Optical Characteristics of a New Molecular Complex: “Nafion–Colloidal CdSe/CdS/ZnS Nanocrystals”

Here, the optical properties of the Nafion polymer membrane containing colloidal CdSe/CdS/ZnS nanocrystals embedded by diffusion have been studied. The CdSe/CdS/ZnS nanocrystals have a core/shell/shell appearance. All experiments were carried out at room temperature (22 ± 2) °C. A toluene solution was used to provide mobility to the active sulfone groups of the Nafion membrane and to embed the nanocrystals inside the membrane. The diffusion process of colloidal CdSe/CdS/ZnS nanocrystals into Nafion proton exchange membrane has resulted in a new molecular complex “Nafion–colloidal CdSe/CdS/ZnS nanocrystals”. The kinetics of the nanocrystals embedding into the membrane matrix was investigated using luminescence analysis and absorption spectroscopy techniques. The embedding rate of CdSe/CdS/ZnS nanocrystals into the Nafion polymer membrane was approximately 4·10⁻³ min⁻¹. The presence of new luminescence centers in the membrane was proved independently by laser emission spectroscopy. The luminescence spectrum of the resulting molecular complex contains intensity maxima at wavelengths of 538, 588, 643 and 700 nm. The additional luminescence maximum observed at the 643 nm wavelength was not recorded in the original membrane, solvent or in the spectrum of the semiconductor nanoparticles. The luminescence maximum of the colloidal CdSe/CdS/ZnS nanocrystals was registered at a wavelength of 634 nm. The intensity of the luminescence spectrum of the membrane with embedded nanocrystals was found to be higher than the intensity of the secondary emission peak of the initial nanocrystals, which is important for the practical use of the “Nafion–colloidal nanocrystals” complex in optical systems. The lines contained in the luminescence spectrum of the membrane, which has been in solution with colloidal nanocrystals for a long time, registered upon its drying, show the kinetics of the formation of the molecular complex “Nafion membrane–nanocrystals”. Colloidal nanocrystals located in the Nafion matrix represent an analog of a luminescent transducer.