Photodegradation of Carbol Fuchsin Dye Using an Fe_2−xCu_xZr_2−xW_xO₇ Photocatalyst under Visible-Light Irradiation

Abstract

Fe_2−xCu_xZr_2−xW_xO₇ (x: 0, 0.05, 0.015) nanoparticles were synthesized following the Pechini method and characterized via X-ray diffraction (XRD), transmission electron microscopy (TEM), and diffuse reflectance spectroscopy (DRS) measurements to be used as photocatalysts in colored water remediation. All of the prepared materials were crystallized in a cubic fluorite phase as the major phase. The band gap was reduced upon doping with W⁶⁺ and Cu²⁺ from 1.96 eV to 1.47 eV for Fe_1.85Cu₀.₁₅Zr_1.85W_0.15O₇. Carbol fuchsin (CF) dye was used to determine the photocatalytic degradation efficiency of the prepared catalysts. Degradation efficiency was directly proportional to the dopant’s concentration. Complete removal of 20 mg/L CF was achieved under optimal conditions (pH 9, and catalyst loading of 1.5 g/L) using Fe_1.85Cu_0.15Zr_1.85W_0.15O₇. The degradation rate followed pseudo-first-order kinetics. The reusability for photocatalysts was tested five times, decreasing its efficiency by 4% after the fifth cycle, which indicates that the prepared Fe_1.85Cu_0.15Zr_1.85W_0.15O₇ photocatalyst is a promising novel photocatalyst due to its superior efficiency in dye photodegradation.

1. Introduction

Water can be contaminated by various industrial effluents, such as dyes, detergents, phenol compounds, heavy metals, and many others. The tremendous demand for textile products causes an accumulation of dye products in wastewater, with the World Bank estimating that 17–20% of these pollutants derive from the textile industry. These pollutants have long-lasting consequences on the environment, since dyes are stable compounds that last for a long time [1].

Dyes are organic colorants that are generally made up of water-soluble materials, and which have been used increasingly in industries all over the world [2]. Carbol fuchsin (CF) dye is one of the pollutants that are found in industrial wastewater [3]. CF is a mixture of phenol and basic fuchsin (BF), which is a common red dye that is widely used for dying different materials—such as leather, paper, and cotton—and for biological staining [4].

Dye-contaminated water is generally treated using cation-exchange membranes [5], electrochemical degradation [6,7] adsorption/precipitation processes [8], and photocatalytic degradation [9,10,11,12,13,14,15].

Recently, photocatalytic degradation has gained much attention as a proper method for water treatment because of its ability to degrade complex organic dyes into simple products. Photocatalysts are not directly involved in the oxidation reaction; however, it is known that the main reactions involved in photocatalytic degradations are the electron–hole interfacial redox reactions, which are generated when the photocatalyst is subjected to light of sufficient energy [13]; they create high levels of oxidizing species (OH, O²⁻) that cause complex organic molecules to degrade in the presence of light due to the difference in potential between oxidizing species and the organic matter [11,16]. Different types of photocatalysts have been used for dye degradation in wastewater, such as metals and metal oxides [2,17,18], carbon-based nanostructures [19,20], semiconductors [21,22], and metal–organic frameworks (MOFs) [23,24,25,26].

Photocatalytic degradation depends on the type and the concentration of the pollutants, the pH of the solution, the catalyst type, the composition and loading, and the intensity of light. To obtain an efficient treatment for polluted water, it is essential to understand the effects of these parameters on the degradation process [14]. Carbol fuchsin (CF) degradation was recently examined using metal oxide photocatalysts [3] (doped and undoped ferric oxide (Fe₃O₄)); they achieved 97% degradation using the doped catalyst under optimal conditions. In another recent study [27], La-doped Bi₂O₃ was used for the degradation of CF, achieving 89% degradation of CF under optimal conditions.

Metal oxides with the chemical formula A₂B₂O₇ are crystallized in pyrochlore or defect fluorite structures, depending on the radius ratio (r_A/r_B) of the A and B cations, where the A site is occupied by a larger trivalent cation (usually a rare-earth element) while the B site is occupied by a smaller tetravalent cation (typically transition metals). When (r_A/r_B) is in the range of 1.46–1.78, a pyrochlore structure is obtained, while a defect fluorite structure is obtained at the upper or lower limits of this range [28]. Many studies are concerned with metal oxide photocatalysts (with the chemical formula A₂B₂O₇ crystallized in a pyrochlore structure) for dye photodegradation. Some examples include Ln₂Ce₂O₇ (Ln = Nd, Pr, or Eu) for the degradation of methylene blue (MB) dye [29], YLnTi₂O₇ (Ln = Nd, Sm, Eu, or Gd) for the degradation of MB [30], K₂Ta₂O₆ for the degradation of rhodamine B [31], and Y₂Ti₂O_7−xN_x for the degradation of MB, rhodamine B, and 4-chlorophenol [32]. Less attention is given to metal oxides with the chemical formula A₂B₂O₇ in the defect fluorite phase. Few studies are concerned with defect-fluorite A₂B₂O₇ metal oxides as photocatalysts, such as the Ga₂Zr_2−xW_xO₇ system used for crystal violet degradation [33]. The Fe₂Zr_2−xW_xO₇ system is used for the photocatalytic degradation of methylene blue (MB) dye [28]. More light should be shed on A₂B₂O₇ metal oxides with a defect fluorite structure, because of their impressive performance in the photocatalytic degradation of dyes. In the present framework, Cu was selected as a co-dopant because the differences in the ionic radii and oxidation states of Cu²⁺ and Fe³⁺ ions allow for the study of the effects of co-doping on the structural properties and photocatalytic activity of the Fe₂Zr_2−xW_xO₇ system. Furthermore, the effects of time, catalyst dose, pH, and initial dye concentration on the photocatalytic activity of the prepared system for the degradation of carbol fuchsin dye as a water contaminant model under visible-light irradiation were studied.

2. Results and Discussion

2.1. Photocatalysis Characterizations

All catalysts were prepared using the Pechini method.

Table 1. Names and compositions of Fe_2−xCuxZr_2−xW_xO₇ catalysts.

Name of Catalyst	Composition of Catalyst
ZF	Fe2Zr2O7
ZFWC1	Fe1.95Cu0.05Zr1.95W0.05O7
ZFWC2	Fe1.85Cu0.15Zr1.85W0.15O7

shows the names and compositions of the prepared catalysts.

2.1.1. X-ray Diffraction

XRD patterns of ZF, ZFWC1, and ZFWC2 are shown in Figure 1. Fe₂Zr₂O₇ was crystallized in a cubic fluorite phase (according to the best-matched card (PDF 78-1299) for Er_0.5Zr_0.5O_1.75) as the major phase, along with a mixture of minor phases, consisting of a rhombohedral phase of Fe₂O₃ (PDF24-0072) and a monoclinic phase of ZrO₂ (PDF 37-1484) [34].

Regarding W- and Cu-co-doped Fe₂Zr₂O₇ samples, the ZFWC1 sample was crystallized in a major phase of cubic fluorite (PDF 78-1299) and a minor rhombohedral phase of Fe₂O₃ (PDF 24-0072). A mixture of phases was detected for ZFWC2; a major phase of cubic fluorite (PDF 78-1299) as well as minor phases of rhombohedral Fe₂O₃ (PDF 24-0072) and monoclinic ZrO₂ (PDF 37-1484). The samples were shifted to a lower theta value compared to Er_0.5Zr_0.5O_1.75 peaks. This can be attributed to the difference in the ionic radii between Fe³⁺ ions (ionic radius ls = 55 pm) and Er³⁺ ions (ionic radius = 89 pm). Similar results were found by Nasr [35], who prepared Ga_−xCu_xZr_2−xW_xO₇ photocatalysts.

All samples were found to be in the nano-sized range (5–15 nm). There were slight variations in the calculated parameters for the different prepared catalysts, which first decreased and then increased upon co-doping (i.e., the co-doping starts to be effective as the concentration of Cu and W increases). The Zr⁴⁺ ions (ionic radius = 72 pm) are expected to be substituted by the smaller W⁶⁺ ions (ionic radius = 60 pm) [35], while the Fe³⁺ ions (ionic radius ls = 55 pm) are expected to be substituted by the larger Cu²⁺ ions (ionic radius = 73 pm) [36]. The increase in the parameters as the concentrations of Cu and W increase might be due to the difference between the ionic radii of Zr⁴⁺ and W⁶⁺ ions being smaller than that between Fe³⁺ and Cu²⁺ ions (

Table 2. The cubic lattice parameters and unit cell volume calculated via XRD.

Sample	a (Å)	V (Å3)
ZF	5.10	132.29
ZFWC1	5.08	130.80
ZFWC2	5.09	131.17

).

2.1.2. Diffuse Reflectance Spectroscopy (DRS)

The optical properties of the prepared photocatalysts were characterized using DRS. Figure 2 shows that the absorption edge decreased upon doping with the lowest values found for ZFWC2 (974 nm). The band gap (BG) value was obtained by plotting F(R∞)E)^1/2 versus photo energy, and then a linear fit was used to detect BG based on the Kubelka–Munk theory [37]. The BG values were obtained using the plots in Figure 3 and Figure 4, and their values are shown in

Table 3. Calculated BG values for the photocatalysts.

Sample	BG
ZF	1.96
ZFWC1	1.86
ZFWC2	1.47

. As can be seen, ZF had a BG of 1.96 eV, while the Cu and W co-doping decreased the BG, with sample ZFWC2 having the lowest value of 1.47 eV. This indicates that the visible light range is the working range for the prepared catalysts. The reason for the decrease in the band gap upon increasing the concentrations of Cu and W might be due to the W forming an energy level below the conduction band, while Cu and Fe formed energy levels above the valence band (Figure 5). When co-doping Ga₂Zr₂O₇ with W and Cu, similar results were obtained by Nasr [35], who attributed this to the formation of new energy levels.

2.1.3. Transmission Electron Microscopy (TEM)

All samples were in the nano-sized range (

Table 4. Size range of particles for the prepared photocatalysts, based on TEM.

Sample	Particle Size Range (nm)
ZF	3–7
ZFWC1	5–7
ZFWC2	3–6

). W and Cu co-doping did not significantly affect the particle size for the Fe_2−xCu_xZr_2−xW_xO₇ system (Figure 6).

2.2. Photocatalytic Degradation of Dye

2.2.1. The Irradiation Time Effect

Figure 7 shows the degradation of CF from 0 to 120 min. It can be seen that the degradation of CF was enhanced by doping with W and Cu, and the enhancement was significant at high concentrations of dopants (15 mol%). The rate of degradation increased during the first hour, and became nearly constant during the second hour. Accordingly, the optimal reaction time is inferred to be one hour, since the degradation of CF at this point reached 20%, 30%, and 55% for ZF, ZFWC1, and ZFWC2, respectively. This enhancement in the photocatalytic activity of ZFWC2 for CF degradation was expected, because of the decrease in the BG as the co-dopant concentration increased. The catalyst utilizes visible-light energy, causing electrons to become excited and be shifted from the valence band to the conduction band, consequently generating electrons and holes on the surface of the catalyst. The holes interact with water, producing ${\mathrm{OH}}^{.}$, while the electrons interact with oxygen, which produces superoxide ${\mathrm{O}}_2^{.-}$. The produced ${\mathrm{OH}}^{.}$. and O₂⁻² cause the degradation of CF into simple products, as showing in Equations 1 to 6

Fe_2−xCu_xZr_2−xW_xO₇ + hʋ (λ > 400 nm) → Fe_2−xCu_xZr_2−xW_xO₇ (e_cb− + h_vb)

(1)

$${\mathrm{Fe}}_{2-\mathrm{x}}{\mathrm{Cu}}_{\mathrm{x}}{\mathrm{Zr}}_{2-\mathrm{x}}{\mathrm{W}}_{\mathrm{x}}{\mathrm{O}}_7\left({\mathrm{e}}_{\mathrm{cb}-}\right)+{\mathrm{O}}_2\to {\mathrm{Fe}}_{2-\mathrm{x}}{\mathrm{Cu}}_{\mathrm{x}}{\mathrm{Zr}}_{2-\mathrm{x}}{\mathrm{W}}_{\mathrm{x}}{\mathrm{O}}_7+{\mathrm{O}}_2^{.-}$$

(2)

$${\mathrm{h}}^{+}+{\mathrm{H}}_2\mathrm{O}\to {\mathrm{OH}}^{.}+\mathrm{H}$$

(3)

$${\mathrm{e}}^{-}+{\mathrm{O}}_2\to {\mathrm{O}}_2^{.-}$$

(4)

h_vb+ + dye → degradation byproduct

(5)

dye → degradation byproduct

(6)

The higher efficiency of co-doped samples may be related to control of the electron–hole pair recombination, in which the dopant ions trap the photogenerated electrons and holes, consequently decreasing the chances of recombination of the electron–hole pair, increasing their lifetime and leading to an improvement in the activity of the photocatalyst [38,39,40]. These effects are expected to increase when increasing the concentration of dopants.

2.2.2. The Effect of Catalyst Dose

Catalyst dose ranged between 0.25 g/L and 2.5 g/L, used at pH 7, 30 mg/L CF concentration, and for 1 h, as shown in Figure 8. The degradation of CF was enhanced with the catalyst dose up to 1.5 g/L (80% CF removal), due to the increase in the number of active sites for degradation, in addition to the generation of more free electrons in the conduction band during photocatalysis [41]. The degradation efficiency decreased at a higher dose as a result of higher solution turbidity, which negatively affected the penetration of light [35]. Moreover, it is expected that a high concentration of photocatalysts may result in particle aggregation, causing a reduction in the number of surface-active sites; consequently, there will be a decrease in the degradation efficiency [42]. A dose of 1.5 g/L was used as the optimal dose for further testing.

2.2.3. Effect of pH

The effect of pH on the photocatalytic degradation of CF was examined by varying the pH between 3 and 11, at 30 mg/L CF and 1.5 g/L catalyst dose. Figure 9 shows that increasing the pH to 9 increased CF degradation, due to the increase in the concentration of hydroxide ions at the active site, which caused an increase in the generation of OH^. radicals due to the oxidation of higher amounts of OH^. [43]. The CF removal using ZFWC2 was 100% at pH 9. Similar results of optimal pH in alkaline solutions were found in [3,44]. At higher pH (>9) the degradation efficiency decreased, since CF—as a cationic dye—turned into an anionic form at high pH, causing repulsion between dye molecules and the negative catalyst surface in alkaline solutions.

2.2.4. The Effect of CF Concentration

The effect of CF concentration on the photodegradation at 1.5 g/L CF and pH 9 under visible-light irradiation is shown in Figure 10. The reaction was found to follow pseudo-first-order kinetics (Equation (2)); the photodegradation reaction rate decreased upon an increase in CF concentration—from 0.065 min⁻¹ at 20 mg/L, to 0.0337 min⁻¹ at 50 mg/L (Figure 11). This was mainly due to a decrease in light penetration with an increase in dye concentration (with the dye acting as a barrier against the light), causing a decrease in the light intensity at the catalyst’s surface [33,35], in addition to the unavailability of active sites upon adsorption and aggregation of dye molecules [37]. Moreover, the reaction kinetics were studied using a pseudo-second-order equation (Equation (3)), and are shown in Figure 12, which shows that the correlation coefficient was very low compared with that found in the pseudo-first-order kinetics (Figure 10). This confirms that CF degradation follows pseudo-first-order kinetics [3,45,46].

According to the photodegradation experimental findings, increasing the co-dopant concentration to 15 mol% has a major impact on photodegradation, which can be attributed to a decrease in the band gap between the parent catalyst and the doped catalyst, with the lowest band gap at 15 mol%, which shifted the photoexcitation reaction to the visible region and demonstrated that the prepared nanocatalyst Fe_1.85Cu_0.15Zr_1.85W_0.15O₇ is a promising new photocatalyst, due to its superior efficiency in dye photodegradation compared to other photocatalysts.

As seen in Figure 13, the maximum absorbance peak at λ_max = (563) decreased over time, due to the degradation of aromatic amines via oxidation, which is expected to degrade the amines into simpler compounds as intermediates before complete degradation to CO₂ and H₂O [16]. Similar results were found in [32], which showed color fading of CF over time using La-Bi₂O_3.

2.2.5. The Effect of Visible Light

A dye solution and catalyst were situated in the dark for 30 min to confirm equilibrium between the adsorption and desorption occurrences of dye molecules on the photocatalyst surface prior to the illumination, and was considered as a control sample, as shown in Figure 14, which shows that the removal of carbol fuchsin dye ranged only from 3 to 8% when using the photocatalyst under dark conditions.

2.2.6. Active Radical Trapping Experiments

A total of 50 mmol L⁻¹ of scavengers (isopropyl alcohol (IPA), benzoquinone (BQ), and EDTA) were introduced to the reaction mixture (30 mg/L CF dye, 1.5 g/L ZFWC2, pH 9) in order to evaluate the most significant contribution of the radicals in the degradation of CF. When IPA was added as an HO· scavenger, the degradation of CF slightly decreased (CF% removal was 80%), proving that the HO· was not the primary interactive species. When 50 mmol L⁻¹ benzoquinone (BQ) was used, CF% removal was 60%, indicating that the ${\mathrm{O}}_2^{-}$. plays a role in the photodegradation process. However, when 50 mmol L⁻¹ EDTA was used, the catalytic degradation of CF strongly decreased (CF removal achieved 35%), demonstrating that the h+ plays a significant role in the catalytic process. Accordingly, h⁺ and ${\mathrm{O}}_2^{-}$. made the greatest contributions to the photocatalytic degradation of CF, while HO· made only a minor contribution [16].

2.2.7. Toxicity

Vibrio fischeri solution was used to examine the toxicity of the treated water reference using ZFWC2, via incubation for 10 min followed by exposure to heavy light. The water treated with ZFWC2 was nontoxic, as evidenced by an EC50 reading of more than 100 mg/L Microtox [28].

2.2.8. The Proposed Mechanism of Photocatalytic Degradation of CF

To elucidate the mechanism of photocatalytic degradation of CF, we conducted GC–MS analysis of the treated water using ZFWC2 under the optimal operating conditions (Figure 15). Detection of low-molecular-weight compounds m/z = (97, 57, 41) proved the degradation of high-molecular-weight CF (338 g/mol) into the smaller compounds hexane, propanol, and acetonitrile, as a result of attack by active radicals generated during the photocatalytic process (Figure 16). Finally, the detected intermediates mineralized to form inorganic compounds (carbon dioxide, water, and nitrates). The nitrate concentration at end of the degradation experiment was 1.5 mg/L, indicating that nitrates are a byproduct of complete degradation [3,16].

2.2.9. The Reusability of ZFWC2

Five cycles of CF degradation were performed using ZFWC2 under optimal conditions, in order to examine the reusability of the prepared catalyst (Figure 17). After each cycle, the catalyst was allowed to settle in order to remove the supernatant, and was then used in the next cycle. Degradation decreased from 100% to 96% between the first cycle and the fifth cycle, which is considered a promising result for reusing the prepared catalyst without significant loss of its capacity for photodegradation of the dye.

Table 5. Comparison of photocatalytic degradation of CF with previous reports.

Photocatalyst	Reaction Time (min)	Catalyst Dose (g/L)	CF Concentration	% Degradation	Reference
Ni- and Zn-modified montmorillonite clay	90	3	15	94	[16]
Undoped Fe3O4	90	8	20	90	[3]
Co2+- and Ni2+-doped Fe3O4 nanoparticles	90	8	20	95	[3]
Undoped Fe2Zr2−xWxO7	60	1.5	30	77	Present work
Fe1.85Cu0.15Zr1.85W0.15O7	60	1.5	30	100	Present work

compares photocatalytic CF degradation with various photocatalysts that demonstrated complete CF degradation in previous studies with the results of the present study, indicating that Fe_1.85Cu_0.15Zr_1.85W_0.15O₇ is an efficient photocatalyst comparable to the cited studies.

3. Materials and Methods

3.1. Materials

All materials were purchased and used without any further purification. Zirconium(IV) oxynitrate hydrate and tungsten(VI) chloride were purchased from Sigma-Aldrich, while iron(III) nitrate nonahydrate was purchased from Guangdong Guanghua Sci-Tech. Copper(II) nitrate trihydrate was purchased from Scharlau, citric acid anhydrous from Loba Chemie, ethylene glycol from CLWYD, and carbol fuchsin from Gurr Microscopy Materials.

3.2. Preparation of Photocatalysts

All catalysts were prepared using the Pechini method. Fe_2−xCu_xZr_2−xW_xO₇ was prepared as described by Abbas et al. (2020) [28], by mixing copper nitrate with an aqueous solution of zirconium oxynitrate hydrate, iron nitrate, and tungsten chloride, according to the proper stoichiometry of the metal oxides in the final solution. For chelation of metal cations, citric acid was added to the aqueous solution, with a 4:1 molar ratio of citric acid: Fe³⁺ in the final product. pH was adjusted to 3 before the addition of ethylene glycol, with a molar ratio of 1:1.5 for ethylene glycol:citric acid. Esterification and polymerization were achieved by continuously stirring the solution and heating it to 140 °C until a gel was formed. Finally, three calcination steps in a muffle furnace were performed, with two hours for each step (300 °C, 500 °C, and 600 °C), with the product being ground between calcination steps. Table 1 shows the names and compositions of the prepared catalysts.

3.3. Characterization Photocatalysts

A Shimadzu 7000 X-ray spectrophotometer was used for XRD characterizations, and UnitCellWin software [34] was used for the calculation of the lattice parameters. Size measurements of prepared catalysts were performed using a JEOL JEM2100 transmission electron microscope (TEM). The band gap calculations were performed using diffuse reflectance measurements from a Shimadzu UV-3600, with a resolution of 0.1 nm and a photomultiplier tube (PMT) detector. A Lovibond SpectroDirect visible spectrophotometer (Germany) was used for measuring absorbance for the sample. Degradation experiments employed an OSRAM GmbH HQI-T250/Daylight (Munich, Germany), which is a visible metal halide lamp with a luminous efficacy of 82 lm/W and a luminous irradiation flux of 20,000 lm.

3.4. Carbol Fuchsin Degradation Experiments

A solution of carbol fuchsin was prepared. Different parameters were examined: equilibrium time (0–120 min), catalyst dosage (0.25, 0.5, 0.75, 1.5, 2.0, and 2.5 g/L), solution pH (3.0, 5.0, 7.0, 9.0, and 11.0), and carbol fuchsin concentration (20, 30, 40, and 50 ppm). A dye solution and catalyst were situated in the dark for 30 min to confirm equilibrium between the adsorption and desorption of dye molecules on the photocatalyst surface prior to the illumination, and this was considered as a control sample. A commercial visible metal halide lamp (HQI-T250/Daylight, OSRAM GmbH, Munich, Germany) with a luminous efficacy of 82 lm/W and a luminous irradiation flux of 20,000 lm (wavelengths 380–780 nm) was used. Catalyst reusability was tested 5 times.

The degradation efficiency was calculated according to Equation (1):

$$\%\mathrm{Degradation}\mathrm{Efficiency}=\frac{C_0-C}{C_0} \times 100\%$$

(7)

where C₀ and C are the initial and final concentrations of CF, respectively, at time t. The concentration of CF dye was measured using the double-beam UV–Vis spectrophotometer (Cary-100). The nitrate concentration was determined as described by the APHA in 2017 (APHA, 2017) [47].

The kinetics of the reaction rate were tested using pseudo-first-order reaction (Equation (2)) and pseudo-second-order reaction (Equation (3)) models.

$$\ln \frac{C_0}{C}=K_{app}t$$

(8)

where C₀ and C are the CF concentration at zero time and time t, respectively, and K_app is the pseudo-first-order rate constant.

$$\frac{t}{q_t}=\frac{1}{k^2{q_e}^2}+\frac{1}{q_e}t$$

where k² is the rate constant, q_e is the amount of CF degraded at equilibrium, and q_t is the amount of CF degraded at time t.

3.5. Active Radical Trapping Experiments

To examine the significance of the active species involved in CF photodegradation, the experiments were conducted using 50 mmol isopropanol (IPA), EDTA, and benzoquinone (BQ) scavenger, which were introduced to the reaction mixture separately in order to explore the role of the HO· radicals, photogenerated holes, (h⁺) and ${\mathrm{O}}_2^{-}$ radicals, respectively.

3.6. Toxicity

The treated water was tested using a Microtox Model 500 analyzer and the ISO 11348-3, 2007 standard. The test organism was lyophilized Vibrio fischeri (NRRLB-11177). The bacterial suspension was introduced to treated water, and photometry was measured on a regular basis [48].

4. Conclusions

A promising new photocatalyst (Fe_2−xCu_xZr_2−xW_xO₇) synthesized using a modified Pechini method showed superior efficiency in dye photodegradation (where x = 0, 0.05, 0.15). The catalysts with the highest concentrations of W and Cu (15 mol%) had the lowest band gap (1.47 eV) among other synthesized catalysts. The prepared catalysts were active under visible light. Complete removal of carbol fuchsin dye (CF) was obtained under optimal conditions of 20 mg/L CF concentration, pH of 9, and catalyst loading of 1.5 g/L of Fe_1.85Cu_0.15Zr_1.85W_0.15O₇. The degradation rate followed first-order kinetics. The reusability of the photocatalyst five times decreased its efficiency by 4%.