Synthesis and Application of Hybrid Polymer Composites Based on Silver Nanoparticles as Corrosion Protection for Line Pipe Steel
Abstract
:1. Introduction
2. Results and Discussion
2.1. Preparation of Silver Nanoparticles
2.2. Synthesis of Hybrid Polymer
2.3. EIS Measurements
Polarization Method | EIS Method | |||||||
---|---|---|---|---|---|---|---|---|
AMPS/NIPAm-Ag NPs Concentrations (ppm) | Ba (mV) | Bc (mV) | Ecorr (V) | icorr µA/cm2 | IE% | Rct Ohm | Cdl (µF/cm2) | IE% |
Blank | 147.00 | 141.00 | − 0.4034 | 745 | - | 1.80 | 334 | - |
50 | 79.40 | 98.33 | − 0.4255 | 350 | 53.02 | 4.0 | 215 | 55.00 |
150 | 83.78 | 102.22 | − 0.4338 | 317 | 57.40 | 4.8 | 163 | 62.50 |
250 | 77.43 | 97.57 | − 0.4532 | 137 | 81.16 | 10.8 | 123 | 81.46 |
2.4. Polarization Measurements
3. Experimental Section
3.1. Materials
3.2. Preparation Methods
3.2.1. Preparation of Silver Nanoparticles
3.2.2. Preparation of Silver AMPS/NIPAm Hybrid Polymer
3.3. Characterization
3.4. Electrochemical Measurements
4. Conclusions
Acknowledgments
Author Contributions
Conflicts of Interest
References
- Bardel, E. Corrosion and protection; Springer-Verlag: London, UK, 2003. [Google Scholar]
- Roberge, P.R. Handbook of Corrosion Engineering; McGraw-Hill: New York, NY, USA, 1999. [Google Scholar]
- Kakooei, S.; Ismail, M.C.; Ariwahjoedi, B. Mechanisms of microbiologically influenced corrosion: A review. World Appl. Sci. J. 2012, 17, 524–531. [Google Scholar]
- Lagrnee, M.; Mernari, B.; Bonanis, M.; Traisnel, M.; Bentiss, F. Study of the mechanism and inhibiting efficiency of 3,5-bis(4-methylthiophenyl)-4H-1,2,4-triazole on mild steel corrosion in acidic media. Corros. Sci. 2002, 44, 573–588. [Google Scholar] [CrossRef]
- Tayaperumal, D.; Muralidharan, S.; Venkatchari, G.; Rengaswamy, N.S. Inhibition effect of ethanolamines on oil well tubular material in hydr-Chloric acid. Anti-corros. Method Mater. 2000, 47, 349–355. [Google Scholar] [CrossRef]
- Lee, W.; Lewandowski, Z.; Nielsen, P.H.; Hamilton, W.A. Role of sulfate-reducing bacteria in corrosion of mild steel: A review. Biofouling 1995, 8, 165–194. [Google Scholar] [CrossRef]
- Sabzi, M.; Mirabedini, S.M.; Zohuriaan-Mehr, J.; Atai, M. Surface modification of TiO2 nano-particles with silane coupling agent and investigation of its effect on the properties of polyurethane composite coating. Prog. Org. Coat. 2009, 65, 222–228. [Google Scholar] [CrossRef]
- Taryba, M.; Lamaka, S.V.; Snihirova, D.; Ferreira, M.G.S.; Montemor, M.F.; Wijting, W.K.; Towes, S.; Grundmeier, G. The combined use of scanning vibrating electrode technique and micro-petentiometry to assess the self-repair processes in defects on ‘‘Smart’’ coatings applied to galvanized steel. Electrochim. Acta 2011, 56, 4475–4488. [Google Scholar] [CrossRef]
- Ramezanzadeh, B.; Attar, M.M. Studying the effects of micro and nano sized ZnO particles on the corrosion resistance and deterioration behavior of an epoxy-polyamide coating on hot-dip galvanized steel. Prog. Org. Coat. 2011, 71, 314–328. [Google Scholar] [CrossRef]
- Ramezanzadeh, B.; Attar, M.M. An evaluation of the corrosion resistance and adhesion properties of an epoxy-nanocomposite on a hot-dip galvanized steel (HDG) treated by different kinds of conversion coatings. Surf. Coat. Techn. 2011, 205, 4649–4657. [Google Scholar] [CrossRef]
- Xu, J.; Tao, J.; Jiang, S.; Xu, Z. Investigation on corrosion and wear behaviors of nanoparticles reinforced Ni-based composite alloying layer. Appl. Surf. Sci. 2008, 254, 4036–4043. [Google Scholar] [CrossRef]
- Truc, T.A.; Hang, T.T.X.; Oanh, V.K.; Dantras, E.; Lacabanne, C.; Oquab, D.; Pébère, N. Incorporation of an indole-3 butyric acid modified clay in epoxy resin for corrosion protection of carbon steel. Surf. Coat. Technol. 2008, 202, 4945–4951. [Google Scholar] [CrossRef] [Green Version]
- Xia, Y.; Whitesides, G.M. Soft lithography. Angew. Chem. Int. Ed. 1998, 37, 550–575. [Google Scholar] [CrossRef]
- Jannings, G.K.; Yong, T.H.; Munro, J.C.; Laibinis, P.E. Structural effects on the barrier properties of self-assembled monolayers formed from long-chain omega-alkoxy-n-alkanethiols on copper. J. Am. Chem. Soc. 2003, 125, 2950. [Google Scholar] [CrossRef]
- Lai, Y.H.; Yeh, C.T.; Cheng, S.H.; Liao, P.; Hung, W.H. Adsorption and thermal decomposition of alkanethiols on Cu(110). J. Phys. Chem. B 2002, 106, 5438–5446. [Google Scholar] [CrossRef]
- Loepp, G.; Vollmer, S.; Witte, G.; Woll, C. Adsorption of heptanethiol on Cu(110). Langmuir 1999, 15, 3767–3772. [Google Scholar] [CrossRef]
- Temgire, M.K.; Joshi, S.S. Optical and structural studies of silver nanoparticles. Radiat. Phys. Chem. 2003, 71, 1039–1044. [Google Scholar] [CrossRef]
- Zheng, M.; Gu, M.; Jin, Y.; Jin, G. Optical properties of silver-dispersed PVP thin film. Mater. Res. Bull. 2001, 36, 853–859. [Google Scholar] [CrossRef]
- Brett, D.W. A discussion of silver as an antimicrobial agent: Alleviating the confusion. Ostomy/Wound Manag. 2006, 52, 34–41. [Google Scholar]
- Raffi, M.; Hussain, F.; Bhatti, T.M.; Akhter, J.I.; Hameed, A.; Hasan, M.M. Antibacterial Characterization of Silver Nanoparticles against E. Coli ATCC-15224. J. Mater. Sci. Technol. 2008, 24, 192–196. [Google Scholar]
- Choi, O.; Deng, K.K.; Kim, N.J.; Ross, L.J.; Surampalli, R.Y.; Hu, Z. The inhibitory effects of silver nanoparticles, silver ions, and silver chloride colloids on microbial growth. Water Res. 2008, 42, 3066–3074. [Google Scholar]
- Radheshkumar, C.; Münstedt, H. Morphology and mechanical properties of antimicrobial polyamide/silver composites. Mater. Lett. 2005, 59, 1949–1953. [Google Scholar] [CrossRef]
- Espuche, E.; David, L.; Rochas, C.; Afeld, J.L.; Compton, J.M.; Thompson, D.W.; Kranbuehl, D.E. In situ generation of nanoparticulate lanthanum(III) oxide-polyimide films: Characterization of nanoparticle formation and resulting polymer properties. Polymer 2005, 46, 6657–6665. [Google Scholar]
- Khanna, P.K.; Singh, N.; Charan, S.; Subbarao, V.V.V.S.; Gokhale, R.; Mulik, U.P. Synthesis and characterization of Ag/PVA nanocomposite by chemical reduction method. Mater. Chem. Phys. 2005, 93, 117–121. [Google Scholar]
- Shimura, T.; Aramaki, K. Improvement of the film thickness by modification of the hydroxymethylbenzene SAM with tetraethoxysilane and otanediol for protection of iron from corrosion in 0.5 M NaCl. Corros. Sci. 2008, 50, 1397–1405. [Google Scholar]
- Shimura, T.; Aramaki, K. Self-assembled monolayers of p-toluene and p-hydroxymethylbenzene moieties adsorbed on iron by the formation of covalent bonds between carbon and iron atoms for protection of iron from corrosion. Corros. Sci. 2007, 49, 1378–1393. [Google Scholar]
- El-Mahdy, G.; Atta, A.M.; Dyab, A.; Al-Lohedan, H.A. Protection of petroleum pipeline carbon steel alloys with new modified core-shell magnetite nanogel against corrosion in acidic medium. J. Chem. 2013, 2013, 1–9. [Google Scholar]
- Atta, A.M.; Hegazy, M.; El-Azabawy, O.E.; Ismail, H.S. Novel dispersed magnetite core–shell nanogel polymers as corrosion inhibitors for carbon steel in acidic medium. Corros. Sci. 2011, 53, 1680–1689. [Google Scholar]
- El-Mahdy, G.A.; Atta, A.M.; Al-Lohedan, H.A. Synthesis and evaluation of poly(sodium 2-acrylamido-2-methylpropane sulfonate-co-styrene)/magnetite nanoparticle composites as corrosion inhibitors for steel. Molecules 2014, 19, 1713–1731. [Google Scholar] [CrossRef]
- Blinova, N.V.; Stejskal, J.; Trchova, M.; Sapurina, I. Ciric-marjanovic the oxidation of aniline with silver nitrate to polyaniline-silver composites. Polymer 2009, 50, 50–56. [Google Scholar] [CrossRef]
- Yang, J.; Yin, H.; Jia, J.; Wei, Y. Facile Synthesis of high-concentration, stable aqueous dispersions of uniform silver nanoparticles using aniline as a reductant. Langmuir 2011, 27, 5047–5053. [Google Scholar] [CrossRef]
- Mehta, S.K.; Chaudhary, S.; Gradzielski, M. Time dependence of nucleation and growth of silver nanoparticles generated by sugar reduction in micellar media. J. Colloid Interface Sci. 2010, 343, 447–453. [Google Scholar] [CrossRef]
- Sapurina, I.; Stejskal, J. The mechanism of the oxidative polymerization of aniline and the formation of supramolecular polyaniline structures. J. Polym. Int. 2008, 57, 1295–1325. [Google Scholar] [CrossRef]
- Hunter, R.J. Double layer interaction and particle coagulation. In Foundations of Colloid Science, 2nd ed.; Oxford University Press: Oxford, UK, 2001; p. 635. [Google Scholar]
- Chou, K.S.; Lai, Y.S. Effect of polyvinyl pyrrolidone molecular weights on the formation of nanosized silver colloids. Mater. Chem. Phys. 2004, 83, 82–88. [Google Scholar] [CrossRef]
- Luo, C.; Zhang, Y.; Zeng, X.; Zeng, Y.; Wang, Y. The role of poly(ethylene glycol) in the formation of silver nanoparticles. J. Colloid Interface Sci. 2005, 288, 444–448. [Google Scholar] [CrossRef]
- Mafune, F.; Kohno, J.; Takeda, Y.; Kondow, T.; Sawabe, H. Structure and stability of silver nanoparticles in aqueous solution produced by laser ablation. J. Phys. Chem. B 2000, 104, 8333–8337. [Google Scholar] [CrossRef]
- Yu, D.B.; Yam, V.W.W. Hydrothermal-Induced assembly of colloidal silver spheres into various nanoparticles on the basis of htab-modified silver mirror reaction. J. Phys. Chem. B 2005, 109, 5497–5503. [Google Scholar] [CrossRef]
- Kvítek, L.; Panáček, A.; Soukupová, J.; Kolář, M.; Večeřová, R.; Prucek, R.; Holecová, M.; Zbořil, R. Effect of surfactants and polymers on stability and antibacterial activity of silver nanoparticles (NPs). J. Phys. Chem. C 2008, 112, 5825–5834. [Google Scholar] [CrossRef]
- Bindhu, M.R.; Umadevi, M. Surface plasmon resonance optical sensor and antibacterial activities of biosynthesized silver nanoparticles. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 2014, 121, 596–604. [Google Scholar] [CrossRef]
- Allpress, J.G.; Sanders, J.V. The structure and orientation of crystals in deposits of metals on mica. Surf. Sci. 1967, 7, 1–25. [Google Scholar] [CrossRef]
- Huang, L.M.; Liao, W.H.; Ling, H.C.; Wen, T.C. Simultaneous synthesis of polyaniline nanofibers and metal (Ag and Pt) nanoparticles. Mater. Chem. Phys. 2009, 116, 474–478. [Google Scholar] [CrossRef]
- Atta, A.M.; Dyab, A.K.F.; Allohedan, H.A. A novel route to prepare highly surface active nanogel particles based on nonaqueous emulsion polymerization. Polym. Adv. Technol. 2013, 24, 986–996. [Google Scholar] [CrossRef]
- Atta, A.M.; Al-Shafey, H. Synthesis and Surface Activity of Amphiphilic 2-Acylamido-2-Methylpropane Sulfonic Acid - co-N-Isopropyl acylamide nanoparticles in aqueous media. Int. J. Electr. Chem. Sci. 2013, 8, 4970–4985. [Google Scholar]
- Kometani, N.; Kaneko, M.; Morita, T.; Yonezawa, Y. The formation of photolytic silver clusters in water/supercritical CO2 microemulsions. Colloid Surf. A Physic. Chem. Eng. Aspects 2008, 321, 301–307. [Google Scholar]
- Henglein, A. Colloidal silver nanoparticles: Photochemical preparation and interaction with O2, CCl4, and some metal ions. Chem. Mater. 1998, 10, 444–450. [Google Scholar] [CrossRef]
- Khan, A.; El-Toni, A.M.; Alrokayan, S.; Alsalhi, M.; Alhoshan, M.; Aldwayyan, A.S. Microwave-assisted synthesis of silver nanoparticles using poly-N-isopropylacrylamide/acrylic acid microgel particles. Colloids and Surfaces A PhysicoChem. Eng. Aspects 2011, 377, 356–360. [Google Scholar] [CrossRef]
- Feng, Y.; Schmidt, A.; Weiss, R.A. Compatibilization of polymer blends by complexation. 1. Spectroscopic characterization of ion-amide interactions in ionomer/polyamide blens. Macromolecules 1996, 29, 3909–3917. [Google Scholar] [CrossRef]
- Mansfeld, F. Tafel slopes and corrosion rates obtained in the pre-Tafel region of polarization curves. Corros. Sci. 2005, 47, 3178–3186. [Google Scholar] [CrossRef]
- Sandenbergh, R.F.; Van der Lingen, E. The use of Tafel back extrapolation to clarify the influence of ruthernium and palladium alloying on the corrosion behaviour of titanium in concentrated hydrochloric acid. Corros. Sci. 2005, 47, 3300–3311. [Google Scholar]
- Flitt, H.J.; Schweinsberg, D.P. Synthesis, matching and deconstruction of polarization curves for the active corrosion of zinc in aerated near-neutral NaCl solutions. Corros. Sci. 2010, 52, 1905–1914. [Google Scholar] [CrossRef]
- McCafferty, E. Validation of corrosion rates measured by the Tafel extrapolation method. Corros. Sci. 2005, 47, 3202–3215. [Google Scholar] [CrossRef]
- Yan, Y.; Li, W.; Cai, L.; Hou, B. Electrochemical and quantum chemical study of purines as corrosion inhibitors for mild steel in 1 M HCl solution. Electrochim. Acta 2008, 53, 5953–5960. [Google Scholar] [CrossRef]
- Atta, A.M.; Dyab, A.K.F.; Al-Lohedan, H.A. Micellization and adsorption behaviors of new reactive polymerizable surfactants based on modified nonyl phenol ethoxylates. J. Surfactants Deterg. 2013, 16, 343–355. [Google Scholar] [CrossRef]
- Sample Availability: Samples of the NMA and AMPS/NIPAm-Ag are available from the authors.
© 2014 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution license ( http://creativecommons.org/licenses/by/3.0/).
Share and Cite
Atta, A.M.; El-Mahdy, G.A.; Al-Lohedan, H.A.; Ezzat, A.O. Synthesis and Application of Hybrid Polymer Composites Based on Silver Nanoparticles as Corrosion Protection for Line Pipe Steel. Molecules 2014, 19, 6246-6262. https://doi.org/10.3390/molecules19056246
Atta AM, El-Mahdy GA, Al-Lohedan HA, Ezzat AO. Synthesis and Application of Hybrid Polymer Composites Based on Silver Nanoparticles as Corrosion Protection for Line Pipe Steel. Molecules. 2014; 19(5):6246-6262. https://doi.org/10.3390/molecules19056246
Chicago/Turabian StyleAtta, Ayman M., Gamal A. El-Mahdy, Hamad A. Al-Lohedan, and Abdurrahman O. Ezzat. 2014. "Synthesis and Application of Hybrid Polymer Composites Based on Silver Nanoparticles as Corrosion Protection for Line Pipe Steel" Molecules 19, no. 5: 6246-6262. https://doi.org/10.3390/molecules19056246