment of the Li–Al–H system for solar thermal energy storage. RSC Adv. 2016, 6, 94927–94933. [Google Scholar] [CrossRef]
  16. Puszkiel, J.; Garroni, S.; Milanese, C.; Gennari, F.; Klassen, T.; Dornheim, M.; Pistidda, C. Tetra- hydroborates: Development and potential as hydrogen storage medium. Inorganics 2017, 5, 74. [Google Scholar] [CrossRef]
  17. Carrillo-Bucio, J.; Tena-García, J.; Suárez-Alcántara, K. Dehydrogenation of surface-oxidized mixtures of 2LiBH4 + Al/Additives (TiF3 or CeO2). Inorganics 2017, 5, 82. [Google Scholar] [CrossRef]
  18. Nakagawa, Y.; Isobe, S.; Ohki, T.; Hashimoto, N. Unique hydrogen desorption properties of LiAlH4/h-BN composites. Inorganics 2017, 5, 71. [Google Scholar] [CrossRef]
  19. Ouyang, L.; Zhong, H.; Li, H.-W.; Zhu, M. A recycling hydrogen supply system of NaBH4 based on a facile regeneration process: A review. Inorganics 2018, 6, 10. [Google Scholar] [CrossRef]
  20. Heere, M.; GharibDoust, S.; Brighi, M.; Frommen, C.; Sørby, M.; Černý, R.; Jensen, T.; Hauback, B. Hydrogen sorption in erbium borohydride composite mixtures with LiBH4 and/or LiH. Inorganics 2017, 5, 31. [Google Scholar] [CrossRef]
  21. Li, G.; Matsuo, M.; Takagi, S.; Chaudhary, A.-L.; Sato, T.; Dornheim, M.; Orimo, S. Thermodynamic properties and reversible hydrogenation of LiBH4–Mg2FeH6 composite materials. Inorganics 2017, 5, 81. [Google Scholar] [CrossRef]
  22. Huen, P.; Paskevicius, M.; Richter, B.; Ravnsbæk, D.; Jensen, T.R. Hydrogen storage stability of nanoconfined MgH2 upon cycling. Inorganics 2017, 5, 57. [Google Scholar] [CrossRef]
  23. Patelli, N.; Calizzi, M.; Pasquini, L. Interface enthalpy-entropy competition in nanoscale metal hydrides. Inorganics 2018, 6, 13. [Google Scholar] [CrossRef]
  24. Wang, L.; Aguey-Zinsou, K.-F. Synthesis of LiAlH4 nanoparticles leading to a single hydrogen release step upon Ti coating. Inorganics 2017, 5, 38. [Google Scholar] [CrossRef]
  25. Sleiman, S.; Huot, J. Microstructure and hydrogen storage properties of Ti1V0.9Cr1.1 alloy with addition of x wt % Zr (x = 0, 2, 4, 8, and 12). Inorganics 2017, 5, 86. [Google Scholar] [CrossRef]
  26. Yang, S.; Wang, H.; Ouyang, L.; Liu, J.; Zhu, M. Improvement in the electrochemical lithium storage performance of MgH2. Inorganics 2018, 6, 2. [Google Scholar] [CrossRef]
  27. Weeks, J.A.; Tinkey, S.C.; Ward, P.A.; Lascola, R.; Zidan, R.; Teprovich, J.A. Investigation of the reversible lithiation of an oxide free aluminum anode by a LiBH4 solid state electrolyte. Inorganics 2017, 5, 83. [Google Scholar] [CrossRef]
  28. Chong, M.; Autrey, T.; Jensen, C. Lewis base complexes of magnesium borohydride: Enhanced kinetics and product selectivity upon hydrogen release. Inorganics 2017, 5, 89. [Google Scholar] [CrossRef]
  29. Hansen, B.; Ravnsbæk, D.; Reed, D.; Book, D.; Gundlach, C.; Skibsted, J.; Jensen, T. Hydrogen storage capacity loss in a LiBH4–Al composite. J. Phys. Chem. C 2013, 117, 7423–7432. [Google Scholar] [CrossRef]
  30. Frommen, C.; Sørby, M.; Heere, M.; Humphries, T.; Olsen, J.; Hauback, B. Rare earth borohydrides-crystal structures and thermal properties. Energies 2017, 10, 2115. [Google Scholar] [CrossRef]
  31. Mansell, S.; Liddle, S. Rare earth and actinide complexes. Inorganics 2016, 4, 31. [Google Scholar] [CrossRef]
  32. Crivello, J.-C.; Denys, R.V.; Dornheim, M.; Felderhoff, M.; Grant, D.M.; Huot, J.; Jensen, T.R.; Jongh, P.; Latroche, M.; Walker, G.S.; et al. Mg-based compounds for hydrogen and energy storage. Appl. Phys. A 2016, 122, 85. [Google Scholar] [CrossRef]
  33. Crivello, J.-C.; Dam, B.; Denys, R.V.; Dornheim, M.; Grant, D.M.; Huot, J.; Jensen, T.R.; Jongh, P.; Latroche, M.; Milanese, C.; et al. Review of magnesium hydride based materials: Development and optimisation. Appl. Phys. A 2016, 122, 97. [Google Scholar] [CrossRef]
  34. Nielsen, T.; Besenbacher, F.; Jensen, T. Nanoconfined hydrides for energy storage. Nanoscale 2011, 3, 2086–2098. [Google Scholar] [CrossRef] [PubMed]
  35. Huot, J.; Ravnsbæk, D.B.; Zhang, J.; Cuevas, F.; Latroche, M.; Jensen, T.R. Mechanochemical synthesis of hydrogen storage materials. Prog. Mater. Sci. 2013, 58, 30–75. [Google Scholar] [CrossRef]
Table 1. Comparison of volumetric and gravimetric energy density in various materials.
Table 1. Comparison of volumetric and gravimetric energy density in various materials.
MaterialsAvailable Gravimetric Hydrogen Density
(wt %)
Available Volumetric Hydrogen Density
(g/L)
Gravimetric Energy Density (kWh/kg) *Volumetric Energy Density (kWh/L) *Ref.
Gaseous H2 (70 MPa)5.740391.6[1]
2LiBH4−MgH211.8965.53.1[5]
2LiBH4−Al/TiF39.31253.62.4 [17]
LiAlH4h-BN7.7713.02.8 [18]
NaBH410.81124.24.3 [19]
3LiBH4−Er(BH4)3−3LiH9.01473.52.3 [20]
LiBH4−Mg2FeH66.01512.34.1 [21]
MgH27.61103.04.4 [22,23]
LiAlH47.9733.12.9 [24]
Ti1V0.9Cr1.1/4 wt %Zr3.52101.44.3 [25]
MgH2–TiO2–EGNoneNone0.05 **0.07 **[26]
Al anode/LiBH4 electrolyteNoneNone0.3 **0.8 **[27]
* The energy density was calculated based on 140.4 MJ/kg H2 at standard condition; ** The energy density was calculated only based on the weight of active materials of electrodes without consideration of the total weight of cell.

Share and Cite

MDPI and ACS Style

Li, H.-W.; Zhu, M.; Buckley, C.; Jensen, T.R. Functional Materials Based on Metal Hydrides. Inorganics 2018, 6, 91. https://doi.org/10.3390/inorganics6030091

AMA Style

Li H-W, Zhu M, Buckley C, Jensen TR. Functional Materials Based on Metal Hydrides. Inorganics. 2018; 6(3):91. https://doi.org/10.3390/inorganics6030091

Chicago/Turabian Style

Li, Hai-Wen, Min Zhu, Craig Buckley, and Torben R. Jensen. 2018. "Functional Materials Based on Metal Hydrides" Inorganics 6, no. 3: 91. https://doi.org/10.3390/inorganics6030091

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.