Next Article in Journal
Dynamics of Cellular Regulation of Fractalkine/CX3CL1 and Its Receptor CX3CR1 in the Rat Trigeminal Subnucleus Caudalis after Unilateral Infraorbital Nerve Lesion—Extended Cellular Signaling of the CX3CL1/CX3CR1 Axis in the Development of Trigeminal Neuropathic Pain
Previous Article in Journal
Duplications and Losses of the Detoxification Enzyme Glycosyltransferase 1 Are Related to Insect Adaptations to Plant Feeding
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
IJMS
Volume 25
Issue 11
10.3390/ijms25116073
ijms-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Antimicrobial Packaging for Plum Tomatoes Based on ZnO Modified Low-Density Polyethylene

by
Ludmila Motelica
1,2,
Denisa Ficai
1,2,
Ovidiu-Cristian Oprea
1,2,*,
Roxana-Doina Trusca
1,
Anton Ficai
1,2,
Maria Daniela Stelescu
3,
Maria Sonmez
3,
Mihaela Nituica
3,
Gabriel Mustatea
4 and
Alina Maria Holban
1,5
1
Faculty of Chemical Engineering and Biotechnologies, National University of Science and Technology POLITEHNICA Bucharest, 1-7 Gh. Polizu, 011061 Bucharest, Romania
2
Academy of Romanian Scientists, 3 Ilfov St., 050044 Bucharest, Romania
3
National Research and Development Institute for Textile and Leather, Leather and Footwear Institute, 93 Ion Minulescu Street, 031215 Bucharest, Romania
4
National R&D Institute for Food Bioresources—IBA Bucharest, Dinu Vintila Street 6, 021102 Bucharest, Romania
5
Microbiology & Immunology Department, Faculty of Biology, University of Bucharest, 077206 Bucharest, Romania
*
Author to whom correspondence should be addressed.
Int. J. Mol. Sci. 2024, 25(11), 6073; https://doi.org/10.3390/ijms25116073
Submission received: 21 April 2024 / Revised: 19 May 2024 / Accepted: 29 May 2024 / Published: 31 May 2024
(This article belongs to the Section Materials Science)
Browse Figures
Versions Notes

Abstract

:
Food safety and quality are major concerns in the food industry. Despite numerous studies, polyethylene remains one of the most used materials for packaging due to industry reluctance to invest in new technologies and equipment. Therefore, modifications to the current materials are easier to implement than adopting whole new solutions. Antibacterial activity can be induced in low-density polyethylene films only by adding antimicrobial agents. ZnO nanoparticles are well known for their strong antimicrobial activity, coupled with low toxicity and UV shielding capability. These characteristics recommend ZnO for the food industry. By incorporating such safe and dependable antimicrobial agents in the polyethylene matrix, we have obtained composite films able to inhibit microorganisms’ growth that can be used as packaging materials. Here we report the obtaining of highly homogenous composite films with up to 5% ZnO by a melt mixing process at 150 °C for 10 min. The composite films present good transparency in the visible domain, permitting consumers to visualize the food, but have good UV barrier properties. The composite films exhibit good antimicrobial and antibiofilm activity from the lowest ZnO composition (1%), against both Gram-positive and Gram-negative bacterial strains. The homogenous dispersion of ZnO nanoparticles into the polyethylene matrix was assessed by Fourier transform infrared microscopy and scanning electron microscopy. The optimal mechanical barrier properties were obtained for composition with 3% ZnO. The thermal analysis indicates that the addition of ZnO nanoparticles has increased thermal stability by more than 100 °C. The UV-Vis spectra indicate a low transmittance in the UV domain, lower than 5%, making the films suitable for blocking photo-oxidation processes. The obtained films proved to be efficient packaging films, successfully preserving plum (Rome) tomatoes for up to 14 days.

1. Introduction

The majority of food packaging materials used at present are based on petrochemical products or cellulose, due to historical factors like low cost or mechanical and barrier properties [1,2]. The pressure of environmental concerns will phase out petroleum-based materials, which will increase the need for innovative, biodegradable polymeric packaging materials like chitosan [3], alginate [4], cellulose [5], starch [6], pullulan [7], polylactic acid [8], etc. The need to decrease food waste and the desire to increase food safety and prolong shelf life create pressure for the food packaging industry to develop and adopt new antimicrobial materials [9,10]. Unfortunately, despite many research reports, the industry is slow in implementing of novel biopolymers, as novel supply chains and new equipment are needed. One strategy to optimize the costs of novel packaging films is to modify the existing ones by introducing antimicrobial agents that can improve the shelf-life of packed food. This will permit producers to use the existing equipment and add value to their product [11].
As low-density polyethylene (LDPE) does not have antimicrobial activity, introducing antimicrobial agents in the polymer film is the only strategy that can generate polyethylene-based antimicrobial packaging. Various strategies were reported in the literature employing organic [12], inorganic [13], or mixed agents [14]. Inorganic nanoparticles (NPs) represent a special class of antimicrobials that can be used in packaging films; here are worth mentioning ZnO, Ag, CuO, TiO2, or SiO2 [15,16,17]. Such innovative antimicrobial biodegradable materials can diminish the microorganisms’ proliferation and thus reduce food spoilage, increase shelf life, and help provide better food quality [18,19,20,21,22]. Among these nanoparticles, silver [23] is the most potent antimicrobial agent, and can bring additional features to a packaging film, like a time–temperature cumulative indicator [24]. Nevertheless, ZnO is considered a safer solution for packaging. Among these nanoparticles, ZnO is considered GRAS (Generally Recognized As Safe) by the US-FDA [25]. The EU recommends a limit of 5–25 mg ZnO/kg of food (article 10/2011 from the Plastics Regulation of the Commission Regulation) [26]. The studies of the European Food Safety Authority (EFSA) concluded that ZnO does not migrate in nanoform and therefore established a specific migration limit (SML) for ionic zinc of maximum 25 mg/kg food [27]. For ionic zinc, no observed adverse effect level was established at 50 mg/day, and an upper limit of 25 mg/person per day was recommended [28]. The scientific literature highlights the antimicrobial activity of ZnO NPs against model pathogens, both Gram- positive or Gram-negative strains [29].
The antimicrobial activity of ZnO is well known, but the exact mechanism is still under debate [30,31]. This is due to the existence of at least three separate pathways: generation of reactive oxygen species (ROS) under light irradiation; mechanical damage generated by nanoparticles, by puncture, rupture, or abrasion, followed by leakage of cellular fluids; internalization of ZnO NPs, followed by the release of Zn2+ ions that can bind proteins, lipids, or other essential substances from inside the cell [32].
As ZnO is polar and LDPE is non-polar, the nanoparticles tend to form agglomerates in the ZnO/LDPE composite due to high interfacial tensions. These agglomerates are characterized by: distinct phase morphologies, coalescence, and poor mechanical properties. Two strategies emerged to ensure compatibility: ZnO surface modification with non-polar substances like oleic acid [33] or adding a compatibilizer to the LDPE, like low-density polyethylene grafted with maleic anhydride (LDPE-g-MA) [34,35,36]. The compatibilizer will reduce the interfacial tension and improve the adhesion between the composites’ phases. The ZnO NPs can reinforce the polymer matrix by acting as crosslinking points, generating a stronger material [37], leading to better mechanical properties. The presence of ZnO should also improve the light and gas barrier properties of the packaging [38]. The nanoparticles act as a physical barrier for water or oxygen molecules, decreasing their permeability [39]. At the same time, ZnO is a known sunscreen substance with high UV absorption capacity, which should improve the light barrier properties of any ZnO-based composite.
When it comes to polyethylene-zinc oxide composites, the literature reports focus on either thermal or mechanical properties [40], increasing the homogeneity of the fillers’ dispersion [35], interactions between ZnO and polymer matrix [41], antimicrobial properties [42], and UV shielding [43], but comprehensive reports are missing.
Depositing ZnO on the film surface [44] might enhance the antimicrobial activity, but will lead to a high transfer rate of zinc ions into the food, will not improve the mechanical properties of the film, and can simply fall off due to poor adherence of ZnO NPs to the polyethylene film [45,46,47]. Therefore, including the nanoparticles in the polyethylene matrix will ensure better overall properties, with long-lasting antimicrobial activity, better mechanical and barrier properties, and low migration of the zinc ions into the food [48,49]. Additionally, such composite material will keep its properties when recycled [50], with the ZnO nanoparticles manifesting continuous antimicrobial action. We have used a melt mixing process at 150 °C for 10 min with the help of a Plasti-Corder Brabender mixer, as this will lead to a homogenous dispersion of ZnO nanoparticles into the polyethylene matrix, not only at the surface, improving the mechanical, thermal, and barrier properties of the packaging.
Our aim was to induce antibacterial properties in polyethylene films by adding ZnO NPs by melt mixing, a facile process for packaging manufacturers, and to investigate the influence on the properties of these packaging films. Here we report the influence of ZnO nanoparticles on the mechanical, thermal, structural, and barrier (UV and gases) properties of LDPE films prepared by a melt mixing process at 150 °C for 10 min, with LDPE-g-MA as a compatibilizer, and verify the possibility of using them as antimicrobial packaging films for tomatoes.

2. Results and Discussion

2.1. UV-Vis Spectroscopy

Transparency is a measure of the ability of a film to block visible light, which protects photosensitive components of food. However, excessive visible light blockage can prevent consumers from visually observing food products. Therefore, a high absorbance in the UV domain coupled with a low one at wavelengths higher than 400 nm is highly desirable.
While the LDPE is transparent, the ZnO is white, therefore presenting little absorption in the visible domain (400–800 nm); nevertheless, the ZnO NPs exhibit a strong absorption band in the UV domain, with the peak at 366 nm (Figure 1).
This UV-centred absorption band is responsible for the ZnO used as sunscreen in cosmetics or as a protective coating, for example, in the textile industry. The fundamental mechanism by which this absorption peak appears is related to the electron jump from the valence band to the conduction band [51], and it has no relation to surface plasmon resonance (SPR), which is specific to metallic particles [52]. Unfortunately, the literature abounds with such mistakes [53,54] and if allowed to become rooted, they will become difficult to combat along with other misconceptions [51]. Some of the most obvious mistakes are when ZnO is considered a metallic particle [55,56] to claim a SPR. As many researchers report the synthesis of Au, Ag, and ZnO NPs by using plant extracts, some misunderstandings are gaining traction when the proposed mechanism for metallic NPs formation and their SPR are applied indiscriminately to ZnO NPs [57]. Therefore, along the non-existent SPR of ZnO, one can read about the bioreduction of Zn2+ ions to ZnO, which calls for elementary notions as oxidation states [58].
The peak at 674 nm is due to the presence of the compatibilizer (LDPE-g-MA), as can be seen by comparing the PE and PE-g-MA spectra in Figure 1. As the mass percent of LDPE-g-MA in composite samples is constant, it can be seen that the peak at 674 nm is decreasing in intensity as the ZnO percent is increasing. This can be due to the interactions between compatibilizers’ polar moieties and ZnO NPs. The same interactions are responsible for the hypsochromic shift of the ZnO peak to 361 nm.
The composite samples present a low absorption in the visible domain, coupled with a strong peak in the UV region. As such, the main optical request for a packaging film is fulfilled. The films are rather transparent under visible light (Figure 2), permitting customers to see the packed food while at the same time blocking the high-energy photons that are responsible for the initiation of oxidation reactions in lipids, vitamins, and other less stable nutrients.
A higher opacity value indicates that the film is less transparent (Table 1). As expected, the composite films present a higher opacity when compared to the simple polyethylene sample, but there is not much difference among the samples as the percentage of ZnO NPs increases from 1 to 5%. A film with opacity <2 can be considered transparent [59].

2.2. FT-IR Spectroscopy and Microscopy

The FTIR spectra of polyethylene and composite samples (Figure 3) present two strong and sharp absorption bands at 2914 and 2848 cm−1, assigned to the asymmetric and symmetric stretching vibrations of the -CH2- group, specific to the LDPE.
At 717–718 cm−1 a sharp peak, with medium intensity can be observed, which is attributed to the in-plane deformation vibration (rocking) of the methylene group -CH2- [60,61,62]. The small split-off peak from 729 to 730 cm−1 is called crystal splitting (Figure 4).
A similar splitting can be observed at 1463–1472 cm−1 (CH2 bending deformation), with the presence of LDPE-g-MA and ZnO NPs acting as nucleating agents that led to a short-range ordering of the samples [39]. Among these bands, those at 1463 and 718 cm−1 refer to the amorphous phase, and those at 1472 cm−1 and 730 cm−1 are generated by the crystalline phase [63,64,65]. The samples containing ZnO nanoparticles exhibit an absorption band at 484–488 cm−1 which is assigned to Zn-O vibration. The principal peaks and their assignments are presented in Table 2.
The FTIR microscopy images (Figure 3) present the spatial distribution of ZnO within the polyethylene composite. Figure 3 illustrates the FTIR 2D maps corresponding to the obtained films at the specific wavenumbers of 2934 cm−1, 1480 cm−1 and 685 cm−1, along with the microscopic view of the subjected region. Red areas indicate the highest absorbance, while blue areas correspond to the lowest absorbance.
The recorded FTIR 2D maps indicate a good homogenization of the ZnO NPs with the simple and functionalized polyethylene, favoring a good dispersion of the inorganic nanoparticles into the final composite. As it can be observed from Figure 3, the samples are quite homogenous, with only minor differences being present at the level of tens of µm maximum. The presence of the compatibilizer, LDPE-g-MA, reduces the agglomeration tendency and improves the dispersion of the ZnO NPs into the LDPE matrix.

2.3. Photoluminescence Spectroscopy

Changes in the fluorescence of materials are usually related to surface modification and the presence of additional interactions. Therefore, along with FTIR spectroscopy, this technique is a valuable instrument to understand the existence of surface interactions between ZnO NPs and polyethylene matrix.
The photoluminescence (fluorescence) spectra of the composite films are presented in Figure 5.
Both PE and PE-g-MA present a high fluorescent emission in the UV and violet-green domains of the visible spectra. The introduction of ZnO NPs is decreasing the intensity of emission of composite films (to 25–50% of the initial visible intensity and to 6–25% for the UV band); the higher the ZnO percent, the lower the fluorescence emission becomes. Additionally, minor shifts of some peaks are recorded, e.g., the 444 nm maximum is bathochromic shifted to 457 nm.
The shape of the emission spectra for composite samples is typical for the presence of ZnO NPs [66], with two specific regions. The emission band in the UV region, called near-band edge emission (NBE), is generated by free exciton recombination. When it has a lower intensity than the emission in the visible domain, it can be considered that the ZnO NPs have a high surface defect density, which generates active centres for fluorescence, photocatalytic activity, and also antimicrobial activity. The presence of these surface defects can act as physical traps for free electrons, which will block the recombination and therefore decrease the NBE emission intensity [67,68,69]. Nevertheless, the intensity of fluorescence spectra for ZnO containing composites is much lower than previously reported for free ZnO NPs, indicating the presence of strong surface interactions between nanoparticles and the polymer matrix [70,71].

2.4. Thermal Analysis TG-DSC

The thermal analysis results are presented in Figure 6. As it can be observed, the thermal stability of the composite films is higher than the control one, with the introduction of ZnO NPs as fillers increasing the stability of polymer chains. The ZnO NPs act as crosslinking points for the polymer chains, stabilizing them and dissipating excess energy. Therefore, the thermal stability is enhanced by ~100 °C, up to 400 °C, when compared with the control film. Similar findings were reported in the literature [13,33,72], but with a lower stabilization effect from the ZnO NPs. The presence of ZnO NPs in the final composite is improving the long-term stability of the material (ageing) as it can generate ROS that can act as scavengers for LDPE fragments, blocking further the propagation of radical reactions and, therefore, slowing degradation.
The principal numeric data are presented in Table 3, together with the calculated crystallinity degree as a ratio between measured melting enthalpy (ΔHmelting) and the melting enthalpy of 100% crystalline polymer reported by Wunderlich (293 J/g) [73,74].
The melting process starts at ~106 °C for the composite samples, about 2 °C lower than the control sample. The mass loss up to 300 °C is ~1% for composite samples and double, ~2% for the control film, mostly originating in the partial oxidation of small-molecule plasticizer. The composite samples further lose 2–3% of their initial mass between 300 and 400 °C, while the control film exhibits a mass loss of ~25% in the same interval. This proves the remarkable thermal stability induced by the presence of ZnO NPs dispersed among polymer chains (Figures S1 and S2).
The calculated crystallinity degree is decreasing, especially for the 3 and 5% ZnO samples. This can be explained by considering the dispersion of ZnO NPs, which act as crosslinking points for LDPE-g-MA and alter the ordered pattern of polymer chains.
The FTIR analysis of evolved gases (Figure 7) indicates the presence of a large quantity of CO2 (2354 cm−1) and some H2O (3500–3900 cm−1) or CO (2100–2200 cm−1) resulted from oxidation reactions, but also an important amount of hydrocarbon fragments resulted from the polymer backbone fragmentation (wavenumbers around 3000 cm−1). The enhanced thermal stability can also be observed from the temperature interval where hydrocarbon fragments start to be identified. For the control sample, all the evolved gases, H2O, CO2, CO, or C-H fragments are being eliminated at lower temperatures when compared with the PE ZnO 5% sample.

2.5. Scanning Electron Microscopy (SEM) Characterization

The SEM micrographs for ZnO NPs are presented in Figure 8. The shape of ZnO NPs is polyhedral, with a uniform size and low agglomeration tendency.
The SEM analysis for the polymer-based samples gives relevant data about surface morphology and other defects that might occur inside or on the surface of the films. The morphology of the composite films is presented in Figure 9. The surface can be considered smooth, with some occasionally scale-like structures for the PE-g-MA and PE_ZnO 1% samples. At higher magnification, the SEM micrographs indicate that on the surface of the films there are random small ZnO agglomerates, visible as white dots. The cross-section micrographs indicate that the composite films are compact, without visible porosity, with a lamellar structure and ZnO NPs well dispersed into the thickness of the films.
The energy dispersive spectrum analysis (EDS) can provide a sharp picture of the homogeneity degree (Figure 10). The elemental maps indicate the rare existence of very small agglomerates of ZnO NPs. Moreover, some defects observed in SEM micrographs can be assigned to matrix imperfections rather than to ZnO agglomerates. The distribution of each element (C, O, and Zn) was determined with the help of the corresponding Kα line from the X-ray spectra. The elemental map images confirm the homogeneity of the films, as indicated by the FTIR maps as well.

2.6. Mechanical and Barrier Properties

Films must prevent the transfer of moisture from the external environment to the food during storage, which affects the shelf life of the food; therefore, composite films must have low water vapor permeability (WVP) values. However, the excessive addition of ZnO nanoparticles might result in their presence as free particles in the composite, with fewer interactions mediated by the compatibilizer molecules, leading to the formation of discontinuous microstructures, which can reduce the mechanical properties of the films.
The mechanical properties of the composite films are presented in Table 4. The influence of ZnO NPs leads to an increase in tensile strength and then a decrease in the final composition. The tensile strength increased from 15.2 MPa for PE-g-MA to 18.9 MPa for PE_ZnO 3%, and then was reduced to 15.5 MPa for the 5% ZnO NPs composite.
The elongation at the break has a non-uniform variation. For low amounts of ZnO NPs, the value increases up to 46.1% for 3% ZnO, as the nanoparticles act as crosslinking points among the polymer chains, allowing them to move independently but still remaining in one structure. Adding more ZnO NPs (5%) leads to a sharp decrease in elongation at the break value (14.6%). This is most probably due to multiple bonding points that are stiffening the structure and do not permit the free movement of polymer chains, as the SEM micrographs did not identify discontinuous microstructures that can act as failure zones.
Ideally, through packaging films for food, the substance exchange with the environment should be negligible (loss of water, flavor, and other specific substances) [75]. Therefore, WVP values are very important, as WPV controls the moisture migration between food and the outside of packaging. In general, the microbial spoilage of food can also be associated with a high value for WVP.
The introduction of ZnO NPs between polymer chains can lead to a larger distance among backbones and therefore create spaces for water molecules to diffuse through composite film. On the other hand, the hydrophobic nature of ZnO is diminishing the capacity of water vapors to penetrate the films. The nanoparticles are acting as a physical barrier, increasing the pathway for water molecules and generating a more tortuous route (Figure 11). The combination of these two effects is what generates the end results. For all composite samples, pathway blocking was the predominant effect, with the permeability decreasing, for both O2 and H2O vapors (Table 4).

2.7. Antimicrobial Activity Assay

The evaluation of the growth inhibition results (Table 5) indicates that the presence of ZnO NPs bestows antibacterial properties on the composite films, with the control PE film exhibiting no antibacterial activity.
Although the diameter of the growth inhibition zone increased as the ZnO NPs concentration varied from 1 to 5%, the values were not statistically different. Overall, E. coli is slightly more susceptible than S. aureus to the presence of ZnO NPs; similar reports have been found in the literature [9,66].
As polyethylene has no antibacterial activity, the results are generated by the presence of ZnO NPs. Overall, the literature reports three distinct mechanisms for the antimicrobial activity of ZnO (Figure 12).
As a bacterial cell approaches the surface of the ZnO NPs, it encounters a zone where ROS production is taking place, and therefore the concentration of ROS is at its maximum. Further damage to the cellular membranes can occur due to oxidation processes. The oxidative stress generated by the accumulation of ROS is the main bactericidal mechanism of the ZnO NPs [76]. A second mechanism implies mechanical damage to the plasma membrane, by puncturing or rupture. This process leads to the leakage of cytoplasmic components (proteins, nucleic acids, etc.) [76,77]. Responsible for such activity are the ZnO NPs that are embedded at the film surface. Finally, the third mechanism is related to the penetration of the cellular membrane and the internalization of ZnO NPs. ROS production can be resumed inside the microbial cell with more devastating effects. Therefore, the capacity to penetrate the bacterial membrane promotes the nanoparticle to a higher efficiency state, where ROS are delivered inside the cell. Additionally, Zn2+ ions are released from the nanoparticles surface and contribute to cell death through cytotoxicity by binding essential components and nutrients of the cell [78].
An important property of antimicrobial packaging films is their capacity to combat biofilm formation on their surface. Therefore, the composite films were tested for surface biofilm development (Figure 13). In this case, the attachment of planktonic cells and biofilm development are significantly reduced after 24 h of incubation, indicating a direct correlation with the ZnO concentration. The highest biofilm inhibition was observed for the sample PE_ZnO at 5% for both bacterial strains. At the same time, the effect is stronger against Gram-negative E. coli when compared with Gram-positive S. aureus.
Understanding microbial adhesion and retention is crucial for controlling many processes, including biofilm formation. Disrupting the microbial ability to adhere to the packaging materials can prevent further contamination of food [79]. For the polyethylene–zinc oxide composites, the presence of the ZnO NPs at the film surface impairs the bacterial colonization of the samples, blocking the biofilm formation as depicted in Figure 14.
The most likely mechanisms involve the presence of nanoparticles embedded onto the film surface that are producing ROS and can also mechanically interact with the bacterial membrane. Zinc ions released from the nanoparticle surface might also play an important role in blocking bacterial proliferation.

2.8. Preliminary Tests on Preserving Tomatoes

Microbiological contamination of food can shorten shelf life, and the presence of antibacterial ZnO NPs in food packaging can slowly act to prevent or kill microorganisms. At the same time, the composite films have better barrier properties, blocking water loss from the packed food.
Oval-shaped tomatoes were packed with the obtained composite films and stored at 4 °C ± 1 °C and 75% relative humidity (RH) for two weeks. A control lot was wrapped in simple polyethylene film.
The preliminary visual quality check (Figure 15) and weight loss data (Table 6) indicate that polyethylene/ZnO composite films were effective in preserving the tomatoes. The samples wrapped in composite films were clearly different from the control sample, with the tomatoes preserving better the shape, color, and consistency. The weight loss increases with storage time, but there are important differences among samples; the composite film with the highest ZnO content preserves the tomatoes better.

3. Experimental Section

3.1. Materials and Methods

3.1.1. Materials

Zinc acetate dihydrate (Zn(CH3COO)2∙2H2O) with 99.9% purity and absolute ethanol and n-butanol were acquired from Merck (Redox Lab Supplies, Bucharest, Romania). Low-density polyethylene (LDPE) TIPOLEN MF 243-51 was obtained from MOL Petrochemicals Co., Ltd., Tiszaújváros, Hungary, while polyethylene grafted with maleic anhydride (LDPE-g-MA) Admer NF 468E was provided by Mitsui Chemicals Europe GmbH, Düsseldorf, Germany.

3.1.2. Instrumental Analysis

A STA 449 C F3 piece of equipment from Netzsch (Netzsch, Selb, Germany) was used for the thermogravimetric analysis coupled with differential scanning calorimetry (TG/DSC). The samples (~20 mg of each film) were placed in an open Al2O3 crucible and heated up with a 10 °C∙min−1 rate until 900 °C in a dynamic atmosphere (flow of 50 mL∙min−1 of dried air—20% O2 and 80% N2). An empty alumina crucible was used as a reference. The evolved gases were transferred through heated transfer lines and analyzed on the fly with the help of a FTIR Tensor 27 from Bruker (Bruker Co., Ettlingen, Germany), equipped with an internal thermostatic gas cell. Crystallinity % was calculated as indicated by Equation (1):
crystallinity (%) = ΔHsample melting/ΔH100% crystalline melting
A Nicolet iS50R spectrometer (Thermo Fisher Scientific, Waltham, MA, USA) was used to record the Fourier transform infrared spectra (FTIR). All measurements were performed at room temperature using the attenuated total reflection (ATR) accessory (Thermo Fisher Scientific, Waltham, MA, USA). Each spectrum is the average of 32 sample scans between 400 and 4000 cm−1, with a resolution of 4 cm−1. The FTIR 2D maps were recorded with a Nicolet iN10 MX (Nicolet, Waltham, MA, USA).
A JASCO (Jasco Inc., Easton, PA, USA) V560 spectrophotometer equipped with a 60 mm integrating sphere (ISV-469) was used to record the UV-Vis spectra. All the measurements were made in the domain 200–900 nm, with a speed of 200 nm min−1. The opacity values were calculated as A600/x = −logT600/x, where A600 is the absorbance at 600 nm, T600 is the fractional transmittance at 600 nm and x is the film thickness in mm [4].
A Perkin Elmer LS55 (Perkin Elmer, Waltham, MA, USA) fluorimeter was used to record the photoluminescence spectra (PL). A Xe lamp was used as an excitation source at ambient temperature. The excitation wavelength was 320 nm. The emission spectra were recorded in the domain 350–650 nm, with a scan speed of 200 nm min−1, a 350 nm cut-off filter, and slits of 10 nm.
Scanning electron micrographs for the determination of the films surface morphology and microstructure were obtained using a QUANTA INSPECT F50, FEI Company, Eindhoven, The Netherlands, scanning electron microscope equipped with a field emission gun—FEG with 1.2 nm resolution and an energy dispersive X-ray spectrometer (EDS) with an MnK resolution of 133 eV. Samples were coated with a thin gold layer to ensure conductivity.
Mechanical property analysis was performed using a 5965 universal testing machine (Instron, Norwood, MA, USA) with a 5 kN load cell and a crosshead speed of 50 mm/min, according to the EN ISO 527 standard [80]. The tested specimen was type 1B (10 ± 0.1 mm width at the narrow portion and 0.36 ± 0.06 mm thickness).
The permeability to water vapors was measured using a Lyssy L80-5000 tester (Dansensor, Ringsted, Denmark) with automatic temperature control and humidity sensor, according to EN ISO 15106-1 standard [81], while the permeability to oxygen was measured with a manometric tester, Lyssy L100-5000 (Dansensor, Ringsted, Denmark), according to ISO 2556:2000 [82]. For both permeability to water vapors and oxygen, samples with dimensions of about 13 × 13 mm were affixed to the self-adhesive sample cards provided with the equipment.

3.1.3. Antimicrobial Assay

An antimicrobial assay was evaluated against model Gram-positive Staphylococcus aureus ATCC 25923 and Gram-negative Escherichia coli ATCC 25922 bacterial strains. To qualitatively screen the antibacterial effect of the obtained materials, we utilized an adapted diffusion assay, respecting the general rules exposed in the CLSI 2020 and in our recent study [5]. Bacterial suspensions (0.5 McFarland, 1.5 × 108 CFU/mL) were prepared in sterile saline solution (0.9% NaCl) and were further utilized as a standardized inoculum to swab inoculate Petri dishes containing nutritive agar. Discs of 6 mm in diameter from the composite films were sterilized by UV exposure for 30 min before use. Sample discs were aseptically placed on the inoculated Petri dishes, and these were incubated for 20 h at 37 °C. After incubation, the diameter of growth inhibition developed around each material specimen was measured and expressed in mm.
The antibiofilm efficiency tests were performed by introducing sterile 6 mm-diameter disks, from each composite film into sterile 24-well plates containing 1 mL of nutritive broth, followed by the inoculation of 10 μL of bacterial suspension of 0.5 McFarland standard density. The as prepared plates were incubated for 24 h at 37 °C. After 24 h the disks were gently washed with 1 mL of sterile saline and transferred to centrifuge tubes containing 1 mL of sterile saline solution. The tubes were vortexed for 30 s to ensure the detachment of biofilm cells in suspension. Serial 10-fold dilutions were obtained and then inoculated on nutrient agar in order to evaluate the viable colony formation, expressed as CFU (colony-forming units)/mL. All experiments were designed and performed in triplicate.

3.2. Synthesis of ZnO Nanoparticles

ZnO synthesis was performed by forced solvolysis, as described previously in [83] with modifications from [32]. Shortly, 2.1950 g of Zn(CH3COO)2∙2H2O was mixed with 50 mL of n-butanol and heated to boiling point under vigorous magnetic stirring for 10 h. The resulting precipitate was washed twice with water and finally with ethanol. The separation was done by centrifugation, and the obtained powder was further dried at 105 °C.

3.3. Synthesis of Polyethylene/ZnO Composite Films

The mixtures (LDPE, LDPE-g-MA, glycerol, and ZnO NPs) in quantities from Table 7 were introduced in an internal Plasti-Corder Brabender mixer at 150 °C with a mixing rate of 50–70 rpm for 10 min.
The resulting mixtures were used to make polyethylene/ZnO composite films using specific moulds and the laboratory electrical press. The metal frame with dimensions of 245 × 300 mm was pressed between metal plates. The processing parameters were: preheating for 2 min at the temperature of 160 °C; modelling at the temperature of 160 °C; with a pressing force of 300 kN for 10 min; followed by the cooling down stage to 45 °C. The schematic process is depicted in Figure 16.

4. Conclusions

In this study, antibacterial packaging films were prepared by introducing ZnO NPs into the polyethylene matrix. The result indicates that even the low concentration of 1% ZnO is enough for the antibacterial and antibiofilm activity to kick in. Innovative antimicrobial packaging films based on polyethylene and ZnO nanoparticles were obtained in a simple melt mixing process at 150 °C for 10 min with the help of a Plasti-Corder Brabender mixer. The FTIR microscopy and SEM micrographs indicate that the ZnO nanoparticles were homogenously dispersed into the polyethylene matrix. The new composite PE-ZnO films exhibited higher thermal stability vs. the simple polyethylene film up to 400 °C. The light barrier properties of the new composite are very good in the UV domain, with a transmittance as low as ~4% at 361 nm, but with high transparency in the visible domain. This is especially important as the high energy photons can induce food alteration by interacting with lipids or proteins. The introduction of ZnO into the composite has not altered dramatically the transparency of the packaging films in the visible domain, allowing customers to see the packed food. Barrier properties are improved by introducing the ZnO NPs into the polyethylene matrix; the mechanical and barrier properties are optimum at a concentration of 3% ZnO. Therefore, improvements in the properties of novel polyethylene composite films will be beneficial for many applications, in particular the packaging of food products, which are very sensitive to oxygen and UV light.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/ijms25116073/s1.

Author Contributions

Conceptualization and methodology, A.F., L.M. and O.-C.O.; composite preparation, M.S., D.F., M.D.S. and M.N.; investigation, M.S., D.F., L.M., R.-D.T., A.M.H., O.-C.O. and G.M.; writing-original draft preparation, R.-D.T., M.D.S., D.F., L.M., A.M.H. and O.-C.O.; writing-review and editing, M.N., A.F., G.M. and O.-C.O. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by a grant of the Ministry of Research, Innovation, and Digitization, CCCDI—UEFISCDI, project number PN-III-P2-2.1-PED-2021-3414, within PNCDI III; 573PED/2022, “Ambalaje inovative cu activitate antimicrobiana pentru siguranta alimentara”. The authors are grateful to the Romanian Government for providing access to the research infrastructure of the National Center for Micro and Nanomaterials through the National Program titled “Installations and Strategic Objectives of National Interest”.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available upon request from the corresponding authors.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Motelica, L.; Ficai, D.; Ficai, A.; Oprea, O.C.; Kaya, D.A.; Andronescu, E. Biodegradable Antimicrobial Food Packaging: Trends and Perspectives. Foods 2020, 9, 1438. [Google Scholar] [CrossRef] [PubMed]
  2. Motelica, L.; Ficai, D.; Oprea, O.C.; Ficai, A.; Andronescu, E. Smart Food Packaging Designed by Nanotechnological and Drug Delivery Approaches. Coatings 2020, 10, 806. [Google Scholar] [CrossRef]
  3. Radulescu, M.; Ficai, D.; Oprea, O.; Ficai, A.; Andronescu, E.; Holban, A.M. Antimicrobial Chitosan based Formulations with Impact on Different Biomedical Applications. Curr. Pharm. Biotechnol. 2015, 16, 128–136. [Google Scholar] [CrossRef] [PubMed]
  4. Motelica, L.; Ficai, D.; Oprea, O.C.; Ficai, A.; Trusca, R.D.; Andronescu, E.; Holban, A. Biodegradable Alginate Films with ZnO Nanoparticles and Citronella Essential Oil—A Novel Antimicrobial Structure. Pharmaceutics 2021, 13, 1020. [Google Scholar] [CrossRef] [PubMed]
  5. Lemnaru (Popa), G.-M.; Trusca, R.D.; Ilie, C.-I.; Tiplea, R.D.; Ficai, D.; Oprea, O.; Stoica-Guzun, A.; Ficai, A.; Ditu, L.-M. Antibacterial Activity of Bacterial Cellulose Loaded with Bacitracin and Amoxicillin: In Vitro Studies. Molecules 2020, 25, 4069. [Google Scholar] [CrossRef] [PubMed]
  6. Wilpiszewska, K.; Antosik, A.K.; Schmidt, B.; Janik, J.; Rokicka, J. Hydrophilic Films Based on Carboxymethylated Derivatives of Starch and Cellulose. Polymers 2020, 12, 2447. [Google Scholar] [CrossRef] [PubMed]
  7. Li, S.B.; Yi, J.J.; Yu, X.M.; Wang, Z.Y.; Wang, L. Preparation and characterization of pullulan derivative/chitosan composite film for potential antimicrobial applications. Int. J. Biol. Macromol. 2020, 148, 258–264. [Google Scholar] [CrossRef] [PubMed]
  8. Conte, A.; Longano, D.; Costa, C.; Ditaranto, N.; Ancona, A.; Cioffi, N.; Scrocco, C.; Sabbatini, L.; Conto, F.; Del Nobile, M.A. A novel preservation technique applied to fiordilatte cheese. Innov. Food Sci. Emerg. 2013, 19, 158–165. [Google Scholar] [CrossRef]
  9. Motelica, L.; Vasile, B.-S.; Ficai, A.; Surdu, V.-A.; Ficai, D.; Oprea, O.C.; Andronescu, E.; Mustățea, G.; Ungureanu, E.L.; Dobre, A.A. Antibacterial activity of zinc oxide nanoparticles loaded with essential oils. Pharmaceutics 2023, 15, 2470. [Google Scholar] [CrossRef]
  10. Motelica, L.; Oprea, O.C.; Vasile, B.S.; Ficai, A.; Ficai, D.; Andronescu, E.; Holban, A.M. Antibacterial Activity of Solvothermal Obtained ZnO Nanoparticles with Different Morphology and Photocatalytic Activity against a Dye Mixture: Methylene Blue, Rhodamine B and Methyl Orange. Int. J. Mol. Sci. 2023, 24, 5677. [Google Scholar] [CrossRef]
  11. Nituica, M.; Oprea, O.; Stelescu, M.D.; Sonmez, M.; Georgescu, M.; Alexandrescu, L.; Motelica, L. Polymeric Biocomposite Based on Thermoplastic Polyurethane (TPU) and Protein and Elastomeric Waste Mixture. Materials 2023, 16, 5279. [Google Scholar] [CrossRef] [PubMed]
  12. Kuplennik, N.; Tchoudakov, R.; Zelas, Z.B.B.; Sadovski, A.; Fishman, A.; Narkis, M. Antimicrobial packaging based on linear low-density polyethylene compounded with potassium sorbate. LWT-Food Sci. Technol. 2015, 62, 278–286. [Google Scholar] [CrossRef]
  13. Charoensri, K.; Shin, Y.J.; Park, H.J. Innovative HDPE Composites Enriched with UV Stabilizer and Diatomaceous Earth/Zinc Oxide for Enhanced Seafood Packaging and Antimicrobial Properties. Polymers 2023, 15, 4577. [Google Scholar] [CrossRef] [PubMed]
  14. Martínez-Tenorio, Y.; Ramírez-Corona, N.; Jiménez-Munguia, M.T.; López-Malo, A.; Mani-López, E. Development of Antifungal Packaging From Low-Density Polyethylene With Essential Oil of Oregano and Potassium Sorbate. Packag. Technol. Sci. 2024; early view. [Google Scholar] [CrossRef]
  15. Motelica, L.; Ficai, D.; Ficai, A.; Trusca, R.D.; Ilie, C.I.; Oprea, O.C.; Andronescu, E. Innovative Antimicrobial Chitosan/ZnO/Ag NPs/Citronella Essential Oil Nanocomposite—Potential Coating for Grapes. Foods 2020, 9, 1801. [Google Scholar] [CrossRef] [PubMed]
  16. Petrisor, G.; Motelica, L.; Ficai, D.; Ilie, C.I.; Trusca, R.D.; Surdu, V.A.; Oprea, O.C.; Mirt, A.L.; Vasilievici, G.; Semenescu, A.; et al. Increasing Bioavailability of Trans-Ferulic Acid by Encapsulation in Functionalized Mesoporous Silica. Pharmaceutics 2023, 15, 660. [Google Scholar] [CrossRef] [PubMed]
  17. Dehghani, S.; Peighambardoust, S.H.; Peighambardoust, S.J.; Fasihnia, S.H.; Khosrowshahi, N.K.; Gullón, B.; Lorenzo, J.M. Optimization of the Amount of ZnO, CuO, and Ag Nanoparticles on Antibacterial Properties of Low-Density Polyethylene (LDPE) Films Using the Response Surface Method. Food Anal. Methods 2021, 14, 98–107. [Google Scholar] [CrossRef]
  18. Zhao, L.Y.; Duan, G.G.; Zhang, G.Y.; Yang, H.Q.; He, S.J.; Jiang, S.H. Electrospun Functional Materials toward Food Packaging Applications: A Review. Nanomaterials 2020, 10, 150. [Google Scholar] [CrossRef]
  19. Xing, Y.G.; Li, X.L.; Guo, X.L.; Li, W.X.; Chen, J.W.; Liu, Q.; Xu, Q.L.; Wang, Q.; Yang, H.; Shui, Y.R.; et al. Effects of Different TiO2 Nanoparticles Concentrations on the Physical and Antibacterial Activities of Chitosan-Based Coating Film. Nanomaterials 2020, 10, 1365. [Google Scholar] [CrossRef] [PubMed]
  20. Viktorova, J.; Stupak, M.; Rehorova, K.; Dobiasova, S.; Hoang, L.; Hajslova, J.; Thanh, T.V.; Tri, L.V.; Tuan, N.V.; Ruml, T. Lemon Grass Essential Oil does not Modulate Cancer Cells Multidrug Resistance by Citral-Its Dominant and Strongly Antimicrobial Compound. Foods 2020, 9, 585. [Google Scholar] [CrossRef]
  21. Fleancu, M.C.; Olteanu, N.L.; Rogozea, A.E.; Crisciu, A.V.; Pincovschi, I.; Mihaly, M. Physical-chemical parameters promoting phase changes in non-ionic environmental-friendly microemulsions. Fluid. Phase Equilibr 2013, 337, 18–25. [Google Scholar] [CrossRef]
  22. Sonseca, A.; Madani, S.; Rodriguez, G.; Hevilla, V.; Echeverria, C.; Fernandez-Garcia, M.; Munoz-Bonilla, A.; Charef, N.; Lopez, D. Multifunctional PLA Blends Containing Chitosan Mediated Silver Nanoparticles: Thermal, Mechanical, Antibacterial, and Degradation Properties. Nanomaterials 2020, 10, 22. [Google Scholar] [CrossRef] [PubMed]
  23. Kim, D.Y.; Patel, S.K.S.; Rasool, K.; Lone, N.; Bhatia, S.K.; Seth, C.S.; Ghodake, G.S. Bioinspired silver nanoparticle-based nanocomposites for effective control of plant pathogens: A review. Sci. Total Environ. 2024, 908, 168318. [Google Scholar] [CrossRef] [PubMed]
  24. Motelica, L.; Ficai, D.; Oprea, O.C.; Ficai, A.; Ene, V.L.; Vasile, B.S.; Andronescu, E.; Holban, A.M. Antibacterial Biodegradable Films Based on Alginate with Silver Nanoparticles and Lemongrass Essential Oil-Innovative Packaging for Cheese. Nanomaterials 2021, 11, 2377. [Google Scholar] [CrossRef] [PubMed]
  25. Senturk Parreidt, T.; Muller, K.; Schmid, M. Alginate-Based Edible Films and Coatings for Food Packaging Applications. Foods 2018, 7, 170. [Google Scholar] [CrossRef] [PubMed]
  26. Smaoui, S.; Chérif, I.; Ben Hlima, H.; Khan, M.U.; Rebezov, M.; Thiruvengadam, M.; Sarkar, T.; Shariati, M.A.; Lorenzo, J.M. Zinc oxide nanoparticles in meat packaging: A systematic review of recent literature. Food Packag. Shelf 2023, 36, 101045. [Google Scholar] [CrossRef]
  27. Bolognesi, C.; Castle, L.; Cravedi, J.P.; Engel, K.H.; Fowler, P.; Grob, K.; Gürtler, R.; Husoy, T.; Mennes, W.; Milana, M.R.; et al. Scientific Opinion on the safety evaluation of the substance zinc oxide, nanoparticles, uncoated and coated with [3-(methacryloxy) propyl] trimethoxysilane, for use in food contact materials. EFSA J. 2015, 13, 4063. [Google Scholar] [CrossRef]
  28. Bolognesi, C.; Castle, L.; Cravedi, J.P.; Engel, K.H.; Franz, R.; Fowler, P.; Grob, K.; Gürtler, R.; Husoy, T.; Kärenlampi, S.; et al. Safety assessment of the substance zinc oxide, nanoparticles, for use in food contact materials. EFSA J. 2016, 14, 4408. [Google Scholar] [CrossRef]
  29. Pavoski, G.; Kalikoski, R.; Souza, G.; Baldisserotto, D.; Brum, L.F.W.; dos Santos, C.; Bergmann, C.; Brandelli, A.; Jacobi, M.; Galland, G. Antimicrobial High-Density Polyethylene (HDPE)/ZnO Nanocomposites Obtained by Polymerization. J. Braz. Chem. Soc. 2020, 31, 1566–1574. [Google Scholar] [CrossRef]
  30. Dumbrava, A.; Berger, D.; Matei, C.; Prodan, G.; Aonofriesei, F.; Radu, M.D.; Moscalu, F. New Composite Nanomaterials with Antimicrobial and Photocatalytic Properties Based on Silver and Zinc Oxide. J. Inorg. Organomet. Polym. Mater. 2019, 29, 2072–2082. [Google Scholar] [CrossRef]
  31. Lungu, I.I.; Holban, A.M.; Ficai, A.; Grumezescu, A.M. Zinc Oxide Nanostrucures: New Trends in Antimicrobial Therapy. In Nanostructures for Antimicrobial Therapy; Elsevier: Amsterdam, The Netherlands, 2017; pp. 503–514. [Google Scholar] [CrossRef]
  32. Motelica, L.; Vasile, B.S.; Ficai, A.; Surdu, A.V.; Ficai, D.; Oprea, O.C.; Andronescu, E.; Jinga, D.C.; Holban, A.M. Influence of the Alcohols on the ZnO Synthesis and Its Properties: The Photocatalytic and Antimicrobial Activities. Pharmaceutics 2022, 14, 2842. [Google Scholar] [CrossRef]
  33. Gao, W.; Li, Y.F.; Zhao, J.T.; Zhang, Z.; Tang, W.W. Influence of surface modification of zinc oxide on physical properties of high density polyethylene. Colloid Surf. A 2022, 653, 130000. [Google Scholar] [CrossRef]
  34. Emamifar, A.; Mohammadizadeh, M. Preparation and Application of LDPE/ZnO Nanocomposites for Extending Shelf Life of Fresh Strawberries. Food Technol. Biotechnol. 2015, 53, 488–495. [Google Scholar] [CrossRef] [PubMed]
  35. Alim, A.A.A.; Baharum, A.; Shirajuddin, S.S.M.; Anuar, F.H. Blending of Low-Density Polyethylene and Poly(Butylene Succinate) (LDPE/PBS) with Polyethylene-Graft-Maleic Anhydride (PE-g-MA) as a Compatibilizer on the Phase Morphology, Mechanical and Thermal Properties. Polymers 2023, 15, 261. [Google Scholar] [CrossRef] [PubMed]
  36. Stelescu, M.D.; Oprea, O.C.; Motelica, L.; Ficai, A.; Trusca, R.D.; Sonmez, M.; Nituica, M.; Georgescu, M. Obtaining and Characterizing New Types of Materials Based on Low-Density Polyethylene and Thermoplastic Starch. J. Compos. Sci. 2024, 8, 134. [Google Scholar] [CrossRef]
  37. Yu, D.R.; Liu, S.Q.; Xin, Y. Air Plasma-Nano ZnO Coating Improves the Impact Resistance of Ultra-High Molecular Weight Polyethylene Fiber. Compos. Interface 2023, 30, 1247–1267. [Google Scholar] [CrossRef]
  38. Agbozouhoue, K.K.; Koffi, D.; Erchiqui, F.; Barnabé, S. ZnO Treatment on Mechanical Behavior of Polyethylene/Yellow Birch Fiber Composites When Exposed to Fungal Wood Rot. Polymers 2023, 15, 3664. [Google Scholar] [CrossRef] [PubMed]
  39. Barabaszová, K.C.; Holesová, S.; Hundáková, M.; Kalendová, A. Tribo-Mechanical Properties of the Antimicrobial Low-Density Polyethylene (LDPE) Nanocomposite with Hybrid ZnO-Vermiculite-Chlorhexidine Nanofillers. Polymers 2020, 12, 2811. [Google Scholar] [CrossRef]
  40. Alsayed, Z.; Awad, R.; Badawi, M.S. Thermo-mechanical properties of high density polyethylene with zinc oxide as a filler. Iran. Polym. J. 2020, 29, 309–320. [Google Scholar] [CrossRef]
  41. Vahidi, G.; Bajwa, D.S.; Shojaeiarani, J.; Stark, N.M. Experimental investigation into the direct feeding of coupling agent, cellulose nanocrystals, and nano zinc oxide in high-density polyethylene. Compos. Part. C-Open 2022, 8, 100287. [Google Scholar] [CrossRef]
  42. Yao, Y.L.; De Guzman, M.R.; Duan, H.; Gao, C.; Lin, X.; Wen, Y.H.; Du, J.; Lin, L.; Chen, J.C.; Wu, C.S.; et al. Infusing High-density Polyethylene with Graphene-Zinc Oxide to Produce Antibacterial Nanocomposites with Improved Properties. Chin. J. Polym. Sci. 2020, 38, 898–907. [Google Scholar] [CrossRef]
  43. Mwafy, E.A.; Abd-Elmgeed, A.A.; Kandil, A.A.; Elsabbagh, I.A.; Elfass, M.M.; Gaafar, M.S. High UV-shielding Performance of Zinc Oxide/High-Density Polyethylene Nanocomposites. Spectrosc. Lett. 2015, 48, 646–652. [Google Scholar] [CrossRef]
  44. Fiedot-Tobola, M.; Ciesielska, M.; Maliszewska, I.; Rac-Rumijowska, O.; Suchorska-Wozniak, P.; Teterycz, H.; Bryjak, M. Deposition of Zinc Oxide on Different Polymer Textiles and Their Antibacterial Properties. Materials 2018, 11, 707. [Google Scholar] [CrossRef]
  45. Vatanpour, V.; Nekouhi, G.N.; Esmaeili, M. Preparation, characterization and performance evaluation of ZnO deposited polyethylene ultrafiltration membranes for dye and protein separation. J. Taiwan Inst. Chem. Eng. 2020, 114, 153–167. [Google Scholar] [CrossRef]
  46. Faraj, M.G.; Ibrahim, K.; Eisa, M.H.; Pakhuruddin, M.K.M.; Pakhuruddin, M.Z. Comparison of Zinc Oxide thin films deposited on the glass and polyethylene terephthalate substrates by thermal evaporation technique for applications in solar cells. Optoelectron. Adv. Mater. 2010, 4, 1587–1590. [Google Scholar]
  47. Alluhaibi, A.A.; Sendi, R.K. Effect of Plasticisers and Zinc Oxide Nanoparticle Concentration on the Properties of Polyethylene Thin Films. IOP Conf. Ser. Mater. Sci. Eng. 2022, 1269, 012002. [Google Scholar] [CrossRef]
  48. Zhu, K.X.; Wang, H.D.; Chen, C.W.; Xie, J. Development of polyethylene antifogging and antibacterial packaging films for lettuce preservation. LWT-Food Sci. Technol. 2023, 181, 114772. [Google Scholar] [CrossRef]
  49. Wang, Y.; Wang, T.; Liu, L.Z.; Wang, Y.X.; Song, L.X.; Shi, Y. Effect of nanometer zinc oxide and processing technology on the properties of antibacterial composites. Polym. Bull. 2023, 81, 7193–7210. [Google Scholar] [CrossRef]
  50. Stelescu, M.D.; Stefan, A.; Sonmez, M.; Nituica, M.; Georgescu, M. Elasto-Plastic Materials Based on EPDM Rubber, LDPE, Plasticized Starch and OMMT. Mater. Plast. 2024, 61, 131–140. [Google Scholar] [CrossRef]
  51. Brik, M.G.; Srivastava, A.M.; Popov, A.I. A few common misconceptions in the interpretation of experimental spectroscopic data. Opt. Mater. 2022, 127, 112276. [Google Scholar] [CrossRef]
  52. Marinescu, L.; Ficai, D.; Oprea, O.; Marin, A.; Ficai, A.; Andronescu, E.; Holban, A.M. Optimized Synthesis Approaches of Metal Nanoparticles with Antimicrobial Applications. J. Nanomater. 2020, 2020, 6651207. [Google Scholar] [CrossRef]
  53. Bala, N.; Saha, S.; Chakraborty, M.; Maiti, M.; Das, S.; Basu, R.; Nandy, P. Green synthesis of zinc oxide nanoparticles using leaf extract: Effect of temperature on synthesis, anti-bacterial activity and anti-diabetic activity. RSC Adv. 2015, 5, 4993–5003. [Google Scholar] [CrossRef]
  54. Padalia, H.; Chanda, S. Characterization, antifungal and cytotoxic evaluation of green synthesized zinc oxide nanoparticles using leaf extract. Artif. Cells Nanomed. Biotechnol. 2017, 45, 1751–1761. [Google Scholar] [CrossRef]
  55. Chaurasia, V.; Chand, N.; Bajpai, S.K. Water Sorption Properties and Antimicrobial Action of Zinc Oxide Nanoparticles-Loaded Cellulose Acetate Films. J. Macromol. Sci. A 2010, 47, 309–317. [Google Scholar] [CrossRef]
  56. Altammar, K.A. A review on nanoparticles: Characteristics, synthesis, applications, and challenges. Front. Microbiol. 2023, 14, 1155622. [Google Scholar] [CrossRef] [PubMed]
  57. Sharmila, G.; Thirumarimurugan, M.; Muthukumaran, C. Green synthesis of ZnO nanoparticles using leaf extract: Characterization and evaluation of its antioxidant, bactericidal and anticancer activities. Microchem. J. 2019, 145, 578–587. [Google Scholar] [CrossRef]
  58. Jayaseelan, C.; Rahuman, A.A.; Kirthi, A.V.; Marimuthu, S.; Santhoshkumar, T.; Bagavan, A.; Gaurav, K.; Karthik, L.; Rao, K.V.B. Novel microbial route to synthesize ZnO nanoparticles using and their activity against pathogenic bacteria and fungi. Spectrochim. Acta A 2012, 90, 78–84. [Google Scholar] [CrossRef] [PubMed]
  59. Dou, Y.; Huang, X.; Zhang, B.N.; He, M.; Yin, G.Q.; Cui, Y.D. Preparation and characterization of a dialdehyde starch crosslinked feather keratin film for food packaging application. RSC Adv. 2015, 5, 27168–27174. [Google Scholar] [CrossRef]
  60. Smith, B.C. The Infrared Spectra of Polymers II: Polyethylene. Spectroscopy 2021, 36, 24–29. [Google Scholar] [CrossRef]
  61. Depan, D.; Chirdon, W.; Khattab, A. Morphological and Chemical Analysis of Low-Density Polyethylene Crystallized on Carbon and Clay Nanofillers. Polymers 2021, 13, 1558. [Google Scholar] [CrossRef]
  62. Agosti, E.; Zerbi, G.; Ward, I.M. Structure of the Skin and Core of Ultradrawn Polyethylene Films by Vibrational Spectroscopy. Polymer 1992, 33, 4219–4229. [Google Scholar] [CrossRef]
  63. Painter, P.C.; Havens, J.; Hart, W.W.; Koenig, J.L. Fourier-Transform Ir Spectroscopic Investigation of Polyethylene Single-Crystals. II. Fine-Structure of CH2 Rocking Mode. J. Polym. Sci. Pol. Phys. 1977, 15, 1237–1249. [Google Scholar] [CrossRef]
  64. Huang, J.B.; Hong, J.W.; Urban, M.W. Attenuated Total Reflectance Fourier-Transform Infrared Studies of Crystalline Amorphous Content on Polyethylene Surfaces. Polymer 1992, 33, 5173–5178. [Google Scholar] [CrossRef]
  65. Fontana, L.; Santoro, M.; Bini, R.; Vinh, D.Q.; Scandolo, S. High-pressure vibrational properties of polyethylene. J. Chem. Phys. 2010, 133, 204502. [Google Scholar] [CrossRef] [PubMed]
  66. Motelica, L.; Popescu, A.; Razvan, A.G.; Oprea, O.; Trusca, R.D.; Vasile, B.S.; Dumitru, F.; Holban, A.M. Facile Use of ZnO Nanopowders to Protect Old Manual Paper Documents. Materials 2020, 13, 5452. [Google Scholar] [CrossRef] [PubMed]
  67. Ghifari, N.; Cinquin, B.; Chahboun, A.; El Abed, A.I. Rhodamine B Doped ZnO Monodisperse Microcapsules: Droplet-Based Synthesis, Dynamics and Self-Organization of ZnO Nanoparticles and Dye Molecules. Nanomaterials 2020, 10, 2351. [Google Scholar] [CrossRef] [PubMed]
  68. Pomastowski, P.; Krol-Gorniak, A.; Railean-Plugaru, V.; Buszewski, B. Zinc Oxide Nanocomposites-Extracellular Synthesis, Physicochemical Characterization and Antibacterial Potential. Materials 2020, 13, 4347. [Google Scholar] [CrossRef] [PubMed]
  69. Asamoah, R.B.; Yaya, A.; Nbelayim, P.; Annan, E.; Onwona-Agyeman, B. Development and Characterization of Clay-Nanocomposites for Water Purification. Materials 2020, 13, 3793. [Google Scholar] [CrossRef] [PubMed]
  70. Tachikawa, S.; Noguchi, A.; Tsuge, T.; Hara, M.; Odawara, O.; Wada, H. Optical Properties of ZnO Nanoparticles Capped with Polymers. Materials 2011, 4, 1132–1143. [Google Scholar] [CrossRef]
  71. Stanculescu, A.; Socol, M.; Rasoga, O.; Breazu, C.; Preda, N.; Stanculescu, F.; Socol, G.; Vacareanu, L.; Girtan, M.; Doroshkevich, A.S. Arylenevinylene Oligomer-Based Heterostructures on Flexible AZO Electrodes. Materials 2021, 14, 7688. [Google Scholar] [CrossRef]
  72. Charoensri, K.; Shin, Y.J.; Kim, K.C.; Park, H.J. Active Packaging Material Based on Immobilized Diatomaceous Earth/Zinc Oxide/High-Density Polyethylene Composite for Sea Food and Products. Polymers 2022, 14, 5228. [Google Scholar] [CrossRef]
  73. Poh, L.; Wu, Q.; Chen, Y.D.; Narimissa, E. Characterization of industrial low-density polyethylene: A thermal, dynamic mechanical, and rheological investigation. Rheol. Acta 2022, 61, 701–720. [Google Scholar] [CrossRef]
  74. Wunderlich, B. (Ed.) Appendix—ATHAS Table of Thermal Properties of Linear Macromolecules; Thermal Analysis; Academic Press: London, UK, 1990; pp. 417–431. [Google Scholar]
  75. Naidu, D.S.; John, M.J. Effect of Clay Nanofillers on the Mechanical and Water Vapor Permeability Properties of Xylan-Alginate Films. Polymers 2020, 12, 2279. [Google Scholar] [CrossRef] [PubMed]
  76. Abebe, B.; Zereffa, E.A.; Tadesse, A.; Murthy, H.C.A. A Review on Enhancing the Antibacterial Activity of ZnO: Mechanisms and Microscopic Investigation. Nanoscale Res. Lett. 2020, 15, 190. [Google Scholar] [CrossRef] [PubMed]
  77. Franco, D.; Calabrese, G.; Guglielmino, S.P.P.; Conoci, S. Metal-Based Nanoparticles: Antibacterial Mechanisms and Biomedical Application. Microorganisms 2022, 10, 1778. [Google Scholar] [CrossRef]
  78. Kang, S.; Park, D.H.; Hwang, J. Hierarchical ZnO nano-spines grown on a carbon fiber seed layer for efficient VOC removal and airborne virus and bacteria inactivation. J. Hazard. Mater. 2022, 424, 127262. [Google Scholar] [CrossRef]
  79. Yongabi, D.; Jooken, S.; Givanoudi, S.; Khorshid, M.; Deschaume, O.; Bartic, C.; Losada-Pérez, P.; Wübbenhorst, M.; Wagner, P. Ionic strength controls long-term cell-surface interactions—A QCM-D study of S. cerevisiae adhesion, retention and detachment. J. Colloid Interface Sci. 2021, 585, 583–595. [Google Scholar] [CrossRef]
  80. ISO 527; Plastics—Determination of Tensile Properties. ISO: Geneva, Switzerland, 2019. Available online: https://standards.iteh.ai/catalog/standards/sist/926d5ea4-e0ad-4a58-b318-520f53bb3c85/iso-527-1-2019 (accessed on 5 April 2024).
  81. ISO 15106-1; Plastics—Film and Sheeting—Determination of Water Vapour Transmission Rate. Part 1: Humidity Detection Sensor Method. ISO: Geneva, Switzerland, 2003. Available online: https://standards.iteh.ai/catalog/standards/sist/c15de716-9989-4c60-ba8a-3efcf6bda179/iso-15106-1-2003 (accessed on 5 April 2024).
  82. ISO 2556:2000; Plastics-Determination of the Gas Transmission Rate of Films and Thin Sheets under Atmospheric Pressure-Manometric Method. ISO: Geneva, Switzerland, 2000. Available online: https://standards.iteh.ai/catalog/standards/cen/7d33cd43-472d-45aa-87af-206abdd15656/en-iso-2556-2000 (accessed on 5 April 2024).
  83. Oprea, O.; Andronescu, E.; Vasile, B.S.; Voicu, G.; Covaliu, C. Synthesis and Characterization of Zno Nanopowder by Non-Basic Route. Dig. J. Nanomater. Biostruct. 2011, 6, 1393–1401. [Google Scholar]
Ijms 25 06073 g001
Figure 1. The UV-Vis spectra for (a) ZnO; (b) PE, PE-g-MA, PE_ZnO 1%, PE_ZnO 3%, and PE_ZnO 5% films.
Figure 1. The UV-Vis spectra for (a) ZnO; (b) PE, PE-g-MA, PE_ZnO 1%, PE_ZnO 3%, and PE_ZnO 5% films.
Ijms 25 06073 g001
Ijms 25 06073 g002
Figure 2. The transparency for PE-g-MA, PE_ZnO 1%, PE_ZnO 3%, and PE_ZnO 5% films.
Figure 2. The transparency for PE-g-MA, PE_ZnO 1%, PE_ZnO 3%, and PE_ZnO 5% films.
Ijms 25 06073 g002
Ijms 25 06073 g003
Figure 3. FTIR spectra and microscopy maps of polyethylene/ZnO composite films at 2914, 1471, and 485 cm–1; red areas indicate the highest absorbance, while blue areas correspond to the lowest absorbance.
Figure 3. FTIR spectra and microscopy maps of polyethylene/ZnO composite films at 2914, 1471, and 485 cm–1; red areas indicate the highest absorbance, while blue areas correspond to the lowest absorbance.
Ijms 25 06073 g003
Ijms 25 06073 g004
Figure 4. Detail of FTIR spectra of the PE ZnO 5% sample for the wavenumber intervals 700–800 cm−1 and 1400–1500 cm−1.
Figure 4. Detail of FTIR spectra of the PE ZnO 5% sample for the wavenumber intervals 700–800 cm−1 and 1400–1500 cm−1.
Ijms 25 06073 g004
Ijms 25 06073 g005
Figure 5. The fluorescence spectra for PE, PE-g-MA and PE_ZnO 1–5% films.
Figure 5. The fluorescence spectra for PE, PE-g-MA and PE_ZnO 1–5% films.
Ijms 25 06073 g005
Ijms 25 06073 g006
Figure 6. TG-DSC curves for PE-g-MA and PE_ZnO 1%, PE_ZnO 3%, and PE_ZnO 5% composite films.
Figure 6. TG-DSC curves for PE-g-MA and PE_ZnO 1%, PE_ZnO 3%, and PE_ZnO 5% composite films.
Ijms 25 06073 g006
Ijms 25 06073 g007
Figure 7. The FTIR 3D diagram for the PE_g_MA–control (a) and PE_ZnO 5% (c), respectively, their 2D projections in the temperature/wavenumber plane PE_g_MA–control (b) and PE_ZnO 5% (d); On top of each 2D projection is the FTIR spectrum at the temperature of the highest decomposition rate (464 and 430 °C); on the right side of each 2D projection is the evolving trace for the wavenumber 2934 cm−1 assigned to the C-H asymmetric vibration from –CH2 moieties.
Figure 7. The FTIR 3D diagram for the PE_g_MA–control (a) and PE_ZnO 5% (c), respectively, their 2D projections in the temperature/wavenumber plane PE_g_MA–control (b) and PE_ZnO 5% (d); On top of each 2D projection is the FTIR spectrum at the temperature of the highest decomposition rate (464 and 430 °C); on the right side of each 2D projection is the evolving trace for the wavenumber 2934 cm−1 assigned to the C-H asymmetric vibration from –CH2 moieties.
Ijms 25 06073 g007
Ijms 25 06073 g008
Figure 8. The SEM micrographs for the ZnO nanoparticles.
Figure 8. The SEM micrographs for the ZnO nanoparticles.
Ijms 25 06073 g008
Ijms 25 06073 g009aIjms 25 06073 g009b
Figure 9. The SEM micrographs for PE-g-MA and PE_ZnO 1%, PE_ZnO 3% and PE_ZnO 5% composite films.
Figure 9. The SEM micrographs for PE-g-MA and PE_ZnO 1%, PE_ZnO 3% and PE_ZnO 5% composite films.
Ijms 25 06073 g009aIjms 25 06073 g009b
Ijms 25 06073 g010
Figure 10. The EDS determined the elemental composition and elemental distribution maps for the PE_ZnO 5% composite film.
Figure 10. The EDS determined the elemental composition and elemental distribution maps for the PE_ZnO 5% composite film.
Ijms 25 06073 g010
Ijms 25 06073 g011
Figure 11. Schematic depiction of the tortuous pathway followed by water molecules passing through the composite films.
Figure 11. Schematic depiction of the tortuous pathway followed by water molecules passing through the composite films.
Ijms 25 06073 g011
Ijms 25 06073 g012
Figure 12. Schematic depiction of the ZnO NPs antibacterial mechanisms.
Figure 12. Schematic depiction of the ZnO NPs antibacterial mechanisms.
Ijms 25 06073 g012
Ijms 25 06073 g013
Figure 13. Graphical representation of log10 CFU/mL values obtained for the tested E.coli and S. aureus, expressing biofilm embedded cells developed on PE_ZnO 1%, PE_ZnO 3%, PE_ZnO 5%, and control (PE) composite films after 24 h incubation. Different small letters indicate statistically significant differences between films (p < 0.05).
Figure 13. Graphical representation of log10 CFU/mL values obtained for the tested E.coli and S. aureus, expressing biofilm embedded cells developed on PE_ZnO 1%, PE_ZnO 3%, PE_ZnO 5%, and control (PE) composite films after 24 h incubation. Different small letters indicate statistically significant differences between films (p < 0.05).
Ijms 25 06073 g013
Ijms 25 06073 g014
Figure 14. Antibiofilm activity of ZnO NPs at the surface of the polyethylene-ZnO composite films.
Figure 14. Antibiofilm activity of ZnO NPs at the surface of the polyethylene-ZnO composite films.
Ijms 25 06073 g014
Ijms 25 06073 g015
Figure 15. The visual appearance of plum tomatoes stored for 14 days in the polyethylene based packaging films.
Figure 15. The visual appearance of plum tomatoes stored for 14 days in the polyethylene based packaging films.
Ijms 25 06073 g015
Ijms 25 06073 g016
Figure 16. The schematic obtaining polyethylene-ZnO films.
Figure 16. The schematic obtaining polyethylene-ZnO films.
Ijms 25 06073 g016
Table 1. A600 values, thickness (mm), and opacity for polyethylene and composite films.
Table 1. A600 values, thickness (mm), and opacity for polyethylene and composite films.
SamplePEPE-g-MAPE_ZnO 1%PE_ZnO 3%PE_ZnO 5%
Absorbance (A600 nm)0.1210.1710.2240.2780.323
Thickness (mm)0.31 ± 0.010.36 ± 0.060.29 ± 0.010.30 ± 0.020.27 ± 0.02
Opacity0.390.470.770.921.19
Table 2. The main FTIR peaks for polyethylene/ZnO samples.
Table 2. The main FTIR peaks for polyethylene/ZnO samples.
Group Frequency (cm−1)Functional Group/Assignment
2914methylene asymmetric stretch (from LDPE)
2848methylene symmetric stretch (from LDPE)
1472crystalline bending methylene (CH2)
1463amorphous bending methylene (CH2)
729–730crystalline rock methylene (CH2)
717–718amorphous rock methylene (CH2)
484–488Zn-O bond
Table 3. Principal data from thermal analysis of polyethylene/ZnO composite films.
Table 3. Principal data from thermal analysis of polyethylene/ZnO composite films.
SampleT5%
(°C)		T10%
(°C)		T15%
(°C)		Mass Loss (%)
RT-300 °C		Tonset (°C)
(melting)		Melting Peak (°C)Mass loss (%)
300–400 °C		ΔHmelting (J/g)Crystallinity Degree (%)
PE-g-MA 334.0366.5380.32.06%108.6117.024.8788.0830.06
PE_ZnO 1% 407.5414.6419.01.19%106.1115.52.6987.9330.01
PE_ZnO 3% 407.9415.7419.91.00%106.8117.42.0180.6127.51
PE_ZnO 5% 413.6420.7425.31.24%106.8114.32.6881.7327.89
Table 4. Mechanical and barrier properties for polyethylene/ZnO composite films.
Table 4. Mechanical and barrier properties for polyethylene/ZnO composite films.
SamplePE-g-MAPE_ZnO 1%PE_ZnO 3%PE_ZnO 5%
Thickness (mm)0.36 ± 0.060.29 ± 0.010.30 ± 0.020.27 ± 0.02
Elongation at break (%)32.5 ± 2.938.0 ± 1.646.1 ± 3.214.6 ± 1.5
Tensile strength (MPa)15.2 ± 0.3317.1 ± 0.3318.9 ± 0.1615.5 ± 0.16
O2 permeability (cm3/m2·bar·day)65.00 ± 0.0263.02 ± 0.0149.56 ± 0.0236.78 ± 0.02
H2O vapor permeability (g/m2·day)0.280 ± 0.0070.125 ± 0.0050.091 ± 0.0020.088 ± 0.002
Table 5. Diameter of the growth inhibition zone (mm) for polyethylene/ZnO composite films.
Table 5. Diameter of the growth inhibition zone (mm) for polyethylene/ZnO composite films.
Sample/
Strain		PE_ZnO 1%PE_ZnO 3%PE_ZnO 5%
S. aureus9 ± 1.010 ± 1.011 ± 1.0
E. coli10 ± 1.010 ± 1.012 ± 1.0
Table 6. Weight loss for tomatoes coated with composite films during storage.
Table 6. Weight loss for tomatoes coated with composite films during storage.
SampleWeight Loss (%)
1 Day3 Days10 Days14 Days
PE-g-MA0.31 ± 0.050.96 ± 0.123.71 ± 0.166.10 ± 0.25
PE_ZnO 1%0.11 ± 0.030.23 ± 0.070.91 ± 0.111.74 ± 0.16
PE_ZnO 3%0.07 ± 0.020.16 ± 0.030.70 ± 0.111.46 ± 0.11
PE_ZnO 5%0.03 ± 0.010.11 ± 0.030.31 ± 0.070.82 ± 0.06
Similar reports on strawberries [34], lettuce [48], meat [26], or seafood [13] were found in the literature.
Table 7. The polyethylene/ZnO film composition and labels.
Table 7. The polyethylene/ZnO film composition and labels.
Sample CodeLDPE (g)LDPE-g-MAZnO NPs (g)Glycerol (g)
PE248002
PE-g-MA2381002
PE_ZnO 1%235.5102.52
PE_ZnO 3%230.5107.52
PE_ZnO 5%225.51012.52
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Motelica, L.; Ficai, D.; Oprea, O.-C.; Trusca, R.-D.; Ficai, A.; Stelescu, M.D.; Sonmez, M.; Nituica, M.; Mustatea, G.; Holban, A.M. Antimicrobial Packaging for Plum Tomatoes Based on ZnO Modified Low-Density Polyethylene. Int. J. Mol. Sci. 2024, 25, 6073. https://doi.org/10.3390/ijms25116073

AMA Style

Motelica L, Ficai D, Oprea O-C, Trusca R-D, Ficai A, Stelescu MD, Sonmez M, Nituica M, Mustatea G, Holban AM. Antimicrobial Packaging for Plum Tomatoes Based on ZnO Modified Low-Density Polyethylene. International Journal of Molecular Sciences. 2024; 25(11):6073. https://doi.org/10.3390/ijms25116073

Chicago/Turabian Style

Motelica, Ludmila, Denisa Ficai, Ovidiu-Cristian Oprea, Roxana-Doina Trusca, Anton Ficai, Maria Daniela Stelescu, Maria Sonmez, Mihaela Nituica, Gabriel Mustatea, and Alina Maria Holban. 2024. "Antimicrobial Packaging for Plum Tomatoes Based on ZnO Modified Low-Density Polyethylene" International Journal of Molecular Sciences 25, no. 11: 6073. https://doi.org/10.3390/ijms25116073

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.