1. Introduction
Al–Cu–Li-based alloys are of great interest as aerospace structural materials, which require a combination of high strength, low density, high fracture toughness, and good corrosion resistance [
1]. Inhibition of alloy recrystallization has been extensively used to improve the overall performances of these Al alloys. An increase in the number of small grains and distribution of fiber-like unrecrystallized microstructures via recrystallization inhibition greatly improves the strength and fracture toughness of an Al alloy [
2,
3,
4,
5]. In the fabrication of high-performance Al–Cu–Li alloys, in particular, recrystallization inhibition can be used to avoid intergranular fractures caused by lower Li segregation levels in small-angle grain boundaries of unrecrystallized grains, and improve the alloy strength and fracture toughness [
6,
7]. This greatly extends the scope of their applications.
Well-distributed nano-sized dispersoids can effectively retain their deformed structure through pinning dislocation and sub-boundaries to inhibit recrystallization and grain growth [
8]. Many attempts have been made to inhibit recrystallization in Al alloys through precipitating L1
2-structured nano-sized dispersoids of Al
3Zr [
9,
10]. However, addition of Zr alone often gives a highly inhomogeneous distribution of dispersoids [
11]. Recently, joint addition of Zr and rare earth elements (e.g., ScZr and ErZr) has been used to solve this problem [
12], but this makes homogenization annealing processes complicated.
Normally the low solute supersaturation near dendrite boundaries results in the dispersoid-free zones formed in Zr containing alloy, leading to dispersoid banding in rolled plates and a low pinning pressure in the critical region of grain boundaries where recrystallization easily initiates [
11]. Similar to the opposite micro segregation patterns of Mn and Zr in Al, the joint addition of Ce and Zr is thought to produce more uniform dispersion coverage [
13]. The precipitation of Ce-containing phase along dendrite boundaries easily occur and it is hardly dissolved in solid solution, due to its micro segregation patterns [
14,
15], and the poor solid solubility of Ce in Al alloy (only 0.05 wt % at 650 °C) [
16]. These fine Ce-containing phases that contribute towards Zener pinning would have a potent effect in retarding grain boundary migration [
17], especially on an Al
3Zr dispersoid-free grain boundary. Moreover, Ce with medium-price and it seems an effective texture modifier in alloy [
18]. However, the rare earth element Ce has traditionally been used as a micro-alloying element in Al alloys to purify melts [
19] and refine dendritic structures [
20,
21]. Improved recrystallization resistance was only clearly observed during annealing of the Mg–Zn–Zr–Ce alloy because of the Zener pinning effect of the Ce enrichment phase [
17]. Similar recrystallization inhibition has also been observed in Al alloys [
22], therefore, we investigated the effects of Ce addition on recrystallization inhibition in an Al–Cu–Li–Zr alloy.
In this study, the effects of Ce addition on inhibition of recrystallization in an Al–Cu–Li–Zr alloy were investigated during isothermal annealing after high-strain rolling. Ce addition to an Al–Cu–Li–Zr alloy greatly improved its recrystallization resistance during isothermal annealing. The observed evolution of textures and microstructures, and the mechanical properties confirmed that Ce addition inhibited recrystallization. Ce addition considerably improves the strength and fracture toughness of Al–Cu–Li–Zr alloys, and this provides a convenient and economical method for enhancement of their overall performance.
3. Results and Discussion
Figure 1 shows the recrystallization degree of the Al–Cu–Li–0.13Zr–0.29Ce alloy (Ce-containing alloy). The degree is far lower than that for the Al–Cu–Li–0.14Zr alloy (Ce-free alloy) under the same conditions, for all annealing processes. As shown in
Figure 1a, little recrystallization of the Ce-containing alloy can be observed along the rolling direction for annealing at temperatures below 520 °C. Clear recrystallization only occurs near the sample surface zone after annealing at 520 °C for 1 h. There are still large areas of unrecrystallized grain structures in the middle area of the sample, even for annealing times of up to 4 h (
Figure 1a) In contrast to the case for the Ce-containing alloy, unrecrystallized microstructures in the Ce-free alloy can only be observed for annealing at 380 °C for 0.5 h. Significant recrystallization occurs after annealing at 430 °C for 0.5 h, and further recrystallization occurs after annealing at 450 °C for 1 h. Almost complete recrystallization can be observed after annealing at 520 °C for 1 h, as shown in
Figure 1b. Ce addition effectively improves the recrystallization resistance of Al–Cu–Li–Zr alloys.
The evolutions of the macro-textures (grain orientations) of the Ce-containing and Ce-free alloys were compared to clarify the process of recrystallization inhibition in Al–Cu–Li–Zr by Ce addition under various isothermal annealing conditions (
Figure 2 and
Figure 3).
Figure 2a shows that typical deformation microstructures such as β-fibers, and textures with the Cu orientation {112}<111>, S orientation {123}<634>, and brass orientation {011}<211>, were clearly formed in the Ce-containing alloy by high-strain rolling.
Figure 2 and
Figure 3 show that in the Ce-containing alloy, the β-fiber texture was first partly replaced by the Cubic texture {001}<100> at 520 °C, which is higher than that in the case of the Ce-free alloy, i.e., about 430 °C. The unrecrystallized β-fiber rolling texture was always retained during isothermal annealing, as shown in
Figure 2b–e. This indicates that Ce addition improved inhibition of recrystallization.
Quantitative date for the unrecrystallized β-fiber and α-fiber textures are presented in
Figure 4; the data show the maximum intensities of the orientation distribution function (ODF)
f(g).
Figure 4 shows that the
f(g) value for the as-rolled Ce-containing alloy was lower than that for the Ce-free alloy. It can be assumed that particle-stimulated nucleation (PSN) of recrystallization occurred [
25] and more randomly oriented nuclei formed [
26] during hot deformation because of the formation of coarse Ce enrichment particles in the Ce-containing alloy [
14]. The SEM images and XRD patterns of the as-homogenized material clearly show the presence of a large number of coarse Al
8Cu
4Ce particles in Ce-containing alloy, and only a few AlCu
2Zr particles in Ce-free alloy (
Figure 5). Obviously, the number density of coarse particles in the Ce-containing alloy is larger than that in Ce-free alloy. Because of more coarse particles in the Ce-containing alloy, particle-stimulated nucleation (PSN) of recrystallization occurs and more randomly oriented nuclei are formed during hot deformation. This analysis is confirmed by the texture of the alloys after the hot rolling stage in
Figure 6. The lower stored energy after deformation through PSN recrystallization in the Ce-containing alloy, therefore, decreased the recrystallization driving force of this alloy [
27]. In addition, unlike the gradual decreases in the α- and β-orientation lines of the Ce-free alloy, the intensities of the β-fiber texture at the positions of brass and S orientations in the Ce-containing alloy continuously increased with increasing annealing temperature up to an annealing time of 4 h at 520 °C. After annealing for 4 h, the orientation densities of brass and S dropped, whereas the Cu {112}<111> and Goss{011}<100> textures increased, as shown in
Figure 4a,c. In general, the
f(g) values for both α-fibers and β-fibers in the Ce-containing alloy (
Figure 4a,c) were much higher than those for the Ce-free alloy (
Figure 4b,d) when the annealing temperature reached 520 °C. The initial increase and subsequent decrease in the value of
f(g) can be explained as follows. Because of the strong inhibition of recrystallization achieved by Ce addition during isothermal annealing after high-strain rolling (
Figure 1), recovery only occurs via formation of a large number of subgrains with the β rolling orientation. The intensities of the preferred nucleation S and brass orientations increase significantly with annealing temperature [
28]. When annealing is extended to 4 h, recovery is associated with the accumulation of misorientations or annihilation of dislocations, leading to the formation of movable high-angle sub-boundaries. The ‘overcritial’ sub-grains (given by the Gibbs Thomson effect) grow and become growing recrystallization grain [
22], with a corresponding decrease in the
f(g) value. Because of the roles played by Ce enrichment particles at different stages, improved recrystallization resistance of the Ce-containing alloy is achieved during isothermal annealing.
Grain orientation evolution in these alloys can be clearly observed by using EBSD, as shown in
Figure 7 and
Figure 8. A considerable amount of unrecrystallized deformed structures, which consisted of subgrains with a high fraction of low-angle grain boundaries, clearly remained in the Ce-containing alloy after annealing at 520 °C for 1 h. In contrast, a large amount of coarse equiaxial recrystallized grains with a cubic texture was observed in the Ce-free alloy. The grain orientation distributions in
Figure 7 and
Figure 8 match those in
Figure 1 well. Furthermore, the grain orientation evolution well explains the extent of recrystallization during the annealing process, based on transformation of the grain orientation from concentrated to more random during recrystallization.
Figure 9 shows that Ce-containing alloy had a lower content of large-angle grain boundaries after annealing at 450 and 520 °C for 1 h; this confirms a lower recrystallization degree in the Ce-containing alloy.
The form and distribution of the Ce enrichment phases were investigated by XRD and SEM to clarify the effects of Ce enrichment particles in Al–Cu–Li–Zr alloys on inhibition of recrystallization; the results are shown in
Figure 10. The SEM images and XRD patterns clearly show the presence of Al
7Cu
4Li, and Al
8Cu
4Ce phases in the as-rolled Ce-containing alloy (
Figure 8a,b). The improved recrystallization resistance achieved by Ce addition to Al–Cu–Li–Zr alloy can be attributed to the formation of these finer Al
8Cu
4Ce phases. These Al
8Cu
4Ce phases had been crushed from their skeletal morphologies in the as-cast state into a smaller size by the large strain rolling [
14]. Al
8Cu
4Ce phases have high-temperature stability and hardly redissolve during high-temperature annealing [
15], as shown in
Figure 10c. Only the fine Al
8Cu
4Ce particles with diameters smaller than 1 μm have been counted, as shown in
Figure 10c. The effective pinning provided by Ce-containing dispersoids is mainly restricted in the Al
3Zr dispersoid-free area. As a result, only the fine Al
8Cu
4Ce particles in Al
3Zr dispersoid-free area have been counted (Insider the box in
Figure 10c). The estimation of the Zener pressure by fine Al
8Cu
4Ce particles has been presented, as below [
29].
For Al alloy the
is
. The size (D) and the volume fraction
are 0.82 μm and at least 6.75% respectively at present work. The estimate of the Zener pressure
which is at least
exert on the grain boundary. So the denser distributions of these fine Ce-contining particles near grain boundary apparently cause the strong recrystallization inhibition in Al
3Zr dispersoid-free grain boundary. The Al
8Cu
4Ce particles make a hole in the grain boundary (GB) and thus reduce GB area, which impose a drag force preventing the GB to escape from the particle. In order to move past the particle, a new boundary must be created, and this is energetically unfavorable [
27]. These high-temperature-stable Al
8Cu
4Ce particles might exerting a Zener pressure on the boundary, especially on a dispersoid-free grain boundary, which would retard their migration [
30] and inhibit recrystallization. Even the effect of Ce solute dragging on recrystallization at lower annealing temperatures can be ignored because of its extreme lower solid solubility [
31]. In addition, the few ternary AlCuZr particles observed in the Ce-free alloy had little recrystallization-inhibiting abilities; this can be attributed to the small quantity of particles and the precipitate position. First, a certain amount of Zr trapped in these AlCuZr particles could decrease the effect of nano-sized Al
3Zr particles on inhibition of recrystallization, corresponding to the higher Zr content in the matrix of the Ce-containing alloy (0.32 wt %) than that in the Ce-free alloy (0.13 wt %), as shown in
Figure 8b,d. Secondly, few AlCuZr particles for recrystallization inhibition were formed near dendrite boundaries because of the low solute supersaturation in the Ce-free alloy, which contained a single dispersoid-forming element, namely Zr [
11]. The enhanced inhibition of recrystallization in Ce-containing alloys can, therefore, mainly be attributed to the formation of a large number of small Al
8Cu
4Ce phases. Improved recrystallization resistance by Ce was only observed during annealing of the Mg alloy [
17]. Similar with Mn and Zr which have the opposite microsegregation patterns in Al alloy [
18], the joint addition of Ce and Zr in present alloy also achieves uniform dispersion coverage. In contrast to the rod-like shaped Al
20Cu
2Mn
3 dispersoids [
32], the spherical Al
8Cu
4Ce dispersoids (with much lower aspect ratio) formed in the Al
3Zr dispersoid-free bands by joint addition of Zr and Ce, can effectively to control texture, to pin grain and sub-grain migration and to inhibit recrystallization, enhancing fracture toughness at present work [
13].
Figure 11 shows that the tensile strength and yield strength of the Ce-containing alloy were higher than those of the Ce-free alloy, by 21 and 38 MPa, respectively, after solid-solution and aging treatment. The average grain size (incl. sun-grain sizes) of the experimental alloy after solid solution treatment at 520 °C for1 h is 5.32 μm in Ce-containing alloy and 31.23 μm in Ce-free alloy respectively, as shown in
Figure 7. The strength increment by grain refinement in two alloys can be achieved through Hall-Peatch relationship [
33]:
For Al alloy the
k is 0.04 MPa × m
1/2, so the strength increment in two alloys obtained by grain refinement is 10.16 MPa. However, the yield strength of the Ce-containing alloy is higher than that of the Ce-free alloy by 38 MPa in
Figure 11. The results indicate that the differences in mechanical properties are due to grain structure (26.74%) and the final precipitation behaviour (73.26%). Moreover, the elongations to break of the two alloys were similar. The UIE value (fracture toughness) of the Ce-containing alloy (31.21 N/mm) was higher than that of the Ce-free alloy (19.97 N/mm). The grain size is one of the main factors that affect the fracture toughness and ductility of a material, therefore, the grain properties of these two alloys after solid-solution and aging treatment are shown in the three-dimensional optical micrographs in
Figure 10. There are clearly many more small grains and fiber-like unrecrystallized microstructures distributed along the rolling direction in the Ce-containing alloy after solid-solution and aging treatment (
Figure 12a). There are many coarse recrystallized grains distributed in the Ce-free alloy (
Figure 12b). The critical effective shear stress and energy of plastic deformation, which are affected by the grain size, are key factors in crack initiation and propagation during deformation of alloys [
4,
30]. These properties determine the overall performance (strength, fracture toughness, etc.) of an alloy. The critical effective shear stress at fracture or crack nucleation should be considered first because gliding dislocations can accumulate at grain boundaries during continuous deformation and some cracks may be formed by piled-up dislocations. The crack initiation resistance is improved by grain refinement in the Ce-containing alloy because the critical effective shear stress at fracture increases with decreasing grain diameter [
30]. Moreover, the fiber-like unrecrystallized microstructures or smaller grain size in the Ce-containing alloy result in larger grain boundary areas. The crack propagation paths are more tortuous, which results in higher crack propagation resistance and higher energy of plastic deformation [
4]. This analysis is consistent with the higher strength and fracture toughness, and uniform elongation results for the Ce-containing alloy in
Figure 11.