1. Introduction
Short fiber has been widely used to reinforce rubber composites of rubber products, such as tires, conveyor belts and seal [
1,
2,
3,
4]. The short fiber addition could generally improve the comprehensive performance of rubber composite, such as hardness, modulus, corrosion resistance, compressibility, and wear resistance. To achieve the best performance of those rubber products, some factors, such as sufficient interaction between fiber and the matrix, sufficient dispersion of fibers, high aspect ratio during processing, and desired orientation in the desired direction [
5], have to be carefully considered [
1].
Because the molecular structure, reactivity, and surface properties of the short fiber and rubber matrix are different, the adhesion between them [
6,
7,
8] is difficult and it has been the primary factor in the preparation of short fiber reinforced rubber composite [
9,
10]. Many methods were found to improve the interaction between fiber and rubber for these differences. The bonding reaction between the rubber and the fiber was mainly carried out by a chemical method, thereby enhancing the adhesion between the short fibers and the rubber molecules [
11]. This is a common method to enhance the adhesion behavior between rubber and short fiber interface by chemical modification [
12]. These methods are very effective and have been widely used.
The processing of short fiber reinforced rubber composite is significantly important, which may receive a better dispersion of fibers, a high aspect ratio during processing and controlling the orientation in the desired direction for application [
13]. There have been many researches on the processing technology of short fiber rubber composite [
14,
15,
16,
17,
18]. Hintze et al. [
1] studied the influence of different processing conditions and fiber contents on the resulting morphology and macroscopic properties. Lekube et al. [
19] investigated the influence of processing temperature and screw configuration in compounding on the properties of glass fiber reinforced polypropylene. In previous work [
20,
21,
22], the mixing methods of short fiber rubber composite and extrusion process with a radial orientation of short fiber in a rubber matrix have been researched. Some equipment and the process technology have been produced, as shown in
Figure 1. However, there are some problems in the extrusion process of using short fiber radial orientation to reinforce rubber composites. The Mooney viscosity of those composite material increases [
23], which causes many unfavorable factors in the extrusion process of the product, such as the increase of extrusion pressure, increase of extrusion temperature, and unstable extrusion quality. These phenomena are even more serious when short fibers orient in the radial direction during extrusion molding.
In order to solve the above-mentioned problems, a gear pump has been applied in the extrusion molding process for short fiber reinforced rubber composite. The gear pump could convey positive displacement, to improve the extrusion stability of the product. Meanwhile, the pressure building function of the extruder can be transferred to the gear pump to reduce the temperature of the rubber composite during extrusion and thus the pumping capacity of the extruder equivalent is improved. In this paper, the melt gear pump auxiliary device was used in conjunction with the extruder to study the processing difficulty and performance of the short fiber reinforced rubber composite at different speeds.
2. Materials and Methods
2.1. Materials
Table 1 shows the different components of the rubber composite formulation. Natural Rubber (NR) SVR3L was bought from Dakruko, Buon Ma Thuot, Vietnam. Carbon blacks N330 was obtained from Jiangxi Black Cat Carbon Black Co., Ltd., Jiangxi, China. Silica HD 115 MP, was obtained from Rhodia White Carbon (Qingdao, China) Co., Ltd. ZnO was bought from Hebei Shijiazhuang Zinc Oxide Factory, Shijiazhuang, China. The oil types added to the NR compounds were VIVATEC500 naphthenic oil from Hansen & Rosenthal Chemical Group, Hamburg, Germany. Anti-aging agent 4020 (
N-(1,3-dimethylbutyl)-
N0-phenyl-
p-phenylenediamine) and Accelerator NS were bought from Shandong shangshun Chemical Co., Ltd., Weifang, China. Stearic acid was bought from Fengyi Grease Technology (Tianjin, China) Co., Ltd. Sulphur was bought from Chaoyang Tianming Industry and Trade Co., Ltd., Beijing, China. Coupling agent Si-69 was supplied by Shandong Ningjin haorun Technology Co., Ltd., Dezhou, China. Resin SL3020(1,3-Dihydroxybenzene), was supplied by Sino Legend (China) Chemical Company Ltd., Suzhou, China. Adhesive RA65, was supplied by Wuxi Huasheng Rubber New Material Technology Co., Ltd., Wuxi, China. Aramid short fibers were supplied by Baoding New Urban Synthetic Material Factory (Baoding, China), with an average initial length of 3 mm and fiber diameter of 10–12 microns.
2.2. Adhesion Mechanism of Short Fiber to Rubber Matrix
Adhesion between short fiber and rubber matrix is the key to ensure the properties of composite materials. The adhesive system, as an active intermediate, participates in the adhesion process between short fiber and rubber matrix [
24,
25]. The specific adhesion mechanism is shown in
Figure 2.
The adhesive system is uniformly dispersed in the rubber matrix after mixing, the chemical components in the adhesive system react first to form active substances in the process of vulcanization, which can react with rubber and short fiber.
Figure 3 describes the chemical reaction process. The active intermediate substances then undergo two important reactions, the first reaction is to form a chemical crosslink with rubber matrix, and the other reaction is to form a hydrogen bond with the short fiber, so as to realize the bonding between short fiber and rubber matrix.
Figure 4 depicts the entire adhesion process.
2.3. Processing Methods
The processing of rubber composites mainly consists of three steps. The first step is the mixing process of rubber composites, which mainly aims to realize the uniform dispersion of materials such as short fibers in the rubber matrix. The second step is the extrusion of rubber composites. In this step, the properties of short fiber rubber composites are investigated in the process of gear pump assisted extrusion. This step is the main content of this study. The third step is the vulcanization of composite materials.
2.3.1. Mixing Process
The mixing process of short fiber rubber composite includes a two-step mixing process of internal mixing and open mixer mixing. In the first stage, the fiber, rubber and most materials were incorporated on a laboratory internal mixing X(S)M-1.7L. In the second stage, Sulphur (resin, and adhesive) was added into the two-roll mill XK-160. The mixing parameters and mixing processing were listed in
Table 2.
2.3.2. Extrusion Process
In order to study the effect of gear pump processing on the properties of short fiber reinforced rubber composites, Herringbone gear pump (Hatec, Germany) and orientation die (manufactured by Qingdao University of Science and Technology,
Figure 5b) were installed on the extruder in sequence. The general orientation of the fiber extrusion process was along the extrusion direction (x-direction), orientation die could implement the short fiber radial orientation(y-direction).
Figure 5 shows the short-fiber radial orientation direction and the detailed structure of orientation equipment.
The mixing rubber was added into extruder XJD-65, manufactured by Inner Mongolia Ford Rubber Machinery Company. The extruder cooling water temperature is 70 °C. Gear pump cooling water temperature is 40 °C. Gear pump speed is 25 rpm.
Table 3 shows the extrusion experimental design.
2.3.3. Vulcanization Process
The orientation direction must be considered during the vulcanization process. The testing specimen is the fiber orientation direction, as illustrated in
Figure 6. The rubber compounds were cured at 150 °C at a pressure of 10 MPa for optimum cure time (t90) + 3 min.
2.4. Characterization
Extrusion stability: The cutter is installed in front of the extruder head, and the cutter speed is 6 rpm. When the rubber composites were continuously extruded from the extruder, the cutter was started and the running time was 3 min. The collected rubber compound was weighed to test the extrusion stability of the rubber compound.
Degree of compaction: The degree of compaction of the rubber compound after extrusion was observed using an optical microscope (LEXT OLS4000, OLYMPUS). The specimen was sliced in the extrusion direction after cooling the extruded rubber mixture to room temperature.
Curing Characterization: Curing characterization of rubber compounds were evaluated using a moving-die rheometer (M-2000-AN) from GOTECH TESTING MACHINES CO., Ltd., Taichung City, Taiwan. The specimens were tested according to ISO 6502-2:2018. The Mooney viscosity values of the rubber compounds were evaluated using a Mooney viscometer (UM-2050, GOTECH TESTING MACHINES CO., Ltd.) according to ISO 289-2:2016.
Physical and Mechanical Properties. The hardness of the rubber vulcanizate was evaluated using Shore Hardmeter (LX-A, Shanghai Liuling Instrument Factory) according to ISO 7619-2: 2004, and three points were measured for each sample and the final result selected the median [
6]. The tensile and tear properties of the vulcanized rubber were tested using a universal testing machine (TS 2005 b, GOTECH TESTING MACHINES CO., Ltd.) at a drawing rate of 500 mm/min according to the standards ISO 37: 2005 and ISO 34-1: 2004, respectively [
6]. Five specimens were tested for each sample type and the final result selected the median. The abrasion of the rubber vulcanizates were evaluated using a DIN wear machine (GT-2012-D, GOTECH TESTING MACHINES CO., Ltd.) according to GB/T 1689-1998, and three specimens were tested and the final result selected the median.
Dynamic Mechanical Thermal Analysis: The viscoelastic mechanical properties of the vulcanizates were evaluated using dynamic thermomechanical analysis (EPLEXOR-150N, Gabo Qualimeter Testanlagen GmbH). The test temperature range is from −65 °C to 65 °C in tensile mode at a heating rate of 2K per minute. The frequency is 10 Hz. The static strain is 5%. The static force is 70 N. The dynamic strain is 0.25%. The dynamic stress is 60 N.
Morphology Analysis. The cross section of the sample after tensile fracture was observed under a scanning electron microscope (JSM-7500F, Japan Electronics Corporation).
3. Results and Discussion
3.1. The Pressure and Temperature of the Rubber Compound during Extrusion
Extrusion temperature and pressure change are important indicators for evaluating the forming process of short fiber rubber composites.
Table 4 shows the data of different extrusion processes.
It can be seen from
Table 4 that, at the same screw speed, the relationships of maximum pressure and extrusion temperature of the mixing rubber at the extrusion head is Y-1 > X-1, Y-2 > X-2, Y-3 > X-3. With the increase of screw speed, compared with X-1, the pressure of the extrusion head of X-3 increased by 1.74 MPa, and the extrusion temperature increased by 15 °C. Compared with Y-1, the pressure of the extrusion head of Y-3 increased 2.26 MPa, and the extrusion temperature increased 18 °C. It is indicated that short fiber rubber composite has a higher viscosity and it is difficult to be extruded. This is because the short fiber has a higher modulus, which greatly increases the effective volume, stress and strain of the filler. The extruder needs to provide more pressure to ensure material handling, which makes the heating rate of the mixing rubber to accelerate. As the screw speed increases, the shear rate of the material in the groove increases, and the temperature rise is further increased, which may cause rubber burning and affect the performance of the rubber compound.
The gear pump was used in the process of the extrusion. The relationships of maximum pressure and maximum temperature in the extruder are Y-1 > Z-1, Y-2 > Z-2, Y-3 > Z-3. This is because the gear pump provides the pressure-building function, making the internal pressure of the extruder reduced and the temperature rise decreased. At the same screw speed, the extrusion temperature relationships of rubber compound are Y-1 > Z-1, Y-2 > Z-2, and Y-3 > Z-3, while the extrusion head pressure relationships are Z-1 > Y-1, Z-2 > Y-2, and Z-3 > Y-3. As the screw speed increases, the pressure of the head of Z-3 increased 3.32 MPa compared with the Z-1 and the extrusion temperature of the rubber compound increased only 15 °C. The results indicated that the gear pump assisted extrusion process could increase the extrusion head pressure and reduces the extrusion temperature of the rubber compound. This is because the flow path of the rubber compound in the used gear pump is short, and the generated shear heat is low, while the range of temperature rise is small. With the increase of the screw speed, the temperature increase is not large, which is beneficial to maintain the performance of the extrusion rubber at high speed.
3.2. Extrusion Stability
In the process of continuous and stable extrusion, the extruded rubber was cut and weighed in a certain time interval. The weight change of the extruded rubber compound under different extrusion process conditions is shown in
Figure 7.
In the same extruder speed, the average weight relationships of the extruded rubber compound is X-1 > Z-1 > Y-1, X-2 > Z-2 > Y-2, and X-3 > Z-3 > Y-3. This is because aramid short fibers mixed in the rubber matrix increased the viscosity of the rubber and the pressure of the die, which caused the pressure reflux and leakage flow in the extruder to increase, and the extrusion volume to decrease. When the gear pump is used to assist extrusion, the two intermeshing gears feed the compound into a confined space and extrude the rubber mixture at the exit, so the pressure backflow and leakage flow of the head could be omitted. When the extruder screw speed is 30 rpm, the average weight ratio of Z-3 is increased by 10.95%, and the extrusion efficiency is significantly improved.
Extrusion stability generally decreases as the extruder screw speed increases. The standard deviation of the weight of X-3 extruded block increased from 0.77 to 4.05 than the X-1. The standard deviation of Y-3 from the weight of the Y-1 extruded block increased from 2.05 to 7.77. The standard deviation of the Z-3 to Z-1extruded block weight increased from 0.95 to 1.85, indicating that the extrusion stability of the short fiber matrix was lower than that of ordinary rubber compounds. When the gear pump is used to assist extrusion, the extrusion stability with short-fiber compound is improved. This is because the gear pump has the characteristics of positive displacement conveying, which can improve the pressure fluctuation during the extrusion of the rubber compound. Therefore, the gear pump assisted process can improve the extrusion efficiency of the short fiber mixture and ensure the extrusion stability.
3.3. Degree of Compaction
In the different process conditions, the compaction degree of the extruded short fiber rubber compound under the optical microscope is shown in
Figure 8.
The pores are clearly visible in
Figure 8a,b because the pressure at the extruder head is low at lower screw speed, and it is difficult to make extrusion molding when the Mooney viscosity of the short fiber rubber composite is large. At the same time, those factors reduced the density of the composite and the quality of the extruded product.
Pores inside the rubber compound are not obvious in
Figure 8d–f. When the gear pump was used in the extrusion process, it could increase extrusion pressure, and keep the compound at a high pressure in the extruder head position. That could increase the degree of adhesion between the layers, thus ensuring the quality of the extruded product.
3.4. Mooney Viscosity and Vulcanization Characteristics
The Mooney viscosity and vulcanization characteristics are important indicators for evaluating polymer extrusion molding [
26].
Table 5 shows the Mooney and vulcanization characteristics of the rubber compound under different extrusion process conditions.
As can be seen from
Table 5, The Mooney viscosity will be significantly increased when the short fiber was added to the rubber compound. The Mooney viscosity decreases as the screw speed increases from the data of X-1, X-2, and X-3. The screw speed increased and leads to the increase of the shearing force and the number of shearing, making the dispersion of the filler become better and the Mooney viscosity lower. From the data of Y-1, Y-2, and Y-3, the Mooney viscosity of the rubber mixture appeared down at first and then rise. This is because the extrusion pressure of fluctuation is increased, when the screw speed increased. The dispersion of the short fibers is deteriorated, then the flow ability of the rubber mixture is lowered. When the gear pump was used in the process of extrusion, the Mooney viscosity gradually decreases with the increase of the screw speed, which indicates that the gear pump can ensure the dispersion of short fibers in the rubber compound at high speed extrusion.
In order to ensure the reinforcing durability of the short fibers in the orientation direction, the resin SL3020 and the adhesive RA65 were incorporated in the processing of the short fiber rubber composite to form the chemical bond between the short fibers and the rubber molecular in the vulcanization stage. These cross-linking structures keep the orientation of short fibers unchanged when the short fibers composite rubber is subjected to stress. However, this cross-linking reaction consumes a portion of zinc oxide [
24,
25], which weakens the concentration of the formulation activation system, thereby slowing down the vulcanization rate of the formulation. This is why the t90 of Y-1–Y-3 and Z-1–Z-3 is prolonged relative to X-1–X-3. At the same time, the cross-linking of short fiber and rubber molecular chain improves the cross-linking density of the total formulation system, so MH is increased and the tensile strength at a given elongation is increased.
3.5. Physical and Mechanical Properties
The physical and mechanical properties of the vulcanizate at different extrusion conditions are shown in
Table 6.
As can be seen in
Table 6, the hardness of the cured short fiber reinforced rubber composites is significantly increased by about 10% compared with that of the ordinary rubber composite. The short fibers added into the rubber matrix are involved in the crosslinking reaction, enhancing the effect of the reinforcement. The tensile and tear strength of the short-fiber vulcanizate is higher and the DIN wear value is lower than that of the normal vulcanizate. This indicates that the short fiber reinforced rubber composite performed a good anisotropy.
The tensile and wear values of Y-3 were significantly reduced, while its tensile strength and DIN wear values are not as good as X-3. The screw rotation speed, the pressure of the extruder, and the extrusion pressure fluctuation is increased, the stability of the extrusion rubber compound decreases, the rubber material flow is disordered, and the physical and mechanical properties of the composite are degraded due to the agglomeration of the short fiber.
The physical and mechanical properties of Z-1, Z-2, Z-3 are greater than that of Y-1, Y-2, Y-3, especially when the screw speed increases to 30 rpm, At this screw speed, the short fiber vulcanizate of Z-3 still maintains good performance, and it is even slightly improved. This is because the rubber compound is pressurized in the gear pump, and the pressure is further increased when passing through the extruder head. It is enhanced that shear tensile action of short fibers is in the flow path of the extruder head. The radial orientation of short fiber became higher, and its compaction increased. As the positive displacement conveying characteristics of the gear pump, it can be greatly reduced the influence of pressure fluctuation, improved the extrusion stability, and ensured the physical and mechanical properties of the extruded product.
3.6. Dynamic Thermo-Mechanical Analysis
The loss factor (tanδ) of the vulcanizate is an important indicator that can be used to characterize the dynamic mechanical properties of rubber composites [
27]. Generally, tan δ at 0 °C is used to characterize the wet skid resistance of the composite [
25,
26]. The larger the tan δ value is, the better the wet skid resistance. The tan δ at 60 °C is used to characterize the rolling resistance of the composite [
28,
29]. The higher the tanδ value is, the higher the rolling resistance. The tanδ of the vulcanizate at 0 °C and 60 °C in different extrusion process conditions is shown in
Figure 9.
The loss factor curve of vulcanized short fiber rubber composite is moved downward, and the loss factor (tanδ) is decreased. This shows that the heat build-up properties of the composites decreased, skidding behavior worse and rolling resistance lower when short fibers were incorporated into the rubber composites. Chemical cross-linking between short fibers and rubber molecular chains formed under the action of resin, so the rigidity of short fiber rubber composites are increased. Under the action of external force, the slippage of the rubber molecules is reduced, thereby reducing the slip friction between the rubber molecular chain and the filler particles, the heat generation is reduced, and the loss is reduced.
The dynamic mechanical properties of short fiber rubber composites processed by gear pumps have also been improved. The difference value of loss factors between Z and Y increases at 0 °C and 60 °C. These indicate that the gear pump used in the extrusion process of the short fiber rubber composite material, could improve the dynamic mechanical properties of the composite material, enhance the wet-slip resistance of rubber composites and reduce the rolling resistance of materials.
3.7. Scanning Electron Microscopy (SEM) Observation and Analysis
Subject to different processes, a section of short fiber reinforced rubber composites was observed by scanning electron microscopy after it was broken. A cross-sectional view is shown in
Figure 10 with 100 times amplification.
It can be seen from
Figure 10 that the orientation and dispersibility of the short fibers were became deteriorated as the screw speed increases. When the screw speed is increased to 30 rpm the degree of orientation of the short fibers in Y-3 was significantly lowered, and the dispersion effect was deteriorated. The short fiber can maintain a certain degree of orientation and dispersibility with the increase of the screw speed when it was extruded by the gear pump. This indicates that using the gear pump can improve the extrusion efficiency while ensuring the quality of the extrusion compound. This is consistent with the experimental results in the performance test.