Next Article in Journal
Influence of Ultraviolet Light and Alternating Wet–Dry Environments on the Corrosion Behavior of Weathering Steels
Previous Article in Journal
Performance Evaluation of Foamed Concrete with Lightweight Aggregate: Strength, Shrinkage, and Thermal Conductivity
Previous Article in Special Issue
Effect of Hot-Pressing Process on Mechanical Properties of UHMWPE Fiber Non-Woven Fabrics
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 17
Issue 15
10.3390/ma17153868
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Incorporation of Nano-Zinc Oxide as a Strategy to Improve the Barrier Properties of Biopolymer–Suberinic Acid Residues Films: A Preliminary Study

by
Aleksandra Jeżo
1,
Faksawat Poohphajai
2,3,4,
Rene Herrera Diaz
2,3 and
Grzegorz Kowaluk
1,*
1
Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences—SGGW, Nowoursynowska St. 159, 02-776 Warsaw, Poland
2
InnoRenew CoE, Livade 6a, 6310 Izola, Slovenia
3
Faculty of Mathematics, Natural Sciences and Information Technologies, University of Primorska, 6000 Koper, Slovenia
4
Department of Bioproducts and Biosystems, Aalto University School of Chemical Engineering, 00076 Aalto, Finland
*
Author to whom correspondence should be addressed.
Materials 2024, 17(15), 3868; https://doi.org/10.3390/ma17153868
Submission received: 24 June 2024 / Revised: 19 July 2024 / Accepted: 30 July 2024 / Published: 5 August 2024
(This article belongs to the Special Issue Preparation and Characterization of Functional Composite Materials)
Browse Figures
Versions Notes

Abstract

:
Finishing coatings in the wood-based composites industry not only influence the final appearance of the product but also serve to protect against fungi and molds and reduce the release of harmful substances, particularly formaldehyde and volatile organic compounds (VOCs). Carbon-rich materials, such as those derived from birch bark extraction, specifically suberin acids, can fulfill this role. Previous research has demonstrated that adding suberin acid residues (SAR) at 20% and 50% by weight significantly enhances the gas barrier properties of surface-finishing materials based on poly(lactide) (PLA) and polycaprolactone (PCL), particularly in terms of total VOC (TVOC) and formaldehyde emissions. This study aims to explore whether these properties can be further improved through the incorporation of nano-zinc oxide (nano-ZnO). Previous research has shown that these nanoparticles possess strong resistance to biological factors and can positively affect the characteristics of nanofilms applied as surface protection. The study employed PLA and PCL finishing layers blended with SAR powder at 10% w/w and included 2% and 4% nano-zinc oxide nanoparticles. The resulting blends were milled to create a powder, which was subsequently pressed into 1 mm-thick films. These films were then applied to raw particleboard surfaces. TVOC and formaldehyde emission tests were conducted. Additionally, the fungal resistance of the coated surfaces was assessed. The results showed that PLA/SAR and PCL/SAR composites with the addition of nano-zinc oxide nanoparticles exhibited significantly improved barrier properties, offering a promising avenue for developing biodegradable, formaldehyde-free coatings with enhanced features in the furniture industry. Furthermore, by utilizing SAR as a post-extraction residue, this project aligns perfectly with the concept of upcycling.

1. Introduction

Surface-finishing technologies in the furniture industry aim to ensure both aesthetic appeal and functional safety, including resistance to hydrolysis [1], biological factors [2], fire retardance [3], and minimizing environmental emissions, depending on the furniture’s intended use. Breakthroughs in green nanotechnology are revolutionizing processes and products, benefiting the environment, reducing pollution, and conserving resources [4,5].
Poly(lactic acid) (PLA) polymers, derived from renewable resources like corn starch or sugarcane [6], offer an eco-friendly alternative for wood-finishing coatings [7], combining sustainability with a durable finish [8,9]. However, due to some drawbacks of PLA, further modifications are implemented, including fiber reinforcement [7,8,9,10,11,12,13,14,15,16], blending [17], or plasticization [18]. The findings by Oksman et al. indicate that PLA serves as an effective matrix material for natural fiber composites, demonstrating promising improvements in the mechanical properties of PLA and flax fiber composites [19].
Aside from PLA, another promising biodegradable polymer is polycaprolactone (PCL), which shows good compatibility with other polymers [20,21,22,23,24,25]. It has also been proven beneficial to incorporate lignocellulosic particles/fibers into PCL to enhance its properties [16,21,26,27] or other compounds like kaolin [28] or bioactive glass [29].
Incorporating nanoparticles into polymers can improve barrier properties due to two main factors: 1. reduction in available diffusion area, achieved by replacing permeable polymer with impermeable nanoparticles; 2. increased path length for the permeant to traverse the film, as it follows a convoluted route around the impermeable nanoparticles [30]. The dispersion of nanoparticles in polymer matrices affects the barrier properties created by making gas fighting more difficult, as the added nanoparticles create a “more difficult”, tortuous gas prevention path [31]. Moreover, the added nanoparticles cause changes in the polymer matrix itself in the interfacial areas. If polymer–nanoparticle interactions are favorable, polymer strands in close proximity to each nanoparticle can be partially immobilized. The result is a reduced velocity of gas particles [32,33]. The incorporation of nanoparticles into polymers, also PLA and PCL, is an area of research that holds promise for enhancing the properties and functionality of these biodegradable materials. Incorporating nanoparticles like SiO2, Al2O3, TiO2, and Fe2O3 into Poli-L-lactide (PLLA) significantly improves the barrier properties of the resulting nanocomposites, reducing water vapor permeability by up to 18% and wet oxygen permeability by up to 9% [34]. By applying CaCO3 nanoparticles up to 5 wt% the gas permeability, the results of N2, O2, and CO2 revealed an improvement in the final barrier properties [35].
Inorganic metal oxide nanoparticles (e.g., TiO2, ZnO, SiO2, and Al2O3) can also absorb UV radiation; however, due to naturally wide bond gaps, their UV absorption is not complete. Nano-ZnO deposited on wood by Kong et al. [36], forming dense and uniform arrays of nanorods, provided UV protection, improved photostability, enhanced flame retardancy, and water repellency when modified with stearic acid. Regarding the organic compounds, cellulose nanocrystals (CNCs) and lignin nanoparticles (LNPs) enabled the creation of PVC-based composites with improved barrier properties, limiting gas migration and enhancing the UV-shielding [37].
One of the other potential improvements that the implementation of nanoparticles can bring is making the composite bioprotective. Nanomaterials have recently become important in many industrial paths due to the larger percentage of atoms at their surface, which lead to high surface reactivity. ZnO nanoparticles have excellent antibacterial properties since they are of a reduced size. Direct contact of nano-ZnO leads to the destruction of bacterial cell integrity [38]. Once the nanoparticles are inside the bacterial cell, they generate ROS (reactive oxygen species), and release of antimicrobial ions, mainly Zn2+ [39]. ZnO possesses significant photocatalytic efficiency and is more biocompatible than TiO2 [40]. Nano-ZnO in aqueous solution under UV radiation presents a phototoxic effect that leads to producing ROS-like hydrogen peroxide (H2O2) and superoxide ions (O2−). The generated active species penetrate the cells, inhibiting or killing microorganisms. Figure 1 presents a schematic of the mechanism of antibacterial the working of nano-ZnO. It has also been proven that the addition of metal-based particles, such as copper [41,42] and silver [15,43,44], into polymers is a versatile route to take advantage of their strong antimicrobial properties, producing novel biocide materials [45]. Moreover, as Wu et al. found out in the example of organoclays, the introduction of nanofillers leads to a significant enhancement in phase morphology, primarily due to their strategic localization, which effectively prevents the merging of discrete domains and encourages the breakup of droplets [25].
Carbon-rich natural substances, like those found in birch bark extraction products, such as suberic acids (SAs) and their residues (SARs), have significant potential for reducing the emissions of harmful substances into the environment. The findings of Jeżo and Kowaluk [16] indicate a positive influence of a 20% and 50% addition of SAR into PLA and PCL blends regarding TVOC and formaldehyde emission from plywood. This can be attributed to the high lignin content in SAR particles. Furthermore, the SAR addition enhances the relative hardness and scratch resistance of PLA- and PCL-based surface-finishing materials. This paper investigates whether adding nano-zinc oxide (nano-ZnO) can improve the barrier properties and biological resistance of nanocomposites created by blending PLA/PCL, SAR, and nanoparticles. While it has been shown that the addition of nano-ZnO to PLA/PCL has potential in medical applications [47,48], it remains to be found if such potential also lies in the wood composites industry. Both the effects of SAR addition and nanoparticle incorporation will be investigated.

2. Materials and Methods

2.1. Materials

The surface-finishing layers were fabricated using two distinct matrices: laboratory-purpose PLA (Sigma-Aldrich, Saint Louis, MO, USA, product no. 38534) and PCL (Sigma-Aldrich, product no. 704105) in drops with a diameter of 3 mm. The suberinic acid residues (SAR) used in the research, which were utilized to prepare the blends, have been described in detail by Makars et al. [49]. The following are the basic chemical properties of SAR: cellulose 9.0 wt%, aromatic suberin, lignin 21.4 wt%, ω-hydroxy acids 17.5%, and α, ω-diacids 11.9%. The nanoparticles used in the study were nano-zinc oxide (nano-ZnO), hereafter called “nano”, obtained from ASTON Chemicals, Warsaw, Poland, with a diameter of 265 nm. Methylene chloride (CH2Cl2) (Sigma-Aldrich, product no. 34856), toluene (C6H5CH3) (Sigma-Aldrich, product no. 320552), and Potato Dextrose Agar (Sigma Aldrich, product no. 70139).

2.2. Blends Processing Methods

(1)
The PLA finishing layer was made by mixing methylene chloride (CH2Cl2) solution for PLA, 21% dry matter content, with SAR powder, 10% w/w, respectively, hereafter called “PLA/SAR”; and with nano-ZnO particles, 2% and 4%, w/w, respectively, hereafter called “PLA/SAR nano 2%” and “PLA/SAR nano 4%”. The samples with the addition of nano-ZnO but without SAR are hereafter called “PLA nano 2%” and “PLA nano 4%”. A pure PLA surface-finishing layer has also been tested (hereafter called “PLA”) as a reference. All the prepared blends were spread on Polytetrafluoroethylene (PTFE) sheets under a fume hood to evaporate the solvent and then milled to attain a powder size smaller than 0.1 mm. Such a powder was formed in a hot press (as mentioned above), as described by Gumowska et al. [50]. The prepared film was pressed in a hot press (pressing time, 75 s; temperature, 185 °C; and pressure, 0.8 MPa) onto the unfinished particleboard surface described above.
(2)
The PCL finishing layer was obtained from toluene (C6H5CH3) solution for PCL, 25% dry matter content. The remaining steps of the surface-finishing preparation are the same as those described above for PLA. Using this method, the subsequent samples were attained: PCL (hereafter called “PCL”; no SAR/nano-ZnO addition, reference sample) “PCL/SAR”, “PCL/SAR nano 2%”, “PCL/SAR nano 4%”, “PCL nano 2%”, “PCL nano 4%”.
According to the research plan, the surface-finishing layers created on the particleboard base were exposed to ambient conditions (20 °C; 65% R.H.) until a constant weight was achieved over a span of seven days before tests. All the variants and their composition were presented in Table 1.
From each variant, one sample was grinded and pressed on the surface twice, to investigate the effect of repeated processing on the relative hardness.

2.3. Relative Hardness

Relative hardness was measured on a pendulum apparatus type AWS—9 (POL-ZAF S.C., Wrocław, Poland) according to the procedure described in the ISO 1522 standard [51]. As many as 2 repetitions per tested sample type were performed.

2.4. Cold Liquids Resistance

Cold liquid resistance was measured according to the procedure described in the EN 12720+A1 standard [52]. As many as 2 repetitions per tested sample type were performed. The following cold liquids were employed: acetone, citric acid, ethanol, and distilled water. The exposition time equaled 24 h.

2.5. Total VOC and Formaldehyde Emission

The total VOC and formaldehyde emission tests were completed in an emission test chamber at a temperature of 23 °C +/− 0.5 °C and relative air humidity of 44% +/− 1%. Other parameters of sample conditioning were performed following the EN 717-1 standard [53]. The TVOC and formaldehyde emission tests were carried out after conditioning the samples for 24 h by analyzing the chamber air over the three repetitions after 20 min each using a JD-3002 Air Quality Tester (Dongguan Jinlide Electronic Technology Co., Ltd., Dongguan City, Guangdong Province, China). We adhered to the standards regarding air-conditioning conditions for samples during the emission test.

2.6. Antifungal Test

In the antifungal study, the disk diffusion method was employed to assess the growth inhibition of the materials on specific mold fungi. A 90 mm Petri dish containing a Potato Dextrose Agar was centrally inoculated with a 100 µL spore suspension of two common mold species, namely Aspergillus niger and Cladosporium cladosporioides. The spores were evenly spread using a sterile plastic spreader. Subsequently, one test disk of each type of test material was placed in the center of the plate, and three replicas of each material were employed for each mold species. The plates were incubated in a growth chamber in the dark under a control temperature of 25 °C. After 10 days of incubation, the growth of fungi was visually evaluated using a Keyence VHX-6000 digital microscope (Keyence, Osaka, Japan). The growth of mold was assessed based on the percentage of mold coverage on the surface. To ensure uniform evaluation of the test, the following six-grade assessment scheme was applied in this experiment:
  • Grade 0 = no infestation of the surface.
  • Grade 1 = 1–20% infestation of the surface.
  • Grade 2 = 21–40% infestation of the surface.
  • Grade 3 = 1–60% infestation of the surface.
  • Grade 4 = 61–80% infestation of the surface.
  • Grade 5 = 81–100% infestation of the surface.

2.7. The Effect of Repeated Processing of Polymer Blends on Their Hardness

The samples were pressed onto the board surface, as described in Section 2.1. and subsequently recovered from the surfaces by scratching off. Then, the recovered blends were ground and pressed onto the surfaces again. One sample of each type was processed this way, and then the relative hardness was examined as described in Section 2.2.

2.8. Statistical Analysis

Analysis of variance (ANOVA) and t-test calculations were used to verify significant differences (α = 0.05) between factors and levels where appropriate, using the RStudio software 2024.04.2 Build 764 © 2009–2024 Posit Software, PBC (R Foundation, Vienna, Austria).

3. Results and Discussion

3.1. Cold Liquids Resistance

The cold liquids resistance evaluation results of the tested surface-finishing layers are presented in Table 2. When it comes to pure PLA, only in the case of citric acid and distilled water was slight cloudiness found. There was no significant influence of the addition of SAR to PLA regarding the resistance to cold liquids. The pure PCL layer was more resistant when referred to PLA. No changes in the surface were found. The addition of SAR to PCL did not significantly lead to the lowering of the resistance of the tested blends. Only in the case of PCL/SAR nano 4% sample was there a slight change observed when affected by ethanol. To compare the results with the commercial coatings, let us regard waterborne coatings (acrylate-based and polyurethane-based). Pavlic et al. [54] found that the best resistance to cold liquids occurred in the case of exposure to water and citric acid, while the fastest changes were observed after acetone application. The coatings that were acrylic-based showed better resistance compared to the polyurethane-based ones. It was also stated by Lis et al. [55] that most of the agents had caused no changes in waterborne UV acrylic coatings even after 24 h. Only the ethyl alcohol showed negative impact on evaluated surfaces, causing slight changes.

3.2. Total VOC and Formaldehyde Emission

Table 3 shows the results of testing the emission of free formaldehyde (HCHO) and (VOCs) in samples covered with coatings on both sides. A particleboard not covered with any coating was used as a control sample (REF). There was a statistically significant reduction in TVOC and HCHO emission between all of the variants tested when the investigated surface-finishing layers were applied. The addition of SAR reduces the revealed emissions. However, the lowest emissions values were obtained for the samples with nano-ZnO incorporated, with the PCL nano 2% and 4% performing the strongest gas barrier properties. The polymer matrix was the only significant factor in this test. The mentioned reduction in TVOC and formaldehyde emission from the particleboard covered with different surface-finishing layers can be an effect of the scavenger nature of lignin, which is the main component (over 21 wt%) of SAR. The SAR-containing surface-finishing layers act as a bi-functional barrier layer, which can avoid the gas transfer from the core of the composite to the environment, as well as can fix the formaldehyde and other emitted compounds in the finishing layer structure [56]. According to [57,58], the blends of PLA, as well as PCL, can be recognized as extremely promising for the development of bio-based and biodegradable polymeric materials with low oxygen permeation, that is, for the development of suitable alternatives to conventional and highly pollutant oil-based plastics. It can be concluded that the tested surface-finishing materials, based on biopolymers with SAR incorporation, have promising features regarding the gas barrier layer on wood-based material surfaces. It is moreover notable that nanoparticles exhibit great advantages since they can reduce formaldehyde emissions through indirectly increasing the curing degree of the resins, thus resulting in improved hydrolytic stability, due to the increased chemical bonds of the resin components with free formaldehyde. Furthermore, the reaction of hydroxyl groups occur on the nanomaterial surface with free formaldehyde, and such coatings are able to perform barrier properties or a “shielding effect” [59]. As [60] found, the application of 8% zinc results in a reduction in formaldehyde emission by an average of 44%.

3.3. Relative Hardness

Figure 2 shows the results of testing the relative hardness of the produced coatings. In coatings made on a PLA matrix, the sample made of pure polymer without additives (0.52) showed the highest hardness. For the sample with a 2% addition of nano-ZnO, a decrease in hardness to 0.43 was observed; meanwhile, when the share of nanoparticles was increased, there was a slight increase in hardness (0.45). The PLA-based samples containing SAR showed statistically significantly lower hardness: 0.33, 0.30, and 0.33 for the PLA/SAR variants, PLA/SAR nano 2%, and PLA/SAR nano 4%, respectively. As for the samples produced based on the PCL matrix, the pure polymer showed a hardness of 0.42. The nano-ZnO tax resulted in an increase in hardness to 0.45 and 0.47, respectively. For the PCL/SAR sample, a decrease in hardness to 0.39 was observed, while for the PCL/SAR nano 2% and PCL/SAR nano 4% variants, an increase in hardness to 0.50 and 0.48 was observed, respectively. Statistical analysis showed that in the tested samples, statistically significant differences were related to the addition of SAR, the type of matrix, and the interaction between the matrix and SAR. The addition of nanoparticles did not have a statistically significant impact on the obtained results.
Previous research conducted by Jeżo and Kowaluk [16] on PLA and PCL blends with SAR showed that the addition of 20% and 50% SAR causes an increase in hardness. However, ref. [61] stated in their study that the mechanical properties of a PLA/IFR (intumescent flame retardant (IFR)-graphene oxide (GO)) blend when incorporated with nano-ZnO were diminished seriously; the tensile strength decreased by 67%, the impact strength decreased by 69%, and the elongation at break was off by 70%. The authors explain their findings with a nano-ZnO-catalyzing PLA, which decomposed into small chains with low molecular and then was destroyed easily. Also, [62] stated that the addition of ZnO nanoparticles introduced an accelerated degradation of the PLA/PCL blends. Rheological results showed that with increasing nanoparticles, the elastic modulus and the complex viscosity decreased, which correlated with the degradation and chain scission of polymeric chains induced by nano-ZnO. The mentioned references are applicable since an approximately linear correlation between the hardness and elastic modulus was established [63]. Moreover, the tensile strength and the hardness of a material are highly correlated [64]. The large size of the nanoparticles could also have influenced the negative results. As shown by [65], big size and aggregates/agglomerates weaken the positive attributes of nanoparticles in nanocomposites. Small nanoparticles and a thick interphase present high levels for the B parameter (interfacial parameter which shows the level of interfacial adhesion), tensile strength, interphase volume fraction, and interphase parameter. Ref. [66] confirms that by decreasing the particle size from 300 nm to 10 nm, the SiO2 nanoparticles become drastically harder (∼39×), stiffer (∼15×), and tougher (>3.5×).
Since the SAR showed statistical significance for the obtained results, the decrease in hardness of samples containing PCL and PLA can also be attributed to its addition. Because improved mechanical properties, including hardness, were observed in the literature after adding natural fibers to polymers [16,60], the authors intend to take a closer look at the observed phenomenon and link it with manufacturing parameters and further processing. The worsening of the relative hardness because of the incorporation of the SAR can be due to its alkaline form. It has been confirmed by [67] that alkali treatment can cause a depolymerization of polymers. Also, [68] reported that at a lignin content of 10 wt%, heterogeneous morphology was observed, suggesting phase separation between PLA and alkali lignin. Similar observations were shown in PLA/kraft lignin blends with lignin concentrations higher than 10 wt% [69,70]. This heterogeneity might be an indication of the weak mechanical properties of the investigated system at concentrations higher than 10 wt%.
Comparing the obtained results with different polymer matrixes, it is worth mentioning that by increasing nano-ZnO up to 0.3% in a polystyrene polymer matrix, there is a remarkable increment of approximately 47% in the hardness [71], while the hardness can be decreased by 5.73% when added into natural rubber [72]. Incorporation of ZnO–Ag hybrid nanoparticles into the acrylate epoxy matrix increases its pendulum hardness [73]; meanwhile, compared with neat polyurethane acrylate (PUA), the hardness in films increases from 0.03 to 0.05 GPa when ZnO in a share of 5% is incorporated [74].
Degradation causes changes in the mechanical properties, particularly when the molecular weight importantly decreases. Reinforcements could attenuate the loss in mechanical properties, depending on its structural integrity and the state of interfacial adhesion [75].

3.4. Antifungal Test

In Figure 3, the results of the antifungal tests are illustrated, with a demonstration of average mold grade values. In Figure 4, Figure 5, Figure 6 and Figure 7, the photos of the infected samples are shown. In the case of samples containing PLA and additives, specifically PLA/SAR nano 2%, PLA/SAR nano 4%, and PLA nano 4%, a higher antifungal effect was observed, with no contact between the fungal spores and the material, in contrast to the PLA control. Additionally, PLA/SAR nano 2% and PLA/SAR nano 4% demonstrated an inhibition zone against A. niger, indicating their ability to prevent or impede fungal growth. Similar antifungal effects were observed in PLA samples against C. cladosporioides, with the highest activity in the PLA/SAR nano 2%, PLA/SAR nano 4%, and PLA nano 4% samples. An exception was found in the PLA/SAR samples, which proved to be the most susceptible to A. niger and C. cladosporioides. Conversely, the samples containing PCL and additives generally exhibited better performance, particularly against C. cladosporioides, notably in the PCL/SAR nano 4%, PCL nano 2%, and PCL nano 4% samples. However, even the PCL control showed some inhibitory effect against C. cladosporioides. In the case of A. niger, the PCL samples displayed similar performance in PCL/SAR nano 2%, PCL/SAR nano 4%, and PCL nano 2%, where few spores were observed, unlike the control sample (PCL) and PCL/SAR, where the samples were colonized by A. niger. The statistical analysis revealed the significant impact of nanoparticles, type of matrix, SAR added, as well as the correlation between SAR and nano-ZnO on the mold grade.
As other studies confirm, the silane-modified ZnO-hybrid-embedded Poly(methyl methacrylate) (PMMA) offers resistance against fungal growth when infected with Aspergillus niger and Aspergillus flavus [76]. Nano-ZnO shows antifungal activity against Aspergillus niger with an MIC of 2.5 mg/mL. Thus, nano-ZnO is twice as potent in killing Aspergillus, as compared to its non-nano-counterpart (micro ZnO) [77].

3.5. Relative Hardness after Repeated Processing of the Samples

Figure 8 shows a comparison of the relative hardness of the tested coatings ground and pressed once and twice. A decrease in the value of the tested parameter (Table 4) can be noticed for samples whose coating was reprocessed after ironing. The decrease in hardness recorded for the samples is shown in the table. Greater differences were observed in the case of samples made based on the PLA matrix than the PCL matrix. Due to the re-processing of the PLA-based blends, the polymer degraded, significantly affecting its mechanical properties, like the loss of hardness. Ref. [78] reports similar observations for PLA blends with starch, where the degradation of PLA was confirmed by SEM tests. The authors observed a decrease in the flexural modulus and impact strength values due to repeated processing of the blends. The degradation of PLA due to repeated processing is also confirmed by [79], who investigated the impact of repeated extrusion on the properties of PLA/HDPE and PLA/PC blends. As demonstrated by [80], mechanically recycled PLA has lower mechanical properties compared to virgin PLA, with impact strength and hardness decreasing by 50% and 4%, respectively.
Although the literature lack examples of a decrease in hardness after regrinding for PCL, researchers have considered many other polymers—polyoxymethylene (POM) [81], thermoplastic polyurethane elastomers [82], or polypropylene [83]—which may confirm a similar trend for PCL as demonstrated in this study. However, polymers have been found that increased their hardness after couple processing cycles, such as high-impact polystyrene [84].
The statistical analysis showed statistically significant differences between the values obtained for hardness after the first and second processing cycle, which confirms that repeated grinding and pressing of polymer blends statistically reduces their relative hardness. Moreover, the only factor that had a statistically significant impact on the percentage decrease in hardness after reprocessing was the type of polymer matrix.

4. Conclusions

The following study aimed to investigate some preliminary examinations on the surface-finishing coatings containing suberinic acid residues (SAR) with nano-zinc oxide (nano-ZnO). The tests included resistance to cold liquids, relative hardness, formaldehyde and VOC emissions and antifungal tests. The results revealed no worsening when exposed to cold liquids in the case of samples based on the PCL matrix, with slight changes in some samples based on the PLA polymer. The relative hardness tests showed a decrease in hardness regarding PLA-based samples when incorporated with nanoparticles, and the PCL-based samples presented a decrease in hardness in the case of SAR incorporation. This phenomenon needs to be further investigated; however, the authors suggest that the reason for this worsening might have been the alkali character of the SAR-incorporated sample. It was concluded that the incorporation of SAR and nano-ZnO enabled the minimization of both the emissions of free formaldehyde as well as TVOC. The investigated samples with fillers incorporated exhibited moreover good antimicrobial properties. Moreover, the impact of repeated processing on the relative hardness was regarded, leading to an observation of a decrease in this parameter for both the PLA and PCL. The authors see great potential in the findings obtained, and the topic will be continuously investigated.

Author Contributions

Conceptualization, A.J. and G.K.; methodology, A.J., G.K., R.H.D. and F.P.; validation, A.J., G.K., R.H.D. and F.P.; formal analysis, A.J., G.K., R.H.D. and F.P.; investigation, A.J., G.K., R.H.D. and F.P.; resources, A.J., G.K., R.H.D. and F.P.; data curation, A.J., R.H.D. and F.P.; writing—original draft preparation, A.J., G.K., R.H.D. and F.P.; writing—review and editing, A.J. and G.K.; visualization, A.J., R.H.D. and F.P.; supervision, G.K. and R.H.D.; project administration, G.K.; funding acquisition, A.J. and G.K. All authors have read and agreed to the published version of the manuscript.

Funding

The research presented is a part of Project BarkBuild that is funded under the ERA-NET Cofund ForestValue program through Vinnova (Sweden), Valsts izglītības attīstības aģentūra (Latvia), Ministry of Education, Science and Sport (JIA) (Slovenia), Academy of Finland, The Research Council of Norway, and the National Science Centre, Poland (contract no. 2021/03/Y/NZ9/00038). The ForestValue program received funding from the Horizon 2020 Research and Innovation program of the European Union under grant agreement No. 773324. The mentioned research is conducted with the support of the Student Furniture Scientific Group (Koło Naukowe Meblarstwa), Faculty of Wood Technology, Warsaw University of Life Sciences—SGGW.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author. The data are not publicly available due to sensitive nature of the research. The participants of this study did not give written consent for their data to be shared publicly (commercial reasons, ongoing research etc.).

Acknowledgments

The authors would acknowledge Janis Rizikovs, Latvian State Institute of Wood Chemistry, Riga, Latvia, for kindly providing the bark post-extraction residues. The authors also thank the ASTON Chemicals Company for providing the nanoparticles for this study.

Conflicts of Interest

The authors claim no conflicts of interest.

References

  1. Yang, L.; Wu, Y.; Yang, F.; Wang, W. The Effect of Antibacterial and Waterproof Coating Prepared From Hexadecyltrimethoxysilane and Nano-Titanium Dioxide on Wood Properties. Front. Mater. 2021, 8, 699579. [Google Scholar] [CrossRef]
  2. Tracton, A.A. Chapter 83: Fluorocarbon Resins for Coatings and Inks. In Coatings Technology Handbook, 3rd ed.; CRC Press: Boca Raton, FL, USA, 2005; ISBN 1574446495. [Google Scholar]
  3. Kozlowski, R.; Wesolek, D.; Wladyka-Przybylak, M. Combustibility and toxicity of board materials used for interior fittings and decorations. Polym. Degrad. Stab. 1999, 64, 595–600. [Google Scholar] [CrossRef]
  4. Eric, J.; Bailey, K.I.W. Dynamics of polymer segments, polymer chains, and nanoparticles in polymer nanocomposite melts: A review. Prog. Polym. Sci. 2020, 105, 101242. [Google Scholar] [CrossRef]
  5. Virkutyte, J.; Varma, R.S. Green synthesis of metal nanoparticles: Biodegradable polymers and enzymes in stabilization and surface functionalization. Chem. Sci. 2011, 2, 837–846. [Google Scholar] [CrossRef]
  6. Vaidya, A.N.; Pandey, R.A.; Mudliar, S.; Kumar, M.S.; Chakrabarti, T.; Devotta, S. Production and recovery of lactic acid for polylactide—An overview. Crit. Rev. Environ. Sci. Technol. 2005, 35, 429–467. [Google Scholar] [CrossRef]
  7. Valerga, A.P.; Batista, M.; Fernandez-Vidal, S.R.; Gamez, A.J. Impact of chemical post-processing in fused deposition modelling (FDM) on polylactic acid (PLA) surface quality and structure. Polymers 2019, 11, 566. [Google Scholar] [CrossRef] [PubMed]
  8. Jordá-Vilaplana, A.; Fombuena, V.; García-García, D.; Samper, M.D.; Sánchez-Nácher, L. Surface modification of polylactic acid (PLA) by air atmospheric plasma treatment. Eur. Polym. J. 2014, 58, 23–33. [Google Scholar] [CrossRef]
  9. Jin, Y.; Wan, Y.; Zhang, B.; Liu, Z. Modeling of the chemical finishing process for polylactic acid parts in fused deposition modeling and investigation of its tensile properties. J. Mater. Process. Technol. 2017, 240, 233–239. [Google Scholar] [CrossRef]
  10. Lv, S.; Gu, J.; Tan, H.; Zhang, Y. The morphology, rheological, and mechanical properties of wood flour/starch/poly(lactic acid) blends. J. Appl. Polym. Sci. 2017, 134, 44743. [Google Scholar] [CrossRef]
  11. Lv, S.; Zhang, Y.; Gu, J.; Tan, H. Biodegradation behavior and modelling of soil burial effect on degradation rate of PLA blended with starch and wood flour. Colloids Surf. B Biointerfaces 2017, 159, 800–808. [Google Scholar] [CrossRef]
  12. Khoo, R.Z.; Chow, W.S. Mechanical and thermal properties of poly(lactic acid)/sugarcane bagasse fiber green composites. J. Thermoplast. Compos. Mater. 2017, 30, 1091–1102. [Google Scholar] [CrossRef]
  13. Müller, K.; Van Opdenbosch, D.; Zollfrank, C. Cellulose blends with polylactic acid or polyamide 6 from solution blending: Microstructure and polymer interactions. Mater. Today Commun. 2022, 30, 103074. [Google Scholar] [CrossRef]
  14. Serra-Parareda, F.; Delgado-Aguilar, M.; Espinach, F.X.; Mutjé, P.; Boufi, S.; Tarrés, Q. Sustainable plastic composites by polylactic acid-starch blends and bleached kraft hardwood fibers. Compos. Part B Eng. 2022, 238, 109901. [Google Scholar] [CrossRef]
  15. Ghasemzadeh, H.; Ghanaat, F. Antimicrobial alginate/PVA silver nanocomposite hydrogel, synthesis and characterization. J. Polym. Res. 2014, 21, 355. [Google Scholar] [CrossRef]
  16. Jeżo, A.; Kowaluk, G. Carbon Capture and Storage through Upcycling of Suberinic Acid Residues in Wood Composites Finishing. C-J. Carbon Res. 2023, 9, 80. [Google Scholar] [CrossRef]
  17. Li, Y.; Shimizu, H. Toughening of polylactide by melt blending with a biodegradable poly(ether)urethane elastomer. Macromol. Biosci. 2007, 7, 921–928. [Google Scholar] [CrossRef] [PubMed]
  18. Martin, O.; Avérous, L. Poly(lactic acid): Plasticization and properties of biodegradable multiphase systems. Polymer 2001, 42, 6209–6219. [Google Scholar] [CrossRef]
  19. Oksman, K.; Skrifvars, M.; Selin, J.F. Natural fibres as reinforcement in polylactic acid (PLA) composites. Compos. Sci. Technol. 2003, 63, 1317–1324. [Google Scholar] [CrossRef]
  20. Sousa, F.M.; Costa, A.R.M.; Reul, L.T.A.; Cavalcanti, F.B.; Carvalho, L.H.; Almeida, T.G.; Canedo, E.L. Rheological and thermal characterization of PCL/PBAT blends. Polym. Bull. 2019, 76, 1573–1593. [Google Scholar] [CrossRef]
  21. de Campos, A.; Tonoli, G.H.D.; Marconcini, J.M.; Mattoso, L.H.C.; Klamczynski, A.; Gregorski, K.S.; Wood, D.; Williams, T.; Chiou, B.-S.; Imam, S.H. TPS/PCL Composite Reinforced with Treated Sisal Fibers: Property, Biodegradation and Water-Absorption. J. Polym. Environ. 2013, 21, 1–7. [Google Scholar] [CrossRef]
  22. Cabedo, L.; Feijoo, J.L.; Villanueva, M.P.; Lagarón, J.M.; Giménez, E. Optimization of biodegradable nanocomposites based on aPLA/PCL blends for food packaging applications. Macromol. Symp. 2006, 233, 191–197. [Google Scholar] [CrossRef]
  23. Todo, M.; Park, S.D.; Takayama, T.; Arakawa, K. Fracture micromechanisms of bioabsorbable PLLA/PCL polymer blends. Eng. Fract. Mech. 2007, 74, 1872–1883. [Google Scholar] [CrossRef]
  24. Fortelny, I.; Ujcic, A.; Fambri, L.; Slouf, M. Phase Structure, Compatibility, and Toughness of PLA/PCL Blends: A Review. Front. Mater. 2019, 6, 206. [Google Scholar] [CrossRef]
  25. Wu, D.; Lin, D.; Zhang, J.; Zhou, W.; Zhang, M.; Zhang, Y.; Wang, D.; Lin, B. Selective localization of nanofillers: Effect on morphology and crystallization of PLA/PCL blends. Macromol. Chem. Phys. 2011, 212, 613–626. [Google Scholar] [CrossRef]
  26. da Silva, W.A.; Luna, C.B.B.; de Melo, J.B.d.C.A.; Araújo, E.M.; Filho, E.A.d.S.; Duarte, R.N.C. Feasibility of Manufacturing Disposable Cups using PLA/PCL Composites Reinforced with Wood Powder. J. Polym. Environ. 2021, 29, 2932–2951. [Google Scholar] [CrossRef]
  27. Barreto Luna, C.B.; dos Santos Filho, E.A.; Siqueira, D.D.; de Souza, D.D.; Ramos Wellen, R.M.; Araújo, E.M. Jatobá wood flour: An alternative for the production of ecological and sustainable PCL biocomposites. J. Compos. Mater. 2022, 56, 3835–3850. [Google Scholar] [CrossRef]
  28. Filho, E.A.S.; Luna, C.B.B.; Silva, A.L.; Ferreira, E.S.B.; Araújo, E.M.; Costa, A.C.F.M. Effect of Kaolin Waste Annealing on the Structural and Thermal Behavior of Poly(Ε−Caprolactone). Momento 2022, 2022, 66–84. [Google Scholar] [CrossRef]
  29. Liverani, L.; Lacina, J.; Roether, J.A.; Boccardi, E.; Killian, M.S.; Schmuki, P.; Schubert, D.W.; Boccaccini, A.R. Incorporation of bioactive glass nanoparticles in electrospun PCL/chitosan fibers by using benign solvents. Bioact. Mater. 2018, 3, 55–63. [Google Scholar] [CrossRef] [PubMed]
  30. Lepot, N.; Van Bael, M.K.; Rul, H.V.D.; D’Haen, J.; Peeters, R.; Franco, D.; Mullens, J. Influence of Incorporation of ZnO Nanoparticles and Biaxial Orientation on Mechanical and Oxygen Barrier Properties of Polypropylene Films for Food Packaging Applications. J. Appl. Polym. Sci. 2011, 120, 1616–1623. [Google Scholar] [CrossRef]
  31. Choudalakis, G.; Gotsis, A.D. Permeability of polymer/clay nanocomposites: A review. Eur. Polym. J. 2009, 45, 967–984. [Google Scholar] [CrossRef]
  32. Kaßner, L.; Nagel, K.; Grützner, R.E.; Korb, M.; Rüffer, T.; Lang, H.; Spange, S. Polyamide 6/silica hybrid materials by a coupled polymerization reaction. Polym. Chem. 2015, 6, 6297–6304. [Google Scholar] [CrossRef]
  33. Wang, Z.F.; Wang, B.; Qi, N.; Zhang, H.F.; Zhang, L.Q. Influence of fillers on free volume and gas barrier properties in styrene-butadiene rubber studied by positrons. Polymer 2005, 46, 719–724. [Google Scholar] [CrossRef]
  34. Lizundia, E.; Vilas, J.L.; Sangroniz, A.; Etxeberria, A. Light and gas barrier properties of PLLA/metallic nanoparticles composite films. Eur. Polym. J. 2017, 91, 10–20. [Google Scholar] [CrossRef]
  35. Aframehr, W.M.; Molki, B.; Heidarian, P.; Behzad, T.; Sadeghi, M.; Bagheri, R. Effect of calcium carbonate nanoparticles on barrier properties and biodegradability of polylactic acid. Fibers Polym. 2017, 18, 2041–2048. [Google Scholar] [CrossRef]
  36. Kong, L.; Tu, K.; Guan, H.; Wang, X. Growth of high-density ZnO nanorods on wood with enhanced photostability, flame retardancy and water repellency. Appl. Surf. Sci. 2017, 407, 479–484. [Google Scholar] [CrossRef]
  37. Yang, W.; Qi, G.; Kenny, J.M.; Puglia, D.; Ma, P. Effect of cellulose nanocrystals and lignin nanoparticles on mechanical, antioxidant and water vapour barrier properties of glutaraldehyde crosslinked PVA films. Polymers 2020, 12, 1364. [Google Scholar] [CrossRef] [PubMed]
  38. Zhang, L.; Jiang, Y.; Ding, Y.; Povey, M.; York, D. Investigation into the antibacterial behaviour of suspensions of ZnO nanoparticles (ZnO nanofluids). J. Nanoparticle Res. 2007, 9, 479–489. [Google Scholar] [CrossRef]
  39. Sirelkhatim, A.; Mahmud, S.; Seeni, A.; Kaus, N.H.M.; Ann, L.C.; Bakhori, S.K.M.; Hasan, H.; Mohamad, D. Review on zinc oxide nanoparticles: Antibacterial activity and toxicity mechanism. Nano-Micro Lett. 2015, 7, 219–242. [Google Scholar] [CrossRef]
  40. Zhang, J. Silver-coated zinc oxide nanoantibacterial synthesis and antibacterial activity characterization. In Proceedings of the 2011 International Conference on Electronics and Optoelectronics, Dalian, China, 29–31 July 2011; IEEE: New York, NY, USA, 2011; Volume 3, pp. V3-94–V3-98. [Google Scholar] [CrossRef]
  41. Ren, G.; Hu, D.; Cheng, E.W.C.; Vargas-Reus, M.A.; Reip, P.; Allaker, R.P. Characterisation of copper oxide nanoparticles for antimicrobial applications. Int. J. Antimicrob. Agents 2009, 33, 587–590. [Google Scholar] [CrossRef]
  42. Delgado, K.; Quijada, R.; Palma, R.; Palza, H. Polypropylene with embedded copper metal or copper oxide nanoparticles as a novel plastic antimicrobial agent. Lett. Appl. Microbiol. 2011, 53, 50–54. [Google Scholar] [CrossRef]
  43. Palomba, M.; Carotenuto, G.; Cristino, L.; Di Grazia, M.A.; Nicolais, F.; De Nicola, S. Activity of antimicrobial silver polystyrene nanocomposites. J. Nanomater. 2012, 2012, 185029. [Google Scholar] [CrossRef]
  44. Thomas, V.; Yallapu, M.M.; Sreedhar, B.; Bajpai, S.K. A versatile strategy to fabricate hydrogel-silver nanocomposites and investigation of their antimicrobial activity. J. Colloid Interface Sci. 2007, 315, 389–395. [Google Scholar] [CrossRef] [PubMed]
  45. Palza, H. Antimicrobial polymers with metal nanoparticles. Int. J. Mol. Sci. 2015, 16, 2099–2116. [Google Scholar] [CrossRef] [PubMed]
  46. Zhou, X.Q.; Hayat, Z.; Zhang, D.D.; Li, M.Y.; Hu, S.; Wu, Q.; Cao, Y.F.; Yuan, Y. Zinc Oxide Nanoparticles: Synthesis, Characterization, Modification, and Applications in Food and Agriculture. Processes 2023, 11, 1193. [Google Scholar] [CrossRef]
  47. Castro, J.I.; Araujo-Rodríguez, D.G.; Valencia-Llano, C.H.; López Tenorio, D.; Saavedra, M.; Zapata, P.A.; Grande-Tovar, C.D. Biocompatibility Assessment of Polycaprolactone/Polylactic Acid/Zinc Oxide Nanoparticle Composites under In Vivo Conditions for Biomedical Applications. Pharmaceutics 2023, 15, 2196. [Google Scholar] [CrossRef] [PubMed]
  48. Tian, J.; Paterson, T.E.; Zhang, J.; Li, Y.; Ouyang, H.; Asencio, I.O.; Hatton, P.V.; Zhao, Y.; Li, Z. Enhanced Antibacterial Ability of Electrospun PCL Scaffolds Incorporating ZnO Nanowires. Int. J. Mol. Sci. 2023, 24, 14420. [Google Scholar] [CrossRef] [PubMed]
  49. Makars, R.; Rizikovs, J.; Godina, D.; Paze, A.; Merijs-Meri, R. Utilization of Suberinic Acids Containing Residue as an Adhesive for Particle Boards. Polymers 2022, 14, 2304. [Google Scholar] [CrossRef] [PubMed]
  50. Gumowska, A.; Kowaluk, G. Physical and Mechanical Properties of High-Density Fiberboard Bonded with Bio-Based Adhesives. Forests 2023, 14, 84. [Google Scholar] [CrossRef]
  51. ISO 1522; Paints and Varnishes—Pendulum Damping Test. European Committee for Standardization: Brussels, Belgium, 2022.
  52. EN 12720+A1; Furniture—Assessment of Surface Resistance to Cold Liquids. European Committee for Standardization: Brussels, Belgium, 2013.
  53. EN 717-1; Wood-Based Panels—Determination of Formaldehyde Release—Part 1: Formaldehyde Emission by the Chamber Method. European Committee for Standardization: Brussels, Belgium, 2004.
  54. Pavlič, M.; Petrič, M.; Žigon, J. Interactions of coating and wood flooring surface system properties. Coatings 2021, 11, 91. [Google Scholar] [CrossRef]
  55. Lis, B.; Krystofiak, T.P.S. Studies of the resistance upon some factors of UV acrylic lacquer coatings on MDF boards. Part I. Resistance of heat and cold liquid action. Ann. Warsaw Univ. Life Sci.—SGGW. For. Wood Technol. 2010, 71, 450–453. [Google Scholar]
  56. Eom, Y.-G.; Kim, J.-S.; Kim, S.; Kim, J.-A.; Kim, H.J. Reduction of Formaldehyde Emission from Particleboards by Bio Scavengers. Mokchae Konghak 2006, 34, 29–41. [Google Scholar]
  57. Aversa, C.; Barletta, M.; Puopolo, M.; Vesco, S. Cast extrusion of low gas permeability bioplastic sheets in PLA/PBS and PLA/PHB binary blends. Polym. Technol. Mater. 2020, 59, 231–240. [Google Scholar] [CrossRef]
  58. Sousa, F.M.; Cavalcanti, F.B.; Marinho, V.A.D.; Morais, D.D.S.; Almeida, T.G.; Carvalho, L.H. Effect of composition on permeability, mechanical properties and biodegradation of PBAT/PCL blends films. Polym. Bull. 2022, 79, 5327–5338. [Google Scholar] [CrossRef]
  59. Lykidis, C. Formaldehyde Emissions from Wood-Based Composites: Effects of Nanomaterials. In Emerging Nanomaterials: Opportunities and Challenges in Forestry Sectors; Springer International Publishing: Cham, Switzerland, 2022; pp. 337–360. [Google Scholar] [CrossRef]
  60. Pinchevska, O.; Lopatko, K.; Lopatko, L.; Oliynyk, R.; Sedliačik, J. The Effect of Metal Nanoparticles on Formaldehyde Emission From Wood Based Materials. Acta Fac. Xylologiae Zvolen 2023, 65, 35–43. [Google Scholar] [CrossRef]
  61. Chen, Y.; Xu, L.; Wu, X.; Xu, B. The influence of nano ZnO coated by phosphazene/triazine bi-group molecular on the flame retardant property and mechanical property of intumescent flame retardant poly (lactic acid) composites. Thermochim. Acta 2019, 679, 178336. [Google Scholar] [CrossRef]
  62. Ahmadzadeh, Y.; Babaei, A.; Goudarzi, A. Assessment of localization and degradation of ZnO nano-particles in the PLA/PCL biocompatible blend through a comprehensive rheological characterization. Polym. Degrad. Stab. 2018, 158, 136–147. [Google Scholar] [CrossRef]
  63. Rebholz, C.; Leyland, A.; Matthews, A.; Charitidis, C.; Logothetidis, S.; Schneider, D. Correlation of elastic modulus, hardness and density for sputtered TiAlBN thin films. Thin Solid Film. 2006, 514, 81–86. [Google Scholar] [CrossRef]
  64. Tien, C.-K.C.; Tzu, L. The indirect measurement of tensile strength by the deterministic grey dynamic model DGDM(1, 1, 1). Int. J. Syst. Sci. 1997, 28, 683–690. [Google Scholar] [CrossRef]
  65. Ashraf, M.A.; Peng, W.; Zare, Y.; Rhee, K.Y. Effects of Size and Aggregation/Agglomeration of Nanoparticles on the Interfacial/Interphase Properties and Tensile Strength of Polymer Nanocomposites. Nanoscale Res. Lett. 2018, 13, 214. [Google Scholar] [CrossRef]
  66. An, L.; Zhang, D.; Zhang, L.; Feng, G. Effect of nanoparticle size on the mechanical properties of nanoparticle assemblies. Nanoscale 2019, 11, 9563–9573. [Google Scholar] [CrossRef]
  67. Aydın, M.; Tozlu, H.; Kemaloglu, S.; Aytac, A.; Ozkoc, G. Effects of Alkali Treatment on the Properties of Short Flax Fiber-Poly(Lactic Acid) Eco-Composites. J. Polym. Environ. 2011, 19, 11–17. [Google Scholar] [CrossRef]
  68. Bužarovska, A.; Blazevska-Gilev, J.; Pérez-Martnez, B.T.; Balahura, L.R.; Pircalabioru, G.G.; Dinescu, S.; Costache, M. Poly(l-lactic acid)/alkali lignin composites: Properties, biocompatibility, cytotoxicity and antimicrobial behavior. J. Mater. Sci. 2021, 56, 13785–13800. [Google Scholar] [CrossRef]
  69. Gkartzou, E.; Koumoulos, E.P.; Charitidis, C.A. Production and 3D printing processing of bio-based thermoplastic filament. Manuf. Rev. 2017, 4, 1. [Google Scholar] [CrossRef]
  70. Park, C.W.; Youe, W.J.; Kim, S.J.; Han, S.Y.; Park, J.S.; Lee, E.A.; Kwon, G.J.; Kim, Y.S.; Kim, N.H.; Lee, S.H. Effect of lignin plasticization on physico-mechanical properties of lignin/poly(lactic acid) composites. Polymers 2019, 11, 2089. [Google Scholar] [CrossRef] [PubMed]
  71. Alam, M.A.; Ya, H.H.; Hussain, P.B.; Azeem, M.; Sapuan, S.M.; Khan, R.; Ahamad, T. Experimental Investigations on the Surface Hardness of Synthesized Polystyrene/ZnO Nanocomposites. In Advances in Manufacturing Engineering; Emamian, S.S., Awang, M., Yusof, F., Eds.; Lecture Notes in Mechanical Engineering; Springer: Singapore, 2020; pp. 345–352. [Google Scholar]
  72. Hadi, F.A.; Kadhim, R.G. A Study of the Effect of Nano Zinc Oxide on Cure Characteristics and Mechanical Properties of Rubber Composites. J. Phys. Conf. Ser. 2019, 1234, 012043. [Google Scholar] [CrossRef]
  73. Nguyen, T.V.; Do, T.V.; Ngo, T.D.; Nguyen, T.A.; Lu, L.T.; Vu, Q.T.; Thi, L.P.; Tran, D.L. Photocurable acrylate epoxy/ZnO-Ag nanocomposite coating: Fabrication, mechanical and antibacterial properties. RSC Adv. 2022, 12, 23346–23355. [Google Scholar] [CrossRef]
  74. Kim, D.; Jeon, K.; Lee, Y.; Seo, J.; Seo, K.; Han, H.; Khan, S. Preparation and characterization of UV-cured polyurethane acrylate/ZnO nanocomposite films based on surface modified ZnO. Prog. Org. Coat. 2012, 74, 435–442. [Google Scholar] [CrossRef]
  75. González-López, M.E.; Martín del Campo, A.S.; Robledo-Ortíz, J.R.; Arellano, M.; Pérez-Fonseca, A.A. Accelerated weathering of poly(lactic acid) and its biocomposites: A review. Polym. Degrad. Stab. 2020, 179, 109290. [Google Scholar] [CrossRef]
  76. Soumya, S.; Kumar, S.N.; Mohamed, A.P.; Ananthakumar, S. Silanated nano ZnO hybrid embedded PMMA polymer coatings on cotton fabrics for near-IR reflective, antifungal cool-textiles. New J. Chem. 2016, 40, 7210–7221. [Google Scholar] [CrossRef]
  77. Gondal, M.A.; Alzahrani, A.J.; Randhawa, M.A.; Siddiqui, M.N. Morphology and antifungal effect of nano-ZnO and nano-Pd-doped nano-ZnO against Aspergillus and Candida. J. Environ. Sci. Heal.—Part A Toxic/Hazard. Subst. Environ. Eng. 2012, 47, 1413–1418. [Google Scholar] [CrossRef]
  78. Sirin, H.; Tuna, B.; Ozkoc, G. The Effects of Thermomechanical Cycles on the Properties of PLA/TPS Blends. Adv. Polym. Technol. 2014, 33, 1–9. [Google Scholar] [CrossRef]
  79. Yarahmadi, N.; Jakubowicz, I.; Enebro, J. Polylactic acid and its blends with petroleum-based resins: Effects of reprocessing and recycling on properties. J. Appl. Polym. Sci. 2016, 133, 1–9. [Google Scholar] [CrossRef]
  80. Budin, S.; Maideen, N.C.; Koay, M.H.; Ibrahim, D.; Yusoff, H. A comparison study on mechanical properties of virgin and recycled polylactic acid (PLA). J. Phys. Conf. Ser. 2019, 1349, 012002. [Google Scholar] [CrossRef]
  81. Archodoulaki, V.M.; Lüftl, S.; Koch, T.; Seidler, S. Property changes in polyoxymethylene (POM) resulting from processing, ageing and recycling. Polym. Degrad. Stab. 2007, 92, 2181–2189. [Google Scholar] [CrossRef]
  82. Smorawska, J.; Włoch, M.; Głowińska, E. Structure–Property Relationship and Multiple Processing Studies of Novel Bio-Based Thermoplastic Polyurethane Elastomers. Materials 2023, 16, 6246. [Google Scholar] [CrossRef] [PubMed]
  83. da Costa, H.M.; Ramos, V.D.; de Oliveira, M.G. Degradation of polypropylene (PP) during multiple extrusions: Thermal analysis, mechanical properties and analysis of variance. Polym. Test. 2007, 26, 676–684. [Google Scholar] [CrossRef]
  84. El Bhilat, H.; El Had, K.; Salmi, H.; Hachim, A. Thermo-mechanical characterization of post-consumer recycled high impact polystyrene from disposable cups: Influence of the number of processing cycles. J. Comput. Appl. Res. Mech. Eng. 2021, 10, 427–436. [Google Scholar] [CrossRef]
Materials 17 03868 g001
Figure 1. Antibacterial mechanism of ZnO NPs (own elaboration based on [46]).
Figure 1. Antibacterial mechanism of ZnO NPs (own elaboration based on [46]).
Materials 17 03868 g001
Materials 17 03868 g002
Figure 2. The results of the relative hardness of the examined coatings (red—PLA and PLA blends; blue—PCL and PCL blends).
Figure 2. The results of the relative hardness of the examined coatings (red—PLA and PLA blends; blue—PCL and PCL blends).
Materials 17 03868 g002
Materials 17 03868 g003
Figure 3. The average mold grade of the examined coatings exposed to A. niger and C. cladosporioides.
Figure 3. The average mold grade of the examined coatings exposed to A. niger and C. cladosporioides.
Materials 17 03868 g003
Materials 17 03868 g004
Figure 4. PCL tested with Cladosporium cladosporiodies (scale bar: 3 mm).
Figure 4. PCL tested with Cladosporium cladosporiodies (scale bar: 3 mm).
Materials 17 03868 g004
Materials 17 03868 g005
Figure 5. PCL tested with Aspergillus niger (scale bar: 3 mm).
Figure 5. PCL tested with Aspergillus niger (scale bar: 3 mm).
Materials 17 03868 g005
Materials 17 03868 g006
Figure 6. PLA tested with Cladosporium cladosporiodies (scale bar: 3 mm).
Figure 6. PLA tested with Cladosporium cladosporiodies (scale bar: 3 mm).
Materials 17 03868 g006
Materials 17 03868 g007
Figure 7. PLA tested with Aspergillus niger (scale bar: 3 mm).
Figure 7. PLA tested with Aspergillus niger (scale bar: 3 mm).
Materials 17 03868 g007
Materials 17 03868 g008
Figure 8. The relative hardness of the samples after one and after repeated processing.
Figure 8. The relative hardness of the samples after one and after repeated processing.
Materials 17 03868 g008
Table 1. The composition of tested surface-finishing layers.
Table 1. The composition of tested surface-finishing layers.
Variant LabelMatrixSAR Filler Content (w/w of Dry Matter)Nano-ZnO Content (w/w of Dry Matter)
PLAPLA00
PLA nano 2%02
PLA nano 4%04
PLA/SAR100
PLA/SAR nano 2%102
PLA/SAR nano 4%104
PCLPCL00
PCL nano 2%02
PCL nano 4%04
PCL/SAR100
PCL/SAR nano 2%102
PCL/SAR nano 4%104
Table 2. Resistance to cold liquids of the tested finishing layers.
Table 2. Resistance to cold liquids of the tested finishing layers.
Variant LabelAcetoneCitric AcidEthanolDistilled Water
mg m−3
PLAABAB
PLA nano 2%BCCB
PLA nano 4%CCBA
PLA/SARBBAA
PLA/SAR nano 2%CCBC
PLA/SAR nano 4%BBCC
PCLAAAA
PCL nano 2%AAAA
PCL nano 4%AABA
PCL/SARAAAA
PCL/SAR nano 2%AAAA
PCL/SAR nano 4%AAAA
Table 3. The TVOC and HCHO emissions of the tested finishing layers.
Table 3. The TVOC and HCHO emissions of the tested finishing layers.
Variant LabelTVOCHCHO
mg m−3
REF0.2450.044
PLA0.2200.039
PLA nano 2%0.1720.030
PLA nano 4%0.1790.031
PLA/SAR0.2220.041
PLA/SAR nano 2%0.2180.039
PLA/SAR nano 4%0.2160.040
PCL0.2640.045
PCL nano 2%0.0680.012
PCL nano 4%0.0650.012
PCL/SAR0.0800.014
PCL/SAR nano 2%0.0780.013
PCL/SAR nano 4%0.0770.016
Table 4. Percentage decrease in the relative hardness of the examined samples after the second processing.
Table 4. Percentage decrease in the relative hardness of the examined samples after the second processing.
Variant LabelHardness Decreases after the Second Pressing
PLA34.60%
PLA nano 2%23.72%
PLA nano 4%26.14%
PLA/SAR16.57%
PLA/SAR nano 2%24.62%
PLA/SAR nano 4%23.32%
PCL−3.81%
PCL nano 2%13.28%
PCL nano 4%15.49%
PCL/SAR−5.00%
PCL/SAR nano 2%24.66%
PCL/SAR nano 4%20.73%
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Jeżo, A.; Poohphajai, F.; Herrera Diaz, R.; Kowaluk, G. Incorporation of Nano-Zinc Oxide as a Strategy to Improve the Barrier Properties of Biopolymer–Suberinic Acid Residues Films: A Preliminary Study. Materials 2024, 17, 3868. https://doi.org/10.3390/ma17153868

AMA Style

Jeżo A, Poohphajai F, Herrera Diaz R, Kowaluk G. Incorporation of Nano-Zinc Oxide as a Strategy to Improve the Barrier Properties of Biopolymer–Suberinic Acid Residues Films: A Preliminary Study. Materials. 2024; 17(15):3868. https://doi.org/10.3390/ma17153868

Chicago/Turabian Style

Jeżo, Aleksandra, Faksawat Poohphajai, Rene Herrera Diaz, and Grzegorz Kowaluk. 2024. "Incorporation of Nano-Zinc Oxide as a Strategy to Improve the Barrier Properties of Biopolymer–Suberinic Acid Residues Films: A Preliminary Study" Materials 17, no. 15: 3868. https://doi.org/10.3390/ma17153868

APA Style

Jeżo, A., Poohphajai, F., Herrera Diaz, R., & Kowaluk, G. (2024). Incorporation of Nano-Zinc Oxide as a Strategy to Improve the Barrier Properties of Biopolymer–Suberinic Acid Residues Films: A Preliminary Study. Materials, 17(15), 3868. https://doi.org/10.3390/ma17153868

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop