Correction: Mirandona-Olaeta et al. Ionic Liquid-Laden Zn-MOF-74-Based Solid-State Electrolyte for Sodium Batteries. Batteries 2023, 9, 588

The authors wish to make the following corrections to their paper [1]:

Error in Table

In the original publication, there was a mistake in Table 1 as published. The superscripts of the conductivity values were written incorrectly. The corrected

Table 1. Conductivities recorded at room temperature (RT) and 70 °C for each IL@MOF sample, together with experimental results extracted from the literature.

Sample	T (°C)	σ (S cm−1)	Reference
Na-β″-alumina	RT	1.7 × 10−3	[35]
Na3Zr2Si2PO12	RT	2.1 × 10−4	[8]
IL@MOF	22.4	1.83 × 10−4	This work
	70.3	1.71 × 10−3
IL0.8@MOF	18.6	7.93 × 10−5
	69.4	9.3 × 10−4
IL0.6@MOF	17.1	4.55 × 10−5
	70.3	6.55 × 10−4
IL0.5@MOF	19.1	4.58 × 10−4
	70.6	3.1 × 10−3
[Na0.1EMIm0.9][TFSI]@ZIF-8	RT crystalline	2.97 × 10−4	[30]
	RT amorphous	2.0 × 10−4
Na[Bmpyr][TFSI]@UiO-66-SO3Na	RT	3.6 × 10−4	[29]
NaTFSI-EIMS@UiO-67-MIMS	30	1.24 × 10−4	[23]
Na[EMIm][BF4]@MIL-101-SO3Na	150	1.32 × 10−2	[36]
Na[EMIm][TFSI]@ZIF-8	RT (ZIF-8micro)	1.6 × 10−5	[37]
	RT (ZIF-8meso)	8.4 × 10−6

appears below. The authors state that the scientific conclusions are unaffected. This correction was approved by the Academic Editor. The original publication has also been updated.