1. Introduction
Ceramic materials are often used as high-temperature structural materials. In extreme high-temperature environments, ceramic materials need to withstand complex loads and environments such as force and stress cycling, environmental media erosion and scouring, and thermal shocks [
1]. Due to the inherent brittleness of ceramics, the thermal stresses caused by temperature differences during rapid warming or thermal shock from high temperatures can lead to the development and rapid propagation of microcracks, resulting in a sudden decay in material strength [
2], which seriously affects the reliability of critical thermal protection structures and limits the practical application of ceramic materials as high-temperature materials. The existence and propagation of cracks is the main cause of fracture of brittle materials [
3]; therefore, the study of the influence of microcrack propagation on the thermal shock resistance of ceramic materials and the exploration of methods to inhibit the propagation of microcracks are key issues that need to be urgently addressed to improve the thermal shock resistance of ceramics.
Based on the thermal shock fracture theory (TSF) and thermal shock damage theory (TSD), Duan et al. [
4] developed a modified thermal shock model that takes into account the variation of material properties with temperature to reveal the thermal shock damage mechanism of ceramic materials in terms of their temperature characteristics. Luo et al. [
5] used ABAQUS finite element software to simulate the generation and propagation of cracks in the indentation zone during microhardness testing of ultrafine crystalline Si
2N
2O-Si
3N
4 ceramics. Li et al. [
6] constructed a fine-scale damage mechanics model to simulate the interaction between thermal impact cracks and prefabricated cracks, extending the study of the thermal impact damage mechanism of ceramics. While the mechanisms of crack generation and propagation have been studied above, Qi et al. [
7] investigated the effect of thermal shock-induced crack propagation on the residual strength of ceramics in terms of fractal geometry, calculated the fractal dimension of thermal shock cracks by the box-counting method, and explained the relationship between crack length and fractal dimension using the fractal energy of microcrack fractal patterns in quasi-brittle solids. Ricco et al. [
8] investigated the effect of microstructure and surface energy on subcritical crack propagation in microcrystalline glass and found that stress corrosion cracking in microcrystalline glass is due to a combination of surface energy and microstructural features. Quan et al. investigated fatigue cracking of metallic materials [
9] and fatigue cracking of bonded joints under type I loading [
10], and verified that crack expansion causes energy dissipation.
It was found that thermal shock cracks in ceramic materials generally have a fractal structure, and the spatial distribution information of cracks is considered when performing fractal characterization of microcracks. The multifractal spectrum of crack propagation after the thermal shock of ceramic materials was calculated to obtain the complexity of crack propagation and spatial distribution characteristics, which can better characterize the non-regular and non-uniform characteristics of cracks. Zhu et al. [
11] used multiple fractals to study random fracture crack networks, providing a possible solution for the study of more complex surface topographies. Ji et al. [
12] used multiple fractals to characterize the phase structure of abradable layers on material surfaces and analyze the high-speed scraping behavior of material surfaces. Pan [
13] and others used multifractal spectra to make up for the shortcomings of traditional methods in revealing the heterogeneity of crack distribution in describing concrete cracks, verified that multifractal spectra can distinguish the subtle differences between two similar concrete crack distributions, and provided a new idea for assessing the damage of concrete structures. Butenko et al. [
14] carried out a multifractal analysis on nitinol glass annealed at different temperatures, counted its surface characteristics, and verified the possibility of detecting system phase transition in crystalline form. Martsepp et al. [
15] irradiated pure tungsten samples with high-temperature deuterium plasma at different times and compared the multifractal spectrum of the sample surface with the Fourier spectrum. The multifractal spectrum of the surface can determine the time dependence of surface damage. Feng et al. [
16] studied the crack propagation and internal fracture process of coal under dynamic load and verified that the crack propagation and internal fracture surface of coal have multifractal characteristics, indicating that the multifractal characteristics can be used to evaluate the brittleness of coal under dynamic load and predict the coal failure risk of underground coal mines. Jouini et al. [
17] used multiple fractals to allow the classification of rock samples according to their degree of inhomogeneity. Astinchap et al. [
18] evaluated chest computed tomography (CT) images of 2019 patients with novel coronavirus disease (neo-coronavirus pneumonia) by multiple fractal techniques, and Tsvetkov et al. [
19] used multiple fractals to develop a kinetic model of the neo-coronavirus pandemic. This shows that multifractals are widely used in various disciplines.
Multifractals have good application prospects in terms of characterizing the surface characteristics of materials and analyzing the fracture process. Therefore, this paper will extract crack characteristics through a multifractal spectrum. Although multifractal spectra can effectively characterize the cracks, they still need a method to learn these characteristics and to objectively identify similar characteristics. Deep learning has excelled in solving many problems such as image target recognition, speech recognition, and natural language processing, avoiding problems such as the subjective influence of manually extracted features and the limited expressiveness of shallow network structures. Among the various types of neural networks, convolutional neural networks have been the most intensively studied. The basic structure of a Convolutional Neural Network (CNN) consists of an input layer, a convolutional layer, a pooling layer, a fully connected layer, and an output layer, and the emergence of large-scale labeled data, such as those found on ImageNet, and the rapid improvement of GPU computing performance have advanced the research on convolutional neural networks. In particular, after the introduction of the AlexNet [
20] network model in 2012, convolutional neural networks have been developed at a high speed, and subsequent convolutional neural network models such as Visual Geometry Group Network (VGG), GoogleNet, Residual Network (ResNet), etc., have emerged.
Li et al. [
21] proposed a new method based on multifractal theory, sequence feature fusion, and an improved probabilistic neural network, which improved the vibration identification performance of the perimeter system of the dual Mach Zehnder interferometer. The feature of the original signal is extracted in the form of multifractal spectra and associated with a probabilistic neural network, which realizes the beneficial fusion of multifractal theory and the probabilistic neural network. Therefore, this paper also integrates multifractal spectra into deep learning algorithms, establishes a correlation model between crack propagation fractal characteristics and the thermal shock damage degree based on multifractal spectra and deep learning, and verifies the validity of the model through thermal shock experiments. The purpose of this study was to realize the combination of nonlinear geometric methods, artificial intelligence methods, and thermal shock damage characterization of composite materials.
4. Discussion
On account of its unique properties, the multifractal spectrum can provide a detailed description of surfaces with complex morphological conditions. In this paper, we characterize the complexity and self-similarity of crack images by calculating the multifractal spectra of crack images, analyzing them from a fractal perspective, combining information on the spatial distribution of cracks with their non-linear characteristics, and converting each set of multifractal spectra into a chromaticity map to visualize the distribution pattern of cracks and the details of complex cracks.
By performing multifractal spectrum calculations on a large number of crack images and observing their chromaticity maps, it is found that the location, width, and bifurcation of the cracks affect the calculation results of the multifractal spectrum, which also verifies that even some minor features on the surface can be faithfully characterized by the multifractal. Based on the results of Qi [
7], the fracture energy of microcrack fractal patterns in quasi-brittle solids can be used to explain the relationship between crack length and fractal dimension. If the crack propagation has the same crack length but a larger fractal dimension, it will absorb more energy. The relationship between the crack energy and the corresponding value of the singularity index, the singularity spectrum, can also be observed from the chromaticity diagram obtained in this paper.
The resulting chromaticity map was input into a deep learning model for training tests, and initially, the recognition accuracy peaked at 70.26%. By increasing the number of cut rows, enhancing the amount of data in the dataset, and model fusion, the recognition rate was increased to 87.50%.
In deep learning, evaluation metrics such as accuracy, precision, recall, and the F1-measure are generally used to evaluate a model.
Table 4 shows the confusion matrix, where TP (True Positive), FP (False Positive), FN (False Negative), and TN (True Negative) are the number of samples in each case.
The formulae for calculating each indicator are as follows [
23]:
These evaluation metrics are usually applied to dichotomous problems. For the multi-classification problems in this paper, both macro-averaging and micro-averaging methods are generally used to calculate each evaluation indicator.
This paper is a four-category problem, where each evaluation indicator
,
, and
is first calculated for category
, where category
is treated as a positive category and the remaining categories as negative categories. The macro-average is calculated as follows [
24]:
The micro-average is calculated as follows [
24]:
Macro-averaging is essentially obtained by averaging the indicators, but this tends to ignore the uneven distribution between samples, which can be compensated for by micro-averaging. A combination of both macro-averaging and micro-averaging allows for a better evaluation of the model.
The final recognition accuracy of the deep learning model was 87.5%, through Equations (6)–(9), we calculated the evaluation indexes for each classification, then the macro-averaging and micro-averaging for each evaluation index are calculated by Equations (10)–(15), as shown in
Table 5. From the evaluation indexes in the table, it can be seen that the evaluation indexes of the model are stable at 87.5%, so the model is reasonable and the results are in line with expectations. The evaluation indicators under the micro-average and macro-average are the same, and this shows that the data in the sample are well-distributed in all categories.
In this paper, multiple fractal spectroscopy is used to characterize cracks at the fractal level and extract crack features. At the same time, multiple fractal spectroscopy is combined with deep learning to achieve automatic recognition and classification of a large number of crack images and to improve their efficiency, accuracy, and repeatability. The chromaticity diagram of the singularity index and the singularity spectrum are obtained using the multiple fractal spectra, which, on the one hand, verifies that the relationship between the crack and fractal dimensions can be explained in terms of energy, and on the other hand, provides a data set for deep learning.
By combining multiple fractal spectroscopy with deep learning, a correlation model between microcrack propagation and thermal impact properties based on multifractal spectra and deep learning is constructed. A novel idea is developed in the study of material damage mechanisms. Crack features are extracted from the fractal level, and then the generalization ability of deep learning is used to transform the extracted features into scientific and reasonable data, to realize the final automatic classification and recognition.
5. Conclusions
This paper uses a combination of experimental evidence, multifractal theory, and deep learning to propose a characterization method for ceramic thermal shock cracks. A correlation model between microcrack propagation and thermal shock performance based on multifractal spectra and deep learning was constructed, which mainly leads to the following conclusions:
(1) Calculation of the multiple fractal spectra of different crack images, conversion of the values of the singularity index and singularity spectra in the multiple fractal spectra into chromaticity diagrams, verification of the relationship between the crack and fractal dimensions that can be explained from the energy point of view, and characterization of thermal shock cracks in ceramics from the fractal level are possible.
(2) The chromaticity map of thermal shock crack images obtained under different thermal shock temperatures was input into the deep learning model. The final recognition accuracy of the crack images was 87.50%, verifying that the model can effectively identify the class of its crack images under different propagation cases, improving the recognition accuracy of the crack images from the fractal level, highlighting the crack features, and extending the research on this kind of complex, non-uniform and non-linear geometric morphology. This provides new research ideas.
(3) This paper focuses on the classification and identification of static crack images. Future research can combine the crack propagation mechanisms to achieve the identification of the dynamic process of crack propagation, predict the crack propagation process, and monitor the health of materials and components in real time to enable targeted repair in advance, reduce costs and avoid accidents.