The ultraviolet (UV) copolymers of two monomers, one methacrylic and the other vinyl monomer (styrene, S) were prepared. As methacrylic monomers, citronellyl methacrylate (CM) or geranyl methacrylate (GM) were used. The preparation was proven to contain high solvent- and chemical-resistant copolymers due to their cross-linked structure with the conversion degree of the double bonds above 0.92 for poly(citronellyl methacrylate)/polystyrene (PCM/PS) and above 0.85 for poly(geranyl methacrylate)/polystyrene (PGM/PS) copolymers. The obtained copolymers showed only one glass transition temperature (T_g). Depending on the structure and amount of the used methacrylic monomer, the T_g values were from 0.4 °C to −15.2 °C for PCM/PS copolymers and from −23.2 °C to −50.5 °C for PGM/PS copolymers. The thermogravimetric analysis (TG/DTG) showed a higher thermal stability for PCM/PS (148–187 °C) than for PGM/PS copolymers (119–159 °C) in inert and oxidative atmospheres. The simultaneous thermogravimetric analysis coupled with Fourier Transform Infrared spectroscopy (TG/FTIR) showed that the pyrolysis and oxidative decomposition of the tested copolymers took place according to the radical mechanism. This led to receiving a mixture of low molecular mass organic molecules containing saturated and unsaturated fragments, carbonyl groups, aromatic fragments as well as to CO, CO₂ and H₂O. This indicated the depolymerization process (inert) and further oxidation processes of the initially formed volatiles and/or residues in oxidative conditions. Full article

More environmentally friendly polymeric materials for use in corrosive conditions were obtained in the process of UV polymerization of terpene methacrylate monomers: geranyl methacrylate and citronellyl methacrylate and the commercially available monomer methyl methacrylate. Selected properties (solvent resistance, chemical resistance, glass transition temperature, thermal stability, and decomposition course during heating) were evaluated. It was found that the properties of the materials directly depended on the monomer percentage and the conditioning temperatures used. An increase in the geranyl or citronellyl methacrylate monomer content in the copolymers reduced the solubility and chemical resistance of the materials post-cured at 50 °C. The samples post-cured at 120 °C were characterized by high resistance to polar and non-polar solvents and the chemical environment, regardless of the percentage composition. The glass transition temperatures for samples conditioned at 120 °C increased with increasing content of methyl methacrylate in the copolymers. The thermal stability of copolymers depended on the conditioning temperatures used. It was greater than 200 °C for most copolymers post-cured at 120 °C. The process of pyrolysis of copolymers led to the emission of geranyl methacrylate, citronellyl methacrylate, and methyl methacrylate monomers as the main pyrolysis volatiles. Full article