A Stable and Indurative Superhydrophobic Film with Excellent Anti-Bioadhesive Performance for 6061 Al Protection
Abstract
:1. Introduction
2. Materials and Experiments
2.1. Materials
2.2. Fabrication of the Anti-Bioadhesive Coating
2.3. Chemical and Morphological Characterization
2.4. Wettability and Robustness Testing
2.5. Anti-Bioadhesive Testing
2.6. Adhesion Test
3. Results and Discussion
3.1. Design Strategy to Obtain the Robust Superhydrophobic Coating
3.2. Analysis of the Morphologies and Components
3.3. Superhydrophilicity, Anti-Bioadhesive Performance, and Robustness
4. Conclusions
Supplementary Materials
Author Contributions
Funding
Conflicts of Interest
References
- Kok, B.; Malcorps, W.; Tlusty, M.F.; Eltholth, M.M.; Auchterlonie, N.A.; Little, D.C.; Harmsen, R.; Newton, R.W.; Davies, S.J. Fish as feed: Using economic allocation to quantify the Fish in-Fish-Out ratio of major fed aquaculture species. Aquaculture 2020, 528, 735474. [Google Scholar] [CrossRef]
- Zhao, W.; Ye, Q.; Hu, H.; Wang, X.; Zhou, F. Grafting zwitterionic polymer brushes via electrochemical surface-initiated atomic-transfer radical polymerization for anti-fouling applications. J. Mater. Chem. B 2014, 2, 5352–5357. [Google Scholar] [CrossRef] [PubMed]
- Gu, Y.; Yu, L.; Mou, J.; Wu, D.; Xu, M.; Zhou, P.; Ren, Y. Research Strategies to Develop Environmentally Friendly Marine Antifouling Coatings. Mar. Drugs 2020, 18, 371. [Google Scholar] [CrossRef]
- Atthi, N.; Sripumkhai, W.; Pattamang, P.; Thongsook, O.; Meananeatra, R.; Saengdee, P.; Ranron, N.; Srihapat, A.; Supadech, J.; Klunngien, N.; et al. Superhydrophobic property enhancement on guard ring micro-patterned PDMS with simple flame treatment. Jpn. J. Appl. Phys. 2020, 59, SIIJ05. [Google Scholar] [CrossRef]
- Qing, Y.; Shi, S.; Lv, C.; Zheng, Q. Microskeleton-Nanofiller Composite with Mechanical Super-Robust Superhydrophobicity against Abrasion and Impact. Adv. Funct. Mater. 2020, 1910665. [Google Scholar] [CrossRef]
- Wang, D.; Sun, Q.; Hokkanen, M.J.; Zhang, C.; Lin, F.-Y.; Liu, Q.; Zhu, S.-P.; Zhou, Q.; Chang, Q.; He, B.; et al. Design of robust superhydrophobic surfaces. Nat. Cell Biol. 2020, 582, 55–59. [Google Scholar] [CrossRef]
- Zhao, G.; Li, J.; Huang, Y.; Yang, L.; Ye, Y.; Walsh, F.C.; Chen, J.; Wang, S. Robust Ni/WC superhydrophobic surfaces by electrodeposition. RSC Adv. 2017, 7, 44896–44903. [Google Scholar] [CrossRef] [Green Version]
- Nguyen, H.H.; Wan, S.; Tieu, K.A.; Zhu, H.; Pham, S.T. Rendering hydrophilic glass-ceramic enamel surfaces hydrophobic by acid etching and surface silanization for heat transfer applications. Surf. Coat. Technol. 2019, 370, 82–96. [Google Scholar] [CrossRef]
- Deng, X.; Mammen, L.; Butt, H.-J.; Vollmer, D. Candle Soot as a Template for a Transparent Robust Superamphiphobic Coating. Science 2012, 335, 67–70. [Google Scholar] [CrossRef]
- Fujii, T.; Aoki, Y.; Habazaki, H. Fabrication of Super-Oil-Repellent Dual Pillar Surfaces with Optimized Pillar Intervals. Langmuir 2011, 27, 11752–11756. [Google Scholar] [CrossRef]
- Chiou, N.-R.; Lu, C.; Guan, J.; Lee, L.J.; Epstein, A.J. Growth and alignment of polyaniline nanofibres with superhydrophobic, superhydrophilic and other properties. Nat. Nanotechnol. 2007, 2, 354–357. [Google Scholar] [CrossRef] [PubMed]
- Li, C.; Feng, D.; Wang, X.; Li, Z.; Zhu, Y. A thermochemical approach to enhance hydrophobicity of SiC/SiO 2 powder using γ-methacryloxypropyl trimethoxy silane and octylphenol polyoxyethylene ether (7). Appl. Surf. Sci. 2016, 360, 45–51. [Google Scholar] [CrossRef]
- Jin, H.; Kettunen, M.; Laiho, A.; Pynnonen, H.; Paltakari, J.; Marmur, A.; Ikkala, O.; Ras, R.H.A. Superhydrophobic and Superoleophobic Nanocellulose Aerogel Membranes as Bioinspired Cargo Carriers on Water and Oil. Langmuir 2011, 27, 1930–1934. [Google Scholar] [CrossRef] [PubMed]
- Maharana, H.; Basu, A.; Mondal, K. Effect of CTAB on the architecture and hydrophobicity of electrodeposited Cu–ZrO2 nano-cone arrays. Surf. Coat. Technol. 2019, 375, 323–333. [Google Scholar] [CrossRef]
- Chen, K.; Zhou, S.; Yang, S.; Wu, L. Fabrication of All-Water-Based Self-Repairing Superhydrophobic Coatings Based on UV-Responsive Microcapsules. Adv. Funct. Mater. 2014, 25, 1035–1041. [Google Scholar] [CrossRef]
- Caicedo, J.C.; Franco, F.; Aperador, W. Variation of adhesive stress in anodized AZ31 magnesium alloy immersed within cement concrete blocks with different solidification times. Mater. Chem. Phys. 2019, 232, 414–421. [Google Scholar] [CrossRef]
- Torun, I.; Celik, N.; Ruzi, M.; Onses, M.S. Transferring the structure of paper for mechanically durable superhydrophobic surfaces. Surf. Coat. Technol. 2020, 23, 673–678. [Google Scholar] [CrossRef]
- Huang, W.; Tang, X.; Qiu, Z.; Zhu, W.; Wang, Y.; Zhu, Y.-L.; Xiao, Z.; Wang, H.; Liang, D.; Li, J.; et al. Cellulose-based Superhydrophobic Surface Decorated with Functional Groups Showing Distinct Wetting Abilities to Manipulate Water Harvesting. ACS Appl. Mater. Interfaces 2020, 12, 40968–40978. [Google Scholar] [CrossRef]
- Liu, C.; Zhang, L.; Zhang, X.; Jia, Y.; Di, Y.; Gan, Z.X. Bioinspired Free-Standing One-Dimensional Photonic Crystals with Janus Wettability for Water Quality Monitoring. ACS Appl. Mater. Interfaces 2020, 12, 40979–40984. [Google Scholar] [CrossRef]
- Zhou, P.; Yu, H.; Zhong, Y.; Zou, W.; Wang, Z.; Liu, L. Fabrication of Waterproof Artificial Compound Eyes with Variable Field of View Based on the Bioinspiration from Natural Hierarchical Micro–Nanostructures. Nano-Micro Lett. 2020, 12, 1–16. [Google Scholar] [CrossRef]
- Jin, H.; Tian, X.; Ikkala, O.; Ras, R.H.A. Preservation of Superhydrophobic and Superoleophobic Properties upon Wear Damage. ACS Appl. Mater. Interfaces 2013, 5, 485–488. [Google Scholar] [CrossRef] [PubMed]
- Peng, C.; Chen, Z.; Tiwari, M.K. All-organic superhydrophobic coatings with mechanochemical robustness and liquid impalement resistance. Nat. Mater. 2018, 17, 355–360. [Google Scholar] [CrossRef] [PubMed]
- Du, X.; Gao, B.; Li, Y.; Song, Z. Super-robust and anti-corrosive NiCrN hydrophobic coating fabricated by multi-arc ion plating. Appl. Surf. Sci. 2020, 511, 145653. [Google Scholar] [CrossRef]
- Lee, W.; Park, S.-J. Porous Anodic Aluminum Oxide: Anodization and Templated Synthesis of Functional Nanostructures. Chem. Rev. 2014, 114, 7487–7556. [Google Scholar] [CrossRef] [PubMed]
- Jani, A.M.M.; Kempson, I.M.; Losic, D.; Voelcker, N.H. Dressing in Layers: Layering Surface Functionalities in Nanoporous Aluminum Oxide Membranes. Angew. Chem. Int. Ed. 2010, 49, 7933–7937. [Google Scholar] [CrossRef] [PubMed]
- Zhang, L.; Wu, Y.; Zhang, L.; Wang, Y.; Li, M. Synthesis and characterization of mesoporous alumina with high specific area via coprecipitation method. Vacuum 2016, 133, 1–6. [Google Scholar] [CrossRef]
- Frantz, C.; Lauria, A.; Manzano, C.V.; Guerra-Nuñez, C.; Niederberger, M.; Storrer, C.; Michler, J.; Philippe, L. Nonaqueous Sol–Gel Synthesis of Anatase Nanoparticles and Their Electrophoretic Deposition in Porous Alumina. Langmuir 2017, 33, 12404–12418. [Google Scholar] [CrossRef]
- Suzuki, S.; Morimoto, A.; Kuwabata, S.; Torimoto, T. Shape-controlled synthesis of Cu2O nanoparticles with single-digit nanoscale void space via ionic liquid/metal sputtering and their photoelectrochemical properties. Jpn. J. Appl. Phys. 2020, 60. [Google Scholar] [CrossRef]
- Nakonieczny, D.; Walke, W.; Majewska, J.; Paszenda, Z. Characterization of magnesia-doped yttria-stabilized zirconia powders for dental technology applications. Acta Bioeng. Biomech. 2014, 16, 99–106. [Google Scholar]
- Nakonieczny, D.; Paszenda, Z.; Drewniak, S.; Radko, T.; Lis, M. sZrO2-CeO2 ceramic powders obtained from a sol-gel process using acetylacetone as a chelating agent for potential application in prosthetic dentistry. Acta Bioeng. Biomech. 2016, 18, 53–60. [Google Scholar]
- Qi, L.; Xu, M.; Tian, Y.; Zhao, J. Preparation of anluminum-doped yttria-stabilized zirconia nanopowders by microwave-assisted peroxyl-complex coprecipitation. Trans. Nonferrous Metals Soc. China 2006, 16, s426–s430. [Google Scholar] [CrossRef]
- Songa, B.; Liua, Q.; Maa, H.; Tanga, Z.; Liua, C.; Zoua, J.; Tanb, M.; Yuana, J. Tumor-targetable magnetoluminescent silica nanoparticles for bimodal time-gated luminescence/magnetic resonance imaging of cancer cells in vitro and in vivo. Talanta 2020, 220, 121378. [Google Scholar] [CrossRef] [PubMed]
- Li, P.; Gao, J.; Gong, M.; Shen, D.; Tong, W. Effects of manganese on diffusion and wear behavior of ZTA particles reinforced iron matrix composites in vacuum. Vac. 2020, 177, 109408. [Google Scholar] [CrossRef]
- Taha, M.A.; Youness, R.A.; Ibrahim, M.A. Evolution of the Physical, Mechanical and Electrical Properties of SiC-Reinforced Al 6061 Composites Prepared by Stir Cast Method. Biointerface Res. Appl. Chem. 2021, 11, 8946–8956. [Google Scholar]
- AlThagafi, I.I.; Ahmed, S.A.; El-Said, W.A. Colorimetric Aflatoxins immunoassay by using silica nanoparticles decorated with gold nanoparticles. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 2021, 246, 118999. [Google Scholar] [CrossRef]
- Safari, J.; Javadian, L. Ultrasound assisted the green synthesis of 2-amino-4H-chromene derivatives catalyzed by Fe3O4-functionalized nanoparticles with chitosan as a novel and reusable magnetic catalyst. Ultrason. Sonochemistry 2015, 22, 341–348. [Google Scholar] [CrossRef]
- Kakunuri, M.; Vennamalla, S.; Sharma, C.S. Synthesis of carbon xerogel nanoparticles by inverse emulsion polymerization of resorcinol–formaldehyde and their use as anode materials for lithium-ion battery. RSC Adv. 2015, 5, 4747–4753. [Google Scholar] [CrossRef]
- Wu, G.; Zhao, C.; Zhou, X.; Chen, J.; Li, Y. DFT study on the interaction of HCHO molecule with S-doped TiO2 (001) surface without and with water and oxygen molecules. J. Mater. 2019, 5, 558–566. [Google Scholar] [CrossRef]
- Nbelayim, P.; Sakamoto, H.; Kawamura, G.; Muto, H.; Matsuda, A. Preparation of thermally and chemically robust superhydrophobic coating from liquid phase deposition and low voltage reversible electrowetting. Thin Solid Films 2017, 636, 273–282. [Google Scholar] [CrossRef]
- Teker, D.; Muhaffel, F.; Menekse, M.; Karaguler, N.G.; Baydoğan, M.; Cimenoglu, H. Characteristics of multi-layer coating formed on commercially pure titanium for biomedical applications. Mater. Sci. Eng. C 2015, 48, 579–585. [Google Scholar] [CrossRef]
- Zhang, X.; Guo, Y.; Zhang, Z.; Zhang, P. Self-cleaning superhydrophobic surface based on titanium dioxide nanowires combined with polydimethylsiloxane. Appl. Surf. Sci. 2013, 284, 319–323. [Google Scholar] [CrossRef]
- Rajender, G.; Giri, P. Strain induced phase formation, microstructural evolution and bandgap narrowing in strained TiO2 nanocrystals grown by ball milling. J. Alloy. Compd. 2016, 676, 591–600. [Google Scholar] [CrossRef]
- Zang, J.; Yu, S.; Zhu, G.; Zhou, X. Fabrication of superhydrophobic surface on aluminum alloy 6061 by a facile and effective anodic oxidation method. Surf. Coat. Technol. 2019, 380, 125078. [Google Scholar] [CrossRef]
- Lee, I.; Wool, R.P. Controlling amine peceptor group density on aluminum oxide surface by mixed silane self assembly. Thin Solid Films 2000, 379, 94–100. [Google Scholar] [CrossRef]
- Fu, X.; He, X. Fabrication of super-hydrophobic surfaces on aluminum alloy substrates. Appl. Surf. Sci. 2008, 255, 1776–1781. [Google Scholar] [CrossRef]
- Okazaki, Y.; Buffeteau, T.; Siurdyban, E.; Talaga, D.; Ryu, N.; Yagi, R.; Pouget, E.; Takafuji, M.; Ihara, H.; Oda, R. Direct Observation of Siloxane Chirality on Twisted and Helical Nanometric Amorphous Silica. Nano Lett. 2016, 16, 6411–6415. [Google Scholar] [CrossRef]
- Lee, W.; Ji, R.; Gösele, U.; Nielsch, K. Fast fabrication of long-range ordered porous alumina membranes by hard anodization. Nat. Mater. 2006, 5, 741–747. [Google Scholar] [CrossRef]
Electrolyte | Concentration (wt%) | Constant Voltage (V) | Temperature (°C) | Time (min) |
---|---|---|---|---|
H3PO4 | 15 | 40/50/60/70 | 20 | 45 |
H2SO4 | 11 | 20/25/30/35 | 0 | 45 |
OA | 5 | 40/45/50/55 | 0 | 45 |
Sample No. | Average Pore Size (nm) | Porosity (%) | Hardness (HV) |
---|---|---|---|
#a1 | 46.3 | 61.5 | 131.7 ± 2.2 |
#a2 | 69.1 | 54.4 | 109.4 ± 3.0 |
#a3 | 96.0 | 41.9 | 100.2 ± 2.1 |
#a4 | 120.4 | 47.2 | 94.3 ± 3.5 |
#b1 | 33.1 | 71.4 | 271.5 ± .9 |
#b2 | 55.0 | 66.3 | 260.4 ± 5.8 |
#b3 | 81.1 | 61.6 | 234.1 ± 5.1 |
#b4 | 86.7 | 51.7 | 205.9 ± 4.6 |
#c1 | 37.3 | 62.1 | 427.2 ± 4.7 |
#c2 | 56.7 | 59.4 | 409.8 ± 3.1 |
#c3 | 74.2 | 57.1 | 394.5 ± 4.0 |
#c4 | 100.9 | 45.9 | 363.9 ± 3.6 |
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations. |
© 2020 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
Share and Cite
Liu, J.; Zhang, X.; Wang, R.; Long, F.; Liu, L. A Stable and Indurative Superhydrophobic Film with Excellent Anti-Bioadhesive Performance for 6061 Al Protection. Materials 2020, 13, 5564. https://doi.org/10.3390/ma13235564
Liu J, Zhang X, Wang R, Long F, Liu L. A Stable and Indurative Superhydrophobic Film with Excellent Anti-Bioadhesive Performance for 6061 Al Protection. Materials. 2020; 13(23):5564. https://doi.org/10.3390/ma13235564
Chicago/Turabian StyleLiu, Jie, Xinwen Zhang, Ruoyun Wang, Fei Long, and Lei Liu. 2020. "A Stable and Indurative Superhydrophobic Film with Excellent Anti-Bioadhesive Performance for 6061 Al Protection" Materials 13, no. 23: 5564. https://doi.org/10.3390/ma13235564