Next Article in Journal
Cold/Hot Deformation Induced Recrystallization of Nickel-Based Superalloys for Molten Salt Reactors
Next Article in Special Issue
Evolution of Microstructure and Hardness of High Carbon Steel under Different Compressive Strain Rates
Previous Article in Journal
Characterization of 17-4PH Single Tracks Produced at Different Parametric Conditions towards Increased Productivity of LPBF Systems—The Effect of Laser Power and Spot Size Upscaling
Previous Article in Special Issue
The Impact of Strain Heterogeneity and Transformation of Metastable Austenite on Springback Behavior in Quenching and Partitioning Steel
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Metals
Volume 8
Issue 7
10.3390/met8070476
metals-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effect of Deformation Temperature on Mechanical Properties and Deformation Mechanisms of Cold-Rolled Low C High Mn TRIP/TWIP Steel

by
Zhengyou Tang
1,*,
Jianeng Huang
1,*,
Hua Ding
1,
Zhihui Cai
1,
Dongmei Zhang
2 and
Devesh Misra
3
1
School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China
2
Shenyang Liming Aero-Engine Corporation, AECC, Shenyang 110043, China
3
Laboratory for Excellence in Advanced Steel Research, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, El Paso, TX 79968, USA
*
Authors to whom correspondence should be addressed.
Metals 2018, 8(7), 476; https://doi.org/10.3390/met8070476
Submission received: 22 May 2018 / Revised: 19 June 2018 / Accepted: 20 June 2018 / Published: 22 June 2018
(This article belongs to the Special Issue Performance of Mechanical Properties of Ultrahigh-Strength Ferrous Steels Related to Strain-Induced Transformation)
Browse Figures
Versions Notes

Abstract

:
The microstructure and mechanical properties of cold-rolled Fe-18Mn-3Al-3Si-0.03C transformation induced plasticity/twinning induced plasticity (TRIP/TWIP) steel in the temperature range of 25 to 600 °C were studied. The experimental steel exhibited a good combination of ultimate tensile strength (UTS) of 905 MPa and total elongation (TEL) of 55% at room temperature. With the increase of deformation temperature from 25 to 600 °C, the stacking fault energy (SFE) of the experimental steel increased from 14.5 to 98.8 mJm−2. The deformation mechanism of the experimental steel is controlled by both the strain induced martensite formation and strain induced deformation twinning at 25 °C. With the increase of deformation temperature from 25 to 600 °C, TRIP and TWIP effect were inhibited, and dislocation glide gradually became the main deformation mechanism. The UTS decreased monotonously from 905 to 325 MPa and the TEL decreased (from 55 to 36%, 25–400 °C) and then increased (from 36 to 64%, 400–600 °C). The change in mechanical properties is related to the thermal softening effect, TRIP effect, TWIP effect, DSA, and dislocation slip.

1. Introduction

Low C, high Mn transformation-induced plasticity/twinning-induced plasticity (TRIP/TWIP) steels are considered to be one of the most attractive materials for automotive steels because of their excellent combination of strength (>900 MPa) and ductility (>50%) at room temperature [1,2,3,4,5]. The outstanding mechanical properties of TRIP/TWIP steels at room temperature are due to the remarkable work-hardening behavior resulting from the evolution of multiple microstructural processes including dislocation slip, formation of stacking fault, deformation induced martensitic transformation and deformation twinning [3,4,5,6,7]. The αbcc/εhcp-martensite and mechanical twins (transformed from austenite during deformation) act as planar obstacles and reduce the mean free path of dislocation glide, promoting working hardening and delaying necking, which results in large uniform elongation [5,7,8]. Recently, it was proposed that the influence of dynamic strain aging (DSA) phenomenon on the mechanical behavior of high Mn TWIP steels should not be ignored, and DSA phenomena may occur in a particular temperature range [9,10,11,12]. The loss of ductility caused by DSA has been reported for ferritic steel, low carbon steel, and dual-phase steel at the DSA temperature range [13,14,15,16]. A change of temperature can influence DSA [17]. Thus, considering the complexity of deformation mechanisms of TRIP/TWIP steel, it is necessary to understand the deformation mechanisms of TRIP/TWIP steels at different temperatures.
The mechanical properties and deformation mechanisms of TRIP/TWIP steels exhibit a strong dependence on temperature and stacking fault energy (SFE) [8,18]. It is well established that the main governing factor responsible for the deformation mechanism in TRIP/TWIP steels is the SFE [19] and the SFE increased with the increased of temperature [7,20]. According to Curtze et al. [21], when SFE below 18 mJm−2, strain induced martensite transformation is the favored transformation mechanism. When the SFE increases from ~18 to 45 mJm−2, deformation-induced twinning occurs [21,22]. When SFE exceeds 45 mJm−2, dislocation glide controls the work hardening [18,21]. The study of SFE for specific plasticity mechanisms is important because deformation mode can affect the mechanical properties of materials or result in deleterious effects. For example, DSA in some TRIP/TWIP steels [8,11,17,23].
A few studies were devoted to TRIP/TWIP steels deformed at different temperatures [7,18,22,24]. Linderov et al. [7] investigated the deformation mechanisms of austenitic TRIP/TWIP steels at two different temperatures—ambient and 373 K (100 °C)—and observed that the temperature strongly affects the deformation-induced processes of metastable austenitic steels. However, a systematic study on the effect of deformation temperature on the deformation mechanism and mechanical properties of TRIP/TWIP steels was not carried out. Martin et al. [24] studied the deformation mechanism in a high-alloy austenitic CrMnNi austenitic TRIP/TWIP steel in the temperature range of −60 and 200 °C, and demonstrated that the change in deformation mechanism was caused by both temperature and SFE. Asghari et al. [19] investigated a TRIP/TWIP steel (Fe–0.07C–18Mn–2Si–2Al) over a wide temperature range from 25 to 1000 °C through compression tests, and showed that the flow stress was strongly dependent on the deformation temperature. Eskandari et al. [25] also conducted compressive tests on a TRIP/TWIP steel (Fe–0.11C–21Mn–2.70Si–1.60Al–0.01Nb–0.01Ti–0.10Cr) from 25 to 1000 °C to investigate the mechanical behavior of the TRIP/TWIP steel. They concluded that both the strain-induced martensite formation and mechanical twinning controlled the plastic deformation in the temperature range of 25–150 °C. In summary, a systematic study on the influence of deformation temperature (over a wide range of temperature) on the deformation mechanism and tensile properties of TRIP/TWIP steel is required at this time.
Thus, The present study is aimed at studying the effect of deformation temperature (over a temperature range of 25 to 600 °C) on the deformation mechanism and tensile properties of TRIP/TWIP steel to get a comprehensive understanding of warm/hot deformation characteristics of TRIP/TWIP steel, having a better insight into the evolution of deformation mechanism in TRIP/TWIP steel at different temperatures, which can provide reference for the best design of some processing route such as warm stamping, hot rolling, thermo-mechanical process. The experimental results have a certain practical significance in the deformation technology of TRIP/TWIP steel in different temperature ranges.

2. Materials and Methods

The nominal chemical composition of the investigated TRIP/TWIP steel was Fe-18.10Mn-3.1Al-3.2Si-0.03C (in wt%). A 50 kg ingot was cast after melting the steel in a vacuum furnace. The ingot was heated at 1200 °C for 2 h and hot forged to rods of section size 100 mm × 30 mm, followed by air cooling to room temperature. Subsequently, the rod was soaked at 1200 °C for 2 h, then hot rolled to 3 mm thickness. The hot rolled plate was reheated to 1100 °C for 30 min and cold-rolled to sheet of 1 mm thickness. Finally, the cold rolled sheet was solution-treated at 1000 °C for 10 min and water-quenched. Tensile specimens with a gage length of 25 mm and width of 6 mm were machined from the cold rolled sheet with the tensile axis parallel to the rolling direction. Tensile tests were conducted from 25 to 600 °C (25 (room temperature), 200, 300, 400, 500, and 600 °C, referred to as 25-sample, 200-sample, 300-sample, 400-sample, 500-sample, and 600-sample, respectively) using CMT5105 tensile testing machine at a constant strain rate of 1.67 × 10−3 s−1. In order to heat the specimen uniformly, high-temperature deformation testing was carried out in a sealed insulation furnace, and a heat-resistant alloy fixture was used. The sample was heated to the deformation temperature at the rate of 10 °C/s and maintained at the test temperature for 5 min.
Microstructure was studied by optical microscope (OM, OLYMPUS-GSX500, OLYMPUS, Tokyo, Japan), field-emission scanning electron microscope (FE-SEM, Supra, SSX-550, Shimadzu, Tokyo, Japan) and a field-emission transmission electron microscope (FE-TEM, FEI, TECNAI G2-20, operated at 200 kV, FEI, Hillsboro, OR, USA). Samples were cut from the tensile specimens near the fracture surface after the tensile tests. Samples were mechanically polished and subsequently electropolished at room temperature in an electrolyte containing 95% CH3COOH+5% HClO4 solution to remove any strain-induced martensite that may have formed during mechanical polishing. Phase analysis was carried out by X-ray diffraction (XRD, Rigaku, D/Max2250/PC, Rigaku Corporation, Tokyo, Japan) with CuKα radiation. Before OM and SEM observations, the samples were etched with 4% nital. For TEM studies, thin foils were first mechanically ground to ~40 μm thickness, then twin-jet polished (Struers, Tenupol-5, Struers, Copenhagen, Denmark) in a solution of 5% perchloric acid and 95% alcohol at ~20 °C. Annealing and deformation twins, stacking faults, martensite, dislocation walls, and slip bands were identified using a TECNAI G2-20 TEM.

3. Results

3.1. Mechanical Properties and Work Hardening Behavior

Figure 1 shows engineering stress-strain curves of the experimental steel at different tensile test temperatures. The statistical results of ultimate tensile strength (UTS), total elongation (TEL), and the product of ultimate tensile strength and total elongation (PSE) of the experimental steel at different deformation temperatures are summarized in Table 1. Combining Figure 1 and Table 1, it may be noted that the deformation temperature has a significant influence on the mechanical behavior of the investigated steel. The thermal softening effect is obvious with the increase of temperature. The UTS and PSE continuously decreased with the increase of temperature from 25 to 600 °C, a behavior similar to the results of Shterner et al. [3]. The TEL decreased from 55 to 36%, as the temperature increased from 25 to 200 °C. Interestingly, TEL remained almost unchanged at 36%, when the deformation temperature was in the range of 200 to 400 °C. Then, TEL increased from 36 to 64% with increase of tensile test temperature from 400 to 600 °C.
It may be noted that the periodic serration and step-like fluctuation appeared in the engineering stress-strain curves, when the deformation temperature was in the range of 200 to 400 °C (Figure 1). According to the conclusion by Lee et al. [11] and Lan et al. [26], the periodic serration and step-like fluctuation are representative of DSA and Portevin Le-Chatelier (PLC) behavior. However, DSA did not appear when the tensile tests were carried out at other temperatures. This indicates that the experimental steel is most susceptible to experience DSA in the temperature range of 200–400 °C.
Figure 2 presents the instantaneous work hardening exponent (n) and true stress as a function of true strain, where the n value was calculated by n = d lnσ/d lnε [27]. The instantaneous work hardening exponent (n) can further reveal the deformation behavior of the experimental steel during straining. Based on Figure 2, it can be seen that the variation in n value was different in samples deformed at different temperatures. The instantaneous work hardening exponent (n) curves can be divided into three stages. In summary, the n value decreased sharply in S1 (elastic stage) for all the samples. During S2, a rapid increase in the n value of 25-sample indicated a high strain hardening rate. A strong fluctuation in the n value was observed for 200-sample, 300-sample and 400-sample, and a gradual increase in the n value for 500-sample and 600-sample. Finally, the n value of 25-sample, 200-sample, 300-sample, and 400-sample decreased rapidly in S3, while, for 500-sample and 600-sample, the decrease was slow.

3.2. Microstructure

Figure 3 shows the X-ray diffraction patterns of the investigated samples before and after tensile deformation at different temperatures. With reference to the work of Egea et al. [28], the percentage of volume fraction of each phase for each temperature configuration has been calculated and summarized in Table 2. It can be seen from Figure 3 and Table 2 that the microstructure of experimental sample before the tensile test was mainly composed of γ-fcc phase (austenite, 66.4%), α-bcc phase (ferrite, 25.8%) and some ε-hcp phase (ε-martensite, 7.8%). After deformation at 25 °C, the peaks of 111γ, 200γ, 220γ, and 311γ for γ-fcc phase became weak (the volume fraction of austenite decreased to 51.6%), but the diffraction peaks of 110α, 200α, and 211α for α-bcc phase were enhanced (the volume fraction of α’-martensite increased to 15.8%), which indicates that significant TRIP effect took place during tensile deformation at 25 °C. With the increase of deformation temperature from 300 to 600 °C, the peaks of 110ε and 002ε for ε-hcp phase disappeared, and the amount of austenite increased to ~73.3% (see Table 2). This may be caused by the reversion from ε-martensite to austenite during tensile deformation.
The OM and SEM micrograph of the experimental steel before deformation are presented in Figure 4. As shown in Figure 4, the annealing twins were present in majority of austenite grains of the sample before the tensile test, and most of the annealing twins were present across the entire austenite grains. After deformation at room temperature, thin lamellar deformation twins (or α′-martensite) nucleated in the austenite matrix and the austenite grains were divided and refined (see Figure 5a). It can be seen from Figure 5b–d that the volume fraction of mechanical twins and α-martensite were remarkably reduced when the deformation temperature was increased to 300–600 °C. This means that the TRIP effect and TWIP effect were inhibited with the increase of temperature.
TEM studies were conducted to reveal stacking faults, deformation twins, α′-martensite and the dislocation substructure development at different temperatures of deformation. Before deformation, the annealing twins (Figure 6a) and abundant stacking faults (Figure 6b) were present in the austenite matrix of experimental steel. The abundant stacking faults can provide favorable conditions for the subsequent strain-induced nucleation of martensite and deformation twins [4]. On deformation at room temperature (25 °C), deformation twins were observed in the austenite grain (Figure 7a). Meanwhile, α′-martensite (confirmed by electron diffraction pattern analysis) transformed from austenite during deformation (shown in Figure 7b), which indicated that the deformation-induced twins (TWIP effect) coexisted with deformation-induced α′-martensite (TRIP effect) and was the predominant deformation mechanism during tensile deformation at room temperature. When the tensile deformation temperature was increased to 300 °C, some dislocation activity was observed with a number of dislocations and dislocation walls (Figure 7c,d). This may be because the temperature of the steel was increased significantly, which led to the increase of SFE, and TRIP and TWIP effect were inhibited, but the dislocation slip was favored [7,29]. When the deformation temperature was 600 °C, dislocation cells and slip bands were observed (Figure 7e,f). Thus, dislocation slip was the main deformation mechanism in the high deformation temperature region.

4. Discussion

4.1. Effect of Deformation Temperature on the Deformation Mechanism

It is known that the deformation temperature has a significant influence on microstructural development during deformation of experimental steel. The temperature change changes SFE, and the deformation behavior of high Mn steels is strongly related to SFE [9,30]. It is well known that the SFE increases with temperature [7,20]. For tests at different temperatures, the temperature rise (ΔT) is enough to affect the SFE. According to the thermodynamic models [31], the value of SFE can be calculated by the equation proposed by Saeed-Akbari et al. [20]. The change in SFE caused by ΔT is shown in Figure 8. It can be seen that the SFE increased with the increase of deformation temperature. The SFE value of the investigated steel at room temperature was 14.5 mJm−2. With the increase of temperature from 200 to 600 °C, the SFE approached 40.0, 54.7, 69.4, 84.1, and 98.8 mJm−2, respectively. According to Allain et al. [6] martensitic transformation occurs below 18 mJm−2 and twinning between 12 and 35 mJm−2 in the Fe–Mn–C TWIP steel. Curtze et al. [21] reported that twinning occurred at SFE: of ~18 mJm−2 ≤ SFE ≤ 45 mJm−2. When SFE > 45 mJm−2, plasticity and strain hardening were controlled solely by the glide of dislocations. Thus, the strain induced martensitic transformation and deformation twinning coexisted at the room temperature deformation because the SFE (14.5 mJm−2) is relatively low (see Figure 5a and Figure 7a,b). Then, the SFE increased with increase in temperature, TRIP effect and TWIP effect were suppressed (see Figure 5b–d). When the temperature was greater than 300 °C, twinning was replaced by dislocation slip because the SFE was greater than 45 mJm−2 (see Figure 7c–f).
In addition, the serrated flow (characteristic of DSA) occurred between 200 and 400 °C (see Figure 1) and implies that DSA effect has a significant effect on the mechanical properties of experimental steel in the temperature range of 200–400 °C, which is similar to the results of Bayramin et al. [16]. The SFE was in the range of 40.0 to 69.4 mJm−2 with the increase of temperature from 200–400 °C. Dislocation slip replaced TRIP/TWIP effect in this temperature range. The moving dislocations were pinned by solute atoms resulting in serrated flow at 200–400 °C [32]. If temperature is too high or too low, solute interstitial atoms (C-atom) may not be able to rearrange themselves with mobile dislocations and hinder them, therefore, the DSA did not take place [15,33].

4.2. Tensile Properties Difference at Different Temperatures

It may be noted from Figure 1 and Table 1 that the experimental steel presents an exceptional mechanical properties with a PSE of 49.3 GPa at room temperature, and the mechanical properties deteriorated with the increase of deformation temperature. The mechanical properties are directly related to the work hardening behavior depending on the mechanisms. 25-sample exhibited the highest UTS (905 MPa) and a good plasticity with the TEL of 55%, and a rapid increase in the n value in S2 (see Figure 2a), because of strain induced martensitic transformation (TRIP effect) and strain induced deformation twinning (TWIP effect) (see Figure 3, Figure 5a, and Figure 7a,b). The formation of martensite and deformation twins act as planar obstacles to dislocation glide during deformation and enhanced the n values (high work hardening rate), delayed necking, which improves the plasticity of the experimental steel and results in highest UTS [2,3,18,34]. It should be also noted that the increase of n value of 25-sample exceeded other samples (see Figure 2). It can be deduced that the TRIP effect and TWIP effect had the most beneficial effect on work hardening among all the deformation modes. With increase of deformation temperature to 200, 300, and 400 °C, the UTS of 200-sample, 300-sample, and 400-sample decreased to 690, 670, and 650 MPa, respectively. Meanwhile, the TEL was only ~36%. As shown in Figure 2b–d, the n value for the three samples exhibited an intense fluctuation in S2 resulting from DSA. The decrease of UTS was due to thermal softening effect. TRIP effect and TWIP effect were suppressed and gradually replaced by dislocation slip with the increase in temperature. In this temperature range, high dislocation density and highly dense dislocation walls (see Figure 7c,d), were the main contributors in enhancing work hardening behavior. Their strengthening effect is weaker than TRIP effect and TWIP effect, hence, UTS was decreased. As regards, low plasticity (TEL of 36%), it is because the TRIP effect and TWIP effect were suppressed. In addition, the role of DSA phenomenon should be taken into account. The DSA took place in this temperature range, and an inhomogeneous plastic deformation because of successive locking of the mobile dislocations and strain localization took place, which prevented high TEL to be obtained [15]. When the deformation temperature was increased to 500–600 °C, high-temperature softening occurred and the UTS of samples was further decreased with the increase of elongation.

5. Conclusions

In the present study, the microstructure and mechanical properties of cold-rolled Fe-18Mn-3Al-3Si-0.03C TRIP/TWIP steel in the temperatures range of 25 to 600 °C was studied. The main conclusions are as follows:
  • Fe-18.1Mn-3.1Al-3.2Si-0.03C TRIP/TWIP steel exhibited excellent mechanical properties at room temperature. The UTS, TEL and PSE were 905 MPa, 55% and 49.3 GPa, respectively. The dominant plasticity mechanism at room temperature was strain induced martensite deformation and deformation twinning.
  • With the increase of deformation temperature from 25 (room temperature) to 600 °C, the SFE of the experimental steel was in the range of 14.5 to 98.8 mJm−2. The deformation mechanism of the experimental steel is controlled by both the strain induced martensite formation and strain induced deformation twinning at 25 °C. With the increase of deformation temperature from 25 to 600 °C, TRIP and TWIP effects were inhibited, and dislocation glide gradually became the main deformation mechanism.
  • The UTS decreased monotonously from 905 to 325 MPa and the TEL decreased (from 55 to 36%, 25–400 °C) and then increased (from 36 to 64%, 400–600 °C). The change in mechanical properties was related to the thermal softening effect, TRIP effect, TWIP effect, DSA, and dislocation slip.

Author Contributions

Z.T. and J.H. designed most of the experiments, performed most experiments, analyzed the results, and wrote this manuscript. Z.C., H.D., D.Z., and D.M. helped analyze the experiment data and gave some constructive suggestions about how to write this manuscript.

Funding

This research received no external funding.

Acknowledgments

The research was supported by the National Natural Science Foundation of China (grant Nos. 51574077 and 51501035) and the Fundamental Research Funds for the Central Universities (N120502005 and N170204017). R.D.K. Misra acknowledges continued collaboration with Northeastern University as an Honorary Professor in providing guidance to students in research.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ding, H.; Tang, Z.Y.; Li, W.; Wang, M.; Song, D. Microstructures and mechanical properties of Fe-Mn-(Al, Si) TRIP/TWIP steels. J. Iron Steel Res. 2006, 13, 66–70. [Google Scholar] [CrossRef]
  2. Ding, H.; Ding, H.; Song, D.; Tang, Z.Y.; Yang, P. Strain hardening behavior of a TRIP/TWIP steel with 18.8% Mn. Mater. Sci. Eng. A 2011, 528, 868–873. [Google Scholar] [CrossRef]
  3. Shterner, V.; Timokhina, I.B.; Beladi, H. On the work-hardening behaviour of a high manganese TWIP steel at different deformation temperatures. Mater. Sci. Eng. A 2016, 669, 437–446. [Google Scholar] [CrossRef]
  4. Tang, Z.Y.; Misra, R.D.K.; Ma, M.; Zan, N.; Wu, Z.Q.; Ding, H. Deformation twinning and martensitic transformation and dynamic mechanical properties in Fe-0.07C-23Mn-3.1Si-2.8Al TRIP/TWIP steel. Mater. Sci. Eng. A 2015, 624, 186–192. [Google Scholar] [CrossRef]
  5. Dufay, A.; Chateau, J.P.; Allain, S.; Migot, S.; Bouaziz, O. Influence of addition elements on the stacking-fault energy and mechanical properties of an austenitic Fe-Mn-C steel. Mater. Sci. Eng. A 2008, 483–484, 184–187. [Google Scholar]
  6. Allain, S.; Chaterau, J.P.; Bouaziz, O.; Migot, S.; Guelton, N. Correlations between the calculated stacking fault energy and the plasticity mechanisms in Fe-Mn-C alloys. Mater. Sci. Eng. A 2004, 387–389, 158–162. [Google Scholar] [CrossRef]
  7. Linderov, M.; Segel, C.; Weidner, A.; Biermann, H.; Vinogradov, A. Deformation mechanisms in austenitic TRIP/TWIP steels at room and elevated temperature investigated by acoustic emission and scanning electron microscopy. Mater. Sci. Eng. A 2014, 597, 183–193. [Google Scholar] [CrossRef]
  8. Pierce, D.T.; Jiménez, J.A.; Bentley, J.; Raabe, D.; Witting, J.E. The influence of stacking fault energy on the microstructural and strain-hardening evolution of Fe-Mn-Al-Si steels during tensile deformation. Acta Mater. 2015, 100, 178–190. [Google Scholar] [CrossRef]
  9. Kim, J.K.; Chen, L.; Kim, H.S.; Kim, S.K.; Estrin, Y.; De Cooman, B.C. On the tensile behavior of high-manganese twinning-induced plasticity steel. Metall. Mater. Trans. A 2009, 40, 3147–3158. [Google Scholar] [CrossRef]
  10. Chen, L.; Kim, H.S.; Kim, S.K.; De Cooman, B.C. Localized deformation due to Portevin-LeChatelier effect in 18Mn-0.6C TWIP austenitic steel. ISIJ Int. 2007, 47, 1804–1812. [Google Scholar] [CrossRef]
  11. Lee, S.J.; Kim, J.Y.; Kane, S.N.; De Cooman, B.C. On the origin of dynamic strain aging in twinning-induced plasticity steels. Acta Mater. 2011, 59, 6809–6819. [Google Scholar] [CrossRef]
  12. Kim, J.G.; Hong, S.; Anjabin, N.; Park, B.H.; Kim, S.K.; Chin, K.G.; Lee, S.; Kim, H.S. Dynamic strain aging of twinning-induced plasticity (TWIP) steel in tensile testing and deep drawing. Mater. Sci. Eng. A 2015, 633, 136–143. [Google Scholar] [CrossRef]
  13. Taheri, A.K.; Maccagno, T.M.; Jonas, J.J. Dynamic strain aging and the wire drawing of low carbon steel rods. ISIJ Int. 1995, 35, 1532–1540. [Google Scholar] [CrossRef]
  14. Li, C.C.; Leslie, W.C. Effects of dynamic strain aging on the subsequent mechanical properties of carbon steels. Metall. Trans. A 1978, 9, 1765–1775. [Google Scholar] [CrossRef]
  15. Shahriary, M.S.; Koohbor, B.; Ahadi, K.; Ekrami, A.; Khakian-Qomi, M.; Izadyar, T. The effect of dynamic strain aging on room temperature mechanical properties of high martensite dual phase (HMDP) steel. Mater. Sci. Eng. A 2012, 550, 325–332. [Google Scholar] [CrossRef]
  16. Bayramin, B.; Şimşir, C.; Efe, M. Dynamic strain aging in DP steels at forming relevant strain rates and temperatures. Mater. Sci. Eng. A 2017, 704, 164–172. [Google Scholar] [CrossRef]
  17. Jung, I.C.; De Cooman, B.C. Temperature dependence of the flow stress of Fe-18Mn-0.6C-xAl twinning-induced plasticity steel. Acta Mater. 2013, 61, 6724–6735. [Google Scholar] [CrossRef]
  18. Benzing, J.T.; Poling, W.A.; Pierce, D.T.; Witting, J.E. Effects of strain rate on mechanical properties and deformation behavior of an austenitic Fe-25Mn-3Al-3Si TWIP-TRIP steel. Mater. Sci. Eng. A 2018, 711, 78–92. [Google Scholar] [CrossRef]
  19. Asghari, A.; Zarei-Hanzaki, A.; Eskandari, M. Temperature dependence of plastic deformation mechanisms in a modified transformation-twinning induced plasticity steel. Mater. Sci. Eng. A 2013, 579, 150–156. [Google Scholar] [CrossRef]
  20. Saeed-Akbari, A.; Imlau, J.; Prahl, U.; Bleck, W. Derivation and variation in composition-dependent stacking fault energy maps based on subregular solution model in high-manganese steels. Metall. Mater. Trans. A 2009, 40, 3076–3090. [Google Scholar] [CrossRef]
  21. Curtze, S.; Kuokkala, V.T. Dependence of tensile deformation behavior of TWIP steels on stacking fault energy, temperature and strain rate. Acta Mater. 2015, 58, 5129–5141. [Google Scholar] [CrossRef]
  22. Allain, S.; Chateau, J.P.; Bouaziz, O. A physical model of the twinning-induced plasticity effect in a high manganese austenitic steel. Mater. Sci. Eng. A 2004, 387–389, 143–147. [Google Scholar] [CrossRef]
  23. Renard, K.; Ryelandt, S.; Jacques, P.J. Characterisation of the Portevin-Le Châtelier effect affecting an austenitic TWIP steel based on digital image correlation. Mater. Sci. Eng. A 2010, 527, 2969–2977. [Google Scholar] [CrossRef]
  24. Martin, S.; Wolf, S.; Martin, U.; Krüger, L.; Rafaja, D. Deformation mechanisms in austenitic TRIP/TWIP steel as a function of temperature. Metall. Mater. Trans. A 2016, 47, 49–58. [Google Scholar] [CrossRef]
  25. Eskandari, M.; Zarei-Hanzaki, A.; Marandi, A. An investigation into the mechanical behavior of a new transformation-twinning induced plasticity steel. Mater. Des. 2012, 39, 279–284. [Google Scholar] [CrossRef]
  26. Lan, P.; Zhang, J.Q. Twinning and dynamic strain aging behavior during tensile deformation of Fe-Mn-C TWIP steel. Mater. Sci. Eng. A 2017, 700, 250–258. [Google Scholar] [CrossRef]
  27. Jacques, P.; Ladriere, J.; Delannay, F. On the influence of interactions between phases on the mechanical stability of retained austenite in transformation-induced plasticity multiphase steels. Metall. Mater. Trans. A 2001, 32, 2759–2768. [Google Scholar] [CrossRef]
  28. Egea, A.J.S.; Rojas, H.A.G.; Celentano, D.J.; Peiró, J.J. Mechanical and metallurgical changes on 308L wires drawn by electropulses. Mater. Des. 2016, 90, 1159–1169. [Google Scholar] [CrossRef]
  29. Lee, S.; Estrin, Y.; De Cooman, B.C. Effect of the strain rate on the TRIP-TWIP transition in austenitic Fe-12 pct Mn-0.6 pct C TWIP steel. Metall. Mater. Trans. A 2014, 45, 717–730. [Google Scholar] [CrossRef]
  30. Van der Wegen, G.J.L.; Bronsveld, P.M.; Hosson, J.T.M. A comparison between different theories predicting the stacking fault energy from extended nodes. Scr. Metall. 1980, 4, 285–288. [Google Scholar] [CrossRef]
  31. Ferreira, P.J.; Müllner, P. A thermodynamic model for the stacking-fault energy. Acta Mater. 1998, 46, 4479–4484. [Google Scholar] [CrossRef] [Green Version]
  32. Peng, K.P.; Qian, K.W.; Chen, W.Z. Effect of dynamic strain aging on high temperature properties of austenitic stainless steel. Mater. Sci. Eng. A 2004, 379, 372–377. [Google Scholar] [CrossRef]
  33. Molaei, M.J.; Ekrami, A. The effect of dynamic strain aging on fatigue properties of dual phase steels with different martensite morphology. Mater. Sci. Eng. A 2009, 527, 235–238. [Google Scholar] [CrossRef]
  34. Bouaziz, O.; Allain, S.; Scott, C. Effect of grain and twin boundaries on the hardening mechanisms of twinning-induced plasticity steels. Scr. Mater. 2008, 58, 484–487. [Google Scholar] [CrossRef]
Metals 08 00476 g001 550
Figure 1. Engineering strain-stress curves at different tensile test temperatures of the experimental steel.
Figure 1. Engineering strain-stress curves at different tensile test temperatures of the experimental steel.
Metals 08 00476 g001
Metals 08 00476 g002 550
Figure 2. Instantaneous work hardening exponent (n) and true stress versus true strain of the experimental steel after deformation at different temperatures of (a) 25 °C; (b) 200 °C; (c) 300 °C; (d) 400 °C; (e) 500 °C; and (f) 600 °C. (S1~S3 mean stage 1–3).
Figure 2. Instantaneous work hardening exponent (n) and true stress versus true strain of the experimental steel after deformation at different temperatures of (a) 25 °C; (b) 200 °C; (c) 300 °C; (d) 400 °C; (e) 500 °C; and (f) 600 °C. (S1~S3 mean stage 1–3).
Metals 08 00476 g002
Metals 08 00476 g003 550
Figure 3. XRD patterns of the investigated steel before and after tensile deformation at different temperatures. ((Before test, ε = 0), (25 °C, ε = 55%), (300 °C, ε = 36%), (500 °C, ε = 44%), (600 °C, ε = 64%)).
Figure 3. XRD patterns of the investigated steel before and after tensile deformation at different temperatures. ((Before test, ε = 0), (25 °C, ε = 55%), (300 °C, ε = 36%), (500 °C, ε = 44%), (600 °C, ε = 64%)).
Metals 08 00476 g003
Metals 08 00476 g004 550
Figure 4. OM (a) and SEM (b) micrographs of the experimental steel before deformation at 25 °C (ε = 0).
Figure 4. OM (a) and SEM (b) micrographs of the experimental steel before deformation at 25 °C (ε = 0).
Metals 08 00476 g004
Metals 08 00476 g005 550
Figure 5. SEM micrographs of the experimental steel after deformation at different temperatures of (a) 25 °C, ε = 55%; (b) 300 °C, ε = 36%; (c) 500 °C, ε = 44%; and (d) 600 °C, ε = 64%.
Figure 5. SEM micrographs of the experimental steel after deformation at different temperatures of (a) 25 °C, ε = 55%; (b) 300 °C, ε = 36%; (c) 500 °C, ε = 44%; and (d) 600 °C, ε = 64%.
Metals 08 00476 g005
Metals 08 00476 g006 550
Figure 6. TEM micrographs of the experimental steel before deformation at 25 °C (ε = 0).
Figure 6. TEM micrographs of the experimental steel before deformation at 25 °C (ε = 0).
Metals 08 00476 g006
Metals 08 00476 g007 550
Figure 7. TEM micrographs of the experimental steel after deformation at different temperatures of (a,b) 25 °C, ε = 55%; (c,d) 300 °C, ε = 36%; and (e,f) 600 °C, ε = 64%.
Figure 7. TEM micrographs of the experimental steel after deformation at different temperatures of (a,b) 25 °C, ε = 55%; (c,d) 300 °C, ε = 36%; and (e,f) 600 °C, ε = 64%.
Metals 08 00476 g007
Metals 08 00476 g008 550
Figure 8. Estimation of SFE with the different deformation temperatures.
Figure 8. Estimation of SFE with the different deformation temperatures.
Metals 08 00476 g008
Table
Table 1. Mechanical properties of experimental steel at different tensile test temperatures.
Table 1. Mechanical properties of experimental steel at different tensile test temperatures.
Temperature (°C)UTS (MPa)TEL (%)PSE (GPa%)
25905 (±7)55 (±0.2)49.8 (±0.5)
200690 (±10)36 (±0.3)24.8 (±0.6)
300670 (±6)36 (±0.3)24.1 (±0.4)
400650 (±8)36 (±0.2)23.4 (±0.4)
500530 (±6)44 (±0.5)23.3 (±0.5)
600325 (±3)64 (±0.6)20.8 (±0.4)
Table
Table 2. Volume fraction of constituent phases estimated by X-ray diffraction (vol%).
Table 2. Volume fraction of constituent phases estimated by X-ray diffraction (vol%).
SampleγαFεα′
Undeformed sample66.425.87.80
25-sample51.625.76.915.8
300-sample73.326.700
500-sample74.125.900
600-sample73.226.800

Share and Cite

MDPI and ACS Style

Tang, Z.; Huang, J.; Ding, H.; Cai, Z.; Zhang, D.; Misra, D. Effect of Deformation Temperature on Mechanical Properties and Deformation Mechanisms of Cold-Rolled Low C High Mn TRIP/TWIP Steel. Metals 2018, 8, 476. https://doi.org/10.3390/met8070476

AMA Style

Tang Z, Huang J, Ding H, Cai Z, Zhang D, Misra D. Effect of Deformation Temperature on Mechanical Properties and Deformation Mechanisms of Cold-Rolled Low C High Mn TRIP/TWIP Steel. Metals. 2018; 8(7):476. https://doi.org/10.3390/met8070476

Chicago/Turabian Style

Tang, Zhengyou, Jianeng Huang, Hua Ding, Zhihui Cai, Dongmei Zhang, and Devesh Misra. 2018. "Effect of Deformation Temperature on Mechanical Properties and Deformation Mechanisms of Cold-Rolled Low C High Mn TRIP/TWIP Steel" Metals 8, no. 7: 476. https://doi.org/10.3390/met8070476

APA Style

Tang, Z., Huang, J., Ding, H., Cai, Z., Zhang, D., & Misra, D. (2018). Effect of Deformation Temperature on Mechanical Properties and Deformation Mechanisms of Cold-Rolled Low C High Mn TRIP/TWIP Steel. Metals, 8(7), 476. https://doi.org/10.3390/met8070476

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop