Bibliometric Map on Corrosion in Concentrating Solar Power Plants
Abstract
:1. Introduction
2. Methodology
3. Results and Discussion
4. Conclusions
Author Contributions
Funding
Institutional Review Board Statement
Informed Consent Statement
Data Availability Statement
Acknowledgments
Conflicts of Interest
References
- International Energy Agency (IEA). Technology Roadmap Concentrating Solar Power; IEA: Paris, France, 2010. [Google Scholar]
- González-Roubaud, E.; Pérez-Osorio, D.; Prieto, C. Review of commercial thermal energy storage in concentrated solar power plants: Steam vs. molten salts. Renew. Sustain. Energy Rev. 2017, 80, 133–148. [Google Scholar] [CrossRef]
- REN21. Renewables 2020 Global Status Report 2020; REN21: Paris, France, 2020. [Google Scholar]
- Fernández, A.G.; Gomez-Vidal, J.; Oró, E.; Kruizenga, A.; Solé, A.; Cabeza, L.F. Mainstreaming commercial CSP systems: A technology review. Renew. Energy 2019, 140, 152–176. [Google Scholar] [CrossRef]
- Walczak, M.; Pineda, F.; Fernández, Á.G.; Mata-Torres, C.; Escobar, R.A. Materials corrosion for thermal energy storage systems in concentrated solar power plants. Renew. Sustain. Energy Rev. 2018, 86, 22–44. [Google Scholar] [CrossRef]
- Gasa, G.; Lopez-Roman, A.; Prieto, C.; Cabeza, L.F. Life cycle assessment (LCA) of a concentrating solar power (CSP) plant in tower configuration with and without thermal energy storage (TES). Sustainability 2021, 13, 3672. [Google Scholar] [CrossRef]
- Ma, L.; Zhang, C.; Wu, Y.; Lu, Y. Comparative review of different influence factors on molten salt corrosion characteristics for thermal energy storage. Sol. Energy Mater. Sol. Cells 2022, 235, 11485. [Google Scholar] [CrossRef]
- Calderón, A.; Barreneche, C.; Hernández-Valle, K.; Galindo, E.; Segarra, M.; Fernández, A.I. Where is Thermal Energy Storage (TES) research going?—A bibliometric analysis. Sol. Energy 2020, 200, 37–50. [Google Scholar] [CrossRef]
- Borri, E.; Zsembinszki, G.; Cabeza, L.F. Recent developments of thermal energy storage applications in the built environment: A bibliometric analysis and systematic review. Appl. Therm. Eng. 2021, 189, 116666. [Google Scholar] [CrossRef]
- Reza, M.S.; Mannan, M.; Wali, S.B.; Hannan, M.A.; Jern, K.P.; Rahman, S.A.; Muttaqi, K.M.; Mahlia, T.I. Energy storage integration towards achieving grid decarbonization: A bibliometric analysis and future directions. J. Energy Storage 2021, 41, 102855. [Google Scholar] [CrossRef]
- Cabeza, L.F.; Frazzica, A.; Chàfer, M.; Vérez, D.; Palomba, V. Research trends and perspectives of thermal management of electric batteries: Bibliometric analysis. J. Energy Storage 2020, 32, 101976. [Google Scholar] [CrossRef]
- Dong, B.; Xu, G.; Luo, X.; Cai, Y.; Gao, W. A bibliometric analysis of solar power research from 1991 to 2010. Scientometrics 2012, 93, 1101–1117. [Google Scholar] [CrossRef]
- Yu, H.; Wei, Y.-M.; Tang, B.-J.; Mi, Z.; Pan, S.-Y. Assessment on the research trend of low-carbon energy technology investment: A bibliometric analysis. Appl. Energy 2016, 184, 960–970. [Google Scholar] [CrossRef]
- Cabeza, L.F.; Chàfer, M.; Mata, É. Comparative analysis of web of science and scopus on the energy efficiency and climate impact of buildings. Energies 2020, 13, 409. [Google Scholar] [CrossRef] [Green Version]
- van Eck, N.J.; Waltman, L. Software survey: VOSviewer, a computer program for bibliometric mapping. Scientometrics 2010, 84, 523–538. [Google Scholar] [CrossRef] [PubMed] [Green Version]
- Lilliestam, J.; Thonig, R.; Gilmanova, A.; Zang, C. CSP.guru 2021-07-01. 2021. Available online: https://zenodo.org/record/5094290#.YkkrETURVPY (accessed on 24 February 2022). [CrossRef]
- Guillot, S.; Faik, A.; Rakhmatullin, A.; Lambert, J.; Veron, E.; Echegut, P.; Bessada, C.; Calvet, N.; Py, X. Corrosion effects between molten salts and thermal storage material for concentrated solar power plants. Appl. Energy 2012, 94, 174–181. [Google Scholar] [CrossRef]
- Ding, W.; Shi, H.; Xiu, Y.; Bonk, A.; Weisenburger, A.; Jianu, A.; Bauer, T. Hot corrosion behavior of commercial alloys in thermal energy storage material of molten MgCl2/KCl/NaCl under inert atmosphere. Sol. Energy Mater. Sol. Cells 2018, 184, 22–30. [Google Scholar] [CrossRef]
- Fernández, A.G.; Galleguillos, H.; Fuentealba, E.; Pérez, F.J. Corrosion of stainless steels and low-Cr steel in molten Ca(NO3)2–NaNO3–KNO3 eutectic salt for direct energy storage in CSP plants. Sol. Energy Mater. Sol. Cells 2015, 141, 7–13. [Google Scholar] [CrossRef]
- Fernández, A.G.; Muñoz-Sánchez, B.; Nieto-Maestre, J.; García-Romero, A. High temperature corrosion behavior on molten nitrate salt-based nanofluids for CSP plants. Renew. Energy 2019, 130, 902–909. [Google Scholar] [CrossRef]
- Fernández, A.G.; Cabeza, L.F. Corrosion evaluation of eutectic chloride molten salt for new generation of CSP plants. Part 1: Thermal treatment assessment. J. Energy Storage 2020, 27, 101125. [Google Scholar] [CrossRef]
- Fernández, A.G.; Cabeza, L.F. Corrosion evaluation of eutectic chloride molten salt for new generation of CSP plants. Part 2: Materials screening performance. J. Energy Storage 2020, 29, 101381. [Google Scholar] [CrossRef]
- Fernández, A.G.; Cabeza, L.F. Anodic protection assessment using alumina-forming alloys in chloride molten salt for CSP plants. Coatings 2020, 10, 138. [Google Scholar] [CrossRef] [Green Version]
- Fernández, A.G.; Cabeza, L.F. Cathodic protection using aluminum metal in chloride molten salts as thermal energy storage material in concentrating solar power plants. Appl. Sci. 2020, 10, 3724. [Google Scholar] [CrossRef]
- Fernández, A.G.; Muñoz-Sánchez, B.; Nieto-Maestre, J.; Cabeza, L.F. Dynamic corrosion test using LiNO3 containing molten salt for CSP applications. Appl. Sci. 2020, 10, 4305. [Google Scholar] [CrossRef]
- Fernández, A.G.; Lasanta, M.I.; Pérez, F.J. Molten salt corrosion of stainless steels and low-Cr steel in CSP plants. Oxid. Met. 2012, 78, 329–348. [Google Scholar] [CrossRef]
- Fernández, A.G.; Pérez, F.J. Improvement of the corrosion properties in ternary molten nitrate salts for direct energy storage in CSP plants. Sol. Energy 2016, 134, 468–478. [Google Scholar] [CrossRef]
- Fernández, A.G.; Galleguillos, H.; Pérez, F.J. Corrosion Ability of a Novel Heat Transfer Fluid for Energy Storage in CSP Plants. Oxid. Met. 2014, 82, 331–345. [Google Scholar] [CrossRef]
- Ding, W.; Bonk, A.; Bauer, T. Corrosion behavior of metallic alloys in molten chloride salts for thermal energy storage in concentrated solar power plants: A review. Front. Chem. Sci. Eng. 2018, 12, 564–576. [Google Scholar] [CrossRef] [Green Version]
- Ding, W.; Gomez-Vidal, J.; Bonk, A.; Bauer, T. Molten chloride salts for next generation CSP plants: Electrolytical salt purification for reducing corrosive impurity level. Sol. Energy Mater. Sol. Cells 2019, 199, 8–15. [Google Scholar] [CrossRef]
- Ding, W.; Bonk, A.; Gussone, J.; Bauer, T. Electrochemical measurement of corrosive impurities in molten chlorides for thermal energy storage. J. Energy Storage 2018, 15, 408–414. [Google Scholar] [CrossRef]
- Ding, W.; Bonk, A.; Gussone, J.; Bauer, T. Cyclic Voltammetry for Monitoring Corrosive Impurities in Molten Chlorides for Thermal Energy Storage. Energy Procedia 2017, 135, 82–91. [Google Scholar] [CrossRef] [Green Version]
- Ding, W.; Bonk, A.; Bauer, T. Molten chloride salts for next generation CSP plants: Selection of promising chloride salts & study on corrosion of alloys in molten chloride salts. AIP Conf. Proc. 2019, 2126, 200014. [Google Scholar]
- Ding, W.; Yang, F.; Bonk, A.; Bauer, T. Molten chloride salts for high-temperature thermal energy storage: Continuous electrolytic salt purification with two Mg-electrodes and alternating voltage for corrosion control. Sol. Energy Mater. Sol. Cells 2021, 223, 110979. [Google Scholar] [CrossRef]
- Villada, C.; Ding, W.; Bonk, A.; Bauer, T. Engineering molten MgCl2–KCl–NaCl salt for high-temperature thermal energy storage: Review on salt properties and corrosion control strategies. Sol. Energy Mater. Sol. Cells 2021, 232, 110979. [Google Scholar] [CrossRef]
- Bonk, A.; Knoblauch, N.; Braun, M.; Bauer, T.; Schmücker, M. An inexpensive storage material for molten salt based thermocline concepts: Stability of AlferRock in solar salt. Sol. Energy Mater. Sol. Cells 2020, 212, 110578. [Google Scholar] [CrossRef]
- Sötz, V.A.; Bonk, A.; Bauer, T. With a view to elevated operating temperatures in thermal energy storage—Reaction chemistry of Solar Salt up to 630 °C. Sol. Energy Mater. Sol. Cells 2020, 212, 110577. [Google Scholar] [CrossRef]
- Ding, W.; Shi, Y.; Braun, M.; Kessel, F.; Frieß, M.; Bonk, A.; Bauer, T. Compatibility of 3d-printed oxide ceramics with molten chloride salts for high-temperature thermal energy storage in next-generation csp plants. Energies 2021, 14, 2599. [Google Scholar] [CrossRef]
- Ding, W.; Bauer, T. Progress in Research and Development of Molten Chloride Salt Technology for Next Generation Concentrated Solar Power Plants. Engineering 2021, 7, 334–347. [Google Scholar] [CrossRef]
- Ding, W.; Shi, Y.; Kessel, F.; Koch, D.; Bauer, T. Characterization of corrosion resistance of C/C–SiC composite in molten chloride mixture MgCl2/NaCl/KCl at 700 °C. npj Mater. Degrad. 2019, 3, 42. [Google Scholar] [CrossRef]
- Ding, W.; Shi, H.; Jianu, A.; Xiu, Y.; Bonk, A.; Weisenburger, A.; Bauer, T. Molten chloride salts for next generation concentrated solar power plants: Mitigation strategies against corrosion of structural materials. Sol. Energy Mater. Sol. Cells 2019, 193, 298–313. [Google Scholar] [CrossRef]
- Encinas-Sánchez, V.; de Miguel, M.T.; Lasanta, M.I.; García-Martín, G.; Pérez, F.J. Electrochemical impedance spectroscopy (EIS): An efficient technique for monitoring corrosion processes in molten salt environments in CSP applications. Sol. Energy Mater. Sol. Cells 2019, 191, 157–163. [Google Scholar] [CrossRef]
- García-Martín, G.; Lasanta, M.I.; Encinas-Sánchez, V.; de Miguel, M.T.; Pérez, F.J. Evaluation of corrosion resistance of A516 Steel in a molten nitrate salt mixture using a pilot plant facility for application in CSP plants. Sol. Energy Mater. Sol. Cells 2017, 161, 226–231. [Google Scholar] [CrossRef]
- Encinas-Sánchez, V.; de Miguel, M.T.; García-Martín, G.; Lasanta, M.I.; Pérez, F.J. Corrosion resistance of Cr/Ni alloy to a molten carbonate salt at various temperatures for the next generation high-temperature CSP plants. Sol. Energy 2018, 171, 286–292. [Google Scholar] [CrossRef]
- Encinas-Sánchez, V.; Batuecas, E.; Macías-García, A.; Mayo, C.; Díaz, R.; Pérez, F.J. Corrosion resistance of protective coatings against molten nitrate salts for thermal energy storage and their environmental impact in CSP technology. Sol. Energy 2018, 176, 688–697. [Google Scholar] [CrossRef]
- Encinas-Sánchez, V.; Lasanta, M.I.; de Miguel, M.T.; García-Martín, G.; Pérez, F.J. Corrosion monitoring of 321H in contact with a quaternary molten salt for parabolic trough CSP plants. Corros. Sci. 2021, 178, 109070. [Google Scholar] [CrossRef]
- Audigié, P.; Encinas-Sánchez, V.; Rodríguez, S.; Pérez, F.J.; Agüero, A. High temperature corrosion beneath carbonate melts of aluminide coatings for CSP application. Sol. Energy Mater. Sol. Cells 2020, 210, 110514. [Google Scholar] [CrossRef]
- Pérez, F.J.; Encinas-Sánchez, V.; Lasanta, M.I.; De Miguel, M.T.; García-Martín, G. Corrosion monitoring of ferritic-martensitic steels in molten salt environments for CSP applications. AIP Conf. Proc. 2019, 2126, 030040. [Google Scholar]
- Pérez, F.J.; Encinas-Sánchez, V.; García-Martín, G.; Lasanta, M.I.; De Miguel, M.T. Dynamic pilot plant facility for applications in CSP: Evaluation of corrosion resistance of A516 in a nitrate molten salt mixture. AIP Conf. Proc. 2017, 1850, 130009. [Google Scholar]
- Pérez, F.J.; de Miguel, M.T.; Encinas-Sánchez, V.; Lasanta, M.I.; Illana, A.; García-Martín, G. Online corrosion monitoring system for thermal storage tanks using molten salts. Laboratory scale-up to demonstration parabolic-trough plant. AIP Conf. Proc. 2020, 2303, 110006. [Google Scholar]
- Pérez, F.J.; Encinas-Sánchez, V.; Lasanta, M.I.; De Miguel, M.T.; García-Martín, G. Dip-coated ZrO2-Y2O3 coatings tested in molten salts for CSP applications. AIP Conf. Proc. 2017, 1850, 120002. [Google Scholar]
- De Miguel, M.T.; Encinas-Sánchez, V.; Lasanta, M.I.; García-Martín, G.; Pérez, F.J. Corrosion resistance of HR3C to a carbonate molten salt for energy storage applications in CSP plants. Sol. Energy Mater. Sol. Cells 2016, 157, 966–972. [Google Scholar] [CrossRef]
- Grosu, Y.; Nithiyanantham, U.; Zaki, A.; Faik, A. A simple method for the inhibition of the corrosion of carbon steel by molten nitrate salt for thermal storage in concentrating solar power applications. npj Mater. Degrad. 2018, 2, 34. [Google Scholar] [CrossRef] [Green Version]
- Piquot, J.; Nithiyanantham, U.; Grosu, Y.; Faik, A. Spray-graphitization as a protection method against corrosion by molten nitrate salts and molten salts based nanofluids for thermal energy storage applications. Sol. Energy Mater. Sol. Cells 2019, 200, 110024. [Google Scholar] [CrossRef]
- Gonzalez, M.; Nithiyanantham, U.; Carbó-Argibay, E.; Bondarchuk, O.; Grosu, Y.; Faik, A. Graphitization as efficient inhibitor of the carbon steel corrosion by molten binary nitrate salt for thermal energy storage at concentrated solar power. Sol. Energy Mater. Sol. Cells 2019, 203, 110172. [Google Scholar] [CrossRef]
- Grosu, Y.; Anagnostopoulos, A.; Navarro, M.E.; Ding, Y.; Faik, A. Inhibiting hot corrosion of molten Li2CO3-Na2CO3-K2CO3 salt through graphitization of construction materials for concentrated solar power. Sol. Energy Mater. Sol. Cells 2020, 215, 110650. [Google Scholar] [CrossRef]
- El Karim, Y.; Grosu, Y.; Faik, A.; Lbibb, R. Investigation of magnesium-copper eutectic alloys with high thermal conductivity as a new PCM for latent heat thermal energy storage at intermediate-high temperature. J. Energy Storage 2019, 26, 100974. [Google Scholar] [CrossRef]
- Ortega-Fernández, I.; Grosu, Y.; Ocio, A.; Arias, P.L.; Rodríguez-Aseguinolaza, J.; Faik, A. New insights into the corrosion mechanism between molten nitrate salts and ceramic materials for packed bed thermocline systems: A case study for steel slag and Solar salt. Sol. Energy 2018, 173, 152–159. [Google Scholar] [CrossRef]
- Nithiyanantham, U.; Grosu, Y.; González-Fernández, L.; Zaki, A.; Igartua, J.M.; Faik, A. Development of molten nitrate salt based nanofluids for thermal energy storage application: High thermal performance and long storage components life-time. AIP Conf. Proc. 2019, 2126, 200025. [Google Scholar]
- Grosu, Y.; Nithiyanantham, U.; Gonzalez, M.; González-Fernández, L.; Zaki, A.; Faik, A. Spray-graphitization against molten salts corrosion for concentrated solar power plants. AIP Conf. Proc. 2020, 2303, 190016. [Google Scholar]
- Grosu, Y.; Bondarchuk, O.; Faik, A. The effect of humidity, impurities and initial state on the corrosion of carbon and stainless steels in molten HitecXL salt for CSP application. Sol. Energy Mater. Sol. Cells 2018, 174, 34–41. [Google Scholar] [CrossRef]
- González-Fernández, L.; Intxaurtieta-Carcedo, M.; Bondarchuk, O.; Grosu, Y. Effect of dynamic conditions on high-temperature corrosion of ternary carbonate salt for thermal energy storage applications. Sol. Energy Mater. Sol. Cells 2022, 111666. [Google Scholar] [CrossRef]
- Motte, F.; Falcoz, Q.; Veron, E.; Py, X. Compatibility tests between Solar Salt and thermal storage ceramics from inorganic industrial wastes. Appl. Energy 2015, 155, 14–22. [Google Scholar] [CrossRef]
- Kruizenga, A.; Gill, D. Corrosion of iron stainless steels in molten nitrate salt. Energy Procedia 2014, 49, 878–887. [Google Scholar] [CrossRef] [Green Version]
- Ruiz-Cabañas, F.J.; Prieto, C.; Osuna, R.; Madina, V.; Fernández, A.I.; Cabeza, L.F. Corrosion testing device for in-situ corrosion characterization in operational molten salts storage tanks: A516 Gr70 carbon steel performance under molten salts exposure. Sol. Energy Mater. Sol. Cells 2016, 157, 383–392. [Google Scholar] [CrossRef]
- Federsel, K.; Wortmann, J.; Ladenberger, M. High-temperature and Corrosion Behavior of Nitrate Nitrite Molten Salt Mixtures Regarding their Application in Concentrating Solar Power Plants. Energy Procedia 2015, 69, 618–625. [Google Scholar] [CrossRef] [Green Version]
- Dorcheh, A.S.; Galetz, M.C. Slurry aluminizing: A solution for molten nitrate salt corrosion in concentrated solar power plants. Sol. Energy Mater. Sol. Cells 2016, 146, 8–15. [Google Scholar] [CrossRef]
- Fähsing, D.; Oskay, C.; Meißner, T.M.; Galetz, M.C. Corrosion testing of diffusion-coated steel in molten salt for concentrated solar power tower systems. Surf. Coatings Technol. 2018, 354, 46–55. [Google Scholar] [CrossRef]
- Oskay, C.; Meißner, T.M.; Dobler, C.; Grégoire, B.; Galetz, M.C. Scale formation and degradation of diffusion coatings deposited on 9% cr steel in molten solar salt. Coatings 2019, 9, 687. [Google Scholar] [CrossRef] [Green Version]
- Pineda, F.; Mallco, A.; De Barbieri, F.; Carrasco, C.; Henriquez, M.; Fuentealba, E.; Fernández, Á.G. Corrosion evaluation by electrochemical real-time tracking of VM12 martensitic steel in a ternary molten salt mixture with lithium nitrates for CSP plants. Sol. Energy Mater. Sol. Cells 2021, 231, 111302. [Google Scholar] [CrossRef]
- Dorcheh, A.S.; Durham, R.N.; Galetz, M.C. Effect of chloride contents on the corrosion behavior of ferritic and austenitic steels in molten solar salts. NACE—Int. Corros. Conf. Ser. 2016, 4, 2615–2622. [Google Scholar]
- Mallco, A.; Pineda, F.; Mendoza, M.; Henriquez, M.; Carrasco, C.; Vergara, V.; Fuentealba, E.; Fernandez, A.G. Evaluation of flow accelerated corrosion and mechanical performance of martensitic steel T91 for a ternary mixture of molten salts for CSP plants. Sol. Energy Mater. Sol. Cells 2022, 238, 111623. [Google Scholar] [CrossRef]
- Myers, P.D.; Goswami, D.Y. Thermal energy storage using chloride salts and their eutectics. Appl. Therm. Eng. 2016, 109, 889–900. [Google Scholar] [CrossRef] [Green Version]
- Gomez-Vidal, J.C.; Tirawat, R. Corrosion of alloys in a chloride molten salt (NaCl-LiCl) for solar thermal technologies. Sol. Energy Mater. Sol. Cells 2016, 157, 234–244. [Google Scholar] [CrossRef] [Green Version]
- Turski, M.; Clitheroe, S.; Evans, A.D.; Rodopoulos, C.; Hughes, D.J.; Withers, P.J. Engineering the residual stress state and microstructure of stainless steel with mechanical surface treatments. Appl. Phys. A Mater. Sci. Process. 2010, 99, 549–556. [Google Scholar] [CrossRef] [Green Version]
- Cho, H.-S.; Van Zee, J.W.; Shimpalee, S.; Tavakoli, B.A.; Weidner, J.W.; Garcia-Diaz, B.L.; Martinez-Rodriguez, M.J.; lson, L.; Gray, J. Dimensionless analysis for predicting Fe-Ni-Cr alloy corrosion in molten salt systems for concentrated solar power systems. Corrosion 2016, 72, 742–760. [Google Scholar] [CrossRef]
- Trent, M.C.; Goods, S.H.; Bradshaw, R.W. Comparison of corrosion performance of grade 316 and grade 347H stainless steels in molten nitrate salt. AIP Conf. Proc. 2016, 1734, 160017. [Google Scholar]
- Summers, K.L.; Chidambaram, D. Corrosion behavior of structural materials for potential use in nitrate salts based solar thermal power plants. J. Electrochem. Soc. 2017, 164, H5357–H5363. [Google Scholar] [CrossRef] [Green Version]
- Palacios, A.; Navarro, M.E.; Jiang, Z.; Avila, A.; Qiao, G.; Mura, E.; Ding, Y. High-temperature corrosion behaviour of metal alloys in commercial molten salts. Sol. Energy 2020, 201, 437–452. [Google Scholar] [CrossRef]
- Grégoire, B.; Oskay, C.; Meißner, T.M.; Galetz, M.C. Corrosion mechanisms of ferritic-martensitic P91 steel and Inconel 600 nickel-based alloy in molten chlorides. Part II: NaCl-KCl-MgCl2 ternary system. Sol. Energy Mater. Sol. Cells 2020, 216, 110675. [Google Scholar] [CrossRef]
- Kongkaoroptham, P.; Boonpensin, M.; Siripongsakul, T.; Promdirek, P. Corrosion behaviour of AISI409 stainless steel with Al slurry coating in molten salt. Appl. Sci. Eng. Prog. 2022, 15. [Google Scholar] [CrossRef]
- Zhang, X.; Li, H.; Li, S.; Xue, W.; Liu, K.; Tang, J.; Gong, J. Research progress on corrosion and damage of stainless steel in high temperature molten salts. Corros. Sci. Prot. Technol. 2019, 31, 349–354. [Google Scholar] [CrossRef]
- Gomes, A.; Navas, M.; Uranga, N.; Paiva, T.; Figueira, I.; Diamantino, T.C. High-temperature corrosion performance of austenitic stainless steels type AISI 316L and AISI 321H, in molten Solar Salt. Sol. Energy 2019, 177, 408–419. [Google Scholar] [CrossRef] [Green Version]
- Zuo, Y.; Cao, M.; Shen, M.; Yang, X. Effect of Mg on corrosion of 316H stainless steel in molten salts MgCl2-NaCl-KCl. J. Chin. Soc. Corros. Prot. 2021, 41, 80–86. [Google Scholar] [CrossRef]
- Li, H.; Yang, X.; Yin, X.; Wang, X.; Tang, J.; Gong, J. Effect of Chloride Impurity on Corrosion Kinetics of Stainless Steels in Molten Solar Salt for CSP Application: Experiments and Modeling. Oxid. Met. 2021, 95, 311–332. [Google Scholar] [CrossRef]
- Ma, L.; Zhang, C.; Wu, Y.; Lu, Y.; Ma, C. Dynamic corrosion behavior of 316L stainless steel in quaternary nitrate-nitrite salts under different flow rates. Sol. Energy Mater. Sol. Cells 2020, 218, 110821. [Google Scholar] [CrossRef]
- Villada, C.; Toro, A.; Bolívar, F. Corrosion performance of austenitic stainless steel SS304 in molten nitrate salts and Raman microscopy for stability analysis in thermal energy storage applications. J. Energy Storage 2021, 44, 103465. [Google Scholar] [CrossRef]
- Singh, M.P.; Basu, B.; Chattopadhyay, K. Probing High-Temperature Electrochemical Corrosion of 316 Stainless Steel in Molten Nitrate Salt for Concentrated Solar Power Plants. J. Mater. Eng. Perform. 2022. [Google Scholar] [CrossRef]
- Valleti, K.; Rao, S.G.; Miryalkar, P.; Sandeep, A.; Rao, D.S. Cr-(CrN/TiAlN)m-AlSiN-AlSiO open-air stable solar selective coating for concentrated solar thermal power applications. Sol. Energy Mater. Sol. Cells 2020, 215, 110634. [Google Scholar] [CrossRef]
- Sandeep, A.; Archana, K.; Ellappan, S.; Mallesham, D. Advancement of solar selective DLC coating using capvd for solar thermal applications. J. Therm. Eng. 2020, 6, 422–437. [Google Scholar] [CrossRef]
- Meißner, T.M.; Oskay, C.; Fähsing, D.; Galetz, M.C. Improving optical properties of diffusion-based absorber coatings for CSP tower systems. AIP Conf. Proc. 2019, 2126, 020003. [Google Scholar]
- Joly, M.; Antonetti, Y.; Python, M.; Gonzalez, M.; Gascou, T.; Scartezzini, J.-L.; Schüler, A. Novel black selective coating for tubular solar absorbers based on a sol-gel method. Sol. Energy 2013, 94, 233–239. [Google Scholar] [CrossRef]
- Mihelčič, M.; Francetič, V.; Kovač, J.; Šurca Vuk, A.; Orel, B.; Kunič, R.; Peros, D. Novel sol–gel based selective coatings: From coil absorber coating to high power coating. Sol. Energy Mater. Sol. Cells 2015, 140, 232–248. [Google Scholar] [CrossRef]
- Joly, M.; Antonetti, Y.; Python, M.; Lazo, M.A.G.; Gascoua, T.; Hessler-Wyser, A.; Scartezzinia, J.-L.; Schüler, A. Selective solar absorber coatings on receiver tubes for CSP—Energy-efficient production process by sol-gel dip-coating and subsequent induction heating. Energy Procedia 2014, 57, 487–496. [Google Scholar] [CrossRef] [Green Version]
- Fernández-García, A.; Díaz-Franco, R.; Martinez, L.; Wette, J. Study of the effect of acid atmospheres in solar reflectors durability under accelerated aging conditions. Energy Procedia 2014, 49, 1682–1691. [Google Scholar] [CrossRef] [Green Version]
- Gomez-Vidal, J.C.; Fernandez, A.G.; Tirawat, R.; Turchi, C.; Huddleston, W. Corrosion resistance of alumina-forming alloys against molten chlorides for energy production. I: Pre-oxidation treatment and isothermal corrosion tests. Sol. Energy Mater. Sol. Cells 2017, 166, 222–233. [Google Scholar] [CrossRef] [Green Version]
- Nithiyanantham, U.; Grosu, Y.; González-Fernández, L.; Zaki, A.; Igartua, J.M.; Faik, A. Corrosion aspects of molten nitrate salt-based nanofluids for thermal energy storage applications. Sol. Energy 2019, 189, 219–227. [Google Scholar] [CrossRef]
- Nieto-Maestre, J.; Muñoz-Sánchez, B.; Fernández, A.G.; Faik, A.; Grosu, Y.; García-Romero, A. Compatibility of container materials for Concentrated Solar Power with a solar salt and alumina based nanofluid: A study under dynamic conditions. Renew. Energy 2020, 146, 384–396. [Google Scholar] [CrossRef]
- Grosu, Y.; Udayashankar, N.; Bondarchuk, O.; González-Fernández, L.; Faik, A. Unexpected effect of nanoparticles doping on the corrosivity of molten nitrate salt for thermal energy storage. Sol. Energy Mater. Sol. Cells 2018, 178, 91–97. [Google Scholar] [CrossRef]
- Nithiyanantham, U.; Grosu, Y.; Anagnostopoulos, A.; Carbó-Argibay, E.; Bondarchuk, O.; González-Fernández, L.; Zaki, A.; Igartua, J.M.; Navarro, M.E.; Ding, Y. Nanoparticles as a high-temperature anticorrosion additive to molten nitrate salts for concentrated solar power. Sol. Energy Mater. Sol. Cells 2019, 203, 110171. [Google Scholar] [CrossRef]
- Wang, J.; Jiang, Y.; Ni, Y.; Wu, A.; Li, J. Investigation on static and dynamic corrosion behaviors of thermal energy transfer and storage system materials by molten salts in concentrating solar power plants. Mater. Corros. 2019, 70, 102–109. [Google Scholar] [CrossRef] [Green Version]
- Muñoz-Sánchez, B.; Iparraguirre-Torres, I.; Madina-Arrese, V.; Izagirre-Etxeberria, U.; Unzurrunzaga-Iturbe, A.; García-Romero, A. Encapsulated High Temperature PCM as Active Filler Material in a Thermocline-based Thermal Storage System. Energy Procedia 2015, 69, 937–946. [Google Scholar] [CrossRef] [Green Version]
- Phan, A.T.; Gheribi, A.E.; Chartrand, P. A reliable framework to predict the temperature dependent thermal conductivity of multicomponent salt based PCMs in both solid and liquid state. Sol. Energy 2022, 233, 309–325. [Google Scholar] [CrossRef]
- Meißner, T.M.; Oskay, C.; Bonk, A.; Grégoire, B.; Donchev, A.; Solimani, A.; Galetz, M.C. Improving the corrosion resistance of ferritic-martensitic steels at 600 °C in molten solar salt via diffusion coatings. Sol. Energy Mater. Sol. Cells 2021, 227, 111105. [Google Scholar] [CrossRef]
- Aljaerani, H.A.; Samykano, M.; Pandey, A.K.; Kadirgama, K.; Saidur, R. Thermo-physical properties and corrosivity improvement of molten salts by use of nanoparticles for concentrated solar power applications: A critical review. J. Mol. Liq. 2020, 314, 113807. [Google Scholar] [CrossRef]
- Liu, M.; Bell, S.; Segarra, M.; Steven Tay, N.H.; Will, G.; Saman, W.; Bruno, F. A eutectic salt high temperature phase change material: Thermal stability and corrosion of SS316 with respect to thermal cycling. Sol. Energy Mater. Sol. Cells 2017, 170, 1–7. [Google Scholar] [CrossRef]
Country/Territory | Operational Capacity Installed [MW] |
---|---|
Europe | 2318 |
USA | 1731 |
China | 881 |
Morocco | 533 |
India | 242 |
Chile | 110 |
Australia | 2.6 |
Institution | Country | Number of Publications |
---|---|---|
DLR | Germany | 22 |
Universidad de Antofagasta | Chile | 17 |
Universidad Complutense de Madrid | Spain | 17 |
NREL | USA | 13 |
Universitat de Lleida | Spain | 13 |
CIC energigune | Spain | 13 |
Universidad del Pais Vasco | Spain | 9 |
DECHEMA Forschungsinstitut | Germany | 8 |
TECNALIA | Spain | 7 |
Queensland University of Technology | Australia | 6 |
Chinese Academy of Sciences | China | 6 |
Harbin Institute of Technology | China | 6 |
CIEMAT-Plataforma Solar de Almeria | Spain | 6 |
Author | Institution | Country | Number of Publications in This Query | Total Number of Publications | h-Index |
---|---|---|---|---|---|
A.G. Fernández | Univ del Pais Vasco | Spain | 23 | 59 | 22 |
T. Bauer | DLR | Germany | 16 | 69 | 22 |
F.J. Pérez | Univ Complutense de Madrid | Spain | 15 | 178 | 30 |
A. Bonk | DLR | Spain | 14 | 44 | 15 |
A. Faik | Mohammed VI Polytechnic Univ | Morocco | 14 | 102 | 23 |
Y. Grosu | Basque Research and Technology Alliance | Spain | 13 | 60 | 16 |
L.F. Cabeza | Universitat de Lleida | Spain | 12 | 546 | 76 |
W. Ding | DLR | Germany | 12 | 15 | 9 |
M.I. Lasanta | Univ Complutense de Madrid | Germany | 12 | 21 | 10 |
M.T. de Miguel | Univ Complutense de Madrid | Spain | 11 | 19 | 8 |
V. Encinás-Sanchez | Univ Complutense de Madrid | Spain | 11 | 22 | 8 |
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations. |
© 2022 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/).
Share and Cite
Cabeza, L.F.; Borri, E.; Prieto, C. Bibliometric Map on Corrosion in Concentrating Solar Power Plants. Energies 2022, 15, 2619. https://doi.org/10.3390/en15072619
Cabeza LF, Borri E, Prieto C. Bibliometric Map on Corrosion in Concentrating Solar Power Plants. Energies. 2022; 15(7):2619. https://doi.org/10.3390/en15072619
Chicago/Turabian StyleCabeza, Luisa F., Emiliano Borri, and Cristina Prieto. 2022. "Bibliometric Map on Corrosion in Concentrating Solar Power Plants" Energies 15, no. 7: 2619. https://doi.org/10.3390/en15072619