1. Introduction
Cross-wedge rolling (CWR) is an innovative manufacturing technology, applied in the manufacturing of stepped shafts and axles as well as preforms for die forging. The CWR process offers numerous advantages, amongst others: High efficiency, low material waste, accurateness of the obtained products, easy automation and eco-friendliness [
1,
2].
Cross-wedge rolling has been used in the industry for c.a. 50 years and since then has been developed in terms of theory and manufacturing technology. The majority of the developed aspects [
3,
4,
5] were connected to the hindrances in the forming process. Among those hindrances there are: Uncontrolled slipping, necking (rupture) of the rolled step and material cracking in the axial area of the workpiece. It is also to be mentioned that the most significant problems are connected to estimating the occurrence of the last hindrance, which is cracking.
The first works on this subject were published in the beginning of the 21st century. In 2002 Li et al. in their work [
6] introduced the results of an analysis stating that the phenomenon of microfractures melding into macrofractures is caused by the occurrence of shear and tensile stresses, which cause the cracking to be cross-shaped. Two years later Li and Lovell [
7] determined the influence of the basic cold CWR parameters on the occurrence of cracks, using the same numerical model. According to the obtained results material cracking was influenced by increasing the wedge angle (forming
α and spreading angle
β) and increasing the reduction of the cross section
Rp (degree of reduction δ).
Later on, numerical modeling became applied in analyses of hot CWR processes. In 2005 Piedrahita et al. [
8] conducted an analysis of several cases of rolling using FORGE® software in order to assess the influence of basic CWR parameters on the Cockroft–Latham damage function. As a result of the research it was stated that material cracking during CWR is most likely to occur when wedges with more significant
α and
β angles are employed as well as when less significant cross section reductions are used. Similar conclusions were drawn by Pater in his work [
1] published in 2014. According to Yang et al. [
9] both significant (
Rp > 75%) and insignificant (
Rp < 30%) reductions of the cross-section facilitate the phenomenon of material cracking in CWR. The cross-sectional reduction
Rp was calculated with the following formulas:
where
Rp—reductions of the cross-section during CWR,
d0—diameter of the billet and
d—diameter of the rolled step.
Lately numerous scientific articles presenting the distributions of damage function in CWR-formed elements were published. In those articles, the following criteria were employed: Oyane–Sato [
10], Oh [
11], Johnson–Cook [
12,
13] and Cockroft–Latham [
8,
14,
15,
16,
17]. In order to determine whether a fracture will occur in a given forming case both the distribution of the damage function and the critical damage value, obtained in so-called calibrating tests, are required. The currently employed tests [
18,
19], based on tension, compression and torsion cannot be employed in a CWR analysis due to significant differences in between the stress state of the test and the real process. For this reason a new test, based on rotational compression was developed in Lublin University of Technology. In the aforementioned test material cracking occurs in the axial area of the sample due to the occurrence of the Mannesmann effect [
20]. Upon obtaining the critical damage values one may prognosticate the cracking of the material in the CWR process.
This article presents the results of a numerical analysis aiming to determine the areas in which cracking occurs during the rolling process of a harrow tooth preform. In the research nine damage criteria were used. Their critical damage values were determined using rotational compression in a channel.
2. Subject of Research
The subject of the analysis was the process of manufacturing a harrow tooth preform presented in
Figure 1 along with a forging. The preform is obtained by flashless forging in a hydraulic press. During forging the working part of the tooth (with a square cross-section) as well as a flange with a cam is formed and finished. The gripping part, securing the tooth, is machined in the next operations.
Upon analyzing the shape of the preform it was to be noticed that it’s manufacturing using the CWR method might pose difficulties. Assuming that forming will be performed from a cylindrical billet with a 22 mm diameter it is to be mentioned that the forming process of the cone would occur at a very high values of strain (maximum value of reduction ratio is equal δ = 5.5, where δ = d0/d; d0—diameter of the billet and d—diameter of the rolled step). The flange, on the other hand, must be formed by rolling with upsetting, which allows one to obtain a diameter bigger than the one of the billet. An additional hindrance to the process is a relatively significant length of the preform, which is rolled on its whole length. Due to this fact, relatively big spreading angle β must be employed.
Preform rolling was conducted in a flat-wedge rolling mill located in Lublin University of Technology, shown in
Figure 2. The rolling mill has a hydraulic drive and is equipped with a set of one (upper) movable tool, working at the speed
v = 300 mm/s. Maximum length of the tools (wedges) is equal 1 m.
Figure 3 presents one of the wedge tools securing the preform rolling process. The forming wedge is characterized by the angles
α = 20° and
β = 9.5°. The side surfaces of the wedges have technological cuts, aiming to hinder the occurrence of uncontrollable slipping. In the ends of those tools two knives for cutting end waste are located.
In the process of manufacturing preforms billets with the dimensions Ø22 × 140 mm, preheated in an electric chamber furnace to 1150 °C were used. The billets were placed on the nether tool. Upon activating the movement of the slide of the rolling mill, the upper wedge came in contact with the workpiece, which was rolled on the stationary tool. In the final stage of the rolling process the side waste was removed and the preform was obtained. The progress of the discussed CWR process is shown in
Figure 4.
The preform manufactured using CWR is shown in
Figure 5. Its shape was compliant with the assumptions and its dimensions remain in the range of tolerance ±0.5 mm. The preform was subjected to non-destructive testing for internal cracking, conducted in an X-ray machine X-VIEW model X25 (NSI North Star Imaging Inc., Rogers, USA). The tests revealed cracking in the griping part of the preform (
Figure 6). The observed cracks were longitudinal, c.a. 24 mm long and began c.a. 4 mm after the step, from which the cam was formed in the forging process. In the cross-section the cracks were of an irregular, dense shape and their size did not exceed 3 mm. No cracks were observed in the remaining part of the preform (also in its conical end, presented in
Figure 7).
The detected cracks did not disqualify this method of forming the harrow tooth, implemented in one of the Polish industry plants. Due to their occurrence in the axial area as well as the type of load during its operation (bending) the lifetime of the teeth was not influenced. In this article the cracks were used determine the possibility of prognosticating the material fracture using numerical modeling.
3. Modeling of the Ductile Fracture
According to the results published by Yang et al. [
21] ductile fracture may occur in elements formed by the CWR method. The most popular method of modeling ductile fracture is, in this case, monitoring the damage function
fi described by the following general dependency:
where
—function describing the influence of the strain state on fracture in
i criterion, and
εf—critical strain.
In order to prognosticate material cracking, value of critical damage
Ci of the damage function
fi at the moment of cracking is required. With the present value of the function
fi and the critical value
Ci fracture indicator
wi can be determined. This indicator shows the degree of exposure to cracking expressed in percent. This indicator is determined from the following dependency:
For the crack to occur
.
In the specialist literature numerous damage criteria varying in the used function
can be found. A list of those functions, presented in chronological order is shown in
Table 1, along with a method of designating for each criterion. The aforementioned damage criteria were applied further in this study.
In order to successfully model fracture the critical damage value
Ci, obtained in calibrating tests must be known. In the case of the CWR process it is advised to use the rotational compression in a channel test, a scheme of which is presented in
Figure 8. In this test a disc-shaped sample with the dimensions
d0 ×
b is placed in a channel of the nether, unmovable tool. The upper tool is then set in reciprocating motion and grips the sample (due to the cut of the
γ angle) and compresses it in the radial direction. Compression is possible due to the fact that the distance between the bottoms of the channels of both tools (marked as 2
h) is smaller than the diameter of the disc
d0.
As a result of the friction forces the sample is rolled in the channel of the nether tool on the length of the path
s and is subjected to the cyclic compressive-tensile stress [
20]. During forming the side walls of the channels hinder material flow to the sides and therefore ensures continuous compression of the sample on the entire length of the forming path. The test aimed to experimentally determine the length of the
s path, at which the crack occurs for the assumed value of the degree of reduction
δ, in this case described as:
Then the performer test ought to be simulated using FEM and the value of the damage function in the axis of the sample ought to be determined. This value is equal to the sought critical damage value.
Figure 9 presents one of the rotational compression tests, performed in order to determine the critical damage values (for the nine discussed criteria, shown in
Table 1) for C45 grade steel formed in 1150 °C. The length of the forming path in the test case was equal
s = 700 mm. The samples of the dimensions Ø40 × 20 mm were heated in an electric resistance furnace and compressed at
δ = 1.053. The speed of the movable jaw was 300 mm/s. It is also to be mentioned that despite a relatively long forming time (
t = 4.7 s) the material in the middle of the sample did not cool down. Heat was transferred to the tools only from the peripheral part of the sample, whereas in the axial area a substantial amount of heat was created as a result of the exchange of the work of plastic strain.
The research allowed the authors to determine that the sought length of the path s at which the material cracking occurs is equal 700 mm (
Figure 10). For this path a simulation in Simufact.Forming v.15 software was conducted.
In the calculations the material model of the formed C45 grade steel is described by the following equation [
32]:
where
σF—flow stress, MPa;
ε—effective strain, -;
—strain ratio, s
−1 and
T—temperature, °C.
Moreover, the Tresca friction model, determined by friction factor m = 0.8 was assumed. Considering the thermal phenomena occurring during the forming process it was presupposed that during the process the temperature of tools is constant and equal to 50 °C, whereas the heat transfer coefficient between the tools and the material is equal to 10000 W/m2K. The remaining parameters were set similarly to the experimental testing.
Figure 11 shows the process of the numerically simulated rotational compression in a channel. In order to enhance the demonstrability, the upper tool was hidden. Additionally the change to temperature of the material in the sample during forming was presented. Interestingly, in the axial area of the sample material temperature not only did it not decrease, but also increased by over 10 °C. Contrastingly, the temperature of the outer (peripheral) surfaces of the disc decreased by c.a. 100–150 °C.
In order to determine the value of the damage function 11 virtual sensors were placed in the axis of the sample, located initially every 2 mm. This way the parameters determining the state of stress and strain were measured. As a result of forming the front surfaces of the sample funnels appeared, as a result of which the thickness of the sample in the axial area was decreased (
Figure 12). This type of strain was deemed beneficial for the test, since the cracking was occurring very fast on the side surface of the sample and observation of the sample was enough to determine its occurrence.
The data recorded using the sensors allowed one to determine the distributions of the damage function in the axis of the sample, after it being subjected to rotational compression on the path
s = 700 mm. In order to achieve this, the fracture criteria presented in
Table 1 were used. The obtained distributions
fi are shown in
Figure 13 and
Figure 14. In order to obtain the critical values of damage, the obtained distributions of the damage function were averaged and the results were listed in
Table 2.
4. Numerical Modeling of the Process of Cross Wedge Rolling of the Harrow Tooth Preform
Upon establishing the critical damage values for the nine
fi functions the authors conducted the numerical simulation of the CWR process of the harrow tooth preform. The simulation was performer in Simufact.Forming v.15, a software that has been used by the authors to model cross and skew rolling processes [
33,
34,
35,
36,
37]. The obtained results remained in compliance with the results of the verifying experimental examination.
Figure 15 presents a geometrical model of the analyzed case of rolling, which accurately portrayed the tools and the billet used in the forming tests performer in laboratory conditions in Lublin University of Technology. Both tools were assumed to be perfectly rigid bodies, whereas the billet modeled by 8-node brick elements behaved as a rigid-elastic material. The material model of the C45 grade steel, described by dependency (5) was identical to the one applied in determining the critical damage values. Similarly to this, the friction factor was also equal
m = 0.8 in this case. A comparison of the remaining parameters assumed in this simulation comprises of a billet temperature 1150 °C, temperature of the tools 50 °C, displacement rate of the movable tool 300 mm/s, heat transfer coefficient between the material and the tools 10,000 W/m
2K.
The conducted numerical simulation allowed for an accurate remodeling of the preform rolling process, as shown in
Figure 16. During the process an insignificant amount of side waste was created and removed in the final stage of the rolling process. Moreover,
Figure 16 shows the change to effective strain on the surface of the workpiece. Upon analyzing the strain values it was observed that it reached the highest values in the conical part—the area of the most significant reduction of the cross section.
The relatively high values of effective strain are located in the areas of the preform close to the flange, where significant material flow in the tangential (peripheral) direction occurred.
The aim of the simulation was to assess the efficiency of the modeling of cracking in the CWR process. In the calculations the fracture criteria shown in
Table 1 were used. Due to the fact that only a few of the criteria are implemented in Simufact.Forming, a similar methodology to the one adopted in the process of determining the critical values for rotational compression was assumed. In the axis of the rolled workpiece 68 virtual sensors were placed to monitor the components of the stress and strain state, necessary to determine the values of each damage function
fi. The way in which the sensors were located both in the billet and in the rolled element are shown in
Figure 17.
Every damage function used in the calculations is related to energy, which is a result of the integration of the stress after strain. Therefore an examination of the distribution of those parameters in the rolled preform was deemed important. The distribution of effective strain, shown in
Figure 18 proved rather uncomplicated. The obtained data shows that the least significant strain occurs in the flange, where the material is being upset. A slightly higher strain value was observed in the near-flange area, from where the material was extruded into the flange. A relatively stable distribution of strain occurred in the cylindrical steps of the product. A very significant increase of strain, with the highest values (
occurred in the end of the cone.
Illustrating the state of strain in the axis of the rolled preform proved more challenging. The chosen method was a presentation of the distributions of stress triaxiality
η and Lode angle parameter
θ, connected to the invariants of the state of stress, which play a significant role in the material cracking [
38,
39,
40]. Stress triaxiality
η is described by the ratio of the first invariant
p to the second invariant
q and is expressed by the following equation:
where
σm—mean stress and
σi—equivalent stress.
The Lode angle parameter, however, is represented by the second
p and third
r invariants of the state of strain
r, and is expressed by the following dependency:
where:
In the above presented dependency σ
1, σ
2 and σ
3 express principal stresses.
Since the values of both
η and
θ change significantly during the forming process, average values of those parameters were determined in each virtual sensor. In order to achieve this, the following dependencies were applied:
The distributions
ηav and
θav, obtained on the basis of the above presented dependencies, are shown in
Figure 19. The analysis of changes to stress triaxiality indicates that on the majority of the preform’s length (apart from the cone)
. According to the test results [
41,
42] in the case of the state of stress compliant with this condition material cracking was caused by void formation. In the case when
the cracks may occur as a result of both void formation and shear fracture. Such a situation occurs during the forming of the working part of the preform (cone), where η
av decreased to 0.172 along with the increase in the reduction of cross section. As far as the Lode angle parameter
θav is concerned, it was observed that its value varied in the range –0.539 to 0.015. In the vast majority of the preform the values of
θav were negative, the smallest in the area where the forming process began. Such values of the Lode angle parameter indicate the occurrence of an intermediate state between the axisymmetric compression, where
θ = –1, and the generalized shear, where
θ = 0.
Obtaining the components of the stress and strain state allowed one to determine the final values of each damage function
fi in the virtual sensors. Then, the value of critical damage indicator
wi was calculated by dividing the obtained
fi damage function by the critical damage values
Ci. Lastly, after considering the changes to the location of each sensor, the distributions of the
wi indicators in the axis of the preform were determined and are shown in
Figure 20. In the areas where
a fracture was prognosticated to occur.
In order to simplify the comparison of the results of modeling with the experimental testing results an additional
Figure 21 was made, where the areas of crack occurrence, prognosticated using the nine criteria, were shown. An analysis of the data presented in this figure showed that all of the applied criteria erroneously indicated cracking in the working part (cone) of the preform, that is in the areas where stress triaxiality
. Assuming energetic models of fracture in this case led, due to very significant values of effective strain, to a major overestimation of the damage function. It seems that in such state of stress criteria ought to be applied, e.g., maximum shear stress criterion.
A contrary situation occurs in the case of prognosticating fracture in the remaining part of the preform, where . In this case applying four out of nine allowed us to indicate the cracking in the proper pace of the gripping part of the preform. One of those criteria (developed by Ayada) falsely indicated that cracking would occur in the cylindrical part of the preform. It was concluded that the accurate indication of fracture occurrence in the gripping part of the preform was developed by: Freudenthal, Cockroft and Latham and Argon et al. The efficiency of those criteria is limited to the state of stress characterized by , which is the cases in which fracture is caused by void formation.