Bioconversion of Cheese Whey and Food By-Products by Phaeodactylum tricornutum into Fucoxanthin and n-3 Lc-PUFA through a Biorefinery Approach
Next Article in Special Issue
Releasing Bioactive Compounds from Brown Seaweed with Novel Cold-Adapted Alginate Lyase and Alcalase
Previous Article in Journal
Fatty Acids in Waste Tissues: The Nutraceutical Value of Gonads and Livers from the Moroccan Hypophthalmichthys molitrix and Cyprinus carpio Fishes
Previous Article in Special Issue
Alginates Combined with Natural Polymers as Valuable Drug Delivery Platforms
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Alginate-Based Biomaterials in Tissue Engineering and Regenerative Medicine

by
Nima Farshidfar
1,
Siavash Iravani
2,* and
Rajender S. Varma
3,*
1
Orthodontic Research Center, School of Dentistry, Shiraz University of Medical Sciences, Shiraz 71348-14336, Iran
2
Faculty of Pharmacy and Pharmaceutical Sciences, Isfahan University of Medical Sciences, Isfahan 81746-73461, Iran
3
Institute for Nanomaterials, Advanced Technologies and Innovation (CxI), Technical University of Liberec (TUL), 1402/2, 461 17 Liberec, Czech Republic
*
Authors to whom correspondence should be addressed.
Mar. Drugs 2023, 21(3), 189; https://doi.org/10.3390/md21030189
Submission received: 2 March 2023 / Revised: 17 March 2023 / Accepted: 17 March 2023 / Published: 18 March 2023
(This article belongs to the Special Issue Alginate-Based Biomaterials and Drug Delivery 2nd Edition)

Abstract

:
Today, with the salient advancements of modern and smart technologies related to tissue engineering and regenerative medicine (TE-RM), the use of sustainable and biodegradable materials with biocompatibility and cost-effective advantages have been investigated more than before. Alginate as a naturally occurring anionic polymer can be obtained from brown seaweed to develop a wide variety of composites for TE, drug delivery, wound healing, and cancer therapy. This sustainable and renewable biomaterial displays several fascinating properties such as high biocompatibility, low toxicity, cost-effectiveness, and mild gelation by inserting divalent cations (e.g., Ca2+). In this context, challenges still exist in relation to the low solubility and high viscosity of high-molecular weight alginate, high density of intra- and inter-molecular hydrogen bonding, polyelectrolyte nature of the aqueous solution, and a lack of suitable organic solvents. Herein, TE-RM applications of alginate-based materials are deliberated, focusing on current trends, important challenges, and future prospects.

1. Introduction

The primary aim of tissue engineering and regenerative medicine (TE-RM) is to create biological substitutes in order to maintain, enhance, or restore damaged tissues/organs [1,2,3,4,5]. It is well known that the application of different types of cells is considered as the most fundamental component of TE-RM strategies [6,7]. However, it has been revealed that following free cell therapy, only a small proportion of cells are viable at the targeted site, and ~90% of them are lost within a few hours after administration [8]. To overcome this challenge, the utilization of cells in combination with biomaterials offers a favorable microenvironment for tissue regeneration [6,9]. Biomaterials are commonly deployed to efficiently transport cells and/or biological factors while also providing an appropriate milieu for cell survival and proliferation [10,11,12,13]. A wide variety of natural and synthetic biomaterials have been introduced that allow the natural deposition of extracellular matrix (ECM) and the regeneration of injured tissues [14].
Alginate, an anionic and hydrophilic polysaccharide, is one of the most abundant biosynthesized biomaterials worldwide [15]. This natural biomaterial is primarily derived from brown seaweed and bacteria (i.e., Pseudomonas and Azotobacter) [16]. Alginate is also commercially produced using various marine algae such as Laminaria hyperborea, Laminaria digitata, Macrocystis pyrifera, Ascophyllum nodosum, Eclonia maxima, Laminaria japonica, Lessonia nigrescens, Durvillea antarctica, and Sargassum spp. [17]. Alginate contains one thousand blocks of β-d-mannuronic acid (M) and α-l-guluronic acid (G) monomers connected via 1→4 linkage. The blocks are typically composed of three different forms of polymer segments G-block, M-block, and GM-block (Figure 1) [18,19]. Alginate-based biomaterials are developed into different forms such as hydrogels, foams, sponges, fibers, microspheres, and microcapsules using various fabrication techniques [20,21,22]. Nevertheless, alginate hydrogels are of great interest for a wide range of applications, particularly as the supporting matrix or delivery system for tissue repair and regeneration [23]. There are different physicochemical crosslinking approaches (covalent or non-covalent) for fabricating alginate hydrogels that are highly dependent on structure types (Figure 2) [23]. In this context, chelating with divalent cations (Mg2+, Ca2+, etc.) is the easiest and most cost-effective way to fabricate alginate hydrogels from an aqueous solution under mild conditions [24,25,26,27].
Alginate and its hydrogels have been widely employed in TE-RM due to its outstanding properties in terms of hygroscopicity, biocompatibility, biodegradability, non-toxicity, flexibility, and chelating ability [24,28,29]. However, alginate alone has some drawbacks (high viscosity, low solubility, poor degradability, etc.) which hinder its potential for further biomedical applications [30]. To overcome this problem, a wide range of natural or synthetic biomaterials have been incorporated into the alginate structure to enhance its properties and multifunctionality [30]. In addition, modifications of alginate hydrogels with various nanomaterials have recently garnered immense attention, leading to their wide-ranging applications in the biomedical field [17]. There are several fabrication methods deployed for synthesizing alginate-based nanomaterials, the most prominent ones being illustrated in Figure 3. These methods include but are not limited to the controlled gelification, spray drying, electrospinning/electro-spraying, ionotropic gelation, thermally-induced phase separation, microfluidics-aided polyelectrolyte complexation, etc. [17,27,28,30].
Due to the pH-dependent anionic nature of alginate, it has the ability to bind and interact with cationic polyelectrolytes and proteoglycans. These simple electrostatic interactions have been exploited to create delivery systems for cationic drugs and molecules [29]. Alginate hydrogels have also been considered as favorable matrices for the immobilization of various responsive biomaterials and proteins which results in a variety of stimuli-responsive nanosystems for cancer treatment. In addition, alginate-based biomaterials are suitable carriers for gene therapeutic agents owing to their high cell transfection ability for many genes. The networks of alginate-based scaffolds also provide a suitable microenvironment for the cultivation and delivery of therapeutically useful stem cells [31]. For TE-RM, alginate-based scaffolds have been applied in the regeneration of both hard and soft tissues such as skin, bone, cartilage, heart, vascular tissues, etc. [32]. Based on the aforementioned information, alginate, a Food and Drug Administration (FDA)-approved polymer, has become one of the most promising biomaterials for a wide range of TE-RM applications [15,33]. Alginate-based biomaterials have been deployed for TE-RM in the forms of hydrogels/gels, films, fibers, gauzes, foams, wafers, etc. [34]. In this context, their several advantages have been mentioned, including their high porosity and surface area (sponges), inexpensive and easy-to-manufacture nature (gauzes), strong absorption capacity (nanofibers), facilitated cell migration ability (hydrogels), among others [35,36]. The most common technique of alginate gel preparation is ionic crosslinking with multivalent cations such as Ca2+, as exemplified in the case of alginate-pectin hydrogel film for diabetic wound healing [37]. Other techniques such as covalent crosslinking (e.g., alginate/chitosan/gelatin hydrogel) [38], enzymatic crosslinking [39], polyelectrolyte crosslinking (e.g., chitosan/alginate hydrogel for bone regeneration) [40], and self-assembly technique (e.g., alginate-based cyclodextrin/azo-polyacrylamide hydrogel) [41], have been introduced.
Alginate with the advantages of biocompatibility and ease of integration with drugs and cells can be simply processed into 3D scaffolding materials such as hydrogels, foams, sponges, microcapsules, microspheres, and fibers [29,42]. However, pure alginate has limited features (e.g., weak mechanical strength), restricting its future clinical applications; thus, suitable hybridization or combination with other materials can improve its properties for TE-RM. One of the disadvantages of using alginate-based biomaterials is that they have poor cell adhesion properties. In addition, the degradation rate of alginate is variable and should be improved depending on its applications [15]. Remarkably, alginate-based biomaterials have several advantages over chitosan-based biomaterials, such as excellent biocompatibility, biodegradability, and low toxicity. Alginate hydrogels can be simply prepared by crosslinking with divalent cations, offering suitable candidates for TE-RM. In addition, alginate hydrogels offer good mechanical features and can be modified to control their degradation rate. Despite the biocompatibility and biodegradability of chitosan-based biomaterials, chitosan has poor solubility in water at a neutral pH, limiting its applications in TE-RM. On the other hand, chitosan-based hydrogels exhibited the disadvantage of low mechanical resistance, difficulty in controlling the pore size, and uncontrollable dissolution, which restrict their future clinical applications [43]. In addition, chitosan has limited mechanical strength and needs chemical modifications to improve its characteristics. It appears that alginate-based biomaterials have several advantages over chitosan-based biomaterials owing to their high biocompatibility, ease of formation into hydrogels, adjustable degradation rate, and good mechanical features [43,44]. This review endeavored to elaborately discuss the current applications of alginate-based biomaterials in TE-RM, with a focus on recent advancements, important challenges, and future perspectives.

2. TE-RM Applications

Several alginate-based composites have been constructed for TE-RM purposes (Table 1). In this context, their biocompatibility and immunogenicity still ought to be systematically evaluated [29,45]. In addition, clinical translational studies and biodegradability improvements still need additional efforts; oxidized alginate displays suitable biodegradability at physiological conditions and can be deployed for targeted drug/cell delivery [45]. For instance, alginate-based hydrogels have been constructed from oxidized alginate, polyethylene glycol (PEG), and carboxymethyl chitosan or gelatin [46]. These hydrogels with a significant degree of crosslinking exhibited the capability of surviving and proliferating mesenchymal stem cells (MSCs), offering them as suitable candidates for injectable self-crosslinking deployment in TE [46]. In another study, thermal-sensitive hydrogels were developed using cystamine-functionalized sodium alginate-g-pluronic F127, showing suitable antibacterial activities and good biocompatibility for long-term cell cultivation [47]. It was revealed that fibroblasts could attach to the hydrogels, which effectively mimic the porous structure of these hydrogels after five days of culture. Such alginate-based composites have been deployed as attractive cellular delivery platforms for versatile TE applications [47]. Overall, the prospects for clinical translation of alginate-based biomaterials are promising because of their biocompatibility and ease of modifications [48]. Some alginate-based composites have been approved by regulatory agencies (such as the FDA) for wound dressings; they have passed clinical assessments and are now available on the market [30,49]. For instance, Kaltostat® (based on calcium alginate or sodium alginate) is one of the commercial wound dressings in the shape of absorbent gel-fiber matrices with fluid contact, thus facilitating atraumatic removal and hemostatic effects as well as helping to control minor bleeding [30]. In another study, alginate-silver wound dressing (Askina® Calgitrol® Ag) was clinically evaluated on patients to compare its activity with the 1% silver sulfadiazine in the outpatient management of partial-thickness burn wounds [50]. Additionally, Emdogain® (Straumann) is a clinically available injectable hydrogel product (porcine enamel matrix derivatives in propylene glycol alginate gel) for the regeneration of periodontal tissue [51].

2.1. Musculoskeletal TE-RM

Scaffolds applied for bone TE and tissue regeneration should have good biocompatibility, osteoconductivity, and biodegradability/bioactivity, along with the promotion of osseointegration as well as stimulation of ingrowth and differentiation of bone [70,71,72]. Different alginate-based composites have been introduced for bone TE applications, including alginate-polymers (e.g., chitosan or PEG), alginate-biosilica, alginate-ceramics, alginate-bioglasses, alginate-bone morphogenetic protein-2, and alginate-proteins (e.g., collagen or gelatin). These composites have shown improved cell adhesion/proliferation, biocompatibility, porosity, mechanical strength, along with alkaline phosphatase (ALP) enhancement, great mineralization, and osteogenic differentiation [28]. Tao et al. [73] prepared polycaprolactone/carboxymethyl chitosan/sodium alginate composite micron-fibers (~2.381 μm) with excellent tensile strength as a scaffold for bone TE through an emulsion electrospinning process, which could facilitate the osteoblast adhesion. The composite could up-regulate the primary expression of osteogenic genes ALP and Runt-related transcription factor 2 (RUNX2), displaying high biocompatibility and osteoinductive potential to osteoblasts. Such composites should be further explored as transplantable scaffolds for treating large-segment bone defects [73]. In another study, an electrospun nanofiber mesh tube was introduced for directing bone regeneration combined with peptide-modified alginate hydrogel injected inside the tube for the controlled release of growth factor (Figure 4). The hybrid delivery system was capable of transferring recombinant bone morphogenetic protein-2 (rhBMP-2) to heal the critically-sized segmental bone defects in a rat model [74]. Despite several advantages of hydrogels, their deployment for repairing bone defects is difficult due to the poor mechanical features and rapid degradation, restricting their bone TE applications. Thus, future explorations ought to be conducted towards the improvement of their mechanical and osteoinductive features through the combination/hybridization with other materials/polymers. In one study, Yan et al. [75] introduced injectable and biodegradable alginate/hydroxyapatite gel scaffolds combined with gelatin microspheres for TE. The addition of hydroxyapatite and gelatin microspheres could improve the mechanical features of these scaffolds, stabilizing the gel network as well as decreasing weight loss, swelling ratio, and gelation time. The alginate-based gel scaffolds with suitable physical activity and bioactive features offer great opportunities for bone TE applications [75].
Alginate-based chitosan hybrid structures were introduced with suitable supporting capabilities for fibroblast adhesion [76]. Compared to the alginate polymer fibers, the prepared alginate-based chitosan hybrid polymer fibers exhibited excellent tensile strength (>200 MPa), offering enhanced adhesion capacity with fibroblasts. After morphologic assessments, it was indicated that the dense fibers of the type I collagen could be generated by the fibroblast in the designed hybrid biomaterials, paving a way for the construction of biomaterial scaffolds with great potential for tendon and ligament TE [76]. Zhou et al. [77] introduced degradable alginate/palygorskite hybrid hydrogels with suitable biocompatibility and robust mechanical features, showing excellent potential for bone defect repair. By increasing the content of palygorskite, the modified hydrogels exhibited improved mechanical features, along with an increased swelling ratio in phosphate-buffered saline (pH = 7.4). The in vitro assessments on bone marrow-derived mesenchymal stem cells (BMSCs) revealed that these composites were cytocompatible after 1, 3, and 7 days [77]. They were loaded with JWH133 (as an agonist of cannabinoid receptor type 2, showing anti-osteoclastogenic and anti-inflammatory effects) to enhance the osteogenic differentiation of rat BMSCs, showing efficient inhibitory effects towards osteoclast generation and the mRNA expression of osteoclast-specific markers. The results of this study indicated that the drug-loading capacity and biocompatibility of alginate-based hydrogels can be improved by suitable modification, paving the way to achieve promising drug carriers against osteoporosis [77]. In addition, 3D-printed scaffolds with desired pore sizes were constructed from sodium alginate and chitosan biomaterials for bone TE and regeneration, exhibiting appropriate capabilities for cell attachment and proliferation. These biocompatible scaffolds with high tensile strength (~0.387 ± 0.015 MPa) exhibited adjustable swelling and degradation manner as well as superb biological properties [78].
Despite several natural or synthetic polymers introduced for cartilage TE, alginate-based composites with tunable mechanical properties and easy manufacturing processes have acquired significant attention [79]. A platelet-rich plasma/sodium alginate-based hydrogel was embedded in a porous 3D scaffold of chitosan/chondroitin sulfate/silk fibroin to obtain a hybrid scaffold for cartilage TE applications, showing a uniform distribution of cells and mimicking gel-like cartilage tissue ECM [80]. The matrix exhibited suitable porosity (~77 ± 4.3%) with compressive strength (~0.13 MPa), offering promising structures for cartilage TE. Notably, the introduced cartilage structure exhibited improved metabolic activities, glycosaminoglycan deposition, and collagen type II expression [80]. In addition, a 3D printed scaffold was developed from a double crosslinked alginate hydrogel, in which human umbilical cord MSCs could differentiate into chondrocytes on it after 4 weeks of culturing [81]. After the modification of alginate with L-cysteine and 5-norbornene-2-methylamine, the double crosslinked alginate hydrogels with robust mechanical features similar to natural cartilage were fabricated utilizing CaCl2 under ultraviolet light. These hydrogels exhibited long-term stability in Dulbecco’s modified eagle medium (>1 month) with suitable viability for human umbilical cord MSCs. In addition, the expression of chondrogenic genes (e.g., asaggrecan, collagen II, and SRY-box transcription factor-9) could be obtained after culture of human umbilical cord MSCs (4 weeks) in the 3D-printed scaffolds, showing great potential for cartilage repair [81].

2.2. Cardiovascular TE-RM

Alginate-based polyurethane elastomers benefiting from the presence of two physical networks of different strengths of soft tertiary ammonium-soft sulfate pairs (as robust ionic bonds) and soft tertiary ammonium-hard carboxylate groups (as the weak bonds) were deployed for vascular TE applications [82]. Notably, considerable toughness/stretchability along with suitable energy dissipation could be obtained due of the existence of sulfate groups, which led to a low Young’s modulus, as well as being endowed with unique self-healing properties. In addition, improved endothelial cell attachment, enhanced anticoagulation performance, and lower platelet adhesion could be obtained, offering these elastomers as attractive candidates for vascular TE applications; the implanted scaffold exhibited low fibrosis and slow biodegradation (within two months) [82]. In addition, alginate dialdehyde was combined with gelatin and MSCs to improve the vascularization capability, along with de novo tissue generation. As a result, alginate dialdehyde-gelatin microcapsules exhibited efficient vascularization by applying an arteriovenous loop tactic, along with enhanced biocompatibility and biodegradability [83].
Tubular alginate-based hydrogels combined with collagen type I were fabricated with high mechanical stability and low swelling ratio through an ionotropic gelation process for blood vessel engineering [84]. The alginate solutions were exposed to Ca2+-loaded gelatin for controlling the wall thickness of the hydrogels; a second crosslinking phase with barium chloride could prevent their degradation for ~14 days and improve mechanical features by two-fold. It has been revealed that alginate-based hydrogels enriched with collagen were capable of successfully supporting EA.hy926 and MRC-5 cells’ growth and characteristic phenotype, showing promising potential for fabricating freestanding vascular substitutes with controllable features [84]. Additionally, stem cell implantation tactics with promising potentials for the treatment of myocardial infarction (MI) still have some drawbacks, such as low retention and survival, limiting their application due to the reactive oxygen species (ROS) microenvironment after MI [85]. Hao et al. [85] incorporated fullerenol nanoparticles into alginate hydrogel to obtain an injectable cell delivery vehicle with antioxidant properties. The hydrogels with excellent injectability and mechanical strength could successfully scavenge the superoxide anion and hydroxyl radicals; they had no cytotoxicity effects on brown adipose-derived stem cells, thereby suppressing the oxidative stress damage of brown adipose-derived stem cells and improving their survival capacity under an ROS microenvironment through the activation of the extracellular signal-regulated kinase (ERK) and p38 pathways while obstructing the c-Jun N-terminal kinase (JNK) pathway. These fullerenol/alginate hydrogels could effectively reduce the ROS level in the MI region, improving the retention and survival of implanted brown adipose-derived stem cells and inducing the angiogenesis to stimulate the recovery of cardiac functions [85].

2.3. Neural TE-RM

Alginate-polyvinyl alcohol hydrogel was deployed as a supportive biomaterial for 3D neural cell cultures, showing stiffness quite similar to brain tissue; neuronal dispersal and 3D network generation could be improved inside the softest hydrogels [86]. In addition, alginate-based hydrogels with a highly anisotropic capillary structure were evaluated for an axon outgrowth assay (in vitro) and healing of spinal cord lesions (in vivo) [87]. Accordingly, the alginate-based scaffolds provoked the regrowth of a vastly oriented linear axon and targeted the re-innervation of a neuron. Notably, alginate-based hydrogels were joined to the spinal cord parenchyma without noticeable inflammatory reactions after implantation into acute cervical spinal cord lesions in adult rats, maintaining their anisotropic structure; they could also stimulate the directed regeneration of axons across the artificial scaffolds. Adult neural progenitor cells with stimulatory effects towards cell-contact-mediated axon regeneration have been seeded into alginate-based hydrogels, improving the regenerative potential of the artificial growth-supportive matrices. Such alginate-based hydrogels can be deployed for inducing directed nerve regrowth after spinal cord injuries [87].

2.4. Corneal TE-RM

Alginates with biocompatibility, non-toxicity, and biodegradability can be deployed for corneal TE-RM, but more elaborative studies are still required to overcome the challenges pertaining to the optimal manufacturing and processing conditions for obtaining alginate-based composites with specific properties [88]. A micro-patterned bioadhesive film with a double-layered structure was developed using silk nanofibrils and gelatin methacrylate-alginate, leading to the sustained release of ascorbic acid for corneal regeneration as well as stimulation of the attachment, alignment, and proliferation of corneal stroma cells (Figure 5) [89]. This hybrid composite film could facilitate the adhesion and orientation of corneal stroma cells, showing suitable mechanical robustness and light transmission owing to the presence of the silk nanofibril/gelatin methacrylate layer; an alginate layer could provide robust adhesion to the tissue. The evaluations indicated that 90% of cells aligned at an angle of 0–20° to the perpendicular axis, signifying the significance of surface micro-patterning to mimic the morphology of the corneal stroma tissue. After accomplishing the optimization process on micro-patterned film, the tensile features near those of native tissue along with the excellent transparency that could be obtained, rendered this composite film suitable for stroma TE-RM [89]. In addition, the alginate-chitosan hydrogel was introduced for limbal stem cells transplantation (in situ), inducing corneal reconstruction after corneal alkali burns [90]. Accordingly, the highly transparent hydrogel with good biocompatibility and low cytotoxicity could be shaped on the wound surface through self-crosslinking with no need for chemical crosslinking components. The hydrogel could significantly improve epithelial reconstruction, leading to rapid and efficient corneal wound healing [90]. It appears that several challenges still exist to specifically control the mechanical and degradation properties of these alginate-based composites for corneal TE-RM purposes [88]. The blend of alginate hydrogels with the protein derived from the ECM (e.g., gelatin and collagen) could provide an improvement in cell adherence, proliferation, and viability in alginate networks. At the post-crosslinking stages, the utilization of suitable chelating agents along with the employment of oxidized alginate form could help improve the biodegradability, drug kinetic release, and functionality of the final alginate-based TE composites [88].

2.5. Skin TE-RM and Wound Healing

Various types of alginate-based materials have been introduced for wound healing and dressings, including hydrogels/gels, films, fibers, gauzes, foams, wafers, etc. [91]. For instance, vitamin E-loaded hydrogels with biodegradability and high porosity (~89.2 ± 12.5%) were developed using alginate and chitosan for skin TE-RM, showing improved healing properties. As a result, the hydrogel-based dressings exhibited promising potential to treat skin injuries in the clinic [92]. Cai et al. [93] introduced a high-water-absorbing calcium alginate fibrous scaffold prepared after microfluidic spinning and centrifugal reprocessing. The scaffolds with biocompatibility could mimic the ECM, offering promising candidates for the healing of chronic wounds and wound dressings [93]. In another study, a hydroxylated lecithin complexed iodine/carboxymethyl chitosan/sodium alginate composite membrane was prepared using a microwave drying process, which displayed high contents of activated iodine (as antibacterial agents) as well as improved mechanical and swelling properties [94]. These membranes with suitable water vapor permeability exhibited pH-controllable iodine release and high antibacterial effects, which could be deployed for treating chronic wounds and repairing open trauma infections [94].
Different adhesive peptides or natural/synthetic polymers have been incorporated into alginate fibers to provide desired physicochemical properties and functionality [27]. 3D alginate-based composites were constructed for wound healing applications with high stability and porous architectures [95]. Accordingly, the utilization of the freeze-dried gel of Aloe vera could accelerate the water uptake ability of these scaffolds and also the employed aqueous leaf extracts of Moringa oleifera could provide suitable antioxidant, anti-inflammatory, and antimicrobial effects. The scaffolds containing plant extracts and Ca-alginate-polyethylene glycol (PEG)-methyl ether methacrylate exhibited an enhanced cell proliferation capability [95]. In addition, bioinspired alginate/gum Arabic hydrogels were constructed to transfer mitsugumin protein for cell membrane treatment and chronic wound healing (Figure 6) [96]. The introduced sundew-inspired hydrogel exhibited biphasic-kinetics release behavior, facilitating rapid delivery of mitsugumin 53 to improve the re-epithelization procedure of the wounds and sustained release of the protein to treat chronic wounds. Such hydrogels with tunable structures and unique physicochemical features can be deployed as promising delivery vehicles for the healing of chronic wounds [96].

2.6. Dental TE-RM

Today, studies have focused on using alginate-based biomaterials in dental TE-RM; alginate hydrogels with non-toxicity can be deployed for directing the differentiation of dental-derived stem cells [97,98]. In addition, injectable hydrogels can be deployed as carriers with excellent potential to incorporate cells or growth factors for dental tissue regeneration [99]. In one study, self-crosslinkable hydrogels were constructed from oxidized alginate and carboxymethyl chitosan as cell carriers for dental enamel regeneration (in vitro), showing suitable self-healing property. These hydrogels also exhibited antibacterial activities against Streptococcus mutans and Streptococcus sobrinus. After in vitro enamel regeneration studies, it was revealed that the dental epithelial cell line, HAT-7, had high cell viability in the injected hydrogels [99]. In addition, an injectable, non-toxic, and biodegradable scaffold was developed using oxidized alginate microbeads, which encapsulated periodontal ligament and gingival MSCs [97]. Compared to the control group, these alginate hydrogels were capable of directing the differentiation of these stem cells to osteogenic and adipogenic tissues (in vitro); these encapsulated stem cells could be viable (in vitro) as well as osteo- and adipo-differentiated after four weeks of culturing in the induction media. Remarkably, the alginate hydrogels had a tunable chemistry and degradation rate, and their degradation profile and swelling kinetics significantly depended on the degree of oxidation [97].
Due to their biocompatibility and biodegradability properties, alginate-based scaffolds are promising candidates in dental TE-RM, especially after suitable modification with definite ligands or combined with other substances. An alginate/hydroxyapatite-based nanocomposite scaffold was constructed for bone TE to enhance dental pulp biomineralization and differentiation. As a result, human dental pulp stem cells expressed osteogenic differentiation-related markers and promoted calcium deposition and biomineralization after growing onto the scaffold [100]. Zhu et al. [101] reported that after the combination of alginate with other materials, self-adhesive hydrogels could be designed for dental pulp regeneration. A calcium alginate hydrogel was combined with dental pulp stem cells and fibroblast growth factor 21 for promoting recovery after spinal cord hemi-section in mice through the regulation of apoptosis and autophagy, offering potential for hemi-section spinal cord injury treatment [101]. Liang et al. [102] introduced core-shell microcapsules constructed from gelatin methacryloyl-alginate for the encapsulation of both human dental pulp stem cells and human umbilical vein endothelial cells. Remarkably, human umbilical vein endothelial cells could promote the osteo/odontogenic differentiation of human dental pulp stem cells in microcapsules. In vivo assessments revealed the improved micro-vessel generation and pulp-like tissue regeneration, offering promising candidates for pre-vascularization micro-tissue formation as well as endodontic regeneration and TE purposes [102].

3. Conclusions and Perspectives

Alginate-based biomaterials have been widely exploited for drug/gene delivery, cancer theranostics, antimicrobial agents, wound dressing/healing, and tissue regeneration applications because of their biocompatibility, cost-effectiveness, and ease of processing/functionalization, among others. Remarkably, alginates can be considered as promising biomaterials for bioinks due to their good biosafety and rapid ionic gelation. However, ionically crosslinked alginate hydrogels have the disadvantages of insufficient mechanical properties and long-term stability owing to ion exchange. Furthermore, alginate-based scaffolds still require additional improvements pertaining to their biodegradability, stability, and mechanical properties before they can be routinely applied in clinical stages; these scaffolds should provide suitable structures with optimal cellular activities. In this context, alginate-based hydrogels comprised of collagen or agarose have shown excellent potential as scaffolds for TE-RM due to their good biocompatibility/biodegradability along with their similarity to the natural ECM; thus, offering 3D support for cellular growth and tissue regeneration. Alginate-based biomaterials can also be deployed for the delivery of drugs/therapeutic agents with sustained release behavior, showing improved biodistribution/dissolution rate, bioavailability, and targeting properties. The delivery systems that are composed of these biomaterials have shown improved stability in the acidic environments of physiological fluids. However, systematic in vivo and clinical translational studies as well as biosafety/biocompatibility assessments are still warranted for evaluating their clinical efficacy. Remarkably, finding the optimal manufacturing conditions focusing on solubility, reactivity, and characterizations can help to obtain efficient alginate-based composites with TE-RM applications. Overall, the renewable and sustainable biomaterials can be utilized in hybridization or modification processes to design next-generation alginate-based composites with multi-functionalities.

Author Contributions

N.F.: conceptualization, writing-review; S.I. and R.S.V.: conceptualization, writing-review, and editing. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

There are no conflicts of interest.

References

  1. Farshidfar, N.; Tanideh, N.; Emami, Z.; Sari Aslani, F.; Sarafraz, N.; Khodabandeh, Z.; Zare, S.; Farshidfar, G.; Nikoofal-Sahlabadi, S.; Tayebi, L.; et al. Incorporation of curcumin into collagen-multiwalled carbon nanotubes nanocomposite scaffold: An in vitro and in vivo study. J. Mater. Res. Technol. 2022, 21, 4558–4576. [Google Scholar] [CrossRef]
  2. Khodabandeh, Z.; Tanideh, N.; Aslani, F.S.; Jamhiri, I.; Zare, S.; Alizadeh, N.; Safari, A.; Farshidfar, N.; Dara, M.; Zarei, M. A Comparative in Vitro and in Vivo Study on Bone Tissue Engineering Potential of the Collagen/Nano-Hydroxyapatite Scaffolds Loaded with Ginger Extract and Curcumin. Mater. Today Commun. 2022, 31, 103339. [Google Scholar] [CrossRef]
  3. Hernández-González, A.C.; Téllez-Jurado, L.; Rodríguez-Lorenzo, L.M. Alginate hydrogels for bone tissue engineering, from injectables to bioprinting: A review. Carbohydr. Polym. 2020, 229, 115514. [Google Scholar] [CrossRef] [PubMed]
  4. Hickey, R.J.; Pelling, A.E. Cellulose biomaterials for tissue engineering. Front. Bioeng. Biotechnol. 2019, 7, 45. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  5. Hutmacher, D.W. Scaffolds in tissue engineering bone and cartilage. Biomaterials 2000, 21, 2529–2543. [Google Scholar] [CrossRef]
  6. Rahmati, M.; Pennisi, C.P.; Budd, E.; Mobasheri, A.; Mozafari, M. Biomaterials for Regenerative Medicine: Historical Perspectives and Current Trends. Cell Biology and Translational Medicine. Stem Cells Cell Based Strateg. Regen. 2018, 4, 1–19. [Google Scholar]
  7. Amiri, M.A.; Farshidfar, N.; Hamedani, S. The Feasibility of Craniofacial-Derived Bone Marrow Stem Cells for the Treatment of Oral and Maxillofacial Hard Tissue Defects. J. Dent. Sci. 2022, 17, 1445. [Google Scholar] [CrossRef]
  8. Mooney, D.J.; Vandenburgh, H. Cell Delivery Mechanisms for Tissue Repair. Cell Stem Cell 2008, 2, 205–213. [Google Scholar] [CrossRef] [Green Version]
  9. Farshidfar, N.; Jafarpour, D.; Firoozi, P.; Sahmeddini, S.; Hamedani, S.; de Souza, R.F.; Tayebi, L. The Application of Injectable Platelet-Rich Fibrin in Regenerative Dentistry: A Systematic Scoping Review of In Vitro and In Vivo Studies. Jpn. Dent. Sci. Rev. 2022, 58, 89–123. [Google Scholar] [CrossRef]
  10. Farshidfar, N.; Amiri, M.A.; Jafarpour, D.; Hamedani, S.; Niknezhad, S.V.; Tayebi, L. The Feasibility of Injectable PRF (I-PRF) for Bone Tissue Engineering and Its Application in Oral and Maxillofacial Reconstruction: From Bench to Chairside. Biomater. Adv. 2022, 134, 112557. [Google Scholar] [CrossRef]
  11. Lee, K.Y.; Mooney, D.J. Hydrogels for tissue engineering. Chem. Rev. 2001, 101, 1869–1879. [Google Scholar] [CrossRef] [PubMed]
  12. Macarthur, B.D.; Oreffo, R.O. Tissue engineering: Mathematical models are helping to take tissue engineering from concept to reality. Nature 2005, 433, 19–20. [Google Scholar] [CrossRef] [PubMed]
  13. Mallick, K.K.; Cox, S.C. Biomaterial scaffolds for tissue engineering. Front. Biosci. 2013, 5, 341–360. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  14. Perez, R.A.; Won, J.-E.; Knowles, J.C.; Kim, H.-W. Naturally and Synthetic Smart Composite Biomaterials for Tissue Regeneration. Adv. Drug. Deliv. Rev. 2013, 65, 471–496. [Google Scholar] [CrossRef] [PubMed]
  15. Sahoo, D.R.; Biswal, T. Alginate and its application to tissue engineering. SN Appl. Sci. 2021, 3, 30. [Google Scholar] [CrossRef]
  16. Ertesvåg, H. Alginate-Modifying Enzymes: Biological Roles and Biotechnological Uses. Front. Microbiol. 2015, 6, 523. [Google Scholar]
  17. Shanura Fernando, I.P.; Lee, W.W.; Han, E.J.; Ahn, G. Alginate-based nanomaterials: Fabrication techniques, properties, and applications. Chem. Eng. J. 2020, 391, 123823. [Google Scholar] [CrossRef]
  18. Abasalizadeh, F.; Moghaddam, S.V.; Alizadeh, E.; Akbari, E.; Kashani, E.; Fazljou, S.M.B.; Torbati, M.; Akbarzadeh, A. Alginate-Based Hydrogels as Drug Delivery Vehicles in Cancer Treatment and Their Applications in Wound Dressing and 3D Bioprinting. J. Biol. Eng. 2020, 14, 8. [Google Scholar] [CrossRef]
  19. Wei, Q.; Zhou, J.; An, Y.; Li, M.; Zhang, J.; Yang, S. Modification, 3D printing process and application of sodium alginate based hydrogels in soft tissue engineering: A review. Int. J. Biol. Macromol. 2023, 232, 123450. [Google Scholar]
  20. Bhattarai, N.; Li, Z.; Edmondson, D.; Zhang, M. Alginate-Based Nanofibrous Scaffolds: Structural, Mechanical, and Biological Properties. Adv. Mater. 2006, 18, 1463–1467. [Google Scholar] [CrossRef]
  21. Lakkakula, J.R.; Gujarathi, P.; Pansare, P.; Tripathi, S. A comprehensive review on alginate-based delivery systems for the delivery of chemotherapeutic agent: Doxorubicin. Carbohydr. Polym. 2021, 259, 117696. [Google Scholar] [CrossRef] [PubMed]
  22. Lee, K.Y.; Mooney, D.J. Alginate: Properties and biomedical applications. Prog. Polym. Sci. 2012, 37, 106–126. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  23. Zhang, M.; Zhao, X. Alginate Hydrogel Dressings for Advanced Wound Management. Int. J. Biol. Macromol. 2020, 162, 1414–1428. [Google Scholar] [CrossRef] [PubMed]
  24. Iravani, S.; Varma, R.S. Alginate-Based Micro- and Nanosystems for Targeted Cancer Therapy. Mar. Drugs 2022, 20, 598. [Google Scholar] [CrossRef]
  25. Tawfik, S.M.; Sharipov, M.; The Huy, B.; Gerelkhuu, Z.; Biechele-Speziale, D.; Lee, Y.-I. Naturally modified nonionic alginate functionalized upconversion nanoparticles for the highly efficient targeted pH-responsive drug delivery and enhancement of NIR-imaging. J. Ind. Eng. Chem. 2018, 57, 424–435. [Google Scholar] [CrossRef]
  26. Yildirim, E.D.; Yin, X.; Nair, K.; Sun, W. Fabrication, characterization, and biocompatibility of single-walled carbon nanotube-reinforced alginate composite scaffolds manufactured using freeform fabrication technique. J. Biomed. Mater. Res. B Appl. Biomater. 2008, 87, 406–414. [Google Scholar] [CrossRef]
  27. Zdiri, K.; Cayla, A.; Elamri, A.; Erard, A.; Salaun, F. Alginate-Based Bio-Composites and Their Potential Applications. J. Funct. Biomater. 2022, 13, 117. [Google Scholar] [CrossRef]
  28. Venkatesan, J.; Bhatnagar, I.; Manivasagan, P.; Kang, K.-H.; Kim, S.-K. Alginate composites for bone tissue engineering: A review. Int. J. Biol. Macromol. 2015, 72, 269–281. [Google Scholar] [CrossRef]
  29. Sun, J.; Tan, H. Alginate-Based Biomaterials for Regenerative Medicine Applications. Materials 2013, 6, 1285–1309. [Google Scholar] [CrossRef]
  30. Raus, R.A.; Nawawi, W.M.F.W.; Nasaruddin, R.R. Alginate and Alginate Composites for Biomedical Applications. Asian J. Pharm. Sci. 2021, 16, 280–306. [Google Scholar] [CrossRef]
  31. Sood, A.; Dev, A.; Das, S.S.; Kim, H.J.; Kumar, A.; Thakur, V.K.; Han, S.S. Curcumin-loaded alginate hydrogels for cancer therapy and wound healing applications: A review. Int. J. Biol. Macromol. 2023, 232, 123283. [Google Scholar] [CrossRef] [PubMed]
  32. Neves, M.I.; Moroni, L.; Barrias, C.C. Modulating Alginate Hydrogels for Improved Biological Performance as Cellular 3D Microenvironments. Front. Bioeng. Biotechnol. 2020, 8, 665. [Google Scholar] [CrossRef] [PubMed]
  33. Iravani, S.; Jamalipour Soufi, G. Algae-derived materials for tissue engineering and regenerative medicine applications: Current trends and future perspectives. Emergent Mater. 2022, 5, 631–652. [Google Scholar] [CrossRef]
  34. Ruvinov, E.; Cohen, S. Alginate biomaterial for the treatment of myocardial infarction: Progress, translational strategies, and clinical outlook: From ocean algae to patient bedside. Adv. Drug Deliv. Rev. 2016, 96, 54–76. [Google Scholar] [CrossRef] [PubMed]
  35. Xie, Y.; Reddy Kollampally, S.C.; Jorgensen, M.; Zhang, X. Alginate microfibers as therapeutic delivery scaffolds and tissue mimics. Exp. Biol. Med. 2022, 247, 2103–2118. [Google Scholar] [CrossRef] [PubMed]
  36. Zhang, H.; Cheng, J.; Ao, Q. Preparation of Alginate-Based Biomaterials and Their Applications in Biomedicine. Mar. Drugs 2021, 19, 264. [Google Scholar] [CrossRef]
  37. Rezvanian, M.; Ng, S.-F.; Alavi, T.; Ahmad, W. In-vivo evaluation of Alginate-Pectin hydrogel film loaded with Simvastatin for diabetic wound healing in Streptozotocin-induced diabetic rats. Int. J. Biol. Macromol. 2021, 171, 308–319. [Google Scholar] [CrossRef]
  38. Chen, H.; Xing, X.; Tan, H.; Jia, Y.; Zhou, T.; Chen, Y.; Ling, Z.; Hu, X. Covalently antibacterial alginate-chitosan hydrogel dressing integrated gelatin microspheres containing tetracycline hydrochloride for wound healing. Mater. Sci. Eng. C 2017, 70, 287–295. [Google Scholar] [CrossRef]
  39. Sakai, S.; Hirose, K.; Moriyama, K.; Kawakami, K. Control of cellular adhesiveness in an alginate-based hydrogel by varying peroxidase and H(2)O(2) concentrations during gelation. Acta. Biomater. 2010, 6, 1446–1452. [Google Scholar] [CrossRef]
  40. Zou, Z.; Wang, L.; Zhou, Z.; Sun, Q.; Liu, D.; Chen, Y.; Hu, H.; Cai, Y.; Lin, S.; Yu, Z.; et al. Simultaneous incorporation of PTH(1–34) and nano-hydroxyapatite into Chitosan/Alginate Hydrogels for efficient bone regeneration. Bioact. Mater. 2020, 6, 1839–1851. [Google Scholar] [CrossRef]
  41. He, F.; Wang, L.; Yang, S.; Qin, W.; Feng, Y.; Liu, Y.; Zhou, Y.; Yu, G.; Li, J. Highly stretchable and tough alginate-based cyclodextrin/Azo-polyacrylamide interpenetrating network hydrogel with self-healing properties. Carbohydr. Polym. 2021, 256, 117595. [Google Scholar] [CrossRef] [PubMed]
  42. Abourehab, M.A.S.; Rajendran, R.R.; Singh, A.; Pramanik, S.; Shrivastav, P.; Javed Ansari, M.; Manne, R.; Amaral, L.S.; Deepak, A. Alginate as a Promising Biopolymer in Drug Delivery and Wound Healing: A Review of the State-of-the-Art. Int. J. Mol. Sci. 2022, 23, 9035. [Google Scholar] [CrossRef]
  43. Croisier, F.; Jérôme, C. Chitosan-based biomaterials for tissue engineering. Eur. Polym. J. 2013, 49, 780–792. [Google Scholar] [CrossRef] [Green Version]
  44. Kim, Y.; Zharkinbekov, Z.; Raziyeva, K.; Tabyldiyeva, L.; Berikova, K.; Zhumagul, D.; Temirkhanova, K.; Saparov, A. Chitosan-Based Biomaterials for Tissue Regeneration. Pharmaceutics 2023, 15, 807. [Google Scholar] [CrossRef]
  45. Abdelbasset, W.K.; Jasim, S.A.; Sharma, S.K.; Margiana, R.; Bokov, D.O.; Obaid, M.A.; Hussein, B.A.; Lafta, H.A.; Jasim, S.F.; Mustafa, Y.F. Alginate-Based Hydrogels and Tubes, as Biological Macromolecule-Based Platforms for Peripheral Nerve Tissue Engineering: A Review. Ann. Biomed. Eng. 2022, 50, 628–653. [Google Scholar] [CrossRef] [PubMed]
  46. Naghizadeh, Z.; Karkhaneh, A.; Khojasteh, A. Self-crosslinking effect of chitosan and gelatin on alginate based hydrogels: Injectable in situ forming scaffolds. Mater. Sci. Eng. C 2018, 89, 256–264. [Google Scholar] [CrossRef]
  47. Dang, L.H.; Doan, P.; Nhi, T.T.Y.; Nguyen, D.T.; Nguyen, B.T.; Nguyen, T.P.; Tran, N.Q. Multifunctional injectable pluronic-cystamine-alginate-based hydrogel as a novel cellular delivery system towards tissue regeneration. Int. J. Biol. Macromol. 2021, 185, 592–603. [Google Scholar] [CrossRef]
  48. Øvrebø, Ø.; Perale, G.; Wojciechowski, J.P.; Echalier, C.; Jeffers, J.R.T.; Stevens, M.M.; Haugen, H.J.; Rossi, F. Design and clinical application of injectable hydrogels for musculoskeletal therapy. Bioeng. Transl. Med. 2022, 7, e10295. [Google Scholar] [CrossRef]
  49. Spoială, A.; Ilie, C.-I.; Ficai, D.; Ficai, A.; Andronescu, E. From Biomedical Applications of Alginate towards CVD Implications Linked to COVID-19. Pharmaceuticals 2022, 15, 318. [Google Scholar] [CrossRef]
  50. Opasanon, S.; Muangman, P.; Namviriyachote, N. Clinical effectiveness of alginate silver dressing in outpatient management of partial-thickness burns. Int. Wound J. 2010, 7, 467–471. [Google Scholar] [CrossRef]
  51. McGuire, M.K.; Scheyer, E.T.; Schupbach, P. A prospective, case-controlled study evaluating the use of enamel matrix derivative on human buccal recession defects: A human histologic examination. J. Periodontol. 2016, 87, 645–653. [Google Scholar] [CrossRef] [PubMed]
  52. Coluccino, L.; Stagnaro, P.; Vassalli, M.; Scaglione, S. Bioactive TGF-β1/HA alginate-based scaffolds for osteochondral tissue repair: Design, realization and multilevel characterization. J. Appl. Biomater. Funct. Mater. 2016, 14, e42–e52. [Google Scholar] [CrossRef] [PubMed]
  53. Cai, K.; Zhang, J.; Deng, L.H.; Yang, L.; Hu, Y.; Chen, C.; Xue, L.; Wang, L. Physical and Biological Properties of a Novel Hydrogel Composite Based on Oxidized Alginate, Gelatin and Tricalcium Phosphate for Bone Tissue Engineering. Adv. Eng. Mater. 2007, 9, 1082–1088. [Google Scholar] [CrossRef]
  54. Nguyen, T.-P.; Lee, B.-T. Fabrication of oxidized alginate-gelatin-BCP hydrogels and evaluation of the microstructure, material properties and biocompatibility for bone tissue regeneration. J. Biomater. Appl. 2012, 27, 311–321. [Google Scholar] [CrossRef]
  55. Sharma, C.; Dinda, A.K.; Potdar, P.D.; Chou, C.-F.; Mishra, N.C. Fabrication and characterization of novel nano-biocomposite scaffold of chitosan–gelatin–alginate–hydroxyapatite for bone tissue engineering. Mater. Sci. Eng. C 2016, 64, 416–427. [Google Scholar] [CrossRef] [PubMed]
  56. Balakrishnan, B.; Joshi, N.; Jayakrishnan, A.; Banerjee, R. Self-crosslinked oxidized alginate/gelatin hydrogel as injectable, adhesive biomimetic scaffolds for cartilage regeneration. Acta Biomater. 2014, 10, 3650–3663. [Google Scholar] [CrossRef] [PubMed]
  57. Yang, X.; Lu, Z.; Wu, H.; Li, W.; Zheng, L.; Zhao, J. Collagen-alginate as bioink for three-dimensional (3D) cell printing based cartilage tissue engineering. Mater. Sci. Eng. C 2018, 83, 195–201. [Google Scholar] [CrossRef]
  58. Zhang, X.; Yan, Z.; Guan, G.; Lu, Z.; Yan, S.; Du, A.; Li, Q. Polyethylene glycol diacrylate scaffold filled with cell-laden methacrylamide gelatin/alginate hydrogels used for cartilage repair. J. Biomater. Appl. 2022, 36, 1019–1032. [Google Scholar] [CrossRef]
  59. Xing, L.; Sun, J.; Tan, H.; Yuan, G.; Li, J.; Jia, Y.; Xiong, D.; Chen, G.; Lai, J.; Ling, Z.; et al. Covalently polysaccharide-based alginate/chitosan hydrogel embedded alginate microspheres for BSA encapsulation and soft tissue engineering. Int. J. Biol. Macromol. 2019, 127, 340–348. [Google Scholar] [CrossRef]
  60. Manju, S.; Muraleedharan, C.V.; Rajeev, A.; Jayakrishnan, A.; Joseph, R. Evaluation of alginate dialdehyde cross-linked gelatin hydrogel as a biodegradable sealant for polyester vascular graft. J. Biomed. Mater. Res. Part B Appl. Biomater. 2011, 98B, 139–149. [Google Scholar] [CrossRef]
  61. Liang, Y.; Liu, W.; Han, B.; Yang, C.; Ma, Q.; Song, F.; Bi, Q. An in situ formed biodegradable hydrogel for reconstruction of the corneal endothelium. Colloids Surf. B Biointerfaces 2011, 82, 1–7. [Google Scholar] [CrossRef] [PubMed]
  62. Baniasadi, H.; Mashayekhan, S.; Fadaoddini, S.; Haghirsharifzamini, Y. Design, fabrication and characterization of oxidized alginate–gelatin hydrogels for muscle tissue engineering applications. J. Biomater. Appl. 2016, 31, 152–161. [Google Scholar] [CrossRef]
  63. Chen, F.; Tian, M.; Zhang, D.; Wang, J.; Wang, Q.; Yu, X.; Zhang, X.; Wan, C. Preparation and characterization of oxidized alginate covalently cross-linked galactosylated chitosan scaffold for liver tissue engineering. Mater. Sci. Eng. C 2012, 32, 310–320. [Google Scholar] [CrossRef]
  64. Wright, B.; De Bank, P.A.; Luetchford, K.A.; Acosta, F.R.; Connon, C.J. Oxidized alginate hydrogels as niche environments for corneal epithelial cells. J. Biomed. Mater. Res. A 2014, 102, 3393–3400. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  65. Abou-Okeil, A.; Fahmy, H.M.; El-Bisi, M.K.; Ahmed-Farid, O.A. Hyaluronic acid/Na-alginate films as topical bioactive wound dressings. Eur. Polym. J. 2018, 109, 101–109. [Google Scholar] [CrossRef]
  66. Pires, A.L.R.; de Azevedo Motta, L.; Dias, A.M.A.; de Sousa, H.C.; Moraes, Â.; Braga, M.E.M. Towards wound dressings with improved properties: Effects of poly(dimethylsiloxane) on chitosan-alginate films loaded with thymol and beta-carotene. Mater. Sci. Eng. C 2018, 93, 595–605. [Google Scholar] [CrossRef]
  67. Shahzad, A.; Khan, A.; Afzal, Z.; Farooq Umer, M.; Khan, J.; Khan, G.M. Formulation development and characterization of cefazolin nanoparticles-loaded cross-linked films of sodium alginate and pectin as wound dressings. Int. J. Biol. Macromol. 2019, 124, 255–269. [Google Scholar] [CrossRef]
  68. Mohabatpour, F.; Duan, X.; Yazdanpanah, Z.; Tabil, X.L.; Lobanova, L.; Zhu, N.; Papagerakis, S.; Chen, X.; Papagerakis, P. Bioprinting of alginate-carboxymethyl chitosan scaffolds for enamel tissue engineering in vitro. Biofabrication 2023, 15, 015022. [Google Scholar] [CrossRef]
  69. Bhoj, M.; Zhang, C.; Green, D.W. A First Step in De Novo Synthesis of a Living Pulp Tissue Replacement Using Dental Pulp MSCs and Tissue Growth Factors, Encapsulated within a Bioinspired Alginate Hydrogel. J. Endod. 2015, 41, 1100–1107. [Google Scholar] [CrossRef]
  70. Valente, J.F.A.; Valente, T.A.M.; Alves, P.; Ferreira, P.; Silva, A.; Correia, I.J. Alginate based scaffolds for bone tissue engineering. Mater. Sci. Eng. C 2012, 32, 2596–2603. [Google Scholar] [CrossRef]
  71. Maity, C.; Das, N. Alginate-based smart materials and their application: Recent advances and perspectives. Top. Curr. Chem. 2022, 380, 3. [Google Scholar]
  72. Murab, S.; Gupta, A.; Włodarczyk-Biegun, M.K.; Kumar, A.; Rijn, P.v.; Whitlock, P.; Han, S.S.; Agrawal, G. Alginate based hydrogel inks for 3D bioprinting of engineered orthopedic tissues. Carbohydr. Polym. 2022, 296, 119964. [Google Scholar] [CrossRef] [PubMed]
  73. Aakyiir, M.; Oh, J.-A.; Araby, S.; Zheng, Q.; Naeem, M.; Ma, J.; Adu, P.; Zhang, L.; Mai, Y.-W. Combining hydrophilic MXene nanosheets and hydrophobic carbon nanotubes for mechanically resilient and electrically conductive elastomer nanocomposites. Compos. Sci. Technol. 2021, 214, 108997. [Google Scholar] [CrossRef]
  74. Kolambkar, Y.M.; Dupont, K.M.; Boerckel, J.D.; Huebsch, N.; Mooney, D.J.; Hutmacher, D.W.; Guldberg, R.E. An alginate-based hybrid system for growth factor delivery in the functional repair of large bone defects. Biomaterials 2011, 32, 65–74. [Google Scholar] [CrossRef] [Green Version]
  75. Yan, J.; Miao, Y.; Tan, H.; Zhou, T.; Ling, Z.; Chen, Y.; Xing, X.; Hu, X. Injectable alginate/hydroxyapatite gel scaffold combined with gelatin microspheres for drug delivery and bone tissue engineering. Mater. Sci. Eng. C 2016, 63, 274–284. [Google Scholar] [CrossRef]
  76. Majima, T.; Funakosi, T.; Iwasaki, N.; Yamane, S.-T.; Harada, K.; Nonaka, S.; Minami, A.; Nishimura, S.-I. Alginate and chitosan polyion complex hybrid fibers for scaffolds in ligament and tendon tissue engineering. J. Orthop. Sci. 2005, 10, 302–307. [Google Scholar] [CrossRef]
  77. Zhou, W.; Li, Q.; Ma, R.; Huang, W.; Zhang, X.; Liu, Y.; Xu, Z.; Zhang, L.; Li, M.; Zhu, C. Modified Alginate-Based Hydrogel as a Carrier of the CB2 Agonist JWH133 for Bone Engineering. ACS Omega 2021, 6, 6861–6870. [Google Scholar] [CrossRef] [PubMed]
  78. Singh, A.K.; Pramanik, K. Fabrication and investigation of physicochemical and biological properties of 3D printed sodium alginate-chitosan blend polyelectrolyte complex scaffold for bone tissue engineering application. J. Appl. Polym. Sci. 2023, 140, e53642. [Google Scholar] [CrossRef]
  79. Farokhi, M.; Shariatzadeh, F.J.; Solouk, A.; Mirzadeh, H. Alginate Based Scaffolds for Cartilage Tissue Engineering: A Review. Int. J. Polym. Mater. Polym. Biomater. 2020, 69, 230–247. [Google Scholar] [CrossRef]
  80. Singh, B.N.; Nallakumarasamy, A.; Sinha, S.; Rastogi, A.; Mallick, S.P.; Divakar, S.; Srivastava, P. Generation of hybrid tissue engineered construct through embedding autologous chondrocyte loaded platelet rich plasma/alginate based hydrogel in porous scaffold for cartilage regeneration. Int. J. Biol. Macromol. 2022, 203, 389–405. [Google Scholar] [CrossRef]
  81. Chu, Y.; Huang, L.; Hao, W.; Zhao, T.; Zhao, H.; Yang, W.; Xie, X.; Qian, L.; Chen, Y.; Dai, J. Long-term stability, high strength, and 3D printable alginate hydrogel for cartilage tissue engineering application. Biomed. Mater. 2021, 16, 064102. [Google Scholar] [CrossRef] [PubMed]
  82. Mostafavi, A.; Daemi, H.; Rajabi, S.; Baharvand, H. Highly tough and ultrafast self-healable dual physically crosslinked sulfated alginate-based polyurethane elastomers for vascular tissue engineering. Carbohydr. Polym. 2021, 257, 117632. [Google Scholar] [CrossRef] [PubMed]
  83. Steiner, D.; Lingens, L.; Fischer, L.; Köhn, K.; Detsch, R.; Boccaccini, A.R.; Fey, T.; Greil, P.; Weis, C.; Beier, J.P.; et al. Encapsulation of Mesenchymal Stem Cells Improves Vascularization of Alginate-Based Scaffolds. Tissue. Eng. Part A 2018, 24, 1320–1331. [Google Scholar] [CrossRef] [PubMed]
  84. Antunes, M.; Bonani, W.; Reis, R.L.; Migliaresi, C.; Ferreira, H.; Motta, A.; Neves, N.M. Development of alginate-based hydrogels for blood vessel engineering. Biomater. Adv. 2022, 134, 112588. [Google Scholar] [CrossRef]
  85. Hao, T.; Li, J.; Yao, F.; Dong, D.; Wang, Y.; Yang, B.; Wang, C. Injectable Fullerenol/Alginate Hydrogel for Suppression of Oxidative Stress Damage in Brown Adipose-Derived Stem Cells and Cardiac Repair. ACS Nano 2017, 11, 5474–5488. [Google Scholar] [CrossRef]
  86. Karvinen, J.; Joki, T.; Ylä-Outinen, L.; Koivisto, J.T.; Narkilahti, S.; Kellomäki, M. Soft hydrazone crosslinked hyaluronan- and alginate-based hydrogels as 3D supportive matrices for human pluripotent stem cell-derived neuronal cells. React. Funct. Polym. 2018, 124, 29–39. [Google Scholar] [CrossRef] [Green Version]
  87. Prang, P.; Müller, R.; Eljaouhari, A.; Heckmann, K.; Kunz, W.; Weber, T.; Faber, C.; Vroemen, M.; Bogdahn, U.; Weidner, N. The promotion of oriented axonal regrowth in the injured spinal cord by alginate-based anisotropic capillary hydrogels. Biomaterials 2006, 27, 3560–3569. [Google Scholar] [CrossRef]
  88. Tarsitano, M.; Cristiano, M.C.; Fresta, M.; Paolino, D.; Rafaniello, C. Alginate-Based Composites for Corneal Regeneration: The Optimization of a Biomaterial to Overcome Its Limits. Gels 2022, 8, 431. [Google Scholar] [CrossRef]
  89. Farasatkia, A.; Kharaziha, M. Robust and double-layer micro-patterned bioadhesive based on silk nanofibril/GelMA-alginate for stroma tissue engineering. Int. J. Biol. Macromol. 2021, 183, 1013–1025. [Google Scholar] [CrossRef]
  90. Xu, W.; Liu, K.; Li, T.; Zhang, W.; Dong, Y.; Lv, J.; Wang, W.; Sun, J.; Li, M.; Wang, M.; et al. An in situ hydrogel based on carboxymethyl chitosan and sodium alginate dialdehyde for corneal wound healing after alkali burn. J. Biomed. Mater. Res. A 2019, 107, 742–754. [Google Scholar] [CrossRef] [Green Version]
  91. Varaprasad, K.; Jayaramudu, T.; Kanikireddy, V.; Toro, C.; Sadiku, E.R. Alginate-based composite materials for wound dressing application:A mini review. Carbohydr. Polym. 2020, 236, 116025. [Google Scholar] [CrossRef]
  92. Ehterami, A.; Salehi, M.; Farzamfar, S.; Samadian, H.; Vaez, A.; Ghorbani, S.; Ai, J.; Sahrapeyma, H. Chitosan/alginate hydrogels containing Alpha-tocopherol for wound healing in rat model. J. Drug Deliv. Sci. Technol. 2019, 51, 204–213. [Google Scholar] [CrossRef]
  93. Cai, J.; Chen, X.; Wang, X.; Tan, Y.; Ye, D.; Jia, Y.; Liu, P.; Yu, H. High-water-absorbing calcium alginate fibrous scaffold fabricated by microfluidic spinning for use in chronic wound dressings. RSC Adv. 2018, 8, 39463–39469. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  94. Chen, Y.; Qiu, H.; Dong, M.; Cheng, B.; Jin, Y.; Tong, Z.; Li, P.; Li, S.; Yang, Z. Preparation of hydroxylated lecithin complexed iodine/carboxymethyl chitosan/sodium alginate composite membrane by microwave drying and its applications in infected burn wound treatment. Carbohydr. Polym. 2019, 206, 435–445. [Google Scholar] [CrossRef]
  95. Rubio-Elizalde, I.; Bernáldez-Sarabia, J.; Moreno-Ulloa, A.; Vilanova, C.; Juárez, P.; Licea-Navarro, A.; Castro-Ceseña, A.B. Scaffolds based on alginate-PEG methyl ether methacrylate-Moringa oleifera-Aloe vera for wound healing applications. Carbohydr. Polym. 2019, 206, 455–467. [Google Scholar] [CrossRef]
  96. Li, M.; Li, H.; Li, X.; Zhu, H.; Xu, Z.; Liu, L.; Ma, J.; Zhang, M. A Bioinspired Alginate-Gum Arabic Hydrogel with Micro-/Nanoscale Structures for Controlled Drug Release in Chronic Wound Healing. ACS Appl. Mater. Interfaces 2017, 9, 22160–22175. [Google Scholar] [CrossRef]
  97. Moshaverinia, A.; Chen, C.; Akiyama, K.; Ansari, S.; Xu, X.; Chee, W.W.; Schricker, S.R.; Shi, S. Alginate hydrogel as a promising scaffold for dental-derived stem cells: An in vitro study. J. Mater. Sci. Mater. Med. 2012, 23, 3041–3051. [Google Scholar] [CrossRef] [PubMed]
  98. Lin, G.S.S.; Cher, C.Y.; Goh, Y.H.; Chan, D.Z.K.; Karobari, M.I.; Hui Lai, J.C.; Noorani, T.Y. An Insight into the Role of Marine Biopolymer Alginate in Endodontics: A Review. Mar. Drugs 2022, 20, 539. [Google Scholar] [CrossRef]
  99. Mohabatpour, F.; Yazdanpanah, Z.; Papagerakis, S.; Chen, X.; Papagerakis, P. Self-Crosslinkable Oxidized Alginate-Carboxymethyl Chitosan Hydrogels as an Injectable Cell Carrier for In Vitro Dental Enamel Regeneration. J. Funct. Biomater. 2022, 13, 71. [Google Scholar] [CrossRef] [PubMed]
  100. Sancilio, S.; Gallorini, M.; Di Nisio, C.; Marsich, E.; Di Pietro, R.; Schweikl, H.; Cataldi, A. Current Status and Perspectives of Human Mesenchymal Stem Cell Therapy. Stem. Cells Int. 2018, 2018, 9643721. [Google Scholar]
  101. Zhu, S.; Ying, Y.; Wu, Q.; Ni, Z.; Huang, Z.; Cai, P.; Tu, Y.; Ying, W.; Ye, J.; Zhang, R.; et al. Alginate self-adhesive hydrogel combined with dental pulp stem cells and FGF21 repairs hemisection spinal cord injury via apoptosis and autophagy mechanisms. Chem. Eng. J. 2021, 426, 130827. [Google Scholar] [CrossRef]
  102. Liang, X.; Xie, L.; Zhang, Q.; Wang, G.; Zhang, S.; Jiang, M.; Zhang, R.; Yang, T.; Hu, X.; Yang, Z.; et al. Gelatin methacryloyl-alginate core-shell microcapsules as efficient delivery platforms for prevascularized microtissues in endodontic regeneration. Acta Biomater. 2022, 144, 242–257. [Google Scholar] [CrossRef] [PubMed]
Figure 1. (A) The conformation of monomers and block distribution of alginate. Adapted from Ref [18] with permission, Copyright 2020 Springer Nature, licensed under the terms of the Creative Commons Attribution License (CC BY). (B) The physical/chemical modification processes, 3D bioprinting techniques, and TE-RM applications of alginate hydrogels. Adapted from Ref. [19] with permission. Copyright 2023 Elsevier.
Figure 1. (A) The conformation of monomers and block distribution of alginate. Adapted from Ref [18] with permission, Copyright 2020 Springer Nature, licensed under the terms of the Creative Commons Attribution License (CC BY). (B) The physical/chemical modification processes, 3D bioprinting techniques, and TE-RM applications of alginate hydrogels. Adapted from Ref. [19] with permission. Copyright 2023 Elsevier.
Marinedrugs 21 00189 g001
Figure 2. Typical crosslinking approaches to form alginate hydrogels. Adapted from Ref. [23] with permission. Copyright 2020 Elsevier.
Figure 2. Typical crosslinking approaches to form alginate hydrogels. Adapted from Ref. [23] with permission. Copyright 2020 Elsevier.
Marinedrugs 21 00189 g002
Figure 3. (AF) Typical fabrication methods used in synthesizing alginate-based nanomaterials. Adapted from Ref. [17] with permission. Copyright 2020 Elsevier.
Figure 3. (AF) Typical fabrication methods used in synthesizing alginate-based nanomaterials. Adapted from Ref. [17] with permission. Copyright 2020 Elsevier.
Marinedrugs 21 00189 g003
Figure 4. (A) Scanning electron microscopy (SEM) image of electrospun nanofiber mesh, showing the smooth and bead-free nano-scaled fibers. (B) Hollow tubular implant without perforations constructed from nanofiber meshes. (C) Tubular implant with perforations. (D) The composite was constructed from an electrospun nanofiber mesh tube applied for repairing the bone defect. (E) Picture of the defect after placement of a perforated mesh tube; the alginate inside the tube can be seen through the perforations. (F) A specimen was taken down after one week and the mesh tube was cut open. The alginate was still present inside the defect, with a hematoma present at the bone ends. (G) The release kinetics of alginate >21 days (in vitro); sustained release of the rhBMP-2 could be detected during the first week. Adapted from Ref. [74] with permission. Copyright 2010 Elsevier.
Figure 4. (A) Scanning electron microscopy (SEM) image of electrospun nanofiber mesh, showing the smooth and bead-free nano-scaled fibers. (B) Hollow tubular implant without perforations constructed from nanofiber meshes. (C) Tubular implant with perforations. (D) The composite was constructed from an electrospun nanofiber mesh tube applied for repairing the bone defect. (E) Picture of the defect after placement of a perforated mesh tube; the alginate inside the tube can be seen through the perforations. (F) A specimen was taken down after one week and the mesh tube was cut open. The alginate was still present inside the defect, with a hematoma present at the bone ends. (G) The release kinetics of alginate >21 days (in vitro); sustained release of the rhBMP-2 could be detected during the first week. Adapted from Ref. [74] with permission. Copyright 2010 Elsevier.
Marinedrugs 21 00189 g004
Figure 5. (A) The representative corneal stroma structure (layers of the cornea and cellular structure of stroma). (B) The preparative process of (i) micro-patterned silk nanofibril (SNF) incorporated gelatin methacrylate (S/G) composite films through a micro-molding technique, under ultraviolet light, and (ii) double-layer micro-patterned S/G-sodium alginate (SA) film, after crosslinking of SA using CaCl2 solution. GelMA: gelatin methacrylate. Adapted from Ref. [89] with permission. Copyright 2021 Elsevier.
Figure 5. (A) The representative corneal stroma structure (layers of the cornea and cellular structure of stroma). (B) The preparative process of (i) micro-patterned silk nanofibril (SNF) incorporated gelatin methacrylate (S/G) composite films through a micro-molding technique, under ultraviolet light, and (ii) double-layer micro-patterned S/G-sodium alginate (SA) film, after crosslinking of SA using CaCl2 solution. GelMA: gelatin methacrylate. Adapted from Ref. [89] with permission. Copyright 2021 Elsevier.
Marinedrugs 21 00189 g005
Figure 6. (A) The preparative process of bioinspired alginate/gum Arabic hydrogels with sustained drug delivery behavior for chronic wound healing. (B) Atomic force microscopy (AFM) topographic micrograph of the sundew mucilage. (C) The hydrogels were generated by Ca2+-dependent crosslinking between sodium alginate and gum Arabic. Adapted from Ref. [96] with permission. Copyright 2017 American Chemical Society.
Figure 6. (A) The preparative process of bioinspired alginate/gum Arabic hydrogels with sustained drug delivery behavior for chronic wound healing. (B) Atomic force microscopy (AFM) topographic micrograph of the sundew mucilage. (C) The hydrogels were generated by Ca2+-dependent crosslinking between sodium alginate and gum Arabic. Adapted from Ref. [96] with permission. Copyright 2017 American Chemical Society.
Marinedrugs 21 00189 g006
Table 1. Some selected examples of alginate-based composites for versatile TE-RM applications.
Table 1. Some selected examples of alginate-based composites for versatile TE-RM applications.
CompositesApplicationsAdvantages/PropertiesRef
Bioactive transforming growth factor beta 1 (TGF-β1)/hydroxyapatite alginate-based scaffoldsOsteochondral tissue repair
-
Proper mechanical features and resorbability
-
Highly porous osteochondral graft with bioactivity
-
Suitable cell adhesion and cell-material interaction for up to seven days
-
No significant evidence of inflammatory reactions (in vivo studies)
[52]
Composite of oxidized alginate, gelatin, and tricalcium phosphateBone TE and regeneration
-
Good biocompatibility (in vitro)
-
The composite exhibited potentials as injectable systems for TE
[53]
Oxidized alginate-gelatin-biphasic calcium phosphate composite hydrogelsBone TE and regeneration
-
Hydrogels with good porosity and excellent biocompatibility
-
Controllable gelation and bio-degradation time
-
Good mechanical strength
[54]
Chitosan-gelatin-alginate-hydroxyapatite scaffoldBone TE
-
Excellent hydrophilicity and biodegradability
-
Good mechanical stability
-
Improved cell viability, proliferation rate, adhesion, and maintenance of osteoblastic phenotype
[55]
Self-crosslinked oxidized alginate/gelatin hydrogelsCartilage regeneration
-
Promising adhesive matrix for neo-cartilage generation
-
Injectable biomimetic scaffolds for cartilage regeneration
[56]
Collagen-alginate three-dimensional (3D) cell printing bioinks Cartilage TE
-
Improved mechanical strength
-
Improved cell adhesion and proliferation, along with an enhancement in the expression of cartilage-specific genes (e.g., Sox9, Col2al, and Acan)
[57]
Cell-laden methacrylamide gelatin/alginate hydrogelsCartilage repair
-
Improved biocompatibility and mechanical properties
-
Excellent potential for cartilage TE
[58]
Covalently polysaccharide-based alginate/chitosan hydrogel-embedded alginate microspheresSoft TE
-
Improved mechanical features and stability
-
Controlled release of bull serum albumin
[59]
Alginate dialdehyde crosslinked gelatin hydrogelsPolyester vascular graft
-
Good biodegradability
-
Nontoxic, hemocompatible, with sufficient efficiency in sealing the pores of the graft
-
Enhanced adhesion and proliferation of endothelial cells
[60]
Oxidized alginate/hydroxypropyl chitosan hydrogels Reconstruction of the corneal endothelium
-
Nontoxic and biodegradable
-
The transplanted corneal endothelial cells by alginate-based composite could survive and retain normal morphology
[61]
Self-crosslinked oxidized alginate-gelatin hydrogelsMuscle TE
-
High rate of cell proliferation in the hydrogel with oxidized alginate-gelatin weight ratio of 30/70
-
Good biodegradability
[62]
Oxidized alginate covalently crosslinked galactosylated chitosan scaffoldLiver TE
-
The porosity of scaffolds was ~70%
-
Good thermal stability and biocompatibility (in vitro)
[63]
Oxidized alginate hydrogelsCorneal dysfunction treatment
-
Oxidized hydrogels with increased pore size and decreased stiffness contributed to enhanced cell viability
-
Hydrogels holding corneal ECM proteins could affect the function of corneal epithelial cells, with beneficial effects on corneal wound healing
[64]
Hyaluronic acid/Na-alginate filmsBioactive wound dressings/healing
-
High antibacterial activities
-
Effective wound dressings to restore the homeostasis of skin tissue
[65]
Chitosan-alginate filmsWound healing
-
Improved mechanical properties; high tensile strength
-
Non-hemolytic and stable in physiological fluids
-
The incorporation of thymol and beta-carotene could improve the bioactivity of the formulation
[66]
Cefazolin nanoparticles-loaded crosslinked films of sodium alginate and pectinWound dressings
-
The alginate-based films with 0.5% crosslinking exhibited improved breaking elongation, water absorption and water vapor transmission, and wetting ratio
-
Efficient treatment of infections, with improved release profiles
[67]
Alginate-carboxymethyl chitosan scaffoldEnamel TE
-
The printed scaffolds were significantly porous
-
The scaffolds exhibited a high degree of printability and structural integrity
-
Excellent capabilities to stimulate ameloblast differentiation, calcium phosphate deposition, and matrix mineralization (in vitro study)
[68]
Bioinspired alginate hydrogelEndodontic regeneration
-
Sustained release from the scaffolds; enhanced cell proliferation
-
Vascular endothelial and fibroblast growth factors synergized co-culture of dental pulp stem cells/human umbilical vein endothelial cells within the scaffolds
[69]
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Farshidfar, N.; Iravani, S.; Varma, R.S. Alginate-Based Biomaterials in Tissue Engineering and Regenerative Medicine. Mar. Drugs 2023, 21, 189. https://doi.org/10.3390/md21030189

AMA Style

Farshidfar N, Iravani S, Varma RS. Alginate-Based Biomaterials in Tissue Engineering and Regenerative Medicine. Marine Drugs. 2023; 21(3):189. https://doi.org/10.3390/md21030189

Chicago/Turabian Style

Farshidfar, Nima, Siavash Iravani, and Rajender S. Varma. 2023. "Alginate-Based Biomaterials in Tissue Engineering and Regenerative Medicine" Marine Drugs 21, no. 3: 189. https://doi.org/10.3390/md21030189

APA Style

Farshidfar, N., Iravani, S., & Varma, R. S. (2023). Alginate-Based Biomaterials in Tissue Engineering and Regenerative Medicine. Marine Drugs, 21(3), 189. https://doi.org/10.3390/md21030189

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop