Search Results (2)

In order to further explore the feasibility of the application of the residue of Chinese herbal medicine in FDM 3D technology and enrich the kinds of printing materials, Astragalus residue powder(ARP)/poly(lactic acid) (PLA) biocomposite was FDM 3D-printed, meanwhile, two traditional biocomposites, i.e., wood flour (WF)/PLA and rice straw powder (RSP)/PLA, were prepared by the same method, and the properties of the biocomposites were comparatively investigated. The results showed that, the tensile and flexural strengths of ARP/PLA were 28.33 MPa and 97.60 MPa, respectively, which were 2.85% and 10.89% smaller than those of WF/PLA, while 15.73% and 7.04% greater than those of RSP/PLA. WF/PLA showed typical brittle fracture characteristics, ARP/PLA and RSP/PLA both showed ductile fracture, but not obviously. Among the three kinds of biocomposites, ARP/PLA was the most thermally stable, followed by WF/PLA and RSP/PLA in turn. The incorporation of natural plant powder had no significant effect on the glassy transition, melting, and cold-crystallization behaviors of PLA, but the crystallinity of PLA could be increased from 0.3% to 2.0% and 1.9%, respectively, by adding ARP and WF. At 20 °C, the storage modulus of ARP/PLA, WF/PLA and RSP/PLA was 2759.4 MPa, 3361.3 MPa, and 2691.5 MPa, respectively, indicating that WF/PLA has the greatest stiffness, and the stiffness of RSP/PLA was the least. In addition to these, all the biocomposites were hydrophilic, the contact angle of the distilled water on the surface of ARP/PLA, WF/PLA or RSP/PLA was correspondingly 73.5°, 77.6° and 71.2°. Overall, it can be concluded that ARP/PLA has moderate strengths, stiffness and wettability, meanwhile, it is the most thermal stable among the three biocomposites, and can be processed at a temperature close to that of PLA. ARP/PLA is suitable as a new kind of feedstock material for FDM 3D printing. Full article

To develop a new kind of environment-friendly composite filament for fused deposition modeling (FDM) 3D printing, rice straw powder (RSP)/poly(lactic acid) (PLA) biocomposites were FDM-3D-printed, and the effects of the particle size and pretreatment of RSP on the properties of RSP/PLA biocomposites were investigated. The results indicated that the 120-mesh RSP/PLA biocomposites (named 120#RSP/PLA) showed better performance than RSP/PLA biocomposites prepared with other RSP sizes. Infrared results showed that pretreatment of RSP by different methods was successful, and scanning electron microscopy indicated that composites prepared after pretreatment exhibited good interfacial compatibility due to a preferable binding force between fiber and matrix. When RSP was synergistically pretreated by alkaline and ultrasound, the composite exhibited a high tensile strength, tensile modulus, flexural strength, and flexural modulus of 58.59, 568.68, 90.32, and 3218.12 MPa, respectively, reflecting an increase of 31.19%, 16.48%, 18.75%, and 25.27%, respectively, compared with unmodified 120#RSP/PLA. Pretreatment of RSP also improved the thermal stability and hydrophobic properties, while reducing the water absorption of 120#RSP/PLA. This work is believed to provide highlights of the development of cost-effective biocomposite filaments and improvement of the properties of FDM parts. Full article