Correction: Bagchi et al. Effects of Carboxyl Functionalized CNT on Electrochemical Behaviour of Polyluminol-CNT Composites. Chemistry 2022, 4, 1561–1575

Text Correction

There was an error in the original publication [1]. The description of the binder addition to the CNTs was unclear and CNT was not mentioned for the mixing step with IPA.

A correction has been made to the first paragraph of Section 2.2.

“The CNT and COOH-CNT, respectively, were mixed with 5% wt. PTFE binder solution using IPA and left to dry under ambient conditions. The dried slurry-like mixture was placed on a pasta roller to compress and form 100–200 μm free-standing films [8].”

Error in Figure Caption

In the original publication, there was a mistake in the caption of Figure 1b as published. The unit eV/ų was used instead of eV Å⁻³, which was originally inconsistent with the paper formatting. The corrected caption appears below.

“Figure 1. (a) Schematic of side (left) and top (right) views of the structural arrangement of luminol adsorbed on COOH-graphene in the interstitial configuration, (b) 3D difference charge density plot of luminol adsorbed on COOH-graphene corresponding to the ±0.2 eV Å⁻³ isosurface. Blue and red wire mesh surfaces correspond to regions of electron accumulation and depletion, respectively. (c) Most significant differences in Bader ionic charges following adsorption and chemical modification of luminol. A positive value indicates an increase in positive ionic charge, and vice versa, in units of fundamental charge (e).”

The authors state that the scientific conclusions are unaffected. This correction was approved by the Academic Editor. The original publication has also been updated.