3.1. Electroplating Using Printed Gels
A single noble metal was first electroplated using printed gels. For this purpose, a base electrode made of copper polyimide foil 20 mm in length and 50 mm wide was fabricated using a xurography lamination technique. After that, nickel was coated on the electrode through electroplating. A mask patterned with xurography and consisting of holes with a 1.5-mm radius was laminated on the substrate. Next, a micropipette was used to print 10-µL droplets of gold electrolytes mixed on the electrode. The deposited droplets automatically self-aligned themselves to the patterned circular holes due to surface tension. The sequence of substrate preparation, including the initial copper foil, nickel-coating, mask lamination, and dispensing of the gels (gels were added with blue dye for visualization), is shown in
Figure 2a. Next, an external direct current (DC) power supply was connected to the substrate. The substrate was immersed into a common working electrolyte container and electrodeposited.
Figure 2b shows a microscope image of the electrodeposited layers of gold on nickel. Silver was electroplated using printed gel by carrying out the same experiment, but with silver plating salts mixed with the agarose.
Figure 2c shows the electroplated layers of silver.
The microscope images of electroplated layers demonstrate that the gold and silver layers were precisely and uniformly deposited on the base electrode. This shows that the gel material did not interfere with the electroplating process. The gel was easily washed away from the surface through purging with water, leaving behind a pristine plated surface. Additionally, since the gel functioned as a limiting environment for the transportation of ions, mass transfer was only restricted to diffusion, which is a crucial factor in this electrodeposition process. As a result, a current density of about 30 mA dm
−2 (4–8 min) was found to be suitable for the electrodeposition of gold and silver layers. This amount of current density produced uniformly bright surfaces. In contrast, increasing or reducing the current density caused black surfaces and nonuniform surfaces. The black deposits (at higher current densities) could have been due to dendritic growth, which leads to a non-smooth surface finish and consequently a dark color [
25]. Subsequently, a range of 600–700 mv of DC voltage between the cathode and anode was the most appropriate potential value in producing a suitable current density for the deposition of gold and silver layers. The thicknesses of the layers formed were extremely thin (a few 100 nm) due to the short duration of the electroplating and the low applied current density. The morphology of the layer formed was found to be similar to that of the underlying Cu substrate, which had the same topography. Therefore, the process produced smooth deposits similar to those made using other electroplating methods.
In order to demonstrate the formation of conformal deposits using the electroplating method and printed gels, images from layers of Cu, Ni, Au, and Ag were obtained through scanning electron microscopy (SEM). The SEM images were obtained using a TESCAN VP system, and the accelerating voltage was set at 30 kV.
Figure 2d shows lowly and highly magnified (as insets) images of layers of Cu, Ni, Au, and Ag from left to right. The low-magnification SEM images show uniform and well-defined coverage of the electrode by the Ag- and Au-deposited layers. The speckle features that are visible were due to the roughness of the starting Cu substrate. The SEM images presented in the high-magnification images demonstrate that the initial surface roughness of the original Cu substrate was around one to five microns. After the deposition of the layers of Ni, Au, or Ag, the surface roughness did not change, indicating a uniform and conformal plating of the functional material over the underlying nickel base layer.
3.2. Parallel Electroplating of Silver and Gold
A base electrode layer made of copper polyimide foil 14 mm in length and 35 mm wide was prepared using a xurography lamination technique, as described in the experimental section. After that, nickel was coated in the base electrode through electroplating. Then, a covering layer (mask) consisting of two holes with a 1-mm radius and 7 mm apart (center to center) was laminated on the electrode. Next, a gel mixture of gold electrolytes in the amount of 10 µL was printed on one of the holes. Accordingly, the same amount of silver electrolytes mixed with gel were printed on the other hole. After that, the electrode was placed in a common working electrolyte container. Electrodeposition was performed, and layers of gold and silver were deposited on the base electrode in parallel.
In order to investigate the elemental composition of the electrodeposited layers, X-ray photoelectron spectroscopy (PHI Qanutera II) was performed to comprehensively analyze the surface of the electrodeposited layers.
Figure 3 shows the XPS spectra of the samples. The spectra show that silver and gold peaks were observed only in the regions that were electroplated. Therefore, electroplating by gel printing enabled the simultaneous deposition of gold and silver on the confined region without any cross-deposition. Cross-deposition was avoided by using gel as an immobilizing environment, which eliminated convective mass transport and limited transport by diffusion. Additionally, a 7-mm distance (center to center) between the two holes with a radius of 1 mm was found to be the smallest pitch size, without any cross-deposition. It is worth mentioning that holes with a radius of 1 mm were designed, as they were the minimum suitable size for elemental analysis in XPS. Designing smaller size holes (0.5 mm in radius) to place smaller droplets may reduce that distance (5 mm center to center). However, the gradual diffusion of metal ions from the gel droplets into the surrounding space can limit the ability to bring these features closer to each other. The diffusion of ions in one dimension in aqueous solution can be modeled in a simplified form [
28]:
where
L is diffusion length,
D is the diffusion coefficient of solute, and
t is time. Since the diffusion coefficient of metal ions in aqueous solution is on the order of 10
−9 m
2 s
−1, the ions travel about 1 mm in 5 min. It can be concluded that the diffusion of ions is a determinant for defining the minimum distance between two droplets containing different metal electrolytes. An alternate approach, such as introducing convection between the gel droplets to carry away the ions diffusing out and diluting them in the larger supporting electrolyte, can be used to mitigate the diffusional effect but still achieve closer spacing.
3.3. Pattern Electroplating: An Array of Dots
In order to demonstrate the scalability of the technique in electroplating metals in parallel, a mask consisting of circular patterns with a radius of 500 µm placed 5 mm apart (center to center) and forming an array of 14 × 4 was fabricated using xurography. The mask was laminated on a nickel-coated copper foil with dimensions of 70 mm (L) and 45 mm (W). Further, 2-µL droplets of gel containing gold and silver electrolytes were dispensed onto alternate circular holes (patterns) on the substrate by a micropipette, and electroplating was performed as described above. After electroplating, the mask was peeled off.
Figure 4a shows parallel electrodeposited layers of gold and silver on a nickel-coated substrate. In addition, a magnified image of the array is shown in
Figure 4b. The microscopic images of individual circles show that layers of Ag and Au were deposited only in confined regions defined by the prepared mask (
Figure 4c,d).
This result demonstrates that gel printing can be used as a comprehensive method to fabricate an electrode that is fundamentally different from conventional electroplating approaches. Conventional methods of electroplating require a set of processes that include coating and the removal of a mask that is time-consuming and expensive when multiple materials are to be electroplated. In addition, the substrate needs to be immersed in a large volume of electrolytes which is suitable for large scale production, but expensive when fabricating small-area prototype electrodes. On the other hand, electroplating with gels eliminates the need for mask coating/removal, since gel has the ability to immobilize the electrolyte solution and can be used as a direct patterning technique. This ability becomes more important when multiple materials need to be electroplated. The method of gel deposition used here was manual. However, it can be easily automated by incorporating inkjet or drop printers in order to deposit smaller volumes of gel loaded with electroplating solutions with much closer spacing. Although a xurographic patterned layer was used as a mask on the substrate, this step can also be eliminated by inkjet-printing a thin layer of insulating material as a covering layer alongside the printed electrolytes.
3.4. Pattern Electroplating: Lines
In order to demonstrate the ability of the gel-printing method to simultaneously electrodeposit Ag and Au in a variety of structures, masks patterned by xurography in the shape of a microfluidic channel with a width of 1 mm were used. For this purpose, thicker masks were required to carry a larger amount of plating solution uniformly across the open microfluidic channels. Therefore, masks made of polyvinyl chloride (PVC) (McMaster Carr, Elmhurst, IL, USA) with a 476-µm thickness (laminated on double-sided adhesive tape (7952, 3M™) with a 50-µm thickness) were used.
In order to perform the experiment, a copper foil with the dimensions 30 mm (L) and 45 mm (W) was cut and coated with nickel, as described above. Then, the substrate was laminated on the prepared mask. A hot plate (VWR, Radnor, PA, USA) was used to keep the temperature of the substrate at 70 °C to prevent the gelation of the solution while the structures were filled. Between 20 and 30 µL of gel-plating solution of gold and silver were placed at the beginning of each channel, and using capillary forces, the plating solution was wicked into the open microchannels automatically (
Figure 5a). Then the substrate was placed in a common working electrolyte bath, and electroplating was performed as described above. After electroplating, the mask was peeled off from the substrate.
Figure 5b shows electrodeposited layers of Ag and Au on nickel-coated substrates. As can be seen, the edges of the electrodeposited layers were well-defined compared to the nickel-coated layer (
Figure 5c). Therefore, using microfluidic flow, gel solutions were patterned, and parallel electroplating of silver and gold was performed. Additionally, the use of capillary wicking eliminated the manual dispensing of gels over entire patterns, which facilitated the printing process. However, for longer distance patterns, capillary flow slows down toward the end of the pattern. In that case, modifying the channel design, such as using slightly conical shape channels or placing a temporary sealing layer on top of the open channel, will enhance the capillary pumping [
29,
30].
3.5. Electrochemical Sensing
Electrochemical sensors have gained increasing attention for chemical [
5] and biochemical analyses [
31] in microfluidics. These methods are highly sensitive and selective, and they use a very small amount of electrical power. These significant characteristics have made electrochemical sensing an ideal choice for miniaturization. However, the conventional fabrication techniques for electrochemical microfluidic sensors are complicated and tedious. In addition, they require a cleanroom and high-cost facilities.
A microfluidic device consisting of an electrochemical sensor and a microchannel was fabricated to demonstrate the capability of the developed technique in the fabrication of high-quality electrodes. In this device, an array of three electrodes that were 2.5 mm wide and 20 mm in length with a gap size of 20 mm was fabricated from copper polyimide film using xurography. The electrodes, including working, counter-, and reference electrodes, were initially coated with nickel, as described above. Next, a layer made of one-sided adhesive tape (9795MP-3M™) consisting of three 1-mm (radius) holes was laminated on the electrodes. These holes defined the contact area between the electrodes and the analyte flow. Next, gel droplets of electrolytes of gold and silver were printed on the side electrodes and on the middle one, respectively. After that, electrodeposition was applied as described in the experimental section.
After that, a layer of double-sided adhesive tape (90176, Adhesive Research, Glen Rock, PA, USA) consisting of a microfluidic channel that was 2 mm wide, 20 mm long, and 89 µm in height was added. Finally, a layer of hydrophilic polyester film (9984, 3M™) was laminated on the device. This layer consisted of a circular inlet and outlet of the liquid channel with a radius of 1 mm (
Figure 6a). This layer automatically wicked the microchannel using capillary forces that eliminated the need for any equipment for the sample injection. After assembly, 20 µL of 1-M potassium chloride (Caledon Laboratories Ltd., Georgetown, ON, Canada) was injected at the inlet of the microchannel. The solution filled the channel automatically due to the hydrophilic nature of the channel. After that, 2 V of DC as an anode was applied for 30 s to the silver electrode to change its surface into silver chloride. Therefore, an electrochemical microfluidic sensor consisting of a three-electrode system, including a silver/silver chloride reference electrode, a gold working electrode, and a counterelectrode, was fabricated (
Figure 6c).
In addition, 20 µL of 100-mM potassium hexacyanoferrate (Sigma-Aldrich, St. Louis, MO, USA) was injected at the inlet of the microfluidic device. Due to the hydrophilicity of the microchannel, the sample filled the microchannel automatically without the need for any excess action. After that, a potentiostat (EmStat2, PalmSense, Houten, The Netherlands) was used to apply cyclic voltammetry (CV) to the sample. Different scan rates were selected, and data were acquired accordingly (
Figure 6b). The results revealed that the current at the cathodic and anodic peaks of the ferricyanide/ferrocyanide redox couple was proportional to the scan rate.
The parallel electroplating technique combined with the xurography lamination technique implemented the integration of high-quality electrode sensors into a microfluidic device in a fast and facile way. The entire process, including cutting the electrodes and layers, gel printing, electrodeposition, and lamination, was performed in less than 30 min. This time is significantly lower than that required by standard microfluidic sensor fabrication techniques, which need multiple sequential steps to deposit and remove each material. In addition, the gel-printing method enabled us to electrodeposit silver and gold simultaneously in a single process on a single layer. Automatic filling of the device using a hydrophilic film made this sensor suitable for end users. Further, the small amount of electroplating solution and the small number of copper and plastic films and facilities used in this approach make the entire process inexpensive and suitable for commercialization.