Effects of Pressure and Cooling Rates on Crystallization Behavior and Morphology of Isotactic Polypropylene

Department of Industrial Engineering, University of Salerno, via Giovanni Paolo II, 132, 84084 Fisciano, SA, Italy
*
Author to whom correspondence should be addressed.
Crystals 2023, 13(6), 922; https://doi.org/10.3390/cryst13060922
Submission received: 4 May 2023 / Revised: 1 June 2023 / Accepted: 6 June 2023 / Published: 8 June 2023

Abstract

Isotactic Polypropylene (iPP) is a widely used polymer due to its excellent mechanical and thermal properties, as well as its chemical resistance. The crystallization behavior of polypropylene is influenced by several factors, such as temperature, cooling rate, and pressure. The effect of pressure is significant for both scientific and technological points of view, since in important industrial processing techniques the polymer solidifies under high pressures. In this paper, the study of the effect of pressure on the crystallization kinetics of iPP was conducted using a dilatometer in the pressure range from 100 to 600 bar and under two cooling rates: 0.1 and 1 °C/s. The morphology of the samples was characterized using DSC, optical microscopy, and X-ray diffraction. The results showed that pressure had a larger effect on specific volume changes at higher temperatures (in the melt state) than at lower temperatures (in the solid state). The polymer crystallization, which determined the transition between the melt and solid state, occurred at higher temperatures with increasing pressure. The cooling rate affected the crystallization process, with higher cooling rates leading to crystallization at lower temperatures. The size of the spherulites decreased with increasing cooling rates. The crystallinity evolution curves showed a linear relationship between the crystallization temperature and pressure. The study used a Kolmogoroff–Avrami–Evans model to describe the evolution into isotropic structures, and the predictions of the model accurately described the effect of pressure and cooling rates on the final spherulite radii.
Keywords: crystallization kinetics; polypropylene; pressure crystallization; pressure dependence of melting points; dilatometry crystallization kinetics; polypropylene; pressure crystallization; pressure dependence of melting points; dilatometry

Share and Cite

MDPI and ACS Style

Speranza, V.; Salomone, R.; Pantani, R. Effects of Pressure and Cooling Rates on Crystallization Behavior and Morphology of Isotactic Polypropylene. Crystals 2023, 13, 922. https://doi.org/10.3390/cryst13060922

AMA Style

Speranza V, Salomone R, Pantani R. Effects of Pressure and Cooling Rates on Crystallization Behavior and Morphology of Isotactic Polypropylene. Crystals. 2023; 13(6):922. https://doi.org/10.3390/cryst13060922

Chicago/Turabian Style

Speranza, Vito, Rita Salomone, and Roberto Pantani. 2023. "Effects of Pressure and Cooling Rates on Crystallization Behavior and Morphology of Isotactic Polypropylene" Crystals 13, no. 6: 922. https://doi.org/10.3390/cryst13060922

APA Style

Speranza, V., Salomone, R., & Pantani, R. (2023). Effects of Pressure and Cooling Rates on Crystallization Behavior and Morphology of Isotactic Polypropylene. Crystals, 13(6), 922. https://doi.org/10.3390/cryst13060922

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop