Next Article in Journal
Immobilization as a Strategy for Improving Enzyme Properties-Application to Oxidoreductases
Next Article in Special Issue
Chitosan-Coated Magnetic Nanoparticles Prepared in One-Step by Precipitation in a High-Aqueous Phase Content Reverse Microemulsion
Previous Article in Journal
Volatile Organic Compound Emissions from Different Stages of Cananga odorata Flower Development
Previous Article in Special Issue
Microwave Resonant and Zero-Field Absorption Study of Doped Magnetite Prepared by a Co-Precipitation Method
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 19
Issue 7
10.3390/molecules19078981
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

MAPLE Fabricated Fe3O4@Cinnamomum verum Antimicrobial Surfaces for Improved Gastrostomy Tubes

by
Alina Georgiana Anghel
1,2,
Alexandru Mihai Grumezescu
3,4,
Mariana Chirea
5,*,
Valentina Grumezescu
3,4,6,
Gabriel Socol
6,
Florin Iordache
7,
Alexandra Elena Oprea
3,
Ion Anghel
1,2 and
Alina Maria Holban
3,4,8
1
ENT, "Carol Davila" University of Medicine and Pharmacy, Traian Vuia no.6, Bucharest 020956, Romania
2
Doctor Anghel Medical Center, Theodor Sperantia Street, Bucharest 30932, Romania
3
Department of Science and Engineering of Oxide Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, Politehnica University of Bucharest, Polizu Street no 1-7, Bucharest 011061, Romania
4
AMG Transcend, Polizu Street no 1-7, Bucharest 011061, Romania
5
Departamento de Química Fisica, Universidade de Vigo, 36310 Vigo, Pontevedra, Spain
6
National Institute for Lasers, Plasma & Radiation Physics, Lasers Department, P.O. Box MG-36, Bucharest-Magurele, Bucharest 769231, Romania
7
Flow Cytometry and Cell Therapy Laboratory, Institute of Cellular Biology and Pathology "Nicolae Simionescu" (ICBP), Bucharest 050568, Romania
8
Microbiology Immunology Department, Faculty of Biology, University of Bucharest, AleeaPortocalelor no 1-3, Bucharest 060101, Romania
*
Author to whom correspondence should be addressed.
Molecules 2014, 19(7), 8981-8994; https://doi.org/10.3390/molecules19078981
Submission received: 20 May 2014 / Revised: 14 June 2014 / Accepted: 23 June 2014 / Published: 27 June 2014
(This article belongs to the Special Issue Bio and Nanomaterials Based on Fe3O4)
Browse Figures
Versions Notes

Abstract

:
Cinnamomum verum-functionalized Fe3O4 nanoparticles of 9.4 nm in size were laser transferred by matrix assisted pulsed laser evaporation (MAPLE) technique onto gastrostomy tubes (G-tubes) for antibacterial activity evaluation toward Gram positive and Gram negative microbial colonization. X-ray diffraction analysis of the nanoparticle powder showed a polycrystalline magnetite structure, whereas infrared mapping confirmed the integrity of C. verum (CV) functional groups after the laser transfer. The specific topography of the deposited films involved a uniform thin coating together with several aggregates of bio-functionalized magnetite particles covering the G-tubes. Cytotoxicity assays showed an increase of the G-tube surface biocompatibility after Fe3O4@CV treatment, allowing a normal development of endothelial cells up to five days of incubation. Microbiological assays on nanoparticle-modified G-tube surfaces have proved an improvement of anti-adherent properties, significantly reducing both Gram negative and Gram positive bacteria colonization.

Graphical Abstract

1. Introduction

Patients who are unable to move food from their mouth to their stomach such as patients suffering of neurological disorders (stroke, brain injury, amyotrophic lateral sclerosis, and impaired swallowing), as well as patient with trauma, cancer or other severe infections in the upper gastrointestinal or the respiratory tract need an alternative solution for nutrition intake.
The percutaneous endoscopic gastrostomy (PEG) technique or gastrostomy tube (G-tube) is a method of placing a tube into the stomach percutaneously, assisted by endoscopy and allowing nutrition intake in these debilitated patients [1]. G-tubes are becoming increasingly more common to provide nutrition to patients due to their decreased risk of aspiration, usually associated with nasogastric tubes [2]. The most common complications associated with G-tube placement range from minor bleeding and poor comfort to wound infections, necrotizing fasciitis and colocutaneous fistula [3]. The reported rates of complications following G-tube placement vary from 16% to 70% [3].
Being in contact with patients’ normal microbiota, medical implanted prostheses are prone to be colonized by bacteria [4]. The failure of such devices relies on the ability of microorganisms to attach on their surfaces and form highly specialized communities called biofilms, which are extremely resistant to host defence mechanisms and antibiotic treatment [5]. Medical biofilms colonizing the surface of prosthetic devices are the cause of 60%–85% of total human acute or chronic infections and the most frequent cause of device surgical removal, associated with additional costs and patients’ discomfort [6] The microbial species of clinical interest, often involved in biofilm associated infections belong to a very wide spectrum, from Gram positive (Staplylococcus aureus and S. epidermidis) to Gram negative pathogens (Escherichia coli and Pseudomonas aeruginosa) and to different members of the Candida genus (particularly C. albicans and C. parapsilosis) [7].
Conventional treatments for device-associated infections typically consist of long-term therapy with a combination of antibiotics, which may lead to side effects and contribute to low patient compliance. Significantly, the increasing emergence of drug resistance to commonly used antibiotics and antifungal has made critical the need for the identification of novel therapeutics and approaches [8,9].
Recent advances in nanotechnology research have demonstrated that bio-functionalized nanomaterials can be used successfully for antibacterial protection of medical devices [10,11,12,13,14,15,16,17,18,19]. This protection of medical devices is easily achieved by directly coating the medical devices with a bio-active antimicrobial film [20,21]. The use of synthetic drugs for antibacterial treatment of medical devices is always accompanied by severe side effects (i.e., high toxicity and low biodegradability, increased bacterial resistance rates) and elimination of these side effects is achievable by using natural products with proved antimicrobial activity [22,23,24,25,26,27]. Plant extracts and essential oils with complex medicinal properties represent a great choice for the development of antimicrobial therapies [28,29,30,31,32,33]. The only drawbacks of these natural products are their low stability and high volatility. The functionalization of biocompatible nanoparticles with these essential oils or plant extracts would provide the means to both increase their stability and decrease their volatility [34,35,36].
In this work, we present the bio-functionalization of magnetic nanoparticles with Cinnamomum verum (CV) and their use for fabrication of protective antibacterial coatings of G-tubes. C. verum contains two antioxidants: proanthocyanidins and cinnamaldehyde (a phenolic compound), the latter being a very powerful anti-inflammatory compound. The most important medicinal properties of C. verum oil are: it stimulates the immune system, it is a general anti-inflammatory oil, extremely powerful antioxidant, major broad-spectrum antibiotic, antiseptic, antifungal and antiviral. It also helps prevent stomach, colon, lung, and breast cancers. Its many uses are known from Traditional Chinese Medicine. It is expected that the bio-functionalization of Fe3O4 nanoparticles with C. verum will lead to the formation of films with strong anti-inflammatory and antibacterial activity and few or no side effects. The fabrication of these films was achieved by matrix assisted pulsed laser evaporation (MAPLE), a technique frequently used for film deposition on substrates [37,38,39,40,41]. MAPLE allows a better control of the film thickness and surface morphology, enhances film/substrate adhesion, facilitates the multi-layer deposition and patterning. Furthermore, being a non-contact procedure it eliminates a major source of contamination and it can be integrated with other sterile processes. The bacterial species under study in this work were a Gram positive one, S. aureus and a Gram negative one, E. coli, which are the most frequent etiologies for severe and persistent infections associated with G-tube implantation.

2. Results and Discussion

Details concerning the method used for magnetite synthesis and procedure for their deposition on G-tubes are presented in the Experimental Section. The morphology and crystallinity of the synthesized magnetite nanoparticles was analysed by TEM, SEM and X-ray diffraction measurements (Figure 1 and Figure 2). The Fe3O4-CV particles were monodisperse, with an average diameter of 9.4 ± 1.0 nm as determined from TEM images (results not shown here). The Fe3O4-CV powder was polycrystalline with diffraction peaks at: 30.368°, 35.748°, 43.368°, 53.718°, 57.218° and 62.778° which correspond to (2 2 0), (3 1 1), (4 0 0), (4 2 2), (5 1 1) and (4 4 0) reflection planes of fcc magnetite [42]. The peaks of Fe3O4-CV indexed in Figure 2 match with the standard pattern of Fe3O4 (ICDD card No. 19-0629).
The chemical composition and surface coverage of Fe3O4@CV films on G-tubes were evaluated by IR–mapping and SEM imaging (Figure 3, Figure 4, Figure 5, Figure 6 and Figure 7). FT-IR spectral analysis of modified surfaces is very complicated because the absorption peaks often overlap with each other. This inconvenience is eliminated by using second derivative spectroscopy, a technique which enhances the separation of overlapping peaks [43]. For this purpose, second derivative IR-maps were recorded (an average of 250 IR spectra) on Fe3O4@CV films obtained in various conditions of MAPLE deposition, namely, at 300 mJ/cm2, 400 mJ/cm2 and 500 mJ/cm2 laser fluences (Figure 3, Figure 4 and Figure 5).
Molecules 19 08981 g001 550
Figure 1. High resolution SEM images of the Fe3O4@CV powder.
Figure 1. High resolution SEM images of the Fe3O4@CV powder.
Molecules 19 08981 g001
Molecules 19 08981 g002 550
Figure 2. XRD pattern of Fe3O4 and Fe3O4@CV.
Figure 2. XRD pattern of Fe3O4 and Fe3O4@CV.
Molecules 19 08981 g002
Molecules 19 08981 g003 550
Figure 3. Second derivate IR mappings and IR spectra of thin coating (F = 300 mJ/cm2) surface: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Figure 3. Second derivate IR mappings and IR spectra of thin coating (F = 300 mJ/cm2) surface: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Molecules 19 08981 g003
Molecules 19 08981 g004 550
Figure 4. Second derivate IR mappings and IR spectra of thin coating (F = 400 mJ/cm2) surface: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Figure 4. Second derivate IR mappings and IR spectra of thin coating (F = 400 mJ/cm2) surface: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Molecules 19 08981 g004
Molecules 19 08981 g005 550
Figure 5. Second derivate IR mappings and IR spectra of thin coating (F = 500 mJ/cm2) surface: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Figure 5. Second derivate IR mappings and IR spectra of thin coating (F = 500 mJ/cm2) surface: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Molecules 19 08981 g005
In order to verify if the MAPLE deposited films were chemically intact, the obtained IR maps were compared to drop-casted Fe3O4@CV films on G-tubes (Figure 6). The IR maps show colour changes, starting from blue (the lowest intensity) and gradually increasing to red (the highest intensity) which illustrate a high degree of film purity and chemical stability [44].
Molecules 19 08981 g006 550
Figure 6. Second derivate IR mappings and IR spectra of Fe3O4@CV dropcasted on substrate: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Figure 6. Second derivate IR mappings and IR spectra of Fe3O4@CV dropcasted on substrate: intensity distribution of (a) 2815 cm−1 and (b) 1689 cm−1.
Molecules 19 08981 g006
Molecules 19 08981 g007 550
Figure 7. Backscattered electron image ofFe3O4@CV thin coating prepared by MAPLE.
Figure 7. Backscattered electron image ofFe3O4@CV thin coating prepared by MAPLE.
Molecules 19 08981 g007
As it can be observed and compared in Figure 3, Figure 4, Figure 5 and Figure 6, the optimal deposition rate and stoichiometric transfer was achieved at a fluence deposition of 400 mJ/cm2, the IR spectra of this MAPLE deposition showing similar features as the ones obtained for the drop-casted Fe3O4@CV films.
The characteristic peaks of the Fe3O4@CV were assigned to: (a) 2815 cm−1 (C-H stretch) and (b) 1689 cm−1 (C=O carbonyl group). The selected functional groups are characteristics to the C. verum (i.e., cinnamaldehyde). The surface coverage of Fe3O4@CV film on G-tubes deposited at 400 mJ/cm2 laser fluence and its topography were analysed by scanning electron microscopy (Figure 7). Both, very uniform surface coverage with Fe3O4@CV nanoparticles being well dispersed together with several aggregates were observed on the modified G-tubes (Figure 7). These results are in good agreement with reported literature on the MAPLE thin coatings of iron oxide nanoparticles [45].
Cytotoxicity assays revealed an improvement of the modified Fe3O4@CV G-tube surface biocompatibility with respect to the bare G-tube.
The MTT assay demonstrated that human cells present a normal metabolism and growth in the presence of nanoparticle modified bioactive G-tubes, the measured values of absorbance at 570 nm being similar for modified and control surfaces in the first 48 h of incubation. Furthermore, after 72 h of incubation, endothelial cells showed a better proliferation on Fe3O4@CV G-tube surfaces, as compared with the control surfaces (Figure 8).
Molecules 19 08981 g008 550
Figure 8. Graphic representation of the MTT results obtained by analyzing endothelial cells grown in the presence of control (uncoated G-tube) and Fe3O4@CVmodified G-tube surfaces for 24, 48 and 72 h.
Figure 8. Graphic representation of the MTT results obtained by analyzing endothelial cells grown in the presence of control (uncoated G-tube) and Fe3O4@CVmodified G-tube surfaces for 24, 48 and 72 h.
Molecules 19 08981 g008
Florescence microscopy results obtained after 5 days of incubation have revealed that endothelial cells grown on the nanoparticle modified bioactive surfaces present a normal aspect, their morphology being similar with the cells grown on control surfaces (Figure 9).
Molecules 19 08981 g009 550
Figure 9. Fluorescence microscopy images of endothelial cells grown in the presence of Fe3O4@CV modified (a) and on control G-tube surfaces (b) after 5 days of incubation.
Figure 9. Fluorescence microscopy images of endothelial cells grown in the presence of Fe3O4@CV modified (a) and on control G-tube surfaces (b) after 5 days of incubation.
Molecules 19 08981 g009
The percentage of attached cells was normal for this incubation time and low detachment rates were noted. Our data revealed that the nanoparticle modified G-tube surfaces have improved anti-adherent properties, considerably reducing both Gram negative and Gram positive bacteria colonization. The phenotypical data demonstrate that biofilms formation is impaired at all tested time points, starting with their initiation and continuing through the maturation process.
The most significant differences were observed on S. aureus biofilms; in this case, the biofilm inhibition rates ranging from more than 4-fold for incipient biofilms to up to 3-fold for mature biofilms (Figure 10). On the other hand, for the Gram negative bacterium E. coli the biofilm inhibition ranged from 2.5-fold for initial biofilms to up to 2-fold for mature biofilms grown onto the bioactive Fe3O4@CVmodified G-tube surface (Figure 11).
Molecules 19 08981 g010 550
Figure 10. S. aureus biofilms formation on ordinary (bare) and bioactive nanoparticle modified G-tubes for 24, 48 and 72 h of incubation at 37 °C.
Figure 10. S. aureus biofilms formation on ordinary (bare) and bioactive nanoparticle modified G-tubes for 24, 48 and 72 h of incubation at 37 °C.
Molecules 19 08981 g010
Molecules 19 08981 g011 550
Figure 11. E. coli biofilms formation on ordinary (bare) and bioactive nanoparticle modified G-tubes for 24, 48 and 72 h of incubation at 37 °C.
Figure 11. E. coli biofilms formation on ordinary (bare) and bioactive nanoparticle modified G-tubes for 24, 48 and 72 h of incubation at 37 °C.
Molecules 19 08981 g011

3. Experimental

3.1. Synthesis of Fe3O4@CV

Fe3O4 nanoparticles functionalized with C. verum were prepared as follow: NH4OH solution (25%, 8 mL) was added into a 0.25% solution of C. verum (200 mL). Then, a solution of Fe3+ and Fe2+ in 2:1 molar ratio was prepared (400 mL), mixed for 10 min and consecutively added dropwise to the basic solution of C. verum. A black precipitate was obtained consisting of C. verum functionalized magnetite nanoparticles (Fe3O4@CV) which were isolated from solution using a 100 kgf Nd-Fe-B external magnetic field. The Fe3O4@CV nanoparticles were purified by washing three times with Millipore water until the pH was near neutral.

3.2. MAPLE Target Preparation and Deposition of Fe3O4@CV-Based Thin Coating

Fe3O4@CV nanoparticles were dispersed in DMSO as a 1.5% (w/v) solution. The MAPLE solutions were poured into a pre-cooled target holder and subsequently immersed in liquid nitrogen for 30 min. MAPLE depositions was performed using a KrF* (λ = 248 nm and τFWHM = 25 ns) COMPexPro 205 model laser source (Lambda Physics-Coherent, Ft. Lauderdale, FL, USA) that operated at a repetition rate of 15 Hz. The laser fluence was within the range of (300–500) mJ/cm2 whereas the laser spot area was set to 36 mm2. A laser beam homogenizer was used to improve the energy distribution of the laser spot. In order to avoid the target heating and drilling during the laser irradiation, the frozen target was rotated at a rate of 0.4 Hz. All depositions were conducted at room temperature into a background pressure of 1 Pa and the films were grown at a target-substrate separation distance of 5 cm by applying (30,000–60,000) subsequent laser pulses. During the deposition process, the target was kept at a temperature of ~173 K by active liquid nitrogen cooling. Thin films were deposited onto double side polished (100) silicon, glass and gastrostomy tubes (obtained from Doctor Anghel Medical Center) for IRM, SEM, XRD and biological assays, respectively. Prior to introduction inside the deposition chamber, the substrates were successively cleaned into an ultrasonic bath with acetone, ethanol and deionized water for 15 min. During the deposition, the substrates were continuously rotated. Thus, the Fe3O4@CV nanoparticles were uniformly spread over the surface of the substrates. For data comparison, a control set of films were prepared by drop casting on the double side polished (100) silicon.

3.3. Characterization of Fe3O4@CV and Prepared Thin Coating

3.3.1. XRD

X-ray diffraction analysis was performed on a Shimadzu XRD 6000 diffractometer (Kyoto, Japan) at room temperature. In all the cases, Cu Kα radiation from a Cu X-ray tube (run at 15 mA and 30 kV) was used. The samples were scanned in the Bragg angle 2θ range of 10–80 degree.

3.3.2. IRM

IR mapping were recorded on a Nicolet iN10 MX FT-IR Microscope (Waltham, MA, USA) with MCT liquid nitrogen cooled detector in the measurement range 4000–700 cm−1. Spectral collection was made in reflection mode at 4 cm−1 resolution. For each spectrum, 32 scans were co-added and converted to absorbance using OmincPicta software (Thermo Scientific, Waltham, MA USA). Approximately 250 spectra were analysed for each sample. Two absorptions peaks known as being characteristics for the Fe3O4@CV nanoparticles were selected as spectral markers.

3.3.3. SEM

SEM analysis was performed on a FEI electron microscope (Hillsboro, OR, USA), using secondary electron beams with energies of 30 keV, on samples covered with a thin silver layer.

3.3.4. Interaction with Eukaryotic Cells

Human endothelial cells (EAhy926 cell line, American Type Culture Collection ‒ ATCC, Manassas, VA, USA) were grown in DMEM culture medium containing 10% FBS, and 1% penicillin and neomycin (Sigma Aldrich, St. Louis, MO, USA). For cell proliferation and viability was used CellTiter96 Non-Radioactive Cell Proliferation Assay, (Promega, Madison, WI, USA). Endothelial cells were seeded in 96-well plate at a density of 5 × 103 cells/well, in DMEM medium, supplemented with 10% FBS and incubated with NMS materials for 72 h, while the controls were represented by endothelial cells grown in the same culture conditions, but on bare substrates. Cell proliferation assay was performed in triplicates, according to manufacturer’s guidelines, at different time intervals. Briefly, Promega Kit Solution I (15 µL) was added in each well and incubated for 4 h. Furthermore, Promega Kit Solution II (100 µL) was added in the 96-well plate and incubated for another hour and spectrophotometry measurements were performed at 570 nm using a Mithras LB 940 spectrophotometer (Berthold Technology, Bad Wildbad, Germany).
RED CMTPX fluorophore (Life Technologies, Invitrogen, Antisel, Bucharest, Romania) is a cell tracker for long-term tracing of living cells. The RED CMTPX dye was added in the culture medium at a final concentration of 5 µM, incubated 30 min for the dye to penetrate through the cells. Furthermore, the cells were washed with PBS and visualized by fluorescent microscopy. Living cells tracing in the presence of thin coating was monitored for 5 days in culture. The micrographs were taken by a digital camera driven by the Axio-Vision 4.6 (Carl Zeiss, Oberkochen, Germany) software.

3.3.5. Interaction with Prokaryotic Cells

Staphylococcus aureus ATCC 25922 and Escherichia coli ATCC 25922 strains were purchased from the ATCC and used to create an artificial biofilm. Both adherence and biofilm formation were analysed in 6 multi-well plates (Nunc, Waltham, MA, USA), using a static model for monospecific biofilms. The tested slides pieces (control and MAPLE coated glass slides) were placed in 2 mL nutrient broth inoculated with 5 µL of S. aureus or E. coli suspension with a density of 0.5 McFarland (1–3 × 108 CFU/mL). After 24 h of incubation, the adherence was assessed by harvesting the adhered cells in sterile phosphate buffered saline (PBS), following the viable cell count assay. The temporal dynamic of biofilm formation was studied by placing the tested slides with attached bacterial cells in nutrient broth and incubation for 24, 48 and 72 h. After incubation, the biofilm developed on the control and test surfaces were harvested and suspensions were performed in sterile PBS (phosphate saline buffer). The obtained suspensions were further ten-fold diluted and 10 µL of each dilution were seeded in triplicates on nutritive agar (Durham, NC, USA), incubated for 24 h at 37 °C in order to determine the viable cell counts and thus, indirectly, to evaluate the number of viable bacterial cells embedded in biofilms. Experiments were performed in triplicate and repeated on three separate occasions.

4. Conclusions

Thin films composed of 9.4 nm Cinnamomum verum-functionalized Fe3O4 particles were successfully transferred onto G-tubes by laser processing. The in vitro results recommend this type of coating for medical use, especially as a medical surface with high resistance to microbial colonization. The good biocompatibility of the Fe3O4-CV films suggests that they can be safely used for the antibacterial protection of medical surfaces and devices to be used for different patients with debilitating diseases.

Acknowledgments

The work has been supported by the Sectoral Operational Programme Human Resources Development 2007-2013 of the Ministry of European Funds through the Financial Agreement POSDRU/159/1.5/S/132397 (ExcelDOC).

Author Contributions

AMG and IA conceived the study; AMH and AGA provided the microbial strains, and drafted the manuscript together with MC, GS and AMG. AMG, VG, GS, AEO and MC performed the synthesis, laser processing and characterization of Fe3O4@CV. AGA, AMH and FI performed the in vitro experiments. AMG, MC and IA participated in the design of the study and coordination. All authors read and approved the final manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Locher, J.L.; Bonner, J.A.; Carroll, W.R.; Caudell, J.J.; Keith, J.N.; Kilgore, M.L.; Ritchie, C.S.; Roth, D.L.; Tajeu, G.S.; Allison, J.J. Prophylactic percutaneous endoscopic gastrostomy tube placement in treatment of head and neck cancer: A comprehensive review and call for evidence-based medicine. J. Parenter. Enter. Nutr. 2011, 35, 365–374. [Google Scholar] [CrossRef]
  2. Keung, E.Z.; Liu, X.; Nuzhad, A.; Rabinowits, G.; Patel, V. In-hospital and long-term outcomes after percutaneous endoscopic gastrostomy in patients with malignancy. J. Am. Coll. Surg. 2012, 215, 777–786. [Google Scholar] [CrossRef]
  3. Blomberg, J.; Lagergren, J.; Martin, L.; Mattsson, F.; Lagergren, P. Complications after percutaneous endoscopic gastrostomy in a prospective study. Scand. J. Gastroenterol. 2012, 47, 737–742. [Google Scholar] [CrossRef]
  4. Beech, I.B.; Sunner, J.A.; Arciola, C.R.; Cristiani, P. Microbially-influenced corrosion: Damage to prostheses, delight for bacteria. Int. J. Artif. Org. 2006, 29, 443–452. [Google Scholar]
  5. Lazar, V. Quorum sensing in biofilms: How to destroy the bacterial citadels or their cohesion power? Anaerobe 2011, 17, 280–285. [Google Scholar] [CrossRef]
  6. Vickery, K.; Hu, H.; Jacombs, A.S.; Bradshaw, D.A.; Deva, A.K. A review of bacterial biofilms and their role in device-associated infection. Healthc. Infect. 2013, 18, 61–66. [Google Scholar] [CrossRef]
  7. Holban, A.M.; Cartelle Gestal, M.; Grumezescu, A.M. New molecular strategies for reducing implantable medical devices associated infections. Curr. Med. Chem. 2014. [Google Scholar] [CrossRef]
  8. Anghel, I.; Grumezescu, A.M.; Holban, A.M.; Ficai, A.; Anghel, A.G.; Chifiriuc, M.C. Biohybrid nanostructured iron oxide nanoparticles and Satureja hortensis to prevent fungal biofilm development. Int. J. Mol. Sci. 2013, 14, 18110–18123. [Google Scholar]
  9. Tran, N.; Tran, P.A. Nanomaterial-Based treatments for medical device-associated infections. ChemPhysChem 2012, 13, 2481–2494. [Google Scholar]
  10. Grumezescu, A.M. Improved wound dressings: Novel approaches. Int. J. Pharm. 2014, 463, 117–118. [Google Scholar] [CrossRef]
  11. Anghel, I.; Grumezescu, A.M.; Holban, A.M.; Gheorghe, I.; Vlad, M.; Anghel, G.A.; Balaure, P.C.; Chifiriuc, C.M.; Ciuca, I.M. Improved activity of aminoglycosides entrapped in silica networks against microbial strains isolated from otolaryngological infections. Farmacia 2014, 62, 69–78. [Google Scholar]
  12. Grumezescu, A.M.; Andronescu, E.; Voicu, G.; Huang, K.-S.; Yang, C.-H.; Ficai, A.; Vasile, B.S.; Grumezescu, V.; Bleotu, C.; Chifiriuc, M.C. New silica nanostructure for the improved delivery of topical antibiotics used in the treatment of staphylococcal cutaneous infections. Int. J. Pharm. 2013, 476, 170–176. [Google Scholar]
  13. Anghel, I.; Grumezescu, A.M. Hybrid nano-structured coating for increased resistance of prosthetic devices to staphylococcal colonization. Res. Lett. 2013, 8. [Google Scholar] [CrossRef]
  14. Anghel, I.; Holban, A.M.; Grumezescu, A.M.; Andronescu, E.; Ficai, A.; Anghel, A.G.; Maganu, M.; Lazar, V.; Chifiriuc, M.C. Modified wound dressing with phyto-nanostructured coating to prevent staphylococcal and pseudomonal biofilms development. Nanoscale Res. Lett. 2012, 7, 690. [Google Scholar] [CrossRef]
  15. Colonna, C.; Dorati, R.; Conti, B.; Caliceti, P.; Genta, I. Sub-unit vaccine against S. aureus-mediated infections: Set-up of nano-sized polymeric adjuvant. Int. J. Pharm. 2013, 452, 390–401. [Google Scholar]
  16. Nafee, N.; Youssef, A.; El-Gowelli, H.; Asem, H.; Kandil, S. Antibiotic-free nanotherapeutics: Hypericin nanoparticles thereof for improved in vitro and in vivo antimicrobial photodynamic therapy and wound healing. Int. J. Pharm. 2013, 454, 249–258. [Google Scholar] [CrossRef]
  17. Tan, S.P.; McLoughlin, P.; O’Sullivan, L.; Prieto, M.L.; Gardiner, G.E.; Lawlor, P.G.; Hughes, H. Development of a novel antimicrobial seaweed extract-based hydrogel wound dressing. Int. J. Pharm. 2013, 456, 10–20. [Google Scholar]
  18. Belcarz, A.; Zima, A.; Ginalska, G. Biphasic mode of antibacterial action of aminoglycoside antibiotics-loaded elastic hydroxyapatite–glucan composite. Int. J. Pharm. 2013, 454, 285–295. [Google Scholar] [CrossRef]
  19. Echezarreta-López, M.M.; Landin, M. Using machine learning for improving knowledge on antibacterial effect of bioactive glass. Int. J. Pharm. 2013, 453, 641–647. [Google Scholar] [CrossRef]
  20. Grumezescu, A.M. Novel strategies to eradicate bacterial communities based on nano and biomaterials. Curr. Org. Chem. 2014, 18, 151. [Google Scholar]
  21. Anghel, I.; Grumezescu, V.; Andronescu, E.; Anghel, G.A.; Grumezescu, A.M.; Mihaiescu, D.E.; Chifiriuc, M.C. Protective effect of magnetite nanoparticle/Salvia officinalis essential oil hybrid nanobiosystem against fungal colonization on the Provox® voice section prosthesis. Dig. J. Nanomater. Bios. 2012, 7, 1205–1212. [Google Scholar]
  22. Grumezescu, A.M.; Saviuc, C.; Chifiriuc, C.M.; Hristu, R.; Mihaiescu, D.E.; Balaure, P.; Stanciu, G.; Lazar, V. Inhibitory activity of Fe3O4/Oleic acid/usnic acid—Core/shell/extra-shell nanofluid on S. aureus biofilm development. IEEE Trans. NanoBiosci. 2011, 10, 269–274. [Google Scholar] [CrossRef]
  23. Grumezescu, A.M.; Andronescu, E.; Albu, M.G.; Ficai, A.; Dragu, D. Wound dressing based collagen biomaterials containing usnic acid as quorum sensing inhibitor agent: Synthesis, characterization and bioevaluation. Curr. Org. Chem. 2013, 17, 125–131. [Google Scholar] [CrossRef]
  24. Grumezescu, A.M.; Cotar, A.I.; Andronescu, E.; Ficai, A.; Ghitulica, C.D.; Grumezescu, V.; VasileB, S.; Chifiriuc, M.C. In vitro activity of the new water dispersible Fe3O4@usnic acid nanostructure against planktonic and sessile bacterial cells. J. Nanopart. Res. 2013, 15, 1766. [Google Scholar]
  25. Holban, A.M.; Grumezescu, A.M.; Andronescu, E.; Grumezescu, V.; Chifiriuc, C.M.; Radulescu, R. Magnetite-usnic acid nanostructured bioactive material with antimicrobial activity. Rom. J. Mater. 2013, 43, 402–407. [Google Scholar] [CrossRef]
  26. Mihaiescu, D.E.; Grumezescu, A.M.; Buteica, A.S.; Mogosanu, D.E.; Balaure, P.C.; Mihaiescu, O.M.; Trăistaru, V.; Vasile, B.S. Bioassay and electrochemical evaluation of controlled release behavior of cephalosporins from magnetic nanoparticles. Dig. J. Nanomater. Bios. 2012, 7, 253–260. [Google Scholar]
  27. Grumezescu, V.; Holban, A.M.; Grumezescu, A.M.; Socol, G.; Ficai, A.; Vasile, B.S.; Trusca, R.; Bleotu, C.; Lazar, V.; Chifiriuc, C.M.; et al. Usnic acid loaded biocompatible magnetic PLGA-PVA microspheres thin films fabricated by MAPLE with increased resistance to staphylococcal colonization. Biofabrication 2014, 6, 035002. [Google Scholar] [CrossRef]
  28. Saviuc, C.M.; Grumezescu, A.M.; Bleotu, C.; Holban, A.M.; Chifiriuc, M.C.; Balaure, P.; Lazar, V. Culture methods versus flow cytometry for the comparative assessment of antifungal activity of Eugenia caryophyllata thunb. (Myrtaceae) essential oil. Farmacia 2013, 61, 912–919. [Google Scholar]
  29. Grumezescu, A.M.; Andronescu, E.; Ficai, A.; Voicu, G.; Cocos, O.; Chifiriuc, M.C. Eugenia cayophyllata essential oil-SiO2 biohybrid structure for the potentiation of antibiotics activity. Rom. J. Mater. 2013, 43, 160–166. [Google Scholar]
  30. Saviuc, C.; Cotar, A.I.; Holban, A.M.; Banu, O.; Grumezescu, A.M.; Chifiriuc, M.C. Phenotypic and molecular evaluation of Pseudomonas aeruginosa and Staphylococcus aureusvirulence patterns in the presence of some essential oils and their major compounds. Lett. Appl. NanoBiosci 2013, 2, 91–96. [Google Scholar]
  31. Saviuc, C.; Holban, A.M.; Grumezescu, A.M.; Bleotu, C.; Banu, O.; Lazar, V.; Mihaiescu, D.E.; Chifiriuc, M.C. Testing antifungal activity of some essential oils using flow cytometry. Lett. Appl. NanoBiosci. 2012, 1, 67–71. [Google Scholar]
  32. Charernsriwilaiwat, N.; Rojanarata, T.; Ngawhirunpat, T.; Sukma, M.; Opanasopit, P. Electrospun chitosan-based nanofiber mats loaded with Garcinia mangostana extracts. Int. J. Pharm. 2013, 452, 333–343. [Google Scholar] [CrossRef]
  33. Song, J.; Bi, H.; Xie, X.; Guo, J.; Wang, X.; Liu, D. Natural borneol enhances geniposide ophthalmic absorption in rabbits. Int. J. Pharm. 2013, 445, 163–170. [Google Scholar] [CrossRef]
  34. Saviuc, C.; Grumezescu, A.M.; Banu, O.; Chifiriuc, C.; Mihaiescu, D.; Balaure, P.; Lazar, V. Biocompatible magnetic MWCNTs based on phytocomponents from Eugenia carryophyllata. Rev. Chim. Bucharest 2012, 63, 531–535. [Google Scholar]
  35. Saviuc, C.; Grumezescu, A.M.; Chifiriuc, M.C.; Mihaiescu, D.E.; Hristu, R.; Stanciu, G.; Oprea, E.; Radulescu, V.; Lazar, V. Hybrid Nanosystem for Stabilizing Essential Oils in Biomedical Applications. Dig. J. Nanomater. Bios. 2011, 6, 1657–1666. [Google Scholar]
  36. Anghel, I.; Holban, A.M.; Andronescu, E.; Grumezescu, A.M.; Chifiriuc, M.C. Efficient surface functionalization of wound dressings by a phytoactive nanocoating refractory to Candida albicans biofilm development. Biointerphases 2013, 8. [Google Scholar] [CrossRef]
  37. Wu, P.K.; Ringeisen, B.R.; Krizman, D.B.; Frondoza, C.G.; Brooks, M.; Bubb, D.M.; Auyeung, R.C.Y.; Piqué, A.; Spargo, B.; McGill, R.A.; et al. Laser transfer of biomaterials: Matrix-assisted pulsed laser evaporation MAPLEand MAPLE Direct Write. Rev. Sci. Instrum. 2003, 74, 2546–2557. [Google Scholar] [CrossRef]
  38. Caricato, A.P.; Luches, A. Applications of the matrix-assisted pulsed laser evaporation method for the deposition of organic, biological and nanoparticle thin films: A review. Appl. Phys. A 2011, 105, 565–582. [Google Scholar] [CrossRef]
  39. Cristescu, R.; Popescu, C.; Dorcioman, G.; Miroiu, F.M.; Socol, G.; Mihailescu, I.N.; Gittard, S.D.; Miller, P.R.; Narayan, R.J.; Enculescu, M.; et al. Antimicrobial activity of biopolymer–antibiotic thin films fabricated by advanced pulsed laser methods. Appl. Surf. Sci. 2013, 278, 211–213. [Google Scholar] [CrossRef]
  40. Iordache, S.; Cristescu, R.; Popescu, A.C.; Popescu, C.E.; Dorcioman, G.; Mihailescu, I.N.; Ciucu, A.A.; Balan, A.; Stamatin, I.; Fagadar-Cosma, E.; et al. Functionalized porphyrin conjugate thin films deposited by matrix assisted pulsed laser evaporation. Appl. Surf. Sci. 2013, 278, 207–210. [Google Scholar] [CrossRef]
  41. Cristescu, R.; Popescu, C.; Socol, G.; Iordache, I.; Mihailescu, I.N.; Mihaiescu, D.E.; Grumezescu, A.M.; Andronie, A.; Stamatin, I.; Chifiriuc, C.; et al. Magnetic core/shell nanoparticle thin films deposited by maple: Investigation by chemical, morphological and in vitro biological assays. Appl. Surf. Sci. 2012, 258, 9250–9255. [Google Scholar] [CrossRef]
  42. Bakhshayesh, S.; Dehghani, H. Synthesis of magnetite-porphyrin nanocomposite and its applicationas a novel magnetic adsorbent for removing heavy cations. Mater. Res. Bull. 2013, 48, 2614–2624. [Google Scholar] [CrossRef]
  43. Rieppo, L.; Saarakkala, S.; Närhi, T.; Helminen, H.J.; Jurvelin, J.S.; Rieppo, J. Application of second derivative spectroscopy for increasing molecular specificity of fourier transform infrared spectroscopic imaging of articular cartilage. Osteoarthr. Cartil. 2012, 20, 451–459. [Google Scholar] [CrossRef]
  44. Grumezescu, V.; Socol, G.; Grumezescu, A.M.; Holban, A.M.; Ficai, A.; Trușcǎ, R.; Bleotu, C.; Balaure, P.C.; Cristescu, R.; Chifiriuc, M.C. Functionalized antibiofilm thin coatings based on PLA-PVA microspheres loaded with usnic acid natural compounds fabricated by MAPLE. Appl. Surf. Sci. 2013, 302, 262–267. [Google Scholar]
  45. Mihaiescu, D.E.; Cristescu, R.; Dorcioman, G.; Popescu, C.; Nita, C.; Socol, G.; Mihailescu, I.; Grumezescu, A.M.; Tamas, D.; Enculescu, M.; et al. Functionalized magnetite silica thin films fabricated by MAPLE with antibiofilm properties. Biofabrication 2013, 5. [Google Scholar] [CrossRef]
  • Sample Availability: Samples of the Fe3O4@CV and thin coatings are available from the authors.

Share and Cite

MDPI and ACS Style

Anghel, A.G.; Grumezescu, A.M.; Chirea, M.; Grumezescu, V.; Socol, G.; Iordache, F.; Oprea, A.E.; Anghel, I.; Holban, A.M. MAPLE Fabricated Fe3O4@Cinnamomum verum Antimicrobial Surfaces for Improved Gastrostomy Tubes. Molecules 2014, 19, 8981-8994. https://doi.org/10.3390/molecules19078981

AMA Style

Anghel AG, Grumezescu AM, Chirea M, Grumezescu V, Socol G, Iordache F, Oprea AE, Anghel I, Holban AM. MAPLE Fabricated Fe3O4@Cinnamomum verum Antimicrobial Surfaces for Improved Gastrostomy Tubes. Molecules. 2014; 19(7):8981-8994. https://doi.org/10.3390/molecules19078981

Chicago/Turabian Style

Anghel, Alina Georgiana, Alexandru Mihai Grumezescu, Mariana Chirea, Valentina Grumezescu, Gabriel Socol, Florin Iordache, Alexandra Elena Oprea, Ion Anghel, and Alina Maria Holban. 2014. "MAPLE Fabricated Fe3O4@Cinnamomum verum Antimicrobial Surfaces for Improved Gastrostomy Tubes" Molecules 19, no. 7: 8981-8994. https://doi.org/10.3390/molecules19078981