1. Introduction
The global demand for mineral fertilizers, particularly those based on nitrogen, is constantly increasing due to the growing population and demand for food [
1]. The most commonly used solid fertilizers based on ammonium nitrate are CAN (calcium ammonium nitrate) and AN (ammonium nitrate). The popularity of these fertilizers stems primarily from the possibility of obtaining high nitrogen content in the product. As nitrogen plays a very important role in the plant growth processes, there is a high demand for fertilizers containing this element in high concentration in granulate [
2].
The physicochemical properties of ammonium nitrate include explosiveness, water solubility, and high hygroscopicity. Ammonium nitrate occurs in different phase variations, which affect the behavior of the fertilizers based on this compound during storage, particularly in conditions of high humidity of both air and the product itself, as well as variable temperature. Such properties of ammonium nitrate contribute to the phenomenon of caking, an undesirable effect observed in nitrate fertilizers [
3,
4,
5]. The phenomenon of granule caking of ammonium nitrate fertilizers is associated with the occurrence of cohesion, affected by the aforementioned physicochemical properties, as well as the storage conditions of the fertilizer. Another factor that determines the susceptibility of nitrogen fertilizers to the caking process is their composition. Furthermore, the shape and size of the granules in these fertilizers determine the tendency of caking, which is directly related to the contact surface between the granules during their transport and storage. As a consequence of caking, the performance of fertilizers deteriorates, rendering their storage difficult. In addition, caked fertilizers result in material loss and impose additional costs, because they cannot be equally dosed without additional works [
5,
6,
7]. Modification of ammonium nitrate surface using coatings (chemical, physical, and encapsulation coating) may reduce hygroscopicity, as described in the literature [
8].
Caking can be prevented in several ways, yet the most common anti-caking method currently used involves coating the prepared granules with an anti-caking agent. In addition, caking increases the propensity of ammonium nitrate to explode when forced by external factors. Therefore, precautionary measures should be taken to reduce the possibility of the occurrence of these negative phenomena. By preventing caking, the quality of ammonium nitrate fertilizers as well as public safety can be improved [
3]. A literature and patent overview showed that the composition of products such as fertilizers is carefully selected by their manufacturers depending on the properties and intended application [
9].
Nowadays, polymer coatings are increasingly proposed, related to the production of slow-release fertilizers (SRFs) and controlled-release fertilizers (CRFs). Furthermore, the application of such coatings on nitrate fertilizer granules restricts their tendency of caking. Thus far, the effects of coatings composed of, among others, polysulfone, cellulose acetate, and polyacrylonitrile have been described. Polymer coatings were applied on fertilizer granules that represent three of the macro-nutrients, nitrogen, phosphorus and potassium (NPK fertilizer), using the phase inversion method. It was determined that increased polymer contribution in the coating mixture reduces the coating porosity, which may be undesirable and highly hazardous due to the decomposition of ammonium nitrate. Therefore, only low amounts of the polymer can be used in the preparation of anti-caking coatings for nitrate fertilizers, while ensuring reduced contact between granules and maintaining appropriate coating porosity [
10,
11]. Research is underway on controlled-release coatings for urea, including particles with bio-based epoxy. The bio-based epoxy was fabricated with liquefied bagasse used as a green coating material for CRF [
12]. In another study, urea with SRF was obtained by coating with polyurethane. Polyurethane was prepared from fully vegetable oil-based polyols and polymethylene polyphenylene isocyanate. The vegetable oil content was 70% in the polyurethane film of SRFs. Additionally, the films had excellent degradability [
13].
However, fertilizers based on ammonium nitrate require slightly different coatings from those used for NPK fertilizers and urea, and several alternative additives have been successfully tested to prevent their caking. These additives include calcium trialkylamine, dimethyl decylamine, potassium dimethyloctylamine, and dimethyl laurylamine [
14]. Other studies have shown that a mixture of mineral oil and slack wax together with high-molecular-weight polyisobutylene additives significantly reduces water absorption and the dust-generating tendency of ammonium nitrate fertilizers [
15]. A reduction in moisture adsorption has also been noticed when additives such as potassium alkyl sulfate, sodium alkyl sulfate, and mono-, di, and triethanolammonium alkyl sulfate were used for nitrate fertilizers [
16]. In addition, it has been reported that coating of nitrogenous fertilizers with bitumen reduced the absorption of moisture by fertilizer granules [
17]. Recently, research was carried out to minimize moisture absorption by ammonium nitrate-based fertilizers by introducing additives such as silicicic acid, calcium lignosulfonate, and sodium silicate in a two-stage vacuum process used for the production of ammonium nitrate [
18]. A patent review has shown that most of the anti-caking preparations have slack waxes in their composition.
The negative environmental impact of oil-derived polymeric materials and depletion of oil resources is currently a significant concern. This necessitates the replacement of oil-based polymeric materials with bio-based polymers obtained from abundant renewable materials and the replacement of petroleum-based raw materials with other more environmentally friendly substances [
19,
20].
The aim of this work was to demonstrate the influence of composition and physicochemical properties of the anti-caking agents commercially used as coatings for ammonium nitrate-based fertilizers on their effectiveness, in order to develop innovative organic coatings of similar or higher efficiency but with a reduced negative environmental impact.
3. Results and Discussion
3.1. Physical and Chemical Parameters of Anti-Caking Agents
Table 2 presents the determined physical and chemical parameters of anti-caking agents. The parameters of each formulation were analyzed to investigate the relationship between their physical and chemical characteristics and their effectiveness to prevent the caking of ammonium nitrate-based fertilizers. The water content of the anti-caking agents can directly increase the water content in the granules of the fertilizers they cover. Taking into account the hygroscopicity of ammonium nitrate fertilizers, and thus their tendency of caking, it is necessary to maintain a low water content in the final fertilizer product. This is therefore a test parameter and is likely to have a large impact on the anti-caking effect in fertilizers. The A2 preparation contained the least water content (0.04%). The anti-caking agents A1 and A2 had a similar density, melting point, and BN. However, they differed significantly in viscosity. The lowest viscosity was found in preparation A2 (8.0 mPa·s) and the highest in A3 (17.0 mPa·s). BN is the amount of potassium hydroxide (in milligrams) determined as equivalent in terms of the acid neutralization capacity of alkaline additives contained in 1 g of anti-caking preparations and was used to assess the content of alkaline additives in the test preparations. The results obtained showed that A3 had a lower BN (18.8 mg KOH/g) than the other anti-caking agents (22.8 and 22.2 mg KOH/g).
3.2. GC–MS Analysis
Chromatographic analysis was performed on the three commercial anti-caking agents dedicated to ammonium nitrate fertilizers. The spectra of these preparations are shown in
Figure 1. It can be seen that all three anti-caking agents were relatively similar. Preparation A1 had most of the peaks with a retention time of 5–15 min. In this area, all preparations had several characteristic peaks with the same retention time but with different signal intensities. Additionally, a wide band with a retention time of 20–30 min can be found for all compounds. On the basis of the MS library database, three compounds were identified in the tested preparations and their samples were purchased. GC–MS analysis was also performed for these compounds to confirm their presence and determine their content in the individual studied anti-caking agents.
Table 3 shows the compounds identified based on the MS library database in particular anti-caking agents.
Figure 2 shows the chromatograms of the standard compounds. Their concentrations were adjusted to be comparable with those of specific compounds in the initial preparations. The obtained chromatograms confirmed the presence of compounds identified based on MS in the commercial anti-caking agents.
A wide range of peaks with a retention time of 20–30 min probably resulted from slack wax. Therefore, a GC–MS/FID analysis of slack wax of hydrocarbons C16–C48 (
Figure 3) was conducted.
Table 4 presents the quantitative analysis results of the identified compounds in mass %.
The composition analysis results of the commercial anti-caking agents showed that all the tested preparations contained hexadecylamine and octadecylamine in comparable amounts. Only in preparation A1, there were more unidentified compounds and a high amount of stearic acid. A less amount of hydrocarbon base was present in this agent. Hexadecylamine and octadecylamine probably originated from the commercial fatty amine with the hydrocarbon chain C16–C18, and additionally identified compounds, such as stearic acid, were also included (at least in some amount) in the commercial fatty amines used.
3.3. Effectiveness of Anti-Caking Agents
All anti-caking agents were found to be very effective in protecting the granules of AN fertilizers against clumping. Effectiveness of anti-caking agents are listed in
Table 5. A2 turned out to be the best (for both AN and CAN), but the differences were very small. In addition, it should be noted that all three commercial anti-caking agents protected AN very well against clumping, but CAN very poorly. This is due to the fact that CAN has a lower critical humidity value, which resulted in higher clumping of this fertilizer. Therefore, it is probably very difficult to choose the right coating to prevent caking. This confirms that not only the anti-caking agent but also the quality and composition of the fertilizer are of key importance. After 10 days of storage, the effectiveness of anti-caking agents decreased and then increased after 1 month of storage. Similar conclusions were drawn from earlier studies [
21].
The decrease in effectiveness is due to the presence of water in the granule. The water concentration at the surface of the granule is different than that on the inside. During storage, water is evenly distributed in the whole granule, and then it is partly evaporated in the storehouse and partly bound in the hydrates. During the storage of fertilizer granules, some reactions take place, which are related to dolomite contamination, migration of the solvent (water), and the action of a strong oxidant (ammonium nitrate). In addition, if such a granule was coated with an anti-caking agent, changes occur in the chemical activity of the components used for its composition. Hence, after a few days, the effectiveness of anti-caking agents decreases compared to that observed immediately after coating the granules. However, after a month, the effectiveness increases and becomes higher than that observed immediately after granule coating.
A very similar composition of the preparations indicates that the key compounds in them are fatty amines and hydrocarbon base, which is the main component by mass. This was already confirmed by the patent review.
The A2 preparation, which was found to be the best, had the lowest viscosity (8.0 mPa·s) and the lowest water content (0.04%). Water content is crucial for a preparation to have good effectiveness as water is involved in the process of granule clumping. The remaining parameters of all preparations were comparable. A significant difference was observed between the preparations in viscosity (8.0–17.0 mPa·s). The research shows that the most optimal viscosity for the tested preparations is about 8 mPa·s.
4. Conclusions
The aim of this work was to examine the composition and physicochemical parameters of commercial anti-caking preparations and to determine the effectiveness of these anti-caking agents in preventing the caking of fertilizers (AN, CAN) coated with them. The study also determined the influence of particular parameters and composition on the effectiveness of protecting fertilizers based on ammonium nitrate against caking. The research was intended to create innovative formulations of anti-caking agents using more environmentally friendly raw materials. Moreover, by preventing the caking of ammonium nitrate fertilizers, it is possible to reduce the propensity of ammonium nitrate to explode when forced by external factors. The conducted research confirmed the data on the composition indicated by the patent review. It was found that the tested anti-caking agents contained hexadecylamine, octadecylamine, and stearic acid, which are the compounds likely to be a part (at least in some amount) of the commercial C16–C18 fatty amines used. The largest part of the preparations was the hydrocarbon base from slack waxes. The composition and physicochemical parameters of the anti-caking preparations showed that their effectiveness in protecting caking was greatly influenced by the water content, appropriate viscosity and appropriate content of fatty amines in them, and the quality and type of fertilizer. Fat amines are a crucial component in anti-caking preparations for ammonium nitrate fertilizers due to their amphiphilic character.
The tests carried out allowed the parameters that influenced the effectiveness of the anti-caking preparations to be determined. The presented results will help to develop new coatings for more environmentally friendly fertilizers based on ammonium nitrate.