Search Results (6)

This study focuses on the preparation and characterization of zinc-based alloys containing magnesium, calcium, and manganese. The alloys were prepared by the melting of pure elements, casting them into graphite molds, and thermo-mechanically treating them via hot extrusion. The phase compositions of the samples were analyzed using X-ray diffraction technique and SEM/EDX analysis. The analysis confirmed that in addition to the Zn matrix, the materials are reinforced by the CaZn₁₃, MgZn_2, and Mn-based precipitates. The mechanical properties of the alloys were ascertained by tensile, compressive, and bending tests, measurement of the samples microhardness and elastic modulus. The results indicate that an increase in Mn content leads to an increase in the maximum stress experienced under both tension and compression. However, the plastic deformation of the alloys decreases with increasing Mn content. This study provides valuable insights into the microstructural changes and mechanical behavior of zinc-based alloys containing magnesium, calcium, and manganese, which can be used to design alloys for specific biomedical applications. Full article

Magnesium is the eighth-most abundant element in the world and its alloys have a widespread application in various industries such as electronic and transport (i.e., air, land, and sea) engineering, due to their significant mechanical properties, excellent machinability, high strength to weight ratios, and low cost. Although monolithic Mg metal is known as the lightest industrial metal (magnesium density is 30% less than the density of the aluminum, and this unique property increases the attractiveness of its usage in the transportation industry), one of the significant limitations of magnesium, which affects on its applications in various industries, is very high reactivity of this metal (magnesium with an electronegativity of 31.1 can give electrons to almost all metals and corrodes quickly). To overcome this problem, scholars are trying to produce magnesium (Mg) alloys that are more resistant to a variety of loads and environmental conditions. In this regard, Mg alloys include well-known materials such as aluminum (Al), Zinc (Zn), Manganese (Mn), Silicon (Si), and Copper (Cu), etc., and their amount directly affects the properties of final products. In the present review paper, the authors attempted to present the latest achievements, methods, and influential factors (finish-rolling, pore defects, pH value, microstructure, and manufacturing processes, etc.) on the fatigue life and corrosion resistance of most significant Mg alloys, including AM50, AM60, AZ31, AZ61, AZ80, AZ91, ZK60, and WE43, under various conditions. The summarized results and practical hints presented in this paper can be very useful to enhance the reliability and quality of Mg-made structures. Full article

Zinc (Zn) and its alloys have been regarded as promising biodegradable metals. The standardized cytotoxicity evaluation is a mandatory step to screen the biocompatibility of novel Zn and its alloys. Nevertheless, the suitability of the tetrazolium-based assay in the direct contact test for some metallic biomaterials (i.e., magnesium and manganese) is questionable. In this study, our results demonstrate an obvious inconsistency between qualitative observation via fluorescence staining and quantitative assessment using water-soluble tetrazolium salt (CCK-8). Subsequent experiments revealed that Zn and pre-treated Zn can directly convert tetrazolium salts to formazan, falsifying the cytotoxicity results. Therefore, we conclude that the CCK-8 assay is not suitable for evaluating the cytotoxicity of biodegradable Zn-based metals in the direct contact test. Full article

Newly developed Zn-Mn-Mg alloys can be invoked as biomedical materials because of their excellent mechanical properties. However, the corrosion behavior of Zn-Mn-Mg alloys was still lacking in research. It had grown to be a hot research topic to improve the corrosion behavior of Zn alloys by surface treatment to meet the application of degradable Zn alloys in biomedical applications. Micro arc oxidation (MAO) is a simple and effective method to improve the corrosion behavior of the alloy. MAO coatings were successfully prepared on the surface of Zn-Mn-Mg alloys by MAO in silicate-based solutions with different NaF concentrations. The microstructure and phase composition of MAO coatings prepared on Zn-Mn-Mg alloys with different NaF concentrations in the electrolyte was examined by a scanning electron microscope and X-ray diffraction. The results showed that the MAO coatings are porous and mainly composed of ZnO. With the increasing NaF concentration in the electrolyte, the average thickness increases. The distribution of the micro/nanopores was uniform, and the pore size ranged from the submicron scale to several micrometers after MAO treatment in the electrolyte containing different concentrations of NaF. Potential dynamic polarization curves and electrochemical impedance spectroscopy were employed to assess the corrosion behavior of MAO coatings in Hank’s solution. The highest corrosion rate can be achieved after MAO treatment, with an electrolyte concentration of 1.5 g/L NaF in Hank’s solution. These results indicated that MAO coating can accelerate the corrosion resistance of a Zn-Mn-Mg alloy. Full article

The present study examined the in vitro and in vivo bone formation and adhesion ability on the surface of a titanium dental implant made by plasma electrolytic oxidation (PEO) in electrolytes containing bioactive ions. To achieve this goal, screw-shaped fabricated Ti-6Al-4V alloy implants were processed via PEO using an electrolyte solution containing calcium (Ca), phosphorous (P), magnesium (Mg), zinc (Zn), strontium (Sr), silicon (Si), and manganese (Mn) species. The screw implants doped with bioactive elements via PEO were placed in rabbit tibia, and the results were compared to the sand-blasted Ti-6Al-4V alloy implants. At eight-week post-surgery, there was no significant difference in the values of removal torque between sand-blasted and PEO-treated implants. However, it was observed that the PEO treatment of dental implants led to the formation of more periphery bone as compared to the case of sand-blasted implants. Accordingly, the PEO-treated implants have the potential to be used as promising materials for dental applications. Full article

Magnesium based nanocomposites, due to their excellent dimensional stability and mechanical integrity, have a lot of potential to replace the existing commercial Al alloys and steels used in aerospace and automotive applications. Mg-Al alloys are commercially used in the form of AZ (magnesium-aluminum-zinc) and AM (magnesium-aluminum-manganese) series in automobile components. However, the Mg₁₇Al₁₂ phase in Mg-Al alloys is a low melting phase which results in a poor creep and high temperature performance of the alloys. Rare earth additions modify the phase and hence improve the properties of the materials. In this paper, Ce and nano ZnO particles were added to Mg-Al alloys to attain a favorable effect on their properties. The developed materials exhibited promising properties in terms of thermal expansion coefficient (CTE), hardness, and tensile strength. Further, the ZnO addition refined the microstructure and helped in obtaining a uniform distribution, however without grain size refinement. The increased addition of ZnO and the improvement in the distribution led to an enhancement in the properties, rendering the materials suitable for a wide spectrum of engineering applications. Full article