1. Introduction
Fracture media have good fractal characteristics. The fractal dimension of the fracture body, surface fractal dimension, and axis fractal dimension can greatly reduce the complexity and dispersion of the test process. Under the action of an arid climate, the soil will have significant shrinkage deformation and cracking, which will directly lead to natural disasters such as land subsidence and water and soil loss, and have a great negative impact on the stability of surface infrastructure and underground engineering structures [
1,
2]. In many parts of the world, large-scale cracking and damage of infrastructure such as houses, roads, and bridges have occurred due to severe drought, resulting in huge economic losses [
3,
4]. China is a country with the most serious extreme climate events and disasters in the world, and there are many kinds—high-intensity, high-frequency, and serious harm [
5,
6]. The research data of the China Meteorological Administration show that the frequency and scope of extreme weather events such as mass or regional high temperatures, rainstorms, and droughts will increase significantly, and that the disaster risk will increase for a long time in the future. Especially in recent decades, the number and scale of major engineering construction projects in China have been increasing [
7,
8]. Drought extreme climate events will lead to geological disasters by affecting major engineering facilities themselves and important auxiliary facilities, especially the engineering geological environment relied upon by major projects, thus further affecting the safety, stability, reliability, and durability of the project; it also has an important impact on the operation efficiency and economic benefits of major projects.
Extreme arid climate disasters change the surface rock and soil temperature field, structure field, and material field, especially the water field, through various action modes, and then they change the engineering geological characteristics of the rock and soil mass, and cause disasters [
9]. The continuous water evaporation caused by an arid climate will also lead to the development of a large number of dry shrinkage cracks in the soil, commonly known as cracking, which greatly weaken the engineering properties of the soil and provide favorable conditions for the development of soil engineering disasters [
10,
11]. In recent years, a large number of scholars and research institutions at home and abroad have begun to pay attention to the cracking behavior of soil under extreme arid climate conditions [
12,
13,
14]. The cracking of the soil surface will multiply the permeability of soil, and will have a negative impact on hydraulic engineering and environmental geotechnical engineering [
15]. In 2007, the severe drought in Chongqing caused serious cracking and reduced the stability of more than 1200 reservoir dams in the region, which directly faced the threat of dam failure after rainstorms. The same problem also occurred in hundreds of kilometers of flood control dams in Britain, the Netherlands, the United States, Australia and many other countries, with tens of billions of dollars needing to be invested every year to check and to repair the cracks developed in the dam body, to prevent piping and collapse. Cracking will greatly weaken the mechanical properties of soil [
16,
17]. Under the action of an arid climate, expansive soil will have a large degree of shrinkage deformation, and a large number of cracks easily develop on the surface. Swelling shrinkage and fissure are the typical characteristics of expansive soil. Therefore, expansive soil is often called “cracked soil”. The middle route of the South-to-North Water Transfer Project in China crosses the expansive soil canal section for nearly 400 km. Most of the canal section collapses, and shallow landslides are related to the cracks developed in the expansive soil, especially under the repeated action of cracking in the dry season and water expansion in the rainy season, resulting in the unsaturated process of the soil and the expansion of the unsaturated zone, which greatly changes the physicochemical, hydraulic, and mechanical properties of the soil [
18]. Under the action of an arid climate, the surfaces of some soil cultural relics or ancient buildings are also easy to develop and crack, so as to accelerate the weathering, denudation, and destruction of the surface structure, which greatly increases the difficulty of the protection of cultural relics and ancient sites. In the design of municipal solid waste sanitary landfill, there are many examples of the cracking failure of the isolation system due to the insufficient consideration of arid climate factors. Some scholars have pointed out that drought evaporation has led to more loose and broken surface source deposits, which have created convenient conditions for the outbreak of large-scale debris flow in the rainy season [
19,
20].
In order to evaluate soil evaporation behavior, based on the classical water heat air transport theory, different scholars have proposed different evaporation models to predict and evaluate soil evaporation under atmospheric action, such as the Penman model, the Philip and De Vries model, and the modified Penman Wilson model [
21,
22]. These classical theoretical models can generally obtain good calculation results in homogeneous sand, but there will be large errors in clay, mainly because the interaction between clay and water molecules is very complex, and because the water migration process in clay under evaporation is much more complex than that in sand [
23]. Most of the existing theoretical models only consider ambient temperature, relative humidity, and other meteorological parameters. Less consideration is given to the influence of soil factors on evaporation and the change in soil engineering properties caused by evaporation, which greatly restricts the popularization and application of the above theoretical results in practical engineering.
In order to study soil cracking, many scholars have proposed different methods in the past, and have basically established the cracking research method system, which is mainly divided into three categories: the indoor model test, the in situ observation test, and numerical simulation [
24,
25,
26]. The quantitative acquisition of geometric parameters of the crack network has always been an important aspect of crack research. It is of great significance to evaluate the crack development state, engineering properties, and potential impact of soil. The early quantitative analysis technology of cracking is mainly based on on-site manual measurement, but the measurement results are easily disturbed by human and environmental factors. In addition, the geometry of the crack network is extremely complex; thus, it is difficult to obtain accurate and comprehensive parameters such as crack length, width, area, and angle in the actual operation process [
27]. Miller et al. [
28] introduced the crack strength factor parameter, which is defined as the ratio of the crack area to the total soil area. Velde [
29] analyzed the fractal dimension of fractures using digital image processing technology. In recent years, with the development of computer science, image processing technology has been widely used in the quantitative analysis of the crack network. The development degree of soil and concrete cracking can be described by fractal [
30].
However, there are few reports on the relationship between soil drying shrinkage cracking, and the friction and permeability of the contact surface. Therefore, in order to fully understand the influence of interface friction and water permeability on soil drying cracking behavior, six samples were prepared in the laboratory. The basic conditions of the substrate were grease, geomembranes, and geotextiles. They were continuously dried at a constant ambient temperature. Using digital image processing technology, crack morphology under different spacing is described quantitatively. The effects of interface friction and permeability on soil cracking behavior are analyzed, and the evolution characteristics and formation mechanism of cracks in soil are revealed.
2. Materials and Methods
2.1. Materials
The soil used in this experiment was from Urumqi, Xinjiang, China. It has a continental arid climate in the middle temperate zone, with less rain and sufficient sunshine. The average annual precipitation is less than 200 mm. The hottest months of the year are July and August, with an average temperature of 25.7 °C. The coldest month is January, with an average temperature of −15.2 °C. In recent years, various construction projects have been accelerating. The sedimentary depth of the test soil is 50~75 cm, and the main mineral components are illite, illite montmorillonite interlayer minerals, and kaolinite. After the test soil is taken back to the laboratory, it needs to be dried at 110 °C for 48 h, and then it is stored in a sealed bottle after grinding and a 2 mm screen. The grease used in this experiment is milky white and viscous. It was purchased from Lingcheng Lubricating Oil Co., Ltd. in Xinxiang City, China. Its temperature range is −30~180 °C. In the industry, it has lubrication, rust prevention, anti-corrosion, and anti-oxidation effects. Its main component is fatty acid lithium soap thickening refined mineral oil, and many additives such as anti-oxidation and anti-rust agents are added. The geomembranes used in this experiment were black, with a thickness of 0.2 mm, a relative density of 0.918~0.965, and a melting point of 110~130 degrees. Additionally, a high-density polyethylene impermeable membrane material was used. The breaking strength of the material was greater than 20.0 KN/m, and the strength retention rate of the material was greater than 85.0% when it was soaked in a solution with pH of 2~11. The geotextiles used in this experiment were gray-white, 2 mm thick, with good water permeability on one side, a strong tensile force, and corrosion resistance.
2.2. Sample Preparation
The prepared soil was fully mixed with distilled water to prepare saturated mud with a water content of 130%. The mud was placed on a shaking table and vibrated for 5 min to remove bubbles in the mud. Six round glass containers were used to hold the mud, with an inner diameter of 20 cm and a height of 4 cm. Grease was applied to the bottom of the container to reduce the floor roughness during mud drying shrinkage. The sample numbers were S1 and S2, where S2 was a parallel sample. Geomembranes and geotextiles were cut into regular circles with a radius of 10 cm and were placed at the bottom of the glass container. The samples were numbered S3, S4, S5 and S6, where S4 and S6 were parallel samples. Then, the saturated mud was carefully poured into containers, and the weight of the mud in each container was about 300 g. The sample preparation process and image processing process are shown in
Figure 1.
Table 1 summarizes the parameter information of the test samples.
2.3. Test Method and Image Processing
The prepared test samples were evaporated and dried in a constant temperature and humidity test chamber; the temperature was controlled at 25 °C, and the relative humidity was 30%. The samples were weighed at different time intervals, accurate to 0.01 g, to determine the change in the moisture content during drying. The dynamic process of sample surface drying cracking was monitored with a digital camera. The crack propagation was quantitatively analyzed via image processing technology. When the mass change for the sample within one day was less than 0.01 g, the drying test was stopped.
The image of the fracture development process was processed, and then, the fracture was quantitatively analyzed. In quantitative analysis, only the edge shrinkage area of the container boundary may be mistaken for soil cracks, resulting in an increase in geometric parameters such as the total length and the average width of the cracks. In order to reduce the influence of the edge shrinkage region on determining the geometric parameters of the crack network, only the central part was used, Π × 10 cm
2, for quantitative analysis. The process of the image processing is shown in
Figure 1. The original color image was first converted to a gray image. In order to enhance the contrast between the crack and the surrounding soil matrix, the homomorphic filtration method was adopted. Then, a Gaussian filter was used to denoise the image. Upon analyzing the pixels of the gray image, gray values of the soil and background that were greater than the threshold of 255 were specified as 0, and gray values of the crack component that were less than the threshold were specified as 1. The filtered gray image was converted into a binary image. Finally, two quantitative parameters, the fracture rate and the fractal dimension of the fracture network, were obtained.
2.4. Crack Characteristics
Various methods have been proposed to calculate the lengths of cracks, such as using observations in convex windows proposed by Kulatilake and Wu [
31]. Therefore, circular windows are used, which improves the estimation of the true trace length distribution of cracks [
32,
33,
34,
35]. However, the use of circular windows is more accurate than observations in convex windows. Therefore, circular windows have been used to estimate the true trace lengths of cracks [
36]. The fractal dimension is an important parameter for quantitatively characterizing the fractal nature of objects, and can be used to comprehensively describe the degree of cracking of soils [
37,
38]. In fractal dimension analyses, the dimension of a straight-line segment is defined as 1, with a length of
X. By dividing the line into
N =
b smaller segments of equal length, each smaller segment is a point of the straight-line segment. Each point is identical to the entire line, and this ratio is known as the similarity ratio
r, where
r = 1/
b = 1/
N. In two-dimensional space, there are
N =
b2 small squares, which are similar to the entire two-dimensional plane, thus satisfying:
The similarity ratio is given by:
Similarly, the similarity ratio for a
Ds-dimension cylinder is given by:
Then,
where
N is the number of units which resembles the entire crack image,
r is a coefficient of the similarity ratio, and
Ds is the fractal dimension from the crack image.
The crack intensity factor
Rt is defined as the ratio of the projected area of the crack on the 2D plane to the total 2D surface area. It represents the space occupied by the crack of the specimen. It can be used to describe the degree of cracking as follows:
where
Scrack is the projected area of the crack and
Ssoil is the total surface area of the sample.
The evaporation rate
E is the weight of water lost per unit time, which can be calculated using Formula (1) according to the change in the recorded sample weight data. The evaporation rate can be calculated using Equation (3).
where Δ
t is the time of evaporation, Δ
m is the amount of evaporated water, and
SE is the area of the sample.
4. Discussion
During the drying process, due to the continuous evaporation of water in the soil, the soil water content and saturation gradually decrease, resulting in a gradual increase in matrix suction and tensile stress in the soil. There is a positive correlation between the tensile strength and the matrix suction of soil. Once the tensile stress generated in the soil exceeds the tensile strength of the soil, cracks will occur on the surface of the sample. The distribution of the tensile stress depends not only on the defects in the soil, but also on the base friction. When the sample base is composed of grease, the friction of the sample base is significantly less than that for when the sample base is geomembranes. When the sample substrate is grease or geomembranes, the substrate is impervious. In the process of the gradual dehydration and drying of the sample, the shrinkage of the sample with friction in the horizontal direction will be limited, which makes it more difficult for the soil particles to become close to each other. In this case, the tensile stress may transfer and lead to dry cracking. The interlayer friction has a constraint on the movement of the soil particles, and a greater constraint on the movement of the soil particles. This will lead to a faster concentration of tensile stress, and increase the propagation rate and crack intensity factor of soil cracks. Therefore, reducing the friction of the sample substrate can reduce the dry cracks on the sample surface.
Through a large number of indoor experiments on soil drying and cracking, it is found that most soil samples are placed in impermeable plastic or glass containers at the bottom. However, the water permeability condition of the sample substrate is also an important factor affecting the surface drying and cracking of soil samples. In this experiment, when the soil sample base is grease and geomembranes, the base is impervious, while when the sample base is geotextiles, the base of the soil sample is permeable. At this time, the sample can dry and lose water from the top, sides, and bottom. The bottom of the soil sample is also the water loss area; therefore, when the base contact condition is geotextiles, the initial water loss rate of the soil sample is relatively fast, and the cracking rate of the surface is relatively large. However, because geotextiles have a certain degree of water absorption, the final soil moisture content in the final state will be higher than that in the other two soils. The soil cracking mechanism under different substrate friction and permeability conditions is shown in
Figure 6.
5. Conclusions
In order to investigate the development of desiccation cracks in soils affected by different geomembrane materials, free drying tests were carried out in the laboratory. The characteristics of the desiccation cracks of soil were determined for different amounts of water loss. The characteristics of the progressive changes in the cracks were quantitatively analyzed using digital image processing.
An important factor affecting the drying and cracking of the soil sample surface is the water permeability of the sample matrix. The dry shrinkage fracture network formed on the soil surface has good statistical self-similar classification characteristics. In the process of the gradual dehydration and drying of the sample, the shrinkage of the sample with friction in the horizontal direction will be limited, which makes it more difficult for the soil particles to become close to each other. Therefore, reducing the friction of the sample substrate can reduce the dry cracks on the sample surface.
Due to the water absorption of geotextiles, when the base of the sample is geotextiles, the base of the soil sample is permeable. At this time, the sample can be dried from the top, sides, and bottom. The bottom of the soil sample is also the water loss area; therefore, the base is geotextiles, the initial water loss rate of the soil sample is relatively fast, and the cracking rate of the surface is relatively large.
According to the variation law of the evaporation curve, the evaporation process of the sample can be divided into three stages. Stage I: constant rate stages of evaluation. Stage II: degradation rate stages of evaluation. Stage III: residual rate stages of evaluation. The evaporation curve can be well fitted using the Boltzmann function.