2. Methods
The hybrid nanostructure under study is comprised of an MNS and an SQD, which are coupled to each other via the Coulomb interaction, as illustrated in
Figure 1. The distance between the SQD and the center of the MNS is denoted by
. The dielectric constants of the SQD and the environment are
and
, respectively. The MNS has a fixed outer radius
and is composed of gold, with dielectric function
. The dielectric constant and the radius of the MNS core are symbolized as
and
; their values may vary in the present study.
In the present study, we apply the semiclassical approximation, which means that the external electric field is treated classically, while the states of the quantum emitter are quantized. Thus, we assume that the hybrid nanostructure interacts with the external linearly polarized laser field
., with polarization direction lying along the axis defined by the centers of the nanoparticles. We treat the surface plasmons of the MNS as a quantum energy continuum. The SQD is described as a two-level system, as seen in
Figure 2, with its ground state
and its excited state
, respectively, and the probe field is nearly resonant with the
interband transition.
Taking into consideration that the electric field inside the SQD is expressed as a summation of the external field and the induced internal field [
8], we can express the Hamiltonian that determines the equations of motion, in the dipole approximation, as follows:
with
where
represents the energy of state
(
,
) and
denotes the non-diagonal density matrix element. In Equation (2), we define the Rabi frequency
, where μ represents the transition dipole moment,
and
(for a polarization direction that lies along the z axis). The first term of this parameter is related to the coupling of the SQD with the probe field and the second term owes its presence to the coupling of the SQD with the field sent back at its position, due to the polarization of the MNS that is purely induced by the probe field. For the derivation of the second term of Equation (2), the first order polarizability of the core-shell nanosystem has been set equal to
. The complex function
is given in Ref. [
30]. The parameter
, the exact origin of which is discussed in Ref. [
10], expresses the bidirectional interaction between the SQD and the MNS. In the multipole expansion approach, we define the higher-order polarizability as
, where an extended mathematical formula is introduced in order to calculate the parameter
, as shown in Ref. [
33].
The susceptibility of the SQD is proportional to the non-diagonal density-matrix element calculated in the steady state, as in Ref. [
10], with V/Γ denoting the ratio of the SQD volume to the optical confinement factor. Next, we expand the density matrix elements in a first-order Taylor series about the weak probe field and substitute these expressions into the equations of motion. After solving the derived equations, in the steady state, we calculate the linear part of the
coefficient, based on the following analytical formula:
where
and
express the real and the imaginary parts of the self-interaction coefficient
, respectively,
is the detuning of the applied field from resonance and
represents the dephasing time. Moreover, the parameter
is equal to
. In Equation (5),
and
denote the real and the imaginary parts of
, respectively, which can be considered as frequency-independent.
The critical points of the imaginary part of the
function are calculated by the analytical expression:
The minimum value of Equation (6) corresponds to the emergence of gain without inversion. If the interparticle distance between the components of the hybrid nanosystem is high enough so that we can practically consider that the interaction between them is infinitesimal, the minimum and the maximum values of
converge to zero and
, respectively. The absorption resonance arises at
and the corresponding full width at half maximum is calculated by Equation (8):
Next, we determine the first-order optical susceptibility of the core-shell nanoparticle [
10]
and we derive an analytical expression for the linear absorption coefficient:
In Equation (10), the parameter
is
-dependent,
is a complex quantity that can be considered as frequency-independent, within the short range of frequencies of interest and
symbolizes the imaginary part of the parameter
. Based on Equation (10), we can determine the magnitude of the gain peak which arises on the MNS absorption spectrum:
3. Results
Here, we examine the forms of the absorption spectra, with regard to the SQD and the MNS. The MNS has an outer radius
and it consists of gold. The value of the corresponding dielectric function
, within a short range of frequencies around
, can be approximately set equal to
, according to Ref. [
34]. The hybrid nanosystem is surrounded by vacuum
. The dielectric constant of the SQD is
, the dephasing time is
and
/
[
35]. The dipole moment for the
transition is
. We also assume that the corresponding energy gap is approximately equal to the excitation energy of the localized MNS surface plasmon.
In
Figure 3a,b, we present the spectra of the
and
coefficients, respectively, as a function of the detuning of the weak probe field from resonance
, for different values of the center-to-center distance (
= 11.5 nm: green solid curve, 13.5 nm: pink dashed curve and 15.5 nm: blue dotted curved). The radius and the dielectric constant of the core are
nm and
, respectively. We note that, when the interparticle distance is reduced, the absorption peak becomes highly asymmetric and is transposed to negative values of the detuning parameter, Equation (7); additionally, its magnitude decreases, Equation (6), and the corresponding FWHM expands, Equation (8). Hence, the lifetime of the hybrid exciton is suppressed, and the excitonic energy exhibits a red shift. The previously reported modifications of the spectral characteristics are caused by the enhancement of the coefficients
and
. In the limiting case where the SQD does not practically interact with the MNS, the profile of the absorption resonance obtains a Lorentzian-like line shape and the gain feature extinguishes, because
. The absorption peak has a magnitude and an FWHM equal to
and
, respectively. This indicates that symmetry is a characteristic of the
spectrum, provided that the interaction between both nanoparticles is significantly weakened. The emergence of gain without population inversion on the same spectrum, within a specific range of frequencies, can also be predicted mathematically, based on Equation (6). According to this equation, for any set of the physical parameters, the coefficient
is negative, due to the negative sign of the constant
. The profile of the
spectrum manifests a strong dependence on both the material and the radius of the dielectric core. It is found that the magnitude of the gain dip is maximized for intermediate values of
, as long as the dielectric core has a dielectric constant close to the one corresponding to vacuum and the radius of the core is about
, as in the case illustrated in
Figure 3a. Specifically, for
, the increase of
leads to the enhancement of the gain dip. However, the characteristics of the absorption resonance are not modified. On the other hand, for
, the increase of
is responsible for the suppression of the gain dip, as well as for the enhancement and the narrowing of the absorption peak.
In
Figure 4a,b, we present the absorption spectra for the SQD and the MNS, respectively. Here, we assume that r
1 = 7 nm. For the rest physical parameters, we use the same values as in
Figure 3. As long as the thickness of the MNS is low enough, the increase of the inner radius of the MNS leads to the transposition of the absorption resonance towards the spectral center. This pattern indicates an important attenuation of the exciton–plasmon interaction and was not observed in the case of
Figure 3, where the radius of the core
was set equal to
; additionally, the gain region that emerges on the
spectrum is substantially shrunk. Moreover, the rise of the gain peak on the
spectrum, for intermediate values of the interparticle distance, exhibits a strong dependence on the radius and the dielectric constant of the core. Practically, for
, a prominent gain dip appears on the spectral form of the MNS absorption coefficient, provided that
. Under the same conditions, the
spectrum becomes highly asymmetric and manifests a dispersion-like line shape. For an extremely thin metal shell of thickness about
, it was found that gain is detected on the MNS absorption spectrum within a much broader range of values of the interparticle distance. Τhis suggests that, when the radius of the core is modified by 5 to 7 nm, the direction of the energy transfer process, due to the coherent interaction between the SQD and MNS, is reversed. This effect can be explained as follows. As we increase the inner radius
, the positive factor
becomes more and more insignificant and, thus, the R-dependent term is the one that practically determines the value of the
coefficient, according to Equation (11). At very high interparticle distances, as in the case with
, the second term of Equation (10) vanishes. This happens because the variable
, which is inversely proportional to the third order of
, converges to zero. The spectral profile of
is a horizontal line (turquoise dashed-dotted curve), as the first term of Equation (10), which is constant, determines the value of the absorption coefficient.
In
Figure 5 and
Figure 6, we present the absorption spectra for the SQD, for the same values of the distance between the centers of the coupled nanoparticles as those considered in
Figure 2. The radius of the core
is set equal to
, and
, in
Figure 5 and
Figure 6, respectively, while, in both figures, the dielectric constant of the core is
= 7.5. After comparing
Figure 5 to
Figure 3a and
Figure 6 to
Figure 4a, we deduce that the increase of
is responsible for the enhancement and the narrowing of the absorption resonance and the suppression of the gain dip. This is expected, based on a brief mathematical analysis based on Equation (6). More specifically, the enhancement of
leads to the decrease of
. As a result, the denominator of Equation (6) decreases, thus leading to the enhancement of the absorption peak. This effect is further intensified, in the limiting case of a quite thin nanoshell (as for
), providing that
. In addition, the lifetime of the hybrid exciton is governed by the exact value of the dielectric permittivity of the core. This stems from the fact that the increase of
leads to the reduction of the FWHM of the absorption resonance. This effect can be understood in terms of Equation (8), according to which the FWHM is proportional to the parameter
, the value of which decreases when the dielectric constant of the core
is enhanced. When the dielectric constant of the core is amplified, the magnitude of the gain dip manifests a notable suppression, because, in this case, the factor
becomes insignificant. This is consistent with the conclusions that stem from a comparative study of the spectral profiles presented in
Figure 3,
Figure 4,
Figure 5 and
Figure 6. However, there is not an explicit pattern that governs the shift of the absorption peak when the dielectric constant of the core is modified. In fact, we can identify two different ranges of values of the inner radius that favor two distinct behaviors with regard to the shift of the resonances. The first one includes values of
that lie below
; in this case, the position of the absorption peak exhibits a slight shift towards higher values of the detuning parameter, when the numerical value of
is increased. The second one includes values of
higher than
. In the case of a thin metal nanoshell, the increase of
induces a redshift of the absorption resonance. This can be easily observed if we compare
Figure 4a to
Figure 6. We observe that the absorption resonance moves to the left, as permittivity of the core material is enhanced. To outline, for
, the increase of
leads to the enhancement and the narrowing of the absorption resonance; it is also responsible for the suppression of the gain dip, in contrast to the case with
. All these effects become significant when the radius of the core is enhanced.
In
Figure 7a, we present the absorption spectrum for the SQD, in the case where the radius of the MNS core
is set equal to 2 nm. In
Figure 7b, we present the absorption spectrum for the MNS, when
r1 = 7 nm. In both cases, we consider that
. The rest parameters take the same values as in
Figure 2. If we comparatively study
Figure 3a and
Figure 7a, we note that, for low values of the inner radius, the modification of the dielectric constant of the core subtly affects the spectral characteristics of
. On the other hand, the profile of the SQD absorption spectrum presents a strong dependence on the dielectric constant of the core. The same holds with regard to the spectral profile of
. When we increase the dielectric constant of the core, the magnitude of the gain dip that arises on the MNS absorption spectrum is suppressed, for any possible value of the inner radius
. Above a critical value of
, which varies according to the value of
, the gain is eliminated, as illustrated in
Figure 7b. For
, the spectral profile of
has a Lorentzian-like line shape, as opposed to the case with
shown in
Figure 4b, where the spectral profile of the absorption coefficient
exhibits a Fano-type line shape. In the limiting case of a quite thick nanoshell (
), the characteristic width of the MNS absorption peak is given by the approximate coefficient
. Moreover, the gain dip does not practically depend on the dielectric constant of the core. The previously reported effects emerge due to the increase of
, which leads to a substantial decrease of the factor
that appears in the
-dependent term of Equation (10).
4. Conclusions
In this work, we present a detailed theoretical analysis of the linear optical response of an SQD–MNS hybrid system. More specifically, we demonstrated that the properties of the MNS core substantially affect the spectral characteristics of the linear absorption coefficient for the MNS and the SDQ, separately. In the present study, we explore how the radius and the dielectric constant of the core affect the absorption spectra of the SQD and the MNS. After deriving the non-linear density matrix equations, we implement a first-order series expansion of the density matrix elements, with respect to the incident field. Next, we obtain analytical expressions for the imaginary part of the linear optical susceptibility of the SQD and the MNS. We also derive analytical expressions for the theoretical prediction of the positions and the magnitudes of the absorption/gain resonances that arise on the absorption spectra; the analytical formula for the FWHM of the absorption peak is presented in the study, which constitutes a measure of the inverse lifetime of the hybrid excitons. More specifically, we have identified two distinct types of hybrid excitons. It is demonstrated that both the dielectric material and the radius of the MNS core determine the type of the hybrid exciton that emerges on the optical absorption spectrum of the SQD.
In particular, the first type of hybrid exciton arises on the absorption spectrum of the quantum emitter, providing that the core of the metal nanoshell is thick and the dielectric constant of its material is close to the one corresponding to vacuum. Under the strong exciton–plasmon coupling regime, the gain without population inversion is importantly enhanced; the absorption peak is also strongly quenched, and the exciton lifetime is importantly shrunk. The second type of hybrid exciton appears under the weak exciton–plasmon coupling regime. Under this regime, the value of the dielectric constant and the radius of the dielectric core are both increased. Typical features of the second type of hybrid exciton are the amplified absorption resonance, the enhanced exciton lifetime, and the suppression of the gain coefficient. The formation of this last type of the hybrid excitons is induced when the dielectric constant of the core is enhanced for any fixed value of the core’s radius. When the core of the MNS has a dielectric constant that tends to unity, the increase of the radius, up until a critical value, leads to the formation of the first type of hybrid exciton. However, above this critical value, the hybrid structure starts exhibiting the characteristics associated with the second type of hybrid exciton. Lastly, the properties of the core govern the absorption response of the MNS, as well. More explicitly, the gain that emerges on the profile of the corresponding spectrum is significantly enhanced, provided that the metal shell becomes exceptionally thin and the dielectric constant of the core tends to unity. Under these conditions, the gain that emerges on the profile of the absorption spectrum of the MNS presents the highest enhancement that can be observed.