Next Article in Journal
The Integration of Reference Electrode for ISFET Ion Sensors Using Fluorothiophenol-Treated rGO
Next Article in Special Issue
PEDOT-Polyamine-Based Organic Electrochemical Transistors for Monitoring Protein Binding
Previous Article in Journal
Complete Breast Cancer Detection and Monitoring System by Using Microwave Textile Based Antenna Sensors
Previous Article in Special Issue
Organic Light-Emitting Diode Based Fluorescence-Linked Immunosorbent Assay for SARS-CoV-2 Antibody Detection
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Biosensors
Volume 13
Issue 1
10.3390/bios13010088
biosensors-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Sensitive and Rapid Detection of Aspartic Acid with Co3O4-ZnO Nanorods Using Differential Pulse Voltammetry

by
Sulaiman Y. Alfaifi
1,
Waheed Abiodun Adeosun
1,2,
Abdullah M. Asiri
1,2 and
Mohammed M. Rahman
1,2,*
1
Chemistry Department, Faculty of Science, King Abdulaziz University, P.O. Box 80203, Jeddah 21589, Saudi Arabia
2
Center of Excellence for Advanced Materials Research (CEAMR), King Abdulaziz University, P.O. Box 80203, Jeddah 21589, Saudi Arabia
*
Author to whom correspondence should be addressed.
Biosensors 2023, 13(1), 88; https://doi.org/10.3390/bios13010088
Submission received: 15 November 2022 / Revised: 25 December 2022 / Accepted: 3 January 2023 / Published: 5 January 2023
(This article belongs to the Special Issue Organic Bioelectronic Materials and Devices for In Vitro/Vivo Diagnostics)
Browse Figures
Versions Notes

Abstract

:
Herein, the detection of aspartic acid by doped Co3O4-ZnO nanorod materials was proposed using differential pulse voltammetry. The nano-composite metal oxide was synthesized by the wet precipitation method in basic media. Aspartic acid is a non-essential amino acid naturally synthesized in the body with lot of health significance, including as a biomarker for several health deficiencies. The synthesized composite Co3O4-ZnO nanorod was well-investigated by using FESEM, XRD, XPS, FTIR, UV/vis., EIS, and CV. The synthesized composite exhibited a low limit of detection (0.03 µM, high sensitivity (0.0014 µA µM−1 cm−2) and wide linear range (0.05–50 µM) for aspartic acid. The substrate, the Co3O4-ZnO nanorod, enhanced the electro-catalytic oxidation of aspartic acid as a result of its catalytic and conductivity properties. The developed sensor based on Co3O4-ZnO has a repeatable, reproducible and stable current response for aspartic acid. Additionally, other electroactive compounds did not interfere with the sensor’s current response. The suitability of the developed sensor for real sample analysis was also established. Therefore, this study proposed the potential use of Co3O4-ZnO nanorod material in healthcare management for the maintenance of human well-being.

1. Introduction

Amino acids are an important organic biochemical in human metabolism. They are among the vital nutrients necessary for body building and general well-being [1]. An important class of amino acid is aspartic acid, which is naturally synthesized in the body. It is also synthesized in the body though oxaloacetate [2]. Another notable source of aspartic acid is sugar cane. Aspartic acid helps in muscle strengthening and enduring strength through the generation of luteinizing and testosterone hormones. In addition, aspartic acid is an important neurological transmitter in the central nervous system. The concentration of aspartic acid in the body could be a biomarker for lung and neck cancer, Alzheimer’s syndrome, Lenox syndrome and epilepsy [2,3]. Due to its physiological and biological importance, several techniques have been proposed for measuring aspartic acid in biological samples. Such methods include chromatography (ion exchange, high-performance liquid chromatography and gas chromatography), fluorescence, spectrophotometry and electrochemical routes (enzyme and non-enzyme-based) [4,5,6,7]. Methods based on chromatography and spectrophotometry are very sensitive but suffer major setbacks because of their long analysis time, tedious sample preparation and high cost of analysis. In contrast, electrochemical methods offer a low cost of analysis, high accuracy and simplicity, which makes the electrochemical method highly attractive [8,9,10]. Gao et al., in their studies, developed an aspartic acid detector using a Cu (II)-catalyzed oscillating reaction. This method is based on the reaction between H2O2 and sodium thiocyanate catalyzed by Cu(II) ions. There was a low limit of detection (5.58 × 10−8 mol L−1) in the linear range of 1.17 × 10−5 to 7.0 × 10−8 mol L−1 [11].
In addition, Fontanarosa and his research group reported the very sensitive detection of aspartic acid with a tandem mass spectrometer. Their study reported a very low limit of detection (0.52 pg/µL) [12]. Similarly, Tabaraki et al. developed a fluorescence-based method for the assay of aspartic acid in human serum. They employed n-doped carbon dots synthesized with the aid of microwave radiation as a fluorescent. The quenching of the fluorescence upon the addition of aspartic acid forms the basis of the sensing. Their method reported a low limit of detection (90.0 nM) in the linear range of 0.5–50 µM [1].
Prasad and his team worked on the fabrication of an electrochemical sensor for D- and L- aspartic acid using molecularly imprinted poly (indole 3-acetic acid)/multiwalled carbon nanotube/pencil graphite electrode. The determination of D-aspartic acid and L-aspartic acid was conducted by differential pulse anodic stripping voltammetry. The detection limits of 0.025 µM and 0.016 µM were reported for D- and L- aspartic acid, respectively [3]. The aforementioned methods offer good performance for aspartic acid detection, but the need for a cheap, sensitive procedure suitable for in situ analysis necessitates further research. This study, therefore, explores the electrochemical method for the detection of aspartic acid in real samples using a metal oxide nanomaterial composite. Co3O4 is a metallic oxide and a semi-conductor which is very interesting due to its electronic, magnetic, optical and electrochemical properties [13,14,15,16,17]. In addition, Co3O4 has good catalytic properties which makes it an ideal material for electrochemical sensing. Likewise, ZnO is another metal oxide and n-type semi-conductor with unique material properties. It has a direct band-gap of 3.5 eV and wide excitation binding energy (60.0 meV), as well as good catalytic properties. ZnO has interesting applications in electro-catalysis, energy storage and electrochemical sensing [17,18,19,20]. The composition of these two materials has been reported to have excellent applications in electrocatalysis. While there are a plethora of studies on the individual synthesis of ZnO and Co3O4, very few studies report the synthesis of Co3O4-ZnO nanorods. For instance, Tak et al. reported the synthesis of Co3O4-ZnO nanorods by the photochemical coating method. In their studies, ZnO nanowires were first synthesized by the hydrothermal method and Co3O4 was then coated on ZnO nanowires by the photochemical reaction [21].
Moreover, Reda and his research group reported Co3O4-ZnO nanorod synthesis by the facile solid-state grinding technique [22]. The synthesized hetero-structure nanocomposite was studied for its photocatalytic property. Other studies by Yang et al. [20], Liu et al. [23], Sharma et al. [16], and Xu et al. [24] have reported successful synthesis of Co3O4-ZnO low-dimensional nanorods. Based on the simplicity and generation of highly structured material, the simple wet chemical method was employed for the synthesis of the Co3O4-ZnO nanorods used for this study. This study therefore reports for the first time the electrochemical detection of aspartic acid using Co3O4-ZnO nanorods, which makes this study an important and a novel study. Additionally, the prospect or suitability of the proposed sensor for real sample analysis was measured and established.

2. Materials and Methods

2.1. Chemicals and Reagents

The essential chemicals used for the proposed experiment include cobalt II nitrate (Sigma Aldrich, New York, NY, USA), zinc II sulfate (Sigma Aldrich, New York, NY, USA), ammonia solution (25%) (Sigma Aldrich, New York, NY, USA), aspartic acid (Sigma Aldrich, New York, NY, USA), sodium dihydrogen phosphate, disodium hydrogen phosphate, potassium chloride, glucose, nitrite, melamine, glutamic acid, leucine, uric acid and ascorbic acid. All of the chemicals used for this study were of analytical grade and were used as bought without any further treatment.

2.2. Apparatus

The apparatus used for this study includes a field emission scanning electron microscope (FESEM, JSM-7600F, JEOL, Tokyo, Japan) fitted with an X-ray electron diffraction spectrometer (Thermo Scientific, Tokyo, Japan), X-ray photoelectron spectrometer (XPS) (Thermo Scientific, Tokyo, Japan), Fourier transform infrared spectrometer (FTIR) (X-Vision, Tokyo, Japan), ultraviolet–visible spectrophotometer (UV-Vis.) (Thermo Scientific, Tokyo, Japan) and potentiostat powered by Autolab Nova 2.1 (Tokyo, Japan) comprising working, reference and counter electrodes. The working electrode at any point in time was a glassy carbon electrode or bare electrode, while the reference and counter electrodes were made up of Ag/AgCl (3 M KCl) and platinum wire, respectively.

2.3. Synthesis of Co3O4-ZnO Nanorods

The facile wet chemical method was used for the synthesis of Co3O4 as described. A total of 0.1 M Co(NO3)3·6H2O (2.91 g/100.0 mL) was prepared. Then, 80.0 mL of the solution was measured into a 250.0 mL beaker. Additionally, 80.0 mL 0.1 M ZnSO4·2H2O (1.97 g/100.0 mL) was prepared and added to the beaker containing 80.0 mL Co3O4. The two mixtures were then stirred for about 90 min upon the dropwise addition of 20.0 mL ammonia solution (25%). After 90 min of continuous stirring at 80 rpm, maintaining a temperature of 80 °C, a pinkish precipitate was formed and well-washed with deionized water followed by acetone. The washed precipitate was completely dried in the oven overnight at 80 °C. The dried powdery material obtained was then properly ground using a mortar and pestle. Lastly, the well-ground powdery sample was calcined in the muffle furnace at 600 °C for 3 h. After calcination, the color of the prepared sample changed from pink to black.

2.4. Fabrication of Co3O4-ZnO Nanorod Coated Electrode

The glassy carbon electrode was first soaked in ethanolic solution for about an hour and was then cleaned by rubbing on a micro-cloth pad soaked with 0.5 µm alumina slurry. It was then washed and rinsed with de-ionized water [25]. In addition, chemically adsorbed material on the GCE surface was removed using cyclic voltammetry (0.25 M sulfuric acid as supporting electrolyte). About 30.0 µg of Co3O4-ZnO nanorod was then measured into a watch glass with the addition of 10 µL of ethanolic solution to disperse the nanoparticle. The dispersed nanoparticle was then applied directly on the GCE surface and was cemented using one drop of nafion solution (conducting binder). The prepared Co3O4-ZnO nanorod was then allowed to dry in the open air for about 2 h and used for further studies.

2.5. Characterization Technique

The surface morphology of the synthesized metallic oxide nanocomposite was assessed using FESEM (tungsten filament, pictures taken using low and high magnifications). The binding energy and elemental composition were obtained using X-ray photoelectron spectroscopy (at the binding energy range of 0–1400 eV). Additionally, XEDS fitted with FESEM was used for analyzing the elemental composition in the synthesized nanocomposite at an electron beam size of 10.0 µm. Optical studies were conducted to determine the band gap and elemental functionality (functional groups) using UV-Vis and FTIR spectrometers. Electrochemical characterization studies such as electrochemical impedance spectroscopy as well as cyclic voltammetry were conducted using a potentiostat. For electrochemical impedance spectroscopy, an amplitude of 5.0 mV and DC potential of +0.2 V were applied. Additionally, cyclic and linear sweep voltametric studies were carried out at a scan rate of 100 mV/s, with a potential window of 0 to 1.0 V, modulation time of 0.0024 s and step potential of 0.008 V.

2.6. Interference Studies

Likely interferents such as electroactive molecules, including ascorbic acid, uric acid, glucose, nitrite, etc., were investigated for interference with the oxidation current given by the Co3O4-ZnO nanorod. Other factors such as repeatability and reproducibility were duly investigated.

2.7. Real Sample Analysis

As-purchased mouse serum was used for real sample analysis. The collected samples were diluted by 10-fold using phosphate buffer (0.1 M PBS-pH 5.7) to mask the effect of the matrix. The standard addition method was used for the detection as well as the determination of the spiked sample.

3. Results and Discussion

3.1. Synthesis of Co3O4-ZnO Nanorod

Synthesis of the Co3O4-ZnO nanorod was thought to have occurred through Ostwald ripening. The obtained Co3O4 was crystalline, which suggests that particle growth is dominated by nucleation during formation. The obtained metal oxide composite was pinkish after drying and turned black upon calcination.

3.2. Structural and Morphological Studies

FESEM analysis was conducted to reveal the morphology and microstructure of the synthesized nanocomposite. The obtained images are presented in Figure 1. The structural property of a nanomaterial could influence the material property of the material, such as the surface area, which may eventually have an effect on the performance of the nanomaterial in applications such as electrocatalysis. FESEM images revealed nanorods (app 30–60 nm) wrapped with semi-crystalline whitish material (Figure 1a–c). The nanorods could be associated with Co3O4 while the whitish patches could be associated with ZnO. ZnO is thought to consist of agglomerated nanoparticle lumps with a denser distribution while Co3O4 has a nanorod structure with high crystallinity [20].

3.3. XEDS Analysis

XEDS is an important characterization tool for the investigation of elemental composition in a material. The obtained XEDS spectrum is shown in Figure 1d. The result indicates the presence of cobalt, zinc and oxygen.

3.4. XPS Analysis

XPS, also called electron spectroscopy for chemical analysis (ESCA), is a surface analysis technique that is commonly utilized for quantitatively investigating the chemical state of elemental composition in a material. The XPS spectrum obtained is given in Figure 2a. The full spectrum indicates peaks at the regions of 530, 782 and 1030, corresponding to cobalt, zinc and oxygen, respectively. The binding energies at 529.8 eV and 531.4 eV could be attributed to the O 1s spectrum of the Co3O4-ZnO nanorod (Figure 2b). The peak at 529.9 eV (low energy oxygen peak) could be assigned to lattice oxygen (O2−) in the Co3O4-ZnO, while the peak at 531.4 eV could be linked to chemisorbed oxygen and surface hydrolysis. The XPS result indicates the presence of Co3O4 and ZnO in the prepared nanocomposite. Deconvoluted peaks at 781.3 and 782.4 eV could be attributable to Co2P3/2 and Co 2P1/2, respectively (Figure 2c). Additionally, the deconvoluted peaks at 1021.6 eV and 1044.95 eV (Figure 2d) are attributable to the binding energy of Zn 2P3/2 and Zn 2P½, respectively [16,20,26].

3.5. XRD Analysis

XRD analysis provides information about the chemical composition of materials as it gives information on the crystalline phases of the component materials. The observed XRD spectrum for the Co3O4-ZnO nanorod is given in Figure 2e. Diffraction peaks at (2θ) 19°, 31.20°, 35.48°, 37.80°, 43.2°, 54.89°, 59.20° and 63.01° corresponding to diffraction lines of (111), (220), (311), (222), (400), (422), (511) and (440), respectively, are typical for the cubic spinal structure of Co3O4 (JCPDS No. 42.1467). Moreover, diffraction peaks at 2θ degree, 34.50°, 56.75°, 62.50°, 68.01°, 69.05°, 72.61° and 76.50°, correspond to diffraction lines of (002), (110), (103), (112), (201), (004) and (202), respectively (JCODS No.79-2205). The above diffraction patterns established the successful formation of Co3O4-ZnO nanorods [16,27]. The size of the nanocomposite crystal was evaluated using the Derbye–Sherrer equation, as presented in Equation (1) [16].
δ = 0.89λ/βcos θ
where δ denotes crystallite size, λ denotes the wavelength of Cu-Kα (given as 0.15 nm), β denotes full width at half maximum of the selected peak, and θ denotes the diffraction angle. The crystallite size of the nanocomposite is 42.0 nm.

3.6. Optical Analysis (UV-Vis and FTIR Analyses)

UV-Vis spectroscopic analysis was conducted to determine the band structure and energy in Co3O4-ZnO nanorods. The obtained UV-Vis spectrum is presented in Figure 2f. The spectrum shows bands at 374 nm attributable to the Co3O4-ZnO nanorod, conforming with previous studies [16].
The obtained FTIR spectrum is given in Figure 2g. The observed peak at 550 cm−1 corresponds to Co-O vibration in Co3O4 [28,29,30]. Usually, characteristic bands in the region of 600–1000 cm−1 are associated with vibration of metallic ions in the crystal lattice. Similarly, the peaks noticed in the region of 390 cm−1 could be attributed to Zn-O in ZnO [17,31,32]. Therefore, the observed FTIR analysis suggests the presence of Co3O4 and ZnO in the prepared nanorod.

3.7. Electrochemical Characterization

3.7.1. Electron Mobility

Electron mobility on the surface of the GCE was accessed by cyclic voltammetry in the ferricyanide couple (Fe(CN)63−/4−). The cyclic voltammetry sweep in 1 mM Fe(CN)63−/4− was conducted in the window range of −0.2 to 0.5 V at a scan rate of 75 mV/s. The obtained result is given in Figure 3a. From the result, it could be observed that a higher oxidation current was recorded with the coated GCE (0.1 mA) compared with bare GCE (80 µA). The increased current indicates improved electron mobility on the surface of GCE [33,34]. Likewise, the peak to peak potential (∆Ep) of the Co3O4-ZnO nanorod modified GCE was smaller (140 mV) compared with the bare GCE (200 mV). This is also an indication of higher electron mobility on the Co3O4-ZnO nanorod modified GCE surface.

3.7.2. Impedance Study

Electrochemical impedance spectroscopy (EIS) was conducted to assess the resistivity between the electrolyte and electrode interface. The obtained spectrum is given in Figure 3b. In EIS, the semi-circle denotes charge transfer resistance (Rct), which is associated with electron/charge mobility on the surface of the electrode. The smaller the Rct, the better the electron mobility and vice versa [35,36,37,38]. As shown in Figure 3a, a smaller Rct was obtained for the Co3O4-ZnO nanorod (219 kΩ) as compared with bare GCE (669 kΩ). This indicates that the substrate on the GCE (Co3O4-ZnO nanorod) improves electron mobility on the electrode surface. This property is also essential for the electrocatalytic properties of the Co3O4-ZnO nanorod. The equivalent circuit diagram for the EIS study is presented in Figure 3b and Electronic Supplemental Section S1, where Rs is the solution resistance, CPE denotes the constant phase element, W is the Warburg constant and Rct/Rp is the charge transfer resistance.

3.8. Sensing Application

3.8.1. Control Study

A control study was conducted to establish that the current response demonstrated by the Co3O4-ZnO nanorod modified GCE was due to the Co3O4-ZnO nanorod substrate (coated material) and not the carbon in the GCE. As compared with the bare GCE, the coated GCE displayed a sharp peak at −0.95 V, signifying the oxidation of aspartic acid at this potential (Figure 4a). The result indicates that the oxidation of aspartic acid was due to the coated substrate.

3.8.2. pH Variation

In most electro-catalyzed reactions, not only is the coated substrate responsible for the catalytic behavior, but the pH also plays an important role. The result of the control experiment is presented in Figure 4b. For this study, phosphate-buffered solution (PBS) of different pH was used (5.7, 6.5, 7.0, and 8.0). The result reveals that the PBS of pH 5.7 had the highest oxidation current while the PBS of pH 8 had the lowest oxidation current.

3.8.3. Scan Rate Effect

Different scan rates ranging from 25 mV/s to 425 mV/s were applied to determine whether the oxidation of aspartic acid on Co3O4-ZnO nanorod is diffusion-controlled or not. The obtained result is presented in Figure 4c. It could be found the oxidation current (ip) increased linearly with increasing scan rate. This suggests that the reaction is diffusion-controlled [39,40,41]. In addition, the plot of the logarithm of the oxidation current (log ip) against the logarithm of the scan rate (log v) had a slope of 0.41. As given in the literature [42], the slope of log ip vs. log v in the range of 0.5 is associated with the diffusion control process, while the one in the range of 1.0 is an adsorption-controlled process. Therefore, for this analysis, the slope is close to 0.5, which indicates that the reaction is diffusion-controlled.

3.8.4. Calibration Plot

The linear sweep voltammetric (LSV) method was utilized to evaluate the current response to varying concentrations of aspartic acid. LSV was selected owing to its high accuracy, as well as its sensitivity, especially to irreversible reactions [43,44].
The obtained linear sweep voltammogram is presented in Figure 5a. From the cyclic voltammetry, it can be seen that the oxidation peak current increased with the increase in aspartic concentration. For the calibration plot, two slopes were obtained, as revealed in Figure 5b. The two slopes obtained indicate that at higher concentrations, the electrocatalytic properties of the substrate (Co3O4-ZnO nanorod) diminished, which could be a result of the blockage of the active sites of the substrate. In this reaction [45], the Co3O4-ZnO nanorod, owing to its electrical conductivity and catalytic potential, electro-catalyzed the oxidation process, leading to an observed increment in the oxidation peak current. In this instance, it is proposed that Co (IV) and Zn (II) are reduced to zero-valent Co and Zn in the acidic medium (pH 5.7). The electrochemical redox reaction in the GCE substrate is proposed in the following reactions (Equations (2) and (3)).
Co3O4 + [Asp-A] + 8H+ = 3Co + 4H2O
ZnO + [Asp-A] + 2H+ = Zn + H2O
The calibration plot was used for investigating the analytical sensor performance of the fabricated sensor probe.

3.8.5. Analytical Performance

The proposed sensor based on a Co3O4-ZnO nanorod was assessed using several parameters, such as the limit of detection (LOD), the limit of quantification (LOQ), sensitivity, etc.
LOD: The limit of detection was calculated as presented in Electronic Supplemental Section S2. The obtained value was 0.032 µM.
LOQ: The limit of quantification was calculated as described in Electronic Supplemental Section S2. The obtained value was 0.11 µM.
Sensitivity: The sensitivity of the proposed sensor was evaluated as described in Electronic Supplemental Section S2. The obtained value was 0.0014 µA µM−1 cm−2.

3.8.6. Sensor Stability

The stability of the proposed fabricated sensor probe was evaluated in terms of current response repeatability and the interference effect.
For the repeatability study, ten consecutive readings were recorded as displayed in Figure 5c. The current responses were very repeatable with a relative standard deviation of 2.1%. Moreover, the effects of likely interfering species such as electroactive compounds, selected types of amino acid and metal ions were investigated (Figure 5d). The relative standard deviation of the oxidation current obtained with and without interference was 2.4%. This value is less than 5% of the adjudged interference threshold RSD [25].

3.8.7. Real Sample Analysis

Real sample analysis was conducted in this study using a beverage drink and mouse serum. The results obtained are presented in Table 1. The percent recovery of the spiked aspartic concentration ranged from 87.6% to 94.4% (as calculated in Electronic Supplemental Section S3). This result indicates that the proposed method is suitable for real sample analysis.

3.8.8. Comparability with Other Reported Methods

As indicated earlier, several methods have been investigated for the determination or detection of aspartic acid. These are presented in Table 2. Most of the earlier methods reported were based on the fluorescence technique and generally showed high accuracy. The proposed method based on the Co3O4-ZnO nanorod compares very well with the reported studies [1,2,46,47,48,49,50,51,52,53]. In addition, the proposed method displays higher stability and suitability for real sample analysis.

4. Conclusions

In this study, a composite Co3O4-ZnO nanorod was prepared by the facile wet chemical approach in alkaline phase at low temperature. The synthesized nano-metal oxide composite was well-characterized by different techniques, which confirms its successful synthesis. The Co3O4-ZnO nanorod was used for the electrochemical detection of aspartic acid through the electrocatalytic oxidation reaction on the surface of the modified GCE. The developed sensor had a low limit of detection, as well as high sensitivity and selectivity towards aspartic acid. Finally, the developed sensor was used for the detection of aspartic acid in real samples (beverage drink and mouse serum) with satisfactory performance. Therefore, this study presents a promising technique for the potential detection of aspartic acid for healthcare management.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/bios13010088/s1, Electronic Supplemental Section: S1, S2 and S3.

Author Contributions

Methodology, S.Y.A., W.A.A., A.M.A. and M.M.R.; Formal analysis, W.A.A. and M.M.R.; Investigation, S.Y.A. and W.A.A.; Resources, A.M.A.; Writing—original draft, W.A.A.; Writing—review & editing, A.M.A. and M.M.R.; Project administration, S.Y.A. and M.M.R.; Funding acquisition, S.Y.A. All authors have read and agreed to the published version of the manuscript.

Funding

The authors acknowledge and thank DSR for technical and financial support.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data will be available upon reasonable request.

Acknowledgments

This project was funded by the Deanship of Scientific Research (DSR) at King Abdulaziz University, Jeddah, under grant no. G-133-130-1443. The authors acknowledge and thank DSR for technical and financial support.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Tabaraki, R.; Abdi, O. Microwave Assisted Synthesis of N-Doped Carbon Dots: An Easy, Fast and Cheap Sensor for Determination of Aspartic Acid in Sport Supplements. J. Fluoresc. 2019, 29, 751–756. [Google Scholar] [CrossRef]
  2. Prasad, B.B.; Jaiswal, S.; Singh, K. Ultra-trace analysis of D-and L-aspartic acid applying one-by-one approach on a dual imprinted electrochemical sensor. Sens. Actuators B Chem. 2017, 240, 631–639. [Google Scholar] [CrossRef]
  3. Prasad, B.B.; Pandey, I. Electrochemically imprinted molecular recognition sites on multiwalled carbon-nanotubes/pencil graphite electrode surface for enantioselective detection of d- and l-aspartic acid. Electrochim. Acta 2013, 88, 24–34. [Google Scholar] [CrossRef]
  4. Van Den Oetelaar, P.J.M.; Van Beijsterveldt, L.E.C.; Van Beckhoven, J.R.C.M.; Hoenders, H.J. Detection of aspartic acid enantiomers by chiral capillary gas chromatography: Determination of in vivo racemization and reduction of metal-induced background. J. Chromatogr. A 1986, 368, 135–143. [Google Scholar] [CrossRef]
  5. Yu, H.; Ding, Y.-S.; Mou, S.-F. Some factors affecting separation and detection of amino acids by high-performance anion-exchange chromatography with integrated pulsed amperometric detection. J. Chromatogr. A 2003, 997, 145–153. [Google Scholar] [CrossRef]
  6. Wang, S.; Fan, L.; Cui, S. CE-LIF chiral separation of aspartic acid and glutamic acid enantiomers using human serum albumin and sodium cholate as dual selectors. J. Sep. Sci. 2009, 32, 3184–3190. [Google Scholar] [CrossRef]
  7. Safronova, E.; Parshina, A.; Kolganova, T.; Bobreshova, O.; Pourcelly, G.; Yaroslavtsev, A. Potentiometric sensors arrays based on perfluorinated membranes and silica nanoparticles with surface modified by proton-acceptor groups, for the determination of aspartic and glutamic amino acids anions and potassium cations. J. Electroanal. Chem. 2018, 816, 21–29. [Google Scholar] [CrossRef]
  8. Adeosun, W.A.; Asiri, A.M.; Marwani, H.M.; Rahman, M.M. Enzymeless Electrocatalytic Detection of Uric Acid Using Polydopamine/Polypyrrole Copolymeric film. ChemistrySelect 2020, 5, 156–164. [Google Scholar] [CrossRef] [Green Version]
  9. Asiri, A.M.; Adeosun, W.A.; Marwani, H.M. Electrocatalytic reduction of 2, 6-dinitrophenol on polycongo red decorated glassy carbon electrode for sensing application. J. Environ. Chem. Eng. 2020, 8, 104378. [Google Scholar] [CrossRef]
  10. Adeosun, W.A.; Asiri, A.M.; Marwani, H.M. Real time detection and monitoring of 2, 4-dinitrophenylhydrazine in industrial effluents and water bodies by electrochemical approach based on novel conductive polymeric composite. Ecotoxicol. Environ. Saf. 2020, 206, 111171. [Google Scholar] [CrossRef]
  11. Gao, J.; Lv, D.; Sun, H.; Yang, W. Determination of L-aspartic acid by using the Cu(II)-catalyzed oscillating reaction. J. Braz. Chem. Soc. 2009, 20, 1827–1832. [Google Scholar] [CrossRef] [Green Version]
  12. Fontanarosa, C.; Pane, F.; Sepe, N.; Pinto, G.; Trifuoggi, M.; Squillace, M.; Errico, F.; Usiello, A.; Pucci, P.; Amoresano, A. Quantitative determination of free D-Asp, LAsp and N-methyl-D-aspartate in mouse brain tissues by chiral separation and Multiple Reaction Monitoring tandem mass spectrometry. PLoS ONE 2017, 12, e0179748. [Google Scholar] [CrossRef] [PubMed]
  13. Singh, N.; Singh, P.K.; Singh, M.; Gangopadhyay, D.; Singh, S.K.; Tandon, P. Development of a potential LPG sensor based on a PANI–Co3O4 nanocomposite that functions at room temperature. New J. Chem. 2019, 43, 17340–17350. [Google Scholar] [CrossRef]
  14. Mini, V.; Archana, K.; Raghu, S.; Sharanappa, C.; Devendrappa, H. Nanostructured multifunctional core/shell ternary composite of polyaniline-chitosan-cobalt oxide: Preparation, electrical and optical properties. Mater. Chem. Phys. 2016, 170, 90–98. [Google Scholar] [CrossRef]
  15. Li, S.J.; Xing, Y.; Yang, H.Y.; Huang, J.Y.; Wang, W.T.; Liu, R.T. Electrochemical synthesis of a binary Mn-Co oxides decorated graphene nanocomposites for application in nonenzymatic H2O2 sensing. Int. J. Electrochem. Sci. 2017, 12, 6566–6576. [Google Scholar] [CrossRef]
  16. Sharma, R.K.; Ghose, R. Synthesis of Co3O4–ZnO mixed metal oxide nanoparticles by homogeneous precipitation method. J. Alloys Compd. 2016, 686, 64–73. [Google Scholar] [CrossRef]
  17. Alam, M.M.; Asiri, A.M.; Uddin, M.T.; Inamuddin; Islam, M.A.; Awual, M.R.; Rahman, M.M. One-step wet-chemical synthesis of ternary ZnO/CuO/Co3O4 nanoparticles for sensitive and selective melamine sensor development. New J. Chem. 2019, 43, 4849–4858. [Google Scholar] [CrossRef]
  18. Zhang, X.; Zhang, Y.C.; Ma, L.X. One-pot facile fabrication of graphene-zinc oxide composite and its enhanced sensitivity for simultaneous electrochemical detection of ascorbic acid, dopamine and uric acid. Sensors Actuators, B Chem. 2016, 227, 488–496. [Google Scholar] [CrossRef]
  19. Ebrahimiasl, S.; Zakaria, A.; Kassim, A.; Basri, S.N. Novel conductive polypyrrole/zinc oxide/chitosan bionanocomposite: Synthesis, characterization, antioxidant, and antibacterial activities. Int. J. Nanomed. 2014, 10, 217–227. [Google Scholar] [CrossRef] [Green Version]
  20. Yang, Y.; Wang, X.; Yi, G.; Li, H.; Shi, C.; Sun, G.; Zhang, Z. Hydrothermal synthesis of co3 o4/zno hybrid nanoparticles for triethylamine detection. Nanomaterials 2019, 9, 1599. [Google Scholar] [CrossRef]
  21. Tak, Y.; Yong, K. A Novel Heterostructure of Co3O4/ZnO Nanowire Array Fabricated by Photochemical Coating Method. J. Phys. Chem. C 2008, 112, 74–79. [Google Scholar] [CrossRef]
  22. Mohamed Reda, G.; Fan, H.; Tian, H. Room-temperature solid state synthesis of Co3O4/ZnO p–n heterostructure and its photocatalytic activity. Adv. Powder Technol. 2017, 28, 953–963. [Google Scholar] [CrossRef]
  23. Liu, Y.; Zhu, G.; Chen, J.; Xu, H.; Shen, X.; Yuan, A. Co 3 O 4 /ZnO nanocomposites for gas-sensing applications. Appl. Surf. Sci. 2013, 265, 379–384. [Google Scholar] [CrossRef]
  24. Xu, J.; Liu, S.; Liu, Y. Co3O4/ZnO nanoheterostructure derived from core–shell ZIF-8@ZIF-67 for supercapacitors. RSC Adv. 2016, 6, 52137–52142. [Google Scholar] [CrossRef]
  25. Adeosun, W.A.; Asiri, A.M.; Marwani, H.M. Sensitive determination of 2-nitrophenol using electrochemically deposited polymethyl red film for healthcare and environmental safety. Synth. Met. 2020, 261, 116321. [Google Scholar] [CrossRef]
  26. Rakibuddin, M.; Ananthakrishnan, R. Porous ZnO/Co3O4 heteronanostructures derived from nano coordination polymers for enhanced gas sorption and visible light photocatalytic applications. RSC Adv. 2015, 5, 68117–68127. [Google Scholar] [CrossRef]
  27. Tabassum, S.; Usman, M.; Al-Lohedan, H.A.; Abdullah, M.M.S.; Ghanem, M.A.; Al-Sharif, M.S.; Ali, M.S. Synthesis of homo- And hetero-metallic cobalt and zinc nano oxide particles by a calcination process using coordination compounds: Their characterization, DFT calculations and capacitance behavioural study. RSC Adv. 2020, 10, 13126–13138. [Google Scholar] [CrossRef] [Green Version]
  28. Prabaharan, D.D.M.; Sadaiyandi, K.; Mahendran, M.; Sagadevan, S. Precipitation method and characterization of cobalt oxide nanoparticles. Appl. Phys. A Mater. Sci. Process. 2017, 123, 264. [Google Scholar] [CrossRef]
  29. Hussain, M.M.; Rahman, M.M.; Asiri, A.M.; Awual, M.R. Non-enzymatic simultaneous detection of l-glutamic acid and uric acid using mesoporous Co3O4 nanosheets. RSC Adv. 2016, 6, 80511–80521. [Google Scholar] [CrossRef]
  30. Al-Senani, G.M.; Deraz, N.M.; Abd-Elkader, O.H. Magnetic and characterization studies of CoO/Co3O4 nanocomposite. Processes 2020, 8, 844. [Google Scholar] [CrossRef]
  31. Geetha, M.S.; Nagabhushana, H.; Shivananjaiah, H.N. Green mediated synthesis and characterization of ZnO nanoparticles using Euphorbia Jatropa latex as reducing agent. J. Sci. Adv. Mater. Devices 2016, 1, 301–310. [Google Scholar] [CrossRef] [Green Version]
  32. Estrada-Urbina, J.; Cruz-Alonso, A.; Santander-González, M.; Méndez-Albores, A.; Vázquez-Durán, A. Physiological and sanitary quality of a Mexican landrace of red maize. Nanomaterials 2018, 8, 247. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  33. Cordeiro, T.A.R.; Gonçalves, M.V.C.; Franco, D.L.; Reis, A.B.; Martins, H.R.; Ferreira, L.F. Label-free electrochemical impedance immunosensor based on modified screen-printed gold electrodes for the diagnosis of canine visceral leishmaniasis. Talanta 2019, 195, 327–332. [Google Scholar] [CrossRef]
  34. Zhu, X.; Zhang, K.; Wang, D.; Zhang, D.; Yuan, X.; Qu, J. Electrochemical sensor based on hydroxylated carbon nanotubes/platinum nanoparticles/rhodamine B composite for simultaneous determination of 2,4,6-trichlorophenol and 4-chlorophenol. J. Electroanal. Chem. 2018, 810, 199–206. [Google Scholar] [CrossRef]
  35. Kuralay, F.; Dumangöz, M.; Tunç, S. Polymer/carbon nanotubes coated graphite surfaces for highly sensitive nitrite detection. Talanta 2015, 144, 1133–1138. [Google Scholar] [CrossRef]
  36. Ahmed, J.; Rakib, R.H.; Rahman, M.M.; Asiri, A.M.; Siddiquey, I.A.; Islam, S.S.M.; Hasnat, M.A. Electrocatalytic Oxidation of 4-Aminophenol Molecules at the Surface of an FeS2/Carbon Nanotube Modified Glassy Carbon Electrode in Aqueous Medium. Chempluschem 2019, 84, 175–182. [Google Scholar] [CrossRef] [PubMed]
  37. Adeosun, W.; Asiri, A.M.; Marwani, H.M. Fabrication of conductive polypyrole doped chitosan thin film for sensitive detection of sulfite in real food and biological samples. Electroanalysis 2020, 32, 1725–1736. [Google Scholar] [CrossRef]
  38. Rahman, M.M.; Adeosun, W.A.; Asiri, A.M. Fabrication of Flower-Flake La2ZnO4 Nanocomposite for Effective Non-Enzymatic Sensing of Hydrogen Peroxide. Microchem. J. 2020, 159, 105536. [Google Scholar] [CrossRef]
  39. Soleimani-Lashkenari, M.; Rezaei, S.; Fallah, J.; Rostami, H. Electrocatalytic performance of Pd/PANI/TiO2 nanocomposites for methanol electrooxidation in alkaline media. Synth. Met. 2018, 235, 71–79. [Google Scholar] [CrossRef]
  40. Karimi-Maleh, H.; Arotiba, O.A. Simultaneous determination of cholesterol, ascorbic acid and uric acid as three essential biological compounds at a carbon paste electrode modified with copper oxide decorated reduced graphene oxide nanocomposite and ionic liquid. J. Colloid Interface Sci. 2020, 560, 208–212. [Google Scholar] [CrossRef]
  41. Asiri, A.M.; Adeosun, W.A.; Marwani, H.M.; Rahman, M.M. Homopolymerization of 3-aminobenzoic acid for enzyme-free electrocatalytic assay of nitrite ions. New J. Chem. 2020, 44, 2022–2032. [Google Scholar] [CrossRef]
  42. Goseer, D.K. Cyclic Voltametry-Simulation and Analysis of Reaction; VCH: New York, NY, USA, 1993; ISBN 3-527-28226-2. [Google Scholar]
  43. Bard, G.A.; Inzelt, F.S. Electrochemistry Dictionary; Springer: Berlin/Heidelberg, Germany, 2008. [Google Scholar]
  44. Bard, A.J.; Faulkner, L.R. Electrochemical Methods: Fundamentals and Applications, 2nd ed.; Wiley: New York, NY, USA, 2001. [Google Scholar]
  45. Asiri, A.M.; Adeosun, W.A.; Rahman, M.M. Development of highly efficient non-enzymatic nitrite sensor using La2CuO4 nanoparticles. Microchem. J. 2020, 159, 105527. [Google Scholar] [CrossRef]
  46. Zhang, Y.; Cao, J.; Ding, L. Fluorescent ensemble based on dansyl derivative/SDS assemblies as selective sensor for Asp and Glu in aqueous solution. J. Photochem. Photobiol. A Chem. 2017, 333, 56–62. [Google Scholar] [CrossRef]
  47. Weng, H.; Yan, B. A sliver ion fabricated lanthanide complex as a luminescent sensor for aspartic acid. Sens. Actuators B Chem. 2017, 253, 1006–1011. [Google Scholar] [CrossRef]
  48. Wu, P.; Jiang, M.; Hu, X.; Wang, J.; He, G.; Shi, Y.; Li, Y.; Liu, W.; Wang, J. Amide-containing luminescent metal–organic complexes as bifunctional materials for selective sensing of amino acids and reaction prompting. RSC Adv. 2016, 6, 27944–27951. [Google Scholar] [CrossRef]
  49. Zhao, X.; Wei, R.; Chen, L.; Jin, D.; Yan, X. Glucosamine modified near-infrared cyanine as a sensitive colorimetric fluorescent chemosensor for aspartic and glutamic acid and its applications. New J. Chem. 2014, 38, 4791–4798. [Google Scholar] [CrossRef]
  50. Das, S.; Guha, S.; Banerjee, A.; Lohar, S.; Sahana, A.; Das, D. 2-(2-Pyridyl) benzimidazole based Co(ii) complex as an efficient fluorescent probe for trace level determination of aspartic and glutamic acid in aqueous solution: A displacement approach. Org. Biomol. Chem. 2011, 9, 7097–7104. [Google Scholar] [CrossRef]
  51. Ranjani, M.; Kalaivani, P.; Dallemer, F.; Selvakumar, S.; Kalpana, T.; Prabhakaran, R. Fluorescent Cu(II) complex as chemosensor for the detection of l-Aspartic acid with high selectivity and sensitivity. Inorg. Chim. Acta 2022, 530, 120683. [Google Scholar] [CrossRef]
  52. Alam, M.M.; Asiri, A.M.; Hasnat, M.A.; Rahman, M.M. Detection of L-Aspartic Acid with Ag-Doped ZnO Nanosheets Using Differential Pulse Voltammetry. Biosensors 2022, 12, 379. [Google Scholar] [CrossRef]
  53. Wei, X.; Chen, Y.; He, S.; Lian, H.; Cao, X.; Liu, B. Bovine serum albumin-coated titanium dioxide modified electrochemical interface for enantioselective discrimination of D/L-aspartic acid. Chirality 2021, 33, 731–744. [Google Scholar] [CrossRef]
Biosensors 13 00088 g001 550
Figure 1. Morphological and elemental analyses. (a–c) FESEM images of Co3O4-ZnO. (d) XEDS spectrum of Co3O4-ZnO.
Figure 1. Morphological and elemental analyses. (a–c) FESEM images of Co3O4-ZnO. (d) XEDS spectrum of Co3O4-ZnO.
Biosensors 13 00088 g001
Biosensors 13 00088 g002 550
Figure 2. Optical, functional and structural analyses. (a) Full XPS spectrum of Co3O4-ZnO nanorod. (b) Deconvoluted peak of oxygen. (c) Deconvoluted peak of cobalt. (d) Deconvoluted peak of zinc. (e) XRD spectrum of Co3O4-ZnO nanorod. (f) Obtained UV-Vis spectrum for Co3O4-ZnO nanorod. (g) FTIR spectrum of Co3O4-ZnO nanorod.
Figure 2. Optical, functional and structural analyses. (a) Full XPS spectrum of Co3O4-ZnO nanorod. (b) Deconvoluted peak of oxygen. (c) Deconvoluted peak of cobalt. (d) Deconvoluted peak of zinc. (e) XRD spectrum of Co3O4-ZnO nanorod. (f) Obtained UV-Vis spectrum for Co3O4-ZnO nanorod. (g) FTIR spectrum of Co3O4-ZnO nanorod.
Biosensors 13 00088 g002
Biosensors 13 00088 g003 550
Figure 3. (a) Cyclic voltammetric response of Co3O4−ZnO nanorod modified GCE in 1 mM Fe (CN)63−/4− at the scan rate of 75 mV/s. (b) EIS spectrum of Co3O4−ZnO nanorod in 0.1 M PBS 5.7/0.1 µM aspartic acid.
Figure 3. (a) Cyclic voltammetric response of Co3O4−ZnO nanorod modified GCE in 1 mM Fe (CN)63−/4− at the scan rate of 75 mV/s. (b) EIS spectrum of Co3O4−ZnO nanorod in 0.1 M PBS 5.7/0.1 µM aspartic acid.
Biosensors 13 00088 g003
Biosensors 13 00088 g004 550
Figure 4. (a) Current response of Co3O4−ZnO nanorod modified GCE and bare GCE in PBS with/without presence of AA. (b) Current response of Co3O4−ZnO nanorod in PBS/AA at different pHs. (c) Current response of Co3O4−ZnO nanorod in PBS/AA at different scan rates (25–425 mV/s). (d) Plot of square root of scan rate versus oxidation peak current. (e) Plot of logarithm of oxidation peak current versus logarithm of scan rate.
Figure 4. (a) Current response of Co3O4−ZnO nanorod modified GCE and bare GCE in PBS with/without presence of AA. (b) Current response of Co3O4−ZnO nanorod in PBS/AA at different pHs. (c) Current response of Co3O4−ZnO nanorod in PBS/AA at different scan rates (25–425 mV/s). (d) Plot of square root of scan rate versus oxidation peak current. (e) Plot of logarithm of oxidation peak current versus logarithm of scan rate.
Biosensors 13 00088 g004
Biosensors 13 00088 g005 550
Figure 5. (a) Current response of Co3O4−ZnO nanorod modified GCE, increasing with AA concentration. (b) Plot of oxidation peak current against varying AA concentration. (c) Current response of Co3O4−ZnO nanorod in 0.05 µM AA taken 10 consecutive times. (d) Current response of Co3O4−ZnO nanorod in 0.05 µM AA with/without likely interfering species (glutamic acid, leucine, ascorbic acid, uric acid, glucose, melamine, nitrite and Zn2+).
Figure 5. (a) Current response of Co3O4−ZnO nanorod modified GCE, increasing with AA concentration. (b) Plot of oxidation peak current against varying AA concentration. (c) Current response of Co3O4−ZnO nanorod in 0.05 µM AA taken 10 consecutive times. (d) Current response of Co3O4−ZnO nanorod in 0.05 µM AA with/without likely interfering species (glutamic acid, leucine, ascorbic acid, uric acid, glucose, melamine, nitrite and Zn2+).
Biosensors 13 00088 g005
Table
Table 1. Results of real sample analysis with a Co3O4-ZnO nanorod by the electrochemical method.
Table 1. Results of real sample analysis with a Co3O4-ZnO nanorod by the electrochemical method.
Sample TypeN/ASpiked (µM)Found (µM)RSD (%)BiasRecovery (%)
Beverage drink30 µMN.DN.D-N.D
350 µM47.2 ± 1.483.14−2.894.4
Mouse serum30 µMN.DN.DN.DN.D
350 µM43.8 ± 1.733.95−6.287.6
N.D: not detected; N/A: number of analyses.
Table
Table 2. Earlier-reported methods for the detection of aspartic acid and their analytical performance.
Table 2. Earlier-reported methods for the detection of aspartic acid and their analytical performance.
Sensing MatrixMethodLOD (µM)# LR (µM)Ref.
Dansyl derivative/SDSFluorescence0.600.04–0.8mM[46]
Lanthanide complexFluorescence0.460.1–1000[47]
Bifunctional materialsFluorescence0.260.1–133[48]
N-Doped carbonFluorescence0.090.5–50[1]
Glucosamine-cyanine probeFluorescence-0.1–10[49]
2-(2-pyridyl) benzimidazoleFluorescence1010–300[50]
Flurescent Cu (II) ionFluorescence0.0841–10[51]
Ag2O/ZnOElectrochemical3.515–105[52]
Polymer/MWCNTsElectrochemical4.08 ng/mL3.89–66.23[2]
Bolvin-serum/TiO2/GCEElectrochemical0.009-[53]
Co3O4-ZnO/GCEElectrochemical0.030.05–50Current study
# LR: linear range.
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Alfaifi, S.Y.; Adeosun, W.A.; Asiri, A.M.; Rahman, M.M. Sensitive and Rapid Detection of Aspartic Acid with Co3O4-ZnO Nanorods Using Differential Pulse Voltammetry. Biosensors 2023, 13, 88. https://doi.org/10.3390/bios13010088

AMA Style

Alfaifi SY, Adeosun WA, Asiri AM, Rahman MM. Sensitive and Rapid Detection of Aspartic Acid with Co3O4-ZnO Nanorods Using Differential Pulse Voltammetry. Biosensors. 2023; 13(1):88. https://doi.org/10.3390/bios13010088

Chicago/Turabian Style

Alfaifi, Sulaiman Y., Waheed Abiodun Adeosun, Abdullah M. Asiri, and Mohammed M. Rahman. 2023. "Sensitive and Rapid Detection of Aspartic Acid with Co3O4-ZnO Nanorods Using Differential Pulse Voltammetry" Biosensors 13, no. 1: 88. https://doi.org/10.3390/bios13010088

APA Style

Alfaifi, S. Y., Adeosun, W. A., Asiri, A. M., & Rahman, M. M. (2023). Sensitive and Rapid Detection of Aspartic Acid with Co3O4-ZnO Nanorods Using Differential Pulse Voltammetry. Biosensors, 13(1), 88. https://doi.org/10.3390/bios13010088

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop