High Oxidation Resistance of CVD Graphene-Reinforced Copper Matrix Composites
Abstract
:1. Introduction
2. Materials and Methods
3. Results and Discussion
4. Conclusions
Author Contributions
Funding
Conflicts of Interest
References
- Zhang, C.; Luo, G.; Zhang, J.; Dai, Y.; Shen, Q.; Zhang, L. Materials & Design Synthesis and thermal conductivity improvement of W-Cu composites modified with WC interfacial layer. Mater. Des. 2017, 127, 233–242. [Google Scholar]
- Yang, X.; Liang, S.; Wang, X.; Xiao, P.; Fan, Z. Effect of WC and CeO2 on microstructure and properties of W–Cu electrical contact material. Int. J. Refract. Met. Hard Mater. 2010, 28, 305–311. [Google Scholar] [CrossRef]
- Dhaou, H.; Khedher, N.B.; Mellouli, S.; Souahlia, A.; Askri, F.; Jemni, A.; Ben Nasrallah, S. Improvement of thermal performance of spiral heat exchanger on hydrogen storage by adding copper fins. Int. J. Therm. Sci. 2011, 50, 2536–2542. [Google Scholar] [CrossRef]
- Lee, H.S.; Lee, H.J.; Kwon, H.C. New methodology for enhancing electrical conductivity and strength of copper alloy using combined structure. In Proceedings of the 60th Electronic Components and Technology Conference (ECTC), Las Vegas, NV, USA, 1–4 June 2010. [Google Scholar]
- Abyzov, A.M.; Kidalov, S.V.; Shakhov, F.M. High thermal conductivity composites consisting of diamond filler with tungsten coating and copper (silver) matrix. J. Mater. Sci. 2011, 46, 1424–1438. [Google Scholar] [CrossRef]
- Bénard, A.E.B.; Hernández, D.M.; Reyes, J.G.G.; Prado, A.O.; Franssens, R.S. Synthesis, Characterization and Cold Workability of Cast Copper-Magnesium-Tin Alloys. Metall. Mater. Trans. A 2014, 45, 555–562. [Google Scholar] [CrossRef]
- Cocke, D.L.; Chuah, G.K.; Kruse, N.; Block, J.H. Copper oxidation and surface copper oxide stability investigated by pulsed field desorption mass spectrometry. Appl. Surf. Sci. 1995, 84, 153–161. [Google Scholar] [CrossRef]
- Karthik, N.; Sethuraman, M.G. Improved copper corrosion resistance of epoxy-functionalized hybrid sol–gel monolayers by thiosemicarbazide. Ionics 2015, 21, 1477–1488. [Google Scholar] [CrossRef]
- Mccarthy, S.L.; Carter, R.O.; Weber, W.H. Lubricant-induced corrosion in copper electrical contacts. In Proceedings of the Forty-Third IEEE Holm Conference on Electrical Contacts, Philadelphia, PA, USA, 20–22 October 1997. [Google Scholar]
- Beloufa, A. Conduction degradation by fretting corrosion phenomena for contact samples made of high-copper alloys. Tribol. Int. 2010, 43, 2110–2119. [Google Scholar] [CrossRef]
- Vojtěch, D.; Kubásek, J.; Šerák, J.; Novák, P. Mechanical and corrosion properties of newly developed biodegradable Zn-based alloys for bone fixation. Acta Biomater. 2011, 7, 3515–3522. [Google Scholar] [CrossRef] [PubMed]
- Yuan, S.J.; Pehkonen, S.O. Surface characterization and corrosion behavior of 70/30 Cu–Ni alloy in pristine and sulfide-containing simulated seawater. Corros. Sci. 2007, 49, 1276–1304. [Google Scholar] [CrossRef]
- Saunders, S.R.J.; Nicholls, J.R. Coatings and surface treatments for high temperature oxidation resistance. Met. Sci. J. 2013, 5, 780–798. [Google Scholar] [CrossRef]
- Özyılmaz, A.T.; Tüken, T.; Yazıcı, B.; Erbil, M. The electrochemical synthesis and corrosion performance of polyaniline on copper. Prog. Org. Coat. 2005, 52, 92–97. [Google Scholar] [CrossRef]
- Novoselov, K.S.; Geim, A.K.; Morozov, S.V.; Jiang, D.; Zhang, Y.; Dubonos, S.V.; Grigorieva, I.V.; Firsov, A.A. Electric field effect in atomically thin carbon films. Science 2004, 306, 666–669. [Google Scholar] [CrossRef] [PubMed]
- Bonaccorso, F.; Sun, Z.; Hasan, T.; Ferrari, A.C. Graphene photonics and optoelectronics. Nat. Photonics 2010, 4, 611–622. [Google Scholar] [CrossRef] [Green Version]
- Stoller, M.D.; Park, S.; Zhu, Y.; An, J.; Ruoff, R.S. Graphene-based ultracapacitors. Nano Lett. 2008, 8, 3498–3502. [Google Scholar] [CrossRef]
- Luechinger, N.A.; Athanassiou, E.K.; Stark, W.J. Graphene-stabilized copper nanoparticles as an air-stable substitute for silver and gold in low-cost ink-jet printable electronics. Nanotechnology 2008, 19, 445201. [Google Scholar] [CrossRef] [PubMed]
- Li, S.; Hou, B.; Dai, D.; Shu, S.; Wu, M.; Li, A.; Han, Y.; Zhu, Z.-X.; Chen, B.-A.; Ding, Y.; et al. CVD Synthesis of Monodisperse Graphene/Cu Microparticles with High Corrosion Resistance in Cu Etchant. Materials 2018, 11, 1459. [Google Scholar] [CrossRef] [PubMed]
- Hu, J.; Ji, Y.; Shi, Y. Review on the use of Graphene as a Protective Coating against Corrosion. Ann. Mater. Sci. Eng. A 2014, 1, 1–16. [Google Scholar]
- Zhou, F.; Li, Z.; Shenoy, G.J.; Li, L.; Liu, H. Enhanced Room-Temperature Corrosion of Copper in the Presence of Graphene. ACS Nano 2013, 6939–6947. [Google Scholar] [CrossRef]
- Tsetseris, L.; Pantelides, S.T. Graphene: An impermeable or selectively permeable membrane for atomic species? Carbon 2014, 67, 58–63. [Google Scholar] [CrossRef]
- Chen, S.; Brown, L.; Levendorf, M.; Cai, W.; Ju, S.; Edgeworth, J.; Ruoff, R.S.; Al, C.E.T. Oxidation Resistance of Graphene- Coated Cu and Cu/Ni Alloy. ACS Nano 2011, 1321–1327. [Google Scholar] [CrossRef] [PubMed]
- Schriver, M.; Regan, W.; Gannett, W.J.; Zaniewski, A.M.; Crommie, M.F. Graphene as a Long-Term Metal Oxidation Barrier: Worse Than Nothing. ACS Nano 2013, 5763–5768. [Google Scholar] [CrossRef] [PubMed]
- Sun, H.; Li, X.; Li, Y.; Chen, G.; Liu, Z.; Alam, F.E.; Dan, D.; Li, L.; Li, T.; Xu, J. Bin High-Quality Monolithic Graphene Films via Laterally Stitched Growth and Structure Repairing of Isolated Flakes for Transparent Electronics. Chem. Mater. 2017, 29, 7808–7815. [Google Scholar] [CrossRef]
- Bolotin, K.I.; Sikes, K.J.; Hone, J.; Stormer, H.L.; Kim, P. Temperature-dependent transport in suspended graphene. Phys. Rev. Lett. 2008, 101, 96802. [Google Scholar] [CrossRef]
- Tripathi, K.; Gyawali, G.; Lee, S.W. CVD-Graphene Coating for Improving Friction and Wear of Grey Cast Iron at Interfaces. ACS Appl. Mater. Interfaces 2017, 9, 32336–32351. [Google Scholar] [CrossRef] [PubMed]
- Chen, Y.; Zhang, X.; Liu, E.; He, C.; Han, Y.; Li, Q.; Nash, P.; Zhao, N. Fabrication of three-dimensional graphene/Cu composite by in-situ CVD and its strengthening mechanism. J. Alloys Compd. 2016, 688, 69–76. [Google Scholar] [CrossRef]
- Lee, J.; Hwang, J.; Yoon, T.; Jin, S.H.; Lee, J.; Kim, T. Enhanced Mechanical Properties of Graphene/Copper Nanocomposites Using a Molecular-Level Mixing Process. Adv. Mater. 2013, 25, 6724–6729. [Google Scholar]
- Procedures, E. Thermal Conductivity of Copper-Graphene Composite Films Synthesized by Electrochemical Deposition with Exfoliated Graphene Platelets. Metall. Mater. Trans. B 2012, 43, 316–324. [Google Scholar]
- Lidong; Wang; Guojian; Weidong Effect of Ball Milling on the Defeat of Few-Layer Graphene and Properties of Copper Matrix Composites. Acta Metall. Sin. 2014, 27, 937–943. [CrossRef]
- Ferrari, A.C.; Meyer, J.C.; Scardaci, V.; Casiraghi, C.; Lazzeri, M.; Mauri, F.; Piscanec, S.; Jiang, D.; Novoselov, K.S.; Roth, S. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 2006, 97, 187401. [Google Scholar] [CrossRef]
- Cui, Y.F.; Cui, J.L.; Xu, X.; Cheng, F.P.; Wang, L.X.; Li, S.; Ji, S.J.; Sun, J.C. Electrochemical Properties of Niobium Modified AISI316L Stainless Steel Bipolar Plates for Direct Formic Acid Fuel Cell. Fuel Cells 2017, 17, 698–707. [Google Scholar] [CrossRef]
© 2019 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
Share and Cite
Wu, M.; Hou, B.; Shu, S.; Li, A.; Geng, Q.; Li, H.; Shi, Y.; Yang, M.; Du, S.; Wang, J.-Q.; et al. High Oxidation Resistance of CVD Graphene-Reinforced Copper Matrix Composites. Nanomaterials 2019, 9, 498. https://doi.org/10.3390/nano9040498
Wu M, Hou B, Shu S, Li A, Geng Q, Li H, Shi Y, Yang M, Du S, Wang J-Q, et al. High Oxidation Resistance of CVD Graphene-Reinforced Copper Matrix Composites. Nanomaterials. 2019; 9(4):498. https://doi.org/10.3390/nano9040498
Chicago/Turabian StyleWu, Mingliang, Baosen Hou, Shengcheng Shu, Ao Li, Qi Geng, He Li, Yumeng Shi, Minghui Yang, Shiyu Du, Jun-Qiang Wang, and et al. 2019. "High Oxidation Resistance of CVD Graphene-Reinforced Copper Matrix Composites" Nanomaterials 9, no. 4: 498. https://doi.org/10.3390/nano9040498