Next Article in Journal
Cation Disorder and Local Structural Distortions in AgxBi1–xS2 Nanoparticles
Next Article in Special Issue
Review of Polymer Composites with Diverse Nanofillers for Electromagnetic Interference Shielding
Previous Article in Journal
In-Situ Gold–Ceria Nanoparticles: Superior Optical Fluorescence Quenching Sensor for Dissolved Oxygen
Previous Article in Special Issue
Graphene Oxide with Controlled Content of Oxygen Groups as a Filler for Polymer Composites Used for Infrared Radiation Shielding
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Eco-Friendly Sustainable Fluorescent Carbon Dots for the Adsorption of Heavy Metal Ions in Aqueous Environment

by
Musa Yahaya Pudza
1,*,
Zurina Zainal Abidin
1,*,
Suraya Abdul Rashid
1,
Faizah Md Yasin
1,
A. S. M. Noor
2 and
Mohammed A. Issa
1
1
Department of Chemical and Environmental Engineering, Faculty of Engineering, Universiti Putra Malaysia, Serdang 43400, Selangor, Malaysia
2
Department of Computer and Communication System Engineering, Faculty of Engineering, Universiti Putra Malaysia (UPM), Serdang 43400, Selangor, Malaysia
*
Authors to whom correspondence should be addressed.
Nanomaterials 2020, 10(2), 315; https://doi.org/10.3390/nano10020315
Submission received: 29 November 2019 / Revised: 9 December 2019 / Accepted: 11 December 2019 / Published: 12 February 2020

Abstract

:
The materials and substances required for sustainable water treatment by adsorption technique, are still being researched widely by distinguished classes of researchers. Thus, the need to synthesize substances that can effectively clean up pollutants from the environment cannot be overemphasized. So far, materials in bulk forms that are rich in carbon, such as biochar and varieties of activated carbon have been used for various adsorptive purposes. The use of bulk materials for such purposes are not efficient due to minimal surface areas available for adsorption. This study explores the adsorption task at nano dimension using carbon dots (CDs) from tapioca. The properties of carbon structure and its influence on the adsorptive efficacy of carbon nanoparticles were investigated by energy-dispersive spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR), high resolution transmission electron microscopy (HrTEM), and atomic force microscopy (AFM). The results implied carbon present in CDs are good adsorbents for effective adsorption of heavy metal ions (lead) with removal efficiency of 80.6% in aqueous environment. The adsorption process as explored by both Langmuir and Freundlich isotherms have proven favorability of the adsorption process. Langmuir form two and three have correlation coefficients R2 at 0.9922 and 0.9912, respectively. The Freundlich isotherm confirms CDs as having defined surface heterogeneity and the exponential distribution of active sites. The adsorption of lead unto CDs obeyed the second order kinetic model with coefficient of determination, R2 of 0.9668 and 0.9996 at an initial lead concentration of 20 mg/L and 100 mg/L, respectively. The findings validated the efficiency of CDs derived from tapioca as an excellent material for further utilization in the environmental fields of wastewater pollution detection and clean up, bio-imaging, and chemical sensing applications.

Graphical Abstract

1. Introduction

Carbon dots (CDs) are dimensionless nanoparticles classified as carbon nanomaterials with >10 nm in size and are considered latest class of fluorescent nanoparticles [1,2,3]. CDs derived from green and sustainable materials are essential aspects of biology, chemistry, and physical sciences with essential applications in computer science and electronic [4,5,6,7]. CDs have several characteristics such as being environmentally friendly, easy to synthesize, non-blinking, high biocompatibility, durability, high photostability, quenchable (on/off) emission with excitation wavelength that can be functionalized based on their desired applications, and dissolve easily in water with a high carbon content (up to 99.9%) [8]. These attributes of CDs have made it an interesting substance to a wide range of researchers [9,10,11].
Comparatively, semiconductor nano crystals otherwise known as quantum dots (QDs) are nanoparticles with diameter ranging from 1–10 nm. When compared to CDs, QDs are toxic and expensive [12]. QDs are conventional fluorescent dyes that have unique optical properties, however, CDs are the best option due to their high degree of biocompatibility, cost effectiveness, non-toxic, and have been successfully applied in bio imaging, bio sensing [13,14,15,16], agricultural diagnosis sectors [17], pharmaceuticals [18,19], solar cells [20], electrochemical functions [21,22,23], wastewater treatment [24], photocatalysis, and chemical sensing [25,26].
There are numerous techniques for synthesizing CDs, such as; arc-discharge [9,21], laser ablation [8,27,28], chemical oxidation [16,29,30,31], and electrochemical [32,33,34,35,36]. However, several factors need to be considered when adopting a synthesis route to obtain CDs [37]. In the synthesis process of CDs there is the possibility of carbonaceous aggregation that tends to form during carbonization process. This challenge is remedied by synthesis processes such as; hydrothermal route [38,39,40,41], organic pyrolysis, and microwave assisted method [42,43,44,45,46]. These techniques possess the abilities to control the size and uniformity of CDs in solvents [37].
Literature provides reports on the applications of agro-based wastes to synthesize CDs such as; cooking oil waste [38], pomelo peal [45], egg-white and egg-yolk [40], orange juice [37], as well as eggshells [44]. Contrary to ethics of reuse of waste material, these biomass, creates residual waste that are toxic. Hence, the need for clean materials in the synthesis of CDs have became a necessity in the modern era of nanoscale materials. It is advantageous to adopt the use of clean materials in the synthesis of CDs for applications such as bioimaging, drug delievry, water treatment, and for other numerous portable uses. It is not ethical to adopt waste materials/biomass for purposes that relates to health and the environment by process that further releases toxins. The noticeable scientific shortfall of applying biomass in the synthesis of CDs is their lack of essential purity and structural homogeneity to obtain homogenous CDs. Hence, it is necessary to apply clean food materials in the synthesis of homogeneous fluorescent CDs [12].
Alqadami et al. [46] applied trisodium citrate based magnetite nanocomposite at pH 4 for the effective removal of toxic dye from aquoues medium in 40 min. Adsorptive performance of Fe3O4@AMCA-MIL-53 (Al) nanocomposite was utilized for the adsorptive removal of highly toxic methylene blue (MB) and malachite green (MG) dyes from aqueous environment [47]. Xiangtao et al. [48] reported the use of nano materials in batch adsorption process of lead ions. The effective use of nanomaterials have been used widely in detection of pollutants [24] and fluorescence quenching [18], chiefly by electrochemical methods of diffusion layer [24] which technically occurs by the adsorption mechanism [11,21,31,45]. In the present study, tapioca was utilized in the synthesis of homogeneous water soluble fluorescent CDs through an improved hydrothermal method. Characterization analysis of the compositional elements, dimensional sizes, and functional groups were analysed for adequate understanding of the structural mechanism of CDs for further application in the adsorption of heavy metal ions (lead).

2. Materials and Methods

Acetone along with sodium hydroxide were of analytical grade obtained from Sigma-Aldrich. (Saint Louis, MO, USA) Tapioca was locally sourced. A 50 mL stainless steel capacity of hydrothermal reactor was used. Convective oven, 365 nm Uv-Lamp, Centrifuge machine, lead (ll) nitrate (Pb(NO3)2) analytical reagent, and M.W. 331.21, were obtained from R & M marketing, Essex, U.K. Solutions used in this study were prepared with deionized water (DI) purified by a Milli-Q water type system (18 MΩ cm).

2.1. Synthesis of Carbon Dots

Tapioca flour (0.1 g) was mixed with 16mL of solvent (D.I H20/NaOH/(CH3)2CO). The mixture was oven heated at 175 °C in a convective oven for 1.45 h which yielded disaccharide and glucose (Figure 1).
The disaccharide crosslinked with several other disaccharides to form polysaccharides (subsequently removed as residue by centrifugation at 3000 rpm for 20 min), while the glucose went through carbonization that produced the needed CDs with functional groups (COO–, C=O, –OH, C–H, C=C, C–O–C) afloat on the surfaces of the synthesized CDs. The mechanism of the synthesized CDs is as displayed in Figure 1.

2.2. Carbon Dots Characterization

The characterization of CDs by Fourier-transform Infrared spectroscopy (FTIR) was conducted by Perkin Elmer spectrum 100 spectrometer (Bridgeport avenue Shelton, CT, USA). The measurement is made by attenuated total reflection method with frequency range of 4000–500 cm−1, that allows for the direct measurement of functional groups in CDs. The absorption spectra were taken from a UV-spectrometer 1800 series. High resolution transmission electron microscopic (HrTem) and energy-dispersive spectroscopy (EDS) were characterized by FEI Tecnai G2 F20, 200 kV, ZrO2/W (100) z-contrast dark-field stem imaging by the HAADF detector. The zeta potential analysis was carried out using zetasizer Nano series (Malvern). Finally, X-ray photoelectron spectroscopy (XPS) was conducted with ULVAC-PHI Quantera II and the X-ray source is Al K-Alpha, monochromatic source (1486.6 eV).

2.3. Adsorption Studies

Different concentrations of lead (ll) nitrate (Pb(NO3)2) at 20 mg/L, 40 mg/L, 60 mg/L, 80 mg/L, and 100 mg/L were prepared with deionized water. These various concentrations of Pb(NO3)2 solution were mixed with CDs at room temperature (25 °C). The solution was next centrifuged at 120 rpm and the supernatant was taken for measurement using UV Spectrometer. The application of CDs for adsorption of lead was conducted by batch adsorption process. The initial concentrations of lead and the amount absorbed by CDs have been reported in the later sections of the article. The mass of CDs is the mass of the tapioca used for the synthesis of CDs (0.1 g) while the contact time and pH were varied from 5–260 min and 3–12, respectively. The amount adsorbed at equilibrium, qe (mg/g) and the percentage removal of lead were calculated as in literature [46,47].
q e = ( c 0 c f ) v M
where, qe is equilibrium concentration of lead at any time (mg/g), M is mass of the adsorbent used (g), and v is volume of the lead solution (L)
% Re m o v a l = c 0 c f c 0 × 100
where, C0 is initial lead concentration in sample (mg/L), Cf is equilibrium lead concentration in final solution after adsorption (mg/L).

2.4. Adsorption Isotherm

Adsorption isotherm describes the equilibrium relationship between adsorbent (CDs) and the adsorbate (lead). It indicates the amount of lead (Pb2+) adsorbed by the CDs and the residual lead in the bulk solution at room temperature [49]. The equilibrium isotherms were obtained graphically by plotting solid phase concentration against liquid phase concentration [50].

2.4.1. Langmuir Isotherm, Adsorption Equation, and Limitations

Langmuir isotherm is one of the famous studies applied for adsorption capacities [49]. It assumed that adsorption is monolayer and reversible. The adsorption is homogenous when it takes place within specific site while the energy is constant and does not depend on the degree of occupation of adsorbents at active center [51]. All adsorption sites are equivalent with no interactions between adsorbate molecules on adjacent sites.
The following equation is Langmuir isotherm Equation [50].
q e = q m a x K L C e 1 + C e K L
where:
  • qe = adsorption capacity (mg/g)
  • qmax = maximum monolayer adsorption capacity of the adsorbent (mg/g)
  • Ce = equilibrium concentration of the adsorbate (mg/L)
  • KL = Langmuir adsorption constant related to free energy adsorption (L/mg)
Since the estimation of the adsorption isotherm parameters interference are through linearization method. The following three forms of linearized isotherm equation are used to determine the constants KL and qmax [52].
Form 1:
C e q e = 1 q m a x K L + C e q m a x
Form 2:
1 q e = 1 q m a x + 1 q m a x K L C e
Form 3:
q e = q e C e K L + q m a x
Equations (4)–(6) are the derivation of Langmuir isotherm model. It clarifies what happens at the equilibrium of monolayer adsorption process. The number of molecules being adsorbed will be equal to the number of molecules leaving the adsorbed site, that is total amount absorbed qmax is directly proportional to concentration in solution and available area for adsorption. The constants can be evaluated from intercept and the slope of linear plots of experimental data of (Ce/qe) versus Ce (for Equation (4)) or (1/qe) versus (1/Ce) (for Equation (5)) or qe versus (qe/Ce) (for Equation (6)). The most popular form of analyzing adsorption equilibrium data is Langmuir Equation (3) [49,50].

2.4.2. Freundlich Isotherm

Freundlich isotherm is an empirical relationship that can be utilized for non-ideal sorption that involves heterogeneous surface energy system [49]. It is assumed that there are neither homogeneous site energies nor limited level of sorption [47]. Freundlich isotherm equation is expressed by the following Equation [49].
qe = KF Ce 1/n
  • qe = adsorption capacity (mg/g)
  • Kf = Freundlich isotherm constant (mg/g)
  • Ce = equilibrium concentration of adsorbate (mg/L)
  • 1/n = adsorption capacity (L/mg)
By linearizing Equation (8), constants KF and n were determined using ln qe versus ln Ce plot.
l n   q e = ln K F + 1 n l n C e
KF is the Freundlich proportionality constant obtained from the intercept and 1/n from the slope. Here KF represents the quantity of the absorbed lead required to maintain lead concentration in the solution at unity (i.e., 1 mg/L). As KF increases, the adsorption capacity for a given adsorbate also increases. The slope 1/n ranges between zero and one and indicates intensity of adsorption or surface uniformity. Higher value of 1/n (or lower n) means adsorption is more favorable and greater surface heterogeneity [46].

3. Results

3.1. Characterization of Carbon Dots (CDs)

3.1.1. Atomic Force Microscopy (AFM) and High Resolution Transmission Electron Microscopy (HrTem) of Carbon Dots (CDs)

It is essential to determine the particle sizes of the synthesized CDs by utilizing precision techniques such as the atomic force microscopy (AFM) and HrTem [25]. The synthesis of CDs with optimal clearance and abundant surface sites are essential for research applications in adsorption by nano processes [39].
Figure 2A,B display 2D and 3D plots of the morphological pattern of carbon dots comprising 32 counts of CDs with mean heights and diameters of 2.440 nm and 32.387 nm, respectively. The AFM images provide the nature of CDs morphological structure. This is important, as it demonstrates the ability of the particles to adsorb heavy metal pollutants that are present in aqueous medium. This is in agreement with previous studies of adsorption isotherms and kinetic models [53].
Figure 2C, is the HrTEM images of CDs with their size distributions. The sizes of CDs on the inset histogram shows an average size of 3.0–3.99 nm as the most abundant available size count. More so, the average size of CDs at 3.0–3.99 nm meaning that there is abundant surface area available for adsorption of lead ions.
Table 1 shows a detailed presentation of size distribution of CDs, obtained by measuring the heights of 32-single carbon dots observed under atomic force microscopy. The mean CDs surface of 1801.610 nm2 and mean diameter of 32.387 nm provides plentiful adsorption sites for the effective removal of lead ions from aqueous solution as reported in this study.

3.1.2. Zeta Potential of Carbon Dots

The Zeta (ζ) potential of CDs, known as electrokinetic potential of the synthesized fluorescent CDs was measured by zetasizer to obtain the surface charge. This technique also provides insight on CDs properties such as double layer attributes with several hydrophilic functional groups (hydroxyl, carboxyl, and carbonyl).
Zeta potential measurements are occasionally presented as a useful and efficient method of evaluating CDs ability to adsorb heavy metal ions. The surface charge of the carbon dots at pH = 7 was obtained as −31.7 mV charge. The negative ζ potential is due to dense electron cloud concentrating on the CDs [52]. The value of ζ potential relies upon a short or a long-term stability of CDs particles. CDs with a high zeta potential (negative or positive) are considered stable electrostatically [38], while particles with low zeta potentials tend to coagulate or aggregate over a brief time period. A low ζ potential results in a weak physical stability of CDs. Scientifically, when the ζ of carbon dots is high, it means that the repulsive forces have exceeded the attractive forces, which creates a relatively stable system. Highly dispersed nanoparticles such as CDs have zeta potential values greater than +30 mV or less than −30 mV [54]. Particles at nano-dimension having zeta potential values ranging from −10 to +10mV are considered to be neutral [55]. The zeta potential is very sensitive to the changes happening upon dilution, such as the variations in pH and ionic strength [54]. At alkaline pH greater than pH 7, the zeta potential remains highly negative to reflect existence of stable anions. As the pH decreases below seven (acidic region), the zeta potential normally becomes less negative in values until it becomes zero. This is known as the point zero charge whereby potential changes from negative to positive (or positive to negative). After that the zeta potential becomes more positive in values (as pH becomes more acidic) which reflects the existence of positively charged surrounding of the CDs. Hence at greater pH than seven, a stable negatively charge carbon dots dominate and attract positively charge heavy metals cations (lead (Pb+2).

3.1.3. Energy Dispersive Spectroscopy (EDS)

This technique has been applied to obtain the elemental composition of synthesized CDs. The EDS is an integrated feature of HrTEM. The CDs specimen were bombarded with an electron beam within the HrTEM. The bombarding electrons collides with the carbon dots, knocking some of their atoms off in the process, which creates a space, vacated by an ejected inner shell electron. This empty space is eventually occupied by another higher-energy electron from an outer shell. This happens because the transferring outer electron relinquishes some energy by emitting an X-ray. Thus, by measuring the amounts of energy present in the X-rays being released by CDs during electron beam bombardment, the identity of atoms from which the X-ray was emitted were established as shown in Figure 3 [56,57,58,59].
Figure 3 (point one EDs) depicts the analysis of the compositional elements in CDs, the figure shows a high carbon content of 95.93%.
The presence of copper (Cu) is as a result of elemental transfer from the measuring tool to CDs. The Eds peaks from zero to 10 energy level depicts the elements available on CDs where the initial peak is considered the top layer of the EDS that represents carbon (C). The second peak is oxygen (O) while subsequent peaks are the tool piece electrode, made of Copper (Cu) material as earlier stated.
Similarly, Figure 3 (EDS point two) shows the EDs measured on another location point two whereby this time a higher concentration of atomic carbon was recorded than previously discovered on EDS point one. Carbon remained the highest compositional element found in CDs (99.05 atomic %). The abscissa axis of the EDS is considered the ionization energy pathway while the ordinate axis indicates the counts per second of the CDs intensity [55]. The EDS spectrums are plots of X-rays received for each energy level indicated. They display peaks that corresponds to individual levels of energy received as generated by X-rays. Each peak is unique to an atom that corresponds to a single element (C, O, and Cu). A higher peak in the spectrum, denotes the most dominant element present in CDs.

3.1.4. X-ray Photoelectron Spectroscopy (XPS)

The XPS technique is an important concept employed in surface science to provide significant and vital information on the chemical state of elements and relative composition by atomic layers present in CDs. This technique employs electron excitement and electron kinetic energy measurement presented in the form of several peaks and positions in a spectrum pattern. Individual elements are determined by the attributes of the CDs such as spin orbital-splitting and peak area ratio.
The XPS results (Figure 4) show clear dominance of carbon at 99.05 atomic percentage (%).
Figure 4A,B shows wide and narrow scan spectrums of tapioca (precursor) and CDs. The XPS wide spectrum (Figure 4A) of CDs at 16,958.334 counts per seconds reflects 57.32% atomic% concentrations of carbon and 8008.3335 counts per seconds of oxygen peaks at 42.68% atomic% concentrations at high photoelectron energies.
There is a significant elemental increase of carbon from 57.32% in tapioca (precursor) to 70.652% in the content of CDs. Furthermore, there is a significant decreased content of oxygen from 42.68% to 21.349% due to the decomposition and intermolecular formation of hydrocarbon rings (cyclization) by hydrothermal reaction [57].
Figure 4B shows a high-resolution of narrow scan for C1s spectra of tapioca (as CDs precursor material) and synthesized CDs. The tapioca validates the presence of C–C, C–O, and C=C bond with atomic concentration of 9.37%, 54.54%, and 36.09%, respectively. Tapioca binding energy (eV) and intensity (c.p.s) for C–C, C–O, and C=C are at 285.018 eV/106.685 c.p.s, 286.618 eV/ 3945.017 c.p.s, and 288.118 eV/ 3151.267 c.p.s, respectively (Figure 4B (Tapioca)). The narrow scan high resolution on C1s spectra (Figure 4B (carbon dots)) shows some significant shifts on the atomic percentages and intensities of C–C, C–O, and C=C. The major peak at 284.755 eV/5167.234 c.p.s, 286.355 eV/1722.329 c.p.s, and 288.955 eV/2378.359 c.p.s correspond to C–C, C–O, and C=C, respectively. While, the atomic percentages of functional groups such as C–C, C–O, and C=C were 58.90%, 15.74%, and 25.36%, respectively [60].
Based on the XPS and EDS elemental analysis, the hybridization and coefficients that exists between the functional groups and carbon core contributed to the luminescent and adsorptive behavior of CDs [61]. In the fields of environmental science and medical application, tapioca-derived CDs that constituted of organic carbon is intrinsically non-toxic [62,63,64] in comparison to quantum dots and hence provides a solution to toxicity concerns.

3.1.5. Fourier Transform Infrared (FTIR) Analysis

Fourier-transform infrared spectroscopy, have been employed in this study to portray and examine the functional structure of CDs. Much more, to reveal the useful compounds of elements present, before and after hydrothermal treatment of the precursor carbon material (tapioca). Figure 5 shows the FTIR spectra of tapioca and carbon dots.
As shown in Figure 5 (tapioca powder), peaks associated with the stretching vibrations of hydroxyl (–OH) and carboxylic (COO–) groups are recorded at 3353.45 and 2933.78 cm−1. Further stretching vibration of C-H occurred from 1645.24 to 1418.70. The peaks at 1151.38, 1079.20, and 1014.41 cm−1 can be due to the C–H stretching vibrations and out-of-plane bending modes of sp2 and sp3 –CH group [45].
Figure 5 (Carbon dots), the spectra of Carbon dots, shows the existence of hydroxyl (–OH) group at 3389.71 cm−1 which increased on the carbon dots structure as a result of hydrolysis phenomenon. The carboxylic (COO–) group 2145.73 cm−1 meanwhile was reduced by thermal destruction of saccharides structure [19,39]. The peaks at 1695.27 cm−1 and 1644.62 cm−1 indicate the increase in the C–H stretching vibrations of the bending modes of the sp2 and sp3 –CH group. The peaks around 1427.63 cm−1 until 1369.43 cm−1 are due to C–O–C [41]. The peak at 1237.62cm−1 corresponds to the C=C stretching vibration while 1094.19 cm−1 and 996.19 cm−1 represents the C=O stretching vibration and the last group at 706.78 cm−1 denotes the C=C bond of the unsaturated glucose structure. The FT-IR graph, shows the formation of unsaturated carbon. Along with oxygen-rich groups such as hydroxyl, carboxyl, and carbonyl situated on carbon dots surface, which are in consonance with the hydrothermal process of synthesizing carbon dots [38,39]. The functional groups here identified are responsible for the water-soluble nature of carbon dots [12].

3.2. Optical Properties of Carbon Dots (CDs)

The UV-vis spectrometry is a necessary instrument used for validating the quality of CDs [13]. Irradiations of UV-spectroscope on CDs excited by absorbing the energy generated, creates an electron excited state on CDs. The molecules of CDs with extended π-electron provides the basics for the fluorescence emission of CDs (Figure 6). The tapioca-derived CDs is a wavelength dependent photoluminescent ionic solution in the visible range with a surface abundant hydroxyl and carboxylic/carboxyl moieties [13]. The synthesized CDs shows a strong optical absorption in the UV region (230–340 nm) with a tail extending to the visible range (800 nm) as presented in Figure 6.
Absorption shoulders in the spectrum may be due to the π-π*of C=C bonds or n-π* of C=O [37]. The uniqueness of CDs is a result of the fluorescence emitted by it. Based on past study, the dependency of intensity and wavelength emission towards excitation wavelength [15]. This is due to the different size of particles and surface chemistry at different emissive traps of CDs surface which is related to the synthesis method.

3.3. Adsorption of Lead Using Carbon Dots (CDs)

Several investigations have been reported regarding the quenching and detection effects that nanomaterials have on heavy metals. These properties of nanomaterials are due to their adsorptive capabilities [65,66]. In this study, batch adsorption was carried out to determine the CDs ability for adsorption of lead ions. Initial experiments were conducted to determine the contact time needed to achieve equilibrium for lead ion adsorption on CDs. The contact time for optimum adsorption was at 260 min with removal efficiency of 80.6% (Figure 7). The adsorption efficiency of CDs to remove lead ions at 80.6% have surpassed recent report by Xu et al. [67] who utilized iron hydroxyphosphate composites derived from waste lithium-ion batteries to remove 75% of lead ions in aqueous medium [67]. Mahar et al. [68] synthesized porous carbon nanofibers to adsorb lead ions in aqueous media and also reported a lower maximum adsorption efficiency of 79% [68]. In another study using Enteromorpha derived biochar, an efficiency of 54% was obtained for adsorbing lead ions [69]. Hence, the results provide clear evidence of CDs superiority for removal of lead ions in aqueous medium.
Initial concentration of lead ion was analyzed to determine the effective adsorption attributes of CDs. The removal efficiency of CDs was high when the initial concentration of lead was at 100 mg/L (Figure 8A,B).
Figure 8A shows the validations of initial concentrations of lead on the adsorption efficiency of CDs. The removal efficiency of lead is proportional to the increase in initial concentration of lead (20–100 mg/L), due to the greater driving force existing at bulk concentration gradient [47].
Figure 8B shows the influence of pH on the adsorptive efficiency of carbon dots. A pH from seven to 13 was confirmed to be the best with efficiencies between 50–80% removal. This is because, at pH 7, the CDs exhibits a zeta potential of −31.7 mV which suggests existence of negative charge on the surface of CDs adsorbent. Zeta potential of CDs is the potential at the slipping plane that separates the mobile fluid from the fluid that remains attached to the solute. Thus, it can easily adsorb the positively charge lead ions [54,55].

3.3.1. Adsorption Equilibrium

Adsorption equilibrium of lead adsorption by CDs was obtained with Langmuir forms one, two, and three by applying Equations (4)–(6). The R2 values were 0.9603, 0.9922, and 0.912 for Langmuir forms one, two, and three, respectively. The Langmuir isotherm model is a linear plot of the total amount of lead adsorbed (qe) against the equilibrium concentration (Ce) for CDs as shown in Figure 9 (Equilibrium of Adsorption). The equilibrium adsorption of lead increased with the concentrations of lead ions. Thus, suggesting a strong affinity of the lead ions for the functional surface sites of CDs [18,59].
The values of the Langmuir constant KL and the monolayer capacity qmax can be evaluated from the three forms of Langmuir adsorption models. Comparing the three Langmuir forms in Figure 9, the Langmuir forms two and three have correlation coefficients R2 at 0.9922 and 0.9912, respectively compared to a lower R2 value obtained at Langmuir form one (0.9603). The coefficient of determination represents the variance about the mean that is used to analyze the fitting degrees of isotherms and kinetic models with experimental data. The Langmuir forms two and three are best suited for the study. Langmuir forms can be correlated with the variation of the suitable area and porosity of the adsorbent. Availability of CDs at nano dimension level offers vast surface area and pore volume availability for pore diffusion-sorption activities [50] that results in a higher adsorption capacity [18].
Based on Freundlich adsorption model, ln qe against ln Ce was plotted as shown in Figure 10. The graph is a straight line that yields values of n (1.61) from the slope and KF (0.0507) from the intercept respectively with coefficient of correlation of R2 = 0.9954. The slope 1/n ranges from zero to one, is a degree of adsorption intensity and surface uniformity. As the value approaches zero, the surface becomes more uniform [36]. The value of 1/n is 0.6188 and it indicates the heterogeneity of CDs. The value of exponent n in this investigation is greater than one which means the adsorption of lead on CDs is favorable.
The Freundlich isotherm confirms CDs as having defined surface heterogeneity and the exponential distribution of active sites [70]. The adsorption process as explored by both Langmuir and Freundlich isotherms have proven favorability of the adsorption process. This means CDs is a versatile substance with existence of heterogeneous surface areas suitable for effective monolayer and multilayer stacking conformed to both adsorption process.

3.3.2. Adsorption Kinetics

The Lagergren equation was used in the determination of rate constant for adsorption of lead. The adsorption experiment was carried out at concentrations of 20–100 mg/L of lead, adsorbent dose of 0.1 g (the dosage of tapioca for synthesizing CDs) and contact time between 5 to 260 min. A graph of t/qt against t was plotted in order to investigate this model.

Pseudo First and Second-Order Kinetic Models

Figure 11 shows linearized form of first order and second order kinetics model of lead concentration on CDs. The adsorption phenomenon of lead by CDs is best described by the second order kinetic model. The coefficient R2 for second order kinetic model at an initial concentration of 20 mg/L and 100 mg/L are 0.9668 and 0.9996, respectively. The calculated and experimental values for the adsorption of lead ions obeyed pseudo-second-order kinetic model [47]. Figure 11 shows the linear forms models for first and second order kinetics at varying lead concentration.
Pseudo-second-order rate constant (k2), qe, and qcal were obtained from the slope and intercept of the graphs in Figure 11. From the calculated data (qecal) values of pseudo-second-order kinetic model, there is compatibility trend when compared to the experimental data (qexp). The pseudo-second-order kinetic equation for adsorption is much similar to the universal rate law for chemical reaction [47]. Since the processes followed the pseudo second-order equation, it literally suggests that the adsorption is mainly by simple chemisorption reaction occurring between the lead ions and the surface functional groups of CDs [49,50].

4. Conclusions

The synthesized CDs is low cost without the need for tedious purification (environmentally friendly process). The CDs demonstrates to be a suitable adsorbent with remarkable properties which can have wide applications. Characterization techniques such as energy-dispersive X-ray spectroscopy (EDXs) and XPS have been utilized to determine quantitatively the compositional elements in CDs. The intensity counts and carbon content of CDs makes it suitable for adsorption studies of heavy metal (lead). CDs with zeta potential −31 mV means it is a stable hydrophilic substance. CDs capacity for absorption of heavy metal (lead) was confirmed with high efficiency of 80.6%. Both Langmuir and Freundlich indicates favorability of the adsorption process as shown by Langmuir Form two and three. Freundlich constant of 1/n indicates surface heterogeneity of CDs that is suitable for adsorption. The adsorption phenomenon of lead by CDs followed the second order kinetic model that is known to be similar to the universal rate law for chemical reaction. It literally suggests that the adsorption proceed mainly by simple chemisorption reaction occurring between the lead ions and the surface functional groups of CDs. The synthesized carbon dots are excellent fluorescent materials proposed for further applications in environmental fields of wastewater pollution detection, medical bio-imaging, and chemical sensing.

Author Contributions

M.Y.P., As the first author; made the Study conception and design (wrote the ANN codes), Acquisition of data and Drafting of manuscript. Z.Z.A., contributed in the Study conception and design, Critical revision of major scientific ideas through clinical experience. S.A.R., As a co-author; served as scientific advisor, critically reviewed the study proposal. F.M.Y., As a co-author; contributed in the Analysis and interpretation of data as well as critically reviewed the study proposal. A.S.M.N., As a co-author; contributed in the Analysis and interpretation of data. M.A.I., As a co-author; contributed in the interpretation of data. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Universiti Putra Malaysia, grant number GP-IPS/2017/9556800.

Acknowledgments

The authors would like to thank technicians of biochemical laboratory, faculty of engineering at Universiti Putra Malaysia (UPM), Malaysia.

Conflicts of Interest

The authors declare that there is no conflict of interest whatsoever regarding the publication of this paper.

References

  1. Sun, Y.; Shen, C.; Wang, J.; Lu, Y. Facile Synthesis of Biocompatible N, S-doped Carbon Dots for Cell Imaging and Ion Detecting. RSC Adv. 2015, 5, 16368–16375. [Google Scholar] [CrossRef]
  2. Puvvada, N.; Prashanth, K.; Suraj, K.; Himani, K.; Mahitosh, M.; Amita, P. Synthesis of biocompatible multicolor luminescent carbon dots for bioimaging applications. Sci. Technol. Adv. Mater 2012, 13, 045008. [Google Scholar] [CrossRef] [PubMed]
  3. David, A.; Mouhamed, D.; Julien, L.; Gilles, L.; Christophe, D. Origin of the nano-carbon allotropes in pulsed laser ablation in liquids synthesis. J. Colloid Interface Sci. 2017, 489, 114–125. [Google Scholar]
  4. Marks, R.S. Handbook of Biosensors and Biochips, 1st ed.; John Wiley & Sons, Ltd.: Chichester, UK, 2007. [Google Scholar]
  5. Zhu, X.; Zhao, T.; Nie, Z.; Miao, Z.; Liu, Y.; Yao, S. Nitrogen-doped carbon nanoparticle modulated turn-on fluorescent probes for histidine detection and its imaging in living cells. Nanoscale 2016, 8, 2205–2211. [Google Scholar] [CrossRef]
  6. Xu, Y.; Wu, M.; Liu, Y.; Feng, X.Z.; Yin, X.B.; He, X.W.; Zhang, Y.K. Nitrogen-doped carbon dots: A facile and general preparation method, photoluminescence investigation, and imaging applications. Chem. Eur. J. 2013, 19, 2276–2283. [Google Scholar] [CrossRef]
  7. Shi, Q.-Q.; Yu-Hao, L.; Yang, X.; Kui, Y.-Z. High-yield and high-solubility nitrogen-doped carbon dots: Formation, fluorescence mechanism and imaging application. RSC Adv. 2013, 4, 1563. [Google Scholar] [CrossRef]
  8. Sun, Y.P.; Zhou, B.; Lin, Y.; Wang, W.; Fernando, K.S.; Pathak, P.; Meziani, M.J.; Harruff, B.A.; Wang, X.; Wang, H.; et al. Quantum-sized carbon dots for bright and colorful photoluminescence. J. Am. Chem. Soc. 2006, 128, 7756–7757. [Google Scholar] [CrossRef]
  9. Xiauyou, X.; Ray, R.; Yunlong, J.G.H.; Gearheart, L.; Kyle, A.R.; Scrivens, W.A. Electrophoretric analysis and purification of fluorescent single-walled carbon nanotube fragments. Am. Chem. Soc. 2004, 126, 12736–12737. [Google Scholar]
  10. Wang, X.; Cao, L.; Meziani, J.; Qi, G.; Zhou, B.; Harruff, A.B.; Sun, P.Y. Photoinduced electron transfers with carbon dots. Chem. Commun. 2009, 25, 3774–3776. [Google Scholar] [CrossRef]
  11. Xu, Z.; Yu, J.; Liu, G. Fabrication of carbon quantum dots and their application for efficient detecting Ru in the solution. Sens. Actuators 2013, 181, 209–214. [Google Scholar] [CrossRef]
  12. Titirici, M.-M.; Robin, J.W.; Nicolas, B.; Vitaliy, L.B.; Dang, S.S.; Francisco, D.M.; James, H.C.; Mark, J.M. Sustainable carbon materials. Chem. Soc. Rev. 2015, 44, 250–290. [Google Scholar] [CrossRef]
  13. Cao, L.; Sheng-Tao, Y.; Xin, W.; Pengju, G.L.; Jia-Hui, L.; Sushant, S.; Yamin, L.; Ya-Ping, S. Competitive Performance of Carbon “Quantum” Dots in Optical Bioimaging. Theranostics 2012, 2, 295–301. [Google Scholar] [CrossRef]
  14. Wang, Y.; Hu, R.; Lin, G.; Roy, I.; Yong, K.T. Functionalized quantum dots for biosensing and bioimaging and concerns on toxicity. ACS Appl. Mater. Interfaces 2013, 5, 2786–2799. [Google Scholar] [CrossRef] [PubMed]
  15. Wang, Y.; Hu, A. Carbon quantum dots: Synthesis, properties and applications. J. Mater. Chem. C 2014, 2, 6921. [Google Scholar] [CrossRef] [Green Version]
  16. Zhou, P.; Lu, X.; Sun, Z.; Guo, Y.; He, H. A review on syntheses, properties, characterization and bioanalytical applications of fluorescent carbon dots. Microchim. Acta 2016, 183, 519–542. [Google Scholar]
  17. Tothill, I.E. Biosensors developments and potential applications in the agricultural diagnosis sector. Comput. Electron. Agric. 2001, 30, 205–218. [Google Scholar] [CrossRef]
  18. Gaddam, R.R.; Vasudevan, D.; Narayan, R.; Raju, K.V. Controllable synthesis of biosourced blue-green fluorescent carbon dots from camphor for the detection of heavy metal ions in water. RSC Adv. 2014, 4, 57137–57143. [Google Scholar] [CrossRef]
  19. Ali, A.E.; Hghighat, S.; Kazemifard, N.; Rezaei, B.; Moradi, F. A novel one-step and green synthesis of highly fluorescent carbon dots from saffron for cell imaging and sensing of prilocaine. Sens. Actuators B Chem. 2017, 253, 451–460. [Google Scholar]
  20. Yang, Y.; Zhao, B.; Gao, Y.; Liu, H.; Tian, Y.; Qin, D.; Wu, H.; Huang, W.; Hou, L. Novel hybrid ligands for passivating PbS colloidal quantum dots to enhance the performance of solar cells. Nano-Micro Lett. 2015, 7, 325–331. [Google Scholar] [CrossRef] [Green Version]
  21. Lim, S.Y.; Shen, W.; Gao, Z. Carbon quantum dots and their applications. Chem. Soc. Rev. 2015, 44, 362–381. [Google Scholar] [CrossRef]
  22. Li, H.; He, X.; Kang, Z.; Huang, H.; Liu, Y.; Liu, J.; Lian, S.; Tsang, C.H.; Yang, X.; Lee, S.T. Water-soluble fluorescent carbon quantum dots and photocatalyst design. Angew. Chem. Int. Ed. 2010, 49, 4430–4434. [Google Scholar] [CrossRef] [PubMed]
  23. Hsu, P.; Shih, Z.; Lee, C.; Chang, H. Synthesis and analytical applications of photoluminescent carbon nanodots. Green Chem. 2012, 14, 917–920. [Google Scholar] [CrossRef]
  24. Zhu, G.M.; Zeng, Y.; Zhang, L.; Tang, J.; Chen, M.; Cheng, L.H.; Zhang, L.; He, Y.; Guo, X.X.; He, M.Y. Highly sensitive electrochemical sensor using a MWCNTs/GNPs-modified electrode for lead (II) detection based on lead(II)-induced G-rich DNA conformation. Analyst 2014, 139, 5014–5020. [Google Scholar] [CrossRef] [PubMed]
  25. Saud, P.S.; Bishweshwar, P.; Al-Mahmnur, A.; Zafar, K.G.; Mira, P.; Hak, Y.K. Carbon quantum dots anchored TiO2 nanofibers: Effective photocatalyst for waste water treatment. Ceram. Int. 2015, 41, 11953–11959. [Google Scholar] [CrossRef]
  26. Etacheria, V.; Cristiana, D.V.; Jenny, S.; Detlef, B.; Suresh, C.P. Visible-light activation of TiO2 photocatalysts: Advances in theory and experiments. J. Photochem. Photobiol. C Photochem. Rev. 2015, 25, 1–29. [Google Scholar] [CrossRef] [Green Version]
  27. Li, X.; Hongqiang, W.; Yoshiki, S.; Alexander, P.; Kenji, K.; Naoto, K. Preparation of carbon quantum dots with tunable photoluminescence by rapid laser passivation in ordinary organic solvents. Chem. Commun. 2011, 47, 932–934. [Google Scholar] [CrossRef]
  28. Yu, H.; Li, X.; Zeng, X.; Lu, Y. Preparation of carbon dots by non-focusing pulsed laser irradiation in toluene. Chem. Commun. 2016, 52, 819–822. [Google Scholar] [CrossRef]
  29. Fang, Y.; Guo, S.; Li, D.; Zhu, C.; Ren, W.; Dong, S.; Wang, E. Easy synthesis and imaging applications of cross-linked green fluorescent hollow carbon nanoparticles. ACS Nano 2012, 6, 400–409. [Google Scholar] [CrossRef]
  30. Sun, D.; Ban, R.; Zhang, P.; Wu, G.; Zhang, J.; Zhu, J. Hair fiber as a precursor for synthesizing of sulfur—And nitrogen-co-doped carbon dots with tunable luminescence properties. Carbon 2013, 64, 424–434. [Google Scholar] [CrossRef]
  31. Gaddam, R.R.; Sudip, M.; Neelambaram, P.; Vasudevan, D.; Raju, K. Facile synthesis of carbon dot and residual carbon nanobeads: Implications for ion sensing, medicinal and biological applications. Mater. Sci. Eng. C 2017, 73, 643–652. [Google Scholar] [CrossRef]
  32. Zhou, J.; Christina, B.; Ruying, L.; Xingtai, Z.; Tsun-Kong, S.; Xueliang, S.; Zhifeng, D. An electrochemical avenue to blue luminescent nanocrystals from multiwalled carbon nanotubes (MWCNTs). J. Am. Chem. Soc. 2007, 129, 744–745. [Google Scholar] [CrossRef] [PubMed]
  33. Yao, S.; Hu, Y.; Li, G. A one-step sonoelectrochemical preparation method of pure blue fluorescent carbon nanoparticles under a high intensity electric field. Carbon 2014, 66, 77–83. [Google Scholar] [CrossRef]
  34. Zhang, P.; Xue, Z.; Luo, D.; Yu, W.; Guo, Z.; Wang, T. Dual-peak electrogenerated chemiluminescence of carbon dots for iron ions detection. Anal. Chem. 2014, 86, 5620–5623. [Google Scholar] [CrossRef] [PubMed]
  35. Deng, J.; Lu, Q.; Mi, N.; Li, H.; Liu, M.; Xu, M.; Tan, L.; Xie, Q.; Zhang, Y.; Yao, S. Electrochemical synthesis of carbon nanodots directly from alcohols. Chem. Eur. J. 2014, 20, 4993–4999. [Google Scholar] [CrossRef]
  36. Mahardika, P.A.; Pradita, A.A.; Jotti, K.; Annisa, L.W. Removal of Heavy Metal Nickel-Ions from Wastewaters Using Carbon Nanodots from Frying Oil. Procedia Eng. 2017, 170, 36–40. [Google Scholar]
  37. Sahu, S.; Behera, B.; Maiti, T.K.; Mohapatra, S. Simple one-step synthesis of highly luminescent carbon dots from orange juice: Application as excellent bio-imaging agents. Chem. Commun. 2012, 48, 8835. [Google Scholar] [CrossRef]
  38. Wei, L.; Sichun, W.; Ying, L.; Chunhui, M.; Shouxin, L. One-step hydrothermal synthesis of fluorescent nanocrystalline cellulose/carbon dot hydrogels. Carbohydr. Polym. 2017, 175, 7–17. [Google Scholar]
  39. Luyao, L.; Xingxian, W.; Zheng, F.; Fengling, C. One-step hydrothermal synthesis of nitrogen- and sulfur-co-doped carbon dots from ginkgo leaves and application in biology. Mater. Lett. 2017, 196, 300–303. [Google Scholar]
  40. Wang, J.; Wang, C.F.; Chen, S. Amphiphilic Egg-Derived Carbon Dots: Rapid Plasma Fabrication, Pyrolysis Process, and Multicolor Printing Patterns. Angew. Chem. Int. Ed. 2012, 51, 9297–9301. [Google Scholar] [CrossRef]
  41. Liu, Y.; Xiao, N.; Gong, N.; Wang, H.; Shi, X.; Gu, W.; Ye, L. One-step microwave-assisted polyol synthesis of green luminescent carbon dots as optical nanoprobes. Carbon 2014, 68, 258–264. [Google Scholar] [CrossRef]
  42. Choi, Y.; Nichaphat, T.; Ari, C.; Seongho, J.; Insik, I. Microwave-assisted synthesis of luminescent and biocompatible lysine-based carbon quantum dots. J. Ind. Eng. Chem. 2017, 47, 329–335. [Google Scholar] [CrossRef]
  43. Bhattacharyya, D.; Prashant, K.S.; Michael, L.F. Quantum dots and carbon dots based fluorescent sensors for TB biomarkers detection. Vacuum 2017, 146, 606–613. [Google Scholar] [CrossRef]
  44. Ke, Y.; Garg, B.; Ling, Y.C. Waste chicken eggshell as low-cost precursor for efficient synthesis of nitrogen-doped fluorescent carbon nanodots and their multi-functional applications. RSC Adv. 2014, 4, 58329–58336. [Google Scholar] [CrossRef]
  45. Lu, W.; Xiaoyun, Q.; Sen, L.; Guohui, C.; Yingwei, Z.; Yonglan, L.; Abdullah, M.A.; Abdulrahman, O.; Xuping, S. Economical, Green Synthesis of Fluorescent Carbon Nanoparticles and Their Use as Probes for Sensitive and Selective Detection of Mercury(II) Ions. Anal. Chem. 2012, 84, 5351–5357. [Google Scholar] [CrossRef]
  46. Alqadami, A.A.; Naushad, M.; Abdalla, M.A.; Khan, M.R.; Alothman, Z.A. Adsorptive removal of toxic dye using Fe3O4–TSC nanocomposite: Equilibrium, kinetic, and thermodynamic studies. J. Chem. Eng. Data 2016, 61, 3806–3813. [Google Scholar] [CrossRef]
  47. Alqadami, A.A.; Naushad, M.; Alothman, Z.A.; Ahamad, T. Adsorptive performance of MOF nanocomposite for methylene blue and malachite green dyes: Kinetics, isotherm and mechanism. J. Environ. Manag. 2018, 223, 29–36. [Google Scholar] [CrossRef]
  48. Xiangtao, W.; Yifei, G.; Li, Y.; Meihua, H.; Jing, Z.; Xiaoliang, C. Nanomaterials as Sorbents to Remove Heavy Metal Ions in Wastewater Treatment. J. Environ. Anal. Toxicol 2012, 2, 145. [Google Scholar]
  49. Nejib, A.; Joelle, D.; Amane, J.; Emna, E.; Malika, G.; Khadija, S.; Malika, T.A. Removal of anionic dye from textile industries’ effluents by using Tunisian clays as adsorbents. Ζeta potential and streaming-induced potential measurements. C. R. Chim. 2019, 22, 113–125. [Google Scholar]
  50. Adeyi, A.A.; Jamil, S.N.A.M.; Abdullah, L.C.; Choong, T.S.Y.; Lau, K.L.; Abdullah, M. Adsorptive Removal of Methylene Blue from Aquatic Environments Using Thiourea-Modified Poly(Acrylonitrile-co-Acrylic Acid). Materials 2019, 12, 1734. [Google Scholar] [CrossRef] [Green Version]
  51. Langmuir, I. The adsorption of gases on plane surfaces of glass, mica and platinum. J. Am. Chem. Soc. 1918, 40, 1361–1403. [Google Scholar] [CrossRef] [Green Version]
  52. Manique, M.C.; Silva, A.P.; Alves, A.K.; Bergmann, C.P. Titanate nanotubes produced from microwave-assisted hydrothermal synthesis: Characterization, adsorption and photocatalytic activity. Braz. J. Chem. Eng. 2017, 34, 331–339. [Google Scholar] [CrossRef] [Green Version]
  53. Jhonsi, M.A.; Thulasi, S. A novel fluorescent carbon dots derived from tamarind. Chem. Phys. Lett. 2016, 661, 179–184. [Google Scholar] [CrossRef]
  54. Clogston, J.D.; Patri, A.K. Zeta potential measurement. Methods Mol. Biol. 2011, 697, 63–70. [Google Scholar]
  55. Barhoum, A.; García-Betancourt, M.L.; Rahier, H.; Van-Assche, G. Physicochemical characterization of nanomaterials: Polymorph, composition, wettability, and thermal stability. In Emerging Applications of Nanoparticles and Architecture Nanostructures; Elsevier: Amsterdam, The Netherlands, 2018; pp. 255–278. [Google Scholar]
  56. Yongli, L.; Qingxiang, Z.; Yongyong, Y.; Yalin, W. Hydrothermal synthesis of fluorescent carbon dots from sodium citrate and polyacrylamide and their highly selective detection of lead and pyrophosphate. Carbon 2017, 115, 550–560. [Google Scholar]
  57. Jie, W.; Yuhao, C.; Fengxian, Q.; Xin, L.; Dongya, Y. One-pot simple green synthesis of water-soluble cleaner fluorescent carbon dots from cellulose and its sensitive detection of iron ion. J. Clean. Prod. 2017, 23–30. [Google Scholar] [CrossRef]
  58. Lingling, L.; Luyao, L.; Chang-Po, C.; Fengling, C. Green synthesis of nitrogen-doped carbon dots from ginkgo fruits and the application in cell imaging. Inorg. Chem. Commun. 2017, 86, 227–231. [Google Scholar]
  59. Bin, W.; Feng, L.; Yuanya, W.; Yanfen, C.; Chang, M.L. Synthesis of catalytically active multielement-doped carbon dots and application for colorimetric detection of glucose. Sens. Actuators B Chem. 2018, 225, 2601–2607. [Google Scholar]
  60. Park, S.Y.; Lee, H.U.; Park, E.S.; Lee, S.C.; Lee, J.W.; Jeong, S.W.; Kim, C.H.; Lee, Y.C.; Huh, Y.S.; Lee, J. Photoluminescent green carbon nanodots from food-waste-derived sources: Large-scale synthesis, properties, and biomedical applications. ACS Appl. Mater. Interfaces 2014, 6, 3365–3370. [Google Scholar] [CrossRef]
  61. Han, S.; He, Z.; Jian, Z.; Yujie, X.; Liangliang, L.; Hangxing, W.; Xiangkai, L.; Weisheng, L.; Yu, T. Fabrication, gradient extraction and surface polarity-dependent photoluminescence of cow milk-derived carbon dots. RSC Adv. 2014, 4, 58084–58089. [Google Scholar] [CrossRef]
  62. Zhu, S.; Zhang, J.; Qiao, C.; Tang, S.; Li, Y.; Yuan, W. Strongly green-photoluminescent graphene quantum dots for bioimaging applications. Chem. Commun. 2011, 47, 6858–6860. [Google Scholar] [CrossRef]
  63. Sayan, G.; Poushali, D.; Madhuparna, B.; Subhadip, M.; Amit, K.D.; Das, N.C. Strongly blue-luminescent N-doped carbogenic dots as a tracer metalsensing probe in aqueous medium and its potential activity towardsin situ Ag-nanoparticle synthesis. Sens. Actuators B 2017, 252, 735–746. [Google Scholar]
  64. Yuqian, P.; Hui, G.; Shaohui, W.; Xiaolong, L. Facile synthesis the nitrogen and sulfur co-doped carbon dots for selective fluorescence detection of heavy metal ions. Mater. Lett. 2017, 193, 236–239. [Google Scholar]
  65. Nisar, U.; Muhammad, M.; Ibrahim, K.; Ahsanulhaq, Q. Nanomaterial-based optical chemical sensors for the detection of heavy metals in water: Recent advances and challenges. Trends Anal. Chem. 2018, 100, 155–166. [Google Scholar]
  66. Laxman, W.; Tanushree, D.; Pawan, K.; Yong, S.O.; Samadhan, P.; Akash, D.; Ki-Hyun, K. Functionalized fluorescent nanomaterials for sensing pollutants in the environment: A critical review. Trends Anal. Chem. 2017, 97, 458–467. [Google Scholar]
  67. Xu, L.; Chen, C.; Huo, J.B.; Chen, X.; Yang, J.C.; Fu, M.L. Iron hydroxyphosphate composites derived from waste lithium-ion batteries for lead adsorption and Fenton-like catalytic degradation of methylene blue. Environ. Technol. Innov. 2019, 16, 100504–100515. [Google Scholar] [CrossRef]
  68. Mahar, F.K.; He, L.; Wei, K.; Mehdi, M.; Zhu, M.; Gu, J.; Kim, I. Rapid adsorption of lead ions using porous carbon nanofibers. Chemosphere 2019, 225, 360–367. [Google Scholar] [CrossRef] [PubMed]
  69. Yang, W.; Wang, Z.; Song, S.; Han, J.; Chen, H.; Wang, X.; Cheng, J. Adsorption of copper (II) and lead (II) from seawater using hydrothermal biochar derived from Enteromorpha. Mar. Pollut. Bull. 2019, 149, 110586–110592. [Google Scholar] [CrossRef]
  70. Silas, K.; Ab Karim Ghani, W.W.; Choong, T.S.; Rashid, U. Optimization of Activated Carbon Monolith Co3O4-Based Catalyst for Simultaneous SO2/NOx Removal from Flue Gas Using Response Surface Methodology. Combust. Sci. Technol. 2019, 2–19. [Google Scholar] [CrossRef]
Figure 1. Carbon dots synthesis mechanism.
Figure 1. Carbon dots synthesis mechanism.
Nanomaterials 10 00315 g001
Figure 2. (A) atomic force microscopy (AFM) 2D image of carbon dots (CDs) (B) AFM 3D morphology of CDs (C) high resolution transmission electron microscopic (HrTEM) image of CDs.
Figure 2. (A) atomic force microscopy (AFM) 2D image of carbon dots (CDs) (B) AFM 3D morphology of CDs (C) high resolution transmission electron microscopic (HrTEM) image of CDs.
Nanomaterials 10 00315 g002
Figure 3. Energy-dispersive spectroscopy (EDS) Spectra of carbon dots at point 1 and 2.
Figure 3. Energy-dispersive spectroscopy (EDS) Spectra of carbon dots at point 1 and 2.
Nanomaterials 10 00315 g003
Figure 4. (A,B) Wide and narrow scan for tapioca (precursor) and synthesized carbon dots.
Figure 4. (A,B) Wide and narrow scan for tapioca (precursor) and synthesized carbon dots.
Nanomaterials 10 00315 g004
Figure 5. Fourier-transform infrared spectroscopy (FT-IR) spectrum of CDs and tapioca.
Figure 5. Fourier-transform infrared spectroscopy (FT-IR) spectrum of CDs and tapioca.
Nanomaterials 10 00315 g005
Figure 6. Optical properties of CDs by UV-visible absorption and emission spectra.
Figure 6. Optical properties of CDs by UV-visible absorption and emission spectra.
Nanomaterials 10 00315 g006
Figure 7. Effect of contact time on the removal efficiency of lead ions by CDs.
Figure 7. Effect of contact time on the removal efficiency of lead ions by CDs.
Nanomaterials 10 00315 g007
Figure 8. (A) initial concentration of lead ions and removal efficiency of CDs and (B) relationship between lead removal and pH.
Figure 8. (A) initial concentration of lead ions and removal efficiency of CDs and (B) relationship between lead removal and pH.
Nanomaterials 10 00315 g008
Figure 9. Equilibrium adsorption and the three forms of Langmuir isotherm for lead adsorption into CDs.
Figure 9. Equilibrium adsorption and the three forms of Langmuir isotherm for lead adsorption into CDs.
Nanomaterials 10 00315 g009
Figure 10. Freundlich Isotherm for CDs.
Figure 10. Freundlich Isotherm for CDs.
Nanomaterials 10 00315 g010
Figure 11. Initial Concentration of lead ions for first and second order kinetics.
Figure 11. Initial Concentration of lead ions for first and second order kinetics.
Nanomaterials 10 00315 g011
Table 1. Atomic force microscopic statistics of CDs.
Table 1. Atomic force microscopic statistics of CDs.
ParameterMeanMinimumMaximumSigma
Total Count32.00032.00032.0000.000
Height2.440 (nm)0.409 (nm)8.168 (nm)1.875 (nm)
Area1801.610 (nm2)95.367 (nm2)31,333.924 (nm2)5432.314 (nm2)
Diameter32.387 (nm)11.019 (nm)199.739 (nm)35.284 (nm)

Share and Cite

MDPI and ACS Style

Yahaya Pudza, M.; Zainal Abidin, Z.; Abdul Rashid, S.; Md Yasin, F.; Noor, A.S.M.; Issa, M.A. Eco-Friendly Sustainable Fluorescent Carbon Dots for the Adsorption of Heavy Metal Ions in Aqueous Environment. Nanomaterials 2020, 10, 315. https://doi.org/10.3390/nano10020315

AMA Style

Yahaya Pudza M, Zainal Abidin Z, Abdul Rashid S, Md Yasin F, Noor ASM, Issa MA. Eco-Friendly Sustainable Fluorescent Carbon Dots for the Adsorption of Heavy Metal Ions in Aqueous Environment. Nanomaterials. 2020; 10(2):315. https://doi.org/10.3390/nano10020315

Chicago/Turabian Style

Yahaya Pudza, Musa, Zurina Zainal Abidin, Suraya Abdul Rashid, Faizah Md Yasin, A. S. M. Noor, and Mohammed A. Issa. 2020. "Eco-Friendly Sustainable Fluorescent Carbon Dots for the Adsorption of Heavy Metal Ions in Aqueous Environment" Nanomaterials 10, no. 2: 315. https://doi.org/10.3390/nano10020315

APA Style

Yahaya Pudza, M., Zainal Abidin, Z., Abdul Rashid, S., Md Yasin, F., Noor, A. S. M., & Issa, M. A. (2020). Eco-Friendly Sustainable Fluorescent Carbon Dots for the Adsorption of Heavy Metal Ions in Aqueous Environment. Nanomaterials, 10(2), 315. https://doi.org/10.3390/nano10020315

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop