Search Results (2)

The bond interface is the weakest part of the repair system, and its performance is a key factor impacting the repair effectiveness of damaged concrete constructions. However, the research on the damage law and the mechanism of repair of the bonded interface in the cold region marine environment is not in-depth. In this study, the influence of polyvinyl alcohol (PVA) fibers and crystalline admixtures (CAs) on the mechanical properties and volumetric deformation performance of cementitious repair materials was researched. Furthermore, the deterioration patterns of the bond strength and chloride ion diffusion characteristics of the repair interface under the coupling of seawater-freeze-thaw cycles were investigated. Combined with the composition, micro-morphology, and micro-hardness of hydration products before and after erosion, the damage mechanism of the repaired bonding interface was revealed. The results indicate that the synergistic use of PVA fibers and CAs can significantly improve the compressive strength, bond strength and volume stability of the repair materials. The compressive strength and 40° shear strength of S0.6CA at 28 d were 101.7 MPa and 45.95 MPa, respectively. Under the seawater-freeze-thaw cycle action, the relationship between the contents of free and bound chloride ions in the bonded interface can be better fitted by the Langmuir equation. The deterioration process of the bonding interface and the penetration rate of chloride ions can be effectively delayed by PVA fiber and CAs. After 700 seawater-freeze-thaw cycles, the loss rates of bond strength and chloride diffusion coefficient of S0.6CA were reduced by 26.34% and 52.5%, respectively, compared with S0. Full article

The use of seawater and sea sand as replacements for fresh water and river sand in the preparation of seawater and sea sand concrete can effectively address issues such as high transportation costs, extended construction periods, and resource wastage. Nevertheless, in northern coastal areas, the problem of concrete durability in the complex and changing marine environment is more prominent. Research on the durability of seawater sea sand concrete is beneficial to the widening of its application range. To investigate the impact of glass fiber (GF) and polyvinyl alcohol fiber (PVA) with different blending methods on the seawater freeze–thaw resistance of seawater sea sand concrete (SSC), corresponding specimens were prepared, and seawater freeze–thaw cycling tests were conducted. By adopting the slow-freezing method and combining macro-structure and micro-morphology, the damage mechanism and the deterioration law of fiber-reinforced SSC under seawater freezing and thawing were investigated. The results indicate that, macroscopically, the incorporation of GF and PVA can effectively mitigate the damage to the matrix and reduce the effects of external erosive substances on the rate of strength loss, the rate of mass loss, and the relative dynamic elastic modulus. After 75 cycles, the SSC with a total volume doping of 0.3% and a blending ratio of 1:1 showed a 41.23% and 27.55% reduction in mass loss and strength loss, respectively, and a 29.9% improvement in relative dynamic elastic modulus compared with the basic group. Microscopic analysis reveals that the combined effect of freezing and expansion forces, the expansive substances generated by seawater intrusion into the interior of the matrix, and salt crystallization all weaken the bond between aggregate and mortar, leading to accelerated deterioration of the concrete. The incorporation of fibers enables the matrix to become denser and improves its crack-resistant properties, resulting in a better durability than that of the basic group. The damage prediction model established by the NSGM(1,N) model of gray system theory exhibits high accuracy and is suitable for long-term prediction, accurately predicting the damage of seawater sea sand concrete under seawater freeze–thaw coupling. Full article