Researchers were invited to submit innovative research papers in the areas of welding metallurgy, weldability, and associated topics of superalloys. In total, six research papers were published in this Special Issue of
Metals, entitled “Welding Metallurgy and Weldability of Superalloys”, which presents some of the research trends in the field [
1,
2,
3,
4,
5,
6]. All six research papers were related to weld cracking in some aspect, with the strongest focus on hot cracking [
1,
2,
3,
4,
6], followed by strain age cracking [
5]. The major part of the submission in terms of material was associated with Alloy 718, the “work horse” within the group of superalloys in the aero-engine industry [
2,
3,
4]. In addition, Haynes
® 282
®, a superalloy that falls into the same class of superalloys (i.e. precipitation hardening Ni- or Ni-Fe based superalloys) as Alloy 718 was covered in one paper that were investigated [
5,
6]. Varestraint weldability testing [
3,
4,
6] was the major testing method addressed within the field of weldability testing, followed by Gleeble thermomechanical testing [
5]. Raza et. al. [
2] investigated tungsten inert gas (TIG) welding on additive manufactured (AM, laser-powder bed fusion) Alloy 718 in different heat treatment conditions. The propensity for cracking in the heat affected zone (HAZ) were shown to be highest in the AM as-built condition and lowest in the AM hot isostatic pressed condition. A second paper by Raza et. al. [
4] focused on the influence of grain orientation on the hot cracking susceptibility of AM Alloy 718 using Varestraint weldability testing. It was shown that cracks in the HAZ of the welded samples primarily took place in high angle grain boundaries with a smaller magnitude of cracking in the samples tested parallel to the elongated grain orientation compared to the tests performed transverse to the elongated grain orientation.
Another interesting contribution by Alvarez et. al. [
3] investigated susceptibility toward hot cracking of wrought and investment cast Alloy 718 by the Varestraint weldability testing method. Testing was performed and compared on both TIG and laser beam welding (LBW). It was shown that the hot cracking susceptibility of LBW was enhanced due to extended center line hot cracking, resulting in a “fishbone” like cracking pattern. Only a minor effect was seen regarding the material form (wrought vs. cast), grain size, and pulsation. In fact, cast samples with coarse grain size had less susceptibility toward hot cracking than wrought material. Singh et. al. [
6] studied Varestraint weldability testing as well as Gleeble thermomechanical simulation of the newly developed cast form of Haynes
® 282
® to understand how HAZ liquation cracking is influenced by different preweld heat treatments. It was found that cracking susceptibility did not improve with a higher degree of homogenization achieved at a higher heat treatment soak temperature, in contrast, cracking was exacerbated. The enhanced degree of cracking was related to B segregation at the grain boundaries, which at the highest heat treatment temperature of 1190 °C indicated the liberation from the dissolution of C–B rich precipitates.
Hanning et. al. [
5] developed a Gleeble-based test method to study the change in the ductility signature of Haynes
® 282
® during isothermal exposure from 5 s to 1800 s within the temperature range of 750 to 950 °C. Microstructural constituents (i.e. primary and secondary type carbides as well as hardening precipitates (γ′) were identified). A ductility minimum was observed at 800–850 °C and the fracture mode was found to be dependent on the stroke rate, where a transition toward intergranular fracture was observed for stroke rates below 0.055 mm/s. Intergranular fracture was identified by microvoids present on the grain facets, while ductility did not change during ongoing age-hardening reactions for intergranularly fractured Haynes
® 282
®.
Chen et. al. [
1] contributed with a paper on Ni-based weld fillers, IN52M and IN52MSS, where its weld performance on a stainless steel (SS) substrate was investigated [
1]. The overlay-welding of IN52M and IN52MSS onto CF8A SS was conducted by a TIG welding process in multiple passes. Hot cracking of the overlay welds was shown to be related to the formation of γ-intermetallic (Ni
3(Nb,Mo)) microconstituents. The greater contents of Nb and Mo in the 52MSS overlay enhanced the formation of these constituents at the interdendritic boundaries. Thus, the hot cracking sensitivity of the 52MSS overlay was higher than that of the 52M overlay.